Patent Application
20200148548
The present application is a continuation of PCT application No. PCT/CN2018/117565, filed on Nov. 27, 2018, which designates United States and claims priority of China Patent Application No. 201711266886.4, filed on Dec. 5, 2017 which is incorporated herein by reference.
The invention relates to the technical field of compound preparation, in particular to a method for preparing copper-nickel cobaltate nanowires and application thereof as a catalyst for ammonia borane hydrolysis to produce hydrogen.
Nickel cobaltate (NiCo2O4) is a composite oxide with an inverse spinel structure. In recent years, various methods have been used to control the synthesis of NiCo2O4 materials having good morphology, which can be divided into physical and chemical methods. The physical method mainly includes a low-temperature crushing method, an ultrasonic crushing method, a shock wave crushing method and the like. However, the nickel cobaltate prepared by the physical method is impure and easy to have impurities. At present, the chemical method is a main method for preparing nickel cobaltate, and includes a coprecipitation method, a template method, a sol-gel method, an electrodeposition method, a hydrothermal method and a low-temperature solid phase method. The sol-gel method is wherein a metal inorganic compound is prepared into a precursor after being subjected to solution, sol, gel and curing treatment, and then the precursor is thermally treated into an oxide or other compound solid. However, it has a longer gelation process and a longer period of synthesis process, resulting in a higher production cost. Electrochemical deposition is an electrochemical method for preparing metal and its ionic films with different densities directly from aqueous solution in the experimental process. However, a large amount of electric energy needs to be consumed in the production process thereof, so that the production cost thereof is expensive, and the application thereof in industry is hindered. The low-temperature solid phase method is wherein a metal salt or a metal oxide is fully mixed and ground according to a certain proportion, then the metal salt or the metal oxide is calcined to generate a solid-phase reaction, and finally the product is obtained through grinding, so that a chemical reaction occurs on the premise of not using any solvent. However, it causes impurities mixing and structural defects caused by subsequent processing such as grinding. The coprecipitation method and the hydrothermal synthesis method can be used for preparing precursor powder in the solution, with low cost, fine and uniform product powder particles, and good morphology, which are very suitable for industrialization. Nanowire arrays, nanoplatelets, and sea urchins, graded flower shape and other morphology of nickel cobaltate have been reported.
The Chinese Patent Application 201310594484.2 (Pub. No. 103594246A, Pub. Date Feb. 19, 2014) proposes a preparation method of a porous NiCo2O4 nanowire array supercapacitor electrode material: dissolving nickel(II) nitrate hexahydrate Ni(NO3)2·6H2O, cobalt(II) nitrate hexahydrate Co(NO3)2·6H2O and urea in water, then putting the cleaned foamed nickel into the solution, carrying out hydrothermal reaction for 3-18 h at 90-180° C., cooling to room temperature, taking out the foamed nickel, then carrying out ultrasonic washing, drying and calcining. The prepared porous NiCo2O4 nanowire array has good electrochemical stability, but the method is directly grown on a foamed nickel current collector, which is not favorable for large-scale production.
The Chinese Patent 201510204162.1 (Pub. No. 104867680A, Pub. Date Aug. 26, 2015) proposes an NiCo2O4@NiCo2O4 nano material used as a supercapacitor electrode and a preparation method thereof: a core structure NiCo2O4 nanowire is prepared by a hydrothermal reaction method, a shell structure NiCo2O4 nanowire is further prepared by an electrochemical deposition method on the nanowire, and finally a NiCo2O4@NiCo2O4 nanowire with a homogeneous core-shell structure is obtained. The invention effectively improves the specific surface area and space utilization of the electrode, and increases the specific capacitance of the electrode material, but it is obvious that the process is complicated and energy-consuming. Therefore, it is the problem to be solved by the present invention to develop a method for industrially producing a cobaltate composite with controllable morphology, low cost and excellent product performance.
The present invention aims to provide a preparation method for synthesizing CuxNi1-xCo2O4 nanowires by using a simple and mild hydrothermal method under the condition that a template is not used, aiming at saving energy, being economical, simple, convenient, capable of being scaled and the like.
In order to solve the above technical problem, the invention provides a method for preparing copper-nickel cobaltate nanowires comprising the steps of:
Preferably, a mixed salt solution A with a molar ratio 2:1 of Co2+/(Ni2+, Cu2+) is prepared in the step (1).
Preferably, the soluble nickel salt in the step (1) is selected from one of nickel chloride hexahydrate, nickel sulfate heptahydrate, nickel(II) nitrate hexahydrate, nickel chloride, nickel sulfate and nickel nitrate.
Preferably, the soluble cobalt salt in the step (1) is selected from one of cobalt acetate tetrahydrate, cobalt chloride, cobalt sulfate, cobalt nitrate, cobalt chloride hexahydrate, cobalt sulfate heptahydrate, and cobalt(II) nitrate hexahydrate.
Preferably, the soluble copper salt is selected from one of copper chloride dihydrate, copper sulfate pentahydrate and copper nitrate.
The invention also discloses an application of the copper-nickel cobaltate nanowire prepared by the method as a catalyst for ammonia borane hydrolysis to produce hydrogen.
In summary, the preparation method has the following beneficial effects. 1) According to a hydrothermal synthesis method of the invention, the raw materials are firstly mixed according to a certain proportion, hexamethylenetetramine is used as a precipitant to generate a multi-element metal hydroxide, and then the multi-element metal hydroxide is calcined to synthesize the cobaltate. The process effectively realizes a nickel-cobalt-copper ratio set in the raw materials, and it is simple to operate, environmentally friendly, good in experimental reproducibility, low in cost, and easy in industrial production, and can produce a composite cobaltate CuxNi1-xCo2O4 with a large scale. 2) The nanowire CuxNi1-xCo2O4 composite cobaltate material prepared by the invention has excellent performance in catalyzing ammonia borane for hydrolysis to produce hydrogen. Especially, Cu0.6Ni0.4Co2O4 has the highest catalytic activity, the TOF value is as high as 119.5 molhydrogen min−1 molcat−1, which is the highest value reported in the current literature. It is expected to realize industrialized preparation of a catalyst for hydrogen production.
The foregoing and other exemplary purposes, aspects and advantages of the present invention will be better understood in principle from the following detailed description of one or more exemplary embodiments of the invention with reference to the drawings, in which:
The invention will now be described in detail through several embodiments with reference to the accompanying drawings.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (2 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 1.2 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 30 min, transferred to a reaction vessel, reacted for 12 h (hours) at 120° C. (Celsius), carried out with suction filtration and washed, and dried under a vacuum oven 40° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 600° C. at a heating rate of 2° C./min, and kept for 2 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O4 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (2 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 0.6 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 30 min, transferred to a reaction vessel, reacted for 12 h at 120° C., carried out with suction filtration and washed, and dried under a vacuum oven 60° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 600° C. at a heating rate of 2° C./min, and kept for 2 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O4 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (4 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 1.2 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 60 min, transferred to a reaction vessel, reacted for 12 h at 120° C., carried out with suction filtration and washed, and dried under a vacuum oven 40° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 600° C. at a heating rate of 2° C./min, and kept for 4 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O4 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (2 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 1.2 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 30 min, transferred to a reaction vessel, reacted for 8 h at 160° C., carried out with suction filtration and washed, and dried under a vacuum oven 40° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 600° C. at a heating rate of 2° C./min, and kept for 2 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O2 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (2 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 1.5 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 30 min, transferred to a reaction vessel, reacted for 20 h at 100° C., carried out with suction filtration and washed, and dried under a vacuum oven 40° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 600° C. at a heating rate of 2° C./min, and kept for 2 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O2 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (2 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 1.2 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 30 min, transferred to a reaction vessel, reacted for 12 h at 120° C., carried out with suction filtration and washed, and dried under a vacuum oven 40° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 800° C. at a heating rate of 2° C./min, and kept for 2 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O2 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
Preparation of a precursor: cobalt acetate (2 mmol), sodium dodecyl sulfate (2 mmol), nickel chloride (x mmol), copper chloride (1-x mmol) were dissolved in 20 mL water (0≤x≤1), and stirred magnetically until dissolved, then 1.2 M hexamethylenetetramine solution (20 mL) was added, and the obtained solution was stirred magnetically for 30 min, transferred to a reaction vessel, reacted for 12 h at 110° C., carried out with suction filtration and washed, and dried under a vacuum oven at 40° C. to obtain a precursor M(OH)2, wherein M is one of nickel, copper and cobalt (i.e. Ni(OH)2, Cu(OH)2 and Co(OH)2).
Preparation of nanowire-shaped CuxNi1-xCo2O4: the dried precursor was uniformly ground in a mortar, placed in a muffle furnace, heated to 350° C. at a heating rate of 2° C./min, and kept for 2 h; and after it was cooled to room temperature, a target product CuxNi1-xCo2O2 was obtained by taking out a sample.
Through measurement, the morphology of the CuxNi1-xCo2O4 obtained in the invention is still a nanowire structure.
The structure and properties of the composite cobaltate prepared according to the present invention are analyzed and tested by taking nanowire Cu0.6Ni0.4Co2O4 as an example.
While the invention has been described in terms of several exemplary embodiments, those skilled on the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims. In addition, it is noted that, the Applicant's intent is to encompass equivalents of all claim elements, even if amended later during prosecution.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201711266886.4 | Dec 2017 | CN | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/CN2018/117565 | Nov 2018 | US |
| Child | 16747233 | US |