The present invention relates to a method for manufacturing a sintered component, a sintered component and a drill for drilling a powder-compact green. In particular, the present invention relates to a method for manufacturing a sintered component, which can suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body and also has a good productivity.
Sintered bodies (sintered alloys) obtained by sintering green bodies made of a metal powder, such as an iron powder, are used for automobile parts or machine parts. For example, such sintered alloy components (hereinafter, simply referred to as a “sintered component”) include sprockets, rotors, gears, rings, flanges, pulleys, vanes, bearings and the like. In general, the sintered components are manufactured by press-molding a raw material powder containing a metal powder to fabricate a powder-compact green body (powder compact body) and then sintering the powder-compact green body. After sintering, if necessary, the sintered components are subjected to machining as a finish processing.
However, as sintered components, components are known, in which a through-hole (open hole), which extends therethrough, or a blind hole, which does not extend therethrough, is formed. For example, a component is known, in which a through-hole (e.g., an oil hole) is formed to extend from an outer circumferential surface thereof to an end surface or an inner circumferential surface. In such a component, a through-hole cannot be integrally formed in a powder-compact green body during molding, and thus after sintering, drilling is performed using a drill (see Patent Document 1).
As drills used for drilling, a drill, in which a cutting edge on a point portion thereof has a V-shaped projection shape, is typical. In the case of sintered carbide drills, a point angle of the cutting edge is in the order of 130° to 140°.
In the case where drilling using a drill is performed on a sintered component, there is a problem in that drilling after sintering is difficult and has a low productivity.
The sintered component is hard, since metal powder particles therein are diffusion-bonded and alloyed with each other by sintering, thereby forming a strong bonding therebetween. Accordingly, when drilling using a drill is performed on the sintered component, a cutting resistance is high and thus the drill is difficult to penetrate into the sintered component. Therefore, cutting is difficult, a long time is required for machining and also a tool life is decreased. Also, since a resistance upon biting of the drill is also high, it is difficult to obtain a stable precision of the machined hole, due to the fact that a rotation axis of the drill is likely to be shaken and the like.
In addition, since a cutting resistance is high and also a thrust load is high, when a through-hole is formed, burrs are likely to occur along an opening edge on the exit side, through which the drill comes out. The burrs occur since if a thickness of a bottom of a hole when a drill penetrates becomes so thin that a strength of the bottom against a thrust load cannot be maintained, the bottom is deformed and pushed out to the exit side. The occurred burrs have to be removed in the subsequent step and thus time and efforts are required for such an operation. It is difficult or impossible to remove the burrs depending on locations where the burrs occur.
Therefore, in view of reduction of manufacturing costs, it is desirable to improve productivity in manufacturing a sintered component.
Accordingly, the preset inventors have considered performing drilling on a powder-compact green body before sintering by a drill so that a through-hole is formed in the powder-compact green body in advance, instead of performing drilling on a sintered component after sintering by a drill. The powder-compact green body is obtained by only agglomerating a raw material powder by molding, and thus metal powder particles therein are mechanically adhered with each other, not strongly bonded to each other as in the sintered body. Therefore, when drilling is performed on the powder-compact green body before sintering, cutting can be easily performed and also a cutting resistance (thrust load) can be significantly reduced, since bonding between metal powder particles thereof is weak. When drilling is performed on the powder-compact green body, a through-hole is formed as metal powder particles are cut while being scrapped by the drill. However, if drilling is performed on the powder-compact green body, when a through-hole is formed, so-called edge chipping that an opening edge on the exit side, through which the drill comes out, is chipped is likely to occur.
Accordingly, one of objects of the present invention is to provide a method for manufacturing a sintered component, which can suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body and also has a good productivity. Another object of the present invention is to provide a sintered component, which has a good productivity. Further another object of the present invention is to provide a drill, which can suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body.
A method for manufacturing a sintered component according to one aspect of the present invention includes a molding step, a drilling step and a sintering step. The molding step is configured to press-mold a raw material powder containing a metal powder and thus to fabricate a powder-compact green body. The drilling step is configured to form a hole in the powder-compact green body using a drill. The sintering step is configured to sinter the powder-compact green body after drilling. The drill used for drilling has a circular-arc shaped cutting edge on a point portion thereof.
A sintered component according to one aspect of the present invention is a sintered component having a hole formed therein. In the sintered component, an inner circumferential surface of the hole has a satin finish shape.
A drill according to one aspect of the present invention is a drill for drilling a work material. The work material is a powder-compact green body fabricated by press-molding a raw material powder containing a metal powder. The drill has a circular arc-shaped cutting edge on a point portion thereof.
The method for manufacturing a sintered component as described above can suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body and also has a good productivity. The sintered component as described above has a good productivity. The drill as described above can suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body.
[Explanation of Exemplary Embodiments of the Invention]
The present inventors have studied technologies for improving productivity of a sintered component and as a result have found that the productivity can be enhanced if drilling using a drill is performed on a powder-compact green body before sintering, not after sintering. The reason is that when drilling is performed on the powder-compact green body, cutting is easily performed and a cutting resistance (thrust load) is significantly reduced, since bonding between metal powder particles is weak. Further, as compared with a conventional case where drilling is performed after sintering, a machining time can be reduced, a precision of a machined hole can be enhanced and also a too life can be significantly improved. Further, when drilling using a drill is performed on the powder-compact green body, burrs hardly occur. Even if burrs have occurred, the burrs can be easily removed by an air blower or the like, and thus time and efforts required for a bur removing operation can be reduced.
Also, the present inventors have further progressed the above studies and as a result have found that occurrence of edge chipping when a through-hole is formed can be suppressed by devising a shape of a drill used for drilling of the powder-compact green body, in particular a shape of a cutting edge on a point portion thereof. Specifically, it has been found that occurrence of edge chipping can be suppressed by forming a shape of the cutting edge into a circular-arc shape (R-shape).
A mechanism of occurrence of edge chipping is thought as follows. The powder-compact green body is soft since bonding between metal powder particles is weak. Therefore, if a thickness of a bottom of a hole formed by a drill when the drill penetrates becomes so thin that a strength of the bottom against a thrust load cannot be maintained, the bottom is not cut by the drill but comes off (pushed out) to an exit side before the drill passes through the bottom. When the bottom is not cut but comes off, the vicinity of the bottom also collapses, and as a result, chipping occurs on an edge of an opening on the exit side, through which the drill comes out.
The reason that occurrence of edge chipping can be suppressed by using a drill having a circular arc-shaped cutting edge (hereinafter, often referred to as an “R drill”) is thought as follows. Views on the left side of
As shown in two views on the left lower side of
In other words, when drilling is performed on the powder-compact green body G using the R drill 10, the thrust load itself is lower and also the trust load exerted on the bottom is dispersed. Accordingly, a stress concentration is reduced and the bottom is hardly chipped.
Also, as shown in the view on the left lower side of
These have an effect even on a blind hole just before penetration, other than a trough-hole. Specifically, even in the case of a blind hole in which a thickness of a bottom of the hole (minimum thickness as measured from a bottom surface of the hole to the opposite surface) is thin, the R dill causes the bottom surface of the hole to be formed in a hemispheric shape, thereby enhancing a strength of the bottom. Namely, even if a thickness of a bottom of a hole is thin, it is possible to suppress the bottom from collapsing and thus to form a blind hole, of which a bottom has a thinner thickness. For example, machining can be performed until a thickness of the bottom becomes ½ of a drill diameter (hole diameter), further ¼ of the drill diameter.
On the other hand, when a drill having a V-shaped cutting edge (hereinafter, often referred to as a “V drill”), which is conventionally widely used, is employed, it is difficult to suppress occurrence of edge chipping. Views on the right side
As shown in two views on the right lower side of
In other words, when drilling is performed on the powder-compact green body G using the V drill 11, the V drill 11 cannot disperse the thrush load exerted on the bottom cannot be dispersed, as compared with the R drill 10, and thus the bottom is likely to be chipped.
Also, in the case of the V drill 11, a maximum thickness of the bottom surface of the hole is smaller and thus a strength of the bottom is decreased corresponding to the thickness. Therefore, when drilling is performed on the powder-compact green body G using the V drill 11, if the thickness of the bottom when the drill penetrates becomes thin, the bottom is likely to collapse without being cut before the drill penetrates therethrough. Accordingly, it is difficult to suppress occurrence of edge chipping.
Meanwhile, the V drill is generally used upon drilling. The reason is that a sharp point of the V drill can be thrust at the center of a hole to be machined into a workpiece and thus the drill can be precisely positioned at the center of the hole. Although attempting to use the R drill for drilling, the R drill cannot be thrust into a workpiece and thus cannot be precisely positioned. For this reason, the V drill is generally used upon drilling.
However, according to the present invention, drilling is performed on a powder-compact green body having a lower strength. Since the strength of the powder-compact green body is lower, the present inventors have found that even in the case of the R drill, a point thereof can be also thrust into the powder-compact green body and thus be precisely positioned. For this reason, the present inventors have found that drilling can be performed by the R dill and then that if drilling is performed using the R drill, it is possible to prevent burrs from occurring as described above and the like.
The present inventors have obtained the above findings and completed the present invention. First, exemplary embodiments of the present invention will be listed and described.
(1) A method for manufacturing a sintered component according to one aspect of the present invention includes a molding step, a drilling step and a sintering step. The molding step is configured to press-mold a raw material powder containing a metal powder and thus to fabricate a powder-compact green body. The drilling step is configured to form a hole in the powder-compact green body using a drill. The sintering step is configured to sinter the powder-compact green body after drilling. The drill used for drilling has a circular-arc shaped cutting edge on a point portion thereof.
According to the method for manufacturing a sintered component as described above, drilling using a drill is performed on a powder-compact green body before sintering. Accordingly, cutting can be easily performed and also a cutting resistance (thrust load) can be significantly reduced. Therefore, as compared with a conventional manufacturing method in which drilling using a drill is performed after sintering, a machining time can be reduced, a precision of a machined hole can be enhanced and also a tool life can be significantly improved. Further, when drilling using a drill is performed on the powder-compact green body, burrs hardly occur. Even if burrs have occurred, the burrs can be easily removed, for example, by an air blower, and thus time and efforts required for a bur removing operation can be reduced. The “hole” includes a through-hole (open hole), which extends throughout, or a blind hole, which does not extend throughout.
Further, in the method for manufacturing a sintered component as described above, drilling is performed using the drill, in which has the circular arc-shaped cutting edge on the point portion thereof. Accordingly, when a through-hole is formed in the powder-compact green body, occurrence of edge chipping can be suppressed. As a result, the method for manufacturing a sintered component as described above can suppress occurrence of edge chipping and also has a good productivity.
Meanwhile, as used herein, the term “shape of the cutting edge” refers to a projection shape of the cutting edge as projected to a plane, which passes through a center axis of the drill and also is parallel to the center axis, in a direction perpendicular thereto in a state where the cutting edge are arranged to be parallel to the parallel plane
Also, the term “circular arc-shaped cutting edge” means that a projection shape of a cutting edge is a circular arc shape (see a view on the left upper side of
(2) In one mode of the method of manufacturing a sintered component as described above, the drill is configured so that a rake angle of the cutting edge may be more than 0° and 10° or less.
In view of suppression of occurrence of edge chipping, it is thought that a smaller cutting resistance (thrust load) is favorable. Since the rake angle of the cutting edge is more than 0° and 10° or less, a thrust load can be reduced and thus occurrence of edge chipping can be more effectively suppressed. Since the rake angle is more than 0°, the cutting edge becomes sharp and thus a thrush load is reduced. On the other hand, if the rake angle is increased, an edge strength is decreased as the cutting edge becomes sharp. However, since a work material to be machined is a powder-compact green body, chipping due to a decrease in edge strength hardly occurs. In view of ensuring an edge strength, the rake angle preferably is more than 0.01°, more preferably 0.1°.
If the rake angle is more than 10°, the thrust load is increased. Therefore, the rake angle preferably is 10° or less. In view of reducing the thrust load, the rake angle is more preferably, for example, 5° or more and 8° or less.
As used herein, the term “rake angle” refers to an angle γ defined between a plane parallel to the center axis of the drill and a rake face in a state where the cutting edge are arranged to be parallel to the parallel plane, as shown in a view on the right lower side of
(3) In one mode of the method of manufacturing a sintered component as described above, the drill may be configured so that a circular arc defining the cutting edge has a central angle of 135° or more and 180° or less.
Since the circular arc defining the cutting edge has a central angle of 135° or more and 180° or less, occurrence of edge chipping can be sufficiently suppressed. If the central angle of the circular arc-shaped cutting edge is 135° or more, the shape of the cutting edge becomes close to a semi-circular shape, thereby causing a thrust load to be dispersed in a radial shape. Therefore, it is possible to enhance the effect of reducing a thrust load and also to cause a thrust load during drilling to be dispersed. Further, a shape of a bottom surface of the hole becomes close to a hemispheric shape, thereby enhancing a strength against a thrust load. In addition, a maximum thickness Ht of the bottom (see views on the left side of
On the other hand, a radius of the circular arc defining of the cutting edge preferably is generally equal to a radius of a drill diameter, for example, preferably 0.4 times or more and 0.6 times or less of the drill diameter. In particular, the shape of the cutting edge preferably is a semi-circular shape, and preferably also, the central angle of the circular arc is 180° and the radius of the circular arc is 0.5 times of the drill diameter, i.e., equal to a radius of the drill diameter. As used herein, the “diameter of drill (or drill diameter)” refers to an outer diameter dimension of a portion on which the cutting edge is formed (so-called edge portion).
(4) A sintered component according to one aspect of the present invention is a sintered component having a hole formed therein. An inner circumferential surface of the hole has a satin finish shape.
When drilling using a drill is performed on a powder-compact green body before sintering as described above, bonding between metal powder particles is weak and thus a hole is formed as metal powder particles are cut while being scrapped by the drill. Accordingly, the inner circumferential surface of the hole formed in the powder-compact green body has a satin finish shape in which concave and convex portions due to particles are formed overall. Since such a surface aspect of the inner circumferential surface of the hole is substantially maintained even after sintering, an inner circumferential surface of the hole of the sintered component, which is obtained by sintering the powder-compact green body having the hole formed therein, has also a satin finish shape. In other words, the fact that the inner circumferential surface of the hole formed in the sintered component has the satin finish shape means that drilling using a drill is performed on the powder-compact green body before sintering. Such a sintered component, in which an inner circumferential surface of a hole thereof has a satin finish shape, has a good productivity, as compared with conventional sintered components, in which a hole is formed after sintering.
In contrast, when drilling using a drill is performed after sintering, bonding between metal powder particles is strong due to sintering and thus a hole is formed as a lump of metal a metal is cut by the drill. Accordingly, the inner circumferential surface of the hole formed by drilling the sintered component using a drill has an overall smooth surface having a few of concave and convex portions and thus becomes a shiny state.
(5) In one mode of the sintered component as described above, a ten point medial height Rz of the inner circumferential surface of the hole may be 20 μm or more.
When a hole is formed in a powder-compact green body by a drill before sintering and then the powder-compact green body is sintered, a ten point median height Rz of an inner circumferential surface of a hole formed in the resulting sintered component may be for example 20 μm or more, although varying depending on shapes/sizes of metal powder particles. An upper limit of the ten point median height Rz of the inner circumferential surface of the hole may be, for example, 150 μm or less. In contrast, if a hole is formed by a drill after sintering, a ten point median height Rz of an inner circumferential surface of the hole formed in the sintered component is typically smaller than 20 μm, further 15 μm or less.
(6) A drill according to one aspect of the present invention is a drill for drilling a work material. The work material is a powder-compact green body fabricated by press-molding a raw material powder containing a metal powder. The drill has a circular arc-shaped cutting edge on a point portion thereof.
According to the drill as described above, it is possible to suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body, since the circular arc-shaped cutting edge is provided on the point portion.
[Details of Exemplary Embodiments of the Invention]
Now, specific examples of a method for manufacturing a sintered component, a sintered component and a drill according to exemplary embodiments of the present invention will be described with reference to the accompanying drawings. Meanwhile, it should be noted that the present invention is intended not to be limited to such examples, but to be defined by the appended claims and also to encompass all of changes within the meaning and scope of equivalency of the claims.
<Method for Manufacturing a Sintered Component>
A method for manufacturing a sintered component according to an embodiment of the present invention includes a molding step of fabricating a powder-compact green body; a drilling step of forming a hole in the powder-compact green body using a drill; and a sintering step of sintering the powder-compact green body after drilling. One of features of the method for manufacturing a sintered component is that a drill having a circular arc-shaped cutting edge on a point portion thereof is used in the drilling step. Hereinafter, each step of the manufacturing method will be described in detail, principally referring to
(Molding Step)
In the molding step, a raw material powder containing a metal powder is press-molded to fabricate a powder-compact green body G (see a view on the top of
<Raw Material Powder>
The raw material powder essentially contains a metal powder. A material for the metal powder can be properly selected depending on a material of a sintered component to be manufactured and may typically include iron-based materials. The “iron-based materials” mean iron or iron alloy, whose main constituent is iron. The iron alloy includes alloy containing one or more additive elements selected, for example, from Ni, Cu, Cr, Mo, Mn, C, Si, Al, P, B, N and Co. Specifically, the iron alloy includes stainless steel, Fe—C alloy, Fe—Cu—Ni—Mo alloy, Fe—Ni—Mo—Mn alloy, Fe—P alloy, Fe—Cu alloy, Fe—Cu—C alloy, Fe—Cu—Mo alloy, Fe—Ni—Mo—Cu—C alloy, Fe—Ni—Cu alloy, Fe—Ni—Mo—C alloy, Fe—Ni—Cr alloy, Fe—Ni—Mo—Cr alloy, Fe—Cr alloy, Fe—Mo—Cr alloy, Fe—Cr—C alloy, Fe—Ni—C alloy, Fe—Mo—Mn—Cr—C alloy and the like. By essentially containing an iron-based material powder, an iron-based sintered component is obtained. If an iron-based material powder is essentially contained, a content thereof may be set to, for example, 90 mass % or more, further 95 mass % or more, assuming that the raw material powder is 100 mass %.
When an iron-based material powder, in particular an iron powder is essentially contained, metal powders, such as Cu, Ni and Mo, may be added as alloy constituents. Cu, Ni and Mo are elements intended to enhance hardenability, and an amount of addition thereof may be set to, for example, more than 0 mass % and 5 mass % or less, further 0.1 mass % or more and 2 mass % or less, assuming that the raw material powder is 100 mass %. Also, a nonmetallic inorganic material, such as carbon (graphite) powder may be added. C is an element intended to enhance strength of a sintered body or heat-treated body, and a content thereof may be set to, for example, more than 0 mass % and 2 mass % or less, further 0.1 mass % or more and 1 mass % or less, assuming that the raw material powder is 100 mass %.
Preferably, the raw material powder contains a lubricant. By containing the lubricant in the raw material powder, when the raw material powder is press-molded to fabricate a powder-compact green body, lubricity upon molding can be increased and thus moldability can be enhanced. Therefore, even if a pressure for press-molding is lower, a densified powder-compact green body G can be easily obtained and thus a high-density sintered component S can also be easily obtained. Further, if the lubricant is mixed with the raw material powder, the lubricant is dispersed inside the powder-compact green body G and thus also serves as a lubricant for a drill when the powder-compact green body G is drilled using the drill 10 in the subsequent step (see a view on the middle of
For this reason, the content of the lubricant may be preferably set to 0.1 mass % or more and 2 mass % or less, further 0.5 mass % or more and 2 mass % or less, 0.1 mass % or more and 1 mass % or less, even 0.5 mass % or less and 1 mass % or less, assuming that the raw material powder is 100 mass %.
The raw material powder contains no organic binder. Since no organic binder is contained in the raw material powder, a proportion of metal powder to be contained in a powder-compact green body can be increased. Accordingly, even if a pressure for press-molding is lower, a densified powder-compact green body G can be easily obtained. In addition, there is no need to degrease the powder-compact green body G in the subsequent step.
The raw material powder essentially consists of the metal powder as described above and is also permitted to contain inevitable impurities.
As the metal powder described above, water atomized powder, reduction powder, gas atomized powder and the like may be employed, and among others, water atomized powder or reduction powder are preferable. The water atomized powder or reduction powder has a lot of concave and convex portions formed on a surface of particles. Accordingly, concave and convex portions of particles are engaged with each other during molding, thereby enhancing a shape retaining ability of the powder-contact green body G. In general, from the gas atomized powder, particles having a few of concave and convex portions on a surface thereof are apt to be obtained, whereas from the water atomized powder or reduction powder, particles having a lot of concave and convex portions on a surface thereof are apt to be obtained. Also, an average particle diameter of the metal powder may be, for example, 20 μm or more, 50 μm or more and 150 μm or less. The “average particle diameter of the metal powder” is a particle diameter (D50), at which a cumulative volume in a volumetric particle size distribution as measured by a laser diffraction particle size measuring device becomes 50%. So long as the average particle diameter of the metal powder is within the above range, treating thereof is easy and thus press-molding is facilitated.
<Press-Molding>
For press-molding, a molding apparatus (mold), by which a shape corresponding to a shape of a sintered component as a final product can be molded, is employed. In the cylindrical powder-compact green body G as illustrated in
[Drilling Step]
In the drilling step, a hole 50 is formed in the powder-compact green body G using a drill 10 (see a view on the middle of
<Drill>
A view on the left upper side of
The drill 10 as illustrated in
<Shape of Cutting Edge>
As shown in the view on the left upper side of
A central angle α of a circular arc defining the cutting edge 110 is, for example, 130° or more, preferably, 135° or more and 180° or less, more preferably 150° or more. In this example, the central angle α of the circular arc is 180°.
A radius R of the circular arc defining the cutting edge is, for example, 0.4 times or more and 0.6 times or less of a drill diameter d and preferably equal to 0.5 times of a diameter d of the drill, i.e., a radius (d/2) of the drill diameter d. In this example, a shape of the cutting edge is a circular arc shape, a central angle of the circular arc is 180°, and a radius R of the circular arc is equal to the radius of the drill diameter d. For example, the diameter d of the drill 10 is, but not particularly limited to, 1.0 mm or more and 20.0 mm or less.
<Rake Angle of Cutting Edge>
A rake angle of the cutting edge 110 is, for example, 0° or more, preferably more than 0° and 10° or less, more preferably 5° or more and 8° or less. As shown in the view on the right lower side of
<Cutting Condition>
Cutting conditions, such as the number of revolutions or a feed rate (or feed amount) of the drill 10, may be properly set depending on a material of the powder-compact green body G (metal powder), a depth of the through-hole 50 to be formed, or a diameter of the drill 10 (see
The inner circumferential surface of the hole (through-hole) 50 formed in the powder-compact green body G using the drill 10 has a satin finish shape. Bonding between metal powder particles in the powder-compact green body G is weak. Therefore, when drilling is performed using the dill, the through-hole 50 is formed as metal powder particles are cut while being scrapped by the drill. Accordingly, the inner circumferential surface of the through-hole 50 formed in the powder-compact green body G has such a satin finish shape in which concave and convex portions due to particles are formed overall.
(Sintering Step)
In the sintering step, the powder-compact green body G after drilling is sintered. For sintering, a sintering furnace (not shown) capable of controlling a temperature atmosphere is used. Sintering conditions may be properly selected from any conditions required for sintering depending on a material of the powder-compact green body G (metal powder) and the like. A sintering temperature may be set to, for example, 1000° C. or more, further 1100° C. or more, 1200° C. or more, and also set to a temperature (e.g., 1400° C. or less) equal to or lower than a melting point of a main metal powder. A sintering time may be set to, for example 15 minutes or more and 150 minutes or less, further 20 minutes or more and 60 minutes or less. By sintering, a sintered component S having a hole (through-hole) 505 is obtained (see a view on the bottom of
<Sintered Component>
In the sintered component S, the hole (through-hole) 505 is formed. The through-hole 505 is the through-hole 50 formed in the powder-compact green body G by drilling using the drill 10 before sintering (see a view on the middle of
In this example, the through-hole 50S is formed at a location where a distance (thickness) between the inner circumferential surface of the through-hole 50S and an outer surface (end surface) of the sintered component S is equal to or more than a diameter of the through-hole 50S.
[Action and Effects]
In the method for manufacturing a sintered component according to the foregoing embodiments, drilling using a drill is performed on a powder-compact green body before sintering. Accordingly, cutting can be easily performed and also a cutting resistance (thrust load) can be significantly reduced. Therefore, as compared with a conventional manufacturing method in which drilling using a drill is performed after sintering, a machining time can be reduced, a precision of a machined hole can be enhanced and also a tool life can be significantly improved. Further, in the method for manufacturing a sintered component according to the above embodiments, drilling is performed using a drill, which has a circular arc-shaped cutting edge on a point portion thereof. Accordingly, when a through-hole is formed in the powder-compact green body, occurrence of edge chipping can be suppressed. As a result, the method for manufacturing a sintered component as described above can suppress occurrence of edge chipping and also has a good productivity.
In the sintered component according to the foregoing embodiments, the hole (through-hole) is formed therein and the inner circumferential surface of the hole has the satin finish shape. Accordingly, since this means that drilling using a drill is performed on a powder-compact green body before sintering, the sintered component has a good productivity.
In the drill according to the foregoing embodiments, the circular arc-shaped cutting edge is provided on the point portion thereof. Accordingly, it is possible to suppress occurrence of edge chipping when a through-hole is formed in a powder-compact green body.
Although in the foregoing embodiments, the case where the though-hole is formed in the powder-compact green body using the drill has been described by way of example, a hole to be formed may be a blind hole. In the case of the blind hole, it is possible to make a thickness of a bottom of the hole thinner. For example, the drill is suitable for a case where a blind hole is formed such that a thickness of a bottom thereof is 2 times or less of a drill diameter (hole diameter). A lower limit of the thickness of the bottom may be set to about ¼ or more of the drill diameter (hole diameter), or about ½ or more.
Powder-compact green bodies were fabricated by press-molding a raw material powder containing a metal powder and then a drilling test was performed on the powder-compact green bodies using drills having different cutting edge shapes.
(Powder-Compact Green Body)
A water atomized iron powder (average particle diameter (D50): 100 μm), a water atomized copper powder (average particle diameter (D50): 30 μm), a carbon (graphite) powder (average particle diameter (D50): 20 μm) and ethylene-bis-stearic acid amide as a lubricant were prepared, and then by mixing them, a raw material powder was prepared.
The prepared raw material powder was filled in a predetermined mold and then press-molded at a pressing pressure of 600 MPa. In this way, plate-shaped powder-compact green bodies having a size of length 50 mm×width 20 mm×thickness 10 mm were fabricated. A density of powder-compact green bodies was 6.9 g/cm3. This density is an apparent density as calculated from size and mass of the powder-compact green bodies.
Subsequently, drilling was performed on the fabricated powder-compact green bodies using the drills, thereby forming a through-hole in a thickness direction of the powder-compact green bodies. Then, an opening on an exit side of the through-hole was observed and an occurrence situation of edge chipping was checked.
As one of drills, an R drill, in which a shape of a cutting edge thereof is semi-circular as shown in
Also, a V drill, in which a shape of a cutting edge thereof is a V-shape, was prepared. The prepared V drill was a drill (Model No. 05WHNSB0400-TH, material: sintered carbide) produced by Hitachi Tool Engineering, Ltd. In the V drill, a drill diameter d was 4.0 mm and a point angle of the cutting edge was 140°.
Drilling was performed on the powder-compact green bodies using the R drill and the V drill, thereby forming a through-hole. In the case of using the R drill, cutting conditions were the number of revolutions of 4000 rpm and a feed rate of 1600 mm/min. In the case of using the V drill, cutting conditions were the number of revolutions of 4000 rpm, a feed rate of 800 mm/min from an entrance of the hole up to a hole depth of 5 mm, and then a feed rate of 1600 mm/min from the hole depth of 5 mm up to penetration.
After drilling, with respect to the powder-compact green bodies in which a through-hole was formed using each of the drills, an opening on an entrance side of the through-hole was observed using an optical microscope. The results are shown in
In
In
From this result, it can be seen that occurrence of edge chipping can be suppressed by using an R drill having a circular-arc shaped cutting edge.
Drilling was performed on powder-compact green bodies using R drills having different rake angles and then thrust loads when forming a through-hole were compared with each other.
As powder-compact green bodies to be machined, the same as those in Test Example were employed.
Like Test Example 1, the R drills used had a cutting edge of a semi-circular shape and were fabricated by grinding a cutting edge on a point portion of a drill (Model No. MDW0800GS4, material: sintered carbide) produced by Sumitomo Electric Hardmetal Co. In these R drills, a drill diameter d was 8.0 mm, a central angle α of a circular arc defining the cutting edge was 180°, and a radios R of the circular arc was 4.0 mm (0.5 times of the drill diameter d). In addition, three types of R drills having rake angles of 0°, 7° and 10°, respectively, were fabricated. An R drill having a rake angle of 0° was referred to as R0, an R drill having a rake angle of 7° was referred to as R7, and an R drill having a rake angle of 10° was referred to as R10.
Drilling was performed three times on the powder-compact green bodies using each of the three types of drill (R0, R7, R10), thereby forming three through-holes in a thickness direction of the powder-compact green bodies. Cutting conditions were the number of revolutions of 2000 rpm and a feed rate of 200 mm/min (feed amount of 0.1 mm/rev). Also, for each of the first to third drilling, thrust loads and torques when forming a through-hole were measured. Thrust loads and torques were measured from beginning of drilling until a through-hole is formed, using a cutting dynamometer (Model No. 9272 produced by Kistler Japan Co., Ltd.), and maximum values thereof were obtained. Also, average values were calculated from each thrust load and torque in each drilling process.
Thrust loads and torques when drilling was performed using the drills R0, R7 and R10 are shown in Tables 1 to 3, respectively. For example, the reference character “R0-1” in Table 1 means the first drilling using the drill R0, and thus the symbol on the front half thereof indicates the drill used and the number on the rear half indicates the number of times of machining (the same is also applied to Tables 2 and 3).
Further, in
From the results of Tables 1 to 3 and
After drilling is performed on a powder-compact green body using an R dill, the powder-compact green body in which a through-hole is formed by the R drill was sintered, thereby fabricating a sintered component.
As the powder-compact green body to be machined, the same as those in Test Example was employed.
Herein, an R drill in which a shape of a cutting edge thereof is semi-circular and a drill diameter d is 3.5 mm was employed. The R drill was fabricated by grinding a cutting edge on a point portion of a drill (Model No. MDW0350GS4, material: sintered carbide) produced by Sumitomo Electric Hardmetal Co. In the R drill, a central angle α of a circular arc defining the cutting edge was 180°, a radios R of the circular arc was 1.75 mm (0.5 times of the drill diameter d), and a rake angle was 0°.
Drilling was performed on the powder-compact green body using the R drill, thereby forming a through-hole in a thickness of the powder-compact green body. Cutting conditions were the number of revolutions of 2000 rpm and a feed rate of 200 mm/min (feed amount of 0.1 mm/rev). After drilling, the powder-compact green body, in which the through-hole was formed, was sintered at a temperature of 1130° C. during 20 minutes, thereby fabricating a sintered component.
A powder-compact green body in which a through-hole was formed in the same manner, was cut along a thickness direction thereof through a center axis of the through-hole, and an inner circumferential surface of the through-hole was observed by an optical microscope. A photograph of the cross section is shown in
A through-hole was formed in a sintered component after sintering, using a drilling and then in the same manner, an inner circumferential surface of the through-hole was observed. As a result, although not shown, the inner circumferential surface of the through-hole was a smooth surface having a few of concave and convex portions and thus was a shiny state. Also, a ten point medial height Rz of the inner circumferential surface of the through-hole was measured as 11 μm. The drill used for drilling of the sintered component was MDW0350GS4 produced by Sumitomo Electric Hardmetal Co., in which a shape of a cutting edge thereof was a V shape, a drill diameter d was 3.5 mm and a point angle of the cutting edge was 135°.
This application is based on Japanese Patent Application No. 2014-252531 filed on Dec. 12, 2014, the entire contents of which are incorporated herein by reference.
The method for manufacturing a sintered component according to one aspect of the present invention can be used for manufacturing various sintered components, such as automobile parts and machine parts (sprockets, rotors, gears, rings, flanges, pulleys, vanes, bearings and like). The sintered component according to one aspect of the present invention can be used for various sintered components, such as automobile parts and machine parts. The drill according to one aspect of the present invention can be used for drilling of a powder-compact green body.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2014-252531 | Dec 2014 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4839949 | Sobue | Jun 1989 | A |
| 4882304 | Novich et al. | Nov 1989 | A |
| 5403373 | Kitagawa et al. | Apr 1995 | A |
| 5725338 | Cabaret et al. | Mar 1998 | A |
| 5900559 | Nakamura et al. | May 1999 | A |
| 20030202853 | Ko | Oct 2003 | A1 |
| 20070274163 | Wild | Nov 2007 | A1 |
| 20090191368 | Hironaga | Jul 2009 | A1 |
| 20100166514 | Okumura | Jul 2010 | A1 |
| 20110064937 | Mukoyama | Mar 2011 | A1 |
| 20110268518 | Sampath | Nov 2011 | A1 |
| 20140169898 | Goh | Jun 2014 | A1 |
| 20150357118 | Lee | Dec 2015 | A1 |
| 20170320136 | Sonoda et al. | Nov 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 102825255 | Dec 2012 | CN |
| 102917823 | Feb 2013 | CN |
| S49-090969 | Aug 1974 | JP |
| S58-189305 | Nov 1983 | JP |
| S61-003803 | Jan 1986 | JP |
| S61-264102 | Nov 1986 | JP |
| S62-096601 | May 1987 | JP |
| S62-208527 | Sep 1987 | JP |
| H05-171205 | Jul 1993 | JP |
| H05-171334 | Jul 1993 | JP |
| H06-145703 | May 1994 | JP |
| H07-195216 | Aug 1995 | JP |
| 10-073132 | Mar 1998 | JP |
| 2002-249887 | Sep 2002 | JP |
| 2003-205410 | Jul 2003 | JP |
| 2004-346358 | Dec 2004 | JP |
| 2006-165300 | Jun 2006 | JP |
| 2006165300 | Jun 2006 | JP |
| 2006-336078 | Dec 2006 | JP |
| 2007-510895 | Apr 2007 | JP |
| 2009-172518 | Aug 2009 | JP |
| 2009-185328 | Aug 2009 | JP |
| 2011-069372 | Apr 2011 | JP |
| 2011-144419 | Jul 2011 | JP |
| 2012-241728 | Dec 2012 | JP |
| 2012-254501 | Dec 2012 | JP |
| 2012254501 | Dec 2012 | JP |
| 2016-113657 | Jun 2016 | JP |
| 2001-0052113 | Jun 2001 | KR |
| 9928067 | Jun 1999 | WO |
| 0250331 | Jun 2002 | WO |
| 2007-114146 | Oct 2007 | WO |
| 2011135277 | Nov 2011 | WO |
| Entry |
|---|
| Machine translation of JP-2012254501-A (Year: 2012). |
| Machine Translation of JP-2006165300-A (Year: 2006). |
| Decision of Refusal issued in counterpart Japanese Patent Application No. 2018-224221 dated Dec. 21, 2020. |
| German et al., “Science of powder metallurgy,” first Edition, Tokyo High Court, 1996, ISBN 4-7536 to 5091-X, pp. 244 to 247, and 300 to 303 [Cited in NPL 1]. |
| Eijiro, “Expansion and contraction accompanied by sintering of metallic green compact,” Journal of the Japan Society of Metallurgy, 1987, vol. 26, No. 9, pp. 842-866 [Cited in NPL 1]. |
| Number | Date | Country | |
|---|---|---|---|
| 20200331065 A1 | Oct 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15535263 | US | |
| Child | 16922287 | US |