Patent Grant
6971144
1. Field of the Invention
The present invention relates to a polyurethane foam injected with strand mats, and more particularly to a method for manufacturing a polyurethane foam injected with strand mats, in which loss of the polyurethane foam is reduced and productivity thereof is improved, resulting from further comprising the step of increasing the volume of each of the strand mats to uniformly distribute the strand mats in the polyurethane foam, and a device for increasing the volume of the strand mats.
2. Description of the Related Art
Generally, polyurethane foam is a porous material in the form of sponge, produced by a chemical reaction of a polyol and an isocyanate, along with other additives. It is divided into a flexible polyurethane foam and a rigid polyurethane foam. The flexible polyurethane foam is used primarily as a cushioning material such as a matrix and the rigid polyurethane foam is utilized mainly as an insulating material. The present invention focuses on the rigid polyurethane foam used for an insulating material, and in particular, a method for manufacturing a polyurethane foam used as a cold-insulating material for a ship intended for transporting mainly a super-low temperature substance such as liquefied natural gas (LNG).
As shown in
The strand mat is produced by binding glass fibers in the form of a solid powder of less than 25 microns with a polyester binder to maintain the shape of the mat. In this case, the amount of the polyester binder must be minimized within an extent that the shape of the mat is maintained. Generally, the polyester binder is used in the range of 1.3 to 3 weight % of the strand mat. If it is outside the above range, various problems may arise.
Specifically, if the amount of the polyester binder is too high, the cohesion between glass fibers in the strand mat increases and thus it is difficult to separate the glass fibers in the strand mat. As a result, when the polyurethane foam solution is sprayed and foam molded, the strand mats are not uniformly distributed in the molded polyurethane foam, thereby a poor quality of polyurethane foam being yielded. While, if the amount of the polyester binder is too small, the cohesion between glass fibers is too low to maintain the shape of a long-fiber mat.
Accordingly, when a polyurethane foam injected with strand mats is manufactured, the strand mats must be uniformly immersed in a polyurethane foam solution so as to be uniformly distributed in a produced polyurethane foam. Therefore, variations in the density, tensile strength, and compression strength between top and bottom layers in the polyurethane foam are reduced, thereby ensuring a uniform quality of the polyurethane foam and reducing quality defects in the interior of the polyurethane foam such as cracks.
However, as for the conventional method for manufacturing a polyurethane foam injected with strand mats, the strand mats are immersed in a polyurethane foam solution in a state wherein glass fibers in the strand mats are strongly bound. Therefore, the polyurethane foam solution cannot uniformly permeate into the glass fibers. As a result, air spaces are present in the produced polyurethane foam and thus the strength and the cold-insulating effect of the polyurethane foam are reduced.
In addition, the nonuniform distribution of strand mats in a polyurethane foam makes it possible to partially decrease the mechanical strength and heat insulating effect of the polyurethane foam. As a result, shrinkage, cracking, distortion and the like are caused in the polyurethane foam under a super-low temperature condition, or the polyurethane foam is liable to be broken by an external impact.
Therefore, the present invention has been made in view of the above problems, and it is an object of the present invention to provide a method for manufacturing a polyurethane foam injected with strand mats, in which shrinkage, cracking, distortion and the like do not occur under a super-low temperature such as less than −165° C., and impact resistance is improved, resulting from increasing the volume of each of the strand mats before spraying a polyurethane foam solution on the strand mats so as to weaken the cohesion between glass fibers forming the strand mats, to uniformly infiltrate the polyurethane foam solution into the strand mats, and to uniformly distribute the strand mats in the polyurethane foam, and a device for increasing the volume of the strand mats.
In accordance with one aspect of the present invention, the above object and other objects can be accomplished by the provision of a method for manufacturing a polyurethane foam injected with strand mats, comprising the steps of continuously supplying and transferring strands mats using multiple winding rollers, spraying a polyurethane foam solution on the strand mats, and foam molding the polyurethane foam solution in which the strand mats are immersed; wherein the improvement is characterized in that the step of increasing the volume of each of the strand mats is carried out before spraying the polyurethane foam solution on the strand mats, so as to weaken the cohesion between glass fibers forming the strand mat.
In accordance with another aspect of the present invention, there is provided a device for increasing the volume of the strand mat, consisting of a first roller with the strand mats made with glass fiber being wound therearound; a volume-increasing means with multiple compression rollers, applying pressure to each of the strand mats supplied from the first roller so as to weaken the cohesion between the glass fibers and increase the volume of the strand mat; a second roller, around which the volume-increased strand mats are wound; and a base, in which the first and second rollers, and the volume-increasing means are installed.
The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
Hereinafter, the preferred embodiments of the present invention will be described in detail with reference to the accompanying figures.
As shown in
As shown in
The volume-increasing means 10 is installed in a manner such that some gear teeth (T) on one end of each of a group of the compression rollers are meshed with each other at a predetermined interval. In the present invention, three compression rollers 11, 12 and 13 are grouped.
The slider 22 is connected to a piston load 21, which is raised and lowered by a hydraulic cylinder 20 installed in the upper side of the support 30. As the piston load 21 is raised and lowered, the slider 22 and the gap adjusting roller 11 are simultaneously raised and lowered. Based on this principle, the gaps between the compression rollers 11,12,13 are adjusted. Specifically, the degree of increase of the volume of the strand mat 1 passing between the compression rollers 11,12,13 can be varied by adjusting the gaps between the driving rollers 12,13 and the gap adjusting roller 11.
In a method for manufacturing a polyurethane foam injected with strand mats according to the present invention, the volume of each of the strand mats is increased by the volume-increasing means shown in
Generally, the strand mats 1 are supplied while being wound around a winding roller. Accordingly, in the present invention, a first roller 6, around which the strand mats 1 are wound, is installed in the volume-increasing apparatus of the present invention. The strand mats 1 are transferred from the first roller 6 via a volume-increasing means 10 to a second roller 4. When a step motor 8 is operated, the first roller 6 and the second roller 4 rotate. As a result, the strand mats 1 are unwound from the first roller 6, pass between the compression rollers 11,12,13 of the volume-increasing means 10, and are wound around the second roller 4.
While each of the strand mats 1 passes through the volume-increasing means 10, the gear teeth (T) formed on the driving rollers 12,13 and the gap adjusting roller 11 compress the glass fibers 1′ in the strand mat 1. Therefore, a binder 1″, which binds the glass fibers 1′ with each other, is broken. As a result, the cohesion between the glass fibers 1′ is weakened and thus the volume of the strand mat 1 is substantially increased.
In this case, the gaps between the driving rollers 12,13 and gap adjusting roller 11 of the volume-increasing means 10 are adjusted by the hydraulic cylinder 20. If the gaps between the compression rollers vary, the amount of the broken binder varies. As a result, the degree of increase of the volume of the strand mat 1 which has passed through the volume-increasing means 10 varies. It is understood that the gaps between the compression rollers of the volume-increasing means 10 are permitted within an extent that the glass fibers 1′ in the strand mat 1 are not damaged, and are adjusted according to the thickness of the strand mat 1. After the volume-increased strand mats 1 are sufficiently wound around the second roller 4, a polyurethane foam is molded by a manufacturing apparatus of the polyurethane foam.
A manufacturing apparatus of a polyurethane foam shown in
In the first conveyor 121 and the second conveyor 122, driving rollers 121b, 122b are installed at positions separated each other by a designated distance. The driving rollers 121b, 122b make conveyor belts 121a, 122a rotate, thereby the strand mats placed on the conveyor belts being transferred.
In addition, a passage 120a is defined in an approximately vertical orientation on the basal plate 120 at a position separated by a predetermined distance from an end of the first conveyor 121. A release paper supply device 128 is installed at the lower side of the basal plate 120 to supply a release paper 129 through the passage 120a. In order for the release paper 129 not to be crumpled, a guide roller 127 is installed in each of the upper and lower sides of the exit of the release paper supply device 128 to guide the supply of the release paper 129.
Hereinafter, the operating procedure of the apparatus for manufacturing the polyurethane foam shown in
Volume-increased strand mats by the volume-increasing means shown in
The polyurethane foam solution is sprayed on the strand mats 1 and release paper 129 by the polyurethane foam solution supply device 125 and permeates into the strand mats 1. In this case, the polyurethane foam solution is sprayed until it covers the uppermost layer of the strand mats 1 so as to immerse the strand mats 1 in the polyurethane foam solution. The release paper 129 placed at the lower side of the strand mats 1 prevents direct contact between the polyurethane foam solution and the upper surface of the basal plate 120. Furthermore, when the polyurethane foam solution is foam molded into a polyurethane foam, the release paper 129 becomes one part of the polyurethane foam and constitutes the packaged one surface of the polyurethane foam.
The polyurethane foam solution sprayed on the strand mats 1 is foam molded by a chemical reaction of an isocyanate and a blowing agent after 30 to 80 seconds. Because the polyurethane foam solution is foam molded in a state wherein the polyurethane foam solution sufficiently permeates into the volume-increased strand mats 1, the produced polyurethane foam has uniformly distributed strand mats 1.
As described in the above, the present invention uses glass fiber reinforcement in order to increase the mechanical strength and super-low temperature stability of the polyurethane foam. In this case, with a result of improving degree of distribution of the glass fibers, the variation in the mechanical strength and physical properties between the layers of the polyurethane foam, and the product loss caused by the poor distribution of the mechanical strength and the physical properties are reduced. Therefore, increased productivity of the polyurethane foam is accomplished. These improvements are demonstrated through the examples below and the results are presented in Table 1 below.
Examples are different in the composition ratio of a polyurethane foam solution and the number of passages of a volume-increasing means. In Table 1, CSM means continuous strand mat.
Comparative examples 1 and 2 are polyurethane foams, each manufactured by spraying a polyurethane foam solution with a composition ratio (weight ratio) of polyol: isocyanate: blowing agent of 100:110:0.9 or 100:130:0.92 on 7-layered strand mats, and foam molding the polyurethane foam solution without passing through the volume-increasing means of the present invention. The distribution states of their strand mats were not uniform and deviated from the standard. The density difference between the top and bottom layers of the polyurethane foam was more than 7 kg/m3. Also, the variations in the physical properties were large, for example, the compression strength varied more than 0.094 kg/cm2, and the room-temperature tensile strength varied more than 0.077 kg/cm2.
Example 1 is a polyurethane foam manufactured after once passing its strand mats through the volume-increasing means of the present invention. It was satisfactory in terms of values of standard average physical properties, on the whole. Specifically, the density difference between the top and bottom layers of the polyurethane foam was lowered to 4 kg/m3, and the variations in the compression strength and room-temperature tensile strength were lowered to 0.077 kg/cm2 and 0.063 kg/cm2, respectively, so as to exhibit almost uniform physical properties. In particular, judging from the fact that the tensile strength variation at a low temperature of −170° C. was 0.051 kg/cm2, it can be seen that the physical properties of the polyurethane foam are almost uniform.
Example 2 is a polyurethane foam manufactured after twice passing its strand mats through the volume-increasing means of the present invention. The variations in the compression strength and room-temperature tensile strength were 0.075 kg/cm2 and 0.061 kg/cm2, respectively, which were much less than those of the polyurethane foam of example 1. The tensile strength variation at a low temperature of −170° C. was 0.047 kg/cm2, which was less than that of the polyurethane foam of example 1.
As apparent from the above description, the present invention provides a method for manufacturing a polyurethane foam injected with strand mats and a device for increasing the volume of each of the strand mats, weakening the cohesion between glass fibers in each of the strand mats before immersing the strand mats in a polyurethane foam solution so as to sufficiently infiltrate the polyurethane foam solution into the strand mats and uniformly distribute the strand mats in the polyurethane foam. As a result, the polyurethane foam useful as a heat insulating material can be obtained, in which shrinkage, cracking, distortion and the like are prevented, and the impact resistance is improved, even under a super-low temperature such as less than −165° C.
Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2001-40090 | Jul 2001 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4279060 | Wirth | Jul 1981 | A |
| 4475271 | Lovgren et al. | Oct 1984 | A |
| 6265047 | Chapuis et al. | Jul 2001 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20030034578 A1 | Feb 2003 | US |