Patent Application
20240033969
The invention relates to a method for manufacturing an engineered stone and an engineered stone.
An engineered stone comprises a stone material or a stone like material, like for example crushed stones, sands or other minerals but also recycled ceramic, glass and metals, bonded by means of a cured binder like for example resin or cement. More particularly, the term engineered stone is intended in encompass a composite material formed by a stone material or a stone like material bonded together by means of a cured binder that it is cured at low temperature, wherein the term low temperature is intended to encompass a temperature below 500° C.
Traditionally, natural stone is used as building material, especially for finishing the buildings like for example for coverings of wall or floor and for producing worktops like kitchen or bathroom countertops and vanities. Natural stones are extracted from mines and subsequently cut and polished to obtain slabs or boards of the desired shape. Due to the mine extraction, natural stones are relatively expensive and produce a high impact on the environment.
Therefore, in the past years methods for manufacturing engineered stones were developed in order to reduce costs and provide a more environment friendly product. A well-known example of such methods is represented by the so called Bretonstone® technology described, for example, in the document, WO 2007/138529. Said document discloses a method for manufacturing an engineered stone which comprises the step of: providing a stone material or a stone like material, for example by grinding sand or quartz; mixing the stone or stone like material with a binder, for example a resin powder, in order to obtain a mixture; depositing the mixture in a mold of a press, having shape and dimension similar to those of the final article; press the mixture applying vacuum, with the accompanying application of a vibratory motion at pre-established frequency; the semi-product obtained is then hardened by means of a heat curing process to obtain the engineered stone; the engineered stone is then subjected to finishing steps like cutting or polishing.
Such kind of engineered stone normally comprises a one-color decoration. Alternatively, the engineered stones comprise a décor comprising artificial veins for imitating a natural stone like marble or granite. As disclosed in WO 2009/010406 such décor is obtained by adding a coloring agent to the mixture before the mixture is deposited in the mold. The mixture is carried by an endless belt above the mold and is loaded into the mold itself by free falling from the end of the belt. The coloring agent is loaded by means of appropriate nozzles to the surface of the mixture substantially in correspondence of the end of the belt so to fall into the mold together with the mixture in a non-controlled manner. Following the vibro-compression step the pigment particles distribute in the mixture thereby generating a veined effect through the entire thickness of the engineered stone. Therefore, with this technique it is not possible to obtain an engineered stone with a reproducible and predefined décor.
WO 2016/113652 discloses an equipment and a method for creating programmable chromatic effect in an engineered stone by means of a computer controlled machine. The machine is an anthropomorphous robot or a cartesian robot provided with one or more nozzles for dispensing a coloring agent on the surface of a mixture in a temporary support. The nozzle is connected to a tool that interacts with the surface of the mixture to create grooves or holes to receive the color. Thus, this equipment needs a machine work of the mixture and provides for décor imitating natural stone or woods with a relative low-quality resolution.
The present invention aims in the first place at providing an alternative method for manufacturing an engineered stone, which, in accordance with several of its preferred embodiments, is directed to solve one or more of the problems arising in the state of the art.
Thereto, the present invention, according to its first independent aspect, relates to a method for manufacturing an engineered stone, comprising the steps of:
The engineered stone can be manufactured in any desired form although substantially flat shapes like a board, a tile or a slab are preferred. The engineered stone is preferably shaped as a slab wherein with slab is intended a substantial rectangular and flat form, preferably comprising a surface of minimum 1.5 square meters. In this way, the engineered stone is manufactured in a shape that is sufficiently large to be versatile and adapted to be cut according to the dimension and shape of the final destination of the engineered stone itself, like for example a kitchen or bathroom countertops. According to a preferred embodiment, the slab has a length of at least 2 m, preferably at least 2.5 m, for example 3 m or more, and a width of at least 1 m preferably 1.5 m or more. Moreover, the slab preferably has a thickness of at least 10 mm, preferably at least 20 mm, for example 30 mm.
The stone or stone like material can comprise any kind of stone, sands, siliceous mineral material, for example quartz, silica sand, clay, feldspar cristobalite granite, talc, or calcareous mineral material, for example, calcium carbonate, marble, gypsum. The stone or stone like material can also comprise ceramic, glass, metals and other inorganic material, for example recycled materials. The stone or stone like material can be in form of powder, granules, shards, grains, aggregates, or any other particulate form although granules and powder forms are preferred. Preferably the stone or stone like material is in powder form having an average particle dimension lower than 45 μm, preferably lower than 20 μm. The stone or stone like material is preferably at least 80% by weight of the mixture, preferably more than 85% and more preferably more than 90%. According to another embodiment of the invention the stone or stone like material can be in form of aggregates, grains and/or granules having a particles size distribution between 0.1 and 0.7 mm. According to still another embodiment of the invention the stone or stone like material comprises at least 60 wt % of grains and/or granules and between 20 to 35 wt % of powder form wherein, for example, the granules have a particles size distribution between 0.1 and 0.7 mm and the powder has an average particle dimension lower than 45 μm, preferably lower than 20 μm.
The binder is a curable substance that is configured to be cured thereby bonding together the particles of the stone or stone like material. The binder can be in any form, i.e., liquid, solid, gel or any form that is suitable to be mixed with the stone or stone like material and to be homogeneously dispersed within. Although any kind of curable substance can be used, heat curable substances are preferred. The binder can be an organic substance, for example a resin, or an inorganic substance, for example a concrete.
If the binder is an organic substance, it can be either a thermoplastic or a thermosetting resin. For example, thermoplastic resins can be polyolefin resins like polyethylene or polypropylene, polystyrene or polyester like polyethylene terephthalate, whereas examples of thermosetting resins are acrylic resin, epoxy resin, polyurethane, rubber, polyester resin preferably unsaturated polyester resin, vinyl ester resin or the like. For example, in a preferred embodiment the binder is unsaturated polyester resin. The binder is preferably less than 20% by weight of the mixture, preferably less than 15% and more preferably less than 10%.
If the binder is an inorganic substance, it is preferably a cement for example a portland cement. In this case the binder can be up to 30% by weight of the mixture and the stone or stone like material can be between 70% and 100% by weight.
It is noted that the mixture can also comprise additives, like for example coupling agents, catalysts, or reagents to activate or speed up hardening of the binder, and/or temporary bonding agent like glues or thermoplastic resins that temporarily bonds the stone or stone like material.
It is also noted the mixture can comprise fillers, for example inorganic fillers like sand, quarts, feldspar, silica, calcium carbonate, more particularly in powder form, for example to reinforce the binder that fills the interstices between the stone or stone like material particles. The fillers are preferably mixed into the binder, for example they are dispersed into the resin or the cement to form a binding past or binder pellets destined to be mixed with the stone or stone like material for forming the mixture.
Moreover, reinforcing elements like, for example, fibers or whisker, can be added to the mixture for reinforcing the engineered stone. Preferably reinforcing elements comprise fiberglass, carbon fibers, or metal fibers.
The mixture can be provided in different forms, for example in form of a pasty material or a slip, although an incoherent particulate form is preferred. According to a preferred embodiment wherein the mixture is provided in form of an incoherent material, the mixture comprises a first particulate of stone or stone like material and a second particulate of binder mixed together, preferably in powder form. Alternatively, the incoherent particulate can be formed by granulates or pellets wherein each granule comprises the stone or stone like material and the binder bonded together for forming the granule. According to this alternative, the stone or stone like material and the binder can be bonded together by means of a temporary bonding agent like a glue or a thermoplastic resin, or the stone or stone like material and the binder can be mechanically or physically bonded together, for example the binder can be a thermoplastic resin partially or fully coating the stone or stone like material, or the stone or stone like material can be dispersed in a solidified thermoplastic resin, or the stone or stone like material and the binder can be compressed together to form said granules.
It is noted that the mixture can be provided directly into a mold, a frame or any other tool suitable to providing a shape to the mixture by means of hopper or feeder, although it is preferred to provide the mixture on a temporary support like for example a conveyor belt or a tray so that it is possible to provides intermediate working step before the compacting phase, like for example machining of the edges of the slab or adding a coloring agent to the mixture.
A coloring agent can be added to the mixture to provide a basic color of the engineered stone. In this way, it is possible to provide a background for the printed pattern like a white, grey, beige, or brown background. Alternatively, the coloring agent can be added in such a manner to form a basic décor, e.g., a veined effect imitating the veins or flakes of a marble, a granite or any natural stone. In this way, it is possible to combine the basic décor obtained by the coloring agent with the printed pattern thereby obtaining more complex and pleasing aesthetic effects of the engineered stone. The coloring agent can be either in liquid form or in powder form. The coloring agent can also be either an inorganic or an organic substance.
If the coloring agent is added to provide a basic color of the engineered stone, it can be dispersed in the mixture before it is loaded in the mold or in the frame or on the temporary support so that the coloring agent colors the bulk of the engineered stone, i.e., the entire body of the engineered stone is colored by the coloring agent. Alternatively, it is possible to provide the coloring agent so that it colors only the surface of the engineered stone. For example, it is possible to provide a coloring agent in order to coat at least partially the surface to be printed so to provide a background for the printed pattern. Such basic color can be obtained either with printing technique, for example a screen printing or a roller printing, or with a coating technique like for example spray technique.
It is noted that, since the coloring agent is dispersed into the mixture this can be inhomogeneous dispersed thereby forming random color shades that substantially form a basic décor of the engineered stone. It is also further noted that said coloring agent random color shades can simulate stone veins or grains.
If the coloring agent is added to create a basic décor, it can be added either after the mixture is loaded in the mold, in the frame, or on the temporary support; or contemporary to the loading of the mixture in the mold, in the frame, or on the temporary support. In the first case, the coloring agent can be added by a computer controlled machine, like for example an anthropomorphous robot or a cartesian robot, provided with one or more nozzles for dispensing the coloring agent. The nozzle is connected to a tool that interacts with the surface of the mixture to create grooves or holes to receive the coloring agent. In the second case, the coloring agent can be randomly dispersed by free falling from a feeder on the surface of the mixture together with the mixture itself so that the veined effect is obtained in an uncontrolled manner and every engineered stone is provided with a unique décor. According to said alternative embodiment of joining the coloring agent, the coloring agent is preferably distributed in the body of the engineered stone along lines imitating the veins or flakes of a marble, a granite, or any natural stone. In both these cases, the basic décor is created in the entire thickness of the engineered stone so that it is visible also from the lateral side of the engineered stone and preferably from any section of the engineered stone itself. For example, the décor is visible also in the new sides generated from a cut created in the engineered stone.
According to a preferred embodiment during the compacting step the mixture is loaded in a mold, a frame, or any other tool suitable for providing a shape to the mixture of a press or compacting device. Preferably, the mold or frame can have the shape and dimension similar to those of the final product to be obtain or to those of a semi product of the process. Preferably the mold or frame has the shape and dimension similar to those of a slab or a block. Preferably the compacting step is conducted under vacuum, i.e., a vacuum is generated in the mold or frame to help extracting air between the mixture particles. More preferably, vibration is applied to the mold or frame during the pressing step thereby helping to compact of the mixture particles, so that the porosity of the engineered stone is significantly reduced. According to a preferred embodiment both vacuum and vibration are applied to the mixture during the compression.
It is not excluded that the engineered stone is formed according to alternative techniques different from compaction like casting, extrusion, or lamination. For example, the mixture, in liquid or pasty form, can be poured into the mold or extruded.
According to an embodiment of the invention the method may comprise the step of forming a relief structure on the top surface of the engineered stone, for example comprising protrusions and/or excavations. Preferably the relief structure comprises features related to the basic décor and or the printed pattern, for example the relief structure comprises protrusions and/or excavations that run substantially parallel with respect to the veins of the imitated natural stone. Preferably the relief structure is created by means of a structured mold during the compacting step, although other techniques are available. For example, the relief structure can be created by means of embossing rollers, or embossed molds after or during the compacting step.
After the compacting step, the engineered stone is carried to a curing station. The cure of the binder can be obtained by means of radiation, heat, chemical curing, or other suitable techniques. In any case, the curing step is conducted at a temperature below 500° C., for example below 200° C., for example at room temperature.
If the binder is a thermosetting resin, the curing step is preferably a heating step because it provides for a homogeneous curing of the binder through the entire body of the engineered stone and it is relatively cheap and easy to control. Preferably the heating step is conducted a temperature below 200° C., more preferably below 100° C., for example at 90° C. During the heating step the binder cures and permeates the interstices between the particles of stone or stone like material thereby bonding together the particles of stone or stone like material and reducing the porosity of the engineered stone.
If the binder is a thermoplastic resin, the curing step is conducted by heating the mixture up at least around or above the Tg (glass transition temperature), preferably up to the melting temperature of the thermoplastic resin so that the viscous or liquid resin permeates the interstices between the particles of stone or stone like material, and then cooling down the mixture to solidify the thermoplastic resin to bond together the particles of stone or stone like material and reduce the porosity of the engineered stone. The cooling step can be conducted either at room temperature or in a forced manner for example by means of belt cooling or blowing air onto the engineered stone.
If the binder is a cementitious material, the curing step is a chemical curing wherein an activator like water or carbon dioxide is added to the mixture to activate the hardening of the cement by means of hydration or carbonation reaction.
The printing step can be conducted by means of a wide variety of techniques, for example screen printing or roller printing although digital printing is preferred. Digital printing, preferably inkjet digital printing, allows to reproduce a wide variety of images with a very high resolution. For example, by means of digital printing it is possible to obtain a printed pattern with a resolution up to 660 dpi. Moreover, digital printing is preferred above roller printing and screen printing because it is a more flexible printing solution. For changing the production from one décor to another décor it is not necessary to change printing tools like the rollers or the screens.
It is noted that the printing step can be conducted either before or after the curing step. According to a preferred aspect of the invention the step of printing is conducted before the step of curing. In this way, since the engineered stone is not hardened the ink can flow through the interstices between the particles of stone or stone like material thereby penetrating into the thickness of the engineered stone so that after the curing step the engineered stone can be polished without deteriorate the printed pattern. More in particular, the printing step can be conducted either before or after the compacting step. Preferably the printing step is conducted before the compacting step so that the subsequent compacting phase, preferably a vibro-compacting phase, helps the inks to penetrate through the surface of the engineered stone. In this way, the printed pattern is preferably present in a thickness of the compacted engineered stone, called penetration depth, of at least 0.5 mm starting from the top surface, more preferably greater than 1 mm, for example greater than 2 mm so that after polishing of the top surface the digital printed pattern is still visible. If the coloring agent is provided on the engineered stone, the printing step is conducted after the step of providing the coloring agent.
It is also noted that, if the printing step on the first surface is performed after said curing step, it is also possible that one or more machining steps, for example calibration and/or polishing steps, are performed on the first surface before the printing step. It is in fact noted that, because of the compacting step occurs via application of vibration and vacuum, the engineered stone requires machining steps to flattening and smoothing the surface of the engineered stone. This polishing can also improve the gripping of primers, inks and/or protective layer.
According to another embodiment of the invention, the printed pattern can be provided also on other surfaces of the engineered stone that are different with respect to the top surface, preferably on the edges of the engineered stone i.e., on surfaces that are inclined or substantially perpendicular to the top surface of the engineered stone. In this case a printing equipment with an orientable printing head can be used. Alternatively, multiple printing steps can be conducted, preferably in a sequential order. For example, a first printing step provides for a first printed pattern on the top surface, and a second printing step provides for a second printed pattern on the longitudinal and/or the transversal edge.
According to a preferred embodiment the printed pattern on the edges are provided after the curing step, more preferably after machining step like calibration or machining.
It is noted that the printed pattern is preferably applied in a fixed relationship to a predetermined point, such that the print is applied at a predetermined location of the of the slab, e.g. at a fixed distance, that may be zero, from an edge or corner, and that the printed pattern is preferably aligned to an edge, preferably a longitudinal edge of the slab. Such can be obtained through a detection of the upcoming slab, and using this detection to control the printer. Applying the printed pattern in a fixed relation to a predetermined point is advantageous for obtaining corresponding structural features in the relief. Furthermore, in case that the multiple printed patterns are provided on different surfaces of the engineered stone it is possible to match the different printed patterns together to form a single image or decoration that continues from one surface to the other.
According to the invention either organic or inorganic inks or a combination of both can be used. For example, water based inks, solvent based ink, or sublimation in can be used. Since it is not necessary to fire the engineered stone at high temperature organic inks can be used so that a wide gamut of color for the décor is obtainable. It is noted that the organic ink can be a curable ink, for example a UV, IR curable ink or heat curable ink, and that the method can comprise a print curing step for curing the printed pattern, wherein the print curing step can be either the same curing step of the engineered stone or a different curing step.
If inorganic inks, for example ceramic inks, are used a durable printed pattern is obtainable, wherein with durable is meant able to resist to physical and chemical agents like UV radiation, acid, or basic attack. Preferably the inorganic inks comprise particles of pigments having a maximum dimension less than 2 μm, for example less than 1.5 μm, so that it is possible to obtain a printed pattern having a very high resolution. Moreover, the inventors have surprisingly found that when using pigments having a maximum dimension less than 2 μm, for example less than 1.5 μm, the penetration depth of the printed pattern is significantly increased.
If sublimation inks are used, the printed inks can be fixed (or cured) onto the substrate by means of application of heat and/or pressure. For example, the sublimation inks can be fixed at a temperature between 100 and 200° C. Sublimation inks can either be printed first onto a transfer substrate, for example a transfer sheet, or, preferably, directly on the engineered stone, for example after the provision of a primer on the surface of the engineered stone.
Moreover, the ink can show a viscosity below 70 cP, preferably below 50 cP and/or a surface tension below 25 dyn/cm. The inventors have surprisingly found that when using inks having low viscosity and/or surface tension it is possible to increase the penetration depth of the ink.
It is noted that the printed pattern can be obtained by means of multiple color inks, for example with four colors, preferably cyan, magenta, yellow and black, or more colors, for example seven or eight colors.
Furthermore, the method can comprise the step of providing at least the surface to be printed with a primer, for example an ink adhesion promoter or a catalyst, before the step of printing itself. The primer can be for example acrylic, methacrylic, polyurethane, water based, solvent based, styrene. The primer can be provided by means of spray, rollers or any other suitable techniques.
It is noted that the method can also comprise the step of providing a protective layer to coat partially or entirely at least the top surface of the engineered stone. Preferably, the protective layer is provided above the printed pattern, in this case it is preferable that the protective layer is a transparent or translucent layer. The protective layer can be, for example, a curable resin like an acrylic or epoxy resin. The protective layer can also be configured to improve superficial properties of the engineered stone like for example cleanability, impermeability, antimicrobial behavior, wear resistance, scratch resistance or the like. In order to improve such superficial properties, the protective layer can comprise fillers, like corundum, silver, titanium dioxide, or others, dispersed therein to improve the superficial properties. The protective layer is preferably provided after the printing step, preferably before the hardening step so that it is hardened together with the mixture and the print. According to an alternative embodiment the protective layer is provided after the curing step of the mixture and the method comprises a second hardening step configured to harden the protective layer. Said hardening step can be a curing and/or a drying step. The protective layer is provided by means of spray, rollers, or any other suitable techniques.
The method may also comprise the step of polishing at least partially the surface of the slab, preferably at least the surface comprising the printed pattern. The polishing step is advantageously conducted in order to remove an amount of material from the surface so that the printed pattern is still visible on the polished surface. For example, the polishing step is performed in such a way to remove less than 2 mm of the thickness of the slab, preferably less than 1 mm, for example 0.5 mm. In other words, the polishing step is performed in such a way to reduce the thickness of the slab of an amount smaller than the penetration depth.
It is noted that said polishing step, being a finishing step, can be performed on the engineered stone already provided with the print and even with the protective layer. It is further noted that said polishing step can be performed after that said printing step is performed, independently from the fact that said printing step is performed before and/or after curing the engineered stone.
Furthermore, the method can comprise further machining steps like for example cutting, drilling, milling, or grinding the engineered stone. In particular, the engineered stone can be cut according to the desired shape and dimension following the specification of the customer design. For example, if the engineered stone is used as a bathroom or kitchen countertop it can be cut to fit to the furniture on which it must be fitted. Also, through holes can be provided in the engineered stone to accommodate a hob, a washbowl, sockets, or other item.
The invention according to its second independent aspect provides for an engineered stone comprising a stone or stone like material and a binder bonding together the particles of stone or stone like material wherein the engineered stone comprises at least a top surface having a printed pattern. The inventors have found that due to this solution an engineered stone with a wider range of décor can be obtained. Furthermore, a higher resolution and more realistic décor can be obtained.
The printed pattern can represent any décor, design or inscription, although it is preferred that the printed pattern represents an imitation of a natural stone, i.e., represents the veins and/or flakes of a natural stone like a marble or a granite.
The engineered stone of the second aspect of the invention is preferably obtained or obtainable through a method in accordance with the first aspect of the invention or the preferred embodiments thereof. The engineered stone may show one or more of the product features described in connection with the first aspect, without necessarily being manufactured in accordance with the method of the first aspect.
Furthermore, the invention according to its third independent aspect provides for a countertop comprising an engineered stone that comprises at least a top surface having a printed pattern. The countertop can be used in a kitchen, a bathroom as well as any other environment. The countertop preferably comprises holes for accommodating a hob, a washbowl, a socket, or any other item. The countertop of the third aspect preferably comprises an engineered stone in accordance with the aforementioned second aspect and/or an engineered stone obtained or obtainable through a method in accordance with the first aspect of the invention.
It is noted that the characteristic that the engineered stone comprises a protective layer forms an inventive idea irrespective of the presence of a top surface comprising a décor and, in particular, irrespective of the top surface comprising a printed pattern. Thus, according to its fourth independent aspect the invention provides for an engineered stone comprising a stone or stone like material and a binder bonding together the stone or stone like material wherein the engineered stone comprises at least a top surface and wherein the engineered stone comprises a protective layer to coat partially or entirely at least the top surface.
The engineered stone, as mentioned in all aspects of the invention, is not limited to the use as a countertop but it can be used as a floor element for floor covering, wall panels, internal or external cladding or panels for furniture and vanities as well.
With the intention of better showing the characteristics of the invention, in the following, as an example without any limitative character, several preferred embodiments are described with reference to the accompanying drawings, wherein:
Referring to
The engineered stone 1 comprises at least a top surface 3 provided with a printed pattern 4. The printed pattern 4 can represent any décor, design or inscription, although it is preferred that the printed pattern 4 represents an imitation of a natural stone, i.e., represents the veins and/or flakes of a natural stone like a marble or a granite.
According to a variant of the invention, the engineered stone 1 can comprise a basic décor 5 defining a background for the printed pattern 4. For example, the basic décor 5 represents an imitation of a natural stone, i.e., represents the veins and/or flakes of a natural stone like a marble or a granite. In this case the printed pattern 4 above the basic décor 5 can represent special features or special effects of the imitated natural stone. As shown from
According to a preferred embodiment, the top surface 3 of the engineered stone 1 is smooth, for example polished.
The stone or stone like material can comprise any kind of stone, sands, siliceous mineral material, for example quartz, silica sand, clay, feldspar cristobalite granite, talc, or calcareous mineral material, for example, calcium carbonate, marble, gypsum. The stone or stone like material can also comprise ceramic, glass, metals, and other inorganic material, for example recycled materials. The stone or stone like material can be in form of powder, granules, shards, or any other particulate form although powder form is preferred. Preferably the stone or stone like material is in powder form having an average particle dimension less than 45 μm, preferably less than 20 μm. The stone or stone like material is preferably at least 80% by weight of the mixture, preferably more than 85% and more preferably more than 90%. According to another embodiment of the invention the stone or stone like material can be in form of aggregates, grains and/or granules having a particles size distribution between 0.1 and 0.7 mm. According to still another embodiment of the invention the stone or stone like material comprises at least 60 wt % of grains and/or granules having a particles size distribution between 0.1 and 0.7 mm and between 20 to 35 wt % of powder form having an average particle dimension less than 45 μm, preferably less than 20 μm.
The binder is a curable substance that is configured to be cured thereby bonding together the particles of the stone or stone like material. The binder can be in any form, i.e., liquid, solid, gel or any form that is suitable to be mixed with the stone or stone like material and to be homogeneously dispersed within. Preferably, the binder is in powder or pellet form. Although any kind of curable substance can be used, heat curable substances are preferred. The binder can be an organic substance, for example a resin, or an inorganic substance, for example a concrete or silica.
According to the preferred embodiments shown in
The mixture M can also comprise additives, like for example catalysts or reagents to activate or speed up hardening of the binder, and/or temporary bonding agent like glues or thermoplastic resins that temporarily bonds the stone or stone like material.
Moreover, the mixture M can comprise fillers, for example inorganic fillers like sand, quarts, feldspar, silica, calcium carbonate in fine powder form to reinforce the binder that fills the interstices between the stone or stone like material particles. The fillers are preferably mixed to the binder, for example they are dispersed into the resin or the cement to form a binding past or are binder pellets destined to be mixed with the stone or stone like material for forming the mixture.
The components of the mixture M are mixed together and are provided on a temporary support 10 by means of a feeding device 11, for example a hopper. The temporary support 10 can be a mold, a frame, a tray, or a conveyor, for example a conveyor having lateral containment means for providing the mixture of a shape similar to that of the final slab. In the embodiment shown in
According to a preferred embodiment shown in the figures, the mixture M is provided in form of an incoherent particulate, and comprises a first particulate of stone or stone like material and a second particulate of binder mixed together, preferably in powder form for example into the feeding device 11.
The method can further comprise the step of forming the basic décor 5 on the engineered stone 1. In the embodiment shown
Referring back to
For example, the printing device 21 is an inkjet digital printer comprising a printing head adapted to print with four or more colors. More in detail, the printed pattern 4 can be obtained by means of multiple color inks, for example with four colors, preferably cyan, magenta, yellow and black, or more colors, for example seven or eight colors.
According to a preferred embodiment organic inks are used for providing the printed pattern 4 on the engineered stone 1. Preferably the inks are curable inks, for example UV, IR or heat curable inks.
The method further comprises the step S3 of compacting the mixture M. according to the embodiment shown in
Preferably the compacting station 30 comprises also a vibrating unit 32 configured to apply a vibration to the mixture during the compacting step S3. Moreover, according to the preferred embodiment, the compacting station 30 comprises also a vacuum unit 33 configured to create vacuum into the mold 12 during the compacting step S3.
In the embodiment shown in
The method further comprises a curing step S4 for curing the binder of the mixture M thereby bonding together the stone or stone like materials and, thus, obtaining the slab 2 of engineered stone 1. According to the embodiment shown in
According to a preferred embodiment, the curing station 40 comprises a heating device 41 configured to heat curing the mixture M, i.e., it is configured to heat the mixture M up to the curing temperature of the binder. Preferably the heating temperature is below 200° C., more preferably below 100°, for example 90° C.
The method, according to the invention, can further comprise one or more machining steps S5, for example a polishing step. According to a preferred embodiment shown in the figures the engineered stone is moved by the second conveyor 34 to a machining station 50 comprising a polishing device 51. The polishing device 51 is configured to polish the top surface 3 of the slab 2. Preferably the polishing step S5 is conducted in such a way to remove a very limited amount of material from the top surface 3 of the slab, and in particular it is conducted in such a way that after the polishing step the printed pattern 4 is visible from the top surface 3 of the slab 2. For example, the polishing step S5 is conducted in such a way to remove less than less than 2 mm of the thickness of the slab, preferably less than 1 mm, for example 0.5 mm, i.e., less than the penetration depth P from the top surface 3.
The method can comprise further machining steps S5, like for example cutting, drilling, or milling step. For example, the machining station 50 can comprise a cutting device for cutting the slab 2 according to the shape and dimension of the design of the desired final use of the engineered stone 1.
For example,
As shown in
The present invention is in no way limited to the hereinabove described embodiments, but such floor, floor covering, and floor elements may be realized according to different variants without leaving the scope of the present invention.
Further, as is clear from the content of the description, the present invention relates to one or more of the items as listed below, numbered from 1 to 21:
This application is a continuation-in-part of U.S. Nonprovisional patent application Ser. No. 18/146,488 filed Dec. 27, 2022, which is a continuation of U.S. Nonprovisional patent application Ser. No. 16/647,055 filed Mar. 13, 2020, now U.S. Pat. No. 11,565,438 issued Jan. 31, 2023, which is a National Stage Entry of, and claims priority to, PCT Patent Application No. PCT/US2018/053836 which was filed on Oct. 2, 2018. PCT Patent Application No. PCT/US2018/053836 claims priority to and the benefit of U.S. Nonprovisional patent application Ser. No. 15/722,804, which was filed on Oct. 2, 2017, now U.S. Pat. No. 11,628,593 issued Apr. 18, 2023. The entire contents and substance of the aforementioned applications are hereby incorporated by reference in their entireties as if fully set forth herein.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16647055 | Mar 2020 | US |
| Child | 18146488 | US | |
| Parent | 15722804 | Oct 2017 | US |
| Child | 16647055 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 18146488 | Dec 2022 | US |
| Child | 18483698 | US |