The present invention relates to a method for manufacturing microfibrillated polysaccharide, preferably a microfibrillated cellulose, wherein said method is refinerless. The invention also relates to a polysaccharide such as microfibrillated cellulose obtainable from said process and also uses of said polysaccharide.
Microfibrillated cellulose (MFC), which also is known as nanocellulose, is a material typically made from wood cellulose fibers. It can also be made from microbial sources, agricultural fibers, dissolved cellulose or CMC etc. In microfibrillated cellulose the individual microfibrils have been partly or totally detached from each other.
Through WO2013121108 there is disclosed a method for manufacturing an MFC using several passages through a homogenizer and performing this at a pressure of between 200-1000 bars.
Further there is disclosed in WO2007091942 a method for making MFC using a refiner.
There is thus a need for an improved process for providing a microfibrillated polysaccharide with a more homogenous size distribution which in turn may be predicted whereas at the same time the use of a refiner can be abolished and the process may be run at a relatively low pressure.
The present invention solves one or more of the above problems, by providing according to a first aspect a method for manufacturing microfibrillated polysaccharide, preferably a microfibrillated cellulose, comprising the following steps:
The present invention also provides according to a second aspect, a microfibrillated polysaccharide, preferably a microfibrillated cellulose, obtainable by the process according to the first aspect.
The present invention also provides according to a third aspect use of the microfibrillated polysaccharide, preferably a microfibrillated cellulose, according to the second aspect in a strength additive, a thickener, a viscosity modifier, a rheology modifier, a cleaning powder, a washing powder, a detergent, a foam composition, a barrier, a film, a food product, a pharmaceutical composition, a cosmetic product, a paper or board product, a coating, a hygiene/absorbent product, an emulsion/dispersing agent, a drilling mud, a composite material, in water purification, in a filter, in a solar cell, in a battery, in an electronic circuit, or to enhance the reactivity of cellulose in the manufacture of regenerated cellulose or cellulose derivatives.
It is intended throughout the present description that the expression “microfibrillated polysaccharide” embraces any type of microfibrillated cellulose, such as microfibrillated cellulose fibres (cellulose material). The cellulose may also be a microfibrillated cellulose (MFC) or nanocellulose, nanofibrillated cellulose (NFC) or cellulose nanofibrils (CNF). The cellulose may be bleached or unbleached. The cellulose may also be crystalline cellulose, MCC (microcrystallinic cellulose; has high purity need due to its potential use in pharmaceutical compositions or other medical uses), BNC, NCC (nanocrystallinic cellulose; may be used in electrical applications and has magnetical properties), CNC, CMC (carboxymethylated cellulose) or synthetic polymer fibers and fibers made from dissolving pulp. The cellulose may be present in the form of a pulp, which may be chemical pulp, mechanical pulp, thermomechanical pulp or chemi (thermo) mechanical pulp (CMP or CTMP). Said chemical pulp is preferably a sulphite pulp or a kraft pulp. In microfibrillated cellulose the individual microfibrils have partly or fully detached from each other. MFC can be made with different means such as mechanically or chemically or enzymatically, or by using bacteria, or by combining e.g. chemical and mechanical treatment steps.
The pulp initially used in the method according to the first aspect, may consist of pulp from hardwood, softwood or both types. The pulp may e.g. contain a mixture of pine and spruce or a mixture of birch and spruce. The chemical pulps that may be used in the present invention include all types of chemical wood-based pulps, such as bleached, half-bleached and unbleached sulphite, kraft and soda pulps, and mixtures of these. The pulp may be of dissolved type. The pulp may also comprise textile fibers. The pulp may also come from agriculture (e.g. potato, bamboo or carrot).
The present invention also relates to a microfibrillated polysaccharide, such as microfibrillated cellulose, obtainable by the process of the first aspect above. It has been shown that by using the method according to the first aspect of the invention it is possible to obtain size distribution which is narrow and predictable and at the same time abolishing the use of a refiner. In addition said microfibrillated polysaccharide may be manufactured at a relatively low pressure. The size distribution of said microfibrillated polysaccharide will also resemble the distribution of a microfibrillated polysaccharide made through using a process involving a refiner.
A microfibrillated cellulose fibril is further normally very thin (˜20 nm) and the length is often between 100 nm to 10 μm. However, the microfibrils may also be longer, for example between 10-200 μm, but lengths even 2000 μm can be found due to wide length distribution. Fibers that have been fibrillated and which have microfibrils on the surface and microfibrils that are separated and located in a water phase of a slurry are also included in the definition MFC. Furthermore, whiskers are also included in the definition MFC.
The microfibrillated cellulose is typically made from wood cellulose fibers, it is as said possible to use both hardwood and softwood fibers. It can also be made from microbial sources, agricultural fibers, such as wheat straw pulp, bamboo or other non-wood fiber sources. It can also be produced by bacteria or made from CMC.
According to a preferred embodiment of the first aspect of the present invention, the microfibrillated polysaccharide obtained in step f) has a relatively narrow size distribution, preferably wherein the distribution resembles a Gaussian curve, most preferred said curve has its endpoints of the size classes at about from 1 to 5, to about from 100 to 300 μm, respectively, especially preferred whereas at the same time the volume density is from about 9.0 to about 10% at the top of said curve, particularly preferred the Gaussian curve has its endpoints of the size classes at about from 3 to 5 to about from 200 to 300 μm.
According to a preferred embodiment of the first aspect of the present invention the Gaussian curve has its endpoints of the size classes at about 8 to about 100-200 μm at a volume density of about 0.5%, or has its endpoints of the size classes at about from 9 to about from 150-175 μm at a volume density of about 1.0%, or has its endpoints of the size classes at about from 15-20, to 100 μm at a volume density of about 4.0%, or a combination of two of said features or all three, wherein preferably size classes at about 30-40 μm provides a peak for the volume density.
According to preferred embodiment of the first aspect of the present invention the homogenization pressure is about 500 bars or higher, preferably about 700 to about 1000 bars.
According to preferred embodiment of the first aspect of the present invention the pressure in one or more of steps d), e) or f) is kept from about 2 to about 6 bars, preferably about 3 to about 5 bars, most preferred said ranges are applied during step d).
According to preferred embodiment of the first aspect of the present invention the continuous, flowing system of cylindrical geometry is a plug flow reactor. The continuous, flowing system of essentially cylindrical geometry may further be in a multigonal shape (thus having multigonal geometry), such as an octagonal shape.
According to preferred embodiment of the first aspect of the present invention the recirculation of the mixture in step e) is performed at least 5 times before harvesting the microfibrillated polysaccharide.
According to preferred embodiment of the first aspect of the present invention the re-circulation of the mixture in step e) is performed using at least two conveying means, such as pipes, preferably connected to said system and connected sequentially, most preferred interconnected through a pump and optionally additionally one mixing tank.
According to preferred embodiment of the first aspect of the present invention the mixture in the plug flow reactor is kept during from 1 to 5 hours, preferably from 2 to 4 hours, at a temperature from about 50° C. to about 70° C., preferably at about 60° C., and at a pressure from 2 to 6 bars, preferably 3 to 5 bars.
According to preferred embodiment of the first aspect of the present invention said pulp is a sulphite pulp, preferably pulp from softwood.
According to preferred embodiment of the first aspect of the present invention, said enzyme is used at a concentration of from 0.1 to 500 ECU/g fibres, preferably from 0.5 to 250 ECU/g fibres, most preferred 5 to 150 ECU/g fibres, especially preferred from 50 to 150 ECU/g fibres.
According to preferred embodiment of the first aspect of the present invention wherein said enzyme is a hemicellulase or a cellulase or a mixture thereof.
According to preferred embodiment of the first aspect of the present invention wherein said enzyme is a cellulase, preferably a cellulase of endoglucanase type, most preferred a mono-component endoglucanase.
Preferred features of each aspect of the invention are as for each of the other aspects mutatis mutandis. The prior art documents mentioned herein are incorporated to the fullest extent permitted by law. The invention is further described in the following examples, together with the appended figures, the only purpose of which is to illustrate the invention and are in no way intended to limit the scope of the invention in any way.
The method according to the first aspect had only two steps; pulp at 5% or higher solids is mixed with enzyme (ECOPULP® 892—4816, AB Enzymes—previously known as ECOPULP®—R) diluted in water so the final solids of pulp is 4%. Both the pulp and the enzyme solution were kept at 60° C. before mixing. This temperature was then kept for 3 hours without further mixing. The pre-treated material was then homogenized at 700 bars in recirculation mode which increases the temperature to 90° C. thus killing the enzyme and potential microbes. If the temperature reached over 90° C. the material was cooled to avoid boiling. The recirculation vessel would be pressurized and the temperature further increased so steam can be flashed off for energy recovery.
Viscous MFC, (see
Compared to refiner based pre-treatment the time for evaluation of MFC starting materials and enzymes is greatly reduced. This is also due to the reduced recirculation volume in this design that reduces the start-up sequence time essentially.
To summarize a simplified process for the manufacture of MFC was developed and implemented in large lab scale as well as in industrial scale. The simplified solution has beside the homogenizer only two vessels one for the enzyme treatment and one for feeding, recirculation and mixing. The refining section is completely omitted. Enzyme is denatured (inactivated) by the temperature increase to 90° C. during the homogenization step. High or low pH is also possible to use.
The process equipment is easy to clean and the temperature increase ensures microbial purity of the product.
Scalability is judged to be improved compared with the current process solution due the simplification and so is the ability to keep the process at high hygienic standard.
In view of the above detailed description of the present invention, other modifications and variations will become apparent to those skilled in the art. However, it should be apparent that such other modifications and variations may be effected without departing from the spirit and scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1451287 | Oct 2014 | SE | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2015/058238 | 10/26/2015 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2016/067180 | 5/6/2016 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4374702 | Turbak et al. | Feb 1983 | A |
| 20110277947 | Hua et al. | Nov 2011 | A1 |
| 20140124150 | Sabourin et al. | May 2014 | A1 |
| 20140127756 | Bolz et al. | May 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 2196579 | Jun 2010 | EP |
| 2007091942 | Aug 2004 | WO |
| 2011004301 | Jan 2011 | WO |
| 2014029909 | Feb 2014 | WO |
| Entry |
|---|
| International Search Report for PCT/IB2015/058238, dated Feb. 25, 2016. |
| Lavoine, N. et al “Microfibrillated Cellulose—Its barrier properties and applications in cellulosic materials: a review”, Carbohydrate Polymers, 2012, pp. 735-764, vol. 90. |
| Henriksson, M. et al “An environmentally friendly method for enzyme-assisted preparation of microfibrillated cellulose (MFC) nanofibers”, European Polymer Journal, 2007, pp. 3434-3441, vol. 43. |
| Pääkkö, M. et al “Enzymatic Hydrolysis Combined with Mechanical Shearing and High-pressure Homogenization for Nanoscale Cellulose Fibrils and Strong Gels”, Biomacromolecules, 2007, pp. 1934-1941, vol. 8. |
| Siqueria, Gilberto, et al., “Morphological Investigation of Nanoparticles Obtained from Combined Mechanical Shearing, and Enzymatic and Acid Hydrolysis of Sisal Fibers,” Cellulose (2010), vol. 17, pp. 1147-1158. |
| Number | Date | Country | |
|---|---|---|---|
| 20170320969 A1 | Nov 2017 | US |