Claims
- 1. A method for producing lithoplate, comprising:
- providing a molten aluminum alloy consisting essentially of the following elements in percent by weight: Cu-0 to 0.20%; Si - 0.055 to 0.085%; Fe - 0.55 to 0.75%; Mn - 0 to 0.20%; Mg - 0.40 to 0.70%; Zn - 0 to 0.25%; Cr - 0 to 0.10%; Ti - 0 to 0.05% (when cast); V - 0 to 0.025%; other elements - 0 to 0.05%, not to exceed 0.15% total; and the remainder Al;
- casting the alloy into a mold to form an ingot;
- homogenizing the ingot at a suitable temperature for a period of time suitable to ensure homogenization of the ingot;
- hot rolling the ingot to produce a reroll stock;
- cold rolling the reroll stock to a finished gauge workpiece; and
- graining at least one surface of the workpiece.
- 2. A method according to claim 1, further comprising providing an anodized finish to the grained workpiece.
- 3. A method according to claim 1, further comprising adding a grain refiner to the molten alloy.
- 4. A method according to claim 3, wherein the grain refiner comprises an element selected from Group VB of the periodic table of elements.
- 5. A method according to claim 1, wherein the ingot as cast has an interior crystalline structure and a disturbed exterior crystalline structure, the process further comprising scalping the ingot to a depth sufficient to remove substantially all of the exterior structure of cast metal.
- 6. A lithoplate having a grained surface, formed of a homogenized aluminum alloy of the 5XXX series, the lithoplate being anodized and substantially free of surface streaks.
- 7. The lithoplate of claim 6, further comprising a light sensitive resist coated on the grained surface.
- 8. The lithoplate of claim 6, wherein the alloy consists essentially of, in weight percent, about 0 to 0.20% Cu; about 0.055 to 0.085% Si; about 0.55 to 0.75% Fe; about 0 to 0.20% Mn; about 0.40 to 0.70% Mg; about 0 to 0.25% Zn; about 0 to 0.10% Cr; about 0 to 0.05% Ti; about 0 to 0.025% V; about 0 to 0.05% other elements not to exceed about 0.5% total; and the remainder Al.
- 9. A lithoplate having a grained surface coated with a light-sensitive resist, the improvement comprising the lithoplate having a composition consisting essentially of 0.20% max. Cu, 0.055-0.085% Si, 0.55-0.75% Fe, 0.20% max. Mn, 0.40-0.70% Mg, 0.25% max. Zn, 0.10% max. Cr, 0.05% max. Ti, 0.025% max. V, 0.05% max. each of other elements not to exceed 0.15% total, and the remainder Al.
Parent Case Info
This application is a continuation of Ser. No. 939,318 filed Dec. 8, 1986 allowed.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4818300 |
Rooy et al. |
Apr 1989 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
939318 |
Dec 1986 |
|