Method for making an aqueous emulsion polymer

Abstract

A method for making a polymer, includes the step of polymerizing a mixture of a vinyl ester monomer, a (C.sub.1 -C.sub.12)alkyl (meth)acrylate monomer and a mono ethylenically unsaturated polar monomer by free radical initiated polymerization in an aqueous medium and in free presence of a colloidal stabilizer, a first poly(alkoxylated) alkyl phenol having less than or equal to 12 alkoxyl units per molecule and a second poly(alkoxylated) alkyl phenol having greater than 12 alkoxyl units per molecule, to form an emulsion of the polymer in the aqueous medium.

Description

Claims

1. A method for making a polymer comprising:

polymerizing monomers in an aqueous medium by free radical initiated polymerization, said monomers comprising:

from about 20 parts by weight to about 70 parts by weight of a vinyl ester monomer per 100 parts by weight of the monomers;

from about 30 parts by weight to about 80 parts by weight of a (C.sub.1 -C.sub.12) alkyl (meth)acrylate monomer per 100 part by weight of the monomers; and

from about 0.1 parts by weight to about 10 parts by weight of a monoethylenically unsaturated polar monomer per 100 parts by weight of the monomer, in the presence of:

from about 1.5 parts by weight to about 2.8 parts by weight of a colloidal stabilizer per 100 parts by weight of the monomers;

from about 1.2 parts by weight to about 1.6 parts by weight of a first poly(alkoxylated) alkyl phenol per 100 parts by weight of the monomers, said first poly(alkoxylated) alkyl phenol having about 10 alkoxyl units per molecule; and

from about 0.3 parts by weight to about 1.4 parts by weight of a second poly(alkoxylated) alkyl phenol per 100 parts per weight of the monomers, said second poly(alkoxylated) alkyl phenol having about 16 alkoxy units per molecule,

to form an emulsion of the polymer in the aqueous medium, said polymer having a glass transition temperature from about -40.degree. C. to about +15.degree. C.;

wherein the total weight of the first and second poly(alkoxylated) alkyl phenol is greater than about 1.8 parts per 100 parts per weight of the monomers.

2. The method of claim 1, wherein the vinyl ester monomer is selected from the group consisting of vinyl acetate, vinyl propionate, vinyl neononanoate, vinyl neodecanoate, vinyl 2-ethylhexanoate, vinyl pivalate, vinyl versatate and mixtures thereof.

3. The method of claim 1, wherein the (C.sub.1 -C.sub.12)alkyl (meth)acrylate monomer is selected from the group consisting of ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, lauryl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, isodecyl methacrylate, lauryl methacrylate and mixtures thereof.

4. The method of claim 1, wherein the monoethylenically unsaturated polar monomer is a monoethylenically unsaturated carboxylic acid monomer.

5. The method of claim 4, wherein the monoethylenically unsaturated carboxylic acid monomer is acrylic acid, methacrylic acid, itaconic acid or a mixture thereof.

6. The method of claim 1, wherein the colloidal stabilizer is selected from the group consisting of poly(vinyl alcohol), partially hydrolyzed poly(vinyl alcohol), fully hydrolized poly(vinyl alcohol) and mixtures thereof.