The invention relates to the field of manufacturing ornamental parts, in particular in watchmaking, jewellery or telephony, the part being made of a hard material with a polymer coating. It relates more specifically to a method for manufacturing a watch middle provided with a polymer coating of the inner face.
In the watchmaking and jewellery industry, various materials are used for the manufacture of cases or bracelets of various appearances. It is in particular known to manufacture timepieces, in particular watch cases, from hard material. Hard material means materials having a Vickers hardness greater than 1000 HV. Such hard materials are, for example, ceramic, silicon nitride, zirconium oxide, sapphire, or alumina.
In watchmaking, they are used for their mechanical properties, in particular because they are difficult to scratch. They are used, for example, to manufacture parts such as watch middles or bracelet links.
The ornamental parts are obtained after an injection step giving the desired shape to the part, then by a sintering step to harden the material.
However, this type of injection method does not allow to obtain sufficiently precise dimensions. For example, for the middle of a watch, it is needed to have housing dimensions that allow a crystal, a bezel, or a back to be pressed in such a way as to be held firmly. There is also a need to drill holes for a crown or push-pieces, which cannot be obtained with the injection method.
To achieve this, it is necessary to machine the middle to correct the dimensions of the middle. However, hard materials are difficult to machine because of their hardness. To this end, diamond tools with a short lifetime are used, which generate significant costs.
It would be advantageous to obtain an ornamental hard material part, which requires little or no machining on the hard material, in particular for ceramic materials, but which comprise functional surfaces.
The present invention provides this type of method. Thanks to the combination of a hard material and a coating of polymer material, the method allows to avoid the direct machining of the hard material on the faces of the part. Polymer is easier to machine than hard material. Thus, the cost of manufacturing the part is reduced by avoiding machining the hard material as much as possible. Furthermore, the water resistance of the part is ensured between the coating and the hard material.
More specifically, the invention relates to a method for manufacturing an ornamental part, for example for a timepiece, jewellery or telephone, in particular a watch middle, the part at least partially comprising a hard material having a Vickers hardness greater than 1000 HV. According to the invention, the method comprises the following main steps:
According to a particular embodiment of the invention, the method comprises an additional step of machining the polymer material coating.
According to a particular embodiment of the invention, the method comprises an additional step of assembling the part.
According to a particular embodiment of the invention, the method comprises a step of machining the green body.
According to a particular embodiment of the invention, the body being provided with an inner face, the deposition step consists in depositing the coating on said inner face.
According to a particular embodiment of the invention, a back of the part is formed of the polymer material during the coating deposition step.
According to a particular embodiment of the invention, the polymer is to be selected from the following list: POM, PA, PUR, PPS, ABS, PC.
According to a particular embodiment of the invention, the hard material is to be selected from materials such as ceramic, silicon nitride, zirconium oxide, sapphire, or alumina.
The invention also relates to an ornamental part, for example for a timepiece, jewellery or telephone, in particular a watch middle, comprising a hard material body and at least one face provided with a polymer material coating, the body defining an inner space.
According to a particular embodiment of the invention, the coating has a functionalised shape.
According to a particular embodiment of the invention, the coating includes a stair-stepped shape, in particular to be able to assemble other portions of a watch case by interlocking.
According to a particular embodiment of the invention, the body defines an internal space, the face bordering said space.
According to a particular embodiment of the invention, the face is an inner face of the body.
According to a particular embodiment of the invention, the part comprises a back obtained during the coating deposition step.
The invention also relates to a watch case comprising such an ornamental part, as well as a crystal and a bezel for holding the glass on the part, the bezel being assembled to the part by the polymer coating.
The invention will be better understood with regard to the appended drawing wherein:
The method 1 for manufacturing an ornamental part 10, for example for a timepiece, jewellery or telephone, is represented in
The method 1 comprises a first step 2 of producing a precursor from a mixture of at least one powder material with a binder. In this context, the ceramic-based powder may include at least one metal oxide, one metal nitride or one metal carbide. For example, the ceramic-based powder may include aluminium oxide in order to form synthetic sapphire or a mixture of aluminium oxide and chromium oxide in order to form synthetic ruby, or else zirconium oxide. In addition, the binder can be of various natures such as, for example, of polymeric types or of organic types.
The method 1 comprises a second step 3 of injecting the precursor into a mould in order to form a green body 12. The mould has substantially the shape of the desired part taking into account a retraction coefficient of the part. The precursor is injected into the mould via a tube, then via circuits for distributing the precursor throughout the mould. The precursor thus takes the shape of the mould, for example a middle of a watch case, as in the examples described in the application. Alternatively, the injection can also be carried out by circular sheet or by channels.
A third step 4 is to machine the green body 12 to remove unnecessary portions of the green body 12 produced by the injection. For example, a tubing 38 or channels 19 formed because of the tube and the distribution circuits are eliminated. Thus, a machined green body 13w is obtained.
The fourth step 5 has the function of sintering said machined green body 13 in order to form a body 14 of the future part from said at least one hard material. Sintering involves heating the precursor so that the powder grains agglomerate. During sintering, the green body 13 hardens by retracting to result in a hard body 14. Preferably according to the invention, the sintering step may include pyrolysis.
An optional fifth step 6 is used to prepare some portions of the body 14 obtained by sintering for the rest of the steps, in particular to prepare the body 10 for the finishing touches.
The method 1 comprises a sixth step 7 of depositing a polymer material coating 16 on one face of the part, the deposition 7 being carried out by overmoulding the body 14, 15, in particular by injection into a mould. A watch case middle is, for example, provided with an inner face 18, which is desired to be covered with a polymer coating 16. The deposition step 7 consists in depositing the coating 16 on said inner face 18. Thus, a hard material part is obtained with a face 18 covered with a polymer material. In this step, the moulding of a polymer material allows to form a coating 16 with more precise dimensions than with a hard material after sintering. Thanks to the method, having to machine the hard material of the part 10 is avoided. It is thus possible to directly form the coating 16 to the appropriate dimensions. Furthermore, the two materials, the hard body and the coating, are assembled inseparably.
The polymer is for example selected from the following list: POM (for polyoxymethylene or polyformaldehyde or polyacetal), PA (for polyamide), PUR (for polyurethane), PPS (for polyphenylene sulphide), ABS (for acrylonitrile butadiene styrene), PC (for polycarbonate).
In a seventh step 8, the polymer material coating 16 can optionally be machined in order to modify some portions, if necessary, in particular to allow the assembly of the other elements of the case.
An eighth step 9 may also be necessary to carry out a satin finishing and/or a polishing of the hard material. Thus, the aesthetic appearance of the middle is improved.
Finally, in a ninth step 11, the part 10 is assembled with other elements by interlocking thanks to the coating 16. For example, if the part 10 is a watch case middle, a watch case 17 is formed by assembling a bezel 21, a crystal 25 and a back to the middle.
In
When there are several injection points, the green body 12 is provided with channels 19 connecting the inner face 18 of the green body at a central crossing 36 arranged at the centre of the inner space. Four perpendicular channels 18 join a tubing 38 orthogonal to the channels 18, the tubing 28 passing through the central crossing 36. The channels 18 and the tubing 38 are produced during the injection step, the precursor being injected into a mould via a tube.
These channels 18 and the tubing 38 are removed during the third step of machining the green body 12 to obtain a machined green body 13 shown in
After the sintering step, the body 14 of
In
After assembly, the watch case 17, shown in
The back 24 of the case 15 is pressed in the coating 16, the coating 16 including a material removal forming a small stair-step 32 to ensure the holding and water resistance of the back 24.
The part 10 comprises a lug 33 on the inner face to prevent the coating from moving in translation or in rotation. The lug 33 is disposed at mid-height of the part 10.
The crown rod 23 passes through the middle through an orifice to reach the crown 22 arranged outside the part 10.
In a variant of the first embodiment, the back covers the coating to conceal it on the lower face of the middle.
A second embodiment of the method consists in forming the back 41 of the case 45 of the same polymer material as the coating 43. The coating 43 and the back 41 are made in one piece and formed during the same deposition step. Thus, the part 40 obtained, shown in
Other parts can be made using the method described above. Thus, for example, it is possible to manufacture a bezel, a back, a stone or a push-piece of a timepiece, as well as a jewellery ring or bracelet, or else a phone case. All these parts include a hard material body provided with a polymer material coating on at least one face.