Patent Application
20080279737
1. Field of the Invention
The present invention relates to a method for processing waste copper solution/liquid to produce high copper content sludge, and more particularly to the process of classifying the waste liquid from PCB production into an acidic low copper content waste solution, an acidic high concentration copper content waste solution and an oxidized acidic high concentration copper waste liquid, and mixing the waste solution or liquid with a strong alkali to raise the content of copper in the sludge, thereby improving the economical values of the recycle.
2. Description of the Prior Art
Following the development and popularization of electronic information products, the PCB output value already exceeded NT$100 billion, and aside from a plurality of organic pollutants in the waste water, waste liquid and other disposables resulting from the use of chemicals and special raw materials for PCB production process, substantial quantities of copper, lead and nickel in copper compounds are also included. If such voluminous heavy metals are not properly treated, serious environmental pollution could be caused and even pose a serious threat to human health.
Presently, the PCB manufacturers would first neutralize the pH value of the discharged low copper content waste solution (or liquid) and then remove water until it reaches the regulated standard for discharge; afterwards, the copper sludge would be outsourced to specialized companies for extraction and recycling of copper. Since treatment fees charged by the outsourced companies are based on the weight of the copper sludge, such charges could be a heavy burden on the PCB manufacturers if the copper content of the sludge is not raised. Following continuous accumulation of disposables, it is critical to resolve the generation of disposables, raise its value for recycling and minimize the impact to the environment by reducing the disposables or completely recycle and reuse the disposables, thereby minimize the threat by disposables to the quality of our living environment.
PCB manufacturers use huge quantities of copper for the production of PCB; during the production process, etching, surface treatment and other processes generate acidic low concentration copper waste solution and acidic high concentration copper waste liquid and oxidized acidic high concentration copper waste liquid, therefore, it is necessary to improve the treatment method of conventional waste water (or liquid) in order to raise the copper content of the sludge to make it valuable for recycle. Presently, however, no recycling flow is available for both treating the low copper content waste solution (or liquid) and also effectively converting the copper waste solution (or liquid) and derivative copper sludge into cupric oxide (CuO) with high recycle value. To raise the value of disposables for recycling and to resolve the problem of output of sludge onsite in the factory can avoid the entailed cost and risk in outsourcing.
Referring to
However, this treatment method is mainly used to discharge the copper ions in the waste liquid so it forms solid copper hydroxide sludge (Cu(OH)2) and the copper content is only 5˜15% with no recycle value and yet has to pay very stiff treatment costs.
In view of the shortcomings of the conventional method, the inventor of the present invention has strived to make improvements to overcome its shortcomings and sought for an integrated and reasonable solution; after conducting extensive researches and experiments, the inventor finally developed a treatment method for producing high copper content sludge from low copper content waste solution (or liquid) in accordance with the present invention.
Therefore, it is a primary objective of the present invention to provide a better method to raise the copper content of sludge for recycling the low copper content waste solution (or liquid) generated from production of PCB and reduce disposables treatment cost for enterprises.
Another objective of the present invention is to provide a treatment method for generating high copper content sludge from low copper content waste solution (or liquid); this is mainly by mixing the acidic low concentration copper waste solution with the strong alkali to a pH value approximately 8.5˜9.5, then add coagulating agent (ferric chloride (FeCl3) or use backflow of copper sludge as substitute) and polymer to turn it into copper hydroxide sludge (Cu(OH)2); further, add oxidized acidic high concentration copper waste liquid and acidic high concentration copper waste liquid to the copper hydroxide till the pH value falls in between 0.5˜2.0 and further add strong alkali (such as sodium hydroxide) to adjust pH value to over 10 to trigger chemical reaction to become cupric oxide sludge.
Another objective of the invention is to provide a treatment method for generating high copper content sludge from low copper content waste solution (or liquid), mainly by adding oxidized acidic high concentration copper waste liquid and acidic high concentration copper waste liquid to the copper hydroxide till the pH value falls in between 0.5˜2.0 and further add strong alkali (such as sodium hydroxide) to adjust the pH value to over 10 to trigger chemical reaction to become cupric oxide sludge.
Another objective of the present invention is to provide a treatment method for generating high copper content sludge from low copper content waste solution (or liquid), mainly by adding strong alkali (such as sodium hydroxide) to the oxidized acidic high concentration copper waste liquid and adjust its pH value to above 10 to trigger chemical reaction to become cupric oxide sludge.
Another objective of the invention is to provide a treatment method for generating high copper content sludge from low copper content waste solution (or liquid), mainly by mixing the oxidized acidic high concentration copper waste liquid with acidic high concentration copper waste liquid to adjust its pH value to between 0.5˜2.0, and further add strong alkali (such as sodium hydroxide) to adjust its pH value to over 10 to trigger chemical reaction to form cupric oxide sludge.
Said cupric oxide sludge generated by chemical reaction would undergo dehydration by a dryer to reduce water content to solid (often referred to as the sludge cake) and then further baked dry with an oven to obtain high copper content cupric oxide sludge; henceforth, it is unnecessary to add additives in order to turn the copper hydroxide sludge into valuable cupric oxide sludge; after further dehydration and baking, the copper content is far higher than copper sludge produced by conventional treatment methods.
To make it easier for our examiner to understand the present invention, the following embodiment accompanied with the related drawings are described in details.
First, copper content of the acidic low concentration copper waste solution as defined in the present invention should be below 1% while the copper content of the acidic high concentration copper waste liquid should be equal to or above 1%. Referring to
Step S01: After mixing the acidic low concentration copper waste solution (such as the low copper content washing waste water) with strong alkali (sodium hydroxide as in this preferred embodiment), adjust its pH value to between 8.5˜9.5 and add coagulating agent (such as ferric chloride (FeCl3) or copper sludge backflow) and polymer to enable it to precipitate and generate copper hydroxide (Cu(OH)2);
Step S02: following step 1, mix the copper hydroxide sludge with the acidic high concentration copper waste liquid and the oxidized acidic high concentration copper waste liquid, and adjust its pH value to between 0.5˜2.0;
Step S03: following step 2, add strong alkali (such as sodium hydroxide) to the acidic copper waste liquid with pH value between 0.5˜2.0 to adjust its pH value to above 10 to trigger chemical reaction to form cupric oxide (CuO) sludge;
Referring to
Referring to
Referring to
Cupric oxide (CuO) generated from above reaction would undergo dehydration by a dryer to make its water content to lower to 50%, and afterwards use an oven to bake dry and get high copper content cupric oxide (CuO) sludge.
Accordingly, it is unnecessary to add additives to turn the copper hydroxide sludge into valuable cupric oxide sludge and its copper content after baking is far higher than that obtained using conventional technology.
The acidic high concentration copper waste solution referred to in the present invention includes the copper sulfate waste liquid.
And the oxidized acidic high concentration copper waste liquid includes copper nitrate waste liquid, sodium persulphate light etching waste liquid, sulfuric chlorine dioxide light etching waste liquid and the cupric chloride waste liquid.
The coagulating agent adopted in the present invention refers to ferric chloride (FeCl3) or copper sludge backflow, and strong alkali refers to the hydroxide compounds such as sodium hydroxide.
In summation of the description above, the present invention provides a simple and easy way to implement treatment of the low copper content waste solution (or liquid) to produce high copper content sludge, and the method can be modified according to the needs of the user to enhance its performance, and its treatment of recycling the PCB is unprecedented, and fully complies with the patent application requirements and is duly filed for the patent application.