Patent Application
20070128747
1. Field of the Invention
The present invention relates to a method for manufacturing a semiconductor device. The present invention relates to a method for manufacturing a semiconductor device which inputs and outputs data by wireless communication.
2. Description of the Related Art
A method for manufacturing a semiconductor device provided with a semiconductor integrated circuit over a flexible substrate has been proposed. In this method, first, a plurality of semiconductor integrated circuits is formed using a thin film transistor over a first substrate, which is not flexible and is formed from a thick glass or the like. The plurality of semiconductor integrated circuits is formed while keeping a predetermined distance from each other over the first substrate. The plurality of semiconductor integrated circuits is transferred from the first substrate to a flexible second substrate. The plurality of semiconductor integrated circuits is completely transferred from the first substrate to the second substrate concurrently; therefore, also over the second substrate, the plurality of semiconductor integrated circuits is aligned while keeping the predetermined distance from each other. Thereafter, the second substrate is divided so as to divide the semiconductor integrated circuits into separate pieces, thereby obtaining a plurality of semiconductor devices (refer to description in Patent Document 1: Japanese Published Patent Application No. 2005-311333). The predetermined distance becomes a margin for division (hereinafter, referred to as a division margin or a scribe margin) when obtaining the plurality of semiconductor devices by dividing the second substrate.
In a conventional method for manufacturing a semiconductor device, providing a division margin has been necessary. Accordingly, it has been difficult to increase the number of semiconductor integrated circuits that can be manufactured over one first substrate, and therefore, it has been difficult to increase the number of semiconductor devices that can be manufactured at once by using one first substrate. Thus, semiconductor device costs have been high.
In addition, if the division margin is not sufficiently secured in order to increase the number of semiconductor devices, a semiconductor integrated circuit is more likely to be damaged when being divided. Therefore, it has been difficult to ensure reliability of the semiconductor integrated circuit.
In view of the above, it is an object of the present invention to provide a method for manufacturing a highly reliable semiconductor device at low cost.
One feature of the present invention is a method for manufacturing a semiconductor device by which a plurality of semiconductor integrated circuits formed over a first substrate is transferred to additional substrates through multiple transfer operations (hereinafter, referred to as “a transfer method through multiple transfer operations”).
In particular, one feature of the present invention is to use multiple types of insulating layers (a first insulating layer and a second insulating layer) as an insulating layer for adhesion between semiconductor integrated circuits and an additional substrate when transferring a plurality of semiconductor integrated circuits to the additional substrate. Adhesion force between each of the first insulating layer and second insulating layer and the semiconductor integrated circuits differs. The first insulating layer is selectively formed over some of the circuits of the plurality of semiconductor integrated circuits formed over the first substrate, and the second insulating layer is selectively formed over rest of the circuits of plurality of the semiconductor integrated circuits formed over the first substrate. An additional substrate, which differs from the first substrate, is provided over the first insulating layer and the second insulating layer to separate the first substrate and the additional substrate from each other. Accordingly, the semiconductor integrated circuits over which the first insulating layer is formed are not transferred to the additional substrate, but the semiconductor integrated circuits over which the second insulating layer is formed are transferred to the additional substrate (the first transfer). At this time, the semiconductor integrated circuits that have not been transferred to the additional substrate remain over the first substrate. After the first transfer, the semiconductor integrated circuits are transferred to a new additional substrate (the second transfer). In this manner, the plurality of semiconductor integrated circuits formed over the first substrate can be transferred to the additional substrate, selectively. Accordingly, the plurality of semiconductor integrated circuits formed over the first substrate can be transferred to the additional substrates through multiple transfer operations.
The plurality of semiconductor integrated circuits formed over the first substrate may have the same configuration or different configurations. For example, the plurality of semiconductor integrated circuits formed over the first substrate may have the same layout or different layouts.
(A method for manufacturing a semiconductor device by a transfer method through multiple transfer operations)
Another feature of the present invention is a method for manufacturing a semiconductor device by which a plurality of first semiconductor integrated circuits and a plurality of second semiconductor integrated circuits arranged so that each of the second semiconductor integrated circuits is adjacent to one of the first semiconductor integrated circuits are formed over a first substrate; a second substrate is attached so as to cover the first semiconductor integrated circuits and the second semiconductor integrated circuits; thereafter, the first substrate and the second substrate are separated from each other and the first semiconductor integrated circuits are transferred to the second substrate (first transfer); a third substrate is attached so as to cover the second semiconductor integrated circuits remaining over the first substrate; thereafter, the first substrate and the third substrate are separated from each other and the second semiconductor integrated circuits are transferred to the third substrate (second transfer); the second substrate is divided so as to divide the plurality of first semiconductor integrated circuits into separate pieces; and the third substrate is divided so as to divide the plurality of second semiconductor integrated circuits into separate pieces.
By a method for manufacturing a semiconductor device of the present invention, a plurality of first semiconductor integrated circuits and a plurality of second semiconductor integrated circuits arranged so that each of which is adjacent to one of the first semiconductor integrated circuits are formed over a first substrate; a first insulating layer is formed so as to cover the second semiconductor integrated circuits; a second insulating layer is formed so as to cover the first semiconductor integrated circuits; a second substrate is attached so as to cover the first insulating layer and the second insulating layer; the first substrate and the second substrate are separated from each other by adding a first external force between the second substrate and the first substrate, and the first semiconductor integrated circuits are transferred to the second substrate (the first transfer); a third substrate is attached so as to cover the second semiconductor integrated circuits remaining over the first substrate; the first substrate and the third substrate are separated from each other by adding a second external force between the first substrate and the third substrate, and the second semiconductor integrated circuits are transferred to the third substrate (the second transfer); the second substrate is divided so as to divide the plurality of first semiconductor integrated circuits into separate pieces; and the third substrate is divided so as to divide the plurality of second semiconductor integrated circuits into separate pieces.
The second insulating layer may be formed so as to cover an edge portion of the first insulating layer or may be formed so as not to cover the edge portion of the first insulating layer.
It is to be noted that, after the first semiconductor integrated circuits are transferred to the second substrate, a plurality of first semiconductor integrated circuits are further transferred to a fourth substrate, and the fourth substrate is divided so as to divide the plurality of first semiconductor integrated circuits into separate pieces. Moreover, after the second semiconductor integrated circuits are transferred to the third substrate, a plurality of second semiconductor integrated circuits is further transferred to a fifth substrate, and the fifth substrate may be divided so as to divide the plurality of second semiconductor integrated circuits into separate pieces.
It is to be noted that, with respect to the first external force, the junction (adhesive) strength between the second insulating layer and the first semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the first insulating layer and the second semiconductor integrated circuits and is made to be higher than the junction strength between the first substrate and the first semiconductor integrated circuits. In addition, with respect to the first external force, the junction strength between the first substrate and the second semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the first insulating layer and the second semiconductor integrated circuits. The second insulating layer can be formed using an epoxy-based resin material (a resin material having an epoxy group), and the first insulating layer can be formed using a vinyl-based resin material (a resin material having a vinyl group).
The first semiconductor integrated circuits and the second semiconductor integrated circuits can be formed over the first substrate at the same time (can be formed by the same process). The first semiconductor integrated circuits and the second semiconductor integrated circuits may have the same structure or may have different structures.
The heat resistance of the first substrate can be made higher than that of the second to fifth substrates. The heat-resistant property indicates a strain point, a melting point, or a glass transition point.
A method for manufacturing a semiconductor device of the present invention can be a method for manufacturing a semiconductor device by which first semiconductor integrated circuits or second semiconductor integrated circuits are electrically connected to an antenna and data is input and output by wireless communication through the antenna. The antenna can be formed when forming the first semiconductor integrated circuits and the second semiconductor integrated circuits over a first substrate. It is to be noted that the antenna may be formed over a substrate which differs from the first substrate.
(A method for manufacturing a semiconductor device by a transfer method through four transfer operations)
By a method for manufacturing a semiconductor device of the present invention, over a first substrate, a plurality of first semiconductor integrated circuits; a plurality of second semiconductor integrated circuits arranged so that each of the second semiconductor integrated circuits is adjacent to one of the first semiconductor integrated circuits; a plurality of third semiconductor integrated circuits arranged so that each of the third semiconductor integrated circuits is adjacent to one of the first semiconductor integrated circuits and one of the second semiconductor integrated circuits; and a plurality of fourth semiconductor integrated circuits arranged so that each of the fourth semiconductor integrated circuits is adjacent to one of the first semiconductor integrated circuits, one of the second semiconductor integrated circuits, and one of the third semiconductor integrated circuits are formed.
A first insulating layer is formed so as to cover the second semiconductor integrated circuits, the third semiconductor integrated circuits, and the fourth semiconductor integrated circuits. A second insulating layer is formed so as to cover the first semiconductor integrated circuits. A second substrate is attached so as to cover the first insulating layer and the second insulating layer. The first substrate and the second substrate are separated from each other by adding a first external force between the first substrate and the second substrate, and the first semiconductor integrated circuits are transferred to the second substrate (the first transfer).
A third insulating layer is formed so as to cover the third semiconductor integrated circuits and the fourth semiconductor integrated circuits remaining over the first substrate. A fourth insulating layer is formed so as to cover the second semiconductor integrated circuits. A third substrate is attached so as to cover the third insulating layer and the fourth insulating layer. The first substrate and the third substrate are separated from each other by adding a second external force between the first substrate and the third substrate, and the second semiconductor integrated circuits are transferred to the third substrate (the second transfer).
A fifth insulating layer is formed so as to cover the fourth semiconductor integrated circuits remaining over the first substrate. A sixth insulating layer is formed so as to cover the third semiconductor integrated circuits. A fourth substrate is attached so as to cover the fifth insulating layer and the sixth insulating layer. The first substrate and the fourth substrate are separated from each other by adding a third external force between the first substrate and the fourth substrate, and the third semiconductor integrated circuits are transferred to the fourth substrate (the third transfer).
A fifth substrate is attached so as to cover the fourth semiconductor integrated circuits remaining over the first substrate. The first substrate and the fifth substrate are separated from each other by adding an external force between the first substrate and the fifth substrate, and the fourth semiconductor integrated circuits are transferred to the fifth substrate (the fourth transfer).
The second substrate is divided so as to divide the plurality of first semiconductor integrated circuits into separate pieces. The third substrate is divided so as to divide the plurality of second semiconductor integrated circuits into separate pieces. The fourth substrate is divided so as to divide the plurality of third semiconductor integrated circuits into separate pieces. The fifth substrate is divided so as to divide the plurality of fourth semiconductor integrated circuits into separate pieces.
The second insulating layer may be formed so as to cover an edge portion of the first insulating layer or may be formed so as not to cover the edge portion thereof. The fourth insulating layer may be formed so as to cover an edge portion of the third insulating layer or may be formed so as not to cover the edge portion thereof. The sixth insulating layer may be formed so as to cover an edge portion of the fifth insulating layer or may be formed so as not to cover the edge portion thereof.
It is to be noted that, after the first semiconductor integrated circuits are transferred to the second substrate, the plurality of first semiconductor integrated circuits may be further transferred to a sixth substrate, and the sixth substrate may be divided so as to divide the plurality of first semiconductor integrated circuits into separate pieces. After the second semiconductor integrated circuits are transferred to the third substrate, the plurality of second semiconductor integrated circuits may be further transferred to a seventh substrate, and the seventh substrate may be divided so as to divide the plurality of second semiconductor integrated circuits into separate pieces. After the third semiconductor integrated circuits are transferred to the fourth substrate, the plurality of third semiconductor integrated circuits may be further transferred to an eighth substrate so as to divide the plurality of third semiconductor integrated circuits into separate pieces. After the fourth semiconductor integrated circuits are transferred to the fifth substrate, the plurality of fourth semiconductor integrated circuits may be further transferred to a ninth substrate, and the ninth substrate may be divided so as to divide the plurality of fourth semiconductor integrated circuits into separate pieces.
It is to be noted that, with respect to the first external force, the junction (adhesive) strength between the second insulating layer and the first semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the first insulating layer and each of the second to fourth semiconductor integrated circuits, and is made to be higher than the junction strength between the first substrate and the first semiconductor integrated circuits. With respect to the first external force, the junction strength between the first substrate and each of the second to fourth semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the first insulating layer and each of the second to fourth semiconductor integrated circuits. With respect to the second external force, the junction (adhesive) strength between the fourth insulating layer and the second semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the third insulating layer and each of the third and fourth semiconductor integrated circuits, and is made to be higher than the junction strength between the first substrate and the second semiconductor integrated circuits. With respect to the second external force, the junction strength between the first substrate and each of the third and fourth semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the third insulating layer and each of the third and fourth semiconductor integrated circuits. With respect to the third external force, the junction (adhesive) strength between the sixth insulating layer and the third semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the fifth insulating layer and the fourth semiconductor integrated circuits, and is made to be higher than the junction strength between the first substrate and the third semiconductor integrated circuits. With respect to the third external force, the junction strength between the first substrate and the fourth semiconductor integrated circuits is made to be higher than the junction (adhesive) strength between the fifth insulating layer and the fourth semiconductor integrated circuits. The second insulating layer, the fourth insulating layer, and the sixth insulating layer can be formed using an epoxy-based resin material (a resin material having an epoxy group). The first insulating layer, the third insulating layer, and the fifth insulating layer can be formed using a vinyl-based resin material (a resin material having a vinyl group).
The first to fourth semiconductor integrated circuits can be formed over the first substrate at the same time (can be formed by the same process). The first to fourth semiconductor integrated circuits may have the same structure or may have different structures.
The heat resistance of the first substrate can be made higher than that of the second to ninth substrates.
A method for manufacturing a semiconductor device of the present invention can be applied to a method for manufacturing a semiconductor device by which any of the first to fourth semiconductor integrated circuits are electrically connected to an antenna and data is input and output by wireless communication through the antenna. The antenna can be formed when forming the first to fourth semiconductor integrated circuits over the first substrate. It is to be noted that the antenna may be formed over a substrate which differs from the first substrate.
By a method for manufacturing a semiconductor device of the present invention, after the first semiconductor integrated circuits formed over the first substrate are transferred to the second substrate, the first semiconductor integrated circuits are divided into separate pieces. Since circuits (the second semiconductor integrated circuits) are not formed to be adjacent to any of the first semiconductor integrated circuits over the second substrate, the first semiconductor integrated circuits are formed while keeping a distance from each other. In addition, after the second semiconductor integrated circuits formed over the first substrate are transferred to the third substrate, the second semiconductor integrated circuits are divided into separate pieces. Since circuits (the first semiconductor integrated circuits) are not formed to be adjacent to any of the second semiconductor integrated circuits over the third substrate, the second semiconductor integrated circuits are formed while keeping a distance from each other. Accordingly, a large division margin of the second substrate and a large division margin of the third substrate can be obtained. In addition, the number of semiconductor devices that can be manufactured from one first substrate can be increased. It is to be noted that, as an area of the semiconductor integrated circuit becomes smaller, high accuracy in dividing into each semiconductor integrated circuit is necessary; therefore, as the area of the semiconductor integrated circuit becomes smaller, an effect of the present invention is high.
In particular, with respect to the transfer method through two transfer operations, by the transfer method through four transfer operations, in each of the first to fourth semiconductor integrated circuits, a plurality of semiconductor integrated circuits can be placed while keeping a wide distance from each other. Therefore, a larger division margin can be obtained. In addition, the number of semiconductor devices that can be manufactured from one first substrate can be increased.
By making the heat resistance of the first substrate higher than that of the substrate to which the semiconductor integrated circuits are transferred, the allowable temperature of a process in manufacturing a plurality of semiconductor integrated circuits can be increased. This makes it possible to perform sufficient heat treatment; therefore, a characteristic of the semiconductor integrated circuit can be improved.
In the method for manufacturing a semiconductor device by the transfer method through two transfer operations, by forming the second insulating layer so as not to cover an edge portion of the first insulating layer, it is possible for the first insulating layer not to remain between the second insulating layer and the first semiconductor integrated circuit. Accordingly, adhesion between the second insulating layer and the first semiconductor integrated circuit is increased and reliability of the semiconductor device can be further improved. In addition, the first insulating layer can be easily removed after the first semiconductor integrated circuits are transferred to a substrate which differs from the first substrate.
Also, in the method for manufacturing a semiconductor device by the transfer method through four transfer operations, by forming the second insulating layer so as not to cover an edge portion of the first insulating layer, it is possible for the first insulating layer not to remain between the second insulating layer and the first semiconductor integrated circuit. By forming the fourth insulating layer so as not to cover an edge portion of the third insulating layer, it is possible for the third insulating layer not to remain between the fourth insulating layer and the second semiconductor integrated circuit. By forming the sixth insulating layer so as not to cover an edge portion of the fifth insulating layer, it is possible for the fifth insulating layer not to remain between the sixth insulating layer and the third semiconductor integrated circuit. Accordingly, adhesion between the second insulating layer and the first semiconductor integrated circuit, adhesion between the fourth insulating layer and the second semiconductor integrated circuit, and adhesion between the sixth insulating layer and the third semiconductor integrated circuit can be increased, and reliability of the semiconductor device can be further improved. In addition, the first insulating layer, the third insulating layer, and the fifth insulating layer can be easily removed after the first semiconductor integrated circuits, the second semiconductor integrated circuits, and the third semiconductor integrated circuits are transferred to substrates that differ from the first substrate.
As described above, a method for manufacturing a highly reliable semiconductor device at low cost can be provided.
In the accompanying drawings:
Embodiment modes of the present invention will be explained with reference to drawings. However, the present invention is not limited to the explanation below, and it is easily understood by those skilled in the art that the modes and details can be modified in various ways without departing from the purpose and the scope of the present invention. Therefore, the present invention is not interpreted as being limited to the explanation of the embodiment modes to be given below. It is to be noted that, in the structure of the present invention hereinafter explained, the reference numerals denoting the same portions are used in common in different drawings. In the present invention, “being connected”is synonymous with “being electrically connected”; therefore, another element may be sandwiched.
A method for manufacturing a semiconductor device of the present invention will be explained. In this embodiment mode, a method for manufacturing a semiconductor device by a transfer method through two transfer operations will be explained.
A semiconductor substrate such as a silicon wafer, a quartz substrate, a glass substrate, or the like can be used as the first substrate 100. By using a substrate having a high heat-resistance temperature as the first substrate 100, an allowable temperature of a process in manufacturing the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202 can be increased. Accordingly, it becomes possible to perform sufficient heat treatment, thereby improving characteristics of the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202. In addition, a substrate having rigidity can also be used as the first substrate 100. By using the substrate having rigidity as the first substrate 100, a distortion of the first substrate 100 can be reduced, and misalignment or the like in manufacturing the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202 can be reduced. Accordingly, reliability of the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202 can be improved.
A first resin material is applied so as to cover the second semiconductor integrated circuits 202. Thereafter, baking treatment is performed using heating means such as an oven, a hot plate, or a furnace to solidify the first resin material, and a first insulating layer 203a formed of a resin is formed (
After the first insulating layer 203a is formed, a second resin material is applied so as to cover the first semiconductor integrated circuits 201. The second resin material differs from the first resin material. Thereafter, baking treatment is performed using heating means such as an oven, a hot plate, or a furnace to solidify the second resin material, and a second insulating layer 204a formed of a resin is formed (
A printing method, a droplet discharge method, or the like can be employed as an application method of the resin material or the like for forming the first insulating layer 203a and the second insulating layer 204a. The droplet discharge method means a method for forming a predetermined pattern by discharging a droplet containing a predetermined composition from a pore. The droplet discharge method is also called an ink jet method depending on its system. The printing method means a screen printing method or an offset printing method.
In
Next, an opening 205 is formed in the semiconductor integrated circuit layer 102, and the peeling layer 101 is exposed (
A second substrate 206a is provided over the second insulating layer 204a (
The first semiconductor integrated circuits 201 are separated from the first substrate 100 by using the second substrate 206a. At this time, an external force may be applied so that the second substrate 206a and the first substrate 100 are separated from each other. The first semiconductor integrated circuits 201 may be separated from the first substrate 100 by etching the peeling layer 101 by introducing a gas or a liquid through the opening 205. Alternatively, the first semiconductor integrated circuits 201 may be separated from the first substrate 100 by etching the peeling layer 101 by introducing a gas or a liquid from the opening 205 and further by applying an external force. For etching, for example, a gas or a liquid containing halogen fluoride or an interhalogen compound can be used. The separation of the first substrate 100 and the first semiconductor integrated circuits 201 is performed inside the peeling layer 101 or at a boundary between the peeling layer 101 and the semiconductor integrated circuit layer 102. Accordingly, the first semiconductor integrated circuits 201 are transferred to the second substrate 206a (
Next, a third resin material is applied over the second semiconductor integrated circuits 202 remaining over the first substrate 100 and is baked, thereby forming a third insulating layer 224b formed of a resin (
In the step shown in
Subsequently, a fourth substrate 209 is provided over the surface of the first semiconductor integrated circuits 201 (
Next, a method for dividing the fourth substrate 209 and a method for dividing the fifth substrate 210 will be explained. Row c and Row d in
The fourth substrate 209 is divided so that a plurality of first semiconductor integrated circuits 201 formed over the fourth substrate 209 is divided into separate pieces. Here, portions (shown by a quadrangle in the drawing) where no semiconductor integrated circuit is formed over the fourth substrate 209 are divided diagonally and are divided along lines 211 passing four corners of each of the plurality of first semiconductor integrated circuits 201 (Column X1, Row c in
If each of the fourth substrate 209 and the fifth substrate 210 is a flexible substrate, a semiconductor device having flexibility can be manufactured. As the flexible substrate, a plastic substrate can be used. Also, a substrate formed by polishing a glass substrate or a semiconductor substrate to be thin may be used. For example, a single crystal silicon substrate having a surface perpendicular to a single crystal silicon crystal axis <100>or <110>, which is polished to have a thickness within the range of 0.1 to 20 μm, typically, a thickness within the range of 1 to 5 μm.
According to this embodiment mode, two types of semiconductor integrated circuits (the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202) that are arranged so that each of the first semiconductor integrated circuits 201 and each of the second semiconductor integrated circuits 202 are adjacent to each other over the first substrate 100 can be transferred to additional substrates (the fourth substrate 209 and the fifth substrate 210) through multiple transfer operations. After each of the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202 formed over the first substrate are transferred to the additional substrates (the fourth substrate 209 and the fifth substrate 210), the first semiconductor integrated circuits 201 and the second semiconductor integrated circuits 202 are divided into separate pieces. Since, over the fourth substrate 209, each of the circuits (the second semiconductor integrated circuits 202) is not arranged to be adjacent to any of the first semiconductor integrated circuits 201, the first semiconductor integrated circuits 201 are arranged while keeping a distance from each other. Also, since, over the fifth substrate 219, each of the circuits (the first semiconductor integrated circuits 201) is not arranged to be adjacent to any of the second semiconductor integrated circuits 202, the second semiconductor integrated circuits 202 are arranged while keeping a distance from each other. Accordingly, a large division margin of the fourth substrate 209 and a large division margin of the fifth substrate 210 can be obtained. In addition, the number of semiconductor devices that can be manufactured from one first substrate can be increased.
By forming the second insulating layer 204a so as not to cover an edge portion of the first insulating layer 203a, it is possible for the first insulating layer 203a not to remain between the second insulating layer 204a and the first semiconductor integrated circuit 201. Accordingly, adhesion between the second insulating layer 204a and the first semiconductor integrated circuit 201 can be increased, and reliability of the semiconductor device can be improved. In addition, the first insulating layer 203a can be easily removed after the first semiconductor integrated circuits 201 are transferred to the substrate which differs from the first substrate.
It is to be noted that, in this embodiment mode, a structure is shown in which, after the first semiconductor integrated circuits 201 transferred to the second substrate 206a are transferred to the fourth substrate 209, the first semiconductor integrated circuits 201 are divided into separate pieces by dividing the fourth substrate 209. In addition, a structure is shown in which, after the second semiconductor integrated circuits 202 transferred to the third substrate 206b are transferred to the fifth substrate 210, the second semiconductor integrated circuits are divided into separate pieces by dividing the fifth substrate 210. Without being limited thereto, a structure may be employed in which, after the first semiconductor integrated circuits 201 are transferred to the second substrate 206a, the first semiconductor integrated circuits 201 are divided into separate pieces by dividing the second substrate 206a. A structure may also be employed in which, after the second semiconductor integrated circuits 202 are transferred to the third substrate 206b, the second semiconductor integrated circuits 202 are divided into separate pieces by dividing the third substrate 206b. Accordingly, a plurality of semiconductor devices is manufactured. If each of the second substrate 206a and the third substrate 206b is a flexible substrate at this time, a semiconductor device having flexibility can be manufactured.
Although the structure is shown in this embodiment mode, in which division is performed so that the semiconductor integrated circuits are divided into separate pieces, the present invention is not limited thereto. The semiconductor integrated circuits may be divided into groups of semiconductor integrated circuits depending on the intended purpose of the semiconductor device. For example, division into a form in which a plurality of semiconductor integrated circuits aligns while keeping a distance from each other may be performed. Since a plurality of semiconductor integrated circuits is connected through a substrate in a structure in which the plurality of semiconductor integrated circuits aligns, it is possible to easily manufacture a semiconductor device having a structure in which the plurality of semiconductor integrated circuits is electrically connected to each other in series or in parallel. Also, a plurality of semiconductor integrated circuits is shipped in a state of being connected through a substrate, and thereafter, the plurality of semiconductor circuits may be further divided into separate pieces to be used. In a state where a plurality of semiconductor integrated circuits is connected to each other through the substrate, connection of the plurality of semiconductor integrated circuits and a plurality of elements can be performed collectively. For example, connection of the plurality of semiconductor integrated circuits with the plurality of elements or the like can be performed by using a roll-to-roll method. Therefore, efficiency of mass production of the semiconductor device can be improved.
Accordingly, a method for manufacturing a highly reliable semiconductor device at low cost can be provided.
In this embodiment mode, a method for manufacturing a semiconductor device by using a transfer through four transfer operations will be explained.
As shown in
By a method as shown in Embodiment Mode 1, the first semiconductor integrated circuits 401 are transferred to a second substrate. In the same way, the second semiconductor integrated circuits 402 are transferred to a third substrate. The third semiconductor integrated circuits 403 are transferred to a fourth substrate. The fourth semiconductor integrated circuits 404 are transferred to a fifth substrate. Furthermore, the semiconductor integrated circuits 401 transferred to the second substrate are transferred to a sixth substrate 501; the second semiconductor integrated circuits 402 transferred to the third substrate are transferred to a seventh substrate 502; the third semiconductor integrated circuits transferred to the fourth substrate are transferred to an eighth substrate 503; and the fourth semiconductor integrated circuits 404 transferred to the fifth substrate are transferred to a ninth substrate 504.
A method for transferring the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 to the sixth substrate 501 to the ninth substrate 504, respectively will be explained in detail with reference to
A cross sectional view of a-a′ in
A semiconductor substrate such as a silicon wafer, a quartz substrate, a glass substrate, or the like can be used as the first substrate 100. By using a substrate having a high heat-resistance temperature as the first substrate 100, an allowable temperature for a process in manufacturing the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 can be increased. Accordingly, it becomes possible to perform sufficient heat treatment, thereby improving characteristics of the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404. In addition, a substrate having rigidity can also be used as the first substrate 100. By using the substrate having rigidity as the first substrate 100, a distortion of the first substrate 100 can be reduced, and misalignment or the like in manufacturing the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 can be reduced. Accordingly, reliability of the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 can be improved.
A first resin material is applied so as to cover the second semiconductor integrated circuits 402 to the fourth semiconductor integrated circuits 404. Thereafter, baking treatment is performed using heating means such as an oven, a hot plate, or a furnace to solidify the first resin material, and a first insulating layer 203a formed of a resin is formed (
After the first insulating layer 203a is formed, a second resin material is applied so as to cover the first semiconductor integrated circuits 401. The second resin material differs from the first resin material. Thereafter, baking treatment is performed using heating means such as an oven, a hot plate, or a furnace to solidify the first resin material, and a second insulating layer 204a formed of a resin is formed (
A printing method, a droplet discharge method, or the like can be employed as an application method of the resin material or the like for forming the first insulating layer 203a and the second insulating layer 204a.
In
Next, an opening 205 is formed in the semiconductor integrated circuit layer 102, and the peeling layer 101 is exposed (
A second substrate 206a is provided over the second insulating layer 204a (
The first semiconductor integrated circuits 401 are separated from the first substrate 100 by using the second substrate 206a. At this time, an external force may be applied so that the second substrate 206a and the first substrate 100 are separated from each other. The first semiconductor integrated circuits 401 may be separated from the first substrate 100 by etching the peeling layer 101 by introducing a gas or a liquid through the opening 205. Alternatively, the first semiconductor integrated circuits 401 may be separated from the first substrate 100 by etching the peeling layer 101 by introducing a gas or a liquid through the opening 205 and further by applying an external force. For etching, for example, a gas or a liquid containing halogen fluoride or an interhalogen compound can be used. The separation of the first substrate 100 and the first semiconductor integrated circuits 401 is performed inside the peeling layer 101 or at a boundary between the peeling layer 101 and the semiconductor integrated circuit layer 102. Accordingly, the first semiconductor integrated circuits 201 are transferred to the second substrate 206a (
Next, a third resin material is applied over the third semiconductor integrated circuits 403 and the fourth semiconductor integrated circuits 404 remaining over the first substrate 100 and is baked, thereby forming a third insulating layer 203b formed of a resin. After the third insulating layer 203b is formed, a fourth resin material is applied so as to cover the second semiconductor integrated circuits 402. Thereafter, baking is performed, and a fourth insulating layer 204b formed of a resin is formed (
Next, a fifth resin material is applied over the fourth semiconductor integrated circuits 402 remaining over the first substrate 100 and is baked, thereby forming a fifth insulating layer 203c formed of a resin. After the fifth insulating layer 203c is formed, a sixth resin material is applied so as to cover the third semiconductor integrated circuits 403. Thereafter, baking is performed, and a sixth insulating layer 204c formed of a resin is formed (
Next, a seventh resin material is applied over the fourth semiconductor integrated circuits 404 remaining over the first substrate 100 and is baked, thereby forming a seventh insulating layer 204d formed of a resin. The seventh resin material can be the same as the second resin material. Furthermore, as described above, an opening is provided by a laser beam or the like. A fifth substrate 206d is provided over the seventh insulating layer 204d (
In the step shown in
Subsequently, a sixth substrate 501 is provided over the surface of the first semiconductor integrated circuits 401 transferred to the second substrate 206a by the step shown in
As shown by Row b in
The sixth substrate 501 is divided so as to divide a plurality of first semiconductor integrated circuits 401 formed over the sixth substrate 501 into separate pieces. The division is performed along lines 213 almost going through the center between the first semiconductor integrated circuits 401 (Column X1, Row c in
Each of the sixth substrate 501 to the ninth substrate 504 can be divided by using a laser, a cutter, a pair of scissors, or the like. In addition, each of the sixth substrate 501 to the ninth substrate 504 can be divided by using a heated wire or the like. For example, a frame of a wire formed into a division shape of the semiconductor integrated circuit is heated and the frame is pushed through, thereby dividing each of the sixth substrate 501 to the ninth substrate 504.
If each of the sixth substrate 501 to the ninth substrate 504 is a flexible substrate, a semiconductor device having flexibility can be manufactured.
According to the present invention, four types of semiconductor integrated circuits (the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404) that are arranged so that, over the first substrate 100, each of the first semiconductor integrated circuits 401, each of the second semiconductor integrated circuits 402, each of the third semiconductor integrated circuits 403, and each of the fourth semiconductor integrated circuits 404 are adjacent to each other can be transferred to additional substrates (the sixth substrate 501 to the ninth substrate 504) through multiple transfer operations. The first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 formed over the first substrate are transferred to additional substrates (the sixth substrate 501 to the ninth substrate 504), respectively, and each of the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 are divided into separate pieces. Over each of the sixth substrate 501 to the ninth substrate 504, the semiconductor integrated circuits are arranged while keeping a distance from each other. Accordingly, a large division margin of each of the sixth substrate 501 to the ninth substrate 504 can be obtained. In addition, the number of semiconductor devices that can be manufactured from one first substrate can be increased.
With respect to the transfer method through two transfer operations shown in Embodiment Mode 1, in the method for manufacturing a semiconductor device by using a transfer method through four transfer operations shown in this embodiment, in each of the first semiconductor integrated circuits to the fourth semiconductor integrated circuits transferred to the substrate which differs from the first substrate, a plurality of semiconductor integrated circuits can be arranged while keeping a wide distance from each other Therefore, a larger division margin can be obtained. Accordingly, the number of semiconductor devices that can be manufactured from one first substrate can be increased.
By forming the second insulating layer 204a so as not to cover an edge portion of the first insulating layer 203a, it is possible for the first insulating layer 203a not to remain between the second insulating layer 204a and the first semiconductor integrated circuit 401. By forming the fourth insulating layer 204b so as not to cover an edge portion of the third insulating layer 203b, it is possible for the third insulating layer 203b not to remain between the fourth insulating layer 204b and the second semiconductor integrated circuit 402. By forming the sixth insulating layer 204c so as not to cover an edge portion of the fifth insulating layer 203c, it is possible for the fifth insulating layer 203c not to remain between the sixth insulating layer 204c and the third semiconductor integrated circuit 403. Accordingly, adhesion between the second insulating layer 204a and the first semiconductor integrated circuit 401, adhesion between the fourth insulating layer 204b and the second semiconductor integrated circuit 402, and adhesion between the sixth insulating layer 204c and the third semiconductor integrated circuit 403 can be enhanced, and reliability of the semiconductor device can be further improved. In addition, after each of the first semiconductor integrated circuits 401, the second semiconductor integrated circuits 402, and the third semiconductor integrated circuits 403 are transferred to the substrate which differs from the first substrate 100, the first insulating layer 203a, the third insulating layer 203b, and the fifth insulating layer 203c can be easily removed.
In this embodiment mode, a structure is shown in which, after the first semiconductor integrated circuits 401 transferred to the second substrate 206a are transferred to the sixth substrate 501, the sixth substrate 501 is divided so that the first semiconductor integrated circuits 401 are divided into separate pieces. However, the present invention is not limited thereto. A structure may also be employed in which, after the first semiconductor integrated circuits 401 are transferred to the second substrate 206a, the second substrate 206a is divided so that the first semiconductor integrated circuits 401 are divided into separate pieces. In the same way, a structure may be employed in which, after the second semiconductor integrated circuits 402 are transferred to the third substrate 206b, the third substrate 206b is divided so that the second semiconductor integrated circuits 402 are divided into separate pieces. In the same way, a structure may be employed in which, after the third semiconductor integrated circuits 403 are transferred to the fourth substrate 206c, the fourth substrate 206c is divided so that the third semiconductor integrated circuits 403 are divided into separate pieces. In the same way, a structure may be employed in which, after the fourth semiconductor integrated circuits 404 are transferred to the fifth substrate 206d, the fifth substrate 206d is divided so that the fourth semiconductor integrated circuits 404 are divided into separate pieces. Accordingly, a plurality of semiconductor devices is manufactured. If each of the second substrate 206a to the fifth substrate 206d is a flexible substrate, a semiconductor device having flexibility can be manufactured.
Although the structure is shown in this embodiment mode, in which division is performed so that the semiconductor integrated circuits are divided into separate pieces, the present invention is not limited thereto. The semiconductor integrated circuits may be divided into groups of semiconductor integrated circuits depending on the intended purpose of the semiconductor device. For example, division into a form in which a plurality of semiconductor integrated circuits aligns while keeping a distance from each other may be performed. Since a plurality of semiconductor integrated circuits is connected through a substrate in a structure in which the plurality of semiconductor integrated circuits aligns, it is possible to easily manufacture a semiconductor device having a structure in which the plurality of semiconductor integrated circuits is electrically connected to each other in series or in parallel. Also, a plurality of semiconductor integrated circuits is shipped in a state of being connected through a substrate, and thereafter, the plurality of semiconductor circuits may be further divided into separate pieces to be used. In a state where a plurality of semiconductor integrated circuits is connected to each other through the substrate, connection of the plurality of semiconductor integrated circuits and a plurality of elements can be performed collectively. For example, connection of the plurality of semiconductor integrated circuits with the plurality of elements or the like can be performed by using a roll-to-roll method. Therefore, efficiency of mass production of the semiconductor device can be improved.
Accordingly, a method for manufacturing a highly reliable semiconductor device at low cost can be provided.
This embodiment mode can be implemented by being freely combined with Embodiment Mode 1.
In this embodiment mode, an example is shown in which the method for manufacturing a semiconductor device shown in Embodiment Mode 2 is applied to a method for manufacturing a semiconductor device which inputs and outputs data by wireless communication.
In
As shown in Row c in
Methods for electrically connecting the conductive layer 307 serving as an antenna with the semiconductor circuit and forming the RFID tag will be explained. In the explanation, a method for electrically connecting the conductive layer 307 serving as an antenna with the first semiconductor integrated circuit 401 is shown. It is to be noted that since a method for electrically connecting the conductive layer 307 serving as an antenna with each of the second semiconductor integrated circuit to the fourth semiconductor integrated circuit is the same as the method for electrically connecting the conductive layer 307 serving as the antenna with the first semiconductor integrated circuit 401, the explanation thereof is omitted.
An electrode 332 is provided so as to be electrically connected to an element (for example, a thin film transistor) included in the first semiconductor integrated circuit 401 (
Next, the sixth substrate 501 and a tenth substrate 306 are attached to each other. The positional relationship between the first semiconductor integrated circuit 401 and the conductive layer 307 when the sixth substrate 501 and the tenth substrate 306 are attached to each other is shown in Row d in
After the sixth substrate 501 and the tenth substrate 306 are attached to each other, the attached substrate 310 is divided so that a plurality of first semiconductor integrated circuits 401 formed over the sixth substrate is divided into separate pieces. Accordingly, the semiconductor device can be manufactured.
According to this embodiment mode, four types of the semiconductor integrated circuits (the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404) that are arranged so that, over the first substrate 100, each of the first semiconductor integrated circuits 401, each of the second semiconductor integrated circuits 402, each of the third semiconductor integrated circuits 403, and each of the fourth semiconductor integrated circuits 404 are adjacent to each other can be transferred to additional substrates (the sixth substrate 501 to the ninth substrate 504) through multiple transfer operations. After the semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 formed over the first substrate 100 are transferred to the additional substrates (the sixth substrate 501 to the ninth substrate 504) respectively, each of the first semiconductor integrated circuits 401 to the fourth semiconductor integrated circuits 404 are divided into separate pieces. The semiconductor integrated circuits are arranged while keeping a distance from each other over each of the sixth substrate 501 to the ninth substrate 504. Accordingly, a large division margin of each of the sixth substrate 501 to the ninth substrate 504 can be obtained. In addition, the number of semiconductor devices that can be manufactured from one first substrate 100 can be increased.
The semiconductor integrated circuits are arranged while keeping a distance from each other over each of the sixth substrate 501 to the ninth substrate 504. Therefore, even if the conductive layer 307 serving as an antenna occupies a large area over the tenth substrate 306, the tenth substrate 306 can be attached to each of the sixth substrate 501 to the ninth substrate 504 so that one semiconductor integrated circuit corresponds to one conductive layer 307. In other words, the tenth substrate 306 can be attached to each of the sixth substrate 501 to the ninth substrate 504 so that the plurality of semiconductor devices does not overlap with one conductive layer 307. Accordingly, the number of semiconductor devices that can be manufactured from one first substrate 100 can be increased.
Consequently, a method for manufacturing a highly reliable semiconductor device at low cost can be provided.
This embodiment mode can be implemented by being freely combined with Embodiment Modes 1 and 2.
In Embodiment Modes 1 to 3, the case where a plurality of semiconductor integrated circuits with the same size is formed over the first substrate 100 is explained. However, the present invention is not limited thereto. The semiconductor integrated circuits formed over the first substrate 100 can be various sizes. In addition, the semiconductor integrated circuits formed over the first substrate 100 can have different structures from each other. An example in which a plurality of semiconductor integrated circuits with different sizes is formed over one first substrate 100 will be explained with reference to
As shown in
The first semiconductor integrated circuits 551 are transferred to a substrate 554 by the method as shown in Embodiment Mode 1 or 2. A state of the substrate 554 over which the first semiconductor integrated circuits 551 are transferred is shown in Column X1, Row b in
According to this embodiment mode, multiple types of semiconductor integrated circuits manufactured over the first substrate 100 can be transferred to separate substrates. Since the substrate to which the semiconductor integrated circuits are transferred can be selected, a substrate which is suitable for each of the semiconductor integrated circuits having different structures can be selected. Accordingly, reliability of the semiconductor integrated circuit can be improved. When semiconductor integrated circuits with one size is formed over the first substrate 100, a space over the first substrate 100 where the first semiconductor integrated circuits are not arranged is generated in view of the size of the first substrate 100. However, by manufacturing multiple types of semiconductor integrated circuits with different sizes over the first substrate 100, the first substrate 100 can be effectively used. Accordingly, the number of semiconductor devices that can be manufactured from one first substrate 100 can be further increased.
Consequently, a method for manufacturing a highly reliable semiconductor device at low cost can be provided.
In addition, the present invention is not limited to the cases of using the transfer method through two transfer operations, the transfer method through three transfer operations, and the transfer method through four transfer operations. The semiconductor device can be manufactured by using a transfer method through arbitrary time transfer method.
This embodiment mode can be implemented by being freely combined with Embodiment Modes 1 to 3.
In this embodiment mode, a method for forming semiconductor integrated circuits over a first substrate 100 will be explained.
As shown in
When the peeling layer 712 has a single layer structure, preferably, a layer containing any of W, Mo, a mixture of W and Mo, oxide of W, nitride oxide of W, oxide of Mo, nitride oxide of Mo, oxide of a mixture of W and Mo, and nitride oxide of a mixture of W and Mo can be used.
When the peeling layer 712 has a stacked layer structure including two layers, preferably, a layer containing any of W, Mo, and a mixture of W and Mo can be used as a first layer, and a layer containing any of oxide of W, nitride oxide of W, oxide of Mo, nitride oxide of Mo, oxide of a mixture of W and Mo, and nitride oxide of a mixture of W and Mo can be used as a second layer. The surface of the first layer is processed by oxygen plasma treatment or N2O plasma treatment, thereby forming these oxide and nitride oxide.
Next, as shown in
As the semiconductor layer 662, an island-shaped crystalline semiconductor film or amorphous semiconductor film can be used. In addition, an organic semiconductor film may also be used. The crystalline semiconductor film can be obtained by crystallizing the amorphous semiconductor film. As a crystallization method, a laser crystallization method, a thermal crystallization method using RTA or furnace annealing, a thermal crystallization method using a crystallization-promoting metal element, or the like can be used. The semiconductor layer 662 has a channel formation region 662a and a pair of impurity regions 662b to which an impurity element imparting a conductivity type is added. Although a structure is shown in which each of low concentration impurity regions 662c to which the impurity element is added at lower concentration than the impurity regions 662b is provided between the channel formation region 662a and one of the pair of impurity regions 662b, the present invention is not limited thereto. A structure may also be employed in which the low concentration impurity region 662c is not provided. Alternatively, a structure may be employed in which silicide is formed over part of the top surface of the pair of impurity regions 662b (especially, a portion which is in contact with a wiring 666) or the entire surface thereof.
It is preferable that a wiring formed concurrently with (by the same step as) the semiconductor layer 662 be led so that comers are rounded when seen from a direction perpendicular to the top surface of the first substrate 100.
An impurity element imparting a conductivity type may be added to the channel formation region 662a of a thin film transistor. As a result, threshold voltage of the thin film transistor can be controlled.
A first insulating layer 663 is formed over the semiconductor layer 662. The first insulating layer 663 can be formed of a single layer or a stacked layer including a plurality of films using silicon oxide, silicon nitride, silicon nitride oxide, or the like. In this case, the surface of the first insulating layer 663 may be processed by high-density plasma treatment in an oxygen atmosphere or a nitrogen atmosphere, and may be processed by oxidation treatment or nitriding treatment to be densified. As described above, high-density plasma is generated by using a high frequency wave, for example, 2.45 GHz. It is to be noted that high-density plasma with an electron density within the range of 1011 to 1013/cm3, an electron temperature of less than or equal to 2 eV, and an ion energy of less than or equal to 5 eV is used. Plasma can be generated using a plasma treatment apparatus utilizing high frequency excitation, which employs a radial slot antenna. In the apparatus for generating high-density plasma, the distance between the antenna which generates a high frequency wave and the first substrate 100 is within the range of 20 to 80 mm (preferably, 20 to 60 mm).
Before forming the first insulating layer 663, the above high-density plasma treatment may be applied to the surface of the semiconductor layer 662 so that the surface of the semiconductor layer 662 is oxidized or nitrided. At this time, by performing the treatment in an oxygen atmosphere or a nitrogen atmosphere with the first substrate 100 at a temperature within the range of 300 to 450° C., a favorable interface with the first insulating layer 663 that is formed over the semiconductor layer 662 can be formed.
As the nitrogen atmosphere, an atmosphere containing nitrogen (N) and a rare gas (containing at least one of He, Ne, Ar, Kr, and Xe), an atmosphere containing nitrogen, hydrogen (H), and a rare gas, or an atmosphere containing ammonia (NH3) and a rare gas can be used. As the oxygen atmosphere, an atmosphere containing oxygen (O) and a rare gas, an atmosphere containing oxygen, hydrogen (H), and a rare gas, or an atmosphere containing dinitrogen monoxide (N2O) and a rare gas can be used.
A gate electrode 664 is formed over the first insulating layer 663. As the gate electrode 664, an element selected from Ta, W, Ti, Mo, Al, Cu, Cr, and Nd, or an alloy or a compound containing a plurality of above elements can be used. In addition, the gate electrode 664 may have a single layer structure or a stacked layer structure including these elements, the alloy, or the compound. In the drawings, the gate electrode 664 having a single layer structure is shown. It is preferable that the gate electrode 664 or a wiring formed concurrently with (by the same step as) the gate electrode 664 be led so that corners are rounded when seen from a direction perpendicular to the top surface of the first substrate 100. A method for leading the wiring is the same as that shown in
The thin film transistor includes the semiconductor layer 662, the gate electrode 664, the first insulating layer 663 serving as a gate insulating film between the semiconductor layer 662 and the gate electrode 664. Although the thin film transistor is a top gate transistor in this embodiment mode, it may be a bottom gate transistor having a gate electrode below the semiconductor layer, or a dual gate transistor having gate electrodes above and below the semiconductor layer.
An insulating film (denoted by a sidewall 667a in
A second insulating layer 667 is formed over the gate electrode 664 and the sidewall 667a. It is desirable that the second insulating layer 667 be an insulating film such as a silicon nitride film, with a barrier property for blocking an ionic impurity. For example, the second insulating layer 667 is formed of silicon nitride or silicon oxynitride. This second insulating layer 667 serves as a protective film for preventing contamination of the semiconductor layer 662. After depositing the second insulating layer 667, a hydrogen gas may be introduced and the above-described high-density plasma treatment may be performed, thereby hydrogenating the second insulating layer 667. Alternatively, the second insulating layer 667 may be nitrided and hydrogenated by introducing an ammonia (NH3) gas. Otherwise, oxidization-nitridation treatment and hydrogenation treatment may be performed by introducing oxygen, a dinitrogen monoxide (N2O) gas, or the like with a hydrogen gas. By performing nitridation treatment, oxidization treatment, or oxidization-nitridation treatment in this manner, the surface of the second insulating layer 667 can be densified. Accordingly, the function of the second insulating layer 667 as a protective film can be enhanced. Hydrogen introduced into the second insulating layer 667 is discharged when thermal treatment is applied at a temperature within the range of 400 to 450° C., thereby hydrogenating the semiconductor layer 662. It is to be noted that the hydrogenation treatment may be performed in combination with hydrogenation treatment using the first insulating layer 663.
A third insulating layer 665 is formed over the second insulating layer 667. The third insulating layer 665 can have a single layer structure or a stacked layer structure of an inorganic insulating film or an organic insulating film. As the inorganic insulating film, a silicon oxide film formed by a CVD method, a silicon oxide film formed by an SOG (spin on glass) method, or the like can be used. As the organic insulating film, a film of polyimide, polyamide, BCB (benzocyclobutene), acrylic, a positive photosensitive organic resin, a negative photosensitive organic resin, or the like can be used.
The third insulating layer 665 may be made of a material having a skeleton structure formed of a bond of silicon (Si) and oxygen (O). An organic group containing at least hydrogen (such as an alkyl group and aromatic hydrocarbon) is used as a substituent of this material. Alternatively, a fluoro group may be used as the substituent. Further alternatively, a fluoro group and an organic group containing at least hydrogen may be used as the substituent.
The wiring 666 is formed over the third insulating layer 665. The wiring 666 can be formed of one element selected from Al, Ni, W, Mo, Ti, Pt, Cu, Ta, Au, and Mn, or an alloy containing a plurality of above elements. Alternatively, a single layer or a stacked layer of these elements or the alloy can be used. In the drawings, an example of a single layer structure is shown. It is to be noted that the wiring 666 is preferably led so that corners thereof are round when seen from a direction perpendicular to the top surface of the first substrate 100. A method for leading the wiring is the same as that shown in
A fourth insulating layer 669 is formed over the wiring 666. The fourth insulating layer 669 can have a single layer structure or a stacked layer structure of an inorganic insulating film or an organic insulating film. As the inorganic insulating film, a silicon oxide film formed by a CVD method, a silicon oxide film formed by an SOG (spin on glass) method, or the like can be used. As the organic insulating film, a film of polyimide, polyamide, BCB (benzocyclobutene), acrylic, a positive photosensitive organic resin, a negative photosensitive organic resin, or the like can be used.
The fourth insulating layer 669 may be made of a material having a skeleton structure formed of a bond of silicon (Si) and oxygen (O). An organic group containing at least hydrogen (such as an alkyl group and aromatic hydrocarbon) is used as a substituent of this material. Alternatively, a fluoro group may be used as the substituent. Further alternatively, a fluoro group and an organic group containing at least hydrogen may be used as the substituent.
An electrode 134 is formed over the fourth insulating layer 669. The electrode 134 can be formed of one element selected from Al, Ni, W, Mo, Ti, Pt, Cu, Ta, Au, and Mn, or an alloy containing a plurality of above elements. Alternatively, a single layer or a stacked layer of these elements or the alloy can be used. In the drawings, an example of a single layer structure is shown.
As shown in
As shown in
When the present invention is applied to a method for manufacturing an RFID (radio frequency identification) tag (also referred to as a wireless tag, an IC tag, an IC chip, an RF tag, an electronic tag, or a transponder), the electrode 134 can be an electrode connected to an electrode 332 shown in
Consequently, a method for manufacturing a highly reliable semiconductor device at low cost can be provided.
This embodiment mode can be implemented by being freely combined with Embodiment Modes 1 to 4.
In this embodiment, a structure of an RFID tag which can be manufactured by the present invention will be explained. Moreover, a wireless communication system using the RFID tag will be explained.
A case where the RFID tag 3000 receives data will be explained. A modulated carrier wave input from the antenna 2202, from which noise is removed by the band-pass filter 2502, is input to the power supply circuit 2503 and the demodulation circuit 2506. The power supply circuit 2503 has a rectifier circuit and a storage capacitor. The modulated carrier wave input through the band-pass filter 2502 is rectified by the rectifier circuit and smoothed by the storage capacitor. In this manner, the power supply circuit 2503 generates a DC voltage. The DC voltage generated in the power supply circuit 2503 is supplied as a power supply voltage to each circuit in the circuit portion 2203 included in the RFID tag 3000. It is to be noted that the power supply voltage output from the power supply circuit 2503 may be supplied to each circuit in the circuit portion 2203 through a constant voltage circuit (a regulator). The modulated carrier wave input through the band-pass filter 2502 is demodulated by the demodulation circuit 2506, and the demodulated signal is input to the digital portion 2205. A signal input from the analog portion 2204, that is, a signal which is made by demodulating the modulated carrier wave by the demodulation circuit 2506, is input to the code extraction circuit 2301, and a code of the signal is extracted. An output of the code extraction circuit 2301 is input to the code determination circuit 2302, and the extracted code is analyzed. The analyzed code is input to the cyclic redundancy check circuit 2303, and an arithmetic processing for identifying a transmission error is performed. Then, the cyclic redundancy check circuit 2303 outputs a result whether the received data has an error or not to the control circuit 2304. It is to be noted that a phase synchronization circuit generating a clock at a predetermined frequency, which is synchronized with a signal, using an output of the demodulation circuit 2506 may be included. As the phase synchronization circuit, a phase locked loop circuit (a PLL circuit) can be used.
Next, a case where the RFID tag 3000 transmits data will be explained. The memory circuit 2305 outputs a stored unique identifier (UID) to the control circuit 2304, depending on a signal input from the code determination circuit 2302. The memory circuit includes a memory, and a memory controller which controls reading of data from the memory. A mask ROM can be used as the memory. The cyclic redundancy check circuit 2303 calculates the CRC code corresponding to the transmitted data and outputs the CRC code to the control circuit 2304. The control circuit 2304 adds the CRC code to the transmitted data. The control circuit 2304 encodes data in which the CRC code is added to the transmitted data. In addition, the control circuit 2304 converts the encoded information into a signal for modulating the carrier wave in accordance with a predetermined modulation method. The output of the control circuit 2304 is input to the modulation circuit 2507 of the analog portion 2204. The modulation circuit 2507 load-modulates the carrier wave depending on the input signal and outputs the carrier wave to the antenna 2202.
By the method for manufacturing a semiconductor device (an RFID tag) of the present invention, a large division margin when dividing a plurality of semiconductor integrated circuits transferred to a substrate which differs from a first substrate into separate pieces can be obtained. In addition, the number of RFID tags that can be manufactured from one first substrate can be increased. Therefore, a method for manufacturing a highly reliable RFID tag at low cost can be provided.
This embodiment can be implemented by being freely combined with the embodiment modes described above.
In this embodiment, a manufacturing method of a memory (corresponding to a memory included in the memory circuit 2305 in
The mask ROM is formed using a plurality of transistors, and the transistor which forms the mask ROM is formed using photolithography. In the case, a selection is conducted whether a contact hole for a wiring connected to, for example, a drain region of the transistor is opened or not in an interlayer insulating film formed over the transistor. Thus, different data can be written. For example, data of a logical value “1”can be written into a memory cell in a case where the contact hole is opened, and alternatively, data of a logical value “0” can be written into the memory cell in a case where the contact hole is not opened.
In a step of exposing a photoresist, before or after a step of conducting exposure through a reticle (a photomask) by using an exposure apparatus such as a stepper, a photoresist over a region in which the contact hole is to be opened is irradiated with an electron beam or a laser. Thereafter, a step such as development, etching, or peeling of a photoresist is normally conducted. Accordingly, only by selecting a region to be irradiated with an electron beam or a laser, a pattern in which the contact hole is opened and a pattern in which the contact hole is not opened can be separately formed without changing a reticle (a photomask). In other words, by selecting the region to be irradiated with an electron beam or a laser, a mask ROM in which different data is written in each semiconductor device can be manufactured without changing a reticle (a photomask).
By using such a manufacturing method of a mask ROM, a unique identifier (UID) can be set for each semiconductor device in manufacturing. The reticle (a photomask) is not necessary to be changed also in a case of setting a different UID; therefore, a semiconductor device can be manufactured at lower cost.
Further, an RFID tag which can be manufactured by the present invention may include, instead of a mask ROM, a memory capable of additional writing or a memory capable of rewriting. In addition, the mask ROM, and the memory capable of additional writing and/or the memory capable of rewriting may be included.
By the method for manufacturing a semiconductor device (an RFID tag) of the present invention, a large division margin when dividing a plurality of semiconductor integrated circuits transferred to a substrate which differs from a first substrate into separate pieces can be obtained. In addition, the number of RFID tags that can be manufactured from one first substrate can be increased. Therefore, a method for manufacturing a highly reliable RFID tag at low cost can be provided.
This embodiment can be implemented by being freely combined with the embodiment modes and Embodiment 1 described above.
In this embodiment, a carrier wave of wireless communication in an RFID tag which can be manufactured by the present invention will be explained.
As for a frequency of a carrier wave, any of the following can be employed: a submillimeter wave of greater than or equal to 300 GHz and less than or equal to 3 THz; an extra high frequency of greater than or equal to 30 GHz and less than 300 GHz; a super high frequency of greater than or equal to 3 GHz and less than 30 GHz; an ultra high frequency of greater than or equal to 300 MHz and less than 3 GHz; a very high wave of greater than or equal to 30 MHz and less than 300 MHz; a high frequency of greater than or equal to 3 MHz and less than 30 MHz; a medium frequency of greater than or equal to 300 KHz and less than 3 MHz; a low frequency of greater than or equal to 30 KHz and less than 300 KHz; and a very low frequency of greater than or equal to 3 KHz and less than 30 KHz. For example, a carrier wave at a frequency of 13.56 MHz may be used or a carrier wave at a frequency of 2.45 GHz may be used.
A shape of the antenna included in the RFID tag can be changed in accordance with the frequency of a carrier wave or a transmission system. For example, the antenna may have a coil shape in a case of utilizing an electromagnetic induction type, or the antenna may have a dipole shape in a case of utilizing a microwave type.
By the method for manufacturing a semiconductor device (an RFID tag) of the present invention, a large division margin when dividing a plurality of semiconductor integrated circuits transferred to a substrate which differs from a first substrate into separate pieces can be obtained. In addition, the number of RFID tags that can be manufactured from one first substrate can be increased. Therefore, a method for manufacturing a highly reliable RFID tag at low cost can be provided.
This embodiment can be implemented by being freely combined with the embodiment modes and Embodiments 1 and 2 described above.
In this embodiment, applications of an RFID tag which can be manufactured by the present invention will be explained with reference to
The RFID tag 3000 can be attached to a surface of an object or embedded in an object to be fixed. For example, the RFID tag 3000 is preferably embedded in a paper of a book or in an organic resin of a package which is formed using the organic resin. By providing the RFID tag 3000 in paper money, coins, securities, unregistered bonds, documents, or the like, forgery thereof can be prevented. Moreover, by providing the RFID tag 3000 in packaging containers, recording media, personal belongings, groceries, clothes, daily commodities, electronic devices, or the like, efficiency of an inspection system or a system of a rental shop can be facilitated. Moreover, by providing the RFID tag 3000 in vehicles, forgery or theft thereof can be prevented. By implanting the RFID tag 3000 in living things such as animals, each living thing can be easily identified. For example, by implanting the RFID tag 3000 in living things such as domestic animals, its year of birth, sex, breed, and the like can be easily identified.
By the method for manufacturing a semiconductor device (an RFID tag) of the present invention, a large division margin when dividing a plurality of semiconductor integrated circuits transferred to a substrate which differs from a first substrate into separate pieces can be obtained. In addition, the number of RFID tags that can be manufactured from one first substrate can be increased. Therefore, the highly reliable RFID tag at low cost can be provided.
This embodiment can be implemented by being freely combined with the embodiment modes and Embodiments 1 to 3 described above.
In this embodiment, one mode of a wireless communication system utilizing an RFID tag 3000 which can be manufactured by the present invention will be explained with reference to
An example of a business model utilizing the system shown in
Alternatively,
By the method for manufacturing a semiconductor device (an RFID tag) of the present invention, a large division margin when dividing a plurality of semiconductor integrated circuits transferred to a substrate which differs from a first substrate into separate pieces can be obtained. In addition, the number of RFID tags that can be manufactured from one first substrate can be increased. Therefore, the highly reliable RFID tag at low cost can be provided.
This embodiment can be implemented by being freely combined with the embodiment modes and Embodiments 1 to 4 described above.
This application is based on Japanese Patent Application serial no. 2005-348872 filed in Japan Patent Office on Dec. 2 in 2005, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2005-348872 | Dec 2005 | JP | national |