The present invention relates to a method for manufacturing a tyre having reinforced tread pattern blocks making it possible to limit the rocking of the tread pattern blocks.
The incorporation of a reinforcer during the production of a tread in a centralized manufacturing process is not economically conceivable, since, during the assembly of these composite semifinished products, scrap that is produced is not recyclable, meaning that it results in losses of material that cannot be reused.
The aim of the invention is to propose a method for manufacturing a recyclable tread that makes it possible to obtain a tyre having reinforced tread pattern blocks.
To this end, the invention relates to a method for manufacturing a tread based on uncured rubber material, characterized in that it has the following steps of:
Advantageously according to the invention, the method makes it possible to form a tread made of uncured rubber material, the scrap of which can be recycled. The method can also be implemented separately or directly on a green form, for example on a carcass, of tyre. The tread can thus be reinforced and mounted on the green form of the tyre before the whole is crosslinked.
Advantageously according to the invention, each tread pattern block is created from several portions made of uncured rubber material that may or may not be in one piece. The geometry of the central portion makes it advantageously possible to choose the angle that the reinforcing ply makes with respect to the contact surface of the tread. The orientation of the reinforcing ply against the central portion is maintained by covering the lateral portion. The latter therefore forms the part of the tyre that is intended to be in contact with the ground. It will also be understood that the reinforcing play can thus be of very different kinds.
The invention may also have one or more of the following optional features, on their own or in combination.
Each central portion and the associated lateral portion(s) thereof are connected by a base, thereby making it possible to ensure a geometry between the portions.
The central portion may have has a prismatic shape with a polygonal base, at least one face of which is intended to receive the reinforcing ply, thereby making it advantageously possible to choose an angle, between the reinforcing ply and the contact surface of the tread, that is substantially constant.
The central portion has a prismatic shape with a triangular base, two adjacent faces of which are intended to receive the reinforcing ply, thereby making it possible to position a reinforcing ply for example in a manner entirely covering the upper surface of the central portion. It will be understood that it is thus possible to obtain a reinforcing ply profiled element with a chevron-shaped cross section, the apex of which is oriented towards the contact surface of the tread.
Each lateral portion has a prismatic shape with a polygonal base, at least one face of which is used to cover a part of the central portion, making it possible to coincide with at least one face of the central portion. The prismatic shape also makes it possible to form the external shape of the tread pattern blocks of the green form of the tread.
Advantageously according to the invention, the green form of tread may have a plurality of tread pattern blocks. It may also be in one piece, thereby making it possible to ensure its geometry and to easily mount it on the green form of the tyre.
The step of forming the green form of tread may be carried out by extrusion in order to provide a profiled element with the desired cross section for all or part of the green form of the tread with the necessary length for the tyre to be manufactured.
The method may also have a final rolling step for improving the adhesion of the lateral portion(s) to its (their) associated central portion.
Moreover, the invention relates to a method for manufacturing a tyre, characterized in that it has a step of manufacturing the tread that is carried out using the manufacturing method as set out above.
The method for manufacturing the tyre therefore makes it possible to produce a green form of tread with at least one reinforced tread pattern block that can be integrated with conventional tyre manufacturing steps, that is to say without any particular adaptation.
Further particular features and advantages will become clearly apparent from the following description thereof, which is given by way of entirely non-limiting example, with reference to the appended drawings, in which:
In the various figures, the elements that are identical or similar bear the same references, possibly supplemented by a suffix. The description of their structure and of their function is therefore not systematically repeated.
In
A “rubber material”, or “rubber”, means a material based on a crosslinkable composition comprising an elastomer, for example a diene elastomer. Such a material is referred to as “uncured rubber material” or “uncured rubber” before crosslinking.
The term “carcass” means any part that does not belong to the tread.
A “tread” means a quantity of rubber material delimited by lateral surfaces and by two main surfaces, one of which, referred to as the tread surface, is intended to come into contact with a road surface when the tyre is being driven on.
The aim of the invention is to propose a method for manufacturing a recyclable tread that makes it possible to obtain a tyre having reinforced tread pattern blocks.
The invention is applicable to any type of tyre, in particular those intended to be fitted on motor vehicles of the passenger or SUV (“Sport Utility Vehicle”) type, two-wheel vehicles (in particular motorcycles), aircraft, industrial vehicles selected from vans, heavy transport vehicles, i.e. light rail vehicles, buses, heavy road transport vehicles (lorries, tractors and trailers), and off-road vehicles such as agricultural or construction plant vehicles, or other transport or handling vehicles. The invention is also applicable to non-motorized vehicles, in particular a trailer, a semi-trailer or a caravan.
The manufacturing method according to the invention makes it possible to obtain a tyre 1, in which the tread pattern 2 blocks 3 of the tread 5 (parts between the circumferential grooves 6 of the tyre 1) are stiffened, as illustrated in
More specifically, in the example illustrated in
Thus, for the block 3c through which the plane PE passes, the first 7a and second 7b reinforcing plies are symmetric with respect to the equatorial plane PE, start substantially from the bottom of the adjacent groove 6 (a thickness of rubber material is visible in
This tyre 1 is obtained by virtue of a first embodiment of the method according to the invention. More specifically, the invention relates to a method for manufacturing a tread 5 based on uncured rubber material and to a method for manufacturing a tyre 1 using the method for manufacturing a tread 5.
According to the first embodiment, the method for manufacturing the tread 5 has a first step intended for forming a green form 9 of tread 5 based on uncured rubber material. The green form 9 has at least one separated tread pattern 2 block 3, that is to say one that is divided into a plurality of portions 11, 12. Preferably, each tread pattern 2 block 3 has a central portion 11 and first 12a and second 12b lateral portions. In the example illustrated in
It will therefore be understood, in the first embodiment, that there is as much lateral portion as there is reinforcing ply to be embedded in the associated tread pattern 2 block 3. By way of entirely non-limiting example, if, in a variant, a single reinforcing ply 7 oriented obliquely were desired in at least one tread pattern 2 block 3, this would entail a step of forming a green form 9 of tread 5 with a central portion 11 and a single lateral portion 12.
For each tread pattern 2 block 3, the profile can thus have a central portion 11 having a prismatic shape with a polygonal base. In the example in
Thus, rather than having rectilinear sections, as illustrated in
By way of entirely non-limiting example, each central portion 11 and each associated lateral portion 12 can be connected by a common base 10, thereby making it possible to ensure the geometry between the portions 11, 12 and, more generally, of the green form 9 of the tread 5.
Preferably, each lateral portion 12, 12a, 12b has a prismatic shape with a polygonal base. In addition, at least one face 14, 14a, 14b of the polygon is used to cover at least a part of the central portion 11 making it possible to coincide with at least the region of the central portion 11 that will be covered by the reinforcing ply 7, 7a, 7b. The prismatic shape also makes it possible to form the external geometry of the tread pattern 2 blocks 3 of the green form 9 of the tread 5. Specifically, the faces that do not cover the central portion 11 are intended to form all or part of the outer envelope of the tread pattern 2 blocks 3.
In the particular example of
As illustrated in
Specifically, the step of forming the green form 9 of tread 5 can be carried out for example by extrusion. It is thus possible to manufacture a profiled element having the desired cross section for all or part of the green form 9 of the tread 5 with the necessary length for the tyre 1 to be manufactured.
The method according to the first embodiment of the invention has a second step intended for mounting at least one reinforcing ply 7, 7a, 7b on at least a part 13, 13a, 13b of the central portion 11. An example of such a step is illustrated in
The method according to the first embodiment of the invention then has a third step intended for covering the central part 11 with the aid of the first and second lateral portions 12, 12a, 12b. This third step makes it possible to form the tread 5 with at least one tread pattern 2 block 3 that envelops a reinforcing ply 7, 7a, 7b. Specifically, each lateral portion 12, 12a, 12b turned down on its central portion 11 makes it possible to form a tread pattern 2 block 3 bordered by a groove 6 on either side of its length, the bottom of which is formed from the void 15 before the covering step.
In the particular example in
The method may also have a final rolling step. This final step could thus make it possible to improve the adhesion of the lateral portions 12, 12a, 12b to their associated central portion 11 and, incidentally, of the reinforcing ply 7, 7a, 7b against these lateral portions.
In the particular example in
Advantageously according to the invention, the method therefore makes it possible to form a tread 5 made of uncured rubber material, the scrap of which can be recycled. The method can also be implemented separately or directly on a green form, for example on a carcass (not shown), of tyre 1. The tread 5 can thus be reinforced and mounted on the green form of the tyre 1 before the whole is crosslinked.
Advantageously according to the invention, each tread pattern 2 block 3 is created from several portions made of uncured rubber material that may or may not be in one piece. The geometry of the central portion 11 makes it advantageously possible to choose the angle that the reinforcing ply 7, 7a, 7b makes with respect to the contact surface of the tread 5. The orientation of the reinforcing ply 7, 7a, 7b against the central portion 11 is maintained by covering the first and second lateral portions 12, 12a, 12b. The latter therefore form the part of the tyre 1 that is intended to be in contact with the ground. It will also be understood that the reinforcing ply 7, 7a, 7b can thus, advantageously according to the invention, be of very different kinds, for example based on fibres based on polymers or on metal-based thread.
The invention also relates to a method for manufacturing a tyre 1 using the method for manufacturing a tread 5 based on uncured rubber material according to the first embodiment as set out above.
By way of entirely non-limiting example, the method for manufacturing a tyre could have the following steps of:
The method for manufacturing the tyre 1 therefore makes it possible to produce a green form 9 of tread 5 with at least one reinforced tread pattern 2 block 3 that can be integrated with conventional tyre 1 manufacturing steps, that is to say without any particular adaptation.
According to a variant of the first embodiment, the step of forming the green form 9 is adapted so as to modify the geometry of the green form 9 of tread 5. Thus, each tread pattern 2 block 3 has a central portion 11 similar to the one explained above. By contrast, as can be seen in
According to the variant of the first embodiment, the method for manufacturing the tread 5 then has second and third steps and, optionally the final step, with the same effects and advantages as the first embodiment.
The manufacturing method according to the variant of the first embodiment of the invention makes it possible to obtain a tyre 1, in which the tread pattern 2 blocks 3 of the tread 5 (parts between the circumferential grooves 6 of the tyre 1) are stiffened, as illustrated in
More specifically, in the example illustrated in
Thus, for the block 3c through which the plane PE passes, the first 7a and second 7b reinforcing plies are symmetric with respect to the equatorial plane PE, start substantially from the bottom of the adjacent groove 6 (a thickness of rubber material is visible in
It will be understood that this configuration, advantageously according to the invention, makes it possible to limit the rocking of the tread pattern 2 blocks 3 when the tyre 1 is loaded, while having a wearing thickness exhibiting only rubber material, that is to say in particular without a reinforcing ply 7, 7a, 7b. It is therefore inferred that the extensions 16a, 16b make it possible to add a thickness of rubber material above the reinforcing plies 7, 7a, 7b.
According to a second embodiment, the method for manufacturing the tread 5 has a first step intended for forming a green form 9 of tread 5 based on uncured rubber material, with the same effects and advantages as the first embodiment. However, the geometry of the green form 9 of tread 5 differs in order to obtain a different type of tread pattern 2 block 3.
The green form 9 has at least one separated tread pattern 2 block 3, that is to say one that is divided into a plurality of portions 11, 12. Preferably, each tread pattern 2 block 3 has a central portion 11 and first 12a and second 12b lateral portions. In the example illustrated in
For each tread pattern 2 block 3, the profile can thus have a central portion 11 having a prismatic shape with a polygonal base. In the example in
It will therefore be understood that the geometry of each receiving face 13a, 13b makes it possible to choose the orientation and the curve that the reinforcing ply 7 will have in the thickness of the tread pattern 2 block 3.
Thus, rather than having rectilinear sections, as illustrated in
By way of entirely non-limiting example, each central portion 11 and each associated lateral portion 12 can be connected by a common base 10, thereby making it possible to ensure the geometry between the portions 11, 12 and, more generally, of the green form 9 of tread 5.
Preferably, each lateral portion 12, 12a, 12b has a prismatic shape with a polygonal base. In addition, at least one face 14, 14a, 14b of the polygon is used to cover at least a part of the central portion 11 making it possible to coincide with at least the region of the central portion 11 that will be covered by the reinforcing ply 7. Moreover, as can be seen in
The prismatic shape also makes it possible to form the external geometry of the tread pattern 2 blocks 3 of the green form 9 of the tread 5. Specifically, the faces that do not cover the central portion 11 are intended to form all or part of the outer envelope of the tread pattern 2 blocks 3.
In the particular example of
As illustrated in
Specifically, the step of forming the green form 9 of tread 5 can be carried out for example by extrusion. It is thus possible to manufacture a profiled element having the desired cross section for all or part of the green form 9 of the tread 5 with the necessary length for the tyre 1 to be manufactured.
The method according to the second embodiment of the invention has a second step intended for mounting at least one reinforcing ply 7 on at least a part 13, 13a, 13b of the central portion 11, with the same effects and advantages as the second step of the first embodiment. The method then has a third step intended for covering the central part 11 with the aid of the first and second lateral portions 12, 12a, 12b. This third step makes it possible to form the tread 5 with at least one tread pattern 2 block 3 that envelops a reinforcing ply 7, with the same effects and advantages as the third step of the first embodiment.
The method according to the second embodiment of the invention may finally have a final rolling step, with the same effects and advantages as the final step of the first embodiment.
Advantageously according to the second embodiment of the invention, the method therefore makes it possible to form a tread 5 made of uncured rubber material, the scrap of which can be recycled. The method can also be implemented separately or directly on a green form, for example on a carcass (not shown), of tyre 1. The tread 5 can thus be reinforced and mounted on the green form of the tyre 1 before the whole is crosslinked.
Advantageously according to the invention, each tread pattern 2 block 3 is created from several portions made of uncured rubber material that may or may not be in one piece. The geometry of the central portion 11 makes it advantageously possible to choose the geometry that the reinforcing ply 7 has with respect to the contact surface of the tread 5. The orientation of the reinforcing ply 7 against the central portion 11 is maintained by covering the first and second lateral portions 12, 12a, 12b. The latter therefore form the part of the tyre 1 that is intended to be in contact with the ground. It will also be understood that the reinforcing ply 7 can thus, advantageously according to the invention, be of very different kinds, for example based on fibres based on polymers or on metal-based thread.
The invention also relates to a method for manufacturing a tyre 1 using the method for manufacturing a tread 5 based on uncured rubber material according to the second embodiment as set out above.
By way of entirely non-limiting example, the method for manufacturing a tyre could have the following steps of:
The method for manufacturing the tyre 1 therefore makes it possible to produce a green form 9 of tread 5 with at least one reinforced tread pattern 2 block 3 that can be integrated with conventional tyre 1 manufacturing steps, that is to say without any particular adaptation.
According to a second embodiment, the manufacturing method according to the invention makes it possible to obtain a tyre 1, in which the tread pattern 2 blocks 3 of the tread 5 (parts between the circumferential grooves 6 of the tyre 1) are stiffened, as illustrated in
More specifically, in the example illustrated in
Thus, for the block 3c through which the plane PE passes, the reinforcing ply 7 is symmetric with respect to the equatorial plane PE, starts substantially from the bottom of the adjacent groove 6 (a thickness of rubber material is visible in
The invention is not limited to the embodiments and variants presented and other embodiments and variants will be clearly apparent to a person skilled in the art. In particular, it is possible, as for the first variant of the first embodiment or the second embodiment, to vary the shape of the green form 9 depending on the application, in particular as regards the geometries and dimensions of the central portions 11 and/or of the lateral portions 12, 12a, 12b and/or of the base 10. By way of entirely non-limiting example, the first embodiment and/or the variant of the first embodiment and/or the second embodiment could be combined in one and the same tread 5 and/or in one and the same tread pattern 2 block 3 depending on the application.
Similarly, the same tread 5 could have reinforcing plies 7, 7a, 7b of different materials between two tread pattern 2 blocks 3 or in the same tread pattern 2 block 3 depending on the application.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1854595 | May 2018 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2019/062881 | 5/17/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/228830 | 12/5/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 1948311 | Orr | Feb 1934 | A |
| 2207098 | Maynard | Jul 1940 | A |
| 2232487 | Smith | Feb 1941 | A |
| 2710042 | Gates, Jr. | Jun 1955 | A |
| 3565716 | Felker | Feb 1971 | A |
| 5298216 | Kim et al. | Mar 1994 | A |
| 10744733 | Sandstrom et al. | Aug 2020 | B2 |
| 10850464 | Sandstrom et al. | Dec 2020 | B1 |
| 20130048171 | Sandstrom et al. | Feb 2013 | A1 |
| 20140138874 | Mayni | May 2014 | A1 |
| 20150007926 | Sandstrom et al. | Jan 2015 | A1 |
| 20160318346 | Clemmer et al. | Nov 2016 | A1 |
| 20200368984 | Sandstrom et al. | Nov 2020 | A1 |
| 20210197511 | Rouby et al. | Jul 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| 2467971 | Jul 1972 | AU |
| 1289306 | Feb 1969 | DE |
| 19542996 | May 1997 | DE |
| 102006028616 | Dec 2007 | DE |
| 102012214485 | Feb 2013 | DE |
| 1870259 | Dec 2007 | EP |
| 2011-37415 | Feb 2011 | JP |
| 2013-237283 | Nov 2013 | JP |
| 2015108744 | Jul 2015 | WO |
| 2016184692 | Nov 2016 | WO |
| Entry |
|---|
| Machine translation for German 102006028616 (Year: 2022). |
| International Search Report dated Jul. 22, 2019, in corresponding PCT/EP2019/062881 (6 pages). |
| Number | Date | Country | |
|---|---|---|---|
| 20210213696 A1 | Jul 2021 | US |