Patent Grant
12011750
The invention relates to a method for producing a carcass for a flexible pipe as well as a method of producing a flexible pipe and a flexible pipe comprising an internal pressure sheath, at least one outer armor layer and a carcass comprising a cover strip.
Flexible offshore pipes are widely used for transport of hydrocarbons such as oil and gas. Basically, a flexible pipe comprises an internal pressure sheath or inner liner with a hollow bore through which the hydrocarbons are transported. The internal pressure sheath is in most cases produced from polymer material, which is extruded to form a tubular internal pressure sheath, which has a high degree of impermeability in respect of the hydrocarbons to be transported. The internal pressure sheath may be supported and reinforced by several other layers, such as pressure armors and tensile armors. These layers are normally applied on the outer surface of internal pressure sheath. However, due to external pressure it may sometimes be necessary to support internal pressure sheath on the inner surface against collapse due to a pressure drop in the pipe bore. Normally, such a support is a metal structure known as a carcass. A carcass is conventionally made from elongate strips of metal, which are wound to form a tubular structure. The strips of metal may be wound with overlaps between consecutive windings to form the tube. Moreover, in their edge parts the metal strips may be provided with bends which may engage in consecutive windings and “lock” the windings to each other, thereby providing longitudinal strength to the resulting tube.
Consequently, flexible offshore pipes, hereafter referred to as flexible pipes, are for example used in the oil industry for raising or transporting hydrocarbons from a subsea well head to a platform or floating equipment such as a Floating Production and Storage Offloading unit known by the abbreviation FPSO. Such steel armored flexible pipes for offshore applications are generally known from the standard “Recommended Practice for Flexible Pipe”, ANSI/API 17B, fifth Edition, May 2014 (hereafter API17B), and the standard “Specification for Unbonded Flexible Pipe”, ANSI/API 17J, Fourth edition, May 2014 (hereafter API17J), published by the American Petroleum Institute.
Several types of carcasses have been applied to support the internal pressure sheath in a flexible pipe structure. The carcasses may be manufactured from elongate metal strips, which may be folded into several different cross sections. The folded cross sections improve the strength in the resulting carcass.
However, these traditional carcass types will have a small gap, groove or interstice between adjacent windings and when gas is flowing through the flexible pipe, pulsations can be generated by lock-in of synchronized vortex shedding in the groves of the carcass. This phenomenon has been observed on floating production platforms connected to flexible risers conveying gas, e.g. for export or for injection into the hydrocarbon reservoir. Thus, when the gas flow reaches a certain velocity, the gaps between the adjacent windings may cause formation of local vortexes in the flow and the formation of these vortexes may again cause high levels of distinctive tonal noise and vibrations in the flexible pipe. This phenomenon is known as “singing carcasses”, “singing risers” or flow-induced pulsations (FIP) and is highly undesirable as the vibrations may result in fatigue damage. In particular, the vibrations may spread to the connected structure comprising parts such as topside piping and subsea manifolds and cause severe fatigue damage on those parts.
Consequently, attempts have been made to reduce or eliminate the formation of the vortexes. One very simple way to eliminate the formation of vortexes in the flow is to reduce the velocity of the flow of gases in the flexible pipe. However, this solution will also reduce the capacity of the flexible pipe. Thus, alternative attempts have been made to avoid vortex formation at high flow velocities of gas.
French patent application FR2930622 A1 discloses a method for eliminating vibrations by providing the strips from which the carcass is made with holes in the surface.
International patent application WO 2014/000816 A1 suggests a solution in which the gaps are provided with an insert profile, which at least partly closes the gaps between adjacent windings.
International patent application WO 2014/135906 A1 discloses a flexible metal pipe made from a layered strip. One of the layers in the strip may be un-folded and cover crevices in the flexible metal pipe. The structure makes it very difficult to achieve a pipe having a uniform diameter. To achieve a uniform diameter the layered strip needs to be modified by twisting or further bending which complicates the manufacture of the metal pipe.
U.S. Pat. No. 6,543,488 B2 and international patent application WO 2015/121424 A1 both discloses an insert piece, which can be inserted in the carcass structure and cover the gaps between consecutive windings.
In practice it has appeared that during manufacturing of a carcass with an integrated cover strip major differences in the forces affecting different parts of the S-shaped cover strip may lead to undesired deformation and undulations of the cover strip, such as buckling and therefore such cover strips have never been used with any success in practice.
An object of the present invention is to provide a method for producing a carcass with an improved carcass structure comprising a cover strip.
In an embodiment, it is an object of the present invention is to provide a method for producing a carcass comprising a cover strip and in which the risk of buckling and resulting formations of undulations of the cover strip during manufacturing of the carcass is significantly reduced.
In an embodiment an object is to provide flexible pipe comprising a carcass with a cover strip for a flexible pipe, which reduces the risk of vortex formation in the transported fluid and preferably at the same time reduces the risk of corrosion of the carcass material.
These and other objects have been solved by the invention as defined in the claims and as described herein below.
It has been found that the invention and embodiments thereof have a number of additional advantages, which will be clear to the skilled person from the following description.
The invention is defined in the claims.
In a first aspect the present invention relates to a method for producing a carcass suitable for a flexible pipe for conveying a fluid, specifically suitable for conveying fluids comprising gas.
The carcass produced according to the method is especially advantageous for use in a subsea flexible pipe and in particular where the subsea pipe is for transporting gas containing fluid.
The method comprises providing at least one first metallic strip and a cover strip both have a length and a width. Preferably the at least one first metal strip is one single first metal strip, but in an alternative embodiment several first strips are interconnected to form a first metallic strip assembly, e.g. by being interconnected along edges.
The terms “first metallic strip” and “first strip” are used interchangeable and also include a strip assembly as mentioned above.
The terms “cover metallic strip” and “cover strip” are used interchangeable
According to the method, the first strip (or strip assembly if there are more than one first strip) is shaped to have a profile with a first fold adapted to face towards the carcass axis and a second fold adapted to face away from the carcass axis. The cover metallic strip has an anchor width section and a cover width section and the method comprises inserting the anchor width section of the cover strip into the first fold of the first strip and providing that the cover width section of the cover strip extends beyond the second fold and helically winding the first metallic strip and the cover strip, to provide that the first fold engages and interlocks with the second fold and that the cover width section covers a helical interstice between windings of the first metallic strip on the inner side of the carcass i.e. the side facing inwards.
According to the method at least a part of the anchor width section of the cover strip is subjected to a pretreatment before insertion into the first fold, wherein the pretreatment comprising a weakening resistance treatment against length extension and/or a length extension of the pretreated part of the anchor width section. The pretreatment is also referred to as the pretreatment of the cover metallic strip to obtain a reduction of resistance against length extension. As explained this pretreatment advantageously also ensures a reduction in resistance to bending
The method according to the invention provides a carcass for a flexible pipe, which have superior qualities and reduces the risk of vortex formation in the fluid transported in a pipe comprising the carcass.
Without being bound by the theory, it is believed that the problem of applying a cover strip in the prior art methods is that the cover width section of the cover strip is a “free width section” where the edge along the cover width section not fixed and in practice the cover strip is only fixed by being anchored by the anchor width section. Further the cover width section has a winding radius which is less than the winding radius of the anchor width section. This difference in winding radius results in excessive tensioning in the cover strip during the helically winding, in particularly in the part of the cover width section closest to the anchor width section and this tensioning results in buckling with resulting tensioning undulations of the cover width section.
By subjecting at least a part of the anchor width section to the pretreatment before insertion into the first fold and thereby before helically winding, the tensioning in the cover strip during the helically winding has been at least partly reduced and thereby the buckling with resulting tensioning undulations of the cover width section is also reduced or fully avoided.
The pretreatment ensures that at least a portion of the anchor width section can be extended in length without extending the cover width section and with a reduced formation of tensioning in the cover width section. The weakening treatment of resistance against length extension ensures that resistance in the anchor width section is against extension in length direction of the cover strip is reduced.
Advantageously the cover width section is not subjected to weakening treatment of resistance against length extension.
In an alternative embodiment the pretreatment comprises actually extending at least a part of the anchor width section in length direction of the strip. Thereby, when helically winding the cover strip with the difference in winding radius of the cover width section and the anchor width section, the anchor width section is subjected to less extension forces, which again results in less tensioning, less buckling and less formation of tensioning undulations.
Advantageously the first metallic strip is or shaped into a substantially “S” shaped cross-sectional profile where the two folds in the “S” provides the first and the second folds. Initially the S-shaped profile is not shaped to the final shape, but kept sufficiently open in its first and second folds to allow insertion of the anchor width section of the cover into the first fold and to allow interlocking the first and the second folds.
The profile of the first metallic strip is brought to the final shape during the helically winding of the first metallic strip and the cover metallic strip to form the carcass. During this process, the profile of the first metallic strip will also be interlocked by interlocking the first fold with the second fold of an adjacent winding and thereby form a tube comprising interlocked windings of first strip(s). Between the interlocked windings is formed a helical interstice—sometimes called a gap, which on the inner side of the tube is covered by the cover width section of the cover metallic strip.
The term “inner side” of a layer is the side of the layer facing the axis of the pipe. The term “outer side” of a layer is the side of the layer facing away from the axis of the pipe.
The term “substantially” should herein be taken to mean that ordinary product variances and tolerances are comprised.
Advantageously the pretreatment provides that the bending resistance to bending perpendicular to the cover strip length in the treated of part of the anchor width section is reduced to less than 50%, when compared to the resistance to bending without the pretreatment.
Thereby, the tensioning in the cover width section when helically winding the cover strip may be even further reduced.
In an embodiment of the method at least 20%, such as at least 40%, such as at least 60%, such as at least 80% of the anchor width section is weakened by the pretreatment. This pretreatment advantageously also ensures that resistance to bending is reduced to less than 50% when compared to the resistance to bending of non-treated cover metallic strip width.
Advantageously, the anchor width section comprises at least 40% of the width of the cover metallic strip and this anchor width section is advantageously inserted in the first fold of the first metallic strip to be anchored in the interlocking provided when the first fold engages and interlocks with the second fold of the first strip.
Advantageously the pretreated part of the anchor width section comprises at least 30% of the width of the cover strip, such as at least 40%, such as at least 50% of the width of the total cover strip.
The first fold of the first strip has a depth and a width at the depth, and the pretreated part of the anchor width section advantageously comprises at least a width corresponding to the width at the depth of the first fold.
Thereby a very strong anchoring of the cover strip may be provided to ensure that the cover strip is not escaping out of the interlocking in the first strip when the carcass is subjected to bends or is coiled.
Advantageously the first fold of the first strip has a depth and curved section between respectively a first edge and a second edge along the depth, where the second edge is closer to the second folding than the first, and wherein the pretreated part of the anchor width section comprises at least a width corresponding to the width at the depth of the first fold.
Thereby an even stronger anchoring may be provided.
In practice the anchor width section of the cover metallic strip inserted in the profile of the first metallic strip may comprise treated and untreated sub-width sections, such as at least an edge section thereof. However, advantageously at least 40% of the width of the cover metallic strip, which is inserted in the profile of the first metallic strip is treated such that the resistance to bending is reduced to less than 50% when compared to the bending resistance to bending of a non-treated cover metallic strip width section.
The treatment of at least 40% of the width of the cover metallic strip, which is inserted in the profile of the first metallic strip, i.e. the anchor width section, has surprisingly appeared to have a good effect during the manufacturing of the carcass appears to further counteract the forces which occur during the helically winding of the metallic strips, and therefore may result in an even further reduction of undesired deformations.
The first metallic strip and the cover metallic strips are advantageously assembled by inserting the anchor width section of the cover strip into the first fold of the first metallic strip and thereafter the assembly is helically wound to form the carcass. The assembly is advantageously wound with a winding angle in the range of 80 to 89.8 degrees in respect of the axis of the carcass. The first metallic strip and the cover metallic strip are preferably made from the same metallic alloy, the alloy may e.g. be selected from carbon steel or duplex steel.
The pretreatment comprising the weakening treatment of resistance against length extension may in an embodiment comprise a mechanical, a chemical and/or a thermal treatment.
In an embodiment, wherein the pretreatment comprises a mechanical pretreatment.
In an embodiment, the pretreatment comprises stretching the material to increase in length, preferably by preforming at least a part of the anchor width section to have a shape adapted to conform to the first fold. Thereby at least the part of the anchor width section is extended and during winding the tension generated in the cover width section may be very low and hence the risk of buckling and resulting tension undulations may be highly reduced or even fully avoided
In an embodiment, the pretreatment comprises providing weakening lines in the anchor width section. Advantageously, the weakening lines are substantially perpendicular to the length of the cover strip. The weakening lines are advantageously in the form of grooves and/or recesses for example provided by cutting, pressing, embossing, such as pressing using a press tool. In an embodiment, the weakening lines are made to fully penetrate the material of the anchor width section, this may advantageously be provided by cutting, wherein the cutting comprises cutting fully through the strip material.
In an embodiment, the weakening lines are made by cutting out strips of the treated part of the anchor width section.
In an embodiment, at least a part of the weakening lines are not fully penetrating the strip material, bur advantageously the weakening lines are sufficiently deep and/or weak to break fully up upon the helically winding if the strips. This embodiment has the benefit that it is very simple to provide.
The weakening lines advantageously has a length of from 1 to 5 cm, such as from 3 to 4 cm. The distance between weakening lines is advantageously from 1 mm to 1 cm, such as from 2 mm to 5 mm.
Where the weakening lines comprises cutting out strips of the treated part of the anchor width section, the strip shaped holes provided advantageously has a width of up to 5 mm, such as from 1 to 4 mm.
It has been found that the cutting of the weakening lines also reduces the resistance to bending discussed above.
Cutting in metallic strips is well-known technique which can be performed easy and cost-effective.
The cutting can be performed partly or fully made by mechanical means. Mechanical cutting is easy and cheap to perform. The cutting can also be performed partly or fully by cutting using focused electromagnetic radiation or an electron beam. Cutting by electromagnetic radiation or an electron beam, such as a laser beam, can provide very precise and focused cuts and the cutting and the process is easy to control.
In an embodiment, the weakening treatment of resistance against length extension is performed using pressing by a press tool. The pressing tool may be used to weakening at least 40% of the width of the anchor width section. This may in addition reduce the resistance to bending.
The weakening lines may in an embodiment be provided by laser cutting and/or electron beam.
The pretreatment may advantageously comprise providing weakening lines in at least a part of the anchor width section of the cover strip by partly or fully cutting through the strip material e.g. as described above.
The cover strip may advantageously have a first edge forming an edge of the cover width section and a second edge forming an edge of the anchor width section. The first and the second edge of the cover strip are advantageously parallel.
Advantageously, the weakening lines individually from each other are perpendicular or up to 10 degrees from being perpendicular to the anchor width section edge, such as perpendicular or up to 10 degrees from being perpendicular to the anchor width section edge, such as perpendicular ±2 degrees to the anchor width section edge.
The weakening lines advantageously comprises substantially parallel and/or straight lines.
In an embodiment, the weakening treatment of resistance against length extension comprises a thermal treatment. The thermal treatment is advantageously localized thermal treatment.
In an embodiment, the thermal treatment may also reduce the resistance to bending of the treated part of the anchor width section. Advantageously at least the 40% of the width of the cover metallic strip is treated by localized thermal treatment. Advantageously, at least 20% of the width of the anchor width section of the cover metallic strip is treated by localized thermal treatment.
The thermal treatment affects the structure of the metallic material such that the resistance against length extension is reduced and in addition also resistance to bending of the thermal treated metallic strip may be reduced.
It has been found that the pretreatment of the cover metallic strip to obtain a reduction of the resistance against length extension and preferably a reduction in resistance to bending, mainly should be carried out on the width part of the strip, which is subjected to major forces and strain during the winding of the carcass. Since the anchor width section is wound with a larger radius than the cover width section, the anchor width section will be subjected to larger forces and strain than the cover width section.
Advantageously, the part of the anchor width section subjected to the pretreatment comprises a width section which during helically winding of the at least one first metallic strip and the cover strip is subjected to tensile strain e.g. provided partly of fully by application of a stretching force.
The anchor width section, may have a sub-width part wound with larger radius than another sub-with section and preferably at least the sub-width section of the anchor width section wound with the larger radius is subjected to the pretreatment e.g. is provided with weakening lines.
Thus, according to an embodiment of the method the pretreatment of the cover metallic strip to obtain a reduction in resistance against length extension and preferably a reduction in resistance to bending is predominantly carried out in sections of the cover metallic strip, which are subjected to tensile strain during final forming of the cover metallic strip in the carcass. Preferably the pretreatment of the cover metallic strip to obtain a reduction in resistance against length extension is predominantly carried out in a width section of the cover metallic strip, which is subjected to tensile strain in the width direction of the cover strip during preshaping, helically winding and/or final forming of the cover metallic strip. Thus, the pretreatment of the cover metallic strip to obtain a reduction in resistance against length extension is predominantly carried out in at least a portion of the width of the anchor width section.
In an embodiment, the pretreatment of the cover metallic strip to obtain a reduction in resistance against length extension and preferably a reduction in resistance to bending, is predominantly carried out in sections of the cover metallic strip which are subjected to compressive strain during final forming of the cover metallic strip in the carcass.
The major load bearing part of the carcass is the profile of the first metallic strip. Therefore the load bearing capacity of the cover metallic strip may be significantly lower than the load bearing capacity of the first metallic strip. Thus, the cover metallic strip does not need to be as thick as the first metallic strip, and in an embodiment the first metallic strip is thicker than the cover metallic strip, such as at least 2 times thicker, such as at least at least 5 times thicker, such as at least 10 times thicker.
The first metallic strip may for example have a thickness of 2 mm and the cover metallic strip may have a thickness of 1 mm. In an embodiment, the first metallic strip may have a thickness of 3 mm and the cover metallic strip may have a thickness of 0.5 mm. Typically, the thickness of the first metallic strip is in the range of 2 to 5 mm and the thickness of the cover metallic strip may be in the range of 0.5 to 2 mm.
In an embodiment, the thickness of the cover metallic strip varies over its width, e.g. such that the anchor width section is up to 50% thinner than the cover width section.
The difference in the thickness of the metallic strips provides material savings and also facilitates the manufacture of the carcass. The difference in the thickness of the metallic strips also makes it easier to obtain an even and smooth surface on the inner side of the carcass.
In an embodiment the anchor width section of the cover metallic strip inserted in the first fold of the first metallic strip is conforming with the profile of the first metallic strip when the profile is closed to its final shape. The embodiment provides a carcass profile with optimized strength-to-weight ratio and also with reduced risk of corrosion.
In an embodiment, the method comprises providing that the major part of the of the anchor width section the first is conforming with the fold, preferably the major part of the of the anchor width section the first is conforming with an inner surface of the fold and hold in fixed position by the second fold in a consecutive winding.
In an embodiment, the first metallic strip has a first edge forming part of the first fold and a second edge forming part of the second fold. The first and the second ends of the first metallic strip are advantageously parallel preferably to provide that the first metallic strip in lengthwise extension is uniform.
In an embodiment, the method comprises forming the first metallic strip to have a lip adjacent to the first edge. Such lip ensures a safe engagement between the first fold and the second fold. Advantageously, the anchor width section of the cover strip located in the first fold extends beyond the lip, to be located between the lip and the second fold which is interlocked with the first fold. This ensures a safe anchoring of the anchor width section of the cover strip, to thereby reduce the risk of local lengthwise portions of the cover strip escapes from the first fold e.g. when the carcass is subjected to bends, such as during coiling onto a reel or when the pipe comprising the carcasse is subjected to excessive forces and/or local bends
In an embodiment, the anchor width section of the cove strip located in the first fold extends to the first edge the first metallic strip. Thereby the anchor width section is very safely anchored in the first fold of the first strip.
The method may advantageously comprise applying a pulling force F to the cover strip during the insertion of the anchor width section of the cover strip into the first fold and/or during the helically winding of the first metallic strip and the cover strip.
The pulling forde applies a tensile strain to the cover strip which may advantageously stretch at least a width portion of the anchor width section, preferably the pretreated portion of the anchor width section.
The pulling force applied to the cover strip is advantageously sufficient to stretching at least the portion of the anchor width section.
In an embodiment, the method comprises subjecting at least a portion of the anchor width section to tensile strain during the insertion of the anchor width section of the cover strip into the first fold and/or during the helically winding of the first metallic strip and the cover strip, wherein the tensile force preferably is at least partly provided by providing a pulling force in the cover strip.
The pulling force may e.g. be applied to the cover strip by a restraining arrangement in a cover strip supply station adapted for pre-shaping and/or pretreating the cover strip.
Advantageously, the tensile strain is sufficient to provide a deformation of a plurality of the weakening lines—such as all of the weakening lines. The deformation of each of the plurality of weakening lines may advantageously comprise providing that a pair of a first and a second opposite edges of a weakening line separates and/or increases distance to each other. In an embodiment, where the respective weakening lines is provided by through holes form out cut strips of material, the deformation of each of the plurality of weakening lines may advantageously comprise providing that the pair of a first and a second opposite edges of the weakening line separates further from each other to provide that the through hole becomes larger. In an embodiment, where the respective weakening lines does not comprise a through hole, the deformation of each of the plurality of weakening lines may advantageously comprise providing that the pair of a first and a second opposite edges of the weakening line separates from each other to provide a through hole in the anchor width section strip material.
The invention also relates to a method for producing a flexible pipe for conveying a fluid. The method comprises
The extruded polymer layer advantageously forms an internal pressure sheath. On the outer side of the extruded polymer layer one or more layers such as armor layers are applied.
In an embodiment the method comprises the step of applying a pressure armor. One or more pressure armor layers may be applied, preferable constituted by wound metallic strips, and preferably wound around the pipe with a winding angle between 65° to 89° in respect of the axis of the pipe. The pressure armor supports the pipe in respect of radial forces exposed to the pipe.
In an embodiment the method comprises the step of applying one or more tensile armors. One or more tensile armoring layers, preferable constituted by wound metallic strips, and preferably wound around the pipe with a winding angle between +/−25° to +/−55° in respect of the longitudinal axis. If two tensile armor layers are applied, the layers are preferably cross-wound. The tensile armor protects the pipe against axial forces.
The term “cross-wound layers” means that the layers comprise wound elongate elements that are wound in opposite direction relatively to the longitudinal axis of the pipe where the angle to the longitudinal axis can be equal or different from each other.
Advantageously the pipe is of the unbonded flexible type.
The unbonded flexible pipe manufactured according to the method of the invention may comprise both pressure armor and tensile armor. If this is the case the one or more pressure armor layers are wound around the internal pressure structure and the one or more tensile armor layers are wound around the pressure armor. In an embodiment the unbonded flexible pipe comprises at least one pressure armor layer and two tensile armor layers. Preferably the two tensile armor layers are cross-wound.
Although the external armor layers may be made from any suitable material such as steel, stainless steel and fibre reinforced polymer, in an embodiment the one or more external armor layers are made from carbon steel. Preferably the external armor layers are located in an annulus of the pipe and protected by the internal pressure sheath and an outer sheath.
Consequently, in an embodiment the method comprises the step of applying an outer polymer layer to form an outer sheath. The outer sheath and the internal pressure sheath form together an annulus in which the armor layers, such as pressure armor and tensile armor can be located and protected from ingress of water.
When the carcass has been formed the polymer layer is extruded onto the outer side of the carcass. The polymer layer forms a substantially fluid tight barrier around the carcass and is normally referred to as the internal pressure sheath.
On the outer side of the internal pressure sheath one or more armor layers may be applied, such as a pressure armor layer and one or more tensile armor layer.
Optionally, the pipe is applied with one or more polymer layers, which may be applied as extruded layers or as wound tape. The polymer layers may e.g. function as intermediate layers, insulating layers, anti-wear layers or anti-creep layers.
The flexible pipe may also comprise an extruded polymer layer constituting an outer sheath, which may serve to prevent ingress of water to the internal pipe parts.
Examples of polymer material which may be applied alone or in combination with other materials suitable for manufacture of the one or more polymer layers comprise the materials selected from polyolefins, e.g. polyethylene or poly propylene; polyamide, e.g. poly amide-imide, polyamide-11 (PA-11), polyamide-12 (PA-12) or polyamide-6 (PA-6)); polyimide (PI); polyurethanes; polyureas; polyesters; polyacetals; polyethers, e.g. polyether sulphone (PES); polyoxides; polysulfides, e.g. polyphenylene sulphide (PPS); polysulphones, e.g. polyarylsulphone (PAS); polyacrylates; polyethylene terephthalate (PET); polyether-ether-ketones (PEEK); polyvinyls; polyacrylonitrils; polyetherketoneketone (PEKK); copolymers of the preceding; fluorous polymers e.g. polyvinylidene diflouride (PVDF), homopolymers or copolymers of vinylidene fluoride (“VF2”), homopolymers or copolymers of trifluoroethylene (“VF3”), copolymers or terpolymers comprising two or more different members selected from VF2, VF3, chlorotrifluoroethylene, tetrafluoroethylene, hexafluoropropene, or hexafluoroethylene; compounds comprising one or more of the above mentioned polymers, and composite materials, such as a polymer (e.g. one of the above mentioned) compounded with reinforcement fibers, such as glass-fibers, carbon-fibers and/or aramide fibers.
The invention also comprises a flexible pipe for conveying a fluid. The pipe may comprise the layers and elements as discussed above and may preferably be an unbonded flexible pipe for use as a rises pipe.
The pipe comprising a center axis along the length of the pipe and from the inside and out; a carcass, an internal pressure sheath and at least one armor layer.
The carcass comprises at least one first metallic strip and a cover strip. The first metallic strip comprises a first fold facing towards the center axis and a second fold facing away from the center axis. The cover strip comprises an anchor width section and a cover width section, and wherein the first and the second fold of the first strip being interlocked with the anchor width section anchored in the interlocking and preferably the cover width section has a winding radius which is less than the winding radius of the anchor width, while the cover width section is substantially free of tension undulations.
Thereby the risk of the phenomenon known as “singing carcasses”, “singing risers” or flow-induced pulsations (FIP) may be reduced or fully avoided.
Advantageously, the cover width section of the cover strip provides a substantially smooth bore in the pipe.
Advantageously the carcass and preferably the flexible pipe is obtainable by the method described above and claimed herein, wherein the anchor width section comprises weakening lines in at least a part, preferably a width portion thereof, of said anchor width section of said cover strip.
In an embodiment, the weakening lines comprises cuts into the cover strip material.
In an embodiment, each of a plurality of the weakening lines comprises a pair of a first and a second opposite edges which are at least partly separated from each other to provide a through going opening in the strip material.
In an embodiment, the first metallic strip has a first edge forming part of the first fold and a second edge forming part of the second fold, wherein the metallic strip is shaped to have a lip adjacent to the first edge, wherein the anchor width section of the cover strip located in the first fold extends beyond the lip, to provide that a portion of the anchor width section is located between the lip and the second fold which is interlocked with the first fold.
In an embodiment, the first metallic strip has a first edge forming part of the first fold and a second edge forming part of the second edge, wherein the anchor width section of the cove strip located in the first fold extends to the first edge the first metallic strip.
The pretreatment of the cover metallic strip to obtain a resistance against length extension reduction and preferably a reduction in resistance to bending results in that the cover width section is substantially free of tension undulations. Heretofore, it has in practice not been possibly to produce a carcass with a cover strip, without many tension undulations at the cover width section.
Thus, the present invention also provides a flexible pipe which may advantageously be manufactured according to method disclosed above and where the cover metallic strip forms a covering the helical interstice (gap) formed between adjacent windings of the profile of the first metallic strip.
The flexible pipe is advantageously of the unbonded type e.g. ad described in API17B and/or API17J. The flexible pipe may advantageously be a subsea pipe. The flexible pipe is advantageously for use in transportation of gas containing fluid, such as for use in the offshore production of oil and gas.
In an embodiment of the flexible pipe, the cover metallic strip is bent such that the cover metallic strip in axial direction of the pipe exhibits varying radius in respect of the axis of the pipe. The varying radius allows the cover metallic strip to be inserted in and conforming to the profile of the first metallic strip.
The varying radius also provides varying tensions in the cover metallic strip, which improve the properties in respect of covering the helical interstice formed between adjacent windings of the profile of the first metallic strip. Thus, the invention provides an embodiment of the flexible pipe where the cover metallic strip provides a substantially smooth bore in the pipe.
In an embodiment of the flexible pipe, the fluid transported in the pipe is gas. Although the flexible pipe according to the invention is suitable for transporting any fluid, such as liquid or gas, the flexible pipe is particular suitable for transporting gases. Gases have a higher tendency of vortex formation creating flow-induced pulsation during transport and the flexible pipe according to the invention provides a high reduction in the risk of vortex formation.
All features of the inventions including ranges and preferred ranges can be combined in various ways within the scope of the invention, unless there are specific reasons not to combine such features.
The above and/or additional objects, features and advantages of the present invention will be further elucidated by the following illustrative and non-limiting description of embodiments of the present invention, with reference to the appended drawings.
The figures are schematic and are not drawn to scale and may be simplified for clarity. Throughout, the same reference numerals are used for identical or corresponding parts.
The width of the cover metallic strip 22 extending from B to C is the cover width section of the cover strip intended to cover a gap between adjacent windings of the first metallic strip 21. The cover width section extends beyond the second fold 21b.
The width extending from A to A′ of the cover metallic strip 22 preferably includes at least 20%, such as at least 40% of the total width extending from A to C of the cover metallic strip. At least a part of the anchor width section A-A′ of said cover strip has been subjected to the weakening treatment of resistance against length extension before insertion into the first fold 21a. Preferably, at least the width portion A1-A1′, which when helically wound will be wound with largest radius and therefore advantageously is subjected to the pretreatment. The pretreatment advantageously also provides a reduction in resistance to bending as described above.
As shown in
Since the anchor width section has been subjected to the pretreatment comprising a weakening treatment of resistance against length extension and/or a length extension of the pretreated part of the anchor width section, the application of the pulling force F primarily results in a stretching of the pretreated portion. Since at least a part of the anchor width section are wound with a larger diameter than the cover width section, this pulling force ensures that the portion of the cover metallic strip located between the anchor width section and the cover width section may be practically free of tension undulations, which result in that the bore may be formed to have a smooth bore wall.
In the variation of
The cover strip 22 has preferably also been subjected to a pre-shaping in a not shown pre-shaping station e.g. as illustrated in
The pulling force F, ensures a stretching of at least a portion of the anchor width section of the cover strip 22 to ensure that the portion of the cover strip adjacent to the anchor width section of the strip may be applied without undesired tension undulations to provide a desired smooth bore wall in the pipe.
As illustrated in
In the illustrated embodiment two winding rollers C1, C2 are shown. In variations thereof there is only the first winding roller C1. In another variation thereof, several further winding rollers, such as 1, 2, 3, 4 or even 5 additional winding rollers may be located along the periphery of the mandrel 15
The assembling is continued as the first metallic strip 21 and the cover metallic strip 22 passes the winding rollers C1, C2 until at some point the assembling is completed. In practice the assembling may be fully completed once the first metallic strip 21 has been interlocked with the subsequent winding thereof.
The winging direction is illustrated with the arrow,
In a further variation thereof the, the entire application system, including the bending roller(s) A, the assembling roller B, the one or more winding rollers C1, C2 and preferably the pre-shaping stations, are rotating around the mandrel 25, which is at stand still or is rotating with a rotating rate which is 10% or less relative to the rotating rate of the entire application system and preferably in the opposite direction.
The final steps of the carcass forming process are shown schematically in further details in
In
By application of a pulling force in the cover strip 22 the pretreated anchor width section is subjected to strain and is thereby stretched as explained above. The portion of the cover metallic strip located between the anchor width section and the cover width section (i.e. A′ to B) may thereby be wound without tension undulations,
When the folds 21a and 21b are interlocked and folded to their final positions the anchor width section will be fully anchored in the interlocking.
This process is illustrated in
The profiles in the first winding of the first metallic strip 21(1) and the cover strip 22(1) have not yet been folded to their finale shape and the first fold 21a and the second fold 21b of the first metallic strip 21(1) in this winding are partly open to allow insertion of the anchor width section of the cover metallic strip 22(1). In the second winding of the strips 21(2) and 22(2) the folding process is not completed. In the third winding of the metallic strips 21(3) and 22(3), the profiles have been folded to their final shape and the interlocking between the first and seconds folds and the anchoring of the anchor width section are complete.
The carcass may advantageously form part of a pipe, wherein the cover width section faces towards the bore B. The carcass comprises a first metallic strip 21 and a cover strip 22. The first metallic strip is shaped to have a first fold 22f1 and a second fold 22f2, which are engaged as described above. The first metallic strip has a first edge 21e1 forming part of the first fold and a second edge 21e2 forming part of the second fold. The first metallic strip is shaped to have a lip 211 adjacent to the first edge 21e1.
The cover strip 22 comprises an anchor width section 22a and a cover width section 22c and comprises an anchor width section edge A and a cover width section edge C. The anchor width section 22a of the cover strip 22 is located in the first fold and extends beyond the lip 211 of the first metallic strip 21. Thereby a width part of the anchor width section is located between the lip 211 and a part of the second fold 21f2 of the first strip.
The cover width section 22c covers a gap 23 between adjacent windings of the first metallic strip 21. In the shown embodiment the cover width section of the cover strip is substantially plane. In a variation thereof the cover width section 22c may be folded slightly into the gap 23 e.g. to form a trench, such as into a depth corresponding to the thickness of the first strip. This slightly depression also referred to as a trench may have the function of terminating that may have been formed. In addition the trench makes it easier to wind the first metallic strip and the cover metallic strip with a relatively large pitch than without the trench.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019 01217 | Oct 2019 | DK | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2020/078847 | 10/14/2020 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2021/074192 | 4/22/2021 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4493140 | Abdullaev | Jan 1985 | A |
| 6543488 | Foti et al. | Apr 2003 | B2 |
| 7971610 | Booth | Jul 2011 | B2 |
| 9506585 | Clements | Nov 2016 | B2 |
| 10001228 | Gundstrup | Jun 2018 | B2 |
| 20080190508 | Booth | Aug 2008 | A1 |
| 20140116565 | Gundstrup | May 2014 | A1 |
| 20140311613 | Clements | Oct 2014 | A1 |
| 20150252920 | Farnes et al. | Sep 2015 | A1 |
| 20160003381 | Király | Jan 2016 | A1 |
| 20200398325 | Stikan et al. | Dec 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 3502535 | Jun 2019 | EP |
| 2930622 | Oct 2009 | FR |
| 3017439 | Aug 2015 | FR |
| 2013088138 | Jun 2013 | WO |
| 2014000816 | Jan 2014 | WO |
| 2014135906 | Sep 2014 | WO |
| 2015121424 | Aug 2015 | WO |
| Entry |
|---|
| International Search Report and Written Opinion for PCT/EP2020/078847 dated Feb. 1, 2021. |
| “Recommended Practice for Flexible Pipe”, ANSI/API Recommended Practice 17B, fifth Edition, May 2014. |
| “Specification for Unbonded Flexible Pipe”, ANSI/API Specification 17J, Fourth edition, May 2014. |