This application is related to a commonly-assigned copending application Ser. No. 11/556,641, entitled “CARBON NANOTUBE FIELD EMISSION DEVICE AND METHOD FOR MANUFACTURING SAME”, filed Nov. 3, 2006.
1. Field of the Invention
The present invention relates to methods for manufacturing cathode assemblies of field emission displays and, more particularly, to a method for manufacturing a cathode assembly containing carbon nanotubes as electron emitters.
2. Description of Related Art
Field emission displays (FEDs) are a new, rapidly developing kind of flat panel display technology. Compared to conventional technologies, e.g., cathode-ray tube (CRT) and liquid crystal display (LCD) technologies, FEDs are superior in having a wider viewing angle, low energy consumption, smaller size, and higher quality display. In particular, carbon nanotube-based FEDs (CNTFEDs) have attracted much attention in recent years.
Carbon nanotube-based FEDs employ carbon nanotubes (CNTs) as electron emitters. Carbon nanotubes are very small tube-shaped structures essentially composed of a graphite material. That carbon nanotubes can be produced by arc discharge between graphite rods was first discovered and reported in an article by Sumio Iijima, entitled “Helical Microtubules of Graphitic Carbon” (Nature, Vol. 354, Nov. 7, 1991, pp. 56-58). Carbon nanotubes can have an extremely high electrical conductivity, very small diameters (much less than 100 nanometers), large aspect ratios (i.e. with length/diameter ratios potentially greater than 1000), and a tip-surface area near the theoretical limit (the smaller the tip-surface area, the more concentrated the electric field, and the greater the field enhancement factor). Thus, carbon nanotubes can transmit an extremely high electrical current and have a very low electric field electron emission activation voltage (approximately 2 volts/micron). In summary, carbon nanotubes are one of the most favorable candidates for electrons emitters in electron emission devices and can play an important role in field emission display applications.
A conventional cathode assembly includes a cathode supporter and a number of carbon nanotubes used as an electron emitter. The number of carbon nanotubes are formed on the cathode supporter. Conventional methods for forming the carbon nanotubes on the cathodes supporter mainly include a mechanical method and a growing method.
The mechanical method glues the carbon nanotubes on the cathode supporter by chemical adhesive. The mechanical method is simple, but it is more difficult to operate and requires more time. Especially, if the diameter of the carbon nanotubes is less than 1 nm, the mechanical method is impossible to operate.
A conventional growing method is plating a metal catalyst on the cathode supporter, then growing carbon nanotubes directly on the cathode supporter using a chemical vapor deposition method or an arc discharge method. However, for a triode type field emission display, the metal catalyst is plated on the cathode supporter through gate holes defined between every two adjacent gate electrodes, therefore, the length of the metal catalyst is the same as the gate holes. If the carbon nanotubes are grown too high, the carbon nanotubes arranged at the periphery will contact with the gate electrodes and a short circuit takes place between a cathode electrode and the gate electrode. Furthermore, part of the electrons emitted from the carbon nanotubes will be transmitted to the gate electrode to creep and decrease the power utilization efficiency.
What is needed, therefore, is a method for manufacturing a cathode assembly of a high-performance field emission display.
A method for manufacturing a cathode assembly of a field emission display in accordance with a preferred embodiment, includes the steps of: providing a substrate; forming a cathode on the substrate; forming an electrically insulating layer on the cathode; forming a gate electrode layer on the electrically insulating layer; forming a photoresist layer on the electrode layer; defining at least one opening in the photoresist layer using a photolithographic process; etching the gate electrode layer through the at least one opening in the photoresist layer so as to form at least one gate electrode opening in the gate electrode layer; etching the electrically insulating layer to define at least one cavity in the electrically insulating layer; pressing the photoresist layer in a manner such that a size of the at least one opening in the photoresist layer is reduced; depositing a catalyst layer on the substrate in the at least one cavity through the at least one opening; and growing carbon nanotubes on the catalyst layer.
The method deposits the catalyst layer through the at least one opening defined by the pressed photoresist layer. Since the at least one gate electrode opening is larger than the at least one opening in the pressed photoresist layer, the catalyst layer is smaller than the at least one gate electrode opening, and a region of the grown carbon nanotubes from the catalyst layer is smaller than the at least one gate electrode opening. Therefore, the cathode assembly efficiently prevents carbon nanotubes contacting with the gate electrode layer. The probability of shorting between the gate electrode layer and the carbon nanotubes is thus decreased. Furthermore, the probability of electrons emitted from the carbon nanotubes being transmitted to the gate electrode layer is decreased. The method is simple and can be performed without using additional material, and as a result the cost is low.
Other advantages and novel features will become more apparent from the following detailed description of present method for manufacturing a cathode assembly of a field emission display, when taken in conjunction with the accompanying drawings.
Many aspects of the present method for manufacturing a cathode assembly of a field emission display can be better understood with reference to the following drawings. The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the present method for manufacturing a cathode assembly of a field emission display. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.
Reference will now be made to the drawings to describe a preferred embodiment of the present method for manufacturing a cathode assembly of a field emission display, in detail.
Referring to
providing a substrate;
forming a cathode on the substrate;
forming an electrically insulating layer on the cathode;
forming a gate electrode layer on the first electrically insulating layer;
forming a photoresist layer on the gate electrode layer;
defining at least one opening in the photoresist layer using a photolithographic process;
etching the gate electrode layer through the at least one opening in the photoresist layer so as to form at least one gate electrode opening in the gate electrode layer;
etching the electrically insulating layer to define at least one cavity in the electrically insulating layer;
pressing the photoresist layer in a manner such that a size of the at least one opening in the photoresist layer is reduced;
depositing a catalyst layer on the substrate in the at least one cavity through the at least one opening; and
growing carbon nanotubes on the catalyst layer.
Referring to
Alternatively, the substrate 110 may be comprised of transparent conducting material, such as indium tin oxide (ITO) or indium zinc oxide (IZO), etc. In which case the substrate 110 can be directly used as a cathode.
Referring to
The electrically insulating layer 120 is used to form an insulating layer between the cathode 113 and the gate electrode layer 130. The electrically insulating layer 120 can be deposited on the substrate 110 by methods involving evaporation, printing, etc. The electrically insulating layer 120 has a thickness in an approximate range from 1 micrometer to 1000 micrometers. Preferably, the thickness of the electrically insulating layer 120 is in an approximate range from 10 micrometers to 200 micrometers. The electrically insulating layer 120 is comprised of a material capable of resisting high temperatures of about 700 degrees centigrade, such as high temperature glass, silicon, silicon oxide, ceramic, or mica, etc.
The gate electrode layer 130 is insulated from the cathode 113 through the electrically insulating layer 120 and is used to form gate electrodes.
The photoresist layer 140 is formed on the gate electrode layer 130 to be used as a mask.
Referring to
The at least one opening 141 in the photoresist layer 140 is formed and the remaining photoresist layer 140 forms a pattern corresponding to the designed gate electrodes. Advantageously, the remaining photoresist layer 140 has an area corresponding to the designed gate electrodes.
Referring to
The gate electrode layer 130 can be etched using dry etching methods. The photoresist layer 140 can be used as a mask in the dry etching process, and at least one gate electrode opening 131 corresponding to the at least one opening 141 in the photoresist layer 140 can be formed in this way. The obtained gate electrode layer 130 serves as the gate electrodes. The electrically insulating layer 120 can be etched using wet etching methods. The photoresist layer 140 and the gate electrode layer 130 can be used as a mask in the wet etching process, and can be used to define at least one cavity 121. The obtained electrically insulating layer 120 serves as the spacer.
Referring to
The photoresist layer 140 is softened by heating and then is pressed to decrease its thickness and increase its area and the at least one opening 141 in the photoresist layer 140 is reduced as a result. Compared with the at least one gate electrode opening 131, a size of the at least one opening 141 in the photoresist layer 140 is smaller than a size of the gate electrode opening 131.
Referring to
The catalyst layer 170 is comprised of a material selected from a group consisting of iron (Fe), cobalt (Co), nickel (Ni), and any alloys thereof. The catalyst layer 170 has a thickness in an approximate range from 1 nanometer to 10 nanometers. Preferably, the thickness of the catalyst layer 170 is in an approximate range from 3 to 5 nanometers. Furthermore, since the size of the at least one opening 141 in the photoresist layer 140 is smaller than the at least one gate electrode opening 131, the catalyst layer 170 in the at least one cavity 121 is smaller than the at least one gate electrode opening 131.
Referring to
The carbon nanotubes 180 are grown by chemical vapor deposition methods and have an growing area similar to the metal catalyst layers 170. Therefore, the growing area of the carbon nanotubes 180 is smaller than the gate electrode opening 131.
Referring to
Compared with the conventional method for manufacturing the cathode assembly of the field emission display, the present method has many advantages. Since the catalyst layer 170 is deposited through the opening 141 in the photoresist layer 140, the catalyst layer 170 is smaller than the gate electrode opening 131, and the grown carbon nanotubes 180 from the catalyst layer 170 have a growing area smaller than the gate electrode opening 131, therefore the cathode assembly prevents carbon nanotubes 180 from contacting with the gate electrode layer 130. The probability of short circuit between the gate electrode layer 130 and the carbon nanotubes 180 is eliminated. Furthermore, the probability of electron emitted from the carbon nanotubes 180 transmitting to the gate electrode layer 130 is decreased. The method is simple and costs less since no any other material is used and no additional steps are needed.
Referring to
It is to be understood that the above-described embodiment is intended to illustrate rather than limit the invention. Variations may be made to the embodiment without departing from the spirit of the invention as claimed. The above-described embodiments are intended to illustrate the scope of the invention and not restricted to the scope of the invention.
Number | Date | Country | Kind |
---|---|---|---|
2006 1 0061097 | Jun 2006 | CN | national |
Number | Name | Date | Kind |
---|---|---|---|
6062931 | Chuang et al. | May 2000 | A |
6440763 | Hsu | Aug 2002 | B1 |
7081030 | Liu et al. | Jul 2006 | B2 |
7501146 | Lee et al. | Mar 2009 | B2 |
20050236963 | Kang et al. | Oct 2005 | A1 |
20060066217 | Son | Mar 2006 | A1 |
20060275966 | Park et al. | Dec 2006 | A1 |
20070099336 | Weston et al. | May 2007 | A1 |
20100009474 | Kim et al. | Jan 2010 | A1 |
Number | Date | Country |
---|---|---|
1532866 | Sep 2004 | CN |
1585067 | Feb 2005 | CN |
Number | Date | Country | |
---|---|---|---|
20070287350 A1 | Dec 2007 | US |