METHOD FOR MANUFACTURING WINDOW

Abstract

A method for manufacturing a window includes providing a base glass, and strengthening the base glass by exposing the base glass to a strengthening molten salt and an additive. The additive contains at least one of Al2(SO4)3, Al(NO3)3, K2SiO3, Na2SiO3, KCl, Ca(NO3)2, and Mg(NO3)2, and a window having good surface compressive stress and excellent surface chemical resistance may thus Ire provided.

Description

TECHNICAL FIELD

The present invention relates to a method for manufacturing a window, and more particularly, to a method for manufacturing a window used as a cover glass of an electronic device.

DISCUSSION OF THE RELATED ART

Electronic devices include windows, housings, and electronic elements Hie electronic elements may include various types of elements activated in response to electrical signals, such as display elements, touch elements, or detection elements.

The windows protect the electronic elements and provide active areas to users. Accordingly, the users provide inputs to the electronic elements or receive information generated in the electronic elements through the windows. In addition, the electronic elements may be stably protected from external shocks through the windows.

In line with the current trend for slimness in electronic devices, the windows are also required to be light and thin, and, in an effort to overcome the resulting structural vulnerability, ways to strengthen the windows to be provided with excellent strength and surface durability are being studied.

SUMMARY

A method for manufacturing a window includes providing a base glass. The base glass is exposed to a mixed melt including a strengthening molten salt and an additive. The additive includes Al₂(SO₄)₃, Al(NO₃)₃, K₂SiO₃, Na₂SiO₃, KCl, Ca(NO₃)₂, and or Mg(NO₃)₂.

The additive may be included in the mixed melt an amount of 0 wt % to 10 wt % with respect to a total weight of the mixed melt.

The additive may be Al₂(SO₄)₃ or Al(NO₃)₃.

The base glass may include SiO₂, Al₂O₃, and Li₂O₃.

The base glass may further include P₂O₃.

The base glass may include SiO₂ in an amount of 50 wt % to 80 wt %, Al₂O₃ in an amount of 10 wt % to 50 wt %, and Li₂O₃ in an amount of 5 wt % to 20 wt %.

The base glass may include SiO₂, Al₂O₃, and P₂O₅.

The strengthening molten salt may be a mixed salt including two or more ions selected from the group consisting of Li⁺, Na⁺, K⁺, Rb⁺ and Cs⁺, or a single salt containing any one ion selected from the group consisting of Li⁺, Na⁺, K⁺, Rb⁺ and Cs⁺.

The step of exposing the base glass to the mixed melt may include exposing the base glass to a first strengthening molten salt and the additive to strengthen the base glass, and exposing the base glass to a second strengthening molten salt, without exposing the base glass to the additive, to further strengthen the base glass.

Exposing the base glass to the first strengthening molten salt and the additive may be performed at a first temperature and exposing the base glass to the second strengthening molten salt, without exposing the base glass to the additive, may be performed at a second temperature that is lower than the first temperature.

Exposing the base glass to the first strengthening molten salt and the additive may be performed at a temperature within a range of 380° C. to 440° C. and exposing the base glass to the second strengthening molten salt, without exposing the base glass to the additive, may be performed at a temperature within a range of 380° C. to 410° C.

The first strengthening molten salt may include KNO₃ and NaNO₃ and the second strengthening molten salt may include KNO₃.

The method may further include a step of forming a printing layer on an upper sur face of the base glass and/or a lower surface of the base glass after having exposed the base glass to the mixed melt.

A method for manufacturing a window includes providing a base glass comprising SiO₂, Al₂O₃, and Li₂O₃, and exposing the base glass to a mixed melt comprising a strengthening molten salt and an additive. The strengthening molten salt is a mixed salt containing two or more ions selected from the group consisting of Li⁺, Na⁺, K⁺, Rb⁺ and Cs⁺, or a single salt containing any one ion selected from the group consisting of Li⁺, Na⁺, K⁺, Rb⁺ and Cs⁺. The additive includes Al₂(SO₄)₃, Al(NO₃)₃, K₂SiO₃, Na₂SiO₃, KCl, Ca(NO₃)₂, and/or Mg(NO₃)₂.

The strengthening molten salt may include KNO₃ and/or NaNO₃ and the additive may include Al₂(SO₄)₃ or Al(NO₃)₃.

The additive may be included in the mixed melt an amount of 0 wt % to 10 wt % with respect to a total weight of the mixed melt.

A method for manufacturing a window includes providing a base glass. The base glass is exposed to a mixed melt including 1 first strengthening molten salt and an additive. The base glass, that has been exposed to the a mixed melt, is then exposed to a melt including a second strengthening molten salt. The additive includes Al₂(SO₄)₃, Al(NO₃)₃, K₂SiO₃, Na₂SiO₃, KCl, Ca(NO₃)₂, and/or Mg(NO₃).

The base glass may include SiO₂, Al₂O₃, and Li₂O₃.

The mixed melt may include Al₂(SO₄)₃ and Al(NO₃)₃, KNO₃, and/or NaNO₃ and the melt may include KNO₃.

The method may further include forming a printing layer on an upper surface of the base glass and/or a lower surface of the base glass after the base glass has been exposed to the melt. The base glass might not be polished after having exposed the base glass to the melt and before forming the printing layer.

BRIEF DESCRIPTION OF THE DRAWINGS

A more complete appreciation of the present disclosure and many of the attendant aspects thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:

FIG. 1 is a perspective view of an electronic device according to an embodiment;

FIG. 2 is an exploded perspective view of the electronic device illustrated in FIG. 1;

FIG. 3 is a cross-sectional view showing a window according to an embodiment;

FIG. 4 is a flowchart of a method for manufacturing a window according to an embodiment;

FIG. 5 is a schematic diagram showing a strengthening step in a method for manufacturing a window according to an embodiment;

FIG. 6 is a flowchart showing a strengthening step in a method for manufacturing a window according to an embodiment;

FIG. 7 is a flowchart of a method for manufacturing a window according to an embodiment;

FIG. 8 is a block diagram schematically showing a method for manufacturing a window according to an embodiment;

FIG. 9 is a cross-sectional view showing a portion of a window according to an embodiment;

FIG. 10 is a flowchart showing a comparative method for manufacturing a window;

FIG. 11 is a graph evaluating chemical resistance of a window manufactured by being strengthened using a comparative strengthening step;

FIGS. 12a to 12f are graphs evaluating chemical resistance of windows manufactured using a method for manufacturing a window according to an embodiment;

FIG. 13 is a perspective view illustrating a window according to an embodiment; and

FIGS. 14a and 14b are perspective views illustrating windows according to an embodiment.

DETAILED DESCRIPTION OF THE DRAWINGS

Embodiments of the present invention described herein may be modified in many alternate forms. It should be understood, however, that the invention it is not necessarily intended to be limited to the particular forms disclosed herein, but rather, the invention is intended to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the present disclosure.

In the present specification, when an element (or a region, a layer, a portion, etc.) is referred to as being “on,” “connected to,” or “coupled to” another element, it means that die element may be directly disposed on/connected to/coupled to the other element, or that a third element may be disposed therebetween.

Like reference numerals may refer to like elements throughout the figures and the detailed description thereof. Also, in the drawings, the thickness, the ratio, and the dimensions of elements may be exaggerated for an effective description of technical contents.

The term “and/or,” includes all combinations of one or more of which associated configurations may define.

It will be understood that, although the terms “first”, “second”, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another. For example, a first element could be termed a second element, and, similarly, a second element could be termed a first element, without departing from the scope of example embodiments of the present invention. The terms of a singular form may include plural forms unless the context clearly indicates otherwise.

In addition, terms such as “below,” “lower,” “above,” “upper,” and the like are used to describe the relationship of the configurations shown in the drawings. The terms are used as a relative concept and are described with reference to the direction indicated in the drawings.

It should be understood that the terms “comprise”, or “have” are intended to specify the presence of stated features, integers, steps, operations, elements, components, or combinations thereof in the disclosure, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.

Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. FIG. 1 is a perspective view showing an electronic device. FIG 1 is a view showing an embodiment of an electronic device including a window manufactured using a method for manufacturing a window according to an embodiment. FIG. 2 is an exploded perspective view of the electronic device illustrated in FIG. 1. FIG. 3 is a cross-sectional view of a window manufactured using a method for manufacturing a window according to an embodiment.

An electronic device EA may be a device activated in response to electrical signals. The electronic device EA may include various embodiments. For example, the electronic device EA may include a tablet, a laptop, a computer, a smart television, etc. In the present embodiment, the electronic device EA is illustratively presented as a smartphone.

The electronic device EA may display an image IM in a direction of a third directional axis DR3 on a display surface IS parallel to a plane defined by a first directional axis Dill and a second directional axis DR2. The display surface IS on which the image IM is displayed may correspond to a front surface of the electronic device EA and may correspond to an upper surface FS of a window CW. In addition, the electronic device EA may have a three-dimensional shape with a predetermined thickness in the direction of the third directional axis DR3, which is a direction perpendicular to a plane defined by the first directional axis DR1 and the second directional axis DR2.

Meanwhile, in the electronic device EA of an embodiment illustrated in FIG. 1, the display surface IS may include a display area DA and a non-display area NDA adjacent to the display area DA. The non-display area NDA is illustrated to be disposed surrounding the display area DA, but the embodiment is not necessarily limited thereto. The display area DA is a portion in which the image IM is provided and may be a portion corresponding to an active area AA of an electronic panel DP. Meanwhile, the image IM may include still images as well as dynamic images. FIG. 1 illustrates an internet search window as an example of the image IM.

In the present embodiment, an upper surface (or a from surface) and a lower surface (or a rear surface) of respective members are defined with respect to a direction in which the image IM is displayed. The upper surface and the lower surface may oppose each other with respect to the third directional axis DR3 and a normal direction of each of the upper and lower surfaces may be parallel to the third directional axis DR3. Meanwhile, the directions indicated by the first to third directional axes DR1, DR2, and DR3 are relative concepts, and may thus be changed to other directions. Hereinafter, first to third directions correspond to directions indicated by the first to third directional axes DR1, DR2, and DR3, respectively, and are given the same reference numerals.

The electronic device EA includes a window CW, an electronic panel DP, and a housing HAU. In the electronic device EA according to an embodiment illustrated in FIGS. 1 and 2. the window CW and the housing HAU may combine together to form an exterior of the electronic device EA.

The upper surface FS of the window CW, as described above, defines an upper surface of the electronic device EA. The upper surface FS of the window CW may include a transmission area TA and a bezel area BZA.

The transmission area TA may be an optically transparent area. For example, the transmission area TA may be an area having a visible light transmittance of about 90% or greater.

The bezel area BZA may be an area having a lower light transmittance than the transmission area TA. The bezel area BZA nay define a shape of the transmission area TA. The bezel area BZA may be adjacent to the transmission area TA and may surround the transmission area TA.

The bezel area BZA may have a predetermined color. The bezel area BZA may cover a peripheral area NAA of the electronic panel DP to prevent the peripheral area NAA from being viewed from the outside. Meanwhile, this is illustrated as an example, and in the window CW according to an embodiment of the present invention, the bezel area BZA may be omitted.

The window CW may include a glass substrate. For example, the window CW may include a strengthened glass substrate subjected to a strengthening treatment. The window CW may provide the transmission area TA by using the light transmittance of the glass, and may stably protect the electronic panel DP from external shocks by including the strengthened surface.

The window CW may be manufactured using a method for manufacturing a window according to an embodiment. The method for manufacturing a window according to an embodiment includes a strengthening step of strengthening a base glass, and in the strengthening step, a mixed melt containing a strengthening molten salt and an additive different from the strengthening molten salt may be provided to the base glass. A detailed description of the method for manufacturing a window according to an embodiment will be described later.

The electronic panel DP may be a device activated in response to electrical signals. In the present embodiment, the electronic panel DP is activated to display an image IM on a display surface IS of the electronic device EA. The image IM is provided to users through the transmission area TA, and the users may receive information through the image IM. However, this is illustrated as an example, and the electronic panel DP may be activated to detect external inputs applied to the upper surface thereof. The external inputs may include a user's touch, contact or proximity of intangible objects, pressure, light, or heat, and are not necessarily limited to any one embodiment.

For example, the electronic panel DP may include an active area AA and a peripheral area NAA. The active area AA may be an area providing the image IM. The transmission area TA may overlap at least a portion of the active area AA.

The peripheral area NAA may be an area covered by the bezel area BZA. The peripheral area NAA is adjacent to the active area AA. The peripheral area NAA may surround the active area AA. A driving circuit or driving wiring for driving the active area AA may be disposed in the peripheral area NAA.

The electronic panel DP may include a plurality of pixels PX. The pixels PX display light in response to electrical signals. The light displayed by the pixels PX makes the image IM. The pixels PX may include a display element. For example, the display element may be an organic light emitting element, a quantum dot light emitting element, a liquid crystal capacitor, an electrophoretic element, or an electrowetting element.

The housing HAU may be disposed below the electronic panel DP. The housing HAU may include a material having relatively high rigidity. For example, the housing HAU may include a plurality of frames and/or plates formed of glass, plastic, or metal. The housing HAU provides a predetermined place for accommodation. The electronic panel DP may be accommodated in the accommodation place and thus protected from external shocks.

FIG. 3 is a cross-sectional view of a window according to an embodiment. Referring to FIG. 3, the window CW may include a strengthened glass substrate BS and a printing layer BZ. The strengthened glass substrate BS may be optically transparent. In the present embodiment, the strengthened glass substrate BS may refer to the base glass BG (FIG. 5) alter being strengthened. In the present specification, a strengthened glass substrate BS described herein refers to the base glass BG (FIG. 5) strengthened in a strengthening step of the method for manufacturing a window.

An upper surface FS of the strengthened glass substrate BS is exposed to the outside of the electronic device EA, and defines an upper surface FS of the window CW and an upper surface of the electronic device EA. A lower surface RS of the strengthened glass substrate BS faces the upper surface FS in a direction of the third directional axis DR3

The printing layer BZ may be disposed on the lower surface RS of the strengthened glass substrate BS to define the bezel area BZA. The printing layer BZ may have a lower light transmittance than the strengthened glass substrate BS. For example, the printing layer BZ may have a predetermined color. Accordingly, the printing layer BZ may selectively transmit/reflect only light of a specific color. Alternatively, for example, the printing layer BZ may be a light blocking layer absorbing incident light. The light transmittance and color of tine printing layer BZ may be variously provided according to types and designs of the electronic device EA.

The printing layer BZ may be formed on the lower surface RS of the strengthened glass substrate BS through printing or deposition. In this case, the printing layer BZ may be directly formed on the lower surface RS of tie strengthened glass substrate BS. Alternatively, the printing layer BZ may be bonded to the lower surface RS of the strengthened glass substrate BS through a separate adhesive member, etc. In this case, the adhesive member may contact the lower surface RS of the strengthened glass substrate BS.

FIG. 4 is a flowchart of a method for manufacturing a window according to an embodiment. The method for manufacturing a window according to an embodiment may include a step S100 of providing a base glass and a step S300 of strengthening the base substrate with providing a mixed melt to the base glass.

In the method for manufacturing a window according to an embodiment, the base glass provided in the step S100 of providing a base glass may be manufactured through a float process. In addition, the provided base glass may be manufactured through a down draw process method or a fusion process method. However, the embodiment is not necessarily limited thereto, and the provided base glass may be manufactured through various methods which are not illustrated as an example.

The base glass provided in the step S100 of providing a base glass may be cut before the strengthening step S300 for intended use. However, the embodiment is not necessarily limited thereto, and the provided base glass may be provided in a size that is not consistent with a size of a finally applied product, and then processed by being cut to a size applied to a final product after the window manufacturing process of an embodiment.

The base glass may be flat. In addition, the base glass may be bent. For example, the base glass cut and provided based on the size of the finally applied product may be bent convex or concave with respect to a central portion. Alternatively, the base glass may include a portion bent in an outer portion. However, the embodiment is not necessarily limited thereto, and the base glass may be provided in various shapes.

The base glass provided in the step S100 of providing a base glass may include SiO₂ and Al₂O₃. In addition, in an embodiment, the base glass may contain SiO₂, Al₂O₃, and Li₂O₃. For example, the base glass may contain SiO₂ in an amount of 50 wt % to 80 wt %, Al₂O₃ in an amount of 10 wt % to 30 wt %, and Li₂O₃ in an amount of 3 wt % to 20 wt %.

In an embodiment, the base glass may contain SiO₂, Al₂O₃, Li₂O₃, and P₂O₅. In addition, in an embodiment, the base glass may contain SiO₂, Al₂O₃, and P₂O₅, and might not contain Li₂O₃. Meanwhile, the base glass may further include at least one of Na₂O, K₂O, MgO, and CaO in addition to SiO₂, Al₂O₃, Li₂O₃, and P₂O₅.

The strengthening step S300 may be a step of chemically strengthening the base glass with providing a mixed melt to the base glass. For example, the strengthening step S300 may be a step of immersing the base glass in the mixed melt to strengthen a surface of the base glass through an ion exchange method. The mixed melt provided to the base glass may include a strengthening molten salt and an additive. The additive may be different from the strengthening molten salt.

The strengthening step S300 through the ion exchange method may be performed by exchanging alkali metal ions having a relatively smaller ionic radius on the surface of the base glass for alkali metal ions having a larger ionic radius. For example, surface strengthening may be achieved by exchanging ions such as Li⁺ or Na⁺ on the surface of the base glass for ions such as Na⁺ or K⁺ provided from the strengthening molten salt; respectively The window manufactured through the strengthening step S300 may include a compressive stress layer CSL (FIG. 9) on the surface thereof. The compressive stress layer CSL (FIG. 9) may be formed on at least one of the upper surface FS and the lower surface RS of the window CW.

The strengthening molten salt provided as a mixed melt in the strengthening step S300 may be a mixed salt or a single salt. The mixed salt may be a molten salt containing at least two ions selected from the group consisting of Li⁺, Na⁺, K⁺, Rb⁺ and Cs⁺. In addition, the single salt may be a molten salt containing any one ion selected from the group consisting of Li⁺, Na⁺, K⁺, Rb⁺, and Cs⁺. For example, the strengthening step of the method for manufacturing a window according to an embodiment may include a molten salt of KNO₃ and NaNO₃ as a mixed salt, and a molten salt of KNO₃ as a single salt.

The additive included in the mixed melt may contain at least one of Al₂(S0₄)₃, Al(NO₃)₃, K₂SiO₃, Na₂SiO₃, KCl, Ca(NO₃)₂, and Mg(NO₃)₂. For example, the additive may be at least any one selected from Al₂(SO₄)₃, Al(NO₃)₃, K₂SiO₃, Na₂SiO₃, KCl, Ca(NO₃)₂, and Mg(NO₃)₂. For example, in an embodiment, the mixed melt may contain Al₂(SO₄)₃ or Al(NO₃)₃ as an additive.

The additive may be provided together with the strengthening molten salt in the strengthening step S300. The additive may be contained in an amount of greater than 0 wt % to 10 wt % with respect to a total weight of the mixed melt containing the additive and the strengthening molten salt. In the strengthening step S300,. the surface durability of the window may be increased by including an additive in an amount of greater than 0 wt % in the mixed melt. For example, when the additive is added in the strengthening step, damage to the window surface caused in the surface strengthening step using the strengthening molten salt may be minimized. In addition, when the additive is included in the mixed melt in an amount of greater than 10 wt % in the strengthening step S300, ion exchanges between the ions of the strengthening molten salt and the ions on the surface of the base glass may be reduced, thereby deteriorating strengthening properties.

The strengthening step S300 maybe performed by providing the mixed melt to the base glass at high temperature. FIG. 5 schematically shows a strengthening step S300 of providing a mixed melt to strengthen a base glass in the method for manufacturing a window according to an embodiment.

In FIG. 5, a strengthening treatment unit HU in which the strengthening step S300 is performed is illustrated as an example. The strengthening treatment unit HU of FIG. 5 is schematically illustrated to describe the strengthening step S300, and the form of the strengthening treatment unit HU is not necessarily limited to the one shown in FIG 5.

Referring to FIG. 5, the strengthening step S300 may be performed by immersing a base glass BG in a mixed melt ML in the strengthening treatment unit HU. In this case, the mixed melt ML may contain at least one oi the strengthening molten salt and the additives described above.

In the illustration of FIG. 5, the strengthening treatment unit HU may include a tank HT containing the molten mixed melt ML, a heating part HP disposed surrounding die tank HT and applying heat to the mixed melt ML in the tank HT, a driving part HD fixing the base glass BG and vertically moving the base glass BG to immerse the provided base glass BG in the mixed melt ML, and a control part HC controlling the operation of the strengthening treatment unit HU. The control pan HC may control the temperature of the mixed melt ML contained in the tank HT. For example, the central part HC may control the heating pan HP to heat the mixed melt ML at a predetermined temperature and keep the temperature of the mixed melt ML at the heated temperature. For example, the heating part HP may serve to provide heat to heat the mixed melt ML, or serve as a heat insulator to keep the temperature of the healed mixed melt ML. The base glass BG may be disposed to be entirely immersed in the mixed melt ML.

Meanwhile, in FIG. 5, only two pieces of base glass BG fixed to the driving part HD and processed in the mixed melt ML are illustrated, but this is presented as an example and the embodiment is not necessarily limited thereto. The base glass BG processed in the mixed melt ML may be one or a plurality of pieces.

The step S300 of strengthening a base glass may be performed as one strengthening step. In addition, unlike the one above, the strengthening step S300 may be divided into a plurality of steps, and the strengthening step S300 of chemically strengthening a base glass may be performed as a multi-stage strengthening step.

Meanwhile, when the strengthening step S300 is performed as a multi-stage strengthening step, configurations of the strengthening molten salts used in each strengthening step may be different. However, the embodiment is not necessarily limited thereto, and the configurations of the strengthening molten silts used in each strengthening step may lie die same or may be different in configurations of some molten salts.

FIG. 6 schematically shows a case in which the strengthening step S300 of strengthening a base glass is performed as a multi-stage strengthening step. Referring to FIG. 6, the strengthening step S300 may include a first strengthening step S310 and a second strengthening step S320 that are sequentially performed.

When the strengthening step S300 is performed as a multi-stage strengthening step, the first strengthening step S310 may be a step of strengthening the base glass with providing a strengthening molten salt and an additive to the base glass. In addition, the second strengthening step S320 may be a step of strengthening the base glass with providing a strengthening molten salt without an additive to strengthen the base glass.

The first strengthening step S310 may be a step of providing a mixed melt containing a first strengthening molten salt and an additive to the base glass to strengthen the base glass, and for example, the first strengthening molten salt may contain KNO₃ and NaNO₃. The second strengthening step S320 is performed after the first strengthening step S310, and may be a step of providing a melt containing the second strengthening molten salt without an additive to the base glass strengthened in the first strengthening step to further strengthen the base glass. For example, the second strengthening molten salt may contain KNO₃ and might not contain NaNO₃. The first strengthening molten salt and the second strengthening molten salt may be different from each other, or when the first strengthening molten salt and the second strengthening molten salt include a plurality of molten salts, at least some of the molten salts may be the same.

When the strengthening step S300 is performed as a multi-stage strengthening step, the first strengthening step S310 may be performed at a first temperature and tire second strengthening step S320 may be performed at a second temperature. For example, the strengthening step S300 may include the first strengthening step S310 of performing an ion exchange treatment at the first temperature and the second strengthening step S320 of performing an ion exchange treatment at the second temperature. The first temperature may be 380° C. to 440° C., and the second temperature may be 380° C. to 410° C. For example, the first strengthening step S310 may be performed at the first temperature of 380° C. to 440° C. for 2 to 5 hours, and the second strengthening step S320 may be performed at the second temperature of 380° C. to 410° C. for 30 minutes to 2 hours.

Meanwhile, in the method for manufacturing a window according to an embodiment, the second temperature of the second strengthening step S320 may be equal to or lower than the first temperature of the first strengthening step S310. For example, when the base glass provided in the method for manufacturing a window according to an embodiment contains SiO₂, Al₂O₃, and Li₂O₃, the first strengthening step S310 may be performed at 420° C. for 2 hours, and then the second strengthening step S320 may be performed at 390° C. for 45 minutes.

FIG. 7 is a flowchart of a method for manufacturing a window according to an embodiment. The method for manufacturing a window according to an embodiment may include a step S100 of providing a base glass and a step S300 of strengthening the base glass, and a step S500 of forming a printing layer or the strengthened base glass.

The printed layer formed in the step S500 of forming a printing layer may be provided on at least one of the upper and lover surfaces of the strengthened base glass. The printing layer may be a printing layer BZ providing the bezel area BZA described in FIG. 3. In the step S500 of forming a printing layer, the printing layer BZ may be, for example, provided on the lower surface RS (FIG. 3) of the strengthened glass substrate BS (FIG. 3), which is a strengthened base glass.

FIG. 8 is a block diagram schematically showing a method for manufacturing a window according to an embodiment. In FIG. 8, each unit performing the step S100 of providing a base glass BG, the strengthening step S300 of strengthening the provided base glass BG, and the printing layer forming step S500 of forming a printing layer on the strengthened glass substrate BS, which correspond to each step in the flowchart of FIG. 7 is indicated as a block. The base glass BG is provided to a strengthening treatment unit, and the strengthened glass substrate BS after chemically strengthened in the strengthening treatment unit is transferred to a printing unit. After a printing layer is formed in the printing unit, a window CW including the strengthened glass substrate BS and the printing layer BZ may be provided in the end.

Meanwhile, although not shown in the drawing, between the strengthening step S300 and the printing layer forming step S500, a cooling step of cooling the strengthened glass substrate BS, a cleaning step of cleaning the strengthened glass substrate BS, etc. may be further included, and accordingly, a cooling unit, a cleaning unit, etc. may be further included between the strengthening treatment unit and the printing unit.

FIG. 9 is a cross-sectional view showing a portion of a window manufactured using the method for manufacturing a window according to an embodiment. FIG. 9 may be a cross-sectional view showing the area AA of FIG. 3. The compressive stress layer CSL may be formed on a surface of a window manufactured using the method for manufacturing a window according to an embodiment. The compressive stress layer CSL may be defined as a layer from the upper surface FS or the lower surface RS of the window to a point at which a compressive stress CS value becomes zero.

Meanwhile, the window manufactured using the method for manufacturing a window according to an embodiment may include the compressive stress layer CSL formed adjacent to the upper surface FS and the lover surface RS, and the surface of the window defining the upper surface FS and the lower surface RS may be provided without damage even after the strengthening step S300.

For example, the method for manufacturing a window according to an embodiment includes an additive together with a strengthening molten salt in the strengthening step to strengthen the base glass, thereby minimizing a decrease in the compressive stress values of the compressive stress layer on the window surface to provide a window having increased surface durability. For example, the window manufactured using the method for manufacturing a window according to an embodiment includes an additive in the strengthening step to strengthen the base glass, thereby minimizing defects on the surface of the manufactured window or voids that may be formed due to vacancies of ions escaping from the inside of the base glass during the strengthening step to exhibit excellent chemical resistance and increased surface strength as well.

In addition, in the method for manufacturing a window according to an embodiment, when the base glass is strengthened by including additives in the strengthening step, defects on the window surface may be minimized, and a uniform window surface may thus be provided even when a separate post-processing process tor improving window surface properties is skipped. In addition, accordingly, when a priming layer is formed on the window surface, the priming quality of the printing layer may be well kept.

FIG. 10 is a flowchart showing a conventional method for manufacturing a window. The conventional method for manufacturing a window may include a step S100′ of providing a base glass, a step S300′ of strengthening the base glass, a step S400′ of performing a polishing treatment, and a step S500′ of forming a printing layer. For example, the conventional method for manufacturing a window is different from the steps of the method for manufacturing a window according to an embodiment in that the conventional method further includes the polishing treatment step S400′ after the strengthening step S300′.

Meanwhile, in the conventional method for manufacturing a window, the step S300′ of strengthening the base glass may be a step of providing a strengthening molten salt to the base glass to chemically strengthen the base glass. For example, in the step S300′ of strengthening the base glass according to the conventional method for manufacturing a window, there is a difference in that when tbe base glass is chemically strengthened using a strengthening molten salt, the additives suggested in die method for manufacturing a window according to an embodiment are not included.

Hereinafter. FIGS. 11 and 12a to 12f are graphs showing results of chemical resistance evaluation for manufactured windows. FIG. 11 shows results of chemical resistance evaluation for a window manufactured using the conventional method for manufacturing a window, and FIGS. 12a to 12f show results of chemical resistance evaluation for Example windows manufactured using the method for manufacturing a window according to an embodiment. FIG. 12a is a case of a strengthening treatment including Al₂(SO₄)₃ as an additive, FIGS. 12b, 12c, 12d, 12e, and 12f slow results of chemical resistance evaluation for windows strengthened by including Al(NO₃)₃, K₂SiO₃, Ca(NO₃)₂, KCl, and Mg(NO₃)₂ as an additive, respectively. In the windows manufactured for the results of chemical resistance evaluation shown in FIGS. 12a to 12f, the additives were contained in an amount of 6 wt % in the mixed melt provided to the base glass.

In FIGS. 11 and 12a to 12f, “REF” is a graph showing transmittance values for each wavelength of windows before acid treatment after being manufactured. In addition, In FIGS. 11 and 12a to 12f, “EXP1” indicates transmittance values for each wavelength after acid treatment by immersing the manufactured windows in a nitric acid (HNO₃) solution having a pH of 1 or less at 50 for 2 minutes, and “EXP2” indicates transmittance values for each wavelength after acid treatment by immersing the manufactured windows in a nitric acid (HNO₃) solution a pH of 1 or less at 60 for 2 minutes. Meanwhile, in some graphs, the transmittance graphs indicated by “REF”, “EXP1”, and “EXP2” overlap each other, and this suggests that a difference in transmittance is minute or similar to the conditions displayed by the overlapping graphs.

Meanwhile, in the windows manufactured for evaluation shown in FIGS. 11 and 12a to 12f, the strengthening step was performed as a multi-stage strengthening step. The first strengthening step included KNO₃ and NaNO₃, as a strengthening molten salt and was performed at 420° C. for 2 hours, and the second strengthening step included KNO₃ as a strengthening molten salt and was performed at 390+ C. for 45 minutes. In the window showing the evaluation results in FIG. 11, additives were not included in the strengthening step, and in the windows showing the evaluation results in FIGS. 12a to 12f, additives each were included in the first strengthening step.

Referring to FIG. 11, when a window is manufactured using the conventional method for manufacturing a window, it is seen that the window transmittance after the acid treatment increased compared to the window transmittance before the acid treatment. This is believed to be due to an increase in the window transmittance when some chemical components were eluted from the window surface during the chemical resistance evaluation called acid treatment, indicating that the physical properties of the window surface changed after the acid treatment.

Referring to FIGS. 12a to 12f, when a window was manufactured using the method for manufacturing a window according to an embodiment, even after the acid treatment, there was little change in transmittance, or the change in transmittance was smaller than that of the window manufactured using the conventional method for manufacturing a window. This is believed to be due to an increase in chemical durability of the window surface when the strengthening treatment is performed by including an additive together with the strengthening molten salt in the strengthening step.

Meanwhile, in FIGS. 12a to 12c, given that there is little change in transmittance before and after the acid treatment, it is seen that the strengthened window has excellent chemical resistance. For example, it is seen that when the base glass is strengthened by including Al₂(SO₄)₃, Al(NO₃)₃, or K₂SiO₃ as an additive together with the strengthening molten salt during the strengthening step in the method for manufacturing a window according to an embodiment, good surface compressive stress values and excellent surface chemical resistance are shown.

FIG. 13 is a perspective view illustrating a window CW-a manufactured using the method for manufacturing a window according to an embodiment of the present invention. FIGS. 14a and 14b are perspective vie vs illustrating windows CW-b1 and CW-b2 manufactured using the method for manufacturing a window according to an embodiment of the present invention. Hereinafter, in the description of the window described with reference to FIGS. 13 and 14a to 14b, differences will be mainly described except for the description overlapping the one described in FIGS. 1 to 10.

As illustrated in FIG 13, the window CW-a may include a bending portion BA bent around a bending axis BX. In an embodiment, the window CW-a may include a flat portion FA and a bending portion BA.

In an embodiment, the bending axis BX may extend along the second directional axis DR2 and may be provided on a rear surface of the window CW-a. The flat portion FA may be a portion parallel to a plane defined by the first and second directional axes DR1 and DR2. The bending portion BA may be a curved portion adjacent to the flat portion FA and having a curved shape. For example, referring to FIG. 13, the bending portion BA is a portion adjacent to both sides of the flat portion FA, and may be a portion bent downwards from the flat portion FA. However, the embodiment is not necessarily limited thereto, and the bending portion BA may be disposed adjacent to only one side of the flat portion FA, or may be disposed adjacent to all four sides of the flat portion FA on a plane.

The window CW-a according to an embodiment includes a base glass strengthened in a mixed melt containing an additive together with a strengthening molten salt, and has good surface compressive stress values and excellent surface chemical resistance without a separate post-processing step after the strengthening step.

In addition, the windows CW-b1 and CW-b2 manufactured the method for manufacturing a window according to an embodiment may be folded or unfolded around a folding axis FX as illustrated in FIGS. 14a and 14b. For ease of description, the window CW-b1 in an unfolded state is shown in FIG. 14a and the window CW-b2 in a folded state is shown in FIG 14b.

The folding axis FX may extend along the first directional axis DR1 and may be defined on an upper surface FS of the window CW-b1. For example, in FIGS. 14a to 14b, an in-folding window in which a lower surface RS of the window CW-b2 is exposed to the outside when being folded is illustrated, but the embodiment is not necessarily limited thereto. For example, the window according to an embodiment may be a window in which the folding axis FX is defined below the lower surface RS of the window CW-b1 and is out-folded unlike the one shown in FIGS. 14a and 14b. Meanwhile, the windows CW-b1 and CW-b2 that are modifiable in shape during use may also be manufactured using the method for manufacturing a window according to an embodiment, and go through the strengthening step S300 by including an additive together with the strengthening molten salt in the strengthening step to have good surface compressive stress values and excellent surface chemical resistance without a separate post-processing step after the strengthening step.

The window CW-a having the bending portion BA manufactured using the method for manufacturing a window according to an embodiment or the windows CW-b1 and CW-b2 that are modifiable in shape may exhibit good surface compressive stress values and excellent durability even without the polishing treatment step after the strengthening step, and may thus be applied to various electronic devices.

The method for manufacturing a window according to an embodiment may provide excellent surface chemical resistance and good surface compressive stress characteristics by strengthening a base glass using a mixed melt containing an additive together with a strengthening molten salt in tie strengthening step. In addition, the method for manufacturing a window according to an embodiment provides good surface compressive stress characteristics and excellent surface durability even without the polishing treatment step provided after the strengthening step in order to remove surface defects of the strengthened glass substrate, thereby showing increased processability. In addition, the method for manufacturing a window according to an embodiment provides good surface characteristics by strengthening the base glass using a mixed melt containing an additive together with a strengthening molten salt in the strengthening step, and provides enhanced printing quality provided on the surface of the strengthened base glass and increased durability of a printed layer to the surface of the base glass.

Although the present invention has been described with reference to a preferred embodiment of the present invention, it will be understood that the present invention should not be limited to these preferred embodiments but various changes and modifications can be made by those skilled in the art without departing from the spirit and scope of the present invention.

Claims

1. A method for manufacturing a window, the method comprising the steps of: providing a base glass; andexposing the base glass to a mixed melt comprising a strengthening molten salt and an additive,wherein the additive comprises Al2(SO4)3, Al(NO3)3, K2SiO3, Na2SiO3, KCl, Ca(NO3)2, and/or Mg(NO3)2.

2. The method of claim 1, wherein the additive is included in the mixed melt an amount of 0 wt % to 10 wt % with respect to a total weight of the mixed melt.

3. The method of claim 1, wherein the additive is Al2(SO4)3 or Al(NO3)3.

4. The method of claim 1, wherein the base glass comprises SiO2, Al2O3, and Li2O3.

5. The method of claim 4, wherein the base glass further comprises P2O5.

6. The method of claim 4, wherein the base glass comprises: SiO2 in an amount of 50 wt % to 80 wt %;Al2O3 in an amount of 10 wt % to 30 wt %; andLi2O3 in an amount of 3 wt % to 20 wt %.

7. The method of claim 1, wherein the base glass comprises SiO2, Al2O3, and P2O5.

8. The method of claim 1, wherein the strengthening molten salt is a mixed salt comprising two or more ions selected from the group consisting of Li+, Na+, K+, Rb+ and Cs+, or a single salt containing any one ion selected from the group consisting of Li+, Na+, K+, Rb+ and Cs+.

9. The method of claim 1, wherein the step of exposing the base glass to the mixed melt comprises: exposing the base glass to a first strengthening molten salt and the additive to strengthen the base glass; andexposing the base glass to a second strengthening molten salt, without exposing the base glass to the additive, to further strengthen the base glass.

10. The method of claim 9, wherein: exposing the base glass to the first strengthening molten salt and the additive is performed at a first temperature; andexposing the base glass to the second strengthening molten salt, without exposing the base glass to the additive, is performed at a second temperature that is lower than the first temperature.

11. The method of claim 9, wherein: exposing the base glass to the first strengthening molten salt and the additive is performed at a temperature within a range of 380° C. to 440° C.; andexposing the base glass to the second strengthening molten salt, without exposing the base glass to the additive, is performed at a temperature within a range of 380° C. to 410° C.

12. The method of claim 9, wherein: the first strengthening molten salt comprises KNO3 and NaNO3; andthe second strengthening molten salt comprises KNO3.

13. The method of claim 1, further comprising a step of forming a printing layer on an upper surface of the base glass and/or a lower surface of the base glass after having exposed the base glass to the mixed melt.

14. A method for manufacturing a window, the method comprising: providing a base glass comprising SiO2, Al2O3, and Li2O3; andexposing the base glass to a mixed melt comprising a strengthening molten salt and an additive,wherein the strengthening molten salt is a mixed salt containing two or more ions selected from the group consisting of Li+, Na+, K+, Rb+ and Cs+ or a single salt containing any one ion selected from the group consisting of Li+, Na+, K+, Rb+ and Cs+, andwherein the additive includes Al2(SO4)3, Al(NO3)3, K2SiO3, Na2SiO3, KCl, Ca(NO3)2, and/or Mg(NO3)2.

15. The method of claim 14, wherein: the strengthening molten salt comprises KNO3 and/or NaNO3; andthe additive comprises Al2(SO4)3 or Al(NO3)3.

16. The method of claim 14, wherein the additive is included in the mixed melt an amount of 0 wt % to 10 wt % with respect to a total weight of the mixed melt.

17. A method for manufacturing a window, the method comprising: providing a base glass;exposing the base glass to a mixed melt comprising a first strengthening molten salt and an additive; andexposing the base glass, that has been exposed to the mixed melt, to a melt comprising a second strengthening molten salt.wherein the additive comprises Al2(SO4)3, Al(NO3)3, K2SiO3, Na2SiO3, KCl, Ca(NO3)2, and/or Mg(NCO3).

18. The method of claim 17, wherein the base glass comprises SiO3, Al2O3, and Li2O3.

19. The method of claim 17, wherein the mixed melt comprises Al2(SO4)3 and Al(NO3)3, and/or NaNO3; andthe melt comprises KNO3.

20. The method of claim 17, further comprising forming a printing layer on an upper surface of the base glass and/or a lower surface of the base glass after the base glass has been exposed to the melt, wherein, the base glass is not polished after having exposed the base glass to the melt and before forming the printing layer.