This application claims the priority, under 35 U.S.C. §119, of German Patent Application DE 10 2013 009 462.3, filed Jun. 6, 2013; the prior application is herewith incorporated by reference in its entirety.
The invention relates to a method for manufacturing a screen structure having at least two mesh layers. The invention also relates to a screen structure, in particular for screen printing, including at least two mesh layers disposed substantially parallel to each other, in particular a screen structure manufactured in accordance with the methods of the invention.
Industrial applications for screens or fabrics are known from many fields. In applications in the field of filtering, a square mesh is the most usual configuration. That mesh configuration has been adopted by the printing industry. With the available photosensitive layers and the known application processes, a reasonable image resolution may only be achieved if a large number of “supports” is provided. Thus, high mesh-count mesh types are becoming more and more widely used.
For printed electronics, screens that are as thin as possible and meshes made of the thinnest possible wire are used to ensure that pastes may pass smoothly and to allow the creation of fine-lined images.
In the field of solar cell coating, a high application of paste and a precise, fine resolution is required, for example to apply PCB tracks as current lines without covering too much of the solar cells to ensure a high degree of efficiency of the solar cells.
The screens or types of mesh used to print electronics are very expensive and delicate to process, i.e. they are not suitable for the production of screen printing plates for rotary screen printing. Their inadequacy is also due to the fact that for a rotary screen, the screen meshes may only be tensioned in one direction, i.e. the direction of the longitudinal axis of the cylinder, whereas in flat-bed screen printing, they may be tensioned in two dimensions.
In rotary screen printing, the ink is transported through the screen due to the hydrodynamic pressure generated in front of the doctor blade by the rotation of the screen and the engagement of the doctor blade. For structural reasons, only open or semi-open blade systems may be used, causing the dynamic pressure to be influenced by many variables such as viscosity, fill level, and rotary speed. Simple ways of increasing the hydrodynamic pressure are increasing the rotary speed or the fill level. Such a screen printing unit is described in International Publication No. WO 99/19146A1, corresponding to U.S. Pat. No. 6,412,407, for instance.
In the prior art, the basic structure for screen materials is plain-weave stainless steel mesh. The ratio between screen opening, surface of contact, and mesh thickness has proved to be suitable. The thickness of the structure, i.e. the mesh thickness (initial dimension prior to calendaring), approximately corresponds to twice the wire thickness. In a further step, the basic structure is calendared to achieve the desired raw mesh thickness. That also achieves a higher degree of smoothness of the screen and thus a lower degree of wear to the screen and to the doctor blade. In the subsequent nickel-plating process, the mesh is reinforced to make it more resistant to wear and the points of support in the region of the intersections are enlarged. A process for creating such screen materials is described, for example, in European Patent Application EP 0 182 195 A2, corresponding to U.S. Pat. No. 4,705,608.
It is also known to use non-woven metal webs, synthetic mesh, perforated metal plates, metal films, and combinations thereof as alternatives.
In general, a close-mesh screen structure that has many points of support is selected to ensure the stability of the screen material. A disadvantage is that the theoretical ink application volume, which is defined by the thickness of the mesh and the percentage of open area of the screen structure, is very limited. Thus, that technology has its limits, in particular if high lines of low width are to be printed as is the case, for example, in the manufacture of solar cells.
It is accordingly an object of the invention to provide a method for manufacturing a screen structure and a screen structure for screen printing, which overcome the hereinafore-mentioned disadvantages of the heretofore-known methods and structures of this general type and in which the screen structure has a particularly high degree of stability. A further object is to provide a screen structure and a method for manufacturing such a screen structure wherein the screen structure has a greater ink application volume if used in screen printing.
With the foregoing and other objects in view there is provided, in accordance with the invention, a method for manufacturing a screen structure having at least two mesh layers, comprising the steps of providing a first mesh layer on a first reel and a second mesh layer on a second reel, bringing the first and second mesh layers together so that they contact each other, and jointly metalizing the first and second mesh layers with the applied metal firmly bonding the two mesh layers together to create a composite mesh.
The method of the invention is used to manufacture a screen structure that has at least two screen-like mesh layers. A first web-shaped mesh layer is provided on a first reel, and a second web-shaped mesh layer is provided on a second reel. In the context of the present invention, a mesh layer is understood to be a two-dimensional structure, including but not limited to a woven surface structure, perforated metal plates, non-woven webs, and electroformed stencils and films. In accordance with the invention, the first and second mesh layers are brought together, in particular by deflection rollers, in such a way that the first and second mesh layers contact each other. Advantageously, the first and second mesh layers are jointly metalized in such a way that the applied metal firmly bonds the two mesh layers to each other to create a composite mesh. A third mesh layer or further mesh layers may be bonded in the same way to create an even thicker composite mesh.
In accordance with another advantageous mode of the method of the invention, the composite mesh is then rinsed and dried and, if desired, if the screen structure is to be used for screen printing, a photosensitive layer or a locally removable polymeric layer is applied before the composite mesh is wound onto a third reel.
In accordance with a further advantageous mode of the method of the invention, in a first alternative, the metalizing that causes the two mesh layers to bond is a chemical metalizing process involving electroless metal deposition, i.e. so-called reductive metal deposition.
In accordance with an added particularly preferred mode of the method of the invention, in a second alternative, the metalizing that causes the two mesh layers to bond is an electrochemical electroplating process carried out, in particular, in a nickel bath.
As an alternative to the nickel bath, a copper bath or a tin bath may be used. The bath may contain a combination of various metals, e.g. nickel and silver.
With the objects of the invention in view, there is also provided a screen structure, in particular a screen structure suited for screen printing, comprising at least two screen-like mesh layers disposed to be substantially parallel to each other, the screen structure, in particular, being created in accordance with the process described above. In accordance with the invention, the mesh layers are provided with a metal layer applied in an electroplating process and the mesh layers are bonded to each other by this metal layer. In accordance with a preferred embodiment, the metal layer is mainly formed of nickel. Alternatively, other metals such as copper or tin may be used. A combination of various metals may be used, e.g. nickel and silver. An alternative field of use for the screen structure is filtration.
In accordance with another advantageous feature of the invention, a respective mesh layer is a steel mesh of thin wires. Such a steel mesh has a high degree of stability and firmness and is particularly easy to electroplate in an electrochemical process. Alternatively, a pre-treated synthetic mesh that has been made conductive, for example a polyester mesh, may be used. The respective mesh layers may be made of different mesh types. The mesh type is understood to be defined by the shape of the mesh, e.g. square mesh or longitudinal mesh, and the type of binding. The mesh type is to be selected as a function of the desired use of the screen structure.
With the objects of the invention in view, there is furthermore provided a method for manufacturing a screen structure that has at least two mesh layers, which comprises providing a first mesh layer on a first reel and a second mesh layer on a second reel and providing the first and/or second mesh layers with an emulsion for bonding the two mesh layers together. The first and second mesh layers are then brought together by deflection rollers to contact each other or to be spaced apart by only a small distance and to be bonded by the emulsion, resulting in a composite mesh. The emulsion may, in particular, be a photosensitive layer or a hot melt adhesive. The emulsion may easily be treated by laser.
With the objects of the invention in view, there is concomitantly provided a screen structure, in particular for screen printing, comprising at least two mesh layers disposed to be substantially parallel to each other and, in particular, manufactured in accordance with one of the methods described above, wherein in accordance with the invention the mesh layers are laminated to form a composite.
An advantage of the screen structures of the invention is that they have a high ink application volume, allowing a high printed line height to line width ratio. Another advantage is that the screen structures have a high degree of stability, ensuring in-register printing of fine lines and increasing the useful life of the screen structures.
Any combination of the invention described above and of the advantageous further developments of the invention above likewise represents an advantageous further development of the invention. The dependent claims and the description of exemplary embodiments with reference to the appended figures provide further advantages and embodiments of the invention that are advantageous in structural and functional terms.
Other features which are considered as characteristic for the invention are set forth in the appended claims.
Although the invention is illustrated and described herein as embodied in a method for manufacturing a screen structure and a screen structure for screen printing, it is nevertheless not intended to be limited to the details shown, since various modifications and structural changes may be made therein without departing from the spirit of the invention and within the scope and range of equivalents of the claims.
The construction and method of operation of the invention, however, together with additional objects and advantages thereof will be best understood from the following description of specific embodiments when read in connection with the accompanying drawings.
Referring now in detail to the figures of the drawings which are not drawn to scale but in which like elements and components are indicated by like reference symbols and first, particularly, to
Such screen materials 10 are used in rotary screen printing.
In a non-illustrated alternative embodiment, the first mesh layer 11 and the second mesh layer 12 may be separately provided with a metal layer 15 in advance in a previous step. The mesh layers 11, 12 that have been metalized in this way may then be bonded to each other in the manner described above by an additional metal layer 15. In other words, the respective mesh layers are electroplated in a first step as is known in the art. Subsequently, the electroplated mesh layers are bonded to each other in accordance with the invention.