1. Technical Field
The present invention relates to a method for manufacturing an optical element, a method for manufacturing a projector, an optical element and a projector.
2. Related Art
In a projector having a liquid crystal device as an optically modulating device, a polarization plate is disposed in at least one of a light-incident side and a light-emission side of the liquid crystal device. The polarization plate that is a two or three-layered lamination, having a polarization layer comprising polyvinyl alcohol (PVA) and at least one supporting layers comprising triacetyl cellulose (TAC) laminated in one side or both sides of the PVA for purpose of enhancing mechanical strength thereof is a well-known example of the polarization plate (see JP-A-7-20317). The supporting layer comprising TAC is excellent in transparency, uniformity and planarity and has very little anisotropic. Accordingly, the supporting layer comprising TAC is widely used for a supporting layer in order to support the polarization layer.
Meanwhile, in a projector of a related art, a light that does not pass through the polarization plate gives rise to an increase in temperature of the polarization plate because the light is absorbed in the polarization plate to generate a considerable amount of heat. Consequently, the projector of the related art has some disadvantages such that a display quality of a projection image is lowered. For example, the polarization characteristics of the polarization plate are deteriorated, the contrast of the projection image is lowered, and an uneven contrast or an uneven color is generated.
Therefore, a projector having an optical element comprising a light transmissive member having a thermal conductivity that is adhered to both sides of the polarization plate (namely, outer surface of the supporting layer of the polarization plate) is provided in order to solve the problem of the projector of the related art (see JP-A-2000-112022). In the projector, the heat generated in the polarization plate is emitted outside of the projector through the light transmissive member having a thermal conductivity so that the increase of the temperature of the polarization plate may be avoided. Therefore, the deterioration of the polarization plate may be prevented and accordingly, the polarization characteristic of the polarization plate may not be lowered. Accordingly, a projector having the optical element may enhance the display quality of the projection image.
Meanwhile, recently, the demand for a projector for use in electric home appliances having a projector, such as a home theater system is increased. Consequently, it is more required for the projector to have an improved quality of the projection image. However, in a projector of a related art, which uses a material having an optical axis as a light transmissive member having a thermal conductivity, the polarization state of a light which passes through the light transmissive member and is incident on the polarization plate or the polarization state of a light which passes through the polarization plate and is incident on the light transmissive member may be varied if an optical axis of the light transmissive member and a polarization axis of the polarization plate do not have a desired positional relationship therebetween. Accordingly, the contrast of the projection image may be decreased, and the temperature of the polarization plate may be increased so that the display quality of the projection image is lowered. In addition, in the projector of the related art, an incident side polarization plate is disposed on a light-incident side of the liquid crystal device and an emission side polarization plate is disposed on a light-emission side of the liquid crystal device, in order that the incident side polarization plate and the emission side polarization plate are in a so-called crossed Nicols state. Herein, if the incident side polarization plate and the emission side polarization plate are not placed in an optimal rotational position, the contrast of the projection image may be decreased, or the temperature of the emission side polarization plate may be increased so that the display quality of the projection image is lowered.
An advantage of some aspects of the invention is to provide a method for manufacturing an optical element and a method for manufacturing a projector where the display quality of the projection image can be improved. Another advantage of some aspects of the invention is to provide an optical element and a projector manufactured according to the methods.
The invention is based on an idea that if a polarization plate and a light transmissive member are adhered to each other in an optimal rotation position, then the display quality of a projection image is increased. Also, the idea that if the polarization plate on the light-incident side and the polarization plate on the light-emission side are positioned in the optimal rotation position, then the quality of the projection image is increased inspired the invention.
According to an aspect of the invention, there is provided a method for manufacturing an optical element having a light transmissive member having an optical axis thereof, and a polarization plate having at least a polarization layer, in which the light transmissive member is bonded to one side of the polarization plate used to manufacture an optical element. The method includes: preparing a light source, the polarization plate, the light transmissive member, a certificating polarization plate and a spectrophotometer; arranging the light transmissive member between the polarization plate and the certificating polarization plate so that the polarization plate and the certificating polarization plate are in a crossed Nicols state, and the polarization plate, the light transmissive member and the certificating polarization plate are arranged between the light source and the spectrophotometer in an order such that a light from the light source is incident on the polarization plate, passes through the polarization plate, the light transmissive member and the certificating polarization plate, and is incident on the spectrophotometer, or in an order such that a light from the light source is incident on the certificating polarization plate, passes through the certification polarization plate, the light transmissive member and the polarization plate, and is incident on the spectrophotometer; measuring a light transmittance spectrum with respect to each rotational position of the light transmissive member within a predetermined wavelength of light incident on the spectrophotometer while the light transmissive member is rotated relative to an axis that is parallel to a central axis of a light transmitting the light transmissive member; determining a rotational position of the light transmissive member based on a measured result of the light transmittance spectrum measured in the measuring of the light transmittance spectrum such that yields a smallest value for a difference between a minimum value and a maximum value of the light transmittance spectrum; and bonding the light transmissive member to the polarization plate at the rotational position of the light transmissive member that is determined in the determining the rotational position.
Therefore, in the method according to the aspect of the invention, the light transmissive member is rotated and a light transmittance spectrum of a light is measured with respect to each rotational position. Based on the measured result of the light transmittance spectrum with respect to each rotational position, the rotational position of the light transmissive member is determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum. The polarization plate and the light transmissive member are bonded at the determined relative rotational position so that the polarization axis of the polarization plate may be adjusted to be parallel to or orthogonal to the optical axis of the light transmissive member with higher precision. Accordingly, the variation of the polarization state of a light when transmitting the optical element may be prevented or reduced. As a result, the degradation of display quality of a projection image may be prevented or reduced.
Therefore, in the method according to the aspect of the invention, it is possible to manufacture an optical element having an improved display quality of projection image.
According to another aspect of the invention, there is provided a method for manufacturing an optical element having a second light transmissive member bonded to a second surface opposing to a first surface of the polarization plate where the light transmissive member is bonded. The method includes: preparing the second light transmissive member; second arranging the second light transmissive member between the polarization plate and the certificating polarization plate so that the to polarization plate and the certificating polarization plate are in a crossed Nicols state, and the polarization plate, the second light transmissive member and the certificating polarization plate are arranged between the light source and the spectrophotometer in an order such that a light from the light source is incident on the polarization plate, passes through the polarization plate, the second light transmissive member and the certificating polarization plate, and is incident on the spectrophotometer, or in an order such that a light from the light source is incident on the certificating polarization plate, passes through the certificating polarization plate, the second light transmissive member and the polarization plate, and is incident on the spectrophotometer; second measuring a light transmittance spectrum with respect to each rotational position of the second light transmissive member within a predetermined wavelength of light incident on the spectrophotometer while the second light transmissive member is rotated relative to an axis that is parallel to a central axis of a light transmitting the second light transmissive member; second determining a rotational position of the second light transmissive member based on a measured result of the light transmittance spectrum measured in the measuring of the second light transmittance spectrum such that yields a smallest value for a difference between a minimum value and a maximum value of the second light transmittance spectrum; and second bonding the second light transmissive member to the polarization plate at the rotational position of the second light transmissive member that is determined in the determining of the second rotational position.
Thus when the polarization plate that is bonded to the light transmissive member and the second light transmissive member are bonded together, similar to a case where the light transmissive member is bonded to the polarization plate, the second light transmissive member is rotated and a light transmittance spectrum of a light is measured with respect to each rotational position. Based on the measured result of the light transmittance spectrum with respect to each rotational position, the rotational position of the second light transmissive member is determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum. The polarization plate and the second light transmissive member are bonded at the determined relative rotational position so that the polarization axis of the polarization plate may be adjusted to be parallel to or orthogonal to the optical axis of the second light transmissive member with higher precision. Accordingly, the variation of the polarization state of a light when transmitting the optical element may be prevented or reduced. As a result, the degradation of display quality of a projection image may be prevented or reduced.
Therefore, in the method for manufacturing an optical element according to another aspect of the invention, it is possible to manufacture an optical element having an improved display quality of projection image.
In the method for manufacturing an optical element, a polarization axis of the polarization plate and an optical axis of the light transmissive member, or the polarization axis of the polarization plate and an optical axis of the second light transmissive member may be adjusted with a precision level equal to or less than 0.5 degree. The precision level equal to or less than 0.5 degree is a precision level that is not easily achieved when measuring a light transmittance in the measuring of the light transmittance using a light of a single wavelength or in the measuring of the light transmittance using a light of a wideband wavelength as it is.
In the method for manufacturing an optical element, at least one of the light transmissive member and the second light transmissive member may use, for example, a light transmissive substrate comprising sapphire or quartz.
In the method for manufacturing an optical element, the light transmissive member and the polarization plate, or the second light transmissive member and the polarization plate are bonded together using a pressure sensitive adhesive. Alternatively, the light transmissive member and the polarization plate, or the second light transmissive member and the polarization plate may be bonded together using an adhesive. Herein, a UV curable adhesive or a visible ray short wavelength curable adhesive may be used as the adhesive.
According to another aspect of the invention, there is provided a method for manufacturing a projector having a light source device for emitting a luminous flux, a liquid crystal device for modulating the luminous flux emitted from the light source according to image information, a projecting optical system for projecting a light modulated by the liquid crystal device, an incident side polarization plate having at least polarization layer, arranged on a light-incident side of the liquid crystal device and an emission side polarization plate having at least polarization layer, arranged on a light-emission side of the liquid crystal device. Here, the method includes: arranging the polarization plate in which the incident side polarization plate and the emission side polarization plate are respectively arranged on the light-incident side and the light-emission side of the liquid crystal device proper polarization relationship therebetween; and arranging a spectrophotometer on the light-emission side of the liquid crystal device prior to performing the arranging of the polarization plate. The arranging of the polarization plate includes a first process in which the incident side polarization plate and the emission side polarization plate are in a crossed Nicols state, and the incident side polarization plate, the liquid crystal device and the emission side polarization plate are disposed in an order such that a light emitted from the light source passes through the incident side polarization plate, the liquid crystal device and the emission side polarization plate and is incident on the spectrophotometer; a second process in which at least one of the incident side polarization plate and the emission side polarization plate is rotated relative to an axis parallel to a central axis of a light transmitting the liquid crystal device to vary an angle between a polarization axis of the incident side polarization plate and a polarization axis of the emission side polarization plate, and a light transmittance spectrum of a light, that is incident on the spectrophotometer in a predetermined wavelength, is measured at respective rotational position; a third process in which a relative rotational position for the incident side polarization plate and the emission side polarization plate is determined based on a measured result of the light transmittance spectrum at respective rotational position, the relative rotational positions providing a smallest value for a difference between a maximum value and a minimum value of the light transmittance spectrum; and a fourth process in which the incident side polarization plate and the emission side polarization plate are fixed to maintain the relative rotational position for the incident side polarization plate and the emission side polarization plate.
Therefore, in the method for manufacturing a projector according to the aspect of the invention, at least one of the polarization plate on a light-incident side and the polarization plate on a light-emission side is rotated and a light transmittance spectrum with respect to respective rotational position is measured. Based on the measured result of the light transmittance spectrum, relative rotational positions of the polarization plate on the light-incident side and the polarization plate on the light-emission side are determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum. The polarization plate on the light-incident side and the polarization plate on the light-emission side are bonded at the determined relative rotational position so that it is prevented or reduced that a light that is to pass through the polarization plate on the light-emission side is absorbed by the polarization plate, or a light that is to be absorbed by the polarization plate on the light-emission side passes through the polarization plate. In addition, lowering in contrast of a projection image, an uneven brightness, or an uneven color may be prevented or reduced. As a result, the deterioration of display quality of a projection image may be prevented or reduced.
Therefore, in the method for manufacturing a projector according to the aspect of the invention, it is possible to manufacture a projector having improved display quality of a projection image.
In the method for manufacturing a projector according to the aspect of the invention, a polarization axis of a polarization plate on the light-incident side and a polarization axis of a polarization plate on the light-emission side may be adjusted with a precision level equal to or less than 0.5 degree. The precision level equal to or less than 0.5 degree is a precision level that is not easily achieved when measuring a light transmittance using a light of a single wavelength or in measuring transmittance using a light of a wideband wavelength as it is.
The method for manufacturing a projector according to further aspect of the invention may also be used to manufacture a projector having a plurality of liquid crystal devices.
According to another aspect of the invention, there is provided an optical element which is manufactured using the method for manufacturing an optical element of the aspect of the invention.
Therefore, the optical element according to the aspect of the invention has enhanced display quality of a projection image.
According to another aspect of the invention, there is provided a projector which is manufactured using the method for manufacturing a projector of the aspect of the invention.
Therefore, the projector according to the aspect of the invention has enhanced display quality of a projection image.
The invention will be described with reference to the accompanying drawings, wherein like numbers reference like elements.
Hereinafter, preferred embodiments of the invention will be described with reference to the accompanying drawings.
First, a configuration of a projector according to a first embodiment will be described with reference to
The projector 1000 according to the first embodiment, as shown in
The lighting device 100 includes a light source device 110 that serves as a light source for emitting substantially parallel luminous fluxes to the illuminated area, a first lens array 120 having a first plurality of small lenses 122 that divides the luminous flux emitted from the light source device 110 into a partial luminous flux, a second lens array 130 having a second plurality of small lenses 132 corresponding to the first plurality of small lenses 122, a polarization converting element 140 that aligns the luminous flux emitted from the light source device 110, of which polarization direction is not aligned to approximately one straight polarized light, and a superposed lens 150 that superpose respective partial luminous flux emitted from the polarization converting element 140 on an illuminated area.
The light source device 110 includes an ellipsoid reflector 114 as a reflector, a luminary conduit 112 that emits a light near a first focus of the ellipsoid reflector 114, a subsidiary mirror 116 that has a reflection surface facing a concave surface of the ellipsoid reflector 114, and a concave lens 118 that converts a collected light that is reflected by the ellipsoid reflector 114 to a parallel light. The light source device 110 emits a luminous flux with an illumination optical axis 100ax as the central axis.
The luminary conduit 112 has an aperture, and a pair of encapsulation units that extend toward both sides of the aperture.
The ellipsoid reflector 114 has a tube-shaped image receiving unit that is passed through and fixed to one encapsulation unit of the luminary conduit 112, and a reflection concave surface that reflects a light radiated from the luminary conduit 112 toward a second focus.
The subsidiary mirror 116 is passed through and fixed to the other encapsulation unit of the luminary conduit 112, and is configured to face the ellipsoid reflector 114 when being inserted into the luminary conduit 112. Also, the subsidiary mirror 116 reflects a light, which is radiated from the luminary conduit 112 and is not directed to the ellipsoid reflector 114, back to the luminary conduit 112 so that the light may be incident on the ellipsoid reflector 114.
The concave lens 118 is positioned in the illuminated area of the ellipsoid reflector 114. In addition, the concave lens 118 is configured to adjust the light emitted from the ellipsoid reflector 114 to a parallel light.
The first lens array 120 functions as a luminous flux division optical element that divides a light emitted from the concave lens 118 into a plurality of partial luminous fluxes. The first lens array 120 includes the first plurality of small lenses 122 that are arranged in a matrix shape on a surface substantially orthogonal to the illumination optical axis 100ax. Although not shown in the figure, the first plurality of small lenses 122 have an external shape that are similar to an external shape of an image forming area of the respective liquid crystal devices 410R, 410G and 410B.
The second lens array 130 is an optical element that collects the plurality of partial luminous fluxes that are divided by the first lens array 120. Similar to the first lens array 120, the second lens array 130 has a second plurality of lenses 132 that are arranged in a matrix shape on a surface substantially orthogonal to the illumination optical axis 100ax.
The polarization converting element 140 adjusts the polarization direction of each partial luminous flux from the first lens array 120 to emit a straight polarized light of approximately one kind.
The polarization converting element 140 has a polarization separation layer, a reflection layer and a phase difference plate. The polarization separation layer penetrates a first straight polarization component among polarization components in the luminous flux received from the light source device 110 to reflect a second straight polarization component in a direction orthogonal to the illumination optical axis 100ax. The reflection layer reflects the second straight polarization component reflected by the polarization separation layer in a direction parallel to the illumination optical axis 100ax. The phase difference plate converts the second straight polarization component reflected by the polarization separation layer into the first straight polarization component.
The superposed lens 150 is used to collect the plurality of the partial luminous fluxes passing through the first lens array 120, the second lens array 130 and the polarization converting element 140, to superpose the collected partial luminous fluxes on the vicinity of the image forming area of the liquid crystal devices 410R, 410G and 410B. In addition, the superposed lens 150 illustrated in
The color division light-guiding optical system 200 includes dichroic mirrors 210, 220, reflection mirrors 230, 240, 250, an incident side lens 260 and a relay lens 270. The color division light-guiding optical system 200 divides the luminous flux emitted from the superposed lens 150 into three color lights of a red light, a green light and a blue light, and guides the respective color lights to the three liquid crystal devices 410R, 410G and 410B that are to be illuminated.
The dichroic mirrors 210, 220 are optical elements where wavelength selection films are formed, wherein the wavelength selection films passes a luminous flux of a determined wavelength and reflects a luminous flux of other predetermined wavelength. The dichroic mirror 210 may reflect a red light component while other color light components penetrate therethrough. The dichroic mirror 220 may reflect a green light component while a blue light component penetrates therethrough.
The red light component reflected by the dichroic mirrors 210 is diffracted by the reflection mirror 230, and is incident on the imaging forming area of the liquid crystal device 400R for the red light through a light collecting lens 300R.
The light collecting lens 300R is used to convert each partial luminous flux received from the superposed lens 150 to a luminous flux that is approximately parallel to a respective principle light. The light collecting lens 300R is maintained by a maintaining member (not shown) that is thermal conductive, and is arranged in the case 10 through the thermal-conductive maintaining member. Light collecting lenses 300G and 300B that are arranged in a front end of an optical path of the liquid crystal devices 410G and 410B have substantially the same structure.
The green light component passing through the dichroic mirror 210 is reflected by the dichroic mirror 220, transmits the light collecting lens 300G and is incident on the imaging forming area of the liquid crystal device 410G for the green light. Meanwhile, the blue light component passing through the dichroic mirror 210 transmits the dichroic mirror 220, incident side lens 260, the reflection mirror 240 on the light-incident side, the relay lens 270, the reflection lens 250 on the light-emission side and the light collecting lens 300B and is incident on the image forming area of the liquid crystal device 410B for the blue light. The incident side lens 260, the relay lens 270 and the reflection mirrors 240 and 250 function to guide the blue light component passing through the dichroic mirror 220 to the liquid crystal device 410B.
In addition, since the blue light has an optical path that is longer than the other color lights, the incident side lens 260, the relay lens 270 and the reflection mirrors 240 and 250 are placed on an optical path of the blue light so as to prevent a lowering of the efficiency in using a light by, for example, light diversion. Thus, the projector 1000 in the first embodiment is configured considering the fact that the blue light has a longer optical path; however, the incident side lens 260, the relay lens 270 and the reflection mirrors 240 and 250 may be placed on an optical path of the red light in alternative implementation.
The liquid crystal devices 410R, 410G and 410B are used to modulate a luminous flux according to image information, and are an object of illumination of the lighting device 100.
The liquid crystal devices 410R, 410G and 410B have liquid crystal, that is an electro-optical substance, sealed by a pair of transparent glass substrates, to modulate a polarization direction of a straight polarization light of one kind emitted from the light-incident side polarization plates 420R, 420G and 420B based on a given image signal using a switching element, for example, a poly silicon TFT. Although the liquid crystal devices 410R, 410G and 410B are not illustrated in the figure, the liquid crystal devices 410R, 410G and 410B may be maintained in a maintaining frame that is a die-cast frame composed of aluminum.
The polarization plates 420R, 420G and 420B are respectively disposed on the light-incident side of the liquid crystal devices 410R, 410G and 410B as illustrated in
As illustrated in
The light transmissive members 430R, 430G and 430B are arranged close to the liquid crystal devices, namely on the light-emission side of the polarization plates 420R, 420G and 420B. A reflection preventing layer (not shown) is formed on the light transmissive members 430R, 430G and 430B close to the liquid crystal devices. The light transmissive members 430R, 430G and 430B are light transmissive substrates comprising, for example, sapphire. Then the light transmissive substrate comprises sapphire, the light transmissive substrate has a higher thermal conductivity of about 40 W/((m·K), a higher degree of hardness, a lower thermal expansion coefficient, a higher degree of transparency, and is hard to crack. In addition, to lower the cost while achieving an average brightness, the light transmissive substrate comprising quartz having a thermal conductivity of about 10 W/(m·K) may be used. It is preferable that the light; transmissive members 430R, 430G and 430B have a thickness of more than 0.2 mm in consideration of the thermal conductivity, and have a thickness of less than 2.0 mm in consideration of manufacturing of a compact and small-sized device.
As illustrated in
The adhesive layer C is formed to surround the light-incident side polarization plates 420R, 420G and 420B. An adhesive for use as the adhesive layer C may be, for example, a UV curable adhesive or a visible ray short wavelength curable adhesive.
As illustrated in
The light-emission side polarization plate 440R, as illustrated in
Light transmissive members 450R, 450G and 450B are respectively arranged on the light-emission side polarization plates 440R, 440G and 440B close to the liquid crystal devices. A reflection preventing layer (not shown) is formed on the light transmissive members 450R, 450G and 450B close to the liquid crystal devices. The light transmissive members 450R, 450G and 450B may be a light transmissive substrate comprising sapphire similar to the light transmissive members 430R, 430G and 430B.
As illustrated in
The adhesive layer C is formed to cover the light-emission side polarization plates 440R, 440G and 440B.
The polarization plates 420R, 420G and 420B on the light-incident side are set up and arranged in such a manner that a polarization axis of the polarization plates 420R, 420G and 420B on the light-incident side is orthogonal to that of- the polarization plates 440R, 440G and 440B on the light-emission side.
The cross dichroic prism 500 is an optical element that combines respective modulated optical image of each color light emitted from the polarization plates 440R, 440G and 440B on the light-emission side. As illustrated in
The cross dichroic prism 500 is arranged in the case 10 through a spacer 12 having a thermal conductivity (refer to
A color image emitted from the cross dichroic prism 500 is enlarged and projected by the projecting optical system 600 to form a large screen image on the screen SCR.
In addition, although not illustrated in the figure, the projector 1000 may include at least one fan for cooling respective optical system and a plurality of flow paths for cooling air. An air coming into the projector 1000 from an outside circulate through the projector 1000 by the fan and the plurality of flow paths for cooling air and then discharged from the projector 1000. As illustrated in
Accordingly, heat may be efficiently removed from respective optical system of the projector 1000.
Next, a method for manufacturing an optical element according to the first embodiment will be described with reference to
In addition, ‘0 degree’ in the light transmittance spectrum of
The method for manufacturing the optical element according to the first embodiment is used to manufacture an optical element having a structure such that the polarization plates 420R, 420G and 420B on the light-incident side have the light transmissive members 430R, 430G, 430B respectively bonding to a first surface thereof and to manufacture an optical element having a structure such that the polarization plates 440R, 440G and 440B on the light-emission side have the light transmissive members 450R, 450G, 450B respectively bonding to a first surface thereof. In the method, ‘1. a preparing process’, ‘2. an arranging process’, ‘3. a light transmittance spectrum measuring process’, ‘4. a rotational position determining process’ and ‘5. a bonding process’ are subsequently performed. Each of the process will be described below. For illustrative purposes, the optical element manufactured by the method has a structure such that the light transmissive member 430R is bonded to one side of the light-incident side polarization plate 420R.
1. Preparing Process
First, a light source 710, a polarization plate 420R on a light-incident side, a light transmissive member 430R, a certificating polarization plate 720 and a spectrophotometer 700 are prepared (step S10 in
2. Arranging Process
As illustrated in
3. Light Transmittance Spectrum Measuring Process
Next, the light transmissive member 430R is rotated relative to an axis that is parallel to a central axis of a light transmitting the light transmissive member 430R. With respect to each rotational position of the light transmissive member 430R, the light transmittance spectrum of the light within a predetermined wavelength that is incident on the spectrophotometer 700 is measured (step S14 in
4. Rotation Position Determining Process
Next, based on a measured result of the light transmittance spectrum at each rotational position of the light transmissive member 430R in the ‘3. light transmittance spectrum determining process’, the rotational position of the light transmissive member 430R is determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum (step S16 of
The detailed explanation of the ‘3. light transmittance spectrum measuring process’ and ‘4. rotation position determining process’ with reference to
In a method for manufacturing an optical element according to the first embodiment, as illustrated in
In a method for manufacturing an optical element according to the first embodiment, when the optical axis of the light transmissive member 430R is parallel to the polarization axis of the light-incident side polarization plate 420R, the light transmittance spectrum of a lights which is emitted from the certificating polarization plate 720, measured in the spectrophotometer 700 is represented as a full line in
As described above, the light transmittance spectrums represented as a full line, a dashed line or a line with dot in
As described above, an angle between the optical axis of the light transmissive member 430R and a polarization axis of the light-incident side polarization plate 420R is closely related with the difference between the maximum value and the minimum value of the light transmittance with respect to a wavelength having a predetermined range. Thus, as illustrated in
In addition, in a method for manufacturing an optical element according to the first embodiment, it is possible to adjust the optical axis of the light transmissive member 430R and the polarization axis of the light-incident side polarization plate 420R with precision level of equal to or less than 0.5 degree.
5. Bonding Process
In addition, as illustrated in
As described above, an optical element having a structure such that the light transmissive member 430R is bonded to one side of the light-incident side polarization plate 420R may be manufactured. Like this manner, an optical element having a structure such that the light transmissive members 430G and 430B are respectively bonding to the light-incident side polarization plates 420G and 420B may be manufactured. Also, an optical element having a structure such that the light-transmissive members 440R, 440G and 440B are bonded to the light-incident side polarization plates 450R, 450G and 450B may be manufactured.
As described above, a manufacturing method of an optical element according to the first embodiment may be used to manufacture an optical element having a structure such that the light transmissive member is bonded to one side of the light-incident side polarization plate. In addition, it is also described above that a manufacturing method of an optical element according to the first embodiment includes a preparing process, an arranging process, a light transmittance spectrum measuring process, a rotational position determining process and a bonding process.
Consequently, according to a manufacturing method of an optical element related to the first embodiment, the light transmittance spectrum in each rotational position is measured while rotating the light transmissive member and, based on the measured light transmittance spectrum, a rotational position of the light transmissive member, which yields a smallest value for the difference between the maximum value and the minimum value of the light transmittance spectrum is determined. The polarization plate and the light transmissive member are bonded to each other at the determined rotational position of the light transmissive member. Therefore, it is possible to adjust a relative position between the polarization plate and the light transmissive member with high precision, in order that the polarization axis of the polarization layer of the polarization plate is parallel or orthogonal to the optical axis of the light transmissive member. Accordingly, the variation of the polarization state when a light transmits an optical element may be prevented or reduced. That is, the variation of the polarization state of a light that is emitted from the light-incident side polarization plate 420R, 420G, or 420B when transmitting the light transmissive member 430R, 430G, or 430B. In addition, the variation of the polarization state of a light that is emitted from the liquid crystal device 400R, 400G or 400B when transmitting the light transmissive member 450R, 450G, or 450B. As a result, the degradation of the display quality of the projection image may be prevented or reduced.
Therefore, according to a manufacturing method of an optical element of the first embodiment, an optical element which may improve the display quality of the projection image may be manufactured.
Next, a method for manufacturing a projector to the first embodiment will be described with reference to
The process of manufacture of the first embodiment is for purpose of manufacturing the projector 1, and in the method, ‘1. a process of arranging spectrophotometer’ and ‘2. a process of arranging polarization plate’ are subsequently performed. Each of the process is described below.
1. Process of Arranging Spectrophotometer
First, as shown in
2. Process of Arranging Polarization Plate
Next, as shown in
In addition, the light transmissive members 430R, 430G, 430B, 450R, 450G, 450B are respectively adhered to the polarization plates 420R, 420G, 420B on the light-incident side and the side polarization plates 440R, 440G, 440B on the light-emission side by the method for manufacturing an optical element according to the first embodiment.
The ‘2. process of arranging polarization plate’ includes ‘2-1. a first process’, ‘2-2. a second process’, ‘2-3. a third process’ and ‘2-4. a fourth process’. The respective process is described below. For illustrative purposes, the description is made as regarding the polarization plate 420R on the light-incident side arranged on an optical path of the red light among the tree color lights, the liquid crystal device 410R and the polarization plate 440R on the light-emission side.
2-1. First Process
The light-incident side polarization plate 420R, the liquid crystal device 410R and the light-emission side polarization plate 440R are disposed between the light source device 110 and the spectrophotometer 700 in an order such that a light emitted from the light source device 110 passes through the light-incident side polarization plate 420R, the liquid crystal device 410R and the light-emission side polarization plate 440R, and is incident on the spectrophotometer 700 (step S210 in
2-2. Second Process
Next, at least one of the polarization plate 420R on the light-incident side or the polarization plate 440R on the light-emission side is rotated relative to an axis that is parallel to a central axis of a light transmitting the liquid crystal device 410R to vary an angle between an optical axis of the polarization plate 420R on the light-incident side and the polarization plate 440R on the light-emission side. With respect to each rotational position thereof, the light transmittance spectrum of a light within a predetermined wavelength that is incident on the spectrophotometer 700 is measured (step S212 in
In addition, in a method for manufacturing an optical element according to the first embodiment, it is possible to adjust the optical axis of the light-incident side polarization plate 420R and the polarization axis of the light-emission side polarization plate 440R with precision level of equal to or less than 0.5 degree.
2-3. Third Process
Next, based on the light transmittance spectrum measured in ‘2-2. second process’ with respect to respective rotational position of the polarization plate 420R on light-incident side and the polarization plate 440R on the light-emission side, a relative rotational position of the polarization plate 420R on the light-incident side and the polarization plate 440R on the light-emission side is determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum (S214 in
2-4. Fourth Process
In addition, positions of the light-incident side polarization plate 420R and the light-emission side polarization plate 440R are fixed in order to maintain the relative rotational position of the light-incident side polarization plate 420R and the light-emission side polarization plate 440R determined in ‘2-3. third process’ (step S216 in
Moreover, in a manufacturing method of a projector according to the first embodiment, the rotational position of the light-incident side polarization plate 420R is fixed by bonding the light-incident side polarization plate 420R to the light-emission side of the light collecting lens 300R, and the rotational position of a light-emission side polarization plate 440R is fixed by bonding the light-emission side polarization plate 440R to the light-incident section of red light of the cross dichroic prism 500.
The ‘2-1. a first process’ through ‘2-4. a fourth process’ are performed regarding the light-incident side polarization plate 420R and the light-emission side polarization plate 440R disposed in an optical path of a red light. Like this manner, the ‘2-1. a first process’ through ‘2-4. a fourth process’ are performed regarding the light-incident side polarization plate 420G and the light-emission side polarization plate 440G disposed in an optical path of a green light. Also, the ‘2-1. a first process’ through ‘2-4. a fourth process’ are performed regarding the light-incident side polarization plate 420B and the light-emission side polarization plate 440B disposed in an optical path of a blue light.
In this manner, the projector 1000 according to the first embodiment of the present invention may be manufactured.
As described above, the method for manufacturing the projector according to the first embodiment of the present invention includes a process of arranging a polarization plate such that the polarization plates 420R, 420G and 420B on the light-incident side and the polarization plates 440R, 440G and 440B on the light-emission side are respectively arranged on the light-incident side and the light-emission side of the liquid crystal devices 410R, 410G and 410B considering polarization direction thereof. Also, the method includes a process of arranging the spectrophotometer that is performed prior to the process of arranging the polarization plate. As described above, the process of arranging the polarization plate includes a first process, a second process, a third process and a fourth process.
According to the method for manufacturing the projector of the first embodiment, either the polarization plates 420R, 420G and 420B on the light-incident side or the polarization plates 440R, 440G, 440B on the light-emission side, or both are rotated and a light transmittance spectrum is measured on respective rotational position thereof. Based on the measured light transmittance spectrum, a relative rotational postion of the respective polarization plates 420R, 420G and 420B on the light-incident side and the polarization plates 440R, 440G, 440B on the light-emission side are determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum. The polarization plates 420R, 420G and 420B on the light-incident side and the polarization plates 440R, 440G and 440B on the light-emission side are bonded at the determined relative rotational position so that it is prevented that a light that is to pass through the polarization plate on the light-emission side is absorbed by the polarization plate, or a light that is to be absorbed by the polarization plate on the light-emission side passes through the polarization plate. In addition, lowering in contrast of a projection image, an uneven brightness, or an uneven color may be prevented or reduced. As a result, the deterioration of display quality of a projection image may be prevented or reduced.
Thus, according to the method for manufacturing a project of the first embodiment, it is possible to manufacture a projector having improved display quality of a projection image.
In addition the projector 1000 that is manufactured according to the method of the first embodiment described above may improve display quality of a projection image.
The method for manufacturing the optical element according to the second embodiment is used to manufacture an optical element having a structure (not illustrated in the figure) such that the polarization plates 420R, 420G and 420B on the light-incident side have the light transmissive members 430R, 430G, 430B respectively bonding to a first surface thereof, and second light transmissive members 460R, 460G and 460B respectively bonding to a surface opposing to the first surface, i.e., a second surface thereof. In addition, the method is used to manufacture an optical element having a structure (not illustrated in the figure) such that the polarization plates 440R, 440G and 440B on the light-emission side have the light transmissive members 450R, 450G, 450B respectively bonding to a first surface thereof, and the second light transmissive members 470R, 470G and 470B bonding to a second surface thereof.
In the method according to the second embodiment, as shown, in
Each of the process will be described below, however, ‘1. a preparing process’ through ‘5. a bonding process’ are substantially the same or similar to those described in the first embodiment, and thus any further explanation will be omitted. Also, for illustrative purposes, the optical element manufactured by the method has a structure such that the light transmissive member 430R is bonded to a first surface of the polarization plate 420R on the light-incident side and the second light transmissive member 460R is bonded to a second surface of the polarization plate 420R on the light-incident sides
6. Process of Preparing the Second Light Transmissive Member
The second light transmissive member 460R is prepared (Step S20 in
In addition, the light source 710 and the second light transmissive member 460R may be prepared together in the ‘1. a preparing process’. In this circumstance, ‘6. a process of preparing the second light transmissive member’ is omitted.
7. Second Arranging Process
The polarization plate 420R on the light-incident side, the second light transmissive member 460R and the certificating polarization plate 720 are arranged between the light source 710 and the spectrophotometer 700 so that a light from the light source 710 is incident on the polarization plate 420R on the light-incident side, passes through the polarization plate 420R on the light-incident side, the second light transmissive member 460R and the certificating polarization plate 720 and is incident on the spectrophotometer 700 (step S22 in
8. Second Light Transmittance Spectrum Measuring Process
Next, as shown in
In addition, in the method for manufacturing the optical element according to the second embodiment, a polarization axis of the polarization plate 420R on the light-incident side and a polarization axis of the second light transmissive member 460R may be adjusted with a precision level equal to or less than 0.5 degree.
9. Second Process of Determining of Rotational Position
Next, based on the measured result of the light transmittance spectrum of the second light transmissive member 460R on respective rotational position in the ‘8. Second process of measuring a light transmittance spectrum’, the rotational position of the second light transmissive member 460R is determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum (step S26 in
10. Second Process of Bonding
As illustrated in
As described above, it is manufactured an optical element having a structure such that the light transmissive member 430R is bonded to a first surface of the polarization plate 420R on the light-incident side, and the second light transmissive member 460R is bonded to a second surface of the polarization plate 420R. In addition, using the above described processes, it is manufactured an optical element having a structure such that the polarization plates 420G and 420B on the light-incident side have the light transmissive members 430G and 430B respectively bonding to a first surface thereof, and the second light transmissive members 460G and 460B bonding to a second surface thereof, and it also is manufactured an optical element having a structure such that the polarization plates 440R, 440G and 440B on the light-emission side have the light transmissive members 450R, 450G and 450B respectively bonding to a first surface thereof and the second light transmissive members 470R, 470G and 470B bonding to a second surface thereof.
Thus, the method for manufacturing an optical element according to the second embodiment is used to manufacture an optical element having a structure such that the polarization plate has a light transmissive member bonded to a first surface thereof and a second light transmissive member bonded to a second surface thereof. As described above, the method according to the second embodiment includes a preparing process, a arranging process, a light transmittance spectrum measuring process, a rotational position determining process, a bonding process, a second process of preparing a second light transmissive member, a second arranging process, a second light transmittance spectrum measuring process, a second rotational position determining process and a second bonding process.
Thus, according to a method for manufacturing the optical element of the second embodiment, when the polarization plate that is bonded to the light transmissive member is also bonded to the second light transmissive member, as in the case of the first embodiment where the polarization plate is bonded to the light transmissive member, the second light transmissive member is rotated and the light transmittance spectrum of the light is measured with respect to each rotational position. Based on the measured result of the light transmittance spectrum with respect to each rotational position, the rotational position of the second light transmissive member is determined such that yields the smallest value for the difference between a minimum value and a maximum value of the light transmittance spectrum. The polarization plate and the second light transmissive member are bonded at the determined relative rotational position so that the polarization axis of the polarization plate may be adjusted to be parallel to or orthogonal to the optical axis of the second light transmissive member with higher precision. Accordingly, the variation of the polarization state of a light when transmitting the optical element may be prevented or reduced. As a result, the degradation of display quality of a projection image may be prevented or reduced.
Therefore, according to a method for manufacturing an optical element of the second embodiment, it is possible to manufacture an optical element having an improved display quality of projection image.
Herein, a method for manufacturing an optical element, a method for manufacturing a projector and a projector is illustrated in the above described embodiments; however, the present invention is not limited to the above embodiments but may be implemented in various alternative embodiments without departing from the spirit and scope of the invention. For example, the following variations of the invention are possible.
(1) Although the optical element of the embodiment of the present invention is described in connection with the application to a projector, however, it is not to be construed as limitations of the present invention. The optical element according to the embodiment of the present invention may be applied to other optical equipment that uses a polarization light such as a polarization microscope or an optical disk device.
(2) In the embodiments, the light transmissive member or the second light transmissive member uses a light transmissive substrate comprising sapphire, however, a light transmissive substrate comprising quartz may also be utilized.
(3) In the ‘2. arranging process’ of the first embodiment, as illustrated in
(4) In the ‘7. second arranging process’ of the second embodiment, as illustrated in
(5) In the projector 1000 of the first embodiment, the polarization plate 420R on the light-incident side is interposed between the light collecting lens 300R and the light transmissive member 430R to adhere thereto. However, this is not construed as limitations of the present invention, and in an alternative implementation, or example, the light collecting lens 300R and the polarization plate 420R on the light-incident side are separated, or the polarization plate 420R on the light-incident side is interposed between the light transmissive member 430R and the second light transmissive member 460R to adhere thereto.
(6) In the protector 1000 of the first embodiment, the polarization plate 440R on the light-emission side is interposed between the cross dichroic prism 500 and the light transmissive member 430R to adhere thereto. However, this is not construed as limitations of the present invention, and in an alternative implementation, for example, the polarization plate 420R on the light-emission side and the cross dichroic prism 500 are separated, or the polarization plate 440R on the light-emission side is interposed between the light transmissive member 450R and the second light transmissive member 460R to adhere thereto.
(7) In the embodiment of the present invention, the polarization plate on the light-incident side or the polarization plate on the light-emission side has a two-layer structure where a supporting layer is laminated on the polarization layer. However, this may not be construed as limitations of the present invention, and the polarization plate may have a three-layer structure where the supporting layer is laminated on both sides of the polarization layer, or may have a single-layer structure.
(8) In the projector 1000 according to the first embodiment, the light source device 110 having the ellipsoid reflector 114, the light emitting tube 112 of which luminance center is near a first focus of the ellipsoid reflector 114 and the concave lens 118 is used. However, this is not construed as limitations of the present invention, and in an alternative implementation, a light source having a parabolic reflector and a light emitting tube of which luminance center is near a focus of the parabolic reflector may be used.
(9) In the projector 1000 according to the first embodiment, the subsidiary mirror 116 is arranged in the light emitting tube 112 to serve as reflection means. However, this is not to be construed as limitations of the present invention, and the light emitting tube 112 may not include the subsidiary mirror 116.
(10) In the projector 1000 according to the first embodiment, a lens integrator optical system, light-uniforming optical system, having a lens array is utilized, however, this is not to be construed as limitations of the present invention and a load integrator optical system having a load member may be preferably utilized.
(11) According to the above described embodiments, the projector has three liquid crystal devices 410R, 410G and 410B. However, this is not to be construed as limitations of the present invention, and the projector may include two or more than four liquid crystal devices.
(12) The present invention can be applied to a front type projector that projects an image from an observer side, and also be applied to a rear type projector that projects an image from an opposite side of the observer side.
The entire disclosure of Japanese Patent Application NO. 2006-049738, filed Feb. 27, 2006 is expressly incorporated by reference herein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006-049738 | Feb 2006 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6885465 | Kitabayashi et al. | Apr 2005 | B2 |
| Number | Date | Country |
|---|---|---|
| A 7-020317 | Jan 1995 | JP |
| A 2000-112022 | Apr 2000 | JP |