Patent Application
20150255223
The present invention relates to a method for manufacturing a solid electrolytic capacitor and a solid electrolytic capacitor.
A method for manufacturing a solid electrolytic capacitor using only manganese dioxide as the solid electrolyte, a method for manufacturing a solid electrolytic capacitor using only a conductive polymer as the solid electrolyte, and a method for manufacturing a solid electrolytic capacitor using manganese dioxide and a conductive polymer (for example, refer to patent literature 3) are conventionally well known.
In patent literature 1, a method for manufacturing a solid electrolytic capacitor is disclosed wherein after forming a conductive polymer in the form of islands on the surface of a dielectric oxide film, a manganese dioxide layer is formed on the entire surface of the dielectric oxide film to cover this conductive polymer.
According to this method of manufacture, since a conductive polymer with a higher conductivity than the manganese dioxide is formed on the surface of the dielectric oxide film, it is possible to prepare a solid electrolytic capacitor with excellent ESR properties that are better than a solid electrolytic capacitor using only manganese dioxide as the solid electrolyte. Also, with this method of manufacture, since manganese dioxide with good adhesion with the dielectric oxide film is formed on the entire surface of the dielectric oxide film to cover this conductive polymer with islands, it is possible to improve the adhesion between the conductive polymer and the dielectric oxide film.
In patent literature 2, a method for manufacturing a solid electrolytic capacitor is disclosed wherein after forming a manganese dioxide layer with a thickness of 1 μm or more on the entire surface of a dielectric oxide film, a conductive polymer layer is formed on the surface of the manganese dioxide layer by chemical bonding using an oxidizing agent.
With this method of manufacture, since a manganese dioxide layer is formed on the entire surface of the dielectric oxide film, it is possible to prevent damage to the dielectric oxide film when the dielectric oxide film is directly exposed to oxygen during chemical bonding.
In patent literature 3, a method for manufacturing a solid electrolytic capacitor is disclosed wherein the anode formed on the manganese dioxide layer on the entire surface of the dielectric, oxide film is immersed in an aqueous suspension where a conductive polymer powder is suspended, and a conductive polymer layer is formed on the surface of the manganese dioxide layer.
With this method of manufacture, since a conductive polymer layer is uniformly formed on the surface of the manganese dioxide layer with sufficient thickness by immersion in the aqueous suspension, it is possible to prevent a deterioration in the ESR properties and the leakage current characteristics from damage to the manganese dioxide layer or dielectric oxide film due to thermal stress during mounting.
Patent Literature 1: Official gazette for Kokai 2008-263167
Patent Literature 2: Official gazette for Kokai 116-69082
Patent Literature 3: Official gazette for Kokai 2006-147900
However, the solid electrolytic capacitor produced according to the method of manufacture set forth in the abovementioned Patent Literature I is manufactured by forming a manganese dioxide layer over the entire surface of a dielectric oxide film to cover the islands of conductive polymer so when compared to a solid electrolytic capacitor using only a conductive polymer on a solid electrolyte, the ESR properties become inferior. Furthermore, with this method of manufacture, the manganese dioxide layer is formed after forming the island shaped conductive polymer so the islands of conductive polymer ends up being inferior due to the heat treatment performed while forming the manganese dioxide layer, so the ESR properties deteriorate even further.
Additionally, with the solid electrolytic capacitor produced according to the method of manufacture set forth in the abovementioned Patent Literature 2, a manganese dioxide layer with a thickness of 1 μm or more is formed between the dielectric oxide film and the conductive polymer layer so when compared to a solid electrolytic capacitor using only a conductive polymer on a solid electrolyte, the ESR properties become inferior.
With the solid electrolytic capacitor produced according to the method of manufacture set forth in the abovementioned Patent Literature 3, a manganese dioxide layer is also formed over the entire surface of a dielectric oxide film so when compared to a solid electrolytic capacitor using only a conductive polymer on a solid electrolyte, the ESR properties become inferior. Also, in general, since the particle diameters of the conductive polymer in an aqueous solution are relatively large, there is a concern that the conductive polymer will not extend to the inside of the anode body. Therefore, the contact portion of the conductive polymer layer and the manganese dioxide layer is reduced, and there is a concern that the ESR properties will deteriorate even further.
That is to say, the solid electrolytic capacitor produced according to the method of manufacture set forth in the abovementioned Patent Literatures 1˜3, all have the benefit of forming a manganese dioxide layer but have the problem of inferior ESR properties when compared to a solid electrolytic capacitor using only a conductive polymer on a solid electrolyte.
The present invention has studied the aforementioned facts and presents a method for manufacturing a solid electrolytic capacitor and a solid electrolytic capacitor with excellent ESR properties.
To solve the abovementioned problems, a method for manufacturing a solid electrolytic capacitor, wherein an anode body is obtained by forming a dielectric oxide film on the surface of a sintered body that is formed by sintering a molded body formed of a valve acting metal powder or on the surface of a roughened valve acting metal foil, wherein the processes forming the solid electrolytic layer comprising a protrusion forming process wherein protrusions formed of manganese dioxide and having an average diameter of 10˜102 nm are formed on the surface of the dielectric oxide coating film so that the projections are scattered like islands and the surface coverage is 1˜20%, and a conductive polymer layer forming process wherein a conductive polymer layer is formed on the surfaces of the protrusions and the dielectric oxide coating film.
With this configuration, since the protrusions are formed of manganese dioxide and scattered in the shape of islands on the surface of the dielectric oxide film, it is possible for the conductive polymer layer to come into contact with the dielectric oxide film between the protrusions. Therefore, with this configuration, by using manganese dioxide, a deterioration of the ESR properties can be inhibited.
Additionally, with this configuration, the plurality of protrusions formed on the surface of the dielectric oxide film during formation of the conductive polymer layer are in a state of getting stuck in the conductive polymer layer so it is possible to improve the adhesion between the dielectric oxide film and the conductive polymer layer. Furthermore, with this configuration, the ESR properties can be improved and it is possible to prevent a deterioration of the ESR properties and the leakage current characteristics when the conductive polymer layer delaminates from the dielectric oxide film due to thermal stress and such.
Furthermore, with this configuration, when forming the conductive polymer layer with chemical polymerization, since the amount of polymerization solution retained increases due to the plurality of protrusions, it is possible to improve the capacitance emergence rate (internal impregnating ability). Additionally, with this configuration, a large capacity solid electrolytic capacitor is easily formed, and it is possible to reduce the number of immersions in a polymerization solution.
In the present invention, “average diameter” refers to the average value of the major axis (maximum diameter) of the protrusions with a planar view.
In the abovementioned (1) method of manufacture, for example, the (2) protrusion formation process includes a pretreatment process to leave the anode body in a humid environment with a humidity of 8 g/cm3 or greater, an immersion treatment process to immerse the anode body in a manganese nitrate solution after the pretreatment process, an intermediate treatment process to leave the anode body in a humid environment with a humidity of 8 g/cm3 or greater after the immersion treatment process and a heat treatment process for a pyrolyzing reaction of the anode body in an environment of a specific relative humidity after the intermediate treatment process.
In the abovementioned (2) method of manufacture, it is preferred that a surfactant be added to the (3) manganese nitrate solution.
With this configuration, since it is possible to lower the surface tension with the surfactant, it is possible to improve the internal impregnating ability of the manganese nitrate.
In the abovementioned (2) or (3) methods of manufacture, for example, it is possible for the (4) specific relative humidity to be 50˜80%.
In the abovementioned (1)˜(4) methods of manufacture, it is also acceptable to conduct a reforming process between the (5) protrusion formation process and the conductive polymer layer formation process in order to re-form the dielectric oxide film.
With this configuration, since the defects in the dielectric oxide film are repaired with the re-forming process, it is possible to improve the leakage current characteristics.
In the abovementioned (1)˜(5) methods of manufacture, it is preferred that the conductive polymer layer be formed with chemical polymerization in the (6) conductive polymer layer formation process,
Also, to solve the abovementioned problems, the solid electrolytic capacitor pertaining to the present invention is (7) a solid electrolytic capacitor, wherein a dielectric oxide film is formed on the surface of a sintered body that is formed by sintering a molded body formed of a valve acting metal powder or on the surface of a roughened valve acting metal foil, and a solid electrolyte layer is formed on the surface of the dielectric, oxide film, wherein the solid electrolytic layer is formed with island shapes scattered on the surface of the dielectric oxide film so the surface coverage is 1˜20%, and there are a plurality of protrusions of manganese dioxide having average diameters of 10˜102 nm, and a conductive polymer layer formed on the surfaces of the protrusions and the dielectric oxide film.
With this configuration, since the conductive polymer layer comes into contact with the dielectric oxide film in between the protrusions of manganese dioxide, it is possible to prevent a deterioration in the ESR properties by using the manganese dioxide.
Also, with this configuration, the plurality of protrusions formed on the surtlice of the dielectric oxide film are stuck in the conductive polymer layer and the adhesion between the dielectric oxide film and the conductive polymer layer is improved so the ESR properties can be improved, and it is possible to prevent a deterioration of the ESR properties and the leakage current characteristics when the conductive polymer layer delaminates from the dielectric oxide film due to thermal stress and such.
Also, with this configuration, when forming the conductive polymer layer with chemical polymerization, since the amount of polymerization solution retained increases due to the plurality of protrusions, it is possible to improve the capacitance emergence rate (internal impregnating ability), and as a result, it is possible to improve the capacitance.
[
[
Next is a description of the preferred embodiments for the method for manufacturing a solid electrolytic capacitor and a solid electrolytic capacitor pertaining to the present invention.
In the porous body production process (S1), an anode lead is embedded in tantalum powder and after press formation, a 1.0 mm×1.5 mm×0.5 mm sintered rectangular porous body (sintered body) was produced.
In the oxide film formation process (S2), the anode oxide porous body produced with the porous body production process (S1) is subject to applied voltage of 10V in a phosphate solution, and a dielectric oxide film was formed on the surface of the porous body. In this manner, the anode body was prepared.
Next, the process forming the solid electrolyte layer (solid electrolyte formation process) includes a protrusion forming process (S3) to form protrusions of manganese dioxide on the surface of a dielectric oxide film such that the protrusions are scattered in the shape of islands and a conductive polymer layer forming process (S4) to form a conductive polymer layer on the surfaces of the protrusions and the dielectric oxide film. Furthermore, the plurality of protrusions and the conductive polymer layer of manganese dioxide correspond to the “solid electrolyte :layer” in the present invention.
During the protrusion forming process (S3), the pretreatment process (S3-1), immersion treatment process (S3-2), intermediate treatment process (S3-3) and heat treatment process (S3-4) are performed in this sequence, as shown in
During the pretreatment process (S3-1), the anode body prepared with the oxide film forming process (S2) was left for 30 minutes in a humid environment with a temperature of 30° C. and a humidity of 8 g/cm3.
During the immersion treatment process (S3-2), the anode body after the pretreatment process (S3-1) was immersed in a manganese nitrate solution with a manganese nitrate concentration of 20 wt %. A wt % surfactant of polyoxyethylene alkyl ether was added to the manganese nitrate solution.
During the intermediate treatment process (S3-3), after the immersion treatment process (S3-2) the titode body was again left for 30 minutes in a humid environment with a temperature of 30° C. and a humidity of 8 g/cm3.
During the heat treatment process (S3-4), after the intermediate treatment process (S3-3), the anode body was heat treated in an environment with a temperature of 250° C. and a relative humidity of 80%, where the manganese nitrate adhering to the surface of the dielectric oxide film was pyrolyzed and protrusions of manganese dioxide were formed and scattered like islands. To be more specific, the surface coverage of all of the protrusions on the dielectric oxide film surface was 10%, and the average diameter of the protrusions was 10 nm.
The surface coverage here indicates the ratio of the surface coverage to the dielectric oxide film of the protrusions of manganese dioxide formed on the surface of the dielectric oxide film. To be more specific, this was calculated from the capacitance (capacitance originally with these capacitor elements: capacitance A) after sufficiently including the conductive solution in the capacitor element after forming the protrusions of manganese dioxide and the capacitance after washing the conductive solution from the abovementioned capacitor element and sufficiently drying off the moisture (capacitance actually with these capacitor elements after formation of the protrusions of manganese dioxide: capacitance B).
Next is the formula to calculate the surface coverage.
During the conductive polymer layer forming process (S4), a monomer solution containing 3,4-ethylene dioxythiophene and an oxidizing agent solution containing iron (II) p-toluenesulfonic acid were combined and after the protrusion forming process (S3), the anode body was immersed in the mixed solution (polymerization solution) maintained at a temperature of −5° C., and then after lifting it out, was chemically polymerized at a temperature of 25° C. In this embodiment, a conductive polymer layer was formed by repeating the conductive polymer layer forming process (S4) a total of 7°.
During the conductive polymer layer forming process (S4), since a product with oxidizability that is stronger than manganese dioxide was used as the oxidizing agent containing an oxidizing agent solution (iron (II) p-toluenesulfonic acid in this embodiment), it can be said that there is essentially no cost reduction with manganese dioxide as the oxidizing agent for the protrusions during chemical polymerization.
Next, the cathode layer forming process (S5) was conducted by coating a carbon paste or a silver paste on the surface of the conductive polymer layer formed in the conductive polymer layer forming process (S4) then drying to form a cathode layer comprising a carbon layer or a silver layer,
Finally, an assembly process (S6) was conducted by connecting the cathode terminal to the surface of the cathode layer, and after connecting the anode terminal to the anode lead protruding from the anode body, and a sheathing resin was implemented with a transfer mold to produce a solid electrolytic capacitor with a rating of 4V-100 μF (2012 size).
With Embodiment 2 in the present invention, (1) the manganese nitrate concentration in the manganese nitrate solution used during the immersion treatment process (S3-2) is 5 wt % and (2) the relative humidity for the heat treatment process (S3-4) is 70% but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1, In this embodiment, the surface coverage for all of the protrusions is 1% that of the dielectric oxide film surface, and the average diameter of the protrusions is 48 nm.
The method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 3 in the present invention has a relative humidity for the heat treatment process (S3-4) that is 70% but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment I. In this embodiment, the surface coverage for all of the protrusions is 10% that of the dielectric oxide film surface, and the average diameter of the protrusions is 51 nm.
The method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 4 in the present invention (1) does not add a surfactant to the manganese nitrate used in the immersion treatment process (S3-2), and (2) has a relative humidity for the heat treatment process (S3-4) that is 70% but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1. In this embodiment, the surface coverage for all of the protrusions is 9% that of the dielectric oxide film surface, and the average diameter of the protrusions is 50 nm.
The method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 5 in the present invention (1) has a relative humidity for the heat treatment process (S3-4) that is 70% and (2) performs a re-forming process one time between the protrusion forming process (S3) and the conductive polymer layer forming process (S4) but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1. During the re-forming process, anode oxidation is performed in a phosphate solution at an applied voltage of 8V to re-form the dielectric oxide film. In this embodiment, the surface coverage for all of the protrusions is 10% that of the dielectric, oxide film surface, and the average diameter of the protrusions is 51 nm.
The method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 6 in the present invention (1) has a relative humidity for the heat treatment process (S3-4) that is 70% and (2) performs the protrusion forming process (S3) a total of two times but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1. In this embodiment, the surface coverage for all of the protrusions is 20% that of the dielectric oxide film surface, and the average diameter of the protrusions is 54 nm.
The method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 7 in the present invention has a relative humidity for the heat treatment process (S3-4) that is 50% but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1. In this embodiment, the surface coverage for all of the protrusions is 11% that of the dielectric oxide film surface, and the average diameter of the protrusions is 102 nm.
The method for manufacturing a solid electrolytic capacitor for the conventional example (1) does not perform the protrusion forming process (S3) and (2) performs the conductive polymer layer forming process (S4) a total of 10 times, but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1.
The method for manufacturing a solid electrolytic capacitor for comparative example 1 does not perform the protrusion forming process (S3) but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1, In other words, the method for manufacturing a solid electrolytic capacitor for comparative example 1 performs the conductive polymer layer forming process (S4) a total of 10 times, but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to the conventional example.
The method for manufacturing a solid electrolytic capacitor for comparative example 2 has a relative humidity for the heat treatment process (S3-4) that is 90% but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1. In comparative example 2, the surface coverage for all of the protrusions is 10% that of the dielectric oxide film surface, and the average diameter of the protrusions is 5 nm.
The method for manufacturing a solid electrolytic capacitor for comparative example 3 (1) has a relative humidity for the heat treatment process (S3-4) that is 70% and (2) performs the protrusion forming process (S3) a total of three times but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment 1. In comparative example 3, the surface coverage for all of the protrusions is 29% that of the dielectric oxide film surface, and the average diameter of the protrusions is 57 nm.
The method for manufacturing a solid electrolytic capacitor for comparative example 4 has a relative humidity for the heat treatment process (S3-4) that is 20% but otherwise, it is the same as the method for manufacturing a solid electrolytic capacitor pertaining to Embodiment I. In comparative example 4, the surface coverage for all of the protrusions is 11% that of the dielectric oxide film surface, and the average diameter of the protrusions is 160 nm.
The key manufacturing conditions for the method for manufacturing a solid electrolytic capacitor in Embodiments 1˜7, the conventional example and comparative examples 1˜4 are summarized as shown in Table 1.
The values for the average protrusion diameter, surface coverage for the protrusions, capacitance, ESR, leaked current, ESR after heat resistance testing and the leaked current after heat resistance testing for each solid electrolytic capacitor produced with the method for manufacturing a solid electrolytic capacitor in Embodiments 1˜7, the conventional example and comparative examples 1˜4 are shown in Table 2. The values shown in Table 2 are all average values for 12 solid electrolytic capacitors. Also, the heat resistance testing shown in Table 2 conducted reflow for 10 seconds at a temperature of 240° C.
[Presence of Protrusions]
One can understand from Table 2 that the solid electrolytic capacitors in Embodiments 1 7 have excellent ESR properties, capacitance, leaked current characteristics, ESR properties after heat resistance testing and leaked current characteristics after heat resistance testing compared to the solid electrolytic capacitors in the conventional example and comparative example 1 where a plurality of protrusions comprising manganese dioxide are not formed,
The excellent ESR properties are thought to be because of the contact between the dielectric oxide film and the conductive polymer layer and the strong adhesion between the dielectric oxide film and the conductive polymer layer. To be more specific, it is thought that the method for manufacturing in Embodiments 1˜7 forms protrusions comprising manganese dioxide on the surface of the dielectric oxide film that are scattered about like islands so it is possible to have the conductive polymer layer contact the dielectric oxide film between the protrusions and thus it is possible to suppress the deterioration of ESR properties due to the use of manganese dioxide. Furthermore, with the method for manufacturing in Embodiments 1˜7, since a plurality of protrusions formed on the surface of the dielectric oxide film when forming the conductive polymer layer are in a state stuck in the conductive polymer layer, it is thought that the adhesion between the dielectric oxide film and the conductive polymer layer is strengthened and the ESR properties can he improved,
The excellent capacitance is due to the large contact area between the dielectric oxide film and the conductive polymer layer. To be more specific, with the method for manufacturing in Embodiments 1˜7, since the amount of polymerization solution retained increases due to the plurality of protrusions, it is possible to improve the capacitance emergence rate (internal impregnating ability). As a result, since it is possible to increase the contact area between the dielectric oxide film and the conductive polymer layer, it is possible to improve the capacitance.
The excellent leaked current characteristics is thought to be due to the formation of a plurality of protrusions of manganese dioxide. The manganese dioxide has a high level of strength compared to the conductive polymer and due to strong stress from the outside, the leaked current characteristics are superior to the conductive polymer. As a result, it is possible to improve the leaked current characteristics with the method for manufacturing in Embodiments 1˜7.
The excellent ESR after heat resistance testing and the excellent leaked current characteristics after heat resistance testing is thought to be due to an increase in the adhesion between the dielectric oxide film and the conductive polymer layer mentioned above and the difficulty in delaminating the conductive polymer layer from the dielectric oxide film due to the heat stress.
Additionally, the solid electrolytic capacitor in comparative example 1 has inferior capacitance, ESR properties, ESR properties after heat resistance testing and leaked current characteristics after heat resistance testing when compared to the solid electrolytic capacitor in the conventional example. This is thought to be due to the inability to form a good conductive polymer layer since the conductive polymer layer formation process (S4) was only performed a total of 7 times in the method of manufacture in comparative example 1.
On the other hand, when the solid electrolytic capacitor in Embodiments 1˜7 were compared with the solid electrolytic capacitor in the conventional example, the capacitance, ESR properties, ESR properties after that resistance testing and leaked current characteristics after heat resistance testing were excellent. Therefore, with the method for manufacture in Embodiments 1˜7, even if the conductive polymer layer formation process (S4) was only performed a total of 7 times, it is understood that a good conductive polymer layer can be formed. This is due to the increase in the amount of polymerization solution retained because of the plurality of protrusions as indicated above and an improvement in the internal impregnating ability.
(Average Diameter of the Protrusions)
The solid electrolytic capacitor in comparative example 2 had capacitance, ESR properties, ESR properties after heat resistance testing and leaked current characteristics after heat resistance testing that changed very little when compared to the solid electrolytic capacitor in the conventional example even with a plurality of protrusions (average diameters of 5 ran). This is thought to he due to the fact that the average diameter of the protrusions was 5 nm, which is very small, so there was almost no impact of the protrusions on the adhesion between the dielectric oxide layer and the conductive polymer layer or the internal impregnating ability.
So, in comparative example 2, it is thought that since the average diameter of 5 nm for the protrusions was very small, and since the relative humidity during the heat treatment process (S3-4) was 90%, which is high, the pyrolizing reaction of the manganese dioxide was delayed, due to the presence of water vapor, and the manganese dioxide was dispersed for formation.
Also, the solid electrolytic capacitor in comparative example 4 had capacitance, ESR properties, and ESR properties after heat resistance testing that changed very little when compared to the solid electrolytic capacitor in the conventional example even with a plurality of protrusions (average diameters of 160 nm). The lack of change in the capacitance was due to the fact that the average diameter of the protrusions was very large, at 160 nm, so the internal impregnating ability did not improve with the protrusions, even with an increased retention of the polymerization solution. The lack of change in the ESR properties, and ESR properties after heat resistance testing is thought to be due to the fact that the average diameters of the protrusions was too large so the adhesion between the dielectric oxide film and the conductive polymer layer did not improve (or was diminished).
On the other hand, the solid electrolytic capacitor in Embodiment 1 (protrusions with average diameters of 10 nm) or the solid electrolytic capacitor in Embodiment 7 (protrusions with average diameters of 102 nm) had excellent ESR properties, capacitance, leaked current characteristics, ESR properties after heat resistance testing and leaked current characteristics after heat resistance testing when compared to the solid electrolytic capacitor in the conventional example. Accordingly, it is understood that the average diameter of the protrusions is preferred to be 10˜102 nm.
(Surface Coverage of the Protrusions)
The solid electrolytic capacitor in comparative example 3 (surface coverage of the protrusions of 29%) has inferior ESR properties and ESR properties after heat resistance testing when compared to the solid electrolytic capacitor in the conventional example. This is due to the reduction in the contact area between the dielectric oxide film and the conductive polymer layer, and by increasing the contact area between the dielectric oxide film and the plurality of protrusions comprising manganese dioxide, the detrimental impact on the ESR properties by using manganese dioxide is enhanced.
On the other hand, the solid electrolytic capacitor in Embodiment 2 (protrusions with surface coverage of 1%) or the solid electrolytic capacitor in Embodiment 6 (protrusions with surface coverage of 20%) had excellent ESR properties, and ESR properties after heat resistance testing when compared to the solid electrolytic capacitor in the conventional example. Accordingly, it is understood that the surface coverage of the protrusions is preferred to be 1˜20%.
(Other)
The solid electrolytic capacitor in Embodiment 4 had excellent ESR properties, capacitance, leaked current characteristics, ESR properties after heat resistance testing and leaked current characteristics after heat resistance testing when compared to the solid electrolytic capacitor in the conventional example. Accordingly, it is understood that a manganese nitrate solution not containing a surfactant can be used in the immersion treatment process (S3-2).
The solid electrolytic capacitor in Embodiment 3 has slightly higher surface coverage of the protrusions when compared to the solid electrolytic capacitor in Embodiment 4 so it is understood that if a manganese nitrate solution containing a surfactant is used in the immersion treatment process (S3-2), the surface coverage of the protrusions increases. This is due to a decrease in the surface tension from the surfactant, which improves the internal impregnating ability of the manganese nitrate solution.
Additionally, the solid electrolytic capacitor in Embodiment 5 has excellent leaked current characteristics, and leaked current characteristics after heat resistance testing when compared to the solid electrolytic capacitor in Embodiments 1˜4, 6 and 7 so it is understood that the leaked current characteristics, and leaked current characteristics after heat resistance testing are improved by performing the re-forming process to re-form the dielectric oxide layer between the protrusion forming process (S3) and the conductive polymer layer forming process (S4). This is thought to be due to repairing the defects and such in the dielectric oxide film with the re-forming process.
The abovementioned explained the preferred embodiment for the method for manufacturing a solid electrolytic capacitor and a solid electrolytic capacitor pertaining to the present invention but the present invention is not limited to the abovementioned embodiments.
For example, it is possible to change the manufacturing conditions for the relative humidity shown in the abovementioned Table 1 or the number of times performing the protrusion forming process (S3) as desired. The relative humidity in the abovementioned embodiments was a parameter to increase and decrease the average diameter of the protrusions and the number of time the protrusion forming process (S3) was performed was a parameter to increase and decrease the surface coverage of the protrusions. However, any manufacturing condition can he used to achieve the same effect as long as the protrusions comprising manganese dioxide have a coverage of 1˜20% on the surface of the dielectric oxide film, and with average diameters of 10˜102 nm that are formed to scatter in the shape of islands.
Additionally, chemical polymerization was performed during the conductive polymer layer forming process (S4) in each of the abovementioned embodiments, but a conductive polymer layer can be formed with a known method other than chemical polymerization such as a method to remove a solvent after being immersed in a conductive polymer solution or a solution in which a conductive polymer is dispersed. When these methods were compared with chemical polymerization, since the molecular weight of the conductive polymer was higher from the beginning, the plurality of protrusions formed on the surface of the dielectric oxide film when forming the conductive polymer layer were in a state of being stuck into the conductive polymer layer, so the maximum demonstration of the effect of the present invention is when performed with chemical polymerization. Also, in each of the abovementioned embodiments, 3,4-ethylene dioxythiophene was used as the conductive polymer but it is not limited to this, and it is possible to use generally known polythiopenes, polypyrrole, polyaniline or any of their derivatives as the conductive polymer used in the solid electrolytic capacitor.
Furthermore, in each of the abovementioned embodiments, a tantalum sintered body was used as the anode body material but it is acceptable to use a valve acting metal sintered body or a roughened valve acting metal foil such as niobium or aluminum. With valve acting metal foil, it is possible to use an aluminum foil in a thickness of 0.1 mm where the surface has been electrochemically etched.
With the present invention, it is possible to present a method for manufacturing a solid electrolytic capacitor and a solid electrolytic capacitor with excellent ESR properties.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-189520 | Aug 2012 | JP | national |