The present invention relates to a method of manufacturing a gold thread, and more particularly, to a method of manufacturing a gold thread without drawing-induced inconsistency and a gold thread manufactured by the same method, which can secure enough rigidity by being relatively thinner than the thickness of typical gold rods and spirally twisting a plurality of gold rods.
In general, non-surgical procedures are generally being used in cosmetic surgery or plastic surgery which is performed to improve an affected part or to correct a partially damaged part of a human body, instead of surgical procedures.
The non-surgical procedures include non-surgical cosmetic procedures using fillers and non-surgical lifting procedures which are wrinkle removal and skin sagging prevention procedures using sutures. Since sutures formed of synthetic resins used for lifting procedures are decomposed in the body after a certain period of time, periodic re-treatment is needed. Also, since side effects may occur in the human body, a thread formed of gold that can prevent the side effects occurring in the human body is being used in recent years.
As a method for manufacturing the gold thread, Korean Patent No. 10-1450454 discloses “manufacturing apparatus and manufacturing method of gold thread using artificial plastic surgery”. In this patent, a gold rod having the same diameter as the aperture of a die is formed while passing a drawing material formed of gold through the diameter of the die. The gold rod is heated and cooled, and then is cut and compressively rolled to manufacture a gold thread having a certain length.
In addition, since the contact area with the skin is narrow, the skin wrinkle improvement, moisturizing effect and antibacterial properties are deteriorated when using the gold thread.
(Patent Document 1) Korean Patent No. 10-1450454
The present invention provides a method of manufacturing a gold thread without drawing-induced inconsistency and a gold thread manufactured by the same method, which can secure enough rigidity by being relatively thinner than the thickness of typical gold rods and spirally twisting a plurality of gold rods.
The present invention also provides a method of manufacturing a gold thread without drawing-induced inconsistency and a gold thread manufactured by the same method, which can increase the skin anti-aging and antibacterial effect by spirally twisting a plurality of gold rods to form a gold thread and thus increasing the frictional force through a wider surface area than a gold thread of the same diameter.
In one general aspect, a method of manufacturing a gold thread without drawing-induced inconsistency includes:
drawing a gold rod having the same diameter and shape as the aperture of a die while passing a drawing material formed of gold through a die aperture having a diameter of 0.02 mm or less and winding the gold rod on a roller; receiving two strands of gold rod wound on the roller and
twisting the two strands of gold rod;
winding a gold thread twisted with the two strands of gold rod on a roller; and
cutting the gold thread wound on the roller into a certain length, wherein the gold thread cut in the cutting of the gold thread is not bent by twisting the two strands of gold rods.
The gold thread may be twisted with three strands of gold rod.
Other features and aspects will be apparent from the following detailed description, the drawings, and the claims.
According to an embodiment of the present invention, since enough rigidity can be secured by being relatively thinner than the thickness of typical gold rods and spirally twisting a plurality of gold rods, the bending property due to drawing can be improved, and the accuracy can be increased. Accordingly, the defective rate is reduced and thus the productivity can be improved.
In addition, by forming a gold thread by twisting a plurality of gold rods spirally, as the surface area increases compared to gold threads of the same diameter, the frictional force with the skin is increased, and the lifting effect of pulling the skin can be enhanced. Also, the pharmacological action of gold can be promoted to improve skin aging, cell regeneration and growth, regeneration of damaged tissues. In addition, antibacterial property can be increased to prevent occurrence of side effects.
Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings such that those skilled in the art can easily implement the present invention. However, the present invention can be implemented in various forms, and is not limited to embodiments described in this disclosure. Like parts are designated by like reference numerals throughout the specification.
Referring to
A process of manufacturing a gold thread used for a subject who undergoes plastic (cosmetic) procedure or surgery using a gold thread having malleability by forming a gold rod having a diameter of 0.02 mm or less and spirally twisting the gold rod will be described in detail with reference to the above processes.
In operation S110, a god rod having the same diameter and shape as the aperture of a die while passing a drawing material formed of gold through a penetrated aperture of the die. The diameter of the aperture may be about 0.02 mm or less.
At least two of dies may be consecutively disposed such that the diameter gradually decreases. Thus, the diameter of the gold rod is sequentially reduced, and the diameter finally becomes 0.02 mm or less. The gold rod 110 projecting from the aperture of the die is wound on a roller.
In operation S120, the plurality of gold rods 110 wound on the roller in operation S110 are supplied to be twisted. A gold thread 100 may be formed by spirally twisting two strands of gold rod while rotating a gold rod supplied from one roller about a gold rod supplied from the other roller as shown in
In operation S130, the gold threads 100 and 100′ twisted with the plurality of gold rods in operation S120 are wound on the rollers.
In operation S140, the gold thread twisted with the plurality of gold rods and wound on the roller in operation S130 is cut into to a certain length by a cutter. The cutter may be an apparatus that can finely cut the gold thread into a length of about 3 cm to about 7 cm.
If the gold thread is cut to 3 cm or less, the procedure and surgery through the syringe is difficult, and if the length exceeds about 7 cm, it is difficult to work due to too long length.
Since the gold thread cut in operation S140 is twisted with a plurality of gold rods, the density difference between the both ends of the gold rod corresponding to each other in the direction orthogonal to the length direction of the gold rod is offset and thus the gold thread is not bent, thereby improving the flexibility due to the drawing of the gold rod. Thus, the productivity can be improved by removing a work process for straightening the gold thread. Also, since the gold thread can maintain the thread shape of about 0.04 mm even if two or three strands of gold rod having a diameter of about 0.02 mm are spirally twisted, the gold thread can be applied to medical procedures and surgery.
Referring to
In operation S210, a god rod having the same diameter and shape as the aperture of a die while passing a drawing material formed of gold through a penetrated aperture of the die. The diameter of the aperture may be about 0.02 mm or less.
At least two of dies may be consecutively disposed such that the diameter gradually decreases. Thus, the diameter of the gold rod is sequentially reduced, and the diameter finally becomes 0.02 mm or less. The gold rod 110 projecting from the aperture of the die is wound on a roller.
In operation S220, two strands of gold rod wound on each of the rollers in operation S210 are each supplied and twisted. A gold thread 220 twisted with two strands of gold rod may be formed by spirally twisting two strands of gold rod while rotating a gold rod supplied from one roller about a gold rod supplied from the other roller as shown in
In operation S230, the gold thread twisted with two strands of gold rods twisted with two gold rods in operation S220 is wound on a roller.
In operation S240, the gold threads twisted with two strands of gold rod wound on each of the rollers in operation S230 are each supplied and twisted. A gold thread 200 twisted with four strands of gold rod may be formed by rotating a gold thread twisted with two strands of gold rod supplied from one roller about a gold thread twisted with two strands of gold rod supplied from the other roller as shown in
In operation S250, the gold thread twisted with four strands of gold rod by twisting the gold threads twisted with two strands of gold rod in operation S240 is wound on a roller.
In operation S260, the gold thread twisted with four strands of gold rod by twisting the gold threads twisted with two strands of gold rod and wound on the roller in operation S240 is cut into to a certain length by a cutter. The cutter may be an apparatus that can finely cut the gold thread twisted with four strands of gold rod into a length of about 3 cm to about 7 cm.
Since the gold thread cut in operation S260 and twisted with four strands of gold rod is twisted with the gold threads twisted with two strands of gold rods, the density difference between the both ends of the gold rod corresponding to each other in the direction orthogonal to the length direction of the gold thread twisted with four strands of gold rod is offset and thus the gold thread is not bent, thereby improving the flexibility due to the drawing of the gold rod. Thus, the productivity can be improved by removing a work process for straightening the gold thread twisted with four strands of gold rod. Also, since the gold thread can maintain the thread shape of 0.04 mm or less even if four strands of gold rod having a diameter of about 0.02 mm are spirally twisted, the gold thread can be applied to medical procedures and surgery.
When a user threads a needle with gold threads according to an embodiment and another embodiment of the present invention and performs a plastic (cosmetic) procedure or surgery, the surface area is wider than that of a thread having the same diameter and the frictional force with the skin is increased. Accordingly, the effect of the lifting procedure and surgery is increased. Also, it is possible to prevent side effects occurring in the body of a procedure or surgical subject.
In addition, since a gold thread having a diameter of 0.04 mm or less can be formed even if four strands of gold rods are twisted, the amount of gold used can be minimized, thereby reducing costs and improving economic efficiency. Also, since the gold threads formed by twisting a plurality of gold rods can maintain malleability, it is possible to obtain an effect of use that allows the procedure and surgery to proceed smoothly while preventing fracture.
As shown in
A number of exemplary embodiments have been described above. Nevertheless, it will be understood that various modifications may be made. For example, suitable results may be achieved if the described techniques are performed in a different order and/or if components in a described system, architecture, device, or circuit are combined in a different manner and/or replaced or supplemented by other components or their equivalents. Accordingly, other implementations are within the scope of the following claims.
100: gold thread
200: gold thread twisted with four strands of gold rod
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2017-0019566 | Feb 2017 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2018/001649 | 2/7/2018 | WO | 00 |