Patent Grant
11647803
This application is based upon and claims the benefit of priority from Patent Application IT 102019000022143, filed on Nov. 26, 2019.
The present invention relates to a method for manufacturing an article of underwear, in particular a bra.
An article of this type must obviously have in general good elasticity characteristics for being able to guarantee a high level of comfort for the person who wears it, preventing discomfort or even skin irritations.
To obtain the desired degree of elasticity, strips of elastic fabric are normally used which however cannot generally ensure optimal results in terms of comfort and prevent, for example, the formation of marks on the skin due to the pressure that such elastics generate. An alternative, particularly in the event of bras formed by two superimposed layers of fabric, could consist in the use of silicone elements that act both as an elastic element, and as a joining element of the two layers of fabric.
However, silicone is often opposed as it can be harmful for health. Furthermore, the use of silicone elements would cause problems in the final thermo-forming step of the bra for shaping it into the definitive form required from the aesthetic and wearability point of view. In fact, thermo-forming is usually performed at temperatures close to 200° C., which would imply a risk of melting the silicone material and the consequent damage of the article.
A general object of the present invention is to overcome the aforementioned drawbacks by providing a method for making an article of underwear, in particular a bra, which does not require elastics for reaching the required wearability characteristics.
A further object of the present invention is to provide a method for making a bra, which is free from silicone materials.
In view of such object, it has been thought, according to the invention, to realize a method for manufacturing an article of underwear, in particular a bra, comprising the steps of:
To clarify the explanation of the innovative principles of the present invention and the advantages thereof with respect to the prior art, one possible illustrative embodiment applying such principles will be described below, with the aid of the attached drawings. In the drawings:
The bra according of the manufacturing method according to the invention is of the type comprised of two superimposed fabric layers, an outer one, with strictly aesthetic functions, and an inner one adapted to ensure high comfort and wearability features for the person wearing it.
The manufacturing method of an article of underwear according to the invention first of all envisages providing a first fabric layer 11, designed to realize the outer layer of the bra, which is cut according to a shape 12 corresponding to the plane projection of the stretched underwear article, but of slightly greater dimensions with respect to the shape that the article itself must have once finished.
“Plane projection of the stretched article” means herein the shape of the article (or a portion thereof) stretched out on a plane. Substantially, such shape corresponds to the one known, in the tailoring/dressmaking world, as a “paper pattern”, i.e. the profile according to which it is necessary to cut the fabric for making a garment.
The manufacturing method according to the invention further envisages providing a second fabric layer 13, designed to realize the inner layer of the bra, cut according to a shape 14 substantially corresponding to the plane projection of the stretched underwear article.
The first fabric layer 11 will therefore have slightly larger dimensions with respect to the second fabric layer 13.
According to the specific organizational requirements of the production site, said first and second fabric layers 11, 13 can be provided as continuous strips or in the form of pieces of cloth of finished dimensions.
The type of material that constitutes said first fabric layer 11 will be essentially selected based on the desired aesthetic characteristics for the article. For example, such material can be selected from lace, tulle, microfiber, silk, stretch cotton, etc.
The type of material that constitutes the second fabric layer 13 will instead be essentially selected based on the desired comfort and wearability characteristics for the article. For example, such material can be selected from microfiber, tulle, silk, stretch cotton, etc.
The manufacturing method according to the invention further envisages providing a third film material 17, designed to realize permanent joining elements between the first fabric layer 11 and the second fabric layer 13 in the finished underwear article.
As schematically illustrated in
The film material 17 used for realizing said permanent joining elements between the first fabric layer 11 and the second fabric layer 13 is a “silicone-free” thermo-adhesive polyurethane film material.
Advantageously, two different weights of said thermo-adhesive polyurethane film are used: a first material, so-called “heavy”, for realizing the central underbreast portion 18 and upper strap portions 19, 19′, and a second material, so-called “light”, for realizing the lateral side portions 20, 20′ having a lower thickness and weight per square meter than the previous one.
More particularly, for said “heavy” thermo-adhesive polyurethane film, a film having a thickness of 180 μm and weight of 210 g/m2 can be used and for the light thermo-adhesive polyurethane film a film having thickness of 75 μm and weight of 90 g/m2 can be used. For example, for these two types of thermo-adhesive polyurethane material, films made by the company FaitPlast have been found optimal for use, known as “Easy-Tech 1381” and “Easy-Tech 897”, respectively. According to the operating features of the production plant, there may be simultaneously the supply, preparation and cutting of the first and second fabric layers 11, 13 and of the thermo-adhesive polyurethane film 17, or a specific sequential order may be envisaged, while remaining within the scope of the innovative principles of the present invention.
The manufacturing method according to the invention further comprises sprinkling said first fabric layer 11, on its inner side (i.e. the one destined to face the second fabric layer 13), with a reactive “hotmelt” polyurethane glue (PUR), capable of being reactivated only once, by heating, within a reactivation period of time of at least 3 days from the application, preferably within 5 days from the application.
The application of the glue onto the fabric is performed hot, at about 140° C., so that it is in the liquid state. After about 30 seconds, this glue spread onto the fabric will pass to the solid state, a condition that will be maintained until the subsequent reactivation thereof.
For this purpose, the use of a reactive polyurethane glue made by the company Kleiberit and known as “Kleiberit 900.7.9967” has been found to be particularly advantageous.
According to the operating features of the production plant, the glue can be applied to the first fabric layer 11 before or after cutting the fabric according to the shape 12.
The manufacturing method according to the invention further envisages applying the aforesaid central underbreast portions 18, upper shoulder strap portions 19, 19′ and lateral side portions 20, 20′, made of thermo-adhesive polyurethane film 17, in the correct position on the inner side (i.e. the one destined to face the first fabric layer 11) of the second fabric layer 13, as shown in
Once said portions 18, 19, 19′, 20, 20′ have been fixed to the fabric layer 13, the protection support of the thermo-adhesive polyurethane film 17 is removed, as well known to a person skilled in the art, leaving only the elastic part of the polyurethane film 17 coupled to said fabric layer 13.
After performing the operations described up to here, and however within the period in which said “hotmelt” reactive polyurethane glue is still reactivatable, the joining of the two fabric layers 11, 13 (previously cut according to the respective shapes 12, 14) can begin, with the portions 18, 19, 19′, 20, 20′ of thermo-adhesive polyurethane film 17 interposed between them, until the definitive and permanent fixing of the parts. For performing the joining step of the two fabric layers 11, 13, it may be advantageous to arrange the first fabric layer 11, destined to realize the outer layer of the bra, on a plane with the side covered with reactive polyurethane glue turned upwards, making the second layer of fabric 13, destined to realize the inner layer of the bra, rest on it, with the portions of thermo-adhesive polyurethane film 17 turned downwards, and taking care so that the shape 14 of said second fabric layer 13 fits into the shape 12 of the first fabric layer 11.
In this way, the portions 18, 19, 19′, 20, 20′ of thermo-adhesive polyurethane film 17 will be correctly interposed between the two fabric layers 11, 13.
The assembly of the two fabric layers 11, 13, with the portions of thermo-adhesive polyurethane film 17 interposed, are then advantageously covered by a paper sheet 21, as shown in
At this point, a hot-pressing of the two superimposed layers of fabric 11, 13 is performed. Thanks to the characteristics described above of the glue used, this operation may be performed within 5 days from the application of the glue itself.
For performing this operation, the assembly of superimposed layers of fabric 11, 13, with the portions of thermo-adhesive polyurethane film 17 interposed and covered with the layer of protective paper 21, is positioned under the plane of a hot press, which subjects the material to heating up to about 120° C. for at least 10 seconds.
Such heating reactivates the “hotmelt” reactive polyurethane glue (PUR), which returns again to the liquid state penetrating through the fibres of the fabrics to be joined. This reaction of the glue initially creates a first mechanical ‘gripping’ step and further initiates a chemical cross-linking process that leads it to solidify definitively, so that the glue itself cannot be removed unless mechanically, ripping the two edges of fabric. Complete cross-linking of the type of glue used in the manufacturing method according to the invention takes place in about 7 days.
The sheet of paper 21 has the function of preventing, during the heating step in the press, and consequent liquefaction of the “hotmelt” polyurethane glue, the latter getting stuck to the plane of the press at the edges of the first fabric layer 11 exceeding the shape 14 of the second fabric layer 13.
Once the hot-pressing of the two superimposed fabric layers 11, 13 has been performed, the paper sheet 21 is removed and the underwear article appears as in
Once at least 7 days have passed from the hot-pressing (i.e. the necessary time for ensuring the complete cross-linking of the polyurethane glue), thermoforming of the article takes place to give the bra the desired shape and size of the cups. Such process is well known to a person skilled in the art and, therefore, will not be described herein in detail.
At this point, the exceeding edges 22 of the first fabric layer 11 are trimmed (also here, according to techniques and methods known to a person skilled in the art) following the profile of the finished garment. Finally, it is possible to proceed with the application of adjustable shoulder straps, hooks, labels, etc., through normal sewing operations, for the definitive completion of the garment.
It is at this point clear how the method for the manufacturing of an article of underwear according to the invention enables a garment to be obtained with the best wearability characteristics although not using elastics or silicone-based materials.
Clearly, the above description of an embodiment applying the innovative principles of the present invention is given by way of an illustrative example of such innovative principles and must not, therefore, be taken to limit the scope of the patent claimed herein.
For example, in addition to the portions 18, 19, 19′, 20, 20′ of polyurethane thermo-adhesive film 17 designed to realize the joining of two layers of fabric 11, 13, further portions could be provided, in the appropriate positions, depending on the particular aesthetic and/or functional characteristics that may be desired or necessary from time to time.
Furthermore, the shape of the garment and the fabrics of which it is composed may likewise be selected on the basis of the specific desired characteristics.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102019000022143 | Nov 2019 | IT | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4701964 | Prunesti | Oct 1987 | A |
| 4776916 | Prunesti | Oct 1988 | A |
| 6344238 | Schmitt | Feb 2002 | B1 |
| 7682219 | Falla | Mar 2010 | B2 |
| 20150017877 | Cholet | Jan 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 123 666 | Aug 2001 | EP |
| 1 123 666 | Aug 2001 | EP |
| 2 826 389 | Jan 2015 | EP |
| WO 2014202477 | Dec 2014 | WO |
| Entry |
|---|
| Italian Search Report dated Jul. 16, 2020 in Italian Application 102019000022143 filed Nov. 26, 2019 (with English translation of Categories of Cited Documents), citing documents AA-AB and AO-AQ therein, 3 pages. |
| European Office Action dated Jan. 28, 2022 in European Patent Application No. 20 209 697.0, 24 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20210153586 A1 | May 2021 | US |