Patent Application
20050118346
1. Field of Invention
The invention relates to a method for manufacturing a glow pin for a ceramic glow plug which is constructed of an inner cylinder and at least one outer layer.
2. Description of Related Art
A glow pin or a glow plug with such a glow pin is known, for example, from U.S. Pat. No. 6,309,859 or German Patent Application DE 100 53 372 A1.
With the shaping methods hitherto conventional for manufacturing such a glow pin, such as dry pressing, injection molding and slip casting, the thin layers necessary for the functionality can only be achieved at great expense. In addition, the shaping process is followed by another cost-intensive sintering process.
The object forming the basis of the invention is thus to provide a method of the type specified initially with which a glow pin can be manufactured cheaply.
This object is solved according to the invention by the fact that the at least one outer layer is formed by thermal spraying.
The at least one outer layer can be an outer layer coaxial to the inner cylinder and/or a layer covering the front face of the inner cylinder.
If the at least one outer layer, especially the coaxial outer layer and/or the layer covering the front face of the inner cylinder, is formed by thermal spraying, the result is a manufacturing method in which simple and cheap shaping and consolidation methods are interlinked.
Especially preferred exemplary embodiments of the method according to the invention are explained in detail subsequently with reference to the accompanying drawings.
The inner cylinder 1 is formed, for example, by uniaxial dry pressing, if necessary with cold-isostatic post-compaction, by extrusion or by powder injection molding. The inner cylinder is then subjected to binder removal and is pre-sintered or compactly sintered in order to give it sufficient strength for the following operations.
After calibrating the diameter and cutting the inner cylinder to length, it is tapered at one end by a machining process or by water jets, and is provided at the other end with a contact hole. These operations can be carried out before the binder removal and pre-sintering or after the binder removal and pre-sintering by white processing using a diamond tool.
The outer layers are then applied by thermal spraying on to the inner cylinder 1.
In a further exemplary embodiment, the conducting inner cylinder 1 and the insulating layer 2 are produced by the shaping method described above and the conductive layer 3 and the layer 5 running perpendicular to the glow pin axis and if necessary, the coaxial layer 4 which is constructed thereon, are thermally sprayed.
Furthermore, it is also possible to produce the conducting inner cylinder 1, the insulating layer 2 and the conductive layer 3 by the shaping method described and to only form the layer 5 running perpendicular to the glow pin axis, and if necessary the coaxial layer 4, by thermal spraying.
The thermal spraying takes place preferably after the pre-sintering or sintering of the components. Especially suitable as thermal spraying methods are atmospheric plasma spraying (APS), vacuum plasma spraying (VPS) and high-velocity flame spraying (HVOF).
In order to avoid thermal stresses during application of the layers, for this purpose, the blank is heated during the spraying. If the surface roughness of the blank is not sufficient for adequate adhesion of the layer to be sprayed on, the surface is roughened mechanically or by another method before the coating. An adhesion promoter can also be sprayed on which can also be used to match the coefficients of thermal expansion of the materials of the inner cylinder 1 and the individual layers 2, 3, 4, 5, one to the other.
In addition, a hardening treatment, e.g., beveling the pin-shaped blank, can take place before spraying. Moreover, as a result of the hardening treatment, a better classification of the individual functional layers can be achieved in order to avoid hot spots.
An insulating layer can also be thermally sprayed onto the outer layer 3 so that this structure makes it possible to use a glow plug with such a ceramic glow pin as an ion current measuring plug.
The electrical functional layers can be thermally sprayed onto a pre-sintered base cylinder wherein, in this case, the final compaction only takes place in a subsequent gas-pressure sintering process.
As shown in
The hard treatment of the glow pin can then take place after the pre-sintering or sintering or after the thermal spraying, for example, by a simple and cheap push-through grinding process, as shown in
Especially suited as the material for the inner cylinder 1 and the layers 2 to 5 are silicide, carbide, nitride or boride materials. Oxides, such as Al2O3 and Y2O3, and in general, oxides of rare-earth metals can be used as sinter additives.
During spraying, the thermal powder can be present both as a pure powder mixture and as already sintered granules. The melt phase required for thermal spraying can be produced by adding fusible semiconductor or metallic components, such as silicon. In a further exemplary embodiment a powder coated with a fusible phase can be used for thermal spraying.