Patent Application
20130269480
1. Field of Invention
The present invention relates to a method for making a strong aluminum alloy and, more particularly, to a method for providing an aluminum alloy with excellent tensile strength, hardness and radiation and low density.
2. Related Prior Art
Al—Si—Mg (6000 series) alloys have been used in the defense industry, automobile industry and sports industry for being light weight. Al—Si—Mg alloys however exhibit inadequate strength and need improvement.
To improve the strength of commercially available Al—Si—Mg alloys, they may be added with Sc as a grain refiner. The concentration of the Sc is about 0.03% to 0.20% to increase the tensile strength and hardness of the Al—Si—Mg alloys to about 450 MPa.
Sc is rare and therefore expensive. Accordingly, the Al—Si—Mg alloys added with the Sc are expensive.
The present invention is therefore intended to obviate or at least alleviate the problems encountered in conventional alloy.
It is the primary objective of the present invention to provide a method for making an aluminum alloy with excellent tensile strength, low density and excellent radiation.
To achieve the foregoing objective, the method includes the steps of providing a base material, adding 0.06 wt % to 0.30 wt % of zirconium and 0.06 wt % to 0.30 wt % of vanadium to the base material, and melting the basic material with the zirconium and vanadium to provide an aluminum alloy.
The base material includes 92.55 wt % to 97.38 wt % of aluminum, 0.9 wt % to 1.8 wt % of silicon, less than 0.5 wt % of iron, 0.6 wt % to 1.2 wt % of copper, 0.4 wt % to 1.1 wt % of manganese, 0.6 wt % to 1.4 wt % of magnesium, less than 0.40 wt % of chromium, less than 0.25 wt % of zinc and less than 0.20 wt % of titanium.
In another aspect, the step of melting the base material with the zirconium and vanadium includes the step of providing an induction furnace for melting the base material with the zirconium and vanadium in argon.
In another aspect, the method further includes the steps of degassing and slag-removing the aluminum alloy melt, turning the aluminum alloy melt into an aluminum alloy nugget by direct chill casting, and pressurizing the aluminum alloy nugget to turn the aluminum alloy nugget into another shape.
In another aspect, the step of pressurizing the aluminum alloy nugget includes the step of extruding the aluminum alloy nugget. The step of extruding the aluminum alloy nugget may include the step of providing an extruding machine.
In another aspect, the step of pressurizing the aluminum alloy nugget includes the step of providing a rolling machine for rolling the aluminum alloy nugget. The step of rolling the aluminum alloy nugget may include the step of providing a rolling machine.
Other objectives, advantages and features of the present invention will be apparent from the following description referring to the attached drawings.
The present invention will be described via detailed illustration of the preferred embodiment referring to the drawings wherein:
Referring to
At first, there is provided a base material 10. The base material 10 includes 92.55 wt % to 97.38 wt % of aluminum 101, 0.9 wt % to 1.8 wt % of silicon 102, 0.5 wt % of iron 103, 0.6 wt % to 1.2 wt % of copper 104, 0.4 wt % to 1.1 wt % of manganese 105, 0.6 wt % to 1.4 wt % of magnesium 106, less than 0.4 wt % of chromium 107, less than 0.25 wt % of zinc 108 and less than 0.20 wt % of titanium 109. Then, the basic material 10 is added with zirconium 111 and vanadium 112, and molten in argon in an induction furnace, thus providing aluminum alloy melt 11.
Secondly, the aluminum alloy melt 11 is subjected to degassing and slag-removing before it is subjected to extruding b in the form of chill casting to provide an aluminum alloy nugget 12.
Thirdly, the aluminum alloy nugget 12 is subjected to pressurizing c, thus providing an aluminum alloy product 1. The aluminum alloy nugget 12 is made into the aluminum alloy product 1 by extruding or rolling. For example, the aluminum alloy nugget 12 may be made into the aluminum alloy product 1 in the form of a rod or plank with an extruding machine. Alternatively, the aluminum alloy nugget 12 may be made into the aluminum alloy product 1 in the form of a board or sheet with a rolling machine.
Referring to
Referring to
The grain-refining of aluminum alloys is mainly done by addition of grain refiners such as scandium (“Sc”) and zirconium 111 (“Zr”) to grow precipitates such as Al3Sc at grain boundaries to interfere with the growth of the grains. Alternatively, a strengthening phase may be distributed in the grains. When the grains are refined and strengthened, the grain boundaries are effective obstacles against slip, concentration of stress in front of the grain boundaries activate a lot of slip systems, and deformation of the alloys become even. Thus, the strength and tenacity of the alloys are increased. The relation of the yield strengths of the alloys to the sizes of the grains can be expressed in a Hall-Petch equation, i.e., a σyield=ρ0+kd−1/2, wherein σ0 stands for the yield strength of a single grain, k stands for a slope in the Hall-Petch equation, and d stands for the size of the grain.
The method of the present invention provides aluminum alloys without the drawbacks of the prior art. For example, the aluminum alloys of the present invention exhibit high tensile strengths, excellent plastic deformations, low densities, radiations and hardness. Hence, the aluminum alloys of the present invention can be used in shells in the defense industry, the aerospace industry, the automobile industry, the appliance industry and the OA industry for example.
The present invention has been described via the detailed illustration of the preferred embodiment. Those skilled in the art can derive variations from the preferred embodiment without departing from the scope of the present invention. Therefore, the preferred embodiment shall not limit the scope of the present invention defined in the claims.