Patent Grant
10730226
The present invention claims priority under 35 U.S.C. 119(a-d) to CN 201711336946.5, filed Dec. 14, 2017.
The present invention relates to a technical field of piezoelectric material to preparation, and more particularly to a method for preparing a pyroelectric polymer film based on a combined process of solution casting and uniaxial stretching.
Poly(vinylidene fluoride) (PVDF) and its copolymers are a class of functional materials with piezoelectric, pyroelectric and ferroelectric properties that are typically prepared as films for being used in a wide variety of devices. It is well known that the dielectric, pyro, and piezoelectric properties of PVDF like polymers depend not only on crystalline phase content, but also on crystallite orientation distribution and particularly on dipole orientation which are determined by the film preparation process and the constituents of the copolymers. The typical polymer film preparation process mainly includes three independent steps: 1) film formation, 2) stretching and 3) poling, in which the film forming process is further subdivided into four methods of a) solution casting, b) solution spilling, c) hot pressing and d) melt extruding. However, no matter which method is used to form the film, the piezoelectric/pyroelectric phase (i.e., β phase) content in the as-formed film is usually low although some exceptions also exist. Thus the as-formed film is usually needed to undergo the stretching process to increase the piezoelectric phase content and crystallite orientation. Nevertheless, dipole orientation in the as-stretched film is still random distributed in the plane perpendicular to the stretching direction thus contributing to a net remanent polarization of zero. Therefore, the stretched film also needs to go through the poling process to improve dipole orientation of the polymer film, thereby increasing the remanent polarization of the film, so as to enhance the piezoelectric, pyroelectric and ferroelectric properties of the material. Please refer to literature {circle around (1)} Effect of drawing on the dielectric properties and polarization of pressed solution cast β-PVDF films, J Mater Sci, 2010, 45: 4206-4215. It reported that the solution casted PVDF film with proper solvent and temperature crystalize to 100% β phase. Subsequently, the β phase is preferentially oriented by uniaxial stretching. However, a poling step can not be avoided before measuring the hysteresis loop.
The conventional stretching process for piezoelectric polymer films is usually as follows: cutting the piezoelectric polymer film (formed by casting, extruding, and so on) into sheets, fixing both ends with clamps, putting on a stretching machine, and then heating the film to an elevated temperature; after the temperature is constant, the film is stretched according to the predetermined stretching speed and stretching length, then the stretching temperature is maintained for a certain time, and finally the film is cooled down to an appropriate temperature under a constant stretching force, so as to obtain the stretched film. In principle, the higher the stretching ratio, the higher the piezoelectric phase content. However, the conventional stretching process can not achieve a stretching ratio higher than 5 since the polymer films used to stretch are fully cured materials. To facilitate the stretching process, the polymer films must be stretched at a higher temperature, whereas the high temperature leads to the degradation of the β phase. Please refer to literature {circle around (2)} Influence of the β-phase content and degree of crystallinity on the piezo and ferroelectric properties of poly(vinylidenefluoride), Smart Mater. Struct., 2010, 19:065010. It reported that it was not possible to stretch the film samples at temperatures lower than 80° C. due to breaking of the samples. And at a higher temperature, the transformation efficiency from α to β phase reduced, thereby reducing the piezoelectric/pyroelectric properties of the film. As a result, the maximum amount of β-phase was obtained by stretching at 80° C. with stretch ratios of 5.
It can be seen from the above that the conventional stretching process is an independent process step among the whole polymer film preparation procedure. The polymer films to be stretched are fully cured films prepared in the previous process (casting, hot pressing and extending), so the stretching ratio is low and the stretched films need to undergo the following poling process for piezoelectric, pyroelectric and ferroelectric applications.
Based on the above analysis, the present invention is directed to the low stretching ratio and the high stretching temperature of the conventional stretching process. Therefore, the present invention provides a method for preparing a pyroelectric polymer film based on a combined process of solution casting and uniaxial stretching, wherein the pyroelectric polymer film is firstly prepared by solution casting, then the casted film is subjected to uniaxial stretching when the film is in a semi-cured state (wet film). Thus a larger stretching ratio at a lower temperature is realized. Without undergoing a further poling process, the as-stretched film does have a fairly good pyroelectric performance. Moreover, the surface of the stretched film is smoother and has fewer surface defects.
Accordingly, in order to accomplish the above objects, the present invention provides a method for preparing a pyroelectric polymer film based on a combined process of solution casting and uniaxial stretching, comprising steps of: preparing a pyroelectric polymer solution using a proper organic solvent, casting the pyroelectric polymer solution into a liquid film, and controlling a casting temperature and a casting time for volatilizing a part of the solvent in the liquid film to form a semi-cured wet film; then stretching the semi-cured wet film and waiting until the stretched film is completely cured, so as to obtain the pyroelectric polymer film.
Preferably, a pyroelectric polymer is a polymer selected from a group consisting of poly(vinylidene fluoride), poly(vinylidene fluoride-trifluoroethylene) polymer, and poly(vinylidene fluoride-hexafluoropropylene).
Preferably, a mass percentage of a pyroelectric polymer in the pyroelectric polymer solution is 10%-35%.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 45-55° C. and the casting time of 0.5-5 h for the pyroelectric polymer solution of N-methyl pyrrolidone.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 45-55° C. and the casting time of 0.25-2.5 h for the pyroelectric polymer solution of N,N-methylformamide.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 55-65° C. and the casting time of 0.5-4 h for the pyroelectric polymer solution of N-methyl pyrrolidone.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 55-65° C. and the casting time of 0.2-2 h for the pyroelectric polymer solution of N,N-methylformamide.
Preferably, a stretching temperature is 20-80° C.
The present invention also provides an apparatus for preparing a pyroelectric polymer film based on a combined process of solution casting and uniaxial stretching, comprising a first plate connected to a temperature control device, wherein a second plate and a third plate are arranged on the top side of the first plate; the second plate is fixed on the first plate, and the third plate is adjacent to the second plate and can be horizontally moved away from the second plate.
Preferably, the third plate is connected to a transmission device, so as to horizontally move away from the second plate.
The present invention also provides a method for preparing a pyroelectric polymer film based on the above apparatus, comprising steps of: casting a pyroelectric polymer solution into a liquid film at a border area across the second plate and the third plate, and controlling a casting temperature and a casting time by the temperature control device for volatilizing a part of the solvent in the liquid film to form a semi-cured wet film; then stretching the semi-cured wet film by moving the third plate, in such a manner that the semi-cured wet film under stretching drops and adheres to a top surface of the first plate by gravity; and adjusting the temperature control device for volatilizing all of the solvent in the stretched film, so as to obtain the pyroelectric polymer film.
Preferably, the third plate is specifically moved by a transmission device connected to the third plate.
Preferably, a pyroelectric polymer is a polymer selected from a group consisting of poly(vinylidene fluoride), poly(vinylidene fluoride-trifluoroethylene) polymer, and poly(vinylidene fluoride-hexafluoropropylene).
Preferably, a mass percentage of a pyroelectric polymer in the pyroelectric polymer solution is 10%-35%.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 45-55° C. and the casting time of 0.5-5 h for the pyroelectric polymer solution of N-methyl pyrrolidone.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 45-55° C. and the casting time of 0.25-2.5 h for the pyroelectric polymer solution of N,N-methylformamide.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 55-65° C. and the casting time of 0.5-4 h for the pyroelectric polymer solution of N-methyl pyrrolidone.
Preferably, controlling the casting temperature and the casting time for volatilizing part of the solvent of the pyroelectric polymer solution to form the semi-cured wet film is specifically executed with the casting temperature of 55-65° C. and the casting time of 0.2-2 h for the pyroelectric polymer solution of N,N-methylformamide.
Preferably, a stretching temperature is 20-80° C.
Compared with the prior art, the beneficial effects of the present invention are as follows.
In the present invention, the solution casted pyroelectric polymer film in the semi-cured state is stretched. Compared with the conventional stretching process using fully cured film, the stretchability of the semi-cured film is much higher. Thus, a higher stretching ratio (>10) can be readily obtained under a lower temperature (even at room temperature). The resistance between the semi-cured pyroelectric polymer molecules is much smaller than that between the fully cured film molecules, thus the pyroelectric polymer molecules under stretching can overcome the intermolecular resistance, so as to achieve the orderly orientation of the piezoelectric crystal phase. In addition, the stretching is carried out at a relative low temperature, so that the orientation of the dipole is not prone to depolarization, guaranteeing that the dipole in the dried film material still maintains the ordered orientation. Therefore, the pyroelectric polymer film prepared by the present invention has the pyroelectric response characteristics even without poling process.
These and other objectives, features, and advantages of the present invention will become apparent from the following detailed description, the accompanying drawings, and the appended claims.
Referring to the drawings, the present invention is further illustrated.
Referring to
A method for preparing the pyroelectric polymer film comprises steps of:
Step A: preparing a pyroelectric polymer solution;
wherein a pyroelectric polymer material and a solvent are properly selected according to actual requirements, and pyroelectric polymer powder or particle is dissolved in the proper solvent and then heated and evenly stirred to obtain the pyroelectric polymer solution;
Step B: establishing an apparatus;
wherein a forming plate 1 is horizontally placed on a temperature-controllable heating plate, a fixed stretching plate 2 is placed at one side of a top surface of the forming plate 1, and then a movable stretching plate 3 is placed beside the fixed stretching plate 2; the movable stretching plate 3 is closely contacted with the fixed stretching plate 2; the movable stretching plate 3 is connected to a stepper motor 6 through a transmission device 5, so as to be horizontally movable on the top surface of the forming plate 1 and away from the fixed stretching plate 2;
Step C: preparing the pyroelectric polymer film, comprising steps of:
casting the pyroelectric polymer solution at a border area across the fixed stretching plate 2 and the movable stretching plate 3, wherein
In order to facilitate a clear and complete understanding of the technical solutions of the present invention, the principle and characteristics of the present invention are described in detail below with reference to specific embodiments.
Dissolving PVDF (polyvinylidene fluoride) powder in an NMP (N-methyl pyrrolidone) solvent with a mass ratio of 25:75, magnetically stirring for 12 h under 70° C. water bath, so as to fully dissolve the PVDF;
A forming plate 1 is horizontally placed on a temperature-controllable heating plate, a fixed stretching plate 2 is placed at one side of a top surface of the forming plate 1, and then a movable stretching plate 3 is placed beside the fixed stretching plate 2; the movable stretching plate 3 is closely contacted with the fixed stretching plate 2; the movable stretching plate 3 is connected to a stepper motor 6 through a transmission device 5; and
Casting the pyroelectric polymer solution at a border area across the fixed stretching plate 2 and the movable stretching plate 3, setting a temperature of the temperature-controllable heating plate to 50° C. to heat the casted film for 4 h, thus volatilizing part of the solvent in the film so as to obtain a semi-cured wet film; stretching the wet film by horizontally moving the movable stretching plate 3 away from the fixed stretching plate 2 with a stretching length of 200 mm and a stretching speed of 400 mm/s controlled by the stepper motor 6 with a programmable servo controller, so as to stretch the film by 20 times and the stretched film forms a layer of even film on the forming plate 1; keeping the temperature of the temperature-controllable heating plate at 50° C. for fully volatilizing the solvent in the PVDF film, so as to complete preparation.
For testing pyroelectric response of the film prepared in the embodiment 1, both faces of the prepared. PVDF film are deposited with aluminum electrodes by vacuum evaporation, then the aluminum electrodes are connected to a signal amplifier through electric leads and the amplified pyroelectric signal is sent to an oscilloscope through a coaxial cable, A testing method comprises steps of:
A pulsed infrared laser is irradiated on the PVDF film prepared in the embodiment 1 to generate an alternating temperature field, adjusting a signal generator to control an output power and an output frequency of the infrared laser to be 20 mw and 1 Hz; thus pyroelectric currents are generated between the top electrode and the bottom electrode due to a temperature change on the surface of the PVDF film; as shown in
Preparing the same NMP solution of PVDF as illustrated in the embodiment 1, casting the solution on a forming plate, and drying at 90° C. for 4 h; then cutting the TWIN film into a rectangle sheet of 2 cm×4 cm; fixing the rectangular sheet on a GGP1204 optical axis ball linear slider (model: EBX1204-100) through a clamp; heating to 80° C. and then stretching by a matched 57-stepper motor with a stretching speed as slow as 0.5 mm/s and eventually reaching a stretching ratio of 5; keeping a stretching force and naturally cooling to a room temperature for completing the preparation process.
Testing a pyroelectric response with the same method as illustrated in the embodiment 1, and no response is detected.
Dissolving P(VDF-TrFE) (polyvinyledenedifluoride-trifluoroethylene) powder in a DMF (N,N-methylformamide) solvent with a mass ratio of 20:80, magnetically stirring for 12 h under 70° C. water bath, so as to fully dissolve the P(VDF-TrFE); and
Establishing the same device as illustrated in the embodiment 1, casting the pyroelectric polymer solution at a border area across the fixed stretching plate 2 and the movable stretching plate 3, setting a temperature of the temperature-controllable heating plate to 55° C. to heat the casted film for 2 h, thus volatilizing part of the solvent in the film so as to obtain a semi-cured wet film; stretching the wet film by horizontally moving the movable stretching plate 3 away from the fixed stretching plate 2 with a stretching length of 150 mm and a stretching speed of 150 mm/s controlled by the stepper motor 6 with a programmable servo controller, so as to stretch the film by 15 times and the stretched film forms a layer of even film on the forming plate 1; keeping the temperature of the temperature-controllable heating plate at 55° C. for fully volatilizing the solvent in the P(VDF-TrFE) film, so as to complete preparation.
Testing pyroelectric response with the same method as illustrated in the embodiment 1, the pyroelectric response read by the oscilloscope has a frequency of 1 Hz.
Dissolving PVDF-HFP (Poly(vinylidene fluoride-co-hexafluoropropylene)) powder in a DMAC, (N,N-dimethylacetamide) solvent with a mass ratio of 35:65, magnetically stirring for 12 h under 70° C.′ water bath, so as to fully dissolve the PVDF-HFP; and
Establishing the same device as illustrated in the embodiment 1, casting the pyroelectric polymer solution at a border area across the fixed stretching plate 2 and the movable stretching plate 3, setting a temperature of the temperature-controllable heating plate to 60° C. to heat the casted film for 2 h, thus volatilizing part of the solvent in the film so as to obtain a semi-cured wet film; stretching the wet film by horizontally moving the movable stretching plate 3 away from the fixed stretching plate 2 with a stretching length of 100 mm and a stretching speed of 50 mm/s controlled by the stepper motor 6 with a programmable servo controller; so as to stretch the film by 10 times and the stretched film forms a layer of even film on the forming plate 1; keeping the temperature of the temperature-controllable heating plate at 60° C. for fully volatilizing the solvent in the PVDF-HFP film; so as to complete preparation.
Testing pyroelectric response with the same method as illustrated in the embodiment 1, the pyroelectric response read by the oscilloscope has a frequency of 1 Hz.
Dissolving PVDF (polyvinylidene fluoride) powder in an NMP (N-methyl pyrrolidone) solvent with a mass ratio of 35:65, magnetically stirring for 12 h under 70° C. water bath, so as to fully dissolve the PVDF; and
Establishing the same device as illustrated in the embodiment 1, casting the pyroelectric polymer solution at a border area across the fixed stretching plate 2 and the movable stretching plate 3, setting a temperature of the temperature-controllable heating plate to 60° C. to heat the casted film for 0.5 h, thus volatilizing part of the solvent in the film so as to obtain a semi-cured wet film; stretching the wet film by horizontally moving the movable stretching plate 3 away from the fixed stretching plate 2 with a stretching length of 11.00 mm and a stretching speed of 200 mm/s controlled by the stepper motor 6 with a programmable servo controller, so as to stretch the film by 10 times and the stretched film forms a layer of even film on the forming plate 1; keeping the temperature of the temperature-controllable heating plate at 50° C. for fully volatilizing the solvent in the PVDF film, so as to complete preparation.
Testing pyroelectric response with the same method as illustrated in the embodiment 1, the pyroelectric response read by the oscilloscope has a frequency of 1 Hz.
One skilled in the art will understand that the embodiment of the present invention as shown in the drawings and described above is exemplary only and not intended to be limiting.
It will thus be seen that the objects of the present invention have been fully and to effectively accomplished. Its embodiments have been shown and described for the purposes of illustrating the functional and structural principles of the present invention and is subject to change without departure from such principles. Therefore, this invention includes all modifications encompassed within the spirit and scope of the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017 1 1336946 | Dec 2017 | CN | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2059284 | Schade | Nov 1936 | A |
| 2163784 | Gammeter | Jun 1939 | A |
| 2405008 | Berry | Jul 1946 | A |
| 2953818 | Bartron | Sep 1960 | A |
| 3081208 | Bottorf | Mar 1963 | A |
| 3139470 | Prengle | Jun 1964 | A |
| 3197538 | Capron | Jul 1965 | A |
| 3325330 | Robb | Jun 1967 | A |
| 3376370 | Koblitz | Apr 1968 | A |
| 3751531 | Foster | Aug 1973 | A |
| 3931446 | Murayama | Jan 1976 | A |
| 3965232 | Chion | Jun 1976 | A |
| 4344908 | Smith | Aug 1982 | A |
| 4448742 | Kromrey | May 1984 | A |
| 4600633 | Kono | Jul 1986 | A |
| 4868284 | Murase | Sep 1989 | A |
| 4935181 | Theophilou | Jun 1990 | A |
| 4948544 | Van Unen | Aug 1990 | A |
| 4966803 | Pluyter | Oct 1990 | A |
| 5171632 | Heeger | Dec 1992 | A |
| 5217650 | Theophilou | Jun 1993 | A |
| 5310866 | Rutten | May 1994 | A |
| 5498371 | Schellekens | Mar 1996 | A |
| 7436099 | Pei | Oct 2008 | B2 |
| 8829121 | Yoshida | Sep 2014 | B2 |
| 10384231 | Swanson | Aug 2019 | B2 |
| 20090127734 | Nozawa | May 2009 | A1 |
| 20090134538 | Takita | May 2009 | A1 |
| 20090146334 | Takita | Jun 2009 | A1 |
| 20150048540 | Hatakeyama | Feb 2015 | A1 |
| 20160152946 | Choi | Jun 2016 | A1 |
| 20180009136 | Rawlings | Jan 2018 | A1 |
| 20180086011 | Blink | Mar 2018 | A1 |
| 20180366709 | Mizuno | Dec 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 106528497 | Mar 2017 | CN |
| 936398 | Sep 1963 | GB |
| Number | Date | Country | |
|---|---|---|---|
| 20180186060 A1 | Jul 2018 | US |