The invention relates to a method for manufacturing a melt launder that comprises a flow channel for molten phase and that is to be used for transferring molten phase such as slag, matte, or metal formed in a process for the production of metals as defined in the preamble of independent claim 1.
The invention also relates to melt launder to be used for transferring molten phase such as slag, matte, or metal formed in a process for the production of metals, wherein the melt launder comprises a launder body of metal, and a flow channel for molten phase as defined in the preamble of independent claim 13.
Melt launder is used for example for transferring molten materials such as metal, matte, or slag from smelters.
Document WO 03/033982 presents a melt launder comprising a bottom and edges, said melt launder being particularly meant to be used for tapping a molten phase, such as slag, from a smelting furnace, which melt launder is manufactured of copper or copper alloy and provided with cooling channels.
Objective of the Invention
The object of the invention is to provide an improved method for manufacturing a melt launder and an improved melt launder.
Short Description of the Invention
The method of the invention is characterized by the definitions of independent claim 1.
Preferred embodiments of the method are defined in the dependent claims 2 to 12.
The melt launder of the invention is correspondingly characterized by the definitions of independent claim 13.
Preferred embodiments of the melt launder are defined in the dependent claims 14 to 24.
The invention is based on lining the launder body of metal with a refractory lining so that the refractory lining at least partly forms a flow surface for molten phase in the flow channel for molten phase and on arranging a layer of steel between the launder body of metal and the refractory lining
In one preferred embodiment the layer of steel has a first face that is in contact with the launder body of metal and an opposite second face that is in contact with the refractory lining
In one preferred embodiment the refractory lining is attached to the layer of steel and the layer of steel is releasable attached to the launder body of metal. Especially this will enable a quick removal of the refractory lining together with the layer of steel from the launder body of metal for example when replacing the refractory lining.
The layer of steel also protects the launder body of metal from direct contact with the transferred molten material i.e. the transferred molten phase.
In the following the invention will be described in more detail by referring to the figures, of which
The invention relates to a method for manufacturing a melt launder 1 to be used for transferring molten phase (not shown in the figures) such as slag, matte, or metal formed in a process (not shown in the figures) for the production of metals.
The invention also relates to a melt launder 1 to be used for transferring molten phase such as slag, matte, or metal formed in a process for the production of metals.
First the method for manufacturing a melt launder 1 that comprises a flow channel 2 for molten phase and that is to be used for transferring molten phase such as slag, matte, or metal formed in a process for the production of metals and some preferred embodiments and variants of the method will be described in greater detail.
The method comprises a providing step for providing a launder body of metal 3.
The method comprises also a lining step for lining the launder body of metal 3 with a refractory lining 4 so that the refractory lining 4 at least partly forms a flow surface 5 for molten phase in the flow channel 2 for molten phase.
The method comprises preferably a lining step for lining the launder body of metal 3 with a refractory lining 4 so that the refractory lining 4 fully forms a flow surface 5 for molten phase in the flow channel 2 for molten phase.
It is obvious to a person skilled in the art that the providing step and that the lining step may be combined to a combined providing and lining step for providing a launder body of metal 3 having a refractory lining 4 so that the refractory lining 4 at least partly forms a flow surface 5 for molten phase in the flow channel 2 for molten phase.
The providing step for providing a launder body of metal 3 may comprise providing a launder body of metal 3 comprising a longitudinal groove (not marked with a reference number) in which the refractory lining 4 is arranged so that the refractory lining 4 at least partly forms a flow surface 5 for molten phase in the flow channel 2 for molten phase.
The providing step for providing a launder body of metal 3 may comprise a step for manufacturing said launder body of metal 3. The launder body of metal 3 can be manufactured in many different ways. One possible way is to manufacture the launder body of metal 3 from a round metal billet through machining Another possible way is to manufacture the launder body of metal 3 through casting. Yet another possible way is to manufacture the launder body of metal 3 by rolling and bending from a billet. The launder body of metal 3 can be manufactured so that it comprises a longitudinal groove in which the refractory lining 4 is arranged so that the refractory lining 4 at least partly forms a flow surface 5 for molten phase in the flow channel 2 for molten phase. The launder body of metal 3 can be manufactured at least partly from copper or copper alloy. The launder body of metal 3 can be manufactured from copper or copper alloy.
The refractory lining 4 can for example comprise graphite or be of graphite, and/or comprise carbon-based refractory material such as carbon, semi-graphite, silicon carbide and/or comprises insulating refractory material and/or zirconium-oxide.
The method comprises an arranging step for arranging a layer of steel 6 between the launder body of metal 3 and the refractory lining 4.
In one embodiment of the method the arranging step includes arranging a layer of steel 6 between the launder body of metal 3 and the refractory lining 4 such that the layer of steel 6 has a first face 7 that is in contact with the launder body of metal 3 and an opposite second face 8 that is in contact with the refractory lining 4.
The arranging step may include using a steel sheet such as a stainless steel sheet in the layer of steel 6.
The arranging step may include using a steel sheet such as a stainless steel sheet as the layer of steel 6. The arranging step for arranging a layer of steel 6 between the launder body of metal 3 and the refractory lining 4 may include a coating step for at least partly coating the launder body of metal 3 with a layer of steel 6 so that a layer of steel 6 that is in the form of a coating of steel on the launder body of metal 3 is arranged between the launder body of metal 3 and the refractory lining 4.
The coating step may include explosion welding a layer of steel 6 such as a steel sheet to the launder body of metal 3 to form said layer of steel 6 that is in the form of a coating of steel on the launder body of metal 3.
The arranging step for arranging a layer of steel 6 between the launder body of metal 3 and the refractory lining 4 may include a coating step for at least partly coating the refractory lining 4 with a layer of steel 6 so that a layer of steel 6 that is in the form of a coating of steel on the refractory lining 4 is arranged between the launder body of metal 3 and the refractory lining 4. The coating step may include explosion welding a layer of steel 6 such as a steel sheet to the refractory lining 4 to form said layer of steel 6 that is in the form of a coating of steel on the refractory lining 4. The arranging step for arranging a layer of steel 6 between the launder body of metal 3 and the refractory lining 4 a combination of the embodiments described above; using a steel sheet in the layer of steel 6, at least partly coating the launder body of metal 3 with a layer of steel 6, and at least partly coating the refractory lining 4 with a layer of steel 6.
The providing step may include providing such a launder body of metal 3 that is provided with cooling channels 9 for circulating cooling medium in the launder body of metal 3. Alternatively, the providing step may include a step for equipping such a launder body of metal 3 with cooling channels 9 for circulating cooling medium in the launder body of metal 3.
The providing step may include providing such a launder body of metal 3 that is at least partly made of copper.
The method may comprise attaching the refractory lining 4 to the layer of steel 6. Especially this will enable a quick removal of the refractory lining 4 together with the layer of to steel 6 from the launder body of metal 3 for example when replacing the refractory lining 4.
The method may comprise releasable attaching the layer of steel 6 to the launder body of metal 3.
The method may comprise providing the layer of steel 6 and the launder body of metal 3 with co-operating fasteners 10 for releasable attaching the layer of steel 6 to the launder body of metal 3.
The method may include providing the layer of steel 6 with lifting means 11 for lifting the layer of steel 6 from the launder body of metal 3 to detach the layer of steel 6 to the launder body of metal 3.
The method may include providing the melt launder 1 with a lid 12, which may be removable and/or openable. The lid 12 may comprise several lid sections (not marked with a reference numeral). In
Next the melt launder 1 to be used for transferring molten phase such as slag, matte, or metal formed in a process for the production of metals and some preferred embodiments and variants of the melt launder 1 will be described in greater detail.
The melt launder 1 comprises a launder body of metal 3.
The melt launder 1 comprises a flow channel 2 for molten phase.
The launder body of metal 3 is provided with a refractory lining 4 so that the refractory lining 4 at least partly forms a flow surface 5 for molten phase in the flow channel 2 for molten phase.
The refractory lining 4 can for example comprise graphite or be of graphite, and/or comprise carbon-based refractory material such as carbon, semi-graphite, silicon carbide and/or comprises insulating refractory material and/or zirconium-oxide.
The launder body of metal 3 may comprise a longitudinal groove in which the refractory lining 4 is arranged to form the flow channel 2 for molten phase.
The melt launder 1 comprises a layer of steel 6 between the launder body of metal 3 and the refractory lining 4.
In one embodiment of the melt launder 1 the layer of steel 6 is arranged between the launder body of metal 3 and the refractory lining 4 such that the layer of steel 6 has a first face 7 that is in contact with the launder body of metal 3 and an opposite second face 8 that is in contact with the refractory lining 4.
The layer of steel 6 may include a steel sheet such as a stainless steel sheet.
The layer of steel 6 may be a steel sheet such as a stainless steel sheet.
The launder body of metal 3 may be at least partly coated with a layer of steel 6 so that a layer of steel 6 that is in the form of a coating of steel on the launder body of metal 3 is provided between the launder body of metal 3 and the refractory lining 4. The layer of steel 6 that is in the form of a coating of steel on the launder body of metal 3 may be explosion welded to the launder body of metal 3. The refractory lining 4 may be at least partly coated with a layer of steel 6 so that a layer of steel 6 that is in the form of a coating of steel on the refractory lining 4 is provided between the launder body of metal 3 and the refractory lining 4. The layer of steel 6 that is in the form of a coating of steel on the refractory lining 4 may be explosion welded to the refractory lining 4.
The melt launder 1 may be provided with layers of steel 6 formed by a combination of the embodiments described above; a steel sheet in the layer of steel 6, a layer of steel 6 in the form of a coating of steel at least partly coating the launder body of metal 3, and a layer of steel 6 in the form of a coating of steel at least partly coating the refractory lining 4.
The launder body of metal 3 may be provided with cooling channels 9 for circulating cooling medium in the launder body of metal 3.
The launder body of metal 3 may be at least partly made of copper or copper alloy.
The launder body of metal 3 can be manufactured from copper or copper alloy.
The refractory lining 4 may be attached to the layer of steel 6.
The layer of steel 6 may be releasable attached to the launder body of metal 3.
The layer of steel 6 and the launder body of metal 3 may be provided with co-operating fasteners 10 for releasable attaching the layer of steel 6 to the launder body of metal 3.
The layer of steel 6 being may be provided with lifting means 11 for lifting the layer of steel 6 from the launder body of metal 3 to detach the layer of steel 6 from the launder body of metal 3.
The melt launder 1 may be provided with a lid 12, which may be removable and/or openable. The lid 13 may comprise several lid sections (not marked with a reference numeral). In
It is apparent to a person skilled in the art that as technology advances, the basic idea of the invention can be implemented in various ways. The invention and its embodiments are therefore not restricted to the above examples, but they may vary within the scope of the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20125140 | Feb 2012 | FI | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FI13/50143 | 2/8/2013 | WO | 00 |