Patent Application
20240408579
The present disclosure relates to the field of a high molecular material, in particular to a method for preparing a core-shell hollow structure with self-driving nucleation of a photocatalytic particle.
As a common photocatalytic material for a semiconductor, titanium dioxide is capable of converting optical energy into chemical energy when irradiated with light, so as to decompose an organic material which is poisonous and harmful. In addition, titanium dioxide has such features as high stability, photocorrosion resistance and being non-poisonous, and no secondary pollution is generated during the treatment, so it has attracted more and more attention in such fields as anti-bacteria, deodorization, contamination decomposition, fungicide, algaecide, and air purification. However, the catalytic reaction is essentially a surface contact reaction, i.e., the reaction merely occurs on a surface of the material. Hence, for a catalyst with a limited surface, it is used not only for the catalytic reaction but also for fixing particles, so usually a catalytic effect is significantly adversely affected.
A core-shell structure is a nanoscale ordered assembly structure in which a nanomaterial is wrapped by another nanomaterial through a chemical bond or any other force. It plays a very important role in maintaining a stable function of a catalyst, adjusting physicochemical features of a material, preventing the agglomeration of nanoparticles and controlling the interfacial interaction of the particles, so it may be widely used in photocatalysis, batteries, gas storage and gas separation. However, for a catalytic nanomaterial which is used to cause a chemical reaction to take place depending on its surface, there is an urgent need to provide a scheme for preventing the catalytic activity of a core from being adversely affected when a surface of the core is covered by a shell.
An object of the present disclosure is to at least solve one of the above-mentioned problems in the related art. In the embodiments of the present disclosure, on the basis of a surface/interface principle that a substance with a hydrophobic surface is aerophilic, tetraoctadecyl orthotitanate is used to modify a surface of a market-available titanium dioxide nanosphere particle to be hydrophobic, and the titanium dioxide particle is placed into a system of water and micro-nano bubbles, and then the titanium dioxide particle moves into the micro-nano bubble in a self-driven manner due to a difference in surface tensions. Finally, a silicon dioxide shell is generated at a water-air interface of the micro-nano bubble, so as to obtain a nanoparticles with a photocatalytic core-shell hollow structure between a core and the shell.
To be specific, the present disclosure provides the following technical solutions.
In one aspect, the present disclosure provides in some embodiments a method for preparing a nanoparticle with a core-shell hollow structure, including: mixing an alcoholic solution of titanium dioxide with tetraoctadecyl orthotitanate to obtain a first solution including modified titanium dioxide nanospheres; injecting air into water through a micro-nano bubble generator to obtain a resultant solution, and shearing and smashing the resultant resolution to obtain a second solution including micro-nano bubbles; mixing the second solution with the first solution at a temperature of 35° C. or more, so as to obtain a third solution; adding ammonium hydroxide and a solution of tetraethyl orthosilicate into the third solution, so as to obtain a fourth solution; and separating a precipitate from the fourth solution, and drying and calcining the precipitate, so as to obtain the nanoparticle with the core-shell hollow structure.
In the embodiments of the present disclosure, the method further includes the following technical features.
In a possible embodiment of the present disclosure, the alcoholic solution of titanium dioxide includes 1 to 4 parts by weight of titanium dioxide, and the amount of tetraoctadecyl orthotitanate is 0.1 to 1.5 parts by weight.
In a possible embodiment of the present disclosure, a titanium dioxide particle in the alcoholic solution of titanium dioxide has a diameter of 200 nm to 400 nm.
In a possible embodiment of the present disclosure, the alcoholic solution of titanium dioxide is an ethanol solution of titanium dioxide including 1 to 4 parts by weight of titanium dioxide and 10 to 50 parts by weight of anhydrous ethanol.
In a possible embodiment of the present disclosure, the micro-nano bubble has a diameter of 600 nm to 1000 nm.
In a possible embodiment of the present disclosure, the resultant solution is sheared and smashed for 4 to 9 hours.
In a possible embodiment of the present disclosure, air is injected into water through the micro-nano bubble generator so that air humidity is 5% to 30%.
In a possible embodiment of the present disclosure, the second solution is mixed with the first solution at a temperature of 40° C.
In a possible embodiment of the present disclosure, when the amount of titanium dioxide is 1 to 4 parts by weight, the amount of ammonium hydroxide is 1 to 10 parts by weight, and the amount of the solution of tetraethyl orthosilicate is 2 to 10 parts by weight.
In a possible embodiment of the present disclosure, the precipitate is calcined at a temperature of 400° C. to 500° C. for 1 to 3 hours.
In a possible embodiment of the present disclosure, the precipitate is dried at a temperature of 70° C. to 90° C.
In another aspect, the present disclosure provides in some embodiments a method for preparing a nanoparticle with a core-shell hollow structure, including: mixing an alcoholic solution of titanium dioxide with tetraoctadecyl orthotitanate to obtain a first solution including modified titanium dioxide nanospheres, the alcoholic solution of titanium dioxide including 10 to 50 parts by weight of anhydrous ethanol and 1 to 4 parts by weight of titanium dioxide; injecting air into water through a micro-nano bubble generator to obtain a resultant solution, and shearing and smashing the resultant resolution to obtain a second solution including micro-nano bubbles, the micro-nano bubble having a diameter of 600 nm to 1000 nm; mixing the second solution with the first solution at a temperature of 40° C., so as to obtain a third solution; adding 1 to 10 parts by weight of ammonium hydroxide and 2 to 10 parts by weight of a solution of tetraethyl orthosilicate into the third solution, so as to obtain a fourth solution; and separating a precipitate from the fourth solution, and drying and calcining the precipitate, so as to obtain the nanoparticle with the core-shell hollow structure.
In yet another aspect, the present disclosure provides in some embodiments a nanoparticle with a core-shell hollow structure prepared through the above-mentioned method.
The present disclosure has the following beneficial effects. According to the method in the embodiments of the present disclosure, the nanoparticle with the photocatalytic core-shell hollow structure is obtained, so it is able to improve the catalytic activity through increasing a surface for the catalytic reaction, and meanwhile save raw materials. In addition, the preparation of the nanoparticle is relatively simple and easily controlled for large-scale production.
The present disclosure will be described hereinafter with reference to the drawings. It should be appreciated that, the following embodiments are for illustrative purposes only, but shall not be used to limit the scope of the present disclosure.
A micro-nano bubble is a special gaseous state on an interface between a gas and a liquid, and it may exist stably for a long time period in the liquid, so it is used as a non-contact preparation template for a catalyst. The micro-nano bubble is obtained through a market-available micro-nano bubble generator. For example, the market-available micro-nano bubble generator is a high-shear generator. Usually, a dynamic or static high-speed shearing device is used to smash a gas-liquid mixture to obtain the micro-nano bubble.
In the embodiments of the present disclosure, on the basis of a surface/interface principle that a substance with a hydrophobic surface is aerophilic, a titanium dioxide particle whose surface is modified to be hydrophobic is placed into a system of water and micro-nano bubbles, and then the titanium dioxide particle moves into the micro-nano bubble in a self-driven manner due to a difference in surface tensions. Finally, a silicon dioxide shell is generated at a water-air interface of the micro-nano bubble, so as to obtain a nanoparticle with a photocatalytic core-shell hollow structure between a core and the shell.
The present disclosure provides in some embodiments a method for preparing a nanoparticle with a core-shell hollow structure, which includes: (1) mixing an alcoholic solution of titanium dioxide with tetraoctadecyl orthotitanate to obtain a first solution including modified titanium dioxide nanospheres; (2) injecting air into water through a micro-nano bubble generator to obtain a resultant solution, and shearing and smashing the resultant resolution to obtain a second solution including micro-nano bubbles; (3) mixing the second solution with the first solution at a temperature of 35° C. or more, so as to obtain a third solution; (4) adding ammonium hydroxide and a solution of tetraethyl orthosilicate into the third solution, so as to obtain a fourth solution; and (5) separating a precipitate from the fourth solution, and drying and calcining the precipitate, so as to obtain the nanoparticle with the core-shell hollow structure.
An order of Steps (1) and (2) will not be particularly defined herein.
In a possible embodiment of the present disclosure, in Step (1), the alcoholic solution of titanium dioxide includes 1 to 4 parts by weight of titanium dioxide, and the amount of tetraoctadecyl orthotitanate is 0.1 to 1.5 parts by weight. Tetraoctadecyl orthotitanate at an appropriate content is used to modify a surface to be hydrophobic, so as to obtain the modified titanium dioxide nanospheres.
In a possible embodiment of the present disclosure, in Step (1), a titanium dioxide particle in the alcoholic solution of titanium dioxide has a diameter of 200 nm to 400 nm.
In a possible embodiment of the present disclosure, in Step (1), the alcoholic solution of titanium dioxide is an ethanol solution of titanium dioxide including 1 to 4 parts by weight of titanium dioxide and 10 to 50 parts by weight of anhydrous ethanol.
In a possible embodiment of the present disclosure, in Step (2), the micro-nano bubble has a diameter of 600 nm to 1000 nm, e.g., 700 nm to 1000 nm, 800 nm to 1000 nm, 900 nm to 1000 nm, or 600 nm to 800 nm. The diameter of the micro-nano bubble may directly affect, to some extent, the performance of the final nanoparticle with the core-shell hollow structure and a size of the space between the core and the shell. When the diameter of the micro-nano bubble is too small, the accommodation of the nanoparticle with the core-shell hollow structure may be adversely affected. When the diameter of the micro-nano bubble is too large, a shell structure of the nanoparticle may be instable.
In a possible embodiment of the present disclosure, the resultant solution is sheared and smashed for 4 to 9 hours.
In a possible embodiment of the present disclosure, in Step (2), air is injected into water through the micro-nano bubble generator so that air humidity is 5% to 30%.
In a possible embodiment of the present disclosure, in Step (3), the second solution is mixed with the first solution at a temperature of 40° C. Along with the volatilization of alcohol, the titanium dioxide nanosphere whose surface is modified into hydrophobic may be provided with a hydrophobic and aerophilic characteristic due to the existence of a surface tension, and then moves into the bubble in a self-driven manner (similar to the removal of impurities through bubbles in water).
Tetraethyl orthosilicate forms silicon dioxide under the effect of ammonium hydroxide. In a possible embodiment of the present disclosure, in Step (4), when the amount of titanium dioxide is 1 to 4 parts by weight, the amount of ammonium hydroxide is 1 to 10 parts by weight, and the amount of the solution of tetraethyl orthosilicate is 2 to 10 parts by weight.
In a possible embodiment of the present disclosure, in Step (5), the precipitate is calcined at a temperature of 400° C. to 500° C. for 1 to 3 hours.
In a possible embodiment of the present disclosure, the precipitate is dried at a temperature of 70° C. to 90° C.
The present disclosure will be described hereinafter in conjunction with the embodiments. The following embodiments are for illustrative purposes only, but shall not be used to limit the scope of the present disclosure. Where no technique or condition is specified, the known technique or condition, or that specified in a product manual, may be applied. Where no manufacturer of a reagent or instrument is specified, the market-available reagent or instrument may be applied.
In this Example, the present disclosure provides a method for preparing a nanoparticle with a core-shell hollow structure, which includes: (1) adding 2 parts by weight of market-available titanium dioxide nanospheres each with a diameter of 200 nm to 400 nm into 30 parts by weight of anhydrous ethanol, and stirring a resultant solution evenly; (2) adding 1 part by weight of tetraoctadecyl orthotitanate into the solution obtained in (1), and stirring a resultant solution for 24 hours, so as to modify a surface of the titanium dioxide nanosphere to be hydrophobic; (3) injecting air into 100 parts by weight of distilled water through a market-available micro-nano bubble generator, and shearing and smashing a resultant solution for 6 hours to obtain micro-nano bubbles each with a diameter of about 800 nm; (4) heating the solution obtained in (3) to 40° C., and rapidly adding 10 parts by weight of the solution obtained in (2) into the solution; (5) adding 5 parts by weight of ammonium hydroxide into the solution obtained in (4), intensely stirring a resultant solution, dripping 5 parts by weight of a solution of tetraethyl orthosilicate, and stirring a resultant solution for 4 hours; and (6) subjecting the solution obtained in (5) to centrifugal treatment to obtain a precipitate, drying the precipitate at a temperature of 80° C. for 12 hours, and calcining the precipitate at a temperature of 400° C. to 500° C. for 1 to 3 hours, so as to obtain the nanoparticle with the core-shell hollow structure.
In addition, XRD data shows that, there is no change in a lattice structure of the titanium dioxide particle in the nanoparticle with the core-shell hollow structure, with parameters of a standard titanium dioxide (anatase) lattice structure, as shown in
In this Example, the present disclosure provides a method for preparing a nanoparticle with a core-shell hollow structure, which includes: (1) adding 4 parts by weight of market-available titanium dioxide nanospheres each with a diameter of 200 nm to 400 nm into 50 parts by weight of anhydrous ethanol, and stirring a resultant solution evenly; (2) adding 1.5 parts by weight of tetraoctadecyl orthotitanate into the solution obtained in (1), and stirring a resultant solution for 40 hours, so as to modify a surface of the titanium dioxide nanosphere to be hydrophobic; (3) injecting air into 100 parts by weight of distilled water through a market-available micro-nano bubble generator, and shearing and smashing a resultant solution for 8 hours to obtain micro-nano bubbles each with a diameter of about 1000 nm; (4) heating the solution obtained in (3) to 40° C., and rapidly adding 20 parts by weight of the solution obtained in (2) into the solution; (5) adding 10 parts by weight of ammonium hydroxide into the solution obtained in (4), intensely stirring a resultant solution, dripping 10 parts by weight of a solution of tetraethyl orthosilicate, and stirring a resultant solution for 4 hours; and (6) subjecting the solution obtained in (5) to centrifugal treatment to obtain a precipitate, drying the precipitate at a temperature of 80° C. for 12 hours, and calcining the precipitate at a temperature of 400° C. to 500° C. for 1 to 3 hours, so as to obtain the nanoparticle with the core-shell hollow structure.
The nanoparticle with the core-shell hollow structure prepared in Example 2 exhibits similar characteristics to that in Example 1.
It is found during the experiments that, when the surface of the titanium dioxide nanosphere is modified to be hydrophobic, the hydrophobicity is insufficient in the absence of tetraoctadecyl orthotitanate. At this time, it is impossible to provide the titanium dioxide nanosphere with a hydrophobic and aerophilic characteristic under the effect of the surface tension and move the titanium dioxide nanosphere into the bubble in a self-driven manner, thereby there is no core inside the final silicon dioxide shell, as shown in
It is found through researches that, in the process of generating the silicon dioxide shell at the water-air interface through the reaction of tetraethyl orthosilicate with ammonium hydroxide, it is impossible to form the shell structure due to the too rapid formation of silicon dioxide, as shown in
It is found through researches that, in the process of generating the silicon dioxide shell at the water-air interface through the reaction of tetraethyl orthosilicate with ammonium hydroxide, the self-agglomeration of silicon dioxide occurs due to excessive silicon dioxide when too much tetraethyl orthosilicate is added, and thereby the normal formation of the shell structure may be adversely affected, as shown in
The above embodiments are for illustrative purposes only, but the present disclosure is not limited thereto. Obviously, a person skilled in the art may make further modifications and improvements without departing from the spirit of the present disclosure, and these modifications and improvements shall also fall within the scope of the present disclosure.
This application is a continuation of International Patent Application No. PCT/CN2022/077328 filed on Feb. 22, 2022, designating the United States, now pending. The content of the aforementioned application, including any intervening amendments thereto, is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/CN2022/077328 | Feb 2022 | WO |
| Child | 18808684 | US |