Patent Application
20210008609
The present invention relates to a method for manufacturing a press-molded article, a retainer, and a manufacturing system for a press-molded article.
Patent document 1 describes heating and annealing a portion of a hot stamped article with a laser. Patent document 2 describes a method for manufacturing a component having a rigid zone and a soft zone by sandwiching and deforming a heated blank with a die assembly and cooling a first portion of the blank while heating a second portion of the blank with an infrared lamp.
Patent document 1: International Publication No. WO2016/088665
Patent document 2: International Publication No. WO2017/190220
Hereinafter, the invention will be described through embodiments of the invention, but the following embodiments do not limit the invention according to the claims. In addition, not all combinations of the features described in the embodiments are necessarily essential to the solution of the invention.
At the hot stamping step, the heated blank material 10 is cooled until martensitic transformation occurs, while being press-molded using the die 200.
The die 200 includes an upper die 202 having a molding surface 203 and a lower die 204 having a molding surface 205. The molding surface 203 is an example of a first molding surface. The molding surface 205 is an example of a second molding surface. The die 200 has a flow path 206 for delivering a coolant, such as water, to cool the blank material 10, along the molding surface 203 and the molding surface 205. The heated blank material 10 is sandwiched between the molding surface 203 and the molding surface 205 to be press-molded into a predetermined shape. While being press-molded, the blank material 10 is cooled by the coolant delivered through the flow path 206 with the blank material 10 sandwiched between the molding surface 203 and the molding surface 205. The blank material 10 is molded into a press-molded article 12 by the above-mentioned hot stamping step. The press-molded article 12 has strength of 1.2 GPa to 1.8 GPa, for example.
Then, at the tempering step or the annealing step, the press-molded article 12 removed from the die 200 is set into a retainer 300 and a predetermined portion 14 of the press-molded article 12 is irradiated with infrared light. In this way, the predetermined portion 14 is softened. That is, the predetermined portion 14 of the press-molded article 12 is subject to tempering or annealing, by irradiating the predetermined portion 14 of the press-molded article 12 with infrared light.
The retainer 300 includes an upper die 301 having a retaining surface 303 along the shape of one surface of the press-molded article 12, and a lower die 302 having a retaining surface 304 along the shape of the other surface on the opposite side of said one surface of the press-molded article 12. The retainer 300 has a flow path 305 for delivering a coolant, such as water, to cool the press-molded article 12, along the retaining surface 303 and the retaining surface 304. The retainer 300 has a recess 306 and a recess 308 in regions of the retaining surface 303 and the retaining surface 304 opposed to the portion 14 of the press-molded article 12. The recess 306 and the recess 308 are examples of a first recess and a second recess. The recess 306 and the recess 308 may be grooves provided on the retaining surface 303 and the retaining surface 304. Note that, the retainer 300 may not have the flow path 305.
An infrared heater 307 for irradiating the portion 14 of the press-molded article 12 with infrared light is provided in the recess 306 of the upper die 301. The infrared heater 307 is an example of a first infrared irradiating unit. The infrared heater 307 may irradiate the portion 14 of the press-molded article 12 with near-infrared light. The retainer 300 may have an infrared lamp instead of the infrared heater. The retainer 300 may have a plurality of infrared heaters disposed along the portion 14. The retainer 300 may have a plurality of infrared lamps arranged along the portion 14. The near-infrared light may be electromagnetic waves with a wavelength of 0.7 to 2.5 micrometers. The width of the recess 308 may be a width corresponding to the width of the portion 14. The recess 308 may function as a shielding wall for shielding infrared light to prevent portions other than the portion 14 of the press-molded article 12 from being irradiated with the infrared light irradiated from the infrared heater 307. In addition, by providing the recess 308, the air inside the recess 308 functions as a heat insulation layer to suppress heat radiation through the lower die 302 of the heat in the portion 14 of the press-molded article 12 heated by the infrared light from the infrared heater 307.
The retainer 300 may also have an infrared heater in the recess 308 to heat the portion 14 of the press-molded article 12 from both sides. The infrared heater provided in the recess 308 is an example of a second infrared irradiating unit.
For example, the press-molded article 12 is an automobile frame component or the like. The automobile frame component may be softened by partially reducing its strength. In this way, in case of a motor vehicle collision, the softened portion can deform and absorb the collision energy. By partially softening the press-molded article 12 as described above, the safety of passengers on the motor vehicle can be ensured.
The wavelength range of the infrared light irradiated by the infrared heater 307 is wider than the wavelength range of a laser light irradiated by a laser as in Patent document 1. Therefore, the portion 14 to be softened of the press-molded article 12 can be irradiated with light having various wavelengths. As such, the absorption of light with which the portion 14 of the press-molded article 12 is irradiated can be facilitated. That is, the portion 14 of the press-molded article 12 can be efficiently heated and softened. The laser light is irradiated locally. On the other hand, infrared light irradiated by the infrared heater 307 is irradiated over a wide range. Therefore, the productivity of softening process of the portion 14 of the press-molded article 12 can be improved.
In addition, the portion 14 is heated by irradiating with infrared light from the infrared heater 307, with the press-molded article 12 sandwiched between the retaining surface 303 of the upper die 301 and the retaining surface 304 of the lower die 302. In this way, the portion 14 of the press-molded article 12 can be accurately softened while suppressing deformation of the press-molded article 12. Deformation of the press-molded article 12 can be further suppressed and the portion 14 of the press-molded article 12 can be more accurately softened by heating the portion 14 by irradiating the portion 14 with infrared light from the infrared heater 307 while cooling portions other than the portion 14 to be softened of the press-molded article 12, with the press-molded article 12 sandwiched between the retaining surface 303 of the upper die 301 and the retaining surface 304 of the lower die 302.
Deformation due to heat by infrared irradiation can be more certainly suppressed by irradiating the entire press-molded article 12 with infrared light, with the entire press-molded article sandwiched between the retaining surface 303 of the upper die 301 and the retaining surface 304 of the lower die 302.
Moreover, portions other than the portion 14 of the press-molded article 12 is cooled by a coolant delivered through the flow path 305, while the portion 14 of the press-molded article 12 is irradiated with infrared light. In this way, the transition width of the hardness at a boundary portion between the portion 14 to be softened and other portions whose hardness are to be maintained may be narrowed.
Note that, in the present embodiment, an example is shown in which the entire portion other than the portion 14 of the press-molded article 12 is cooled. However, instead of the entire portion other than the portion 14 of the press-molded article 12, only portions around the portion 14 of the press-molded article 12 may be cooled. In addition, the press-molded article 12 may not be cooled while being irradiated with infrared light.
In addition, as described in Patent document 2, when infrared light is irradiated at the hot stamping step, portions that can be irradiated with infrared light is limited to flat portions that are not deformed by press-molding. That is, when infrared light is irradiated at the hot stamping step, the portions deformed by press-molding cannot be softened. In addition, when a steel plate heated to a temperature in an austenite region or higher is rapidly cooled and partially heated at the same time, the position of the portion to be softened shifts by the amount of contraction of the steel plate upon rapid cooling. Due to such shift in the position, the stability of the shape of the press-molded article becomes lower, and the transition width of the hardness at the boundary portion between the portion to be softened and the portion not to be softened becomes wider.
As described above, according to the present embodiment, regions of any size at any location of the press-molded article can be efficiently softened.
The infrared heater 407 and the infrared heater 409 can be deformed into any shape and disposed. Therefore, as shown in
The infrared heater 507 and the infrared heater 509 can be disposed at any place on the retaining surface 503 and the retaining surface 504. For example, as shown in
As described above, according to the present embodiment, regions of any size at any location of the press-molded article 12 can be further efficiently softened with infrared light, at the tempering step or the annealing step after the press-molding step.
Note that, in the above-mentioned embodiment, an example has been described in which a region of any size at any location of the press-molded article 12 is irradiated with infrared light at the tempering step or the annealing step after the hot stamping step. However, the press-molded article to be tempered or annealed with infrared irradiation is not limited to a press-molded article formed by hot stamping. For example, the press-molded article to be tempered or annealed with infrared irradiation may be a press-molded article formed by cold-pressing a steel material such as a high strength material.
While the embodiments of the present invention have been described, the technical scope of the invention is not limited to the above described embodiments. It is apparent to persons skilled in the art that various alterations and improvements can be added to the above-described embodiments. It is also apparent from the scope of the claims that the embodiments added with such alterations or improvements can be included in the technical scope of the invention.
The operations, procedures, steps, and stages of each process performed by an apparatus, system, program, and method shown in the claims, embodiments, or diagrams can be performed in any order as long as the order is not indicated by “prior to,” “before,” or the like and as long as the output from a previous process is not used in a later process. Even if the process flow is described using phrases such as “first” or “next” in the claims, embodiments, or diagrams, it does not necessarily mean that the process must be performed in this order.
10: blank material, 12: press-molded article, 100: heating furnace, 200: die, 202: upper die, 203, 205: molding surface, 204: lower die, 206: flow path, 300, 400, 500: retainer, 301, 401, 501: upper die, 302, 402, 502: lower die, 303, 304, 403, 404, 503, 504: retaining surface, 305, 405, 505: flow path, 306, 308, 406, 408, 506, 508: recess, 307, 407, 409, 509: infrared heater
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-191744 | Oct 2018 | JP | national |
The contents of the following Japanese patent applications are incorporated herein by reference: No. 2018-191744 filed in JP on Oct. 10, 2018 and No. PCT/JP2018/040534 filed on Oct. 31, 2018.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2018/040534 | Oct 2018 | US |
| Child | 17037758 | US |