Patent Application
20160141858
A method for manufacturing a plurality of arresters as a composite structure, an arrester, and a composite structure of arresters are provided.
An arrester may be used as a surge arrester. In the interior of the surge arrester, when a threshold voltage, the breakdown voltage, is exceeded, an arc-over occurs between two electrodes. The threshold voltage is referred to as the response DC voltage Urdc in the case of static or steady-state loading with a voltage rise of 100 V/s, and is referred to as the response surge voltage Urs in the case of dynamic loading with a voltage rise of 1 kV/μs. The arc is maintained by the feeding current as long as the electrical conditions for the arc exist.
Known arresters are problematic because of the complex and therefore costly manufacturing processes, which are also poorly suited to manufacturing arresters having unconventional properties, for example, particularly small arresters.
Embodiments of the invention provide a simple and thus economically implementable manufacturing method for an arrester, which is capable of generating qualitatively high-value arresters as well as unconventional arresters. Additional embodiments provide an improved arrester.
A method is provided for manufacturing a plurality of arresters as a composite structure. In one step, the method comprises providing a ceramic carrier having a plurality of holes, and providing two electrode bodies. In a subsequent step, the method comprises assembling the ceramic carrier and the two electrode bodies under a gas atmosphere into a base body, wherein the ceramic carrier is situated between the electrode bodies. Subsequently, the electrode bodies are soldered to the ceramic carrier. The resulting base body is separated into a plurality of gas-filled arresters.
The advantage of such a method is that the manufacture of arresters may be carried out considerably more efficiently, as each arrester does not have to be assembled individually. As a result, the handling of the individual components during the manufacturing process is facilitated. Furthermore, the manufacturing time is reduced. In addition, the method also enables the manufacture of arresters which are significantly smaller than in the case of arresters assembled separately, generally manually, or at least individually. Since the individual process steps are less susceptible to defects, the defect rate may also be reduced in comparison to manual methods, and the probability of a later failure of the arrester is therefore reduced.
A ceramic carrier has, for example, an edge length of 35 mm or more. The ceramic carrier preferably has a square or rectangular surface area. The surface area of the electrode body preferably corresponds to the surface area of the ceramic carrier.
According to one specific embodiment, the electrode bodies may have protuberances which engage with the holes of the ceramic carrier during assembly. The protuberances are preferably conical. This facilitates the introduction of the protuberances into the holes of the ceramic carrier. The protuberances may also be cylinder-shaped or dome-shaped.
The height of the protuberances is preferably less than half the height of the ceramic carrier. As a result, during the assembly of the electrode bodies and the ceramic carrier into a base body, gas-filled hollow spaces are formed in the holes of the ceramic carrier.
The gas atmosphere may, for example, contain hydrogen or a noble gas such as helium, neon, argon, krypton, xenon, or a mixture of these gases.
Before soldering the base body, a solder layer may be arranged between the ceramic carrier and each of the electrode bodies. The solder layer covers at least the area in which the holes are situated. The solder layer may, for example, be applied to the ceramic carrier in the form of a solder paste. In particular, the solder layer may be applied to both sides of the ceramic carrier. The solder layer may, for example, be applied by means of a screen printing method. By using a pre-soldered ceramic, the complexity during the manufacture of the base body may be decreased. In an additional specific embodiment, the solder layer may be a solder foil. The solder foil may have a plurality of holes. The size and arrangement of the holes in the solder foil may match those of the ceramic carrier.
According to one specific embodiment, the hollow spaces in the holes of the ceramic carrier are sealed via the solder when soldering the base body.
The base body may be divided into individual arresters during the separation via sawing, water jet cutting, or laser cutting.
The ceramic carrier may include a matrix made up of 15×15 holes. The holes may be situated in an area which has a square or rectangular surface. The surface on which the holes are arranged has, for example, an edge length of 15 mm or more. The holes preferably have equal distances from each other. The holes are preferably arranged in rows and columns. As a result, the separation of the base body is facilitated. In particular, it may be prevented that individual arresters are damaged during the separation of the base body. The ceramic carrier may also have a different number of holes. For example, the ceramic carrier may include a matrix made up of 10×20 or 15×20 holes.
In addition, a gas-filled arrester is provided which has a height of maximal 2 mm and electrode surfaces of maximal 1.2×1.2 mm2. The electrode surfaces correspond to the surface area of the arrester. The electrode surfaces may be square or rectangular.
The advantage of an arrester having such a ratio in dimensions is that it is particularly favorable due to its low material use. In addition, due to its small size, the arrester may be integrated into other components, for example, on a printed circuit board, in a particularly simple manner. In addition, since the individual process steps are less susceptible to defects, such an arrester is less susceptible to defects, and the probability of a later failure of the arrester is therefore reduced.
The present invention is explained below based on schematic figures.
The holes 4 are spaced at uniform distances from each other. The centers of the holes 4 have a spacing of 1.5±0.02 mm from each other. In total, 225 holes 4 are arranged in 15 rows and 15 columns. The holes 4 form a square pattern. The region in which the holes are arranged has a square area with an edge length of 21±0.05 mm.
The ceramic carrier 1 shown in
In total, two solder foils 12 are required for soldering a base body 3. The solder foil 12 has holes 13. The arrangement of the holes 13 of the solder foil 12 matches the arrangement of the holes 4 of the ceramic carrier 1. As a result, the holes 4 of the ceramic carrier 1 are not covered by the solder foil 12. The holes 13 of the solder foil also have a diameter of 0.65 mm. The height of the solder foil is 0.05 mm. The solder foil may contain silver. The solder foil is made up of, for example, a silver-copper eutectic or another solder material. For example, the solder foil 12 contains or is made up of the material Ag/Cu 72/28.
As shown in
The electrode body 2 contains or is made up of an electrically conductive material. For example, the electrode body 2 contains an iron-nickel alloy or copper or is made up of such a material.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2013 012 842.0 | Aug 2013 | DE | national |
This patent application is a national phase filing under section 371 of PCT/EP2014/066390, filed Jul. 30, 2014, which claims the priority of German patent application 10 2013 012 842.0, filed Aug. 2, 2013, each of which is incorporated herein by reference in its entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2014/066390 | 7/30/2014 | WO | 00 |