Patent Application
20090123357
1. Field of the Invention
The present invention relates to a method for making nanoparticles, and more particularly to a method for making silica nanoparticles by flame spray pyrolysis adopting a two-fluid nozzle, which sprays droplets under high pressure from a silicon alkoxide solution to directly oxidize in a flame thereby producing spherical silica nanoparticles.
2. Description of the Prior Art
In general, nanoparticles refer to particles having a size 100 nm or less, which are mainly used as advanced materials due to high specific area per mass and novel functions.
Silica (SiO2) particles are adopted in various applications such as fillers of Epoxy display and semiconductor Molding Compound (EMC), fillers of cosmetics and copy machine toner, components of paint and ink for improving endurance and inducing diffused reflection, raw materials of optical fibers, ceramic ware and glasses.
Examples of technologies for making such silica particles are known from U.S. Pat. No. 6,322,765, titled “Process for preparing silicon dioxide”, filed Sep. 8, 1998; U.S. Pat. No. 6,386,373, titled “Process for making silica powder and use of such powder in the manufacture of an optical fiber preform”, filed Mar. 10, 2000; U.S. Pat. No. 6,698,247, titled “Method and feedstock for making silica by flame combustion”, filed May 4, 2001; Korean Patent No. 10-0354432, titled “Method for making spherical silica particles by spray pyrolysis”, filed Jul. 12, 2000; Korean Patent No. 10-0468050, titled “Method for making spherical silica powder”, filed Dec. 4, 2001; Korean Patent No. 10-0503675, titled “Method for making high purity silica”, filed Mar. 9, 2002; and Korean Patent No. 10-0477200, titled “Method for making silica particles by supersonic spray pyrolysis”, filed Jun. 5, 2002.
To be used in advanced material fields such as semiconductor fields which require high integration, small size and thickness reduction, silica particles should be produced in nanosize and maintain a spherical geometry to obtain high filling density.
To make silica nanoparticles, many researchers have developed physical/chemical approaches. Examples of such approaches are known from U.S. Pat. No. 5,580,655, titled “Silica nanoparticles”, filed Mar. 3, 1995; U.S. Pat. No. 5,770,022, titled “Method of making silica nanoparticles”, filed Jun. 5, 1997; and Korean Patent No. 10-0330626, titled “Method for making nanosize silica fine particles”, filed Mar. 7, 2000.
U.S. Pat. No. 5,580,655 relates to a method for vaporizing Si metal with a pulse laser to react with oxygen in order to produce silica nanoparticles. However, pulse laser method shows a low yield of silica nanoparticles, and thus is hardly applicable in the industry.
U.S. Pat. No. 5,770,022 relates to a method for synthesizing silica, in which a direct current discharge is performed with an anode of Si and a cathode of Cu or W to generate plasma in an oxygen atmosphere so that Si in the anode is vaporized and oxidized to synthesize silica. Korean Patent No. 10-0330626 relates to a method for synthesizing silica nanoparticles, in which an evaporator vaporizes source material for silica such as silicon alkoxide, which is then supplied to a flame reactor to be synthesized into silica nanoparticles through Chemical Vapor Deposition (CVD).
According to these methods, however, a large amount of energy is consumed and it is difficult to make spherical silica nanoparticles since source material such as Si metal or silicon alkoxide compound is vaporized and oxidized to produce silica nanoparticles.
Accordingly, the present invention has been made to solve the above-mentioned problems occurring in the prior art, and an object of the present invention is to provide a method for making silica nanoparticles by flame spray pyrolysis adopting a two-fluid nozzle, which sprays droplets under high pressure from a silicon alkoxide solution to directly oxidize in a flame thereby producing spherical silica nanoparticles.
In order to accomplish this object, there is provided a method for making silica nanoparticles using a flame reactor, which includes a droplet spray having a two-fluid nozzle and a burner of a quintuple tube structure, the method comprising steps of: spraying droplets of silicon alkoxide as liquid Si compound through the droplet spray of the flame reactor; generating a flame by the flow of inert gas, oxygen, hydrogen and air simultaneously into the burner of the flame reactor; delivering the liquid Si compound through the flame of the burner to produce silica nanoparticles having a mean particle size ranging from 9 nm to 68 nm; and collecting and recovering resultant nanoparticles in a particle collector.
Here, the droplet spray is inserted into an innermost first tube of quintuple tubes of the burner, and dispersed air at 1% to 3% in volume of the entire flow rate of gas is blown into the droplet spray, by which silicon alkoxide introduced into the droplet spray is sprayed in the form of fine droplets under high pressure, Ar gas at 7% to 8% in volume of the entire flow rate of gas is blown into the second tube, hydrogen gas at 3% to 13% in volume of the entire flow rate of gas is blown into the third tube, oxygen gas at 21% to 23% in volume of the entire flow rate of gas is blown into the fourth tube, and air at 53% to 62% in volume of the entire flow rate of gas is blown into the fifth tube.
Preferably, the input of silicon alkoxide is varied from 2.1×10 mol/l to 8.7×10−4 mol/l to control the mean size of the silica nanoparticles.
Preferably, the dispersed air is varied from 1.0 kgf/cm2 to 5.0 kgf/cm2 to control the mean size of the silica nanoparticles.
Preferably, the silicon alkoxide is pretreated through thinning with ethanol or methanol prior to being sprayed by the droplet spray.
The above and other objects, features and advantages of the present invention will be more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which:
In the following description and drawings, the same reference numerals are used to designate the same or similar components, and so repetition of the description on the same or similar components will be omitted. The following terminologies used in view of the functions may be construed differently according to users, operator's intention and practices. Accordingly, such terminologies should be defined based on the general concept disclosed herein.
An apparatus for making silica nanoparticles by flame spray pyrolysis adopting a two-fluid nozzle according to the invention will now be described in detail with reference to the accompanying drawings.
In the drawings,
Referring to
The flame reactor includes a droplet spray 10 having a two-fluid nozzle and a burner 20 of a quintuple tube structure including five tubes 21 to 25. The droplet spray 10 having a two-fluid nozzle is inserted into the innermost first tube 21, and dispersed air is blown into the droplet spray 10. In addition, inert gas, oxygen, hydrogen and air are blown in their order to the second to fifth tubes 22 to 25, respectively.
The dust collector 30 collects nanoparticles produced through the flame of the burner 20, and cooling water is flown into the dust collector 30.
Now a process for making silica nanoparticles by flame spray pyrolysis adopting a two-fluid nozzle according to the invention will be described in detail with reference to the accompanying drawings.
The process includes steps of spraying droplets of silicon alkoxide as liquid Si compound through the droplet spray 10 having a two-fluid nozzle of the flame reactor (S100), generating a flame by the flow of inert gas, oxygen, hydrogen and air simultaneously into the burner 20 of the flame reactor (S110), delivering the liquid Si compound through the flame of the burner 20 to produce silica nanoparticles having a mean particle size ranging from 9 nm to 68 nm (S120), and collecting and recovering the resultant nanoparticles in the particle collector 30 (S130). Here, silicon alkoxide comprises tetraethylorthosilicate (TEOS) or tetramethylorthosilicate (TMOS).
In the meantime, the droplet spray 10 having a two-fluid nozzle is inserted into the innermost first tube 21 of the quintuple tubes 21 to 25. Dispersed air occupying 1% to 3% in volume of the entire flow rate of gas is blown into the droplet spray 10, by which silicon alkoxide introduced into the droplet spray 10 is sprayed in the form of fine droplets under high pressure. Ar gas at 7% to 8% in volume of the entire flow rate of gas is blown into the second tube 22, hydrogen gas at 3% to 13% in volume of the entire flow rate of gas is blown into the third tube 23, oxygen gas at 21% to 23% in volume of the entire flow rate of gas is blown into the fourth tube 24, and air at 53% to 62% in volume of the entire flow rate of gas is blown into the fifth tube 25.
In addition, the amount of silicon alkoxide is varied in the range from 2.1×10 mol/l to 8.7×10−4 mol/l of the entire flow rage of gas to control the mean particle size of the silica nanoparticles.
The pressure of dispersed air is varied in the range from 1.0 kgf/cm2 to 5.0 kgf/cm2 to control the mean particle size of the silica nanoparticles.
Silicon alkoxide is pretreated through thinning with ethanol or methanol prior to being sprayed by the droplet spray having a two-fluid nozzle.
Now examples of a process for making silica nanoparticles by flame spray pyrolysis adopting a two-fluid nozzle according to the invention will be described in detail with reference to the accompanying drawings.
Example 1 was aimed to adjust the size of resultant particles by varying the pressure of dispersed air for micronizing liquid source material during the production of nanoparticles.
An experiment was carried out to make silica nanoparticles, in which silicon alkoxide (TEOS) mixed with ethanol were delivered through a flame under the following conditions.
A liquid sample or TEOS was injected into the droplet spray 10 as shown in
Describing the flow rate of gas introduced into the flame reactor, dispersed air was blown into the first tube 21 of the burner 20 having the first to fifth tubes 21 to 25, at a volume fraction of 2% to 3% in the entire flow rate of gas with varying pressures of 1.0 kgf/cm2, 3.0 kgf/cm2 and 5.0 kgf/cm2, in order to make the TEOS reactive material into fine droplets having a molarity of 2.1×10−4 mol/l. In addition, Ar gas at 7% in volume fraction was blown into the second tube 22, hydrogen gas at 14% in volume fraction was blown into the third tube 23, oxygen gas at 21% in volume fraction was blown into the fourth tube 24, and air at 55% to 56% in volume fraction was blown into the fifth tube 25.
Changes in the specific surface area and particle size of resultant particles were examined with a specific surface area analyzer (BET method). The specific area increased from 40m2/g to 113m2/g and 318m2/g as the pressure of dispersed air was raised from 1.0 kgf/cm2 to 3.0 kgf/cm2 and 5.0 kgf/cm2. The mean size of particles was decreased from 68 nm to 24 nm and 9 nm when calculated from a conversion formula dp=6/(ρp·A), where dp is particle size, ρp is silica density, and A is specific surface area.
Example 2 was aimed to adjust the size of resultant particles by injecting a reactive material into a hot flame with different concentrations of 2.1×10−4 mol/l, 3.3×10−4 mol/l and 4.8×10−4 mol/l while maintaining constantly the pressure of dispersed air for micronizing liquid source material during the production of nanoparticles.
Describing the flow rate of gas blown into the flame reactor, the pressure of the dispersed air introduced into the first tube of the burner was maintained constantly at 3.0 kgf/cm2, which is 1% to 2% in volume of the entire flow rate of gas, in order to make a TEOS reactive material into fine droplets having molarities of 2.0×10−4 mol/l, 3.3×10−4 mol/l and 4.8×10−4 mol/l. In addition, Ar gas at 7% in volume fraction was blown into the second tube 22, hydrogen gas at 14% in volume fraction was blown into the third tube 23, oxygen gas at 21% in volume fraction was blown into the fourth tube 24, and air at 56% to 57% in volume fraction was blown into the fifth tube 25. With these conditions, silica nanoparticles were produced.
Examining changes in the specific surface area and size of resultant particles, the specific surface area decreased from 113 m2/g to 51 m2/g with the input of reactive material increasing, and the mean particle size increased from 24 nm to 54 nm.
Example 3 was aimed to adjust the size of resultant particles by adjusting the flow rate of hydrogen gas used as fuel to 3% in volume fraction and then changing the flow rate of a TEOS reactive material.
Describing the flow rate of gas blown into the flame reactor, the pressure of the dispersed air introduced into the first tube of the burner was maintained constantly at 3.0 kgf/cm2, which is 2% in volume of the entire flow rate of gas, in order to make the TEOS reactive material into fine droplets having molarities of 2.1×10−4 mol/l, 3.3×10−4 mol/l and 4.8×10−4 mol/l. In addition, Ar gas at 8% in volume fraction was blown into the second tube 22, hydrogen gas at 3% in volume fraction was blown into the third tube 23, oxygen gas at 24% in volume fraction was blown into the fourth tube 24, and air at 63% in volume fraction was blown into the fifth tube 25. With these conditions, silica nanoparticles were produced.
Examining changes in the specific surface area and size of resultant particles, the specific surface area decreased from 150 m2/g to 87 m2/g as the input of the reactive material increases, and the mean particle size increased from 18 nm to 32 nm.
Example 4 was aimed to produce silica nanoparticles by substituting TMOS for TEOS, which was used as the reactive material in the production of the nanoparticles.
Describing the flow rate of gas blown into the flame reactor, the pressure of the dispersed air introduced into the first tube of the burner was maintained constantly at 3.0 kgf/cm2, which is 2% in volume of the entire flow rate of gas, in order to make the TMOS reactive material into fine droplets having a molarity of 5.0×10−4 mol/l. In addition, Ar gas at 7% in volume fraction was blown into the second tube 22, hydrogen gas at 14% in volume fraction was blown into the third tube 23, oxygen gas at 21% in volume fraction was blown into the fourth tube 24, and air at 56% in volume fraction was blown into the fifth tube 25.
According to the method for making silica nanoparticles by flame spray pyrolysis of the invention, a droplet spray having a two-fluid nozzle and a burner of a quintuple tube structure are used to change the pressure of dispersed air, the input of reactive solution and the flow rate hydrogen gas in a reactive system of TEOS (or TMOS)-alcohol-Ar—H2-O2-air in order to controllably produce silica nanoparticles having a mean parade size of 9 nm to 68 nm. This also provides design sources for a reactor for mass production of such silica nanoparticles.
Although a preferred embodiment of the present invention has been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.