Patent Application
20080134510
1. Field of the Invention
The present invention relates generally to a method of forming a bearing or a shaft, and more particularly to a method of manufacturing a bearing or a shaft with hydrodynamic pressure generating grooves.
2. Description of Related Art
At present, a plurality of so-called hydrodynamic bearings have been widely used in spindle motors of electronic driving devices, such as compact disc read-only memory (CD-ROM), digital video disc (DVD), hard disks, laser beam printers, floppy disks or other heat-dissipation fans. In the electronic driving devices, it is desired to provide a hydrodynamic bearing with small size, high rotational accuracy and long life.
A typical hydrodynamic bearing comprises a bearing surface defining a bearing hole and a shaft rotatably received in the bearing hole with a bearing clearance formed between an inner circumferential surface of the bearing and an external circumferential surface of the shaft. A plurality of hydrodynamic pressure generating grooves are defined either in the inner circumferential surface of the bearing or in the external circumferential surface of the shaft. The grooves can accommodate lubricant, such as oil. During rotation of the shaft, the lubricant is driven with the rotating shaft due to the viscosity of the lubricant. A lubricating film is thus formed in the bearing clearance between the shaft and the bearing. The shaft is supported under hydrodynamic shearing stress and dynamic pressure generated by the lubricating film. The hydrodynamic bearing has low abrasion as well as long life and low extent of noise because of no radial contact between the shaft and the bearing under hydrodynamic action.
A related method of manufacturing a hydrodynamic bearing 50 showed in
A hydrodynamic bearing having a plurality of hydrodynamic pressure generating grooves defined in an inner surface thereof has been proposed (see US Patent Pub No. US 2006/0051003 A1). Each of the grooves is wedge-shaped in cross section and extends to sides of the bearing in an axial direction. During rotation of the shaft, the lubricant may leak through the sides of the bearing. As a result, the hydrodynamic action of the bearing is weakened. US No. 2006/0002640 A1 discloses a method for manufacturing a composite hydrodynamic bearing. The composite bearing is formed by combining a plurality of bearing blocks. Because the bearing blocks are manufactured separately, the composite bearing can not obtain an accurate size and concentricity. Furthermore, the lubricant is inclined to leak through interfaces between the bearing blocks. Thus the hydrodynamic action of the bearing is weakened.
It is therefore desirable to provide an improved method for mass production of a hydrodynamic bearing with good hydrodynamic properties.
A method for manufacturing a hydrodynamic bearing in accordance with a preferred embodiment of the present invention, comprises the steps of: 1. providing a substrate with a plurality of protrusions formed on a periphery thereof; 2. placing the substrate in a hollow mold, then pushing a feedstock of powder and molten binder into the mold to surround the substrate under pressure, thus forming a desired bearing preform; 3. separating the substrate from the bearing preform by means of debinding; 4. sintering the bearing preform; 5. precision machining the bearing preform to form a desired hydrodynamic bearing.
Other advantages and novel features of the present invention will become more apparent from the following detailed description of preferred embodiment when taken in conjunction with the accompanying drawings, in which:
Many aspects of the present driving device can be better understood with reference to the following drawings. The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the present driving device. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.
Referring to
step 201: providing a substrate 10 with a plurality of protrusions 14 formed on a periphery thereof;
step 202: placing the substrate 10 in a middle of a hollow mold, then pushing a feedstock of powder and molten binder into the mold to surround the substrate 10 under a pressure, thus forming a desired bearing preform;
step 203: separating the substrate 10 from the bearing preform 20 by means of debinding;
step 204: sintering the bearing preform 20;
step 205: performing a precision machining to the bearing preform 20, thereby forming the desired hydrodynamic bearing 30.
The step 201 is described in detail as follows: a material for forming the substrate 10 should meet requirements in the step 202 and the step 203. On one hand, in the step 202, a melting point of the material for forming the substrate 10 is required to be higher than that of the molten binder of the feedstock so that the substrate 10 can keep shape when the molten binder is fed to enclose the substrate 10. On the other hand, in the step 203, the material for forming the substrate 10 should be able to be easily separated from the hydrodynamic bearing preform 20 by means of debinding. For example, a material composed of a kind of paraffin having a high melting point can be provided for forming the substrate 10. Meanwhile, the binder used in the step 202 should be a kind of paraffin having a low melting point. The material for forming the substrate 10 further comprises dispersant, surfactant and additive.
External periphery of the substrate 10 corresponds to an inner surface of the desired hydrodynamic bearing 30. The substrate 10 comprises a cylindrical body 12 and a plurality of herringbone-shaped protrusions 14 formed on a circumferential surface of the body 12. The body 12 is used for forming a bearing hole of the hydrodynamic bearing 30 and the protrusions 14 are used to form the herringbone-shaped grooves 34 of the hydrodynamic bearing 30 which can generate hydrodynamic pressure. Each of the protrusions 14 is spaced from each other.
The substrate 10 can be manufactured by means of injection molding, cast molding or machining. Taking the injection molding as an example, it comprises processes of: (c1) melting the material for forming the desired substrate 10; (c2) injecting the molten material into a mold (not shown) to form the substrate 10; (c3) cooling the mold and taking the substrate 10 out of the mold. The injection molding can be performed in a normal injection machine.
The step 202 is described in detail as follows: the hydrodynamic bearing preform 20 is formed by powder extrusion molding (PEM) or metal injection molding (MIM) according to melting points of the materials of the substrate 10 and the binder. For example, the PEM is applied when the substrate 10 is mainly composed of paraffin with a high melting point and the binder is composed of paraffin with a low melting point. The MIM is applied when the substrate 10 is mainly composed of a kind of plastic having a high melting point. The PEM has many same processes with the MIM as follows: (d1) mixing powder and the binder as a feedstock; (d2) pushing the feedstock to form a desired shape such as the hydrodynamic bearing preform 20 in a mold under a pressure. However, the differences between the PEM and the MIM are that the feedstock of the PEM is extruded to form under a pressure less than 300 Mpa, while the feedstock of the MIM is injected into the mold at a high speed. The feedstock generally comprises metal powder or ceramic powder. The injection machine used in the step 201 for forming the substrate 10 can be used to manufacture the hydrodynamic bearing preform 20 in the step 202. The MIM used to manufacture the hydrodynamic bearing preform 20 has many advantages such as high shape complexity, low cost, tight tolerances, high density, high performance etc.
The step 203 is described in detail as follows: the debinding methods available include solvent and thermal cracking debinding. The thermal cracking debinding is applied when the substrate 10 is mainly composed of the paraffin having a high melting point and the binder in the step 202 is composed of the paraffin having a low melting point. The thermal cracking debinding comprises pressure debinding, vacuum debinding and microwave debinding. The solvent debinding is applied when the substrate 10 is mainly composed of a kind of plastic having a high melting point. The solvent debinding comprises following processes: applying the solvent debinding to the hydrodynamic bearing preform 20 formed in the step 202 to remove the binder in the bearing preform 20 partly out, then applying the thermal cracking debinding to the hydrodynamic bearing preform 20 to remove the substrate 10 out of the hydrodynamic bearing preform 20 completely. It is noted that, the hydrodynamic bearing preform 20 is inclined to break during the thermal cracking debinding because of the difference between a coefficient of expansion of the substrate 10 and that of the hydrodynamic bearing preform 20.
The step 204 is described in detail as follows: after the debinding of the step 203, the binder is moved out from the bearing preform 20; thus the bearing preform 20 becomes loosened. Therefore, it is necessary to sinter the bearing preform 20 in place. The sinter process can be performed in a vacuum, or in an oxygen and/or nitrogen atmosphere.
The step 205 is described in detail as follows: generally, the hydrodynamic bearing preform 20 is inclined to shrink during sintering. In order to make a hydrodynamic bearing preform 20 having a high level of precision in its manufacture, it is necessary to perform a machining operation to the bearing preform 20 using methods such as broaching, grinding, milling, polishing, and so on.
Compared with the related method for manufacturing the hydrodynamic bearing 50, the hydrodynamic bearing 30 is adapted for mass-production by the method in accordance with the preferred embodiment of the present invention. Also, the hydrodynamic bearing 30 manufactured by the present method can provide good hydrodynamic characteristics and reduced leakage. Furthermore, the method in accordance with the preferred embodiment of the present invention can be used for manufacturing other kinds of hydrodynamic bearings or shaft with different shapes of grooves. When applying the method to make a desired shaft with hydrodynamic pressure generating grooves formed in a circumferential surface thereof, a substrate with a central hole defined therein should be provided. An internal surface of the substrate is required to correspond to the circumferential surface of the desired shaft.
It is to be understood that the above-described methods are intended to illustrate rather than limit the invention. Variations may be made to the methods without departing from the spirit of the invention. Accordingly, it is appropriate that the appended claims be construed broadly and in a manner consistent with the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 200610157365.0 | Dec 2006 | CN | national |