The invention relates to a method for producing a connecting part using an injection foam molding process, preferably using a synthetic material. The invention specifically relates to the production of a connecting part, which has, on one side, a fastening part having adhesive and/or hooking elements, said fastening part forming a component of a contact fastener. The connecting part may be part of a fastening system, in which system attachment parts are provided in order to form a contact fastener connection to a component that is to be connected, said attachment parts having adhesive and/or hooking elements, which can be releasably engaged with the corresponding adhesive and/or hooking elements of the respective connecting part.
Contact fastener connections are used in many areas in order to fasten objects or components such that they can be detached again. In motor vehicles, in order to prevent the mats from slipping or lifting up, said mats are frequently secured to the vehicle floor in such a way that connecting parts, which are anchored to the floor, and which have adhesive and/or hooking elements, are brought into adhesive contact or interlocking engagement with attachment parts, which are fastened to the floor mats, and which have corresponding adhesive and/or hooking elements. With reference to this, in the prior art, the connecting parts are designed having a disk-shaped support part, which can be anchored to the vehicle floor, on the upper side of which support part a fastening part having adhesive and/or hooking elements is attached. This is done by means of chemical or thermal adhesive bonds, for example using adhesives or hot glues that contain solvents. Apart from the environmental impact associated with solvent-containing substances, neither the chemical, nor the thermal adhesive bonds are satisfactory. As has been shown, when used in floor mats in motor vehicles, there is a risk that the fastening part and the support part will become detached from one another when the temperature and/or the relative humidity in the vehicle is too high. There is also a risk of detachment when the floor mat has been used for an extended period of time. This constitutes a safety risk, in particular when the floor mat on the driver's side slides forward towards the pedals while driving, which can lead to uncertainty on the part of the driver and may possibly result in an accident.
In order to avoid the risk that the fastening part may become detached from the support part, a solution disclosed in DE 10 2009 054 896 A1 is also prior art, according to which, the connecting part is produced in such a way that the support part and hooks are simultaneously formed as fastening elements in a single process step in an injection mold. Although in this procedure, there is practically no risk of detachment, the number of hooks that can be formed in the injection mold in which the support part is molded is nevertheless extremely limited, for example to a number not exceeding 50 hooks per cm2. Such a limited achievable packing density of the hooking elements is not satisfactory.
In order to retain the advantage of the integrated design of the support part and fastening part in a connecting part, while at the same time avoiding the disadvantages of an inadequate design of the fastening part, according to a teaching disclosed in the patent application, DE 10 2013 009 091 A1, it is provided that the fastening part with the adhesive and/or hooking elements thereof, is produced in a first step, and introduced as an insert part into an injection mold, in which mold the connecting part in the form of a component is formed in a second step by means of a back injection process, which connecting part contains the fastening part as an integrated component. A connecting part can thereby be produced, for which there is no risk of detachment due to the integrated formation of support part and fastening part, and in which the adhesive and/or hooking elements can be designed in different ways because the fastening part can be prefabricated as an insert part in a separate production process so that, in addition to hooks, loops or mushroom-shaped elements having round or flat heads may also be provided, as can be produced having very high packing densities using special processes provided to this end. In carrying out this method, during the back injection process, in which a molten mass made of a thermoplastic synthetic material such as polyamide or polypropylene, preferably having glass fiber reinforcement, is injected into the injection mold, it is necessary to ensure that no damage occurs to the elements of the fastening part as a result of excessive molding pressure, such as the flattening of the adhesive or hooking elements. In order to eliminate this risk, a correspondingly complex design of the injection mold is necessary, for example in order to avoid longer flow paths and the increased injection pressures that such a flow path requires.
With respect to this problem, the object of the invention is to specify a method, with which connecting parts, in which the support part contains the fastening part as an integrated component, can be efficiently and reliably produced with low equipment complexity.
This object is achieved by the method according to the invention having the features of claim 1 in its entirety.
Accordingly, an essential feature of the invention is that the second production step, the back injection process, in which the support part is formed through back injection of the insert part, which has been introduced into the injection mold, is carried out by means of injection foam molding. In this injection molding process, which is known in professional circles as thermoplastic injection foam molding (TSG), the polymer melt is loaded with a foaming agent, which results in the foaming of the molding material in the mold cavity after the injection molding process. As compared to compact injection molding, in the case of injection foam molding, longer flow paths can be implemented at lower process temperatures, which allow the tool to have a simplified structural design. Corresponding lower injection pressures result in lower closing forces for the mold. In addition, the risk that the adhesive and/or hooking elements might be damaged by the effects of compressive forces is reduced.
In the case of back injection by means of injection foam molding, the foamed support part can be designed as a damping layer, which makes it possible to use higher injection pressures without resulting in damage to the adhesive and/or hooking elements of the insert part.
The injection foam molding can be carried out by means of a chemical foaming agent, which has been admixed with the base polymer, or by means of a physical foaming agent, wherein the polymer melt is charged with a blowing gas. Since, in the case of chemical foaming agents, solid decomposition residues remain in the polymer melt after the separation of blowing gases, the method according to the invention is advantageously carried out in such a way that, for the foam injection molding process, at least one foaming agent is admixed with the synthetic material in a physical manner, and carbon dioxide (CO2) or nitrogen (N2) gas is preferably admixed with a polymer melt as a foaming agent, said polymer melt preferably comprising polyamide (PA), polypropylene (PP), polyethylene (PE) or acrylonitrile butadiene styrene (ABS).
It is of particular advantage that the method according to the invention be carried out in such a way that a coating is introduced between the insert part, also as a component thereof, and the foamed support part, the insert part (16) being preferably provided with reaction mediator on the side of said insert part facing the support part (26), said reaction mediator particularly preferably containing polyurethane. During back injection, an additive of this kind promotes the formation of a firmly bonded connection of the foamed support part with the insert part. A solvent-free, moisture-curing hot-melt adhesive based on reactive polyurethane prepolymers may also serve as a reaction mediator or adhesive for producing the connection, said hot-melt adhesive containing at least one polyester polyol in a concentration between 10% and 90%, possibly polyether polyol in a concentration between 0% through 50%, as well as at least polydisocyanate in a concentration by weight between 5% and 35%.
The connecting part produced in such a manner may form a kind of semi-finished product, which is preferably connected to additional synthetic materials within the context of further injection molding, thereby forming an end component, said additional synthetic materials bonding solidly with the foamed support part of the connecting part.
For a particularly efficient production of end components using the connecting parts produced in accordance with the method according to the invention, it is possible to advantageously proceed in such a way that the respective connecting part is separated from a plurality of connecting parts, which are produced such that they are joined together in the manner of a coil, in order that said connecting part can be further processed.
It is of particular advantage that the arrangement such that the respective support part laterally overlaps the insert part with a predefinable projection to form a seal, and thereby forming a kind of barrier, which protects the adhesive and/or hooking elements of the respective connecting part against clogging due to laterally penetrating dirt or dust particles, said connecting part being designed such that it is disk-shaped, for example.
The respective adhesive and/or hooking elements of the insert part may be formed in various ways in the manner known per se in the contact fastener technology, for example being molded, woven, multi-thread knitted, single-thread knitted or crinkled, wherein the elements may be designed such that they are hook-shaped, mushroom-shaped or loop-shaped. “Male” hooking elements may be molded elements having mushroom shapes made of polyamide or polypropylene, referred to as Mikroplast®. Woven textile elements having hooks may be elements made of polyamide or polypropylene, referred to as Klettostar®, and woven textile elements having mushroom-shaped elements, known as Pressotex®, likewise made of polyamide or polypropylene, may be provided, wherein the textile elements may also be provided with a flame retardant. “Female” hooking elements may be woven, multi-thread knitted, single-thread knitted or crinkled as fleece, loop fabric or velour, for example as Klettostar® fleece having loops as hooking elements. Likewise, instead of hooking elements, adhesive elements that function through adhesion, so-called “gecko elements”, may be provided, in which mushroom-shaped adhesive elements have planar head surfaces, which, together with planar mating surfaces, form an adhesive connection by means of van der Waals forces. Mushroom-shaped elements of this kind having widened heads as compared to the stems can be produced by means of molding processes, such as the process described in DE 198 28 856 C1, wherein, inter alia, synthetic materials such as polyamide 6, polyamide 6.6, polyamide 12, may be advantageously used. Elements provided for interlocking such as mushroom shapes without planar head surfaces or hooks, can be produced on a synthetic woven fabric or synthetic knitted fabric according to a method known in the prior art, as can be found, inter alia, from DE 10 2008 007 913 A1 for example, said fabric having projecting filaments, for example, in the form of pile threads of a single-knitted fabric. Hooks can be formed as hooking elements by cutting loops in this woven or knitted textile in two. In order to obtain mushroom heads, the pile threads, each of which has been cut through at the upper arch thereof, may be heated in such a way that said threads are deformed to produce mushroom heads.
The subject matter of the invention is also a connecting part, in particular a connecting part that has been produced using a method according to claim 9, and having the features of claim 10.
The invention is explained in greater detail below on the basis of the attached drawings.
Shown are:
As shown in
The hooking elements 18 extend as a circular surface area up to the projection 30 enclosing said elements, which projection extends along the outer circumference 32. The rear surface of the connecting part 28 facing away from the hooking elements 18 is not completely planar, as is most clearly evident from
As shown in
The end component 42, which contains the connecting part 28 as a component of a fastening system, with which an object such as a mat can be fastened to a floor structure by means of a contact fastener connection, has the shape of a round connection disk, the shape of which can be seen most clearly in
During the injection molding process, in which the connecting part 28 is connected to the upper side of the base body 44, a raised outer edge 56 is formed on the base body 44, as is shown more clearly in
The foamed synthetic material has a softening and melting temperature that is comparable to that of the synthetic material of the fastening part. In this way, the synthetic materials of the fastening part, together with the foamed synthetic material within the mold, form a common molten mass, after the cooling of which, the fastening part is connected to the foam in a firmly bonded manner. As such, the melting temperature of polyethylene falls within a range of approximately 110° through 135° Celsius, that of polypropylene within a range of 160° through 170° Celsius, and possible polyamide materials melt in a temperature range of between 170° and 260° Celsius. Polyethylene terephthalate (PET), on the other hand, has a very high melting point of 250° through 260° Celsius. By selecting the ideal pairings of materials with the melting temperatures thereof, it is possible to produce the firmly bonded connection after cooling via a common molten pool.
Number | Date | Country | Kind |
---|---|---|---|
10 2013 009 091.1 | May 2013 | DE | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/EP2014/001357 | 5/20/2014 | WO | 00 |