Patent Grant
12051703
The present invention relates to a semiconductor device and a method for manufacturing the semiconductor device.
In recent years, transistors that are formed using a semiconductor thin film having a thickness of several nanometers to several hundreds of nanometers over a substrate having an insulating surface such as a glass substrate have been attracting attentions. Transistors are widely used for electronic devices such as ICs (integrated circuits) and electro-optical devices. In addition, transistors are used as switching elements of active matrix display devices typified by liquid crystal display devices and active matrix light-emitting devices typified by light-emitting devices including organic electroluminescence (EL) elements.
The ranges of uses of such an active matrix display device and such a light-emitting device are expanding, and demands for larger screen size, higher definition, and higher aperture ratio are increasing. In addition, these devices are required to have high reliability, and production methods of these devices are required to provide high yield and to have low production cost.
A reduction in the number of photolithography processes in manufacture of transistors for an active matrix display device and an active matrix light-emitting device is important for cost reduction. For example, one photomask for the eighth generation glass substrate costs tens of millions of yen, and one photomask for the tenth generation glass substrate or the eleventh generation glass substrate costs hundreds of millions of yen. Moreover, even when only one photolithography step is added in the manufacturing process, the number of steps relating to the photolithography step is significantly increased. Therefore, many techniques for reducing the number of photolithography processes have been developed.
As typical means for reducing the number of photolithography processes in a manufacturing process of a transistor, a technique using a multi-tone mask (also called a half-tone mask or a gray-tone mask) is widely known. As examples of the known technique for reducing the number of manufacturing steps by using a multi-tone mask, Patent Documents 1 to 3 are given.
An object of one embodiment of the present invention is to reduce the number of masks used in a manufacturing process of a semiconductor device. Another object is to reduce the number of photolithography processes. Another object is to reduce the manufacturing time of a semiconductor device. Another object is to reduce the manufacturing cost of a semiconductor device.
One embodiment of the present invention is a method for manufacturing a semiconductor device that includes the steps of forming a first conductive film over a substrate; forming a first insulating film over the first conductive film; forming a semiconductor film over the first insulating film; forming a semiconductor film including a channel region by etching at least part of the semiconductor film; forming a second insulating film over the semiconductor film including the channel region; forming a mask over the second insulating film; performing a first step in which at the same time as removing a first portion of the second insulating film that overlaps the semiconductor film including the channel region and that the mask does not overlap, second portions of the first insulating film and the second insulating film that do not overlap the semiconductor film including the channel region and that the mask does not overlap are removed; removing the mask after the first step; and forming a second conductive film electrically connected to the semiconductor film including the channel region over at least part of the second insulating film.
It is preferable that in the above-described method, the mask be made to recede to expose part of the second insulating film and the part of the second insulating film be removed between the first step and the removal of the mask.
Another embodiment of the present invention is a method for manufacturing a semiconductor device that includes the steps of forming a first conductive film over a substrate; forming a first insulating film over the first conductive film; forming a semiconductor film over the first insulating film; forming a semiconductor film including a channel region by etching at least part of the semiconductor film; forming a second insulating film over the semiconductor film including the channel region; forming a mask including a first region and a second region having a thickness smaller than that of the first region over the second insulating film; performing a first step of removing portions of the first insulating film and the second insulating film that the mask does not overlap; performing a second step of removing part of the mask that is in the second region by making the mask recede after the first step; performing a third step of removing a portion of the second insulating film that the second region overlaps after the second step; removing the mask after the third step; and forming a second conductive film electrically connected to the semiconductor film including the channel region over at least part of the second insulating film.
Another embodiment of the present invention is a method for manufacturing a semiconductor device that includes the steps of forming a first conductive film over a substrate; forming a first insulating film over the first conductive film; forming a semiconductor film over the first insulating film; forming a mask including a first region and a second region having a thickness smaller than that of the first region over the semiconductor film; performing a first step of forming an opening in the first insulating film by removing portions of the first insulating film and the semiconductor film that the mask does not overlap; performing a second step of removing part of the mask that is in the second region by making the mask recede after the first step; performing a third step of forming a semiconductor film including a channel region by removing a portion of the semiconductor film that the second region overlaps after the second step; removing the mask after the third step; forming a second insulating film over the semiconductor film including the channel region; removing at least a portion of the second insulating film that overlaps the opening; and forming a second conductive film electrically connected to the semiconductor film including the channel region over at least part of the second insulating film.
Another embodiment of the present invention is a method for manufacturing a semiconductor device that includes the steps of: forming a first electrode over a substrate; forming a first insulating film over the first electrode; forming a second insulating film over the first insulating film; forming a first conductive film over the second insulating film; forming a mask including a first region and a second region having a thickness smaller than that of the first region over the first conductive film; performing a first step of removing portions of the first insulating film, the second insulating film, and the first conductive film that the mask does not overlap; performing a second step of removing part of the mask that is in the second region by making the mask recede after the first step; performing a third step of removing portions of the first conductive film that the second region overlaps after the second step; removing the mask after the third step; forming a third insulating film over at least part of the second insulating film; and forming a second conductive film electrically connected to the first electrode over at least part of the third insulating film.
In the above-described method, a step of forming a semiconductor film over the substrate, a step of forming a fourth insulating film over the semiconductor film, and a step of forming a first opening in the fourth insulating film may be performed before the formation of the first electrode. In the above-described method, the first electrode may be electrically connected to the semiconductor film through the first opening formed in the fourth insulating film. In the above-described method, the semiconductor film may include an oxide semiconductor. In the above-described method, the first opening may have a tapered shape. In the above-described method, an opening formed in the second insulating film by the first step may have a tapered shape. In the above-described method, an opening formed in the first insulating film by the first step may have a tapered shape. In the above-described method, the third insulating film may have tapered side surfaces.
Another embodiment of the present invention is a method for manufacturing a semiconductor device that includes the steps of: forming a first electrode over a substrate; forming a first insulating film over the first electrode; forming a second insulating film over the first insulating film; forming a first conductive film over the second insulating film; forming a mask including a first region and a second region having a thickness smaller than that of the first region over the first conductive film; performing a first step of removing portions of the first insulating film, the second insulating film, and the first conductive film that the mask does not overlap; performing a second step of removing part of the mask that is in the second region by making the mask recede after the first step; performing a third step of removing portions of the first conductive film that the second region overlaps after the second step; removing the mask after the third step; forming a third insulating film over at least part of a top surface of the second insulating film and on at least part of a side surface of the second insulating film in an opening formed in the second insulating film by the first step; and forming a second conductive film electrically connected to the first electrode over at least part of the third insulating film.
Another embodiment of the present invention is a method for manufacturing a semiconductor device that includes the steps of: forming a first electrode over a substrate; forming a first insulating film over the first electrode; forming a second insulating film over the first insulating film; forming a first conductive film over the second insulating film; forming a mask including a first region and a second region having a thickness smaller than that of the first region over the first conductive film; performing a first step of removing portions of the first insulating film, the second insulating film, and the first conductive film that the mask does not overlap; performing a second step of removing part of the mask that is in the second region by making the mask recede after the first step; performing a third step of removing portions of the first conductive film that the second region overlaps after the second step; removing the mask after the third step; forming a third insulating film over at least part of a top surface of the second insulating film, on a side surface of the second insulating film in an opening formed in the second insulating film by the first step, and over at least part of the first electrode; and forming a second conductive film electrically connected to the first electrode over at least part of the third insulating film.
According to one embodiment of the present invention, the number of masks used in a manufacturing process of a semiconductor device can be reduced. The number of photolithography processes can also be reduced. The manufacturing time of a semiconductor device can also be reduced. The manufacturing cost of a semiconductor device can also be reduced.
Embodiments of the present invention are described below in detail with reference to the accompanying drawings. Note that the present invention is not limited to the description below, and it is easily understood by those skilled in the art that modes and details thereof can be modified in various ways. Further, the present invention is not construed as being limited to description of the embodiments. In describing structures of the present invention with reference to the drawings, common reference numerals are used for the same portions in different drawings. Note that the same hatched pattern is applied to similar parts, and the similar parts are not especially denoted by reference numerals in some cases.
Note that the ordinal numbers such as “first” and “second” in this specification and the like are used for convenience and do not denote the order of steps or the stacking order of layers. Therefore, for example, description can be made even when “first” is replaced with “second” or “third”, as appropriate. In addition, the ordinal numbers in this specification are not necessarily the same as the ordinal numbers used to specify one embodiment of the present invention.
Note that in this specification and the like, the term such as “over” does not necessarily mean that a component is placed “directly on” another component. For example, the expression “a gate electrode over an insulating layer” can mean a case where there is an additional component between the insulating layer and the gate electrode. The same applies to the term “under”. The expression can also mean a case where there is no planar overlap between the insulating layer and the gate electrode (i.e., the insulating layer and the gate electrode do not overlap each other).
In addition, in this specification and the like, terms such as “electrode” and “wiring” do not limit the functions of components. For example, an “electrode” can be used as part of a “wiring”, and the “wiring” can be used as part of the “electrode”. The terms such as “electrode” and “wiring” can also mean a combination of a plurality of “electrodes” and “wirings”.
Functions of a “source” and a “drain” are sometimes replaced with each other, for example, when a transistor of opposite polarity is used or when the direction of flow of current is changed in circuit operation. Therefore, the terms “source” and “drain” can be replaced with each other in this specification.
The term “electrically connected” includes the case where components are connected through an “object having any electric function”. There is no particular limitation on the “object having any electric function” as long as electric signals can be transmitted and received between the components connected through the object. Examples of the “object having any electric function” are an electrode and a wiring.
Note that a “semiconductor” can have characteristics of an “insulator”, for example, when the conductivity is sufficiently low. Further, a “semiconductor” and an “insulator” cannot be strictly distinguished from each other in some cases because a border between the “semiconductor” and the “insulator” is not clear. Therefore, a “semiconductor” in this specification can be called an “insulator” in some cases. Similarly, an “insulator” in this specification can be called a “semiconductor” in some cases.
Further, a “semiconductor” can includes characteristics of a “conductor”, for example, when the conductivity is sufficiently high. Further, a “semiconductor” and a “conductor” cannot be strictly distinguished from each other in some cases because a border between the “semiconductor” and the “conductor” is not clear. Therefore, a “semiconductor” in this specification can be called a “conductor” in some cases. Similarly, a “conductor” in this specification can be called a “semiconductor” in some cases.
In this specification and the like, the term “parallel” indicates that the angle formed between two straight lines is greater than or equal to −10° and less than or equal to 10°, and accordingly also includes the case where the angle is greater than or equal to −5° and less than or equal to 5°. In addition, the term “perpendicular” indicates that the angle formed between two straight lines ranges from 80° to 100°, and accordingly also includes the case where the angle ranges from 85° to 95°.
In this specification and the like, trigonal and rhombohedral crystal systems are included in a hexagonal crystal system.
A method for manufacturing a semiconductor device that is one embodiment of the present invention is described with reference to
<<Manufacturing Method 1>>
First, a method for forming a transistor 150 and a connection portion 160, which are illustrated in
<Substrate>
First, a substrate 100 is provided (
Alternatively, a semiconductor substrate or an SOI substrate provided with a semiconductor element may be used as the substrate 100. In this case, the transistor 150 is formed over the substrate 100 with an interlayer insulating layer interposed therebetween. The transistor 150 in this case may have a structure in which at least one of a conductive film 102b, a conductive film 114b, and a conductive film 114c is electrically connected to the semiconductor element by a connection electrode embedded in the interlayer insulating layer. Forming the transistor 150 over the semiconductor element with the interlayer insulating layer interposed therebetween can suppress an increase in area due to the formation of the transistor 150.
Alternatively, a flexible substrate such as a plastic substrate may be used as the substrate 100, and the transistor 150 may be provided directly on the flexible substrate. Further alternatively, a separation layer may be provided between the substrate 100 and the transistor 150. The separation layer can be used when part or the whole of the transistor formed over the separation layer is formed and separated from the substrate 100 and transferred to another substrate. Thus, the transistor 150 can be transferred to a substrate having low heat resistance or a flexible substrate.
<Formation of Conductive Film>
Next, a conductive film is formed over the substrate 100 by a sputtering method, a CVD method, an evaporation method, or the like, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form a conductive film 102a and the conductive film 102b (
The conductive film 102a and the conductive film 102b can be formed using a metal selected from aluminum, chromium, copper, tantalum, titanium, molybdenum, and tungsten, an alloy containing any of these metals as its component, an alloy containing any of these metals in combination, or the like. Further, one or more metals selected from manganese and zirconium may be used.
The conductive film 102a and the conductor film 102b may have a single-layer structure or a layered structure of two or more layers. For example, a two-layer structure in which a film functioning as a barrier film such as a film of a metal selected from tungsten, titanium, and molybdenum or an alloy containing any of the metals as its component is stacked over or under an aluminum film may be employed. Alternatively, a three-layer structure in which the above-described films functioning as barrier films are stacked over and under an aluminum film may be employed. Further alternatively, a two-layer structure in which the above-described film functioning as a barrier film is stacked over or under a copper film may be employed. Still alternatively, a three-layer structure in which the above-described films functioning as barrier films are stacked over and under a copper film may be employed.
By using the aluminum film or the copper film, which has low resistance, for the conductive film 102a and the conductive film 102b, the power consumption of the semiconductor device can be reduced. In addition, by stacking the film functioning as a barrier film, such as a tungsten film, a titanium film, or a molybdenum film, to be in contact with the aluminum film or the copper film, diffusion of aluminum or copper can be suppressed and the reliability of the semiconductor device can be improved.
Further, an In—Ga—Zn-based oxynitride semiconductor film, an In—Sn-based oxynitride semiconductor film, an In—Ga-based oxynitride semiconductor film, an In—Zn-based oxynitride semiconductor film, a Sn-based oxynitride semiconductor film, an In-based oxynitride semiconductor film, or a film of a metal nitride (e.g., InN or ZnN), or the like may be provided between the conductive film 102b and the insulating film 104 described later. These films each have a work function higher than or equal to 5 eV, preferably higher than or equal to 5.5 eV, which is higher than the electron affinity of an oxide semiconductor; thus, the threshold voltage of a transistor can be shifted in the positive direction in the case where an oxide semiconductor is used for a semiconductor film described later, and what is called a normally-off switching element can be obtained. For example, as an In—Ga—Zn-based oxynitride semiconductor film, an In—Ga—Zn-based oxynitride semiconductor film having a higher nitrogen concentration than at least a semiconductor film 106b, specifically an In—Ga—Zn-based oxynitride semiconductor film having a nitrogen concentration higher than or equal to 7 atom %, is used.
<Formation of Insulating Film>
Next, an insulating film 104 is formed over the substrate 100, the conductive film 102a, and the conductive film 102b (
The insulating film 104 can be formed to have a single-layer structure or a stacked-layer structure using, for example, one or more of a silicon oxide film, a silicon oxynitride film, a silicon nitride oxide film, a silicon nitride film, an aluminum oxide film, a hafnium oxide film, a gallium oxide film, and a Ga—Zn-based metal oxide film.
The insulating film 104 may be formed using a high-k material such as hafnium silicate (HfSiOx), hafnium silicate to which nitrogen is added (HfSixOyNz), hafnium aluminate to which nitrogen is added (HfAlxOyNz), hafnium oxide, or yttrium oxide, so that gate leakage current of the transistor can be reduced.
The insulating film 104 is formed by a sputtering method, a CVD method, an evaporation method, or the like.
In the case where a silicon nitride film is formed as the insulating film 104, it is preferable to use a two-step formation method. First, a first silicon nitride film with a small number of defects is formed by a plasma CVD method in which a mixed gas of silane, nitrogen, and ammonia is used as a source gas. Then, a second silicon nitride film in which the hydrogen concentration is low and hydrogen can be blocked is formed by switching the source gas to a mixed gas of silane and nitrogen. The formation method can form a silicon nitride film with few defects and a blocking property against hydrogen as the insulating film 104.
In the case where a gallium oxide film is formed as the insulating film 104, metal organic chemical vapor deposition (MOCVD) method can be employed.
<Formation of Semiconductor Film>
Next, a semiconductor film is formed over the insulating film 104 by a sputtering method, a CVD method, an evaporation method, or the like, and a resist mask is formed over the semiconductor film by a photolithography process. After that, at least part of the semiconductor film is etched using the resist mask to form a semiconductor film 106a and the semiconductor film 106b (
A variety of semiconductor materials can be used for the semiconductor film 106a and the semiconductor film 106b. Specifically, a single layer or a stacked layer of amorphous silicon, microcrystalline silicon, polycrystalline silicon, single-crystal silicon, or the like can be used. In addition, an impurity imparting a conductivity type may be added to part of the semiconductor film or to at least one layer in the case of the stacked layer.
Besides the semiconductor materials given above, an oxide semiconductor can be used. A transistor including an oxide semiconductor has extremely low off-state current in some cases. By using such a transistor, the holding capability of a signal input to a capacitor of each pixel in a liquid crystal display device can be improved, so that the frame rate in, for example, still-image display can be reduced. The reduction in the frame rate leads to a reduction in the power consumption of the display device.
An oxide semiconductor that can be used for the semiconductor film 106a and the semiconductor film 106b is described below.
The oxide semiconductor contains, for example, indium. An oxide semiconductor containing indium has high carrier mobility (electron mobility). An oxide semiconductor preferably contains an element M. Examples of the element M include aluminum, gallium, yttrium, and tin. For example, the element M has high bond energy to oxygen. For example, the element M increases the energy gap of the oxide semiconductor. Further, the oxide semiconductor preferably contains zinc. When containing zinc, the oxide semiconductor easily becomes crystalline. The energy at the top of the valence band (Ev) of the oxide semiconductor can be controlled by, for example, the atomic ratio of zinc, in some cases.
The oxide semiconductor does not necessarily contain indium. The oxide semiconductor may be, for example, a Zn—Sn oxide or a Ga—Sn oxide.
The oxide semiconductor may be an In-M-Zn oxide having any of the following atomic ratios of In to M: the atomic percentage of In is smaller than 50 atomic % and the atomic percentage of M is larger than or equal to 50 atomic %, and the atomic percentage of In is smaller than 25 atomic % and the atomic percentage of M is larger than or equal to 75 atomic %, when summation of In and M is assumed to be 100 atomic %. Further, the oxide semiconductor may be an In-M-Zn oxide having any of the following atomic ratios of In to M: the atomic percentage of In is larger than or equal to 25 atomic % and the atomic percentage of M is smaller than 75 atomic %, and the atomic percentage of In is larger than or equal to 34 atomic % and the atomic percentage of M is smaller than 66 atomic %, when summation of In and M is assumed to be 100 atomic %.
The oxide semiconductor has a large energy gap. The energy gap of the oxide semiconductor is greater than or equal to 2.7 eV and less than or equal to 4.9 eV, preferably greater than or equal to 3 eV and less than or equal to 4.7 eV, more preferably greater than or equal to 3.2 eV and less than or equal to 4.4 eV.
In order to obtain stable electrical characteristics of a transistor, it is effective to reduce the concentration of impurities in the oxide semiconductor so that the oxide semiconductor is highly purified to be intrinsic. In the oxide semiconductor, a light element, a semimetal element, a metal element, and the like (lower than 1 atomic %) other than main components serve as impurities. For example, hydrogen, lithium, carbon, nitrogen, fluorine, sodium, silicon, chlorine, potassium, calcium, titanium, iron, nickel, copper, germanium, strontium, zirconium, and hafnium might be impurities in the oxide semiconductor. Thus, it is preferable to reduce the concentration of impurities in a film adjacent to the oxide semiconductor.
For example, in some cases, silicon in an oxide semiconductor forms impurity states. Further, in some cases, silicon at the surface of an oxide semiconductor forms impurity states. Thus, the concentration of silicon in an oxide semiconductor or at the surface of an oxide semiconductor, which is measured by secondary ion mass spectrometry (SIMS), is preferably lower than 1×1019 atoms/cm3, more preferably lower than 5×1018 atoms/cm3, still more preferably lower than 2×1018 atoms/cm3.
Further, in some cases, hydrogen in an oxide semiconductor forms impurity states, whereby carrier density is increased. Thus, the concentration of hydrogen in the oxide semiconductor, which is measured by SIMS, is lower than or equal to 2×1020 atoms/cm3, preferably lower than or equal to 5×1019 atoms/cm3, more preferably lower than or equal to 1×1019 atoms/cm3, still more preferably lower than or equal to 5×1018 atoms/cm3. Further, in some cases, nitrogen in an oxide semiconductor forms impurity levels, whereby carrier density is increased. Thus, the concentration of nitrogen in the oxide semiconductor, which is measured by SIMS, is lower than 5×1019 atoms/cm3, preferably lower than or equal to 5×1018 atoms/cm3, more preferably lower than or equal to 1×1018 atoms/cm3, still more preferably lower than or equal to 5×1017 atoms/cm3.
An oxide semiconductor film is classified roughly into a single-crystal oxide semiconductor film and a non-single-crystal oxide semiconductor film. The non-single-crystal oxide semiconductor film includes any of a c-axis aligned crystalline oxide semiconductor (CAAC-OS) film, a polycrystalline oxide semiconductor film, a microcrystalline oxide semiconductor film, an amorphous oxide semiconductor film, and the like.
An oxide semiconductor film may include a CAAC-OS film. First, the CAAC-OS film is described.
The CAAC-OS film is one of oxide semiconductor films including a plurality of crystal parts, and most of the crystal parts each fit inside a cube whose one side is less than 100 nm. Thus, there is a case where a crystal part included in the CAAC-OS film fits inside a cube whose one side is less than 10 nm, less than 5 nm, or less than 3 nm.
In a transmission electron microscope (TEM) image of the CAAC-OS film, a boundary between crystal parts, that is, a grain boundary is not clearly observed. Thus, in the CAAC-OS film, a reduction in electron mobility due to the grain boundary is less likely to occur.
According to the TEM image of the CAAC-OS film observed in the direction substantially parallel to a sample surface (cross-sectional TEM image), metal atoms are arranged in a layered manner in the crystal parts. Each metal atom layer has a morphology reflected by a surface over which the CAAC-OS film is formed (hereinafter, a surface over which the CAAC-OS film is formed is referred to as a formation surface) or a top surface of the CAAC-OS film, and is arranged in parallel to the formation surface or the top surface of the CAAC-OS film.
On the other hand, according to the TEM image of the CAAC-OS film observed in a direction substantially perpendicular to the sample surface (plan TEM image), metal atoms are arranged in a triangular or hexagonal configuration in the crystal parts. However, there is no regularity of arrangement of metal atoms between different crystal parts.
From the results of the cross-sectional TEM image and the plan TEM image, alignment is found in the crystal parts in the CAAC-OS film.
A CAAC-OS film is subjected to structural analysis with an X-ray diffraction (XRD) apparatus. For example, when the CAAC-OS film including an InGaZnO4 crystal is analyzed by an out-of-plane method, a peak appears frequently when the diffraction angle (2θ) is around 31°. This peak is derived from the (009) plane of the InGaZnO4 crystal, which indicates that crystals in the CAAC-OS film have c-axis alignment, and that the c-axes are aligned in a direction substantially perpendicular to the formation surface or the top surface of the CAAC-OS film.
On the other hand, when the CAAC-OS film is analyzed by an in-plane method in which an X-ray enters a sample in the direction substantially perpendicular to the c-axis, a peak appears frequently when 2θ is around 56°. This peak is derived from the (110) plane of the InGaZnO4 crystal. Here, analysis (ϕ scan) is performed under conditions where the sample is rotated around a normal vector of a sample surface as an axis (ϕ axis) with 2θ fixed at around 56°. In the case where the sample is a single-crystal oxide semiconductor film of InGaZnO4, six peaks appear. The six peaks are derived from crystal planes equivalent to the (110) plane. On the other hand, in the case of a CAAC-OS film, a peak is not clearly observed even when ϕ scan is performed with 2θ fixed at around 56°.
According to the above results, in the CAAC-OS film having c-axis alignment, while the directions of a-axes and b-axes are different between crystal parts, the c-axes are aligned in a direction parallel to a normal vector of a formation surface or a normal vector of a top surface. Thus, each metal atom layer arranged in a layered manner observed in the cross-sectional TEM image corresponds to a plane parallel to the a-b plane of the crystal.
Note that the crystal part is formed concurrently with deposition of the CAAC-OS film or is formed through crystallization treatment such as heat treatment. As described above, the c-axis of the crystal is aligned in the direction parallel to a normal vector of a formation surface or a normal vector of a top surface. Thus, for example, in the case where the shape of the CAAC-OS film is changed by etching or the like, the c-axis might not be necessarily parallel to a normal vector of a formation surface or a normal vector of a top surface of the CAAC-OS film.
The degree of crystallinity in the CAAC-OS film is not necessarily uniform. For example, in the case where crystal growth leading to the CAAC-OS film occurs from the vicinity of the top surface of the film, the degree of the crystallinity in the vicinity of the top surface is higher than that in the vicinity of the formation surface in some cases. Further, when an impurity is added to the CAAC-OS film, the crystallinity in a region to which the impurity is added is changed, and the degree of crystallinity in the CAAC-OS film varies depending on regions.
Note that when the CAAC-OS film with an InGaZnO4 crystal is analyzed by an out-of-plane method, a peak of 2θ may also be observed at around 36°, in addition to the peak of 2θ at around 31°. The peak of 2θ at around 36° indicates that a crystal having no c-axis alignment is included in part of the CAAC-OS film. It is preferable that in the CAAC-OS film, a peak of 2θ appear at around 31° and a peak of 2θ do not appear at around 36°.
The CAAC-OS film is an oxide semiconductor film having low impurity concentration. The impurity is an element other than the main components of the oxide semiconductor film, such as hydrogen, carbon, silicon, or a transition metal element. In particular, an element that has higher bonding strength to oxygen than a metal element included in the oxide semiconductor film, such as silicon, disturbs the atomic arrangement of the oxide semiconductor film by depriving the oxide semiconductor film of oxygen and causes a decrease in crystallinity. Further, a heavy metal such as iron or nickel, argon, carbon dioxide, or the like has a large atomic radius (molecular radius), and thus disturbs the atomic arrangement of the oxide semiconductor film and causes a decrease in crystallinity when it is contained in the oxide semiconductor film. Note that the impurity contained in the oxide semiconductor film might serve as a carrier trap or a carrier generation source.
The CAAC-OS film is an oxide semiconductor film having a low density of defect states. For example, oxygen vacancies in the oxide semiconductor film serve as carrier traps or serve as carrier generation sources in some cases when hydrogen is captured therein.
The state in which the impurity concentration is low and the density of defect states is low (the number of oxygen vacancies is small) is referred to as a highly purified intrinsic state or a substantially highly purified intrinsic state. A highly purified intrinsic or substantially highly purified intrinsic oxide semiconductor film has few carrier generation sources, and thus can have a low carrier density. Thus, a transistor including the oxide semiconductor film rarely has negative threshold voltage (is rarely normally on). The highly purified intrinsic or substantially highly purified intrinsic oxide semiconductor film has few carrier traps. Accordingly, the transistor including the oxide semiconductor film has small variations in electrical characteristics and high reliability. Electric charge trapped by the carrier traps in the oxide semiconductor film takes a long time to be released, and might behave like fixed electric charge. Thus, the transistor that includes the oxide semiconductor film having high impurity concentration and a high density of defect states has unstable electrical characteristics in some cases.
With the use of the CAAC-OS film in a transistor, variation in the electrical characteristics of the transistor due to irradiation with visible light or ultraviolet light is small.
Next, a microcrystalline oxide semiconductor film is described.
In an image obtained with the TEM, crystal parts cannot be found clearly in the microcrystalline oxide semiconductor in some cases. In most cases, the size of a crystal part in the microcrystalline oxide semiconductor is greater than or equal to 1 nm and less than or equal to 100 nm, or greater than or equal to 1 nm and less than or equal to 10 nm. A microcrystal with a size greater than or equal to 1 nm and less than or equal to 10 nm, or a size greater than or equal to 1 nm and less than or equal to 3 nm is specifically referred to as nanocrystal (nc). An oxide semiconductor film including nanocrystal is referred to as an nc-OS (nanocrystalline oxide semiconductor) film. In an image of the nc-OS obtained with a TEM, for example, a crystal grain cannot be observed clearly in some cases.
In the nc-OS film, a microscopic region (for example, a region with a size greater than or equal to 1 nm and less than or equal to 10 nm, in particular, a region with a size greater than or equal to 1 nm and less than or equal to 3 nm) has a periodic atomic order. Further, there is no regularity of crystal orientation between different crystal parts in the nc-OS film; thus, the orientation is not observed in the whole film. Accordingly, in some cases, the nc-OS film cannot be distinguished from an amorphous oxide semiconductor depending on an analysis method. For example, when the nc-OS film is subjected to structural analysis by an out-of-plane method with an XRD apparatus using an X-ray having a diameter larger than that of a crystal part, a peak which shows a crystal plane does not appear. Further, a halo pattern is shown in an electron diffraction pattern (also referred to as a selected-area electron diffraction area) of the nc-OS film obtained by using an electron beam having a diameter (e.g., larger than or equal to 50 nm) larger than that of a crystal part. Meanwhile, spots are shown in a nanobeam electron diffraction pattern of the nc-OS film obtained by using an electron beam having a diameter (e.g., larger than or equal to 1 nm and smaller than or equal to 30 nm) close to, or smaller than or equal to that of a crystal part. Further, in a nanobeam electron diffraction pattern of the nc-OS film, regions with high luminance in a circular (ring) pattern are shown in some cases. Also in a nanobeam electron diffraction pattern of the nc-OS film, a plurality of spots are shown in a ring-like region in some cases.
Since the nc-OS film is an oxide semiconductor film having more regularity than the amorphous oxide semiconductor film, the nc-OS film has a lower density of defect states than the amorphous oxide semiconductor film. However, there is no regularity of crystal orientation between different crystal parts in the nc-OS film; hence, the nc-OS film has a higher density of defect states than the CAAC-OS film.
Note that an oxide semiconductor film may be a stacked film including two or more kinds of, for example, an amorphous oxide semiconductor film, a microcrystalline oxide semiconductor film, and a CAAC-OS film.
For example, a multilayer film in which an oxide semiconductor layer (S1) and an oxide semiconductor layer (S2) are formed in this order may be used.
In this case, for example, the energy (Ec) at the bottom of the conduction band of the oxide semiconductor layer (S2) is set to be higher than that of the oxide semiconductor layer (S1). Specifically, for the oxide semiconductor layer (S2), an oxide semiconductor having lower electron affinity than the oxide semiconductor layer (S1) by greater than or equal to 0.07 eV and less than or equal to 1.3 eV, preferably greater than or equal to 0.1 eV and less than or equal to 0.7 eV, more preferably greater than or equal to 0.15 eV and less than or equal to 0.4 eV is used. Note that the electron affinity refers to an energy gap between the vacuum level and the bottom of the conduction band.
Alternatively, for example, the energy gap of the oxide semiconductor layer (S2) is set to be larger than that of the oxide semiconductor layer (S1). The energy gap can be obtained by, for example, an optical method. Specifically, for the oxide semiconductor layer (S2), an oxide semiconductor having a larger energy gap than the oxide semiconductor layer (S1) by greater than or equal to 0.1 eV and less than or equal to 1.2 eV, preferably greater than or equal to 0.2 eV and less than or equal to 0.8 eV is used.
Alternatively, the oxide semiconductor may be, for example, a multilayer film in which the oxide semiconductor layer (S1), the oxide semiconductor layer (S2), and an oxide semiconductor layer (S3) are formed in this order.
For example, the energy (Ec) at the bottom of the conduction band of the oxide semiconductor layer (S2) is set to be lower than that of the oxide semiconductor layer (S1) and the oxide semiconductor layer (S3). Specifically, for the oxide semiconductor layer (S2), an oxide semiconductor having higher electron affinity than the oxide semiconductor layer (S1) and the oxide semiconductor film (S3) by greater than or equal to 0.07 eV and less than or equal to 1.3 eV, preferably greater than or equal to 0.1 eV and less than or equal to 0.7 eV, more preferably greater than or equal to 0.15 eV and less than or equal to 0.4 eV is used.
Alternatively, for example, the energy gap of the oxide semiconductor layer (S2) may be smaller than that of each of the oxide semiconductor layers (S1) and (S3). Specifically, for the oxide semiconductor layer (S2), an oxide semiconductor having smaller energy gap than the oxide semiconductor layers (S1) and (S3) by greater than or equal to 0.1 eV and smaller than or equal to 1.2 eV or by greater than or equal to 0.2 eV and smaller than or equal to 0.8 eV is used.
For example, to increase the on-state current of the transistor, the thickness of the oxide semiconductor layer (S3) is preferably as low as possible. For example, the thickness of the oxide semiconductor layer (S3) is less than 10 nm, preferably less than or equal to 5 nm, more preferably less than or equal to 3 nm. Meanwhile, the oxide semiconductor layer (S3) blocks entry of elements (e.g., silicon) contained in the insulating film 104 to the oxide semiconductor layer (S2) having a high current density. Thus, the oxide semiconductor layer (S3) preferably has a certain thickness. The thickness of the oxide semiconductor layer (S3) is, for example, greater than or equal to 0.3 nm, preferably greater than or equal to 1 nm, more preferably greater than or equal to 2 nm.
The thickness of the oxide semiconductor layer (S1) is preferably larger than that of the oxide semiconductor layer (S2), and the thickness of the oxide semiconductor layer (S2) may be larger than that of the oxide semiconductor layer (S3). Specifically, the thickness of the oxide semiconductor layer (S1) is greater than or equal to 20 nm, preferably greater than or equal to 30 nm, more preferably greater than or equal to 40 nm, still more preferably greater than or equal to 60 nm. With the oxide semiconductor layer (S1) having the above thickness, the interface between the insulating film and the oxide semiconductor layer (S1) can be separated from the oxide semiconductor layer (S2) with high current density to have a distance greater than or equal to 20 nm, preferably greater than or equal to 30 nm, more preferably greater than or equal to 40 nm, still more preferably greater than or equal to 60 nm. To prevent the productivity of the semiconductor device from being lowered, the thickness of the oxide semiconductor layer (S1) is less than or equal to 200 nm, preferably less than or equal to 120 nm, more preferably less than or equal to 80 nm. The thickness of the oxide semiconductor layer (S2) is greater than or equal to 3 nm and less than or equal to 100 nm, preferably greater than or equal to 3 nm and less than or equal to 80 nm, more preferably greater than or equal to 3 nm and less than or equal to 50 nm.
Next, a method for forming the oxide semiconductor film is described. The oxide semiconductor film may be formed by a sputtering method, a CVD method, an MBE method, an ALD method, or a PLD method.
When In-M-Zn oxide is formed by a sputtering method for the oxide semiconductor film to be a semiconductor film 106, the atomic ratio of the target may be as follows: In:M:Z=3:1:1, 3:1:2, 3:1:4, 1:1:0.5, 1:1:1, 1:1:2, 1:3:1, 1:3:2, 1:3:4, 1:3:6, 1:6:2, 1:6:4, 1:6:6, 1:6:8, 1:6:10, 1:9:2, 1:9:4, 1:9:6, 1:9:8, 1:9:10, or the like. Examples of the element M include aluminum, gallium, yttrium, and tin.
When the oxide semiconductor film is formed by a sputtering method, it is formed under an atmosphere containing oxygen. The proportion of oxygen in the atmosphere is, for example, larger than or equal to 10 volume %, preferably larger than or equal to 20 volume %, more preferably larger than or equal to 50 volume %, still more preferably larger than or equal to 80 volume %. In particular, the proportion of oxygen in the atmosphere is preferably 100 volume %. When the proportion of oxygen in the atmosphere is 100 volume %, the concentration of impurities (e.g., a rare gas) contained in the oxide semiconductor film to be the semiconductor film 106 can be reduced.
In the case where the oxide semiconductor film to be the semiconductor film 106 is formed by a sputtering method, a film having an atomic ratio deviated from the atomic ratio of the target is formed in some cases. For example, when zinc is formed under an atmosphere containing oxygen, the atomic ratio of zinc in the formed film is easily smaller than that in the target in some cases. Specifically, the atomic percentage of zinc in the film is higher than or equal to approximately 40% and lower than or equal to approximately 90% of that of zinc in the target in some cases. Further, for example, when indium is formed under an atmosphere containing oxygen, the atomic ratio of indium in the formed film is easily smaller than that in the target in some cases.
First heat treatment is preferably performed after the oxide semiconductor film to be the semiconductor film 106 is formed. The first heat treatment may be performed at higher than or equal to 70° C. and lower than or equal to 450° C., preferably higher than or equal to 100° C. and lower than or equal to 300° C., more preferably higher than or equal to 150° C. and lower than or equal to 250° C. The first heat treatment is performed in an inert gas atmosphere or an atmosphere containing an oxidizing gas at 10 ppm or more, 1 volume % or more, or 10 volume % or more. The first heat treatment may be performed under a reduced pressure. Alternatively, the first heat treatment may be performed in such a manner that heat treatment is performed in an inert gas atmosphere, and then another heat treatment is performed in an atmosphere containing an oxidizing gas at 10 ppm or more, 1 volume % or more, or 10 volume % or more in order to compensate desorbed oxygen. The first heat treatment can remove impurities such as hydrogen and water from the oxide semiconductor film to be the oxide semiconductor film 106. In addition, the first heat treatment can highly purify the oxide semiconductor film to be the oxide semiconductor film 106.
<Formation of Insulating Film>
Next, an insulating film 108 is formed over the insulating film 104, the semiconductor film 106a, and the semiconductor film 106b (
The insulating film 108 can be formed using a material, a structure, and a method similar to those of the insulating film 104.
In the case where the insulating film 104 has a layered structure of films formed of different materials, the same material can be used for an upper layer of the insulating film 104 and the insulating film 108. When the same material is used for the upper layer of the insulating film 104 and the insulating film 108, the upper layer of the insulating film 104 and the insulating film 108 can be etched at the same time in etching of the insulating film 104 and the insulating film 108 in a later step. After that, a remaining lower layer of the insulating film 104 is etched. Thus, an opening in which the taper angle of the upper layer of the insulating film 104 and the insulating film 108 is different from the taper angle of the lower layer of the insulating film 104 can be formed. The opening having the different taper angles can prevent disconnection of a conductive film formed in the opening.
<Formation of Mask and Etching of Insulating Film>
Next, a resist mask 110 is formed over the insulating film 108 by a photolithography process (
Next, portions of the insulating film 104 and the insulating film 108 that the resist mask 110 does not overlap are removed by etching to form an opening 111a, an opening 111b, an opening 111c, and an opening 111d (
As illustrated in
The opening 111b is formed in such a manner that portions of the insulating film 104 and the insulating film 108 that overlaps the conductive film 102a and overlaps neither the semiconductor film 106a nor the semiconductor film 106b and that the resist mask 110 does not overlap are removed.
Then, the resist mask 110 is removed (see
<Formation of Conductive Film>
Next, a conductive film is formed over the insulating film 108, the semiconductor film 106a, the semiconductor film 106b, and the conductive film 102a, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form a conductive film 114a, a conductive film 114b, and a conductive film 114c (
The conductive film 114a is electrically connected to the conductive film 102a and the semiconductor film 106a. In addition, the conductive film 114b and the conductive film 114c are electrically connected to the semiconductor film 106b.
The conductive film 114a can function as a wiring that electrically connects the conductive film 102a and the semiconductor film 106a. The conductive film 114b can function as a source electrode in the transistor 150, and the conductive film 114c can function as a drain electrode in the transistor 150.
The conductive films 114a, 114b, and 114c can be formed using a material, a structure, and a method similar to those of the conductive films 102a and 102b.
Through the above-described steps, the transistor 150 and the connection portion 160 can be formed.
As described above, in the manufacturing method 1, at the same time as forming the openings in the portions of the insulating film 108 that overlap the semiconductor films, the opening is formed in the insulating film 104 as well as in the insulating film 108 in the portion that does not overlap the semiconductor films. This step enables the number of masks and the number of photolithography processes to be reduced compared to the case where openings are formed separately in the insulating film 108 and the insulating film 104. Thus, the manufacturing time and manufacturing cost of the semiconductor device can be reduced.
<<Manufacturing Method 2>>
A method for forming the transistor 150 and the connection portion 160, which are illustrated in
The substrate 100, the conductive films 102a and 102b, the insulating film 104, the semiconductor films 106a and 106b, and the insulating film 108, which are illustrated in
<Formation of Mask and Etching of Insulating Film>
A resist mask 210 is formed over the insulating film 108 by a photolithography process (
The resist mask 210 is formed by a photolithography process using a multi-tone mask (a half-tone photomask or a gray-tone photomask).
Next, portions of the insulating film 104 and the insulating film 108 that overlap the conductive film 102a and that the resist mask 210 does not overlap are removed by etching to form the opening 111b (
Next, ashing is performed on the resist mask 210. The ashing reduces the area (the volume in three dimensions) and thickness of the resist mask 210. Thus, part of the resist mask 210 that is in the region 210b and has a small thickness is removed to form a resist mask 212 (
The ashing can be performed with, for example, oxygen plasma.
Next, portions of the insulating film 108 that the resist mask 212 does not overlap are removed by etching to form an opening 211a, an opening 211b, an opening 211c, and an opening 211d (
As illustrated in
The opening 211b is formed in such a manner that a portion of the insulating film 108 that overlaps neither the semiconductor film 106a nor the semiconductor film 106b and that the resist mask 212 does not overlap is removed. As illustrated in FIG. 5C, the opening 211b is formed in such a manner that part of the insulating film 108 that is in the vicinity of the opening 111b is removed to enlarge the opening in the insulating film 108. This can prevent disconnection of a conductive film to be formed over and in the opening 211b in a later step.
Then, the resist mask 212 is removed (see
<Formation of Conductive Film>
Next, a conductive film is formed over the insulating film 108, the semiconductor film 106a, the semiconductor film 106b, and the conductive film 102a, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form the conductive films 114a, 114b, and 114c (
The conductive films 114a, 114b, and 114c can be formed using a material, a structure, and a method similar to those in the manufacturing method 1.
Through the above-described steps, the transistor 150 and the connection portion 160 can be formed.
In the manufacturing method 2, as described above, the use of the multi-tone mask enables the openings 211a, 211b, 211c, and 211d to be formed using one mask. In addition, in the opening 211b, an opening in the insulating film 108 can be larger than an opening in the insulating film 104, which can prevent disconnection of the conductive film 114a.
The above-described steps can reduce the number of masks and the number of photolithography processes. Thus, the manufacturing time and manufacturing cost of the semiconductor device can be reduced. In addition, the yield and reliability of the semiconductor device can be improved.
<<Manufacturing Method 3>>
A method for forming the transistor 150 and the connection portion 160, which are illustrated in
The substrate 100, the conductive films 102a and 102b, and the insulating film 104, which are illustrated in
<Formation of Semiconductor Film>
A semiconductor film 106 is formed over the insulating film 104. The semiconductor film 106 can be formed using a material, a structure, and a method similar to those in the manufacturing method 1.
<Formation of Mask and Etching of Insulating Film and Semiconductor Film>
A resist mask 307 is formed over the semiconductor film 106 by a photolithography process (
The resist mask 307 is formed by a photolithography process using a multi-tone mask (a half-tone photomask or a gray-tone photomask).
Next, portions of the insulating film 104 and the semiconductor film 106 that overlap the conductive film 102a and that the resist mask 307 does not overlap are removed by etching to form an opening 308b (
Next, ashing is performed on the resist mask 307. The ashing reduces the area (the volume in three dimensions) of the resist mask 307. Thus, part of the resist mask 307 that is in the region 307b and has a small thickness is removed to form a resist mask 309 (
The ashing can be performed with, for example, oxygen plasma.
Next, a portion of the semiconductor film 106 that the resist mask 309 does not overlap is removed by etching to form the semiconductor film 106a and the semiconductor film 106b (
Then, the resist mask 309 is removed (
<Formation of Insulating Film>
Next, an insulating film is formed over the insulating film 104, the semiconductor film 106a, and the semiconductor film 106b, and a resist mask is formed over the insulating film by a photolithography process. Then, part of the insulating film is etched using the resist mask to form the insulating film 108 that has an opening 311a, an opening 311b, an opening 311c, and an opening 311d (
As illustrated in
The opening 311b is formed in such a manner that a portion of the insulating film that overlaps neither the semiconductor film 106a nor the semiconductor film 106b is removed. Note that as illustrated in
The insulating film 108 functions as a film that protects the channel region in the semiconductor film 106b in the transistor 150 and can be formed using a material, a structure, and a method similar to those in the manufacturing method 1.
<Formation of Conductive Film>
Next, a conductive film is formed over the insulating film 108, the semiconductor film 106a, the semiconductor film 106b, and the conductive film 102a, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form the conductive films 114a, 114b, and 114c (
The conductive films 114a, 114b, and 114c can be formed using a material, a structure, and a method similar to those in the manufacturing method 1.
Through the above-described steps, the transistor 150 and the connection portion 160 can be formed.
In the manufacturing method 3, as described above, the use of the half-tone photomask enables the opening in the insulating film 104 and the semiconductor films 106a and 106b to be formed using one mask. In addition, in the opening 311b, the opening in the insulating film 108 can be larger than the opening in the insulating film 104, which can prevent disconnection of the conductive film 114a.
The above-described steps can reduce the number of masks and the number of photolithography processes. Thus, the manufacturing time and manufacturing cost of the semiconductor device can be reduced. In addition, the yield and reliability of the semiconductor device can be improved.
<Variations on Opening>
Note that the connection portion 160 illustrated in
First, the resist mask 307 that has a shape illustrated in
After that, the semiconductor film 106a and the semiconductor film 106b are formed by steps similar to those illustrated in
Next, an insulating film is formed over the insulating film 104, the semiconductor film 106a, and the semiconductor film 106b, and a resist mask is formed over the insulating film by a photolithography process. Then, part of the insulating film is etched using the resist mask to form the insulating film 108 that has the openings 311a, 311c, and 311d and an opening 312b. In this case, the opening 312b in the insulating film 108 is formed so as to be smaller than the opening 308b in the insulating film 104.
Through the above-described steps, the connection portion 160 illustrated in
Even the above-described steps enable the opening in the insulating film 104 and the semiconductor films 106a and 106b to be formed using one mask and disconnection of the conductive film 114a to be prevented. Thus, the number of masks, the number of photolithography processes, and the manufacturing time and manufacturing cost of the semiconductor device can be reduced. In addition, the yield and reliability of the semiconductor device can be improved.
<<Manufacturing Method 4>>
A method for forming the transistor 150 and the connection portion 160, which are illustrated in
The substrate 100, the conductive films 102a and 102b, the insulating film 104, the semiconductor films 106a and 106b, the insulating film 108, and the openings 111a, 111b, 111c, and 111d, which are illustrated in
<Ashing of Mask>
The openings 111a, 111b, 111c, and 111d are formed using the resist mask 110 as illustrated in
The ashing reduces the area (the volume in three dimensions) and thickness of the resist mask 110 to form a resist mask 412 (
Next, the portions of the insulating film 108 that the resist mask 412 does not overlap are removed by etching to form an opening 411a, an opening 411b, an opening 411c, and an opening 411d (
As illustrated in
The opening 411b is formed in such a manner that a portion of the insulating film that overlaps the conductive film 102a and overlaps neither the semiconductor film 106a nor the semiconductor film 106b is removed. As illustrated in
The resist mask 412 is formed by ashing the resist mask 110. Thus, the differences in size between the resist mask 110 and the resist mask 412, that is, the widths of parts of the insulating film 108 that are not covered with the resist mask 412 are substantially equal.
Thus, the widths of steps formed by the insulating film 104 and the insulating film 108 in the opening 411b, that is, Ls in
Then, the resist mask 412 is removed (see
<Formation of Conductive Film>
Next, a conductive film is formed over the insulating film 108, the semiconductor film 106a, the semiconductor film 106b, and the conductive film 102a, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form the conductive films 114a, 114b, and 114c (
The conductive films 114a, 114b, and 114c can be formed using a material, a structure, and a method similar to those in the manufacturing method 1.
Through the above-described steps, the transistor 150 and the connection portion 160 can be formed.
As described above, in the manufacturing method 4, at the same time as forming the openings in the portions of the insulating film 108 that overlap the semiconductor films, the opening is formed in the insulating film 104 as well as in the insulating film 108 in the portion that does not overlap the semiconductor films. This step enables the number of masks and the number of photolithography processes to be reduced compared to the case where openings are formed separately in the insulating film 108 and the insulating film 104. In addition, the ashing performed on the resist mask 110 enables the opening in the insulating film 108 to be larger than the opening in the insulating film 104 in the opening 411b, which can prevent disconnection of the conductive film 114a.
The above-described steps can reduce the number of masks and the number of photolithography processes. Thus, the manufacturing time and manufacturing cost of the semiconductor device can be reduced. In addition, the yield and reliability of the semiconductor device can be improved.
A method for manufacturing a semiconductor device that is one embodiment of the present invention is described with reference to
The method for manufacturing a semiconductor device that is described in this embodiment can be applied to a case where a plurality of conductive films are formed above a transistor. For example, the method is suitable for a liquid crystal display device in an in-plane-switching (IPS) mode or a fringe field switching (FFS) mode where a common electrode and a pixel electrode are formed on the same substrate.
<<Manufacturing Method 5>>
A method for forming a connection portion 550 and a connection portion 560, which are illustrated in
<Lower Structure>
First, a substrate provided with a conductive film is prepared. The substrate may be the substrate over which the transistor 150 and the connection portion 160 are formed that is described in Embodiment 1 or a substrate over which a conductive film having a different structure is formed by another method. The substrate is not limited to, for example, a substrate provided with the bottom-gate transistor 150 described in Embodiment 1 and may be a substrate provided with a top-gate transistor.
In this embodiment, a substrate provided with the transistor 150 in the cross section X1-X2 and the connection portion 160 in the cross section Y1-Y2, which are formed in a manner similar to that of the manufacturing method 2 in Embodiment 1, and the insulating film 104, the insulating film 108, and the conductive film 114d in the cross section Z1-Z2, which are formed through steps similar to those in the manufacturing method 2, is prepared (
<Formation of Insulating Film>
An insulating film 500 is formed over the conductive films 114a, 114b, 114c, and 114d (
<Formation of Insulating Film>
Next, an insulating film 502 is formed over the insulating film 500 (
The insulating film 502 can be formed of a single layer or a stacked layer of, for example, acrylic, acrylamide, ester, and another known material.
<Formation of Conductive Film>
Next, a conductive film 504 is formed over the insulating film 502 (
For the conductive film 504, a light-transmitting conductive material such as indium oxide containing tungsten oxide, indium zinc oxide containing tungsten oxide, indium oxide containing titanium oxide, indium tin oxide containing titanium oxide, indium tin oxide (hereinafter referred to as ITO), indium zinc oxide, or indium tin oxide to which silicon oxide is added can be used.
A conductive composition containing a conductive macromolecule (also referred to as a conductive polymer) can be used to form the conductive film 504. The sheet resistance of the light-transmitting conductive film formed using a conductive composition is preferably less than or equal to 10000 Ω/square and light transmittance thereof is preferably greater than or equal to 70% at a wavelength of 550 nm. Further, the resistivity of the conductive high molecule contained in the conductive composition is preferably 0.1 Ω·cm or less.
As the conductive high molecule, what is called a π-electron conjugated conductive polymer can be used. Examples are polyaniline and a derivative thereof, polypyrrole and a derivative thereof, polythiophene and a derivative thereof, and a copolymer of two or more of aniline, pyrrole, and thiophene and a derivative thereof.
The conductive film 504 can be formed of a single layer or a stacked layer of any of the materials given above.
<Formation of Mask and Etching of Conductive Film and Insulating Film>
Next, a resist mask 506 is formed over the conductive film 504 by a photolithography process (
The resist mask 506 is formed by a photolithography process using a multi-tone mask (a half-tone photomask or a gray-tone photomask).
Next, portions of the insulating film 500, the insulating film 502, and the conductive film 504 that the resist mask 506 does not overlap are removed by etching to form an opening 507a and an opening 507c (
Next, ashing is performed on the resist mask 506. The ashing reduces the area (the volume in three dimensions) and thickness of the resist mask 506. Thus, part of the resist mask 506 that is in the region 506b and has a small thickness is removed to form a resist mask 508 (
The ashing can be performed with, for example, oxygen plasma.
Next, a portion of the conductive film 504 that the resist mask 508 does not overlap is removed by etching, and then the resist mask 508 is removed to form a conductive film 504a (
<Formation of Insulating Film>
Next, an insulating film is formed over the conductive film 504a, the insulating film 502, the insulating film 500, the conductive film 114d, and the conductive film 114c, and a resist mask is formed over the insulating film by a photolithography process. After that, part of the insulating film is etched using the resist mask to form an insulating film 510 (
The insulating film 510 can be formed using a material, a structure, and a method similar to those of the insulating film 104 in Embodiment 1.
<Formation of Conductive Film>
Next, a conductive film is formed over the insulating film 510, the conductive film 504a, the insulating film 502, the insulating film 500, the conductive film 114d, and the conductive film 114c, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form a conductive film 512a and a conductive film 512b (
The conductive film 512a is electrically connected to the conductive film 114d and the conductive film 504a. The conductive film 512b is electrically connected to the conductive film 114c. The conductive film 512b can function as a pixel electrode in a liquid crystal display device. In addition, although not illustrated, a portion where the conductive film 504a and the conductive film 512b overlap each other can function as a capacitor. However, the capacitor is not limited thereto, and a portion other than the portion where the conductive film 504a and the conductive film 512b overlap each other can function as a capacitor. For example, a portion where the conductive film 504a and a conductive film formed separately overlap each other may function as a capacitor.
The conductive film 512a and the conductive film 512b can be formed using a material, a structure, and a method similar to those of the conductive film 504a.
Through the above-described steps, the connection portion 550 and the connection portion 560 can be formed.
In the manufacturing method 5, as described above, the use of the half-tone photomask enables the openings 507a and 507c and the conductive film 504a to be formed using one mask.
The above-described steps can reduce the number of masks and the number of photolithography processes. Thus, the manufacturing time and manufacturing cost of the semiconductor device can be reduced.
Another embodiment of the method for manufacturing a semiconductor device that is one embodiment of the present invention, which is described in Embodiment 2, is described with reference to
The method for manufacturing a semiconductor device that is described in this embodiment can be applied to a case where a plurality of conductive films are formed above a transistor. For example, the method is suitable for a liquid crystal display device in an in-plane-switching (IPS) mode or a fringe field switching (FFS) mode where a common electrode and a pixel electrode are formed on the same substrate.
<<Manufacturing Method 6>>
A method for forming a connection portion 650 and a connection portion 660, which are illustrated in
<Formation of Insulating Film>
Next, an insulating film is formed over the conductive film 504a, the insulating film 502, the insulating film 500, the conductive film 114c, and the conductive film 114d, and a resist mask is formed over the insulating film by a photolithography process. Then, part of the insulating film is etched using the resist mask to form an insulating film 610 (
Unlike the manufacturing method 5 in Embodiment 2, the insulating film 610 is also formed inside the opening 507a and the opening 507c. Thus, the side surfaces of the insulating film 502 in the opening 507a and the opening 507c are covered with the insulating film 610. This structure can suppress diffusion of impurities inside the insulating film 502 or impurities and the like attached to the side surfaces of the insulating film 502 in the opening 507a and the opening 507c in a step such as ashing of the multi-tone mask to the outside of the insulating film 502. When the impurities are mixed in liquid crystal in, for example, a liquid crystal display device described later in Embodiment 4, the liquid crystal deteriorates. The suppression of diffusion of the impurities by the insulating film 502 can prevent the deterioration of the liquid crystal display device.
<Formation of Conductive Film>
Next, a conductive film is formed over the insulating film 610, the conductive film 504a, the insulating film 502, the insulating film 500, the conductive film 114c, and the conductive film 114d, and a resist mask is formed over the conductive film by a photolithography process. After that, part of the conductive film is etched using the resist mask to form a conductive film 612a and a conductive film 612b (
The conductive film 612a is electrically connected to the conductive film 114d and the conductive film 504a. The conductive film 612b is electrically connected to the conductive film 114c. The conductive film 612b can function as a pixel electrode in a liquid crystal display device. In addition, although not illustrated, a portion where the conductive film 504a and the conductive film 612b overlap each other can function as a capacitor. However, the capacitor is not limited thereto, and a portion other than the portion where the conductive film 504a and the conductive film 612b overlap each other can function as a capacitor. For example, a portion where the conductive film 504a and a conductive film formed separately overlap each other may function as a capacitor.
The conductive film 612a and the conductive film 612b can be formed using a material, a structure, and a method similar to those of the conductive film 504a.
Through the above-described steps, the connection portion 650 and the connection portion 660 can be formed.
As is understood from the cross-sectional views of
As described above, in the manufacturing method 6, the use of the half-tone mask enables the opening 507a, the opening 507c, and the conductive film 504a to be formed using one mask. In addition, diffusion of impurities from the side surfaces of the insulating film 502 can be suppressed.
The above-described steps can reduce the number of masks and the number of photolithography processes. Thus, the manufacturing time and manufacturing cost of the semiconductor device can be reduced. In addition, the semiconductor device can be used without a decrease in the reliability.
In this embodiment, a semiconductor device such as a display device, to which any of the methods for manufacturing a semiconductor device described in Embodiments 1 to 3 can be applied, is described.
The manufacturing method described in Embodiment 1 can be suitably used as a method for manufacturing a switching element of an active matrix liquid crystal display device and can be applied to liquid crystal display devices in a variety of modes such as a twisted nematic (TN) mode, a vertical alignment (VA) mode, and an IPS mode.
The manufacturing method described in Embodiment 1 can also be suitably used as a method for manufacturing a switching element of a light-emitting device including an active matrix organic EL element.
The manufacturing method described in Embodiment 2 and Embodiment 3 can be suitably used as a method for manufacturing a switching element of, particularly, a liquid crystal display device in an IPS mode. In this case, a pixel electrode having slits is formed. The stacking order of the pixel electrode and the common electrode in Embodiment 2 and Embodiment 3 may be switched to form a common electrode having slits.
The manufacturing methods described in Embodiments 1 to 3 can be suitably used as a method for manufacturing a semiconductor device such as a memory device, an arithmetic device, a CPU, or a microcomputer, without limitation to a display device and a light-emitting device.
A liquid crystal display device 1000 in an IPS (FFS) mode, in which the semiconductor device described in Embodiment 1 is used, is described below as an example of a semiconductor device with reference to
As illustrated in
As illustrated in
In a terminal portion, the substrate 1121 and the substrate 1111 are bonded to each other by a sealing material 1421. An electrode 1122 and an FPC 1433 are electrically connected to each other through a conductive film 1431 and a conductive film 1432. A conductive film 1422 and an FPC 1424 are electrically connected to each other through a conductive film 1423.
Although the structure in which the insulating film 502 that can function as a planarization film is provided is illustrated in
In this embodiment, examples of an electronic appliance including a liquid crystal display device to which one embodiment of the present invention is applied are described with reference to
Electronic appliances described in this embodiment each include the liquid crystal display device of one embodiment of the present invention in a display portion.
Examples of an electronic appliance including the liquid crystal display device are television devices (also referred to as televisions or television receivers), monitors of computers or the like, digital cameras, digital video cameras, digital photo frames, mobile phone sets (also referred to as mobile phones or mobile phone devices), portable game machines, portable information terminals, audio reproducing devices, and large-sized game machines such as pachinko machines. Specific examples of these electronic appliances are illustrated in
The television device 7100 can be operated with an operation switch of the housing 7101 or a separate remote controller 7111. With operation keys of the remote controller 7111, channels and volume can be controlled and images displayed on the display portion 7102 can be controlled. The remote controller 7111 may be provided with a display portion for displaying data output from the remote controller 7111.
Note that the television device 7100 is provided with a receiver, a modem, and the like. With the use of the receiver, general television broadcasting can be received. Moreover, when the television device is connected to a communication network with or without wires via the modem, one-way (from a sender to a receiver) or two-way (between a sender and a receiver or between receivers) information communication can be performed.
When the display portion 7402 of the mobile phone 7400 illustrated in
There are mainly three screen modes of the display portion 7402. The first mode is a display mode mainly for displaying an image. The second mode is an input mode mainly for inputting data such as characters. The third mode is a display-and-input mode in which two modes of the display mode and the input mode are combined.
For example, in the case of making a call or creating e-mail, a character input mode mainly for inputting characters is selected for the display portion 7402 so that characters displayed on the screen can be input.
When a sensing device including a sensor such as a gyroscope sensor or an acceleration sensor for sensing inclination is provided inside the mobile phone 7400, display on the screen of the display portion 7402 can be automatically changed in direction by determining the orientation of the mobile phone 7400 (whether the mobile phone 7400 is placed horizontally or vertically for a landscape mode or a portrait mode).
The screen modes are changed by touch on the display portion 7402 or operation with the operation button 7403 of the housing 7401. The screen modes can be switched depending on the kind of images displayed on the display portion 7402. For example, when a signal of an image displayed on the display portion is a signal of moving image data, the screen mode is switched to the display mode. When the signal is a signal of text data, the screen mode is switched to the input mode.
Moreover, in the input mode, if a signal detected by an optical sensor in the display portion 7402 is detected and the input by touch on the display portion 7402 is not performed for a certain period, the screen mode may be controlled so as to be changed from the input mode to the display mode.
The display portion 7402 may function as an image sensor. For example, an image of a palm print, a fingerprint, or the like is taken by touch on the display portion 7402 with the palm or the finger, whereby personal authentication can be performed. Further, when a backlight or a sensing light source which emits near-infrared light is provided in the display portion, an image of a finger vein, a palm vein, or the like can be taken.
Part of the display portion 7502a or the display portion 7502b can be used as a touch panel region, where data can be input by touching displayed operation keys. For example, a keyboard can be displayed on the entire region of the display portion 7502a so that the display portion 7502a is used as a touch screen, and the display portion 7502b can be used as a display screen.
This embodiment can be combined with any of the other embodiments as appropriate.
This application is based on Japanese Patent Application serial no. 2013-078908 filed with the Japan Patent Office on Apr. 4, 2013, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-078908 | Apr 2013 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5621556 | Fulks et al. | Apr 1997 | A |
| 5682211 | Yao et al. | Oct 1997 | A |
| 5731856 | Kim et al. | Mar 1998 | A |
| 5744864 | Cillessen et al. | Apr 1998 | A |
| 5867242 | Yao et al. | Feb 1999 | A |
| 6294274 | Kawazoe et al. | Sep 2001 | B1 |
| 6310669 | Kobayashi et al. | Oct 2001 | B1 |
| 6563174 | Kawasaki et al. | May 2003 | B2 |
| 6650378 | Kobayashi et al. | Nov 2003 | B2 |
| 6727522 | Kawasaki et al. | Apr 2004 | B1 |
| 6822703 | Hwang et al. | Nov 2004 | B2 |
| 6927809 | Gotoh et al. | Aug 2005 | B2 |
| 7049190 | Takeda et al. | May 2006 | B2 |
| 7061014 | Hosono et al. | Jun 2006 | B2 |
| 7064346 | Kawasaki et al. | Jun 2006 | B2 |
| 7105868 | Nause et al. | Sep 2006 | B2 |
| 7208760 | Hector et al. | Apr 2007 | B2 |
| 7211825 | Shih et al. | May 2007 | B2 |
| 7271409 | Young et al. | Sep 2007 | B2 |
| 7282782 | Hoffman et al. | Oct 2007 | B2 |
| 7291968 | Fish et al. | Nov 2007 | B2 |
| 7297977 | Hoffman et al. | Nov 2007 | B2 |
| 7315076 | Nomura et al. | Jan 2008 | B2 |
| 7323356 | Hosono et al. | Jan 2008 | B2 |
| 7358529 | Childs et al. | Apr 2008 | B2 |
| 7385224 | Ishii et al. | Jun 2008 | B2 |
| 7402506 | Levy et al. | Jul 2008 | B2 |
| 7411209 | Endo et al. | Aug 2008 | B2 |
| 7453065 | Saito et al. | Nov 2008 | B2 |
| 7453087 | Iwasaki | Nov 2008 | B2 |
| 7462862 | Hoffman et al. | Dec 2008 | B2 |
| 7468304 | Kaji et al. | Dec 2008 | B2 |
| 7501293 | Ito et al. | Mar 2009 | B2 |
| 7674650 | Akimoto et al. | Mar 2010 | B2 |
| 7732819 | Akimoto et al. | Jun 2010 | B2 |
| 7786482 | Yamazaki et al. | Aug 2010 | B2 |
| 7817121 | Young et al. | Oct 2010 | B2 |
| 7824939 | Hosoya et al. | Nov 2010 | B2 |
| 7846618 | Chai et al. | Dec 2010 | B2 |
| 7915074 | Yoon | Mar 2011 | B2 |
| 7952099 | Deng et al. | May 2011 | B2 |
| 7989815 | Yamazaki et al. | Aug 2011 | B2 |
| 8101445 | Koo et al. | Jan 2012 | B2 |
| 8129719 | Yamazaki et al. | Mar 2012 | B2 |
| 8174633 | Segawa et al. | May 2012 | B2 |
| 8188477 | Miyairi et al. | May 2012 | B2 |
| 8284142 | Yamazaki et al. | Oct 2012 | B2 |
| 8314423 | Chen et al. | Nov 2012 | B2 |
| 8334540 | Yamazaki et al. | Dec 2012 | B2 |
| 8344374 | Yamazaki et al. | Jan 2013 | B2 |
| 8378946 | Toyota et al. | Feb 2013 | B2 |
| 8384079 | Yamazaki et al. | Feb 2013 | B2 |
| 8461630 | Endo et al. | Jun 2013 | B2 |
| 8487308 | Ikeda et al. | Jul 2013 | B2 |
| 8530285 | Yamazaki et al. | Sep 2013 | B2 |
| 8530897 | Koyama et al. | Sep 2013 | B2 |
| 8575606 | Park et al. | Nov 2013 | B2 |
| 8674371 | Yamazaki et al. | Mar 2014 | B2 |
| 8685803 | Chikama et al. | Apr 2014 | B2 |
| 8686425 | Yamazaki et al. | Apr 2014 | B2 |
| 8729612 | Katsui et al. | May 2014 | B2 |
| 8759133 | Park et al. | Jun 2014 | B2 |
| 8772093 | Yamazaki et al. | Jul 2014 | B2 |
| 8809856 | Yamazaki et al. | Aug 2014 | B2 |
| 8822264 | Yamazaki et al. | Sep 2014 | B2 |
| 8884284 | Koyama | Nov 2014 | B2 |
| 8901563 | Park et al. | Dec 2014 | B2 |
| 8907348 | Miyairi et al. | Dec 2014 | B2 |
| 8927981 | Akimoto et al. | Jan 2015 | B2 |
| 9019440 | Kuwabara | Apr 2015 | B2 |
| 9034104 | Yamazaki et al. | May 2015 | B2 |
| 9048147 | Yamazaki et al. | Jun 2015 | B2 |
| 9054134 | Yamazaki et al. | Jun 2015 | B2 |
| 9142570 | Yamazaki et al. | Sep 2015 | B2 |
| 9196713 | Yamazaki et al. | Nov 2015 | B2 |
| 9202854 | Song et al. | Dec 2015 | B2 |
| 9257082 | Kimura et al. | Feb 2016 | B2 |
| 9293594 | Nishimura et al. | Mar 2016 | B2 |
| 9419113 | Asano et al. | Aug 2016 | B2 |
| 9515192 | Yamazaki et al. | Dec 2016 | B2 |
| 9563094 | Yamazaki et al. | Feb 2017 | B2 |
| 9570619 | Miyairi et al. | Feb 2017 | B2 |
| 9666689 | Kuwabara | May 2017 | B2 |
| 9779679 | Umezaki et al. | Oct 2017 | B2 |
| 9859401 | Yamazaki et al. | Jan 2018 | B2 |
| 9865742 | Yamazaki et al. | Jan 2018 | B2 |
| 9875713 | Umezaki et al. | Jan 2018 | B2 |
| 9893089 | Miyairi et al. | Feb 2018 | B2 |
| 9911865 | Yamazaki et al. | Mar 2018 | B2 |
| 10079306 | Yamazaki et al. | Sep 2018 | B2 |
| 10134912 | Kimura et al. | Nov 2018 | B2 |
| 10243006 | Miyairi et al. | Mar 2019 | B2 |
| 10290742 | Yamazaki et al. | May 2019 | B2 |
| 10573673 | Kasahara | Feb 2020 | B2 |
| 10622381 | Miyairi et al. | Apr 2020 | B2 |
| 10680111 | Yamazaki et al. | Jun 2020 | B2 |
| 11106101 | Yamazaki et al. | Aug 2021 | B2 |
| 11495626 | Kasahara | Nov 2022 | B2 |
| 20010046027 | Tai et al. | Nov 2001 | A1 |
| 20020056838 | Ogawa | May 2002 | A1 |
| 20020132454 | Ohtsu et al. | Sep 2002 | A1 |
| 20030189401 | Kido et al. | Oct 2003 | A1 |
| 20030218222 | Wager, III et al. | Nov 2003 | A1 |
| 20040038446 | Takeda et al. | Feb 2004 | A1 |
| 20040127038 | Carcia et al. | Jul 2004 | A1 |
| 20050017302 | Hoffman | Jan 2005 | A1 |
| 20050142680 | Ha et al. | Jun 2005 | A1 |
| 20050199959 | Chiang et al. | Sep 2005 | A1 |
| 20060035452 | Carcia et al. | Feb 2006 | A1 |
| 20060043377 | Hoffman et al. | Mar 2006 | A1 |
| 20060091793 | Baude et al. | May 2006 | A1 |
| 20060108529 | Saito et al. | May 2006 | A1 |
| 20060108636 | Sano et al. | May 2006 | A1 |
| 20060110867 | Yabuta et al. | May 2006 | A1 |
| 20060113536 | Kumomi et al. | Jun 2006 | A1 |
| 20060113539 | Sano et al. | Jun 2006 | A1 |
| 20060113549 | Den et al. | Jun 2006 | A1 |
| 20060113565 | Abe et al. | Jun 2006 | A1 |
| 20060169973 | Isa et al. | Aug 2006 | A1 |
| 20060170111 | Isa et al. | Aug 2006 | A1 |
| 20060197092 | Hoffman et al. | Sep 2006 | A1 |
| 20060208977 | Kimura | Sep 2006 | A1 |
| 20060228974 | Thelss et al. | Oct 2006 | A1 |
| 20060231882 | Kim et al. | Oct 2006 | A1 |
| 20060238135 | Kimura | Oct 2006 | A1 |
| 20060244107 | Sugihara et al. | Nov 2006 | A1 |
| 20060284171 | Levy et al. | Dec 2006 | A1 |
| 20060284172 | Ishii | Dec 2006 | A1 |
| 20060292777 | Dunbar | Dec 2006 | A1 |
| 20070024187 | Shin et al. | Feb 2007 | A1 |
| 20070046191 | Saito | Mar 2007 | A1 |
| 20070052025 | Yabuta | Mar 2007 | A1 |
| 20070054507 | Kaji et al. | Mar 2007 | A1 |
| 20070090365 | Hayashi et al. | Apr 2007 | A1 |
| 20070108446 | Akimoto | May 2007 | A1 |
| 20070146592 | Kimura | Jun 2007 | A1 |
| 20070152217 | Lai et al. | Jul 2007 | A1 |
| 20070172591 | Seo et al. | Jul 2007 | A1 |
| 20070187678 | Hirao et al. | Aug 2007 | A1 |
| 20070187760 | Furuta et al. | Aug 2007 | A1 |
| 20070194379 | Hosono et al. | Aug 2007 | A1 |
| 20070252928 | Ito et al. | Nov 2007 | A1 |
| 20070272922 | Kim et al. | Nov 2007 | A1 |
| 20070287296 | Chang | Dec 2007 | A1 |
| 20080006877 | Mardilovich et al. | Jan 2008 | A1 |
| 20080038882 | Takechi et al. | Feb 2008 | A1 |
| 20080038929 | Chang | Feb 2008 | A1 |
| 20080050595 | Nakagawara et al. | Feb 2008 | A1 |
| 20080073653 | Iwasaki | Mar 2008 | A1 |
| 20080083950 | Pan et al. | Apr 2008 | A1 |
| 20080106191 | Kawase | May 2008 | A1 |
| 20080119018 | Toyota et al. | May 2008 | A1 |
| 20080128689 | Lee et al. | Jun 2008 | A1 |
| 20080129195 | Ishizaki et al. | Jun 2008 | A1 |
| 20080150435 | Park et al. | Jun 2008 | A1 |
| 20080166834 | Kim et al. | Jul 2008 | A1 |
| 20080182358 | Cowdery-Corvan et al. | Jul 2008 | A1 |
| 20080224133 | Park et al. | Sep 2008 | A1 |
| 20080254569 | Hoffman et al. | Oct 2008 | A1 |
| 20080258139 | Ito et al. | Oct 2008 | A1 |
| 20080258140 | Lee et al. | Oct 2008 | A1 |
| 20080258141 | Park et al. | Oct 2008 | A1 |
| 20080258143 | Kim et al. | Oct 2008 | A1 |
| 20080296568 | Ryu et al. | Dec 2008 | A1 |
| 20090068773 | Lai et al. | Mar 2009 | A1 |
| 20090073325 | Kuwabara et al. | Mar 2009 | A1 |
| 20090114910 | Chang | May 2009 | A1 |
| 20090134399 | Sakakura et al. | May 2009 | A1 |
| 20090140438 | Yamazaki et al. | Jun 2009 | A1 |
| 20090152506 | Umeda et al. | Jun 2009 | A1 |
| 20090152541 | Maekawa et al. | Jun 2009 | A1 |
| 20090159885 | Yamazaki et al. | Jun 2009 | A1 |
| 20090278122 | Hosono et al. | Nov 2009 | A1 |
| 20090280600 | Hosono et al. | Nov 2009 | A1 |
| 20100065844 | Tokunaga | Mar 2010 | A1 |
| 20100092800 | Itagaki et al. | Apr 2010 | A1 |
| 20100096645 | Sonoda et al. | Apr 2010 | A1 |
| 20100109002 | Itagaki et al. | May 2010 | A1 |
| 20100140613 | Kimura | Jun 2010 | A1 |
| 20100270538 | Kang | Oct 2010 | A1 |
| 20100301329 | Asano et al. | Dec 2010 | A1 |
| 20100327281 | Nakajima et al. | Dec 2010 | A1 |
| 20110084268 | Yamazaki et al. | Apr 2011 | A1 |
| 20110111543 | Ono | May 2011 | A1 |
| 20120081715 | Takano | Apr 2012 | A1 |
| 20120188478 | Kuwabara | Jul 2012 | A1 |
| 20120242624 | Tomiyasu et al. | Sep 2012 | A1 |
| 20120292645 | Park et al. | Nov 2012 | A1 |
| 20120298984 | Park et al. | Nov 2012 | A1 |
| 20130023086 | Chikama et al. | Jan 2013 | A1 |
| 20130161609 | Koyama | Jun 2013 | A1 |
| 20130214279 | Nishimura et al. | Aug 2013 | A1 |
| 20140004704 | Hung et al. | Jan 2014 | A1 |
| 20150064841 | Koyama | Mar 2015 | A1 |
| 20150108467 | Moriguchi et al. | Apr 2015 | A1 |
| 20170179162 | Moriguchi et al. | Jun 2017 | A1 |
| 20180145153 | Yamazaki et al. | May 2018 | A1 |
| 20180190834 | Yamazaki et al. | Jul 2018 | A1 |
| 20180226040 | Umezaki et al. | Aug 2018 | A1 |
| 20190088793 | Kimura et al. | Mar 2019 | A1 |
| 20200066918 | Kimura et al. | Feb 2020 | A1 |
| 20200203386 | Miyairi et al. | Jun 2020 | A1 |
| 20220043314 | Yamazaki et al. | Feb 2022 | A1 |
| Number | Date | Country |
|---|---|---|
| 103022080 | Apr 2013 | CN |
| 0679922 | Nov 1995 | EP |
| 0745885 | Dec 1996 | EP |
| 0745886 | Dec 1996 | EP |
| 1737044 | Dec 2006 | EP |
| 2073255 | Jun 2009 | EP |
| 2226847 | Sep 2010 | EP |
| 2500946 | Sep 2012 | EP |
| 2506307 | Oct 2012 | EP |
| 2511896 | Oct 2012 | EP |
| 2518772 | Oct 2012 | EP |
| 2521180 | Nov 2012 | EP |
| 2657974 | Oct 2013 | EP |
| 2743983 | Jun 2014 | EP |
| 60-198861 | Oct 1985 | JP |
| 63-210022 | Aug 1988 | JP |
| 63-210023 | Aug 1988 | JP |
| 63-210024 | Aug 1988 | JP |
| 63-215519 | Sep 1988 | JP |
| 63-239117 | Oct 1988 | JP |
| 63-265818 | Nov 1988 | JP |
| 05-251705 | Sep 1993 | JP |
| 07-335756 | Dec 1995 | JP |
| 08-264794 | Oct 1996 | JP |
| 08-328041 | Dec 1996 | JP |
| 11-505377 | May 1999 | JP |
| 11-242241 | Sep 1999 | JP |
| 2000-044236 | Feb 2000 | JP |
| 2000-150900 | May 2000 | JP |
| 2002-076356 | Mar 2002 | JP |
| 2002-289859 | Oct 2002 | JP |
| 2002-333641 | Nov 2002 | JP |
| 2003-086000 | Mar 2003 | JP |
| 2003-086808 | Mar 2003 | JP |
| 2004-103957 | Apr 2004 | JP |
| 2004-151546 | May 2004 | JP |
| 2004-273614 | Sep 2004 | JP |
| 2004-273732 | Sep 2004 | JP |
| 2005-011920 | Jan 2005 | JP |
| 2005-521206 | Jul 2005 | JP |
| 2007-188936 | Jul 2007 | JP |
| 2008-129314 | Jun 2008 | JP |
| 2009-124124 | Jun 2009 | JP |
| 2009-158940 | Jul 2009 | JP |
| 2009-170900 | Jul 2009 | JP |
| 2010-080947 | Apr 2010 | JP |
| 2010-097077 | Apr 2010 | JP |
| 2010-107976 | May 2010 | JP |
| 2010-109342 | May 2010 | JP |
| 2010-129859 | Jun 2010 | JP |
| 2010-153828 | Jul 2010 | JP |
| 2010-161351 | Jul 2010 | JP |
| 2010-256556 | Nov 2010 | JP |
| 2010-263182 | Nov 2010 | JP |
| 2010-272691 | Dec 2010 | JP |
| 2011-009724 | Jan 2011 | JP |
| 2011-044701 | Mar 2011 | JP |
| 2011-049548 | Mar 2011 | JP |
| 2011-076079 | Apr 2011 | JP |
| 2011-100041 | May 2011 | JP |
| 2011-100995 | May 2011 | JP |
| 2011-118422 | Jun 2011 | JP |
| 2011-146698 | Jul 2011 | JP |
| 2011-155249 | Aug 2011 | JP |
| 2011-155303 | Aug 2011 | JP |
| 2011-221097 | Nov 2011 | JP |
| 2012-164976 | Aug 2012 | JP |
| 2012-178545 | Sep 2012 | JP |
| 2012-195283 | Oct 2012 | JP |
| 2013-149961 | Aug 2013 | JP |
| 2010-0109395 | Oct 2010 | KR |
| 2012-0131776 | Dec 2012 | KR |
| WO-2003079440 | Sep 2003 | WO |
| WO-2003079441 | Sep 2003 | WO |
| WO-2003079442 | Sep 2003 | WO |
| WO-2003079449 | Sep 2003 | WO |
| WO-2004114391 | Dec 2004 | WO |
| WO-2010038819 | Apr 2010 | WO |
| WO-2010058746 | May 2010 | WO |
| WO-2011010546 | Jan 2011 | WO |
| WO-2011013522 | Feb 2011 | WO |
| WO-2011043195 | Apr 2011 | WO |
| WO-2011065059 | Jun 2011 | WO |
| WO-2011070981 | Jun 2011 | WO |
| WO-2011074506 | Jun 2011 | WO |
| WO-2011077607 | Jun 2011 | WO |
| WO-2011080879 | Jul 2011 | WO |
| WO-2011081009 | Jul 2011 | WO |
| WO-2011135908 | Nov 2011 | WO |
| WO-2012086513 | Jun 2012 | WO |
| Entry |
|---|
| Asakuma.N et al., “Crystallization and Reduction of Sol-Gel-Derived Zinc Oxide Films by Irradiation With Ultraviolet Lamp”, Journal of Sol-Gel Science and Technology, 2003, vol. 26, pp. 181-184. |
| Asaoka.Y et al., “29.1:Polarizer-Free Reflective LCD Combined With Ultra Low-Power Driving Technology”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 395-398. |
| Chern.H et al., “An Analytical Model for the Above-Threshold Characteristics of Polysilicon Thin-Film Transistors”, IEEE Transactions on Electron Devices, Jul. 1, 1995, vol. 42, No. 7, pp. 1240-1246. |
| Cho.D et al., “21.2:Al and Sn-Doped Zinc Indium Oxide Thin Film Transistors for AMOLED Back-Plane”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 280-283. |
| Clark.S et al., “First Principles Methods Using CASTEP”, Zeitschrift fur Kristallographie, 2005, vol. 220, pp. 567-570. |
| Coates.D et al., “Optical Studies of the Amorphous Liquid-Cholesteric Liquid Crystal Transition:The “Blue Phase””, Physics Letters, Sep. 10, 1973, vol. 45A, No. 2, pp. 115-116. |
| Costello.M et al., “Electron Microscopy of a Cholesteric Liquid Crystal and Its Blue Phase”, Phys. Rev. A (Physical Review. A), May 1, 1984, vol. 29, No. 5, pp. 2957-2959. |
| Dembo.H et al., “RFCPUS on Glass and Plastic Substrates Fabricated by TFT Transfer Technology”, IEDM 05: Technical Digest of International Electron Devices Meeting, Dec. 5, 2005, pp. 1067-1069. |
| Fortunato.E et al., “Wide-Bandgap High-Mobility ZnO Thin-Film Transistors Produced at Room Temperature”, Appl. Phys. Lett. (Applied Physics Letters) , Sep. 27, 2004, vol. 85, No. 13, pp. 2541-2543. |
| Fung.T et al., “2-D Numerical Simulation of High Performance Amorphous In—Ga—Zn—O TFTs for Flat Panel Displays”, AM-FPD '08 Digest of Technical Papers, Jul. 2, 2008, pp. 251-252, The Japan Society of Applied Physics. |
| Godo.H et al., “P-9:Numerical Analysis on Temperature Dependence of Characteristics of Amorphous In—Ga—Zn-Oxide TFT”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 1110-1112. |
| Godo.H et al., “Temperature Dependence of Characteristics and Electronic Structure for Amorphous In—Ga—Zn-Oxide TFT”, AM-FPD '09 Digest of Technical Papers, Jul. 1, 2009, pp. 41-44. |
| Hayashi.R et al., “42.1: Invited Paper: Improved Amorphous In—Ga—Zn—O TFTs”, SID Digest '08 : SID International Symposium Digest of Technical Papers, May 20, 2008, vol. 39, pp. 621-624. |
| Hirao.T et al., “Novel Top-Gate Zinc Oxide Thin-Film Transistors (ZnO TFTs) for AMLCDS”, J. Soc. Inf. Display (Journal of the Society for Information Display), 2007, vol. 15, No. 1, p. 17-22. |
| Hosono.H et al., “Working hypothesis to explore novel wide band gap electrically conducting amorphous oxides and examples”, J. Non-Cryst. Solids (Journal of Non-Crystalline Solids), 1996, vol. 198-200, pp. 165-169. |
| Hosono.H, “68.3:Invited Paper:Transparent Amorphous Oxide Semiconductors for High Performance TFT”, SID Digest '07 : SID International Symposium Digest of Technical Papers, 2007, vol. 38, pp. 1830-1833. |
| Hsieh.H et al., “P-29:Modeling of Amorphous Oxide Semiconductor Thin Film Transistors and Subgap Density of States”, SID Digest '08 : SID International Symposium Digest of Technical Papers, May 20, 2008, vol. 39, pp. 1277-1280. |
| Ikeda.T et al., “Full-Functional System Liquid Crystal Display Using Cg-Silicon Technology”, SID Digest '04 : SID International Symposium Digest of Technical Papers, 2004, vol. 35, pp. 860-863. |
| Janotti.A et al., “Native Point Defects in ZnO”, Phys. Rev. B (Physical Review. B), Oct. 4, 2007, vol. 76, No. 16, pp. 165202-1-165202-22. |
| Janotti.A et al., “Oxygen Vacancies in ZnO”, Appl. Phys. Lett. (Applied Physics Letters) , 2005, vol. 87, pp. 122102-1-122102-3. |
| Jeong.J et al., “3.1: Distinguished Paper: 12.1-Inch WXGA AMOLED Display Driven by Indium-Gallium-Zinc Oxide TFTs Array”, SID Digest '08 : SID International Symposium Digest of Technical Papers, May 20, 2008, vol. 39, No. 1, pp. 1-4. |
| Jin.D et al., “65.2:Distinguished Paper:World-Largest (6.5″) Flexible Full Color Top Emission AMOLED Display on Plastic Film and Its Bending Properties”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 983-985. |
| Kanno.H et al., “White Stacked Electrophosphorecent Organic Light-Emitting Devices Employing MOO3 as a Charge-Generation Layer”, Adv. Mater. (Advanced Materials), 2006, vol. 18, No. 3, pp. 339-342. |
| Kikuchi.H et al., “39.1:Invited Paper:Optically Isotropic Nano-Structured Liquid Crystal Composites for Display Applications”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 578-581. |
| Kikuchi.H et al., “62.2:Invited Paper:Fast Electro-Optical Switching in Polymer-Stabilized Liquid Crystalline Blue Phases for Display Application”, SID Digest '07 : SID International Symposium Digest of Technical Papers, 2007, vol. 38, pp. 1737-1740. |
| Kikuchi.H et al., “Polymer-Stabilized Liquid Crystal Blue Phases”, Nature Materials, Sep. 2, 2002, vol. 1, pp. 64-68. |
| Kim.S et al., “High-Performance oxide thin film transistors passivated by various gas plasmas”, 214th ECS Meeting, 2008, No. 2317, ECS. |
| Kimizuka.N et al., “Spinel, YbFe2O4, and Yb2Fe3O7 Types of Structures for Compounds in the In2O3 and Sc2O3—A2O3—BO Systems [A; Fe, Ga, or Al; B: Mg, Mn, Fe, Ni, Cu, or Zn] at Temperatures Over 1000° C.”, Journal of Solid State Chemistry, 1985, vol. 60, pp. 382-384. |
| Kimizuka.N et al., “Syntheses and Single-Crystal Data of Homologous Compounds, In2O3(ZnO)m (m=3, 4, and 5), InGaO3(ZnO)3, and Ga2O3(ZnO)m (m=7, 8, 9, and 16) in the In2O3—ZnGa2O4—ZnO System”, Journal of Solid State Chemistry, Apr. 1, 1995, vol. 116, No. 1, pp. 170-178. |
| Kitzerow.H et al., “Observation of Blue Phases in Chiral Networks”, Liquid Crystals, 1993, vol. 14, No. 3, pp. 911-916. |
| Kurokawa.Y et al., “UHF RFCPUS on Flexible and Glass Substrates for Secure RFID Systems”, Journal of Solid-State Circuits , 2008, vol. 43, No. 1, pp. 292-299. |
| Lany.S et al., “Dopability, Intrinsic Conductivity, and Nonstoichiometry of Transparent Conducting Oxides”, Phys. Rev. Lett. (Physical Review Letters), Jan. 26, 2007, vol. 98, pp. 045501-1-045501-4. |
| Lee.H et al., “Current Status of, Challenges to, and Perspective View of AM-OLED”, IDW '06 : Proceedings of the 13th International Display Workshops, Dec. 7, 2006, pp. 663-666. |
| Lee.J et al., “World's Largest (15-Inch) XGA AMLCD Panel Using IGZO Oxide TFT”, SID Digest '08 : SID International Symposium Digest of Technical Papers, May 20, 2008, vol. 39, pp. 625-628. |
| Lee.M et al., “15.4:Excellent Performance of Indium-Oxide-Based Thin-Film Transistors by DC Sputtering”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 191-193. |
| Li.C et al., “Modulated Structures of Homologous Compounds InMO3(ZnO)m (M=In,Ga; m=Integer) Described by Four-Dimensional Superspace Group”, Journal of Solid State Chemistry, 1998, vol. 139, pp. 347-355. |
| Masuda.S et al., “Transparent thin film transistors using ZnO as an active channel layer and their electrical properties”, J. Appl. Phys. (Journal of Applied Physics) , Feb. 1, 2003, vol. 93, No. 3, pp. 1624-1630. |
| Meiboom.S et al., “Theory of the Blue Phase of Cholesteric Liquid Crystals”, Phys. Rev. Lett. (Physical Review Letters), May 4, 1981, vol. 46, No. 18, pp. 1216-1219. |
| Miyasaka.M, “SUFTLA Flexible Microelectronics on Their Way to Business”, SID Digest '07 : SID International Symposium Digest of Technical Papers, 2007, vol. 38, pp. 1673-1676. |
| Mo.Y et al., “Amorphous Oxide TFT Backplanes for Large Size AMOLED Displays”, IDW '08 : Proceedings of the 6th International Display Workshops, Dec. 3, 2008, pp. 581-584. |
| Nakamura.M et al., “The phase relations in the In2O3—Ga2ZnO4—ZnO system at 1350° C.”, Journal of Solid State Chemistry, Aug. 1, 1991, vol. 93, No. 2, pp. 298-315. |
| Nakamura.M, “Synthesis of Homologous Compound with New Long-Period Structure”, NIRIM Newsletter, Mar. 1, 1995, vol. 150, pp. 1-4. |
| Nomura.K et al., “Amorphous Oxide Semiconductors for High-Performance Flexible Thin-Film Transistors”, Jpn. J. Appl. Phys. (Japanese Journal of Applied Physics) , 2006, vol. 45, No. 5B, pp. 4303-4308. |
| Nomura.K et al., “Carrier transport in transparent oxide semiconductor with intrinsic structural randomness probed using single-crystalline InGaO3(ZnO)5 films”, Appl. Phys. Lett. (Applied Physics Letters) , Sep. 13, 2004, vol. 85, No. 11, pp. 1993-1995. |
| Nomura.K et al., “Room-Temperature Fabrication of Transparent Flexible Thin-Film Transistors Using Amorphous Oxide Semiconductors”, Nature, Nov. 25, 2004, vol. 432, pp. 488-492. |
| Nomura.K et al., “Thin-Film Transistor Fabricated in Single-Crystalline Transparent Oxide Semiconductor”, Science, May 23, 2003, vol. 300, No. 5623, pp. 1269-1272. |
| Nowatari.H et al., “60.2: Intermediate Connector With Suppressed Voltage Loss for White Tandem OLEDs”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, vol. 40, pp. 899-902. |
| Oba.F et al., “Defect energetics in ZnO: A hybrid Hartree-Fock density functional study”, Phys. Rev. B (Physical Review. B), 2008, vol. 77, pp. 245202-1-245202-6. |
| Oh.M et al., “Improving the Gate Stability of ZnO Thin-Film Transistors With Aluminum Oxide Dielectric Layers”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2008, vol. 155, No. 12, pp. H1009-H1014. |
| Ohara.H et al., “21.3:4.0 In. QVGA AMOLED Display Using In—Ga—Zn-Oxide TFTs With a Novel Passivation Layer”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, pp. 284-287. |
| Ohara.H et al., “Amorphous In—Ga—Zn-Oxide TFTs with Suppressed Variation for 4.0 inch QVGA AMOLED Display”, AM-FPD '09 Digest of Technical Papers, Jul. 1, 2009, pp. 227-230, The Japan Society of Applied Physics. |
| Orita.M et al., “Amorphous transparent conductive oxide InGaO3(ZnO)m (m<4):a Zn4s conductor”, Philosophical Magazine, 2001, vol. 81, No. 5, pp. 501-515. |
| Orita.M et al., “Mechanism of Electrical Conductivity of Transparent InGaZnO4”, Phys. Rev. B (Physical Review. B), Jan. 15, 2000, vol. 61, No. 3, pp. 1811-1816. |
| Osada.T et al., “15.2: Development of Driver-Integrated Panel using Amorphous In—Ga—Zn-Oxide TFT”, SID Digest '09 : SID International Symposium Digest of Technical Papers, May 31, 2009, vol. 40, pp. 184-187. |
| Osada.T et al., “Development of Driver-Integrated Panel Using Amorphous In—Ga—Zn-Oxide TFT”, AM-FPD '09 Digest of Technical Papers, Jul. 1, 2009, pp. 33-36. |
| Park.J et al., “Amorphous Indium-Gallium-Zinc Oxide TFTs and Their Application for Large Size AMOLED”, AM-FPD '08 Digest of Technical Papers, Jul. 2, 2008, pp. 275-278. |
| Park.J et al., “Dry etching of ZnO films and plasma-induced damage to optical properties”, J. Vac. Sci. Technol. B (Journal of Vacuum Science & Technology B), Mar. 1, 2003, vol. 21, No. 2, pp. 800-803. |
| Park.J et al., “Electronic Transport Properties of Amorphous Indium-Gallium-Zinc Oxide Semiconductor Upon Exposure to Water”, Appl. Phys. Lett. (Applied Physics Letters) , 2008, vol. 92, pp. 072104-1-072104-3. |
| Park.J et al., “High performance amorphous oxide thin film transistors with self-aligned top-gate structure”, IEDM 09: Technical Digest of International Electron Devices Meeting, Dec. 7, 2009, pp. 191-194. |
| Park.J et al., “Improvements in the Device Characteristics of Amorphous Indium Gallium Zinc Oxide Thin-Film Transistors by Ar Plasma Treatment”, Appl. Phys. Lett. (Applied Physics Letters) , Jun. 26, 2007, vol. 90, No. 26, pp. 262106-1-262106-3. |
| Park.S et al., “Challenge to Future Displays: Transparent AM-OLED Driven by Peald Grown ZnO TFT”, IMID '07 DIGEST, 2007, pp. 1249-1252. |
| Park.S et al., “42.3: Transparent ZnO Thin Film Transistor for the Application of High Aperture Ratio Bottom Emission AM-OLED Display”, SID Digest '08 : SID International Symposium Digest of Technical Papers, May 20, 2008, vol. 39, pp. 629-632. |
| Prins.M et al., “A Ferroelectric Transparent Thin-Film Transistor”, Appl. Phys. Lett. (Applied Physics Letters) , Jun. 17, 1996, vol. 68, No. 25, pp. 3650-3652. |
| Sakata.J et al., “Development of 4.0-IN. AMOLED Display With Driver Circuit Using Amorphous In—Ga—Zn-Oxide TFTs”, IDW '09 : Proceedings of the 16th International Display Workshops, 2009, pp. 689-692. |
| Son.K et al., “42.4L: Late-News Paper: 4 Inch QVGA AMOLED Driven by the Threshold Voltage Controlled Amorphous GIZO (Ga2O3—In2O3—ZnO) TFT”, SID Digest '08 : SID International Symposium Digest of Technical Papers, May 20, 2008, vol. 39, pp. 633-636. |
| Takahashi.M et al., “Theoretical Analysis of IGZO Transparent Amorphous Oxide Semiconductor”, IDW '08 : Proceedings of the 15th International Display Workshops, Dec. 3, 2008, pp. 1637-1640. |
| Tsuda.K et al., “Ultra Low Power Consumption Technologies for Mobile TFT-LCDs”, IDW '02 : Proceedings of the 9th International Display Workshops, Dec. 4, 2002, pp. 295-298. |
| Ueno.K et al., “Field-Effect Transistor on SrTiO3 With Sputtered Al2O3 Gate Insulator”, Appl. Phys. Lett. (Applied Physics Letters) , Sep. 1, 2003, vol. 83, No. 9, pp. 1755-1757. |
| Van de Walle.C, “Hydrogen as a Cause of Doping in Zinc Oxide”, Phys. Rev. Lett. (Physical Review Letters), Jul. 31, 2000, vol. 85, No. 5, pp. 1012-1015. |
| Number | Date | Country | |
|---|---|---|---|
| 20230059502 A1 | Feb 2023 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17230631 | Apr 2021 | US |
| Child | 17976450 | US | |
| Parent | 16782455 | Feb 2020 | US |
| Child | 17230631 | US | |
| Parent | 16537091 | Aug 2019 | US |
| Child | 16782455 | US | |
| Parent | 16157158 | Oct 2018 | US |
| Child | 16537091 | US | |
| Parent | 15407287 | Jan 2017 | US |
| Child | 16157158 | US | |
| Parent | 14219752 | Mar 2014 | US |
| Child | 15407287 | US |