Patent Application
20120178321
The present invention relates to a method for producing a metallized fabric and to any type of fabric which can be obtained by applying such a method.
Metallized fabrics have many applications, in particular in the field of protective clothing and infrared reflector devices forming a heat shield.
In a context of energy conservation, infrared reflector devices such as curtains or blinds are highly advantageous insofar as they serve to limit heat losses in winter at the windows of premises, and to protect against heat in summer.
Existing solutions generally comprise the combination of a fabric support and a metal film, obtained by bonding.
The material thus prepared nevertheless has the drawback of being stiff and unpleasant to the touch.
The research of the inventor in this field has led him to investigate the advantage of applying the metallization technique, commonly used in the field of packaging, to coat fabrics.
It thus appeared that by treating certain types of fabric, before metallizing them, it was possible to obtain a novel product meeting the requisite specifications, in particular for the abovementioned applications.
It is therefore the object of the invention to provide a method for producing a metallized fabric that has, in particular, a pleasant texture and improved flexibility, while having thermal insulation properties.
It also relates, as novel products, to the fabrics obtained and to their applications.
The method for producing a metallized fabric of the invention is characterized in that it comprises the steps of:
In the case of the use of yarns having a weight of 50 decitex, the minimum is 30 filaments per yarn.
The use of fine strands serves to increase the luster of the substrate and thus to increase the luster of the metallized fabric. Preferably, a yarn having a weight of 50 decitex in the warp and filling directions and comprising 36 filaments is used.
The yarns used are flat, neither textured nor twisted.
The tests performed by the inventor have demonstrated that the use of a woven substrate, commonly called a fabric, is essential for achieving the desired flexibility.
Preferably, the woven substrate used, also called fabric, is based on synthetic fibers.
The woven substrate may be based on microfibers, that is to say fibers having more than 100 filaments per decitex, or fine strands, that is to say fibers close to 100 filaments per decitex.
The use of synthetic fibers serves to have a material that can at least partially melt, without burning. The use of microfibers or fine strands serves to preserve the flexibility of the fabric.
The weave of the yarns is dense and very tight. Preferably, the woven substrate comprises at least 42 warp yarns and 40 filling yarns per centimeter. Even more preferably, the woven substrate comprises 44 warp yarns and 41 filling yarns per centimeter.
The fabric washing step is also called desizing. In fact, in the usual fabric manufacturing techniques, a size deposit is applied to the yarns before they are woven. It is advantageous, particularly to preserve the flexibility of the product, to remove this size.
In order to obtain optimal desizing, it is possible to carry out two desizing passes, using caustic soda during one of the two passes.
Calendering is carried out in one or more successive passes on one or on both sides of the substrate, during which a compressive force is applied hot to the fabric.
One pass at 15 m/minute on each side at a temperature of 195° C. and with a force of 80 tonnes serves to obtain the desired effect.
The objective is to remove part of the air present in the fabric. It is found that a vacuum pressure of 2.3×10−3 (value higher than 2.4×10−2) is required for carrying out the metallization phase. The construction, that is to say the overall properties of the fabric, and the treatments carried out on the fabric make it possible to remain below this value.
The metallization phase takes place under vacuum at a rate of 420 m/minute, in particular, by metal vapor deposition. The metal deposited may, for example, be aluminum or silver.
It is found that the metallization machines generally used are unsuitable for metallizing large lengths of substrate. The vacuum becomes insufficient and the machine stalls.
It is necessary to use a specific method to remedy this. 200-meter strips of substrate are alternated and placed end to end with 500-meter strips of polyester film to form a continuous strip that is introduced into the metallization machine. This serves to prevent the machine stalling from by loss of vacuum. During the passage of the strips of polyester film, serving as primer, the travel speed is reduced to 180 meters/minute in order to restore the vacuum.
It may be necessary to make one or more preventive interruptions to restore the vacuum, during the passage of the strip, in order to prevent the machine from stalling.
As an alternative, it is possible to use a specific metallization machine, comprising a plurality of vacuum chambers.
A vacuum deposition test was performed. The fiber to be treated was in the form of a strip that entered the vacuum deposition apparatus. As the strip of fabric passed through the machine, measurements were taken of the pressure in the vacuum chamber. The following results were obtained:
The vacuum present at the start, before the passage of the fabric, had a pressure of 3.2×10−4 bar.
After the passage of 500 m of a strip of polyester film, a pressure of 4×10−4 bar was measured.
After the passage of 200 m of fabric after the primer, a pressure of 1×10−2 bar was measured.
After the passage of a second 500 m strip of polyester film, the vacuum was restored at 5.9×10−4 bar.
It was also found that the vacuum deposition apparatus malfunctioned when the vacuum became too low. As a consequence, in the case of a fabric based on textured microfiber, the aim is not to exceed a pressure of 4×10−2 bar. In the case of an untextured fine strand, the aim is not to exceed a pressure of 2.3×10−3 bar.
Tests were performed by the inventor, demonstrating the feasible nature of the inventive method. The characteristics of the fabric used are given below:
The warp yarn comprised 100% polyester. It was a flat semi-matte yarn comprising between 44 and 50 filaments per decitex for 43 yarns/cm.
The filling yarn also comprised 100% polyester. It was a flat semi-matte yarn comprising between 44 and 50 filaments per decitex for 43 yarns/cm.
The weave consisted of a taffeta-type toile.
The steps of the method are then carried out as follows:
Desizing takes place by washing at 85° C. in alkaline medium at pH 8/8.5 using surfactants and sequestering agents by a technique known to a person skilled in the art.
Calendering is then carried out at a rate of 15 meters/minute under 80 tonnes at a temperature of 195° C.
Finally, the vacuum metallization takes place at a maximum pressure of 2.3×10−3 bar.