Patent Grant
7544847
1. Field of the Invention
The present invention relates to a method for producing 1,4-bis(dichloromethyl)tetrafluorobenzene (DCMTFB) and, more particularly, to a method for producing high-yield 1,4-bis(dichloromethyl)tetrafluorobenzene in mass production.
2. Description of Related Art
Parylene polymers possess numerous advantages for manufacturing purposes. For example, the coating environment is at room temperature; no residual stress exists after coating; and precise controls are allowed on the thickness of the deposition film. Additionally, parylene polymer films have advantages such as uniformity, excellent acid and alkali resistance, high transparency and low dielectric constant. Therefore, they have been widely employed in electric insulation on printing circuit boards, damp-proofing on sensors or medical instruments, and anti-corrosion on metal-coating, etc. Presently, the fluoro parylene polymers, for their low dielectric constant and high melting point, can be utilized on dielectric coating in the electrical and coating industries and have become the focus of the attention.
One of fluoro parylene polymers, for example, poly(tetrafluoro-p-xylene) has the structure represented by the following Formula (1).
Fluoro parylene polymers are generally coated on products by means of chemical vapor deposition in a vacuum at room temperature. Products coated with fluoro parylene polymers not only possess excellent anticorrosive, damp-proofing and insulating characteristics, but also have the advantages of extra thinness, transparency and being poreless. By polymerizing active monomers on the object surfaces, fluoro parylene polymer coatings can be formed. Unlike the general steps of liquid coating process, there is another coating process to have the parylene dimers vaporized first, and as the dimer bonds are cleaved to yield monomer free radicals at a pyrolysis condition, the monomer free radicals are polymerized to form parylene polymers.
Currently, the dimer of fluoro parylene polymers often used in the industry is octafluoro-2,2-paracyclophane represented by the following Formula (2).
The dielectric constant of fluoro parylene polymers decreases as the number of fluorine atoms increases within the polymers. Thus, it can be predicted that the parylene polymers polymerized from the dimer of fluoro parylene polymers, represented by the following Formula (3) and containing no hydrogen atoms, can have a lower dielectric constant.
It is important for 1,4-bis(bromodifluoromethyl)tetrafluorobenzene (BFTFB) represented by the following Formula (4) to be the monomer of the above-mentioned dimer, to not contain any hydrogen atoms, of fluoro parylene polymers.
1,4-bis(dichloromethyl)tetrafluorobenzene (DCMTFB), as shown in the following Formula (5), is a critical precursor for synthesis of the foregoing 1,4-bis(bromodifluoromethyl)tetrafluorobenzene (BFTFB).
Nowadays, 1,4-bis(dichloromethyl)tetrafluorobenzene (DCMTFB) is synthesized by reacting 1,2,4,5-tetrafluorobenzene (TFB) with CHCl3, as shown in the following Reaction (I).
However, this method is time-consuming and low-yielding, and needs silica-gel column chromatography to purify the crude product. Hence, this method is unsuitable for mass production.
Therefore, it is desirable to provide a prompt and high-yield method for synthesize 1,4-bis(dichloromethyl)tetrafluorobenzene (DCMTFB), and such method is appropriate for mass production.
The present invention provides a method for producing 1,4-bis(dichloromethyl)tetrafluorobenzene. This method can reduce the reaction time, simplify the procedures and promote the yield for producing 1,4-bis(dichloromethyl)tetrafluorobenzene. The reaction of the method is shown as the following Reaction (II).
The present invention provides a method for producing 1,4-bis(dichloromethyl)tetrafluorobenzene, which comprises the following steps:
(a) mixing tetrafluoroterephthaldehyde, a catalyst and SOCl2 with or without organic solvents to form a mixture, wherein the catalyst belongs to formamides;
(b) heating the mixture;
(c) cooling the mixture, adding the mixture into water slowly, and letting the mixture separate into two layers;
(d) obtaining an organic layer from the layers of the mixture; and
(e) purifying the organic layer and removing the organic solvents and the catalyst in the organic layer and affording 1,4-bis(dichloromethyl)-tetrafluorobenzene.
In the method of the present invention, the molar ratio of tetrafluoroterephthaldehyde to SOCl2 is at least more than 2. The molar ratio of tetrafluoroterephthaldehyde to SOCl2 is preferably in the range from 2 to 20, and more preferably in the range from 5 to 8.
In the method of the present invention, the weight ratio of the catalyst to tetrafluoroterephthaldehyde is in the range from 0.1 to 1.0, and preferably in the range from 0.2 to 0.4.
In the method of the present invention, the weight ratio of the organic solvent to tetrafluoroterephthaldehyde is in the range from 0 to 3, and preferably in the range from 1 to 2.
In the method of the present invention, the mixture in the step (b) is heated until the temperature thereof rises to the range from 60 to 130° C., and preferably to the range from 85 to 100° C.
In the method of the present invention, the reaction time of the step (b) is in the range from 2 to 30 hours, and preferably to the range from 4 to 6 hours.
In the method of the present invention, the mixture is cooled in the range from 0 to 60° C. in the step (c), and preferably in the range from 25 to 40° C. so as to avoid the overreaction of hydrolysis.
In the method of the present invention, the mixture can be added into water slowly at 0 to 25° C., and preferably into iced water in the step (c) to avoid the overreaction of hydrolysis.
The method of the present invention can be performed without or with an organic solvent nonreactive to SOCl2. The organic solvent is preferably at least one selected from the group consisting of toluene, chloroform, p-xylene, benzene, dioxane, 1,2-dichloroethane, tetrachloromathane, tetrahydrofuran, nitrobenzene, and o-dichlorobenzene, and more preferably is toluene or benzene.
In the method of the present invention, the catalyst is N,N-dialkylformamide, wherein the alkyl group is a C1˜C7 alkyl group. Preferably, the catalyst is N,N-dimethylformamide (DMF), or N,N-diethylformamide (DEF).
In the method of the present invention, the purification of the step (e) preferably comprises the following steps:
(e1) adding an organic solvent and water (H2O) into the organic layer under stirring;
(e2) neutralizing the mixture;
(e3) isolating the organic layer and then concentrating the organic layer; and
(e4) cooling the organic layer to obtain a solid product.
In the above-mentioned step (e), the volume ratio of the organic solvent to water is in the range from 1 to 10 in the step (e1), and preferably is 1. The organic solvent can be any organic solvent which can dissolve 1,4-bis(dichloromethyl)tetrafluorobenzene but is not miscible with water, and preferably is dichloromethane in the step (e1). The mixture can be neutralized by any basic solution, and preferably by concentrated ammonia in the step (e2).
Other objects, advantages, and novel features of the invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings.
Tetrafluoroterephthaldehyde (TFTPA, 15.45 g), N,N-dimethylformamide (DMF, 3.01 g), and toluene (15.01 g) were added into a 250 mL three-necked reactor equipped with a temperature probe, a condenser and an aeration tube. Under nitrogen atmosphere, SOCl2 (63.37 g) was slowly added into the flask via the channel for the temperature probe by a feed hopper. After the feed hopper was removed, the flask was reequipped with the temperature probe. The reaction mixture was heated in an oil bath under stirring while the aeration of nitrogen was closed, and it was refluxed at 85˜95° C. for 2 hours until gas chromatography (GC) analysis informed that the reaction was completed. After the reaction mixture was cooled to room temperature, iced water was slowly introduced thereto to hydrolyze residual SOCl2. The reaction mixture was stood for a while and the aqueous layer was removed. Subsequently, appropriate amounts of dichloromethane (DCM) and H2O (the volume ratio of DCM to H2O=1/1) were added into the remaining organic layer. The pH value of the mixture was adjusted to 7.0 by concentrated ammonia (conc. NH3(aq)). Then, the organic phase was isolated, washed by water, dehydrated by anhydrous magnesium sulfate, and concentrated to remove DCM, toluene, and DMF. Finally, the resultant was cooled to room temperature so that the crude product (22.23 g, crude yield: 93.8%) was obtained. The crude product was recrystallized in n-heptane to afford 13.33 g of the crystal product. The residual n-heptane solution was evaporated, and then recrystallized once again to obtain 6.28 g of the crystal product. The total quantity of recrystallization twice amounted to 19.61 g of the crystal product (the yield: 82.75%).
Data of Chemical Analyses:
(a). Mass spectrum: M+=316.
(b). 1H NMR (CDCl3; external standard: TMS) chemical shift (δ): 6.90 ppm (s, 2H).
(c). 19F NMR (CDCl3; external standard: CFCl3) chemical shift (δ): −139.37 ppm (s, 4F).
(d). 13C NMR (CDCl3; external standard: TMS) chemical shift (δ): 143.45 ppm (d, JC-F=257 Hz, 4 Aromatic C), 120.72 ppm (s, 2 Aromatic C), 58.26 ppm (s, 2 Aliphatic C).
Examples 2 to 16 were performed in the manner the same as Example 1. However, the amounts of the reagents and the solvent, the reaction conditions, and the yields of the products are listed in Table 1.
Examples 1 to 16 illustrate that the solvent can be toluene, chloroform, p-xylene, benzene, dioxane, 1,2-dichloroethane, tetrachloromathane, tetrahydrofuran, nitrobenzene, or o-dichlorobenzene, and the catalyst is formamides most preferably.
Comparative Example is a conventional method of producing 1,4-bis(dichloromethyl)tetrafluorobenzene, in which 1,2,4,5-tetrafluorobenzene (TFB) is reacted with CHCl3 to yield 1,4-bis(dichloromethyl)tetrafluorobenzene. This method is detailed in the following.
1,2,4,5-tetrafluorobenzene (TFB, 3.77 g), anhydrous AlCl3 (20.34 g), and CHCl3 dehydrated by NaH as the solvent were added into a 100 mL reactor. The mixture was heated in an oil bath under stirring and refluxed for 24 hours. Subsequently, the mixture was added into iced water slowly to hydrolyze residual AlCl3. The mixture was extracted with chloroform, and then the organic phase was washed by water, dehydrated by anhydrous magnesium sulfate, and concentrated to obtain the crude product. The crude product was purified by silica-gel column chromatography using n-hexane as the eluent, and recrystallized with n-hexane to obtain 1,4-bis(dichloromethyl)tetrafluorobenzene (yield: 59.33%).
Table 2 shows the drawbacks and advantages of the present Comparative Example compared with Example 1.
Based on Table 2, the cost of Example 1 is 1.5-fold more than that of the Comparative Example. However, the method of Example 1 can reduce the reaction time, simplify the procedures, have a larger reactor capacity and promote the yield for producing 1,4-bis(dichloromethyl)tetrafluorobenzene. These aspects of Example 1 are better than those of the Comparative Example.
Although the present invention has been explained in relation to its preferred embodiment, it is to be understood that many other possible modifications and variations can be made without departing from the scope of the invention as hereinafter claimed.