The invention relates to a method for manufacturing a fuel tank on the basis of thermoplastic material.
Known fuel tanks of thermoplastic material are mainly formed on the basis of polyethylene (HDPE). These often have a multi-layered wall structure with barrier layers for hydrocarbons. Known fuel tanks of thermoplastic material are manufactured either by injection moulding, extrusion blow-moulding or thermoforming or by combinations of the aforementioned processes. In comparison with fuel tanks of sheet metal, fuel tanks of thermoplastic material have the advantage that they can be manufactured relatively easily with a spatially complex contour and are just as relatively deformation-resistant and stable. The plastic has a certain elasticity, so that short-term deformations of a fuel tank of thermoplastic material are non-critical, insofar as they generally do not lead to permanent changes in the contour of the tank.
Since, however, the HDPE that is usually used for the manufacture of plastic fuel tanks has a tendency to flow when it is subjected to tensile/compressive loading over prolonged periods of time, without additional reinforcing measures fuel tanks are not suitable for permanently withstanding increased internal pressure without permanent deformations of the tank contour occurring.
Therefore, various measures for the structural reinforcement/structural stiffening of fuel tanks of thermoplastic material are known. On the one hand, it is known to reinforce the tank walls locally, on the other hand it is known to provide within the fuel tanks supporting elements and tie bars, which are intended to avoid bulging or buckling of the fuel tank under variations in pressure. EP 2067648 A1 describes a a fuel tank and a method for producing such wherein two discrete parts of a tank, each having a laminate structure comprising a fluororesin layer and a thermoplastic resin layer are utilized. All of the known reinforcing measures significantly increase the mass of the fuel tank. Plastic tanks according to the present state of the art, of one or more layers, have an average wall thickness of 5 to 6 mm and, depending on the tank volume, a mass of about 6 to 10 kg. Additional requirements for stability and fire protection inevitably lead to an increase in this mass, which is actually undesirable in respect of a lightweight structure.
The invention is based on the object of providing a method of the type mentioned at the beginning with which fuel tanks which have a likewise reduced wall thickness with a significantly reduced weight can be manufactured.
The object is achieved by a method for manufacturing a fuel tank on the basis of thermoplastic material, the method comprising the following method steps:
An essential aspect of the method according to the invention concerns the provision of film-laminated semifinished products of a fibre composite material with a matrix of thermoplastic material, the thermoplastic matrix allowing these semifinished products to be formed into corresponding shells in a separate shaping process. Such semifinished products of fibre composite material are, for example, so-called organometallic sheets with a thermoplastic matrix, which can be produced in relatively small material thicknesses with increased strength.
A relatively thin film is laminated onto these relatively stiff semifinished products.
Firstly, the finished-laminated semifinished products produced by the method are cooled and cured. They may be configured in any way desired in a moulding process performed at a different time than the production of the semifinished products.
The heat treatment of the laminated semifinished products may be performed, for example, by means of a known infrared heating device on a thermoforming mould.
In the course of this heat treatment, a preconditioning of the semifinished products may be provided, i.e. preheating of the semifinished products before the final step of heating up until the thermoplastic material plasticizes.
In the case of a particularly expedient embodiment of the method according to the invention, it is provided that the semifinished products are only laminated on one side and that the laminated side forms the inner side of the fuel tank.
The shells are expediently formed in each case with a peripherally encircling flange. The shells may, for example, be bent over to create an edge-formed seam, such an edge-formed seam or lock seam forming a labyrinth seal of the tank seam. In particular if the film that is laminated-on on the inside has a relatively small thickness, bending the peripherally encircling flange over to create an edge-formed seam is advantageous.
Alternatively, the flange may be provided with a peripheral profile, which reaches around the end faces of the shells and forms a peripheral abutting edge. Such a peripheral profile may be formed, for example, as a C profile or a U profile, which is adhesively bonded or welded to the shells. The peripheral profile may also be moulded on in one piece in a downstream injection-moulding process.
Woven or laid fibre structures that are embedded in a thermoplastic matrix are preferably used as fibre composite materials. An HDPE comes into consideration, for example, as the thermoplastic matrix. The fibres may be selected from a group comprising glass fibres, carbon fibres and aramid fibres.
The method according to the invention also comprises the introduction of inserts into the tank before the joining of the shells. For the purposes of the present invention, inserts are valves, lines, surge tanks, feed units or the like.
In the case of a particularly advantageous variant of the method according to the invention, the inserts are premounted on an insert carrier. The insert carrier may be inserted into a shell as a lost carrier. For example, such an insert carrier may be formed as an injection-moulded plastic carrier that is already adapted to the tank contour. Fastening means for venting lines, valves, nipples and the like may already be moulded onto this carrier.
The inserts are preferably fastened to the insert carrier in the position in which they are later to be installed.
The insert carrier may be welded, clamped or latched.
Expediently, before the joining, at least one shell is provided with at least one lead-through for at least one line connection, into which a connection element is inserted from the inside in a sealing manner Such a connection element may be, for example, a connection nipple for a venting line of the tank or the like. The connection element may, for example, be already provided on a venting spider (line spider with valves) premounted on the insert carrier and is inserted into the correspondingly lead-through in a sealing manner during mounting of the insert carrier, for example in an upper shell of the tank, and is fastened from the outside after joining of the tank shells.
The welding or joining of the shells to form the closed tank may be performed, for example, by means of heated elements/hot plates, lasers, infrared heating devices or the like.
The semifinished products may also be formed such that they have, encircling the periphery on the laminated side, a narrow strip that is excluded from the film lamination. This periphery may form part of the encircling flange of the shells that absorbs the joining pressure during the welding, so that the EVOH layer of the laminate is not exposed by the joining, which would lead to impairment of the welded connection, since EVOH does not enter into an adhesive bond with HDPE.
The invention also relates to a fuel tank manufactured by the previously described method, the fuel tank comprising a tank body with a self-supportingly stiff outer shell of a fibre-reinforced thermoplastic material, which on the inner side of the tank is laminated with a multi-layered film of plastic, the outer shell being thicker than the film of plastic and the film of plastic comprising at least one barrier layer for hydrocarbons.
The film of plastic may, for example, have a maximum thickness of 1.25 mm. It may be formed as a five-layered laminate with EVOH as the barrier layer.
This five-layered laminate comprises, for example, EVOH in a layer thickness of between fifty and two hundred and fifty micrometres, which is embedded in two layers of adhesion promoter of at most two hundred micrometres each. HDPE covering layers, each of a layer thickness of three hundred micrometres, may be provided, for example, as outer layers.
It is advantageous if the ratio of the thickness of the outer shell to the thickness of the film of plastic is between 2 and 1.2.
The outer shell or the base material of a thermoplastic fibre-reinforced material may, for example, have a thickness of approximately 1.5 mm, so that the finished tank has a maximum total wall thickness of 2.75 mm, and at the same time a relatively high strength.
The invention is explained below on the basis of an exemplary embodiment that is represented in the drawings, in which:
Reference is first made to
Both the upper shell and the lower shell are provided with an encircling flange 8, at which the upper shell 1 and the lower shell 2 are joined to form the closed tank.
As already mentioned at the beginning, both the upper shell 1 and the lower shell 2 consist of a carrier material in the form of an organometallic sheet 3 and a laminate 4 laminated-on on one side, which in the present case is formed as a multi-layer film. The organometallic sheet 3 consists, for example, of a base material/matrix material of HDPE (High-Density Polyethylene) with fibres embedded in it in the form of carbon fibres, glass fibres or aramid fibres. The fibres are embedded in the matrix material in the form of a laid or woven structure. The organometallic sheet 3 may be additionally provided on the visible side/outer side with an HDPE covering layer, which ensures that the fibre reinforcement is completely covered.
The laminate 4 that is provided on the inside of the organometallic sheet 3 comprises two HDPE covering layers 5, two layers of adhesion promoter 6 and an EVOH layer 7 as a barrier layer.
A method for manufacturing the fuel tank according to the invention envisages the provision of a completely made-up and laminated semifinished product in the form illustrated in
At the same time, the shells are formed with a preferably encircling flange 8.
In the region of this flange, the shells, i.e. the upper shell 1 and the lower shell 2, are preferably joined, i.e. connected to one another with a material bond, preferably welded to one another.
The different variants of the peripheral connection of the upper shell 1 and the lower shell 2 are illustrated in
In a first step, the just-formed upper shell 1 and lower shell 2 are placed one on top of the other, as represented in
In principle, however, the upper shell 1 and the lower shell 2 may also have been placed one on top of the other in the cold state. Then, for example, the flange 8 of both shells 1, 2 is heated by means of infrared radiation and softened until they plasticize.
In a next step, for example, the flange 8 of the lower shell 2 is folded over around the flange 8 of the upper shell 1 with a suitable tool (see
This type of connecting technique makes allowance in particular for the fact that the layer thickness of the laminate 4 is at most 1.25 nm, essentially only the covering layers 5 of the laminate 4 contributing to the welding.
An alternative embodiment of the joining operation is represented in
The upper shell 1 and the lower shell 2 have a flange of the same dimensions; the flanges 8 are placed flush one on top of the other for the purpose of connecting the shells. Then, a U-shaped peripheral profile 10 of thermoplastic material, preferably of HDPE, is placed onto the tank seam, reaching around the flanges 8. The peripheral profile 10 is welded to the outer side of the organometallic sheets 3 while applying pressing pressure under heat.
Alternatively, adhesive bonding of the peripheral profile 10 may be provided, for example, with an adhesion promoter on the basis of LDPE.
The method according to the invention comprises the introduction of inserts 11 into the fuel tank before the joining of the upper shell 1 and the lower shell 2. For this purpose, the inserts, for example in the form of valves, nipples, filling-level sensors, surge tanks or the like, are premounted in a predetermined layout of the tank shell concerned on an insert carrier 12 in the form of a lattice support of thermoplastic material. The insert carrier 12 is then placed in the position shown in
The insert carrier 12 is formed, for example, as an injection-moulded plastic carrier, which is adapted to the contour of the upper shell 1 and has, for example, been placed into the upper shell 1. Alternatively, clamping or else welding is possible. The inserts 11, in the present case valves, are connected to one another by way of a relatively stiff venting line 13. One of the inserts 11 is provided with a connection nipple 14, which passes through a lead-through 15 of the upper shell 1.
The lead-through 15 is produced, for example, after completion of the upper shell 1 and before joining of the upper shell 1 to the lower shell 2, by cutting out a circle. Then, the insert carrier 12 is brought into the upper shell 1 in such a way that the connection nipple 14 passes through the lead-through 15. The connection nipple 14 lies, for example, with an encircling collar 16 against the laminate 4. The collar is provided with an annular groove 17, placed in which is an O-ring seal, which seals off the connection nipple 14 from the the lead-through 15.
The connection nipple 14 is also provided with a thread 19, which passes through the lead-through 15. On the outer side of the upper shell 1, the nipple is secured by a nut 20, which engages in the thread 19.
Alternatively, the connection nipple 15 may be latched by a fastening element provided on the outer side of the upper shell 1.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2013 004 931.8 | Mar 2013 | DE | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14779266 | Sep 2015 | US |
| Child | 16000097 | US |