Method for producing a part using a deposition technique

Information

  • Patent Grant
  • 10213938
  • Patent Number
    10,213,938
  • Date Filed
    Monday, August 1, 2016
    8 years ago
  • Date Issued
    Tuesday, February 26, 2019
    5 years ago
Abstract
The invention relates to a method for producing a part using a deposition technique. A layered composite is built up in layers, the individual layers each containing particulate material and binding material as well as optionally, a treatment agent. The layers maintain a predetermined porosity. The layer composite is built up in the absence of hardening agent. Once construction is complete, the layer composite is hardened.
Description
FIELD OF THE INVENTION

This invention relates to a method for producing a part in layers using a deposition technique to build a layered composite containing the part made of a particulate matter. The part produced is either a casting mould or core. The method is also suitable for manufacturing a metal part from a particulate metallic material, such as a metal powder or a granular synthetic material.


BACKGROUND OF THE INVENTION

A conventional method for producing patterns and/or cores for metal casting utilizes a mixture of sand with a hardening binder filled in a box. A positive pattern for making the metal casting is embedded in the sand-binder mixture prior to its curing and is then removed again. This leaves an impression in the sand-binder mixture, which represents a negative pattern of the casting. The pattern of the sand-binder mixture is cured such that an adequately resistant mould of the negative pattern is produced.


Another alternative approach for manufacturing castings utilizes either a mixture of sand and binder also called Croning sand, which is a particulate matter made of moulding sand, such as quartz or zircon sand, pre-coated with a synthetic resin.


The bonding of the particulate matter is achieved by smelting the dry binder with applied heat. The attendant energy required for making the casting cores or moulds is thus not insignificant. Besides, the method requires use of relatively complex machines.


Cold curing techniques, such as the Cold Box method, are advantageous, in terms of energy savings for pattern fabrication. Here, the binder is cured chemically. This is done either with the addition of a cold-curing dual-component binder into the moulding sand, which remains workable for a limited time period before it hardens, or the pattern from the sand-binder mixture is alternatively flooded with a curing gas that cures the binder. The latter is referred to as a gas curing technique.


Conventional pattern making methods as described above then finish the positive pattern in an NC milling machine or NC lathe, which is especially time-consuming and expensive with increasing complexity of the desired metal part.


With a layered deposition technique, also called rapid prototyping in which the pattern making material is deposited in layers, it is possible to produce the castings, moulds, or other parts faster and more cost-effectively.


A known method for building a part in layers is described in U.S. Pat. No. 5,182,170 (Marcus et al). In this method, a layer of a binder-containing powder is deposited on a base. This layer is then subjected to a reactive gas atmosphere, which activates the binder. In this activating atmosphere, a predefined subarea of the layer is heated locally. The reactive gas and the added heat interact with the binder, initiating a localized chemical reaction of the binder leading to consolidation of the layer in the particular location. A laser, for example, could be the heat source. The powder deposition and subsequent activation and consolidation are carried out layer-by-layer until the part is finished.


Another layer deposition technique is known from the patents U.S. Pat. No. 5,204,055 and EP-0 431 924 B1 (Sachs et al). In this method, a layer of a particulate building material (e.g. ceramic or metal) is deposited. Through selective application of a self-curing binder in a predefined subarea of each layer, the building layer is bonded in the selected area and also bonded to the previously formed layer, before the next layer is deposited. This process is repeated in layers to produce a layered composite, in which the part to be made is contained within particulate matter is loose, since it has not been wetted with a binder. The binder can be applied as droplets through a printing technology device known as a Drop-On-Demand dispensing head, such as an inkjet print head, which is guided in a controlled manner by a predetermined program. The predefined subarea of each layer is consolidated at least partially, through application of heat radiation or by a chemical reaction of the binder, prior to deposition of the subsequent layer. Following building of the layered composite, post-treatment with applied heat can be conducted to fully consolidate all subareas forming the part.


A problem with the EP-0 431 924 B1 (Sachs) method relates to the binder's self-curing property, which can affect the cohesion between successive layers. Additionally, the binder in the Drop-On-Demand print head tends to cure and block the print head, making frequent cleaning of the print head necessary.


A rapid prototyping method described in DE 198 53 834.0 (Höchsmann et al.) involves depositing a layer of a particulate matter, the entire surface of which is then covered with a binder. Prior to depositing the next layer, a curing agent is applied to selected subareas of the layer treated with a binder, whereby the binder hardens in those selected subareas. The curing agent is, for instance, applied with a Drop-On-Demand print head. The curing agent does not harden without the binder, and thereby the print head nozzles do not get blocked with a hardening material. A layered composite comprised of many layers is accordingly built layer-by-layer.


Another rapid prototyping method is described in DE 197 23 892.0 (Höchsmann et al.), in which a layer of a packable particulate building material is first deposited on particles pre-coated with a curable binder. The building material could, for example, be Croning sand. A treatment agent is applied to selected subareas of each layer, which modifies the curing reactivity of the binder within the binder coating. Before deposition of the subsequent layer, energy with a given level of specific energy is then applied to this layer. This energy level is selected to match the modified curing reactivity of the binder achieved with the treatment agent, such that the binder cures in only the locations treated with the treatment agent. Each layer is accordingly cured before the next layer is added.


This invention fulfils the requirement to provide a rapid prototyping method for manufacturing parts, in particular casting moulds and cores, which is cost-effective and combines high manufacturing speed with fabrication precision.


According to the invention, in the method for producing a part in layers using a deposition technique by building a layered composite containing the part made of particulate matter comprised of particles of a prescribed particle size, the particulate matter is deposited layer-by-layer to form successive layers of a porous bulk, and in at least one predefined subarea of each layer, which subarea could vary from layer to layer, and prior to deposition of the subsequent layer a treatment agent in a free-flowing state is apportioned on each layer. The treatment fluid sets up a bonding process, in which the particles in the predefined subareas bond firmly to one another, through the binder contained either in the particulate matter or deposited thereon, in the presence of an initiator.


According to the invention, however, the layered composite is built in the absence of an initiator. This initiator is added only after the layered composite has been completed, such that the bonding process is executed only after completion of the layered composite.


For the known methods described above, appropriate actions are necessary to always ensure that each predefined subarea of each layer is consolidated at least partially through bonding of the binder immediately following deposition of a layer and prior to deposition of the next layer. During the course of the invention, however, it was surprisingly discovered that even partial consolidation of the predefined subarea may not be required, if an effort is made to prevent the free-flowing treatment agent from flowing and spreading out beyond or at least not far beyond the boundaries of the predefined subarea into the surrounding untreated particulate matter. This can be achieved especially through appropriate limitation of the treatment agent dosage by matching it to the volume of the predefined subarea as determined from its surface area, layer thickness, and particle size, and therewith the porosity of the particulate matter and its wettability depending on the flow characteristics of the treatment agent.


According to the invention, bonding of the particulate matter particles in the predefined subareas is also achieved with a binder. In the primary embodiment of the method, it could be the binder itself that functions as the treatment agent, in the form of a free-flowing powder or a liquid, apportioned over the predefined subareas.


In another embodiment of the method, the binder can be applied on the deposited layer before or after application of the treatment agent over the full surface, or the binder can be mixed with the particulate matter prior to its deposition, or at least the majority of the particulate matter particles are pre-coated with the binder. In this embodiment of the method, the treatment agent is selected such that it modifies the key binding property of the binder from a specific initial value or initial range of values, as determined prior to application of the treatment agent, to a markedly different value or range of values. Hereafter, this key specific property of the binder will be designated in terms of its reactivity. In this second embodiment of the method, the reaction effectiveness of the initiator is adjusted and set according to the modified reactivity of the binder, such that the unmodified binder reacts selectively and bonds either to the areas outside of the predefined subareas treated with the treatment agent, or to the predefined subareas in which the binder is modified through its contact with the treatment agent. The treatment agent could thus be a liquid like hydrochloric acid or such that soaks into the dry binder or alters its composition and thereby makes it more amenable for bonding through application of energy or a chemical reaction, compared with the untreated binder. For example, the smelting point or range could be lowered by a given amount with an appropriately selected treatment agent, such that when the temperature of the subsequently applied initiator lies between the smelting points of an unmodified and a modified binder, selective smelting of the modified binder can be induced. Another possibility is that the treatment agent is a chemical catalyst or an inhibitor, with which the modified binder's chemical reactivity for chemical bonding or a curing reaction with a chemical gas or fluid, depending on its concentration and temperature, is increased or reduced by the given amount.


In this second embodiment of the method, it is preferred to use a particulate matter pre-coated with the binder, such as Croning sand. This sand contains a minimal quantity of a binder enveloping each particle, making it essentially necessary to apply the treatment agent only in a quantity adequate to attain appropriate wetting of the sheathing at the reciprocal contact points of the particles.


The initiator could be an immaterial medium like energy in the form of heat or radiation. The initiator could also be a material medium like a liquid or gaseous heat transfer agent or chemical reaction agent. The binder is preferably cured chemically calling for the use of a heating or a chemical curing agent that leads to linkage of the binder. The initiator could also be an energy medium and a material liquid at the same time.


It is preferred to apply the treatment agent on to the particulate matter, deposited as a porous bulk with a particle size dependent porosity, such that the predetermined minimum porosity is maintained in the predefined subareas, which can then be exploited to finally flood the layered composite with a liquid or gaseous initiator. Such flooding of the layered composite could possibly be promoted and aided by evacuating the layered composite in an enclosed container prior to the flooding.


The method according to the invention has several advantages:


A bonding process and especially hardening of the binder can lead to shrinkage. If thermal bonding or hardening is implemented separately for each layer, stresses will be generated in the layered composite, which could lead to distortion or damage of the part. Since according to the invention, the bonding takes place at the end and not separately for each layer, if volumetric shrinkage occurs, the entire composite will shrink and become smaller overall, without generating any stresses. Any shrinkage can be compensated for through inclusion of an appropriate shrinkage mass when specifying the size of the relevant subarea for apportioned application of the treatment agent.


Since the bonding or curing is done after producing the whole layered composite and not after depositing each layer, no bonding step is required per layer and the fabrication time for each layer is accordingly reduced. Bonding of the layered composite requires just one single step at the end of the process, which also enhances the manufacturing speed.


Additional time is also saved, since there is no need to wait until each layer is bonded or particularly hardened.


Additionally, the final bonding of the layered composite can be executed at a location other than where the layered composite is built, which thereby necessitates waiting only for building of the next layered composite rather than waiting for the former one to harden. Accordingly, the layered composite is built preferably in a container to hold the layered composite together without allowing it to fall apart both during building and after it is finished, and also for transporting it to the bonding location. During the bonding process, the layered composite could thus remain in the same container in which it was built.


Another advantage of this method is that the deposition devices for applying the binder and/or treatment agent cannot become blocked by curing agents.


Another advantage of the method according to the invention lies therein that the building material outside of the predefined subareas can remain untreated, thereby allowing it to be reused easily after being removed from the bonded part. Besides, when the building material is used in an uncoated form, cleaning of the deposition devices utilized for the method becomes easy. Moreover, the method is more cost-effective, since the binder is deposited only on the spots where the part is subsequently formed.


The preferred building materials for a method to produce casting moulds and cores and for a deposition technique are typical sands such as quartz, silicate, chromite, olivine, or zircon sand. Any other appropriately packable particulate material, or a mixture of different sands can also be used.


For the above-described second embodiment of the method, it is preferred to use pretreated sand, such as Croning sand pre-coated with a binder.


Untreated materials have the advantage that they are more cost-effective than materials pre-treated with a binder.


The prescribed particle size, which is the size of the sand grains in the case of sand, lies preferably in the particle size range from 90 to 200 μm, and therein preferably in the range of 110 to 160 μm. It is also possible to use smaller or larger particles. Air movements, however, easily affect very small particles, thereby hampering homogeneous deposition of the particles. Small particles additionally reduce the porosity and impact the gas blast when pouring. On the contrary, extra large particles result in undesirable surficial graininess of the finished part. Typically, the median particle diameter or average particle size is approximately 140 μm. Normally not all particles are of the same size, but instead exhibit a certain size distribution. The preferred quartz sand has an average grain or particle size of 140 μm, with approximately 5% of the grains ranging from 180 to 200 μm in size, 59% from 125 to 180 μm, 30% lying between 90 and 125 μm, and 1% of the grains being smaller than 63 μm. This type of quartz sand, as a building material, is typically deposited at a bulk density of 1.32 t/m3.


The thickness of each layer of particulate material can vary. Thinner layers enable the part to be produced with a higher resolution of its design details. With very thin layers, however, reducing the layer thickness further does not result in any increase in the resolution, since process fluctuations limit the achievable resolution. Conversely, extremely thin layers result in lower fabrication speeds, since many layering steps become necessary. Thicker layers raise the achievable manufacturing speed, but all layer thicknesses are also not feasible. Very thick layers make it difficult to apply the treatment agent uniformly on the particulate matter, such that these work steps take longer and either the fabrication speed does not improve markedly with a greater layer thickness, or it may even drop. Besides, the application of thick layers results in poorer resolution of the part's design details. The preferred layer thickness is in the range of 0.15 to 0.30 mm, making it possible to not only attain a relatively high manufacturing speed, but also adequate cohesion between the successive layers and an appropriate resolution of the part's details.


The layer thickness can be varied during manufacturing of the part. Hence, to raise the fabrication speed thicker layers can be selected for areas of the part with fewer design details. In areas of the part with complicated and finer design details, the layer thickness can be lowered to enhance both the resolution and manufacturing precision.


The treatment agent is apportioned on to the previously deposited building material layer, such that the building material is just wetted, without any inhomogeneous distribution and local accumulation of the treatment agent, which would lower the performance of the part built according to this method.


The treatment agent and binder are applied in an amount such that the particle layer has a residual porosity, whereby the curing agent can penetrate into the part through these remaining pores during the subsequent curing stage.


The prescribed binder dosage is preferably selected to maintain a binder to building material weight ratio of less than 6%, and therein preferably between 2 and 3%. The amount of binder applied relative to the building material can vary from layer to layer.


It is preferred to select a similar weight ratio between the treatment agent and the building material.


If the part is a casting mould or core, the residual porosity of the bonded part that remains after hardening has the added effect that the gases formed under a subsequent casting process can escape. In such a situation, the binder and/or treatment agent are preferably apportioned such that, on the one hand, the pattern used to produce a casting out of a molten mass withstands the pressure of the molten mass, as long as it is not set, and on the other hand, at the point where the molten mass is partially solidified such that the casting is essentially stable, the binder and/or treatment agent should have almost vaporized. Once the casting has solidified, the pattern can be simply destroyed without any significant effort to remove it, as in a lost pattern process.


The binder and/or treatment agent could be applied in a fluid state.


The liquid binder and/or treatment agent can, for example, be applied on the particle layer as a spray. However, it is preferred to apply the fluid binder and/or treatment agent as liquid binder droplets with a prescribed droplet diameter. The prescribed diameter of the binder and/or treatment agent droplets lies preferably in the size range from 50 to 100 μm. For droplets with a diameter of less than about 5 μm, anti-gravitational frictional forces of the air cannot be neglected, thereby making it difficult to dependably deposit the droplets on to the building material. Conversely, large drops result in inhomogeneous distribution of the liquid in the building material layer.


In such situations, the binder and/or treatment agent should be fluid enough to enable the prescribed dosage to be applied on to the building material layer and such that they utilize the capillary action in the particle interstices for spreading out and wetting the particles. Accordingly, the viscosity of the liquid binder and/or treatment agent is preferably in the range of 1 to 25 mPas, when applied. Additionally, in order that coloured patterns could also be produced, the binder could contain a colouring agent, especially a pigment, or alternatively it could impart a specific colour to the powdered material. Use of several different coloured binders, each specifically apportioned like the colour mixing done in an inkjet system, it becomes possible to make fully coloured patterns or ones with colour schemes, for manufacturing applications calling for interesting display patterns or quite realistic replicas.


The operating temperature for implementing this method is determined by the material properties, for instance the viscosity and smelting point of the building material, binder, or treatment agent used. The method is conducted preferably at temperatures between 10 and 40° C. It is additionally preferred to use a binder and/or treatment agent that allow the method to be conducted at room temperature, to minimize unnecessary equipment complications. Hence, the viscosity of the binder and/or treatment agent lies preferably in the stated range of 1 to 25 mPas at a temperature of 20° C.


When applied, the binder and/or treatment agent could be at the ambient temperature or alternatively slightly above that, to reduce the viscosity for eased distribution of the binder and/or treatment agent into the layer. The ambient temperature refers to the temperature in the immediate vicinity of the location where the part is produced, for example, the atmospheric temperature in the close environs thereof.


Alternatively, to promote distribution of the binder and/or treatment agent in the layer, the layer itself could be heated each time prior to applying the binder and/or treatment agent.


Instead of as a fluid, the binder and/or treatment agent could optionally be applied also as a fine powder with binder and/or treatment agent particles of a prescribed size. As such, the particle size of the binder and/or treatment agent should be smaller than that of the building material, in order that the binder and/or treatment agent particles can wet or envelop the building material particles. Copying machines, for example, successfully deposit fine particulate materials with a toner on to paper, just as sublimation printers apply coloured powders on paper. In a copying machine, the toner is fixed through heating, although the toner clings to the paper on being applied even without being fixed.


The liquid or particulate binder and/or treatment agent, for instance, could be applied with the known airless technique, in which a pure binder and/or treatment agent are squeezed under high pressure through a nozzle.


Alternatively, the binder and/or treatment agent could be applied with the airbrushing technique, in which the binder and/or treatment agent are fed to a tip, where a fast moving air stream flowing by or alternatively a rotation technique sweeps it along. Alternatively, the treatment agent could be applied with an ultrasonic sprayer, in which a piezo-activated membrane generates droplets of the treatment agent, which can be targeted precisely with an air stream on to the predefined subarea of the building zone. With these techniques mentioned, the binder and/or treatment agent can be apportioned very precisely. The binder and/or treatment agent could alternatively be applied with a silk-screen printing technology or with a technique to spray on the binder and/or treatment agent through a mask. A particulate binder and/or treatment agent could alternatively be sprinkled on.


A Drop-On-Demand print head, operated for example through a bubble jet or a piezo technique, such as is known for an inkjet print head, is preferred for applying the fluid or particulate binder and/or treatment agent.


When applying a liquid binder and/or treatment agent, it is preferred to use a Drop-On-Demand print head for application at a droplet line density in the range of 300 to dpi.


The preferred material for the binder and/or treatment agent to be applied is at least one from the material group that includes sodium silicate, phenol resin, polyisocyanate, polyurethane, epoxy resin, furan resin, polyurethane polymer, peroxide, polyphenol resin, or resol ester.


A gas, a liquid, or a liquid vapour could be applied as the curing agent.


Once all the layers of the part to be produced are deposited and the binder and/or treatment agent have been applied, the liquid curing agent is flooded throughout the part. The curing agent penetrates through the residual pores of the part that remain after application of the binder and/or treatment agent. In this way, the binder and the binder treated with the treatment agent are cured.


The curing can be accelerated through heating of the fluid and/or the complete part. If a heated vapour is applied when using vapour curing, the heat of the vapour could promote and/or accelerate the curing.


The preferred curing agent for application is at least a gas from the group of gases that includes carbon dioxide, dimethylethylamine, triethylamine, sulphur dioxide, methylformiate, formaldehyde-dimethylacetate, or isocyanate.


The appropriate binder and/or treatment agent are accordingly selected such that the resulting material combination is one with which the binder can be cured.


The following table lists some of the known binder and curing agent combinations, which can also be applied according to the invention:











TABLE 1





Method
Binder
Curing Agent







CO2
Sodium silicate
Carbon dioxide


Cold Box Polyurethane
Phenol resin and
Dimethylethylamine



polyisocyanate
or triethylamine


Cold Box Plus
Polyurethane
Dimethylethylamine


SO2
Furan resin and peroxide
Sulphur dioxide


FRC
Polyurethane polymer
Sulphur dioxide



and peroxide


Pep Set
Polyphenol resin and
Methylformiate



an acid









The Cold Box Plus technique is normally conducted at a slightly elevated temperature of 65 to 70° C.


Nevertheless, other material combinations are feasible. When using an isocyanate as the binder, steam can be applied as the curing agent.


The method according to the invention is suited for producing different types of parts, such as design or construction models. It is preferred to apply the method to produce a casting mould or core, therein preferably a mould.





The preferred embodiment of the invention will now be explained in more detail with reference to the accompanying drawings, in which:



FIG. 1a is a schematic sectional representation of a part produced according to a preferred embodiment of the invention through the application of a binder and/or treatment agent;



FIG. 1b illustrates the fully completed part of FIG. 1a, and



FIG. 2 shows a device for implementing the method according to the invention during operation of the dispensing head.






FIG. 1a depicts a schematic sectional view of a part produced according to a preferred embodiment of the invention, such as a casting mould or core, through deposition of the binder, thereby illustrating the principle of the method. According to the method for building the part, a series of n layers are produced sequentially from s1 through sn. Accordingly, the first step involves depositing the first building layer s1 over the entire surface. In the next step, the binder and/or treatment agent are applied on a selected subarea t1 (hatched) of the first layer s1. These two steps are then repeated in sequence for the remaining layers s2 through sn. The subareas ti, tj for the different layers si, sj are generally different, but they at least overlap each other partially such that they are firmly bound to each other.


Once the binder and/or treatment agent have been applied on the last layer, the entire part is flooded with the curing agent and thereby hardened. As a helpful measure, the layered composite can be evacuated prior to application of the curing agent. Finally, the loose building material lying outside of the areas t1 to tn is removed, resulting in the finished part shown in FIG. 1b.


To produce a pattern with the method according to the invention, the building material is deposited as described above. Conversely, the binder and/or treatment agent are applied outside of the subareas ti, i=1 . . . n respectively. These areas outside ti are accordingly consolidated through final curing. Once the part has hardened, the loose particulate matter in the subareas ti, i=1 . . . n is removed, with the result that the remaining part reflects a hollow space in the shape of the body of FIG. 1b.


A device for producing parts according to a preferred embodiment of the invention is shown in FIG. 2. Such a device is comprised of the following components:


A vertically movable building platform 1,

    • A control mechanism,
    • A horizontally movable deposition device 2 steerable with the control mechanism, with which a packable building material can be deposited in layers on building platform 1 or on to a previous layer up to a prescribed layer thickness, and a horizontally movable dispensing head 3 arranged on a slide 42, which is steerable with the control mechanism and with which a liquid or particulate binder and/or treatment agent can be applied to a selected area of the layer.


The building material deposition device 2 is arranged with a long box 21, open above and below, designed for receiving and depositing the building material on to building platform 1 and on to the last deposited layer. In the vicinity of the lower open edge of box 21 facing building platform 1 is an outlet device 22 with an opening that can be adjustably opened or closed and which is arranged with coating blades. Deposition device 2 is movable at a settable velocity perpendicularly to the long direction of box 21, as depicted by axis y in FIG. 2, from one end of building platform 2 and back.


Slide 42 with dispensing head 3 for applying the binder is movable in a manner similar to the building material deposition device 2. Dispensing head 3 is movable perpendicularly, as depicted by axis x in FIG. 2, to the movement direction of slide 42, such that dispensing head 3 can be moved throughout the entire level above building platform 1.


This method is implemented with the device according to a preferred embodiment of the invention, as follows.


Deposition of Building Material Layers:


On commencement of the procedure, deposition device 2 with box 21 filled with the building material, as shown in FIG. 2, is positioned at the initial edge of building platform 1. The outlet device 22 of box 21 is opened to deposit a strip of the building material. At the same time deposition device 2 is driven to the opposing edge of building platform 1 at a constant velocity, such that all of building platform 1 is covered with a uniform layer of the building material. Box 21 is thereby moved over building platform 1 in such a manner as to use its lower edge to smooth out the building material layer already deposited. The vertical position of building platform 1 with respect to box 21 is set such that the building material layer attains a predefined desired thickness, following smoothing out of the layer by the blade located on the lower edge of box 21. The velocity and/or the degree of opening of the deposition device 22 is accordingly preferably selected and set by the control mechanism such that precisely the amount of building material necessary to obtain the predefined layer thickness lands on building platform 1. As soon as deposition device 2 reaches the opposing edge of building platform 1, the material feeding process is interrupted.


Application of the Binder and/or Treatment Agent:


Dispensing head 3, preferably a Drop-On-Demand dispensing head known from inkjet printers, is moved along a prescribed path over building platform 1, through movement of slide 42 relative to building platform 1 and through movement of dispensing head 3 relative to slide 42. Simultaneously, dispensing head 3 ejects the binder and/or treatment agent. This leads to creation of a pattern with the binder and/or treatment agent in the building material layer, which reflects the part's cross-section through the layer level.


The first layer is now complete and a second layer is to be deposited. Accordingly building platform 1 is moved a given distance downwards from the deposition device 2. A second layer of building material is then deposited and imparted a pattern with the binder and/or treatment agent.


Additional layers are made in the same way until a layered composite is fully built.


The layered composite is finally cured, preferably analogous to a conventional gas curing technique.


For example, following deposition of the last layer and application of the binder on to this layer, the layered composite is removed from the deposition device. The building platform can be removed along with the layered composite to provide support thereto. The layered composite is then transferred, possibly with the building platform, to a processing chamber. The processing chamber is then flooded with an appropriate gas to cure the layered composite.


Alternatively, the device for producing a part is integrated into a processing chamber, such that the layered composite can be cured directly therein.


The layers of the layered composite exhibit sufficient reciprocal cohesion, such that the uncured layered composite can be removed from the deposition device without problems.


However, the device can also have a building box in which the layers of the layered composite are produced such that the building box is filled up with the layers. The building box serves as a support means for the layered composite and reduces the danger of damage to the uncured layered composite, for instance during transport into a processing chamber for curing.

Claims
  • 1. A method for producing a part using a deposition technique in layers by building a layered composite containing the part from particulate matter comprised of particles of a prescribed particle size, the method comprising steps of: depositing the particulate matter layer-by-layer to form successive layers of a porous bulk in a build location, andselectively apportioning a treatment agent in a predefined subarea of the layer prior to deposition of a subsequent layer, wherein the treatment agent is apportioned in a free-flowing state for setting up a bonding process, in which the particles in the predefined subarea bond firmly to one another, through a binder contained either in the particulate matter or deposited thereon, in the presence of an initiator,moving the layered composite to a different location; andbonding the particulate matter in the different location;whereby the building of the layered composite is done in the absence of an initiator, and the bonding process is executed only after completion of the layered composite, through addition of such initiator.
  • 2. The method of claim 1, wherein the layered composite is in a same container during the building of the layered composite and during the bonding of the particulate matter.
  • 3. The method of claim 1, wherein the predefined subarea of the layer is different from a predefined subarea of the subsequent layer.
  • 4. The method of claim 1, wherein bonding of the particulate matter is in a single step at the different location.
  • 5. The method of claim 1, wherein the binder is in the particulate material.
  • 6. The method of claim 1, wherein the binder is in the treatment agent.
  • 7. The method of claim 1, wherein the initiator is added in the different location.
  • 8. The method of claim 1, wherein during the bonding of the layered composite, an additional layered composite is built in the build location.
  • 9. The method of claim 1, wherein the particulate material is deposited with a deposition device having a coating blade.
  • 10. The method of claim 9, wherein each layer of particulate material is deposited in a single pass of the deposition device over a building platform.
  • 11. The method of claim 1, wherein the treatment agent is dispensed using an inkjet printer.
  • 12. The method of claim 1, wherein loose particulate material is removed after the step of bonding.
  • 13. The method of claim 1, wherein the subareas of adjacent layers at least partially overlap and the layers are firmly bound to each other in the regions of overlap.
  • 14. The method of claim 13, wherein the layered composite is in a same container during the building of the layered composite and during the bonding of the particulate matter.
  • 15. The method of claim 1, wherein bonding of the particulate matter is in a single step at the different location;the initiator is added in the different location;the particulate material is deposited with a deposition device having a coating blade;each layer of particulate material is deposited in a single pass of the deposition device over a building platform;the treatment agent is dispensed using an inkjet printer;loose particulate material is removed after the step of bonding; andthe subareas of adjacent layers at least partially overlap and the layers are firmly bound to each other in the regions of overlap.
  • 16. The method of claim 15, wherein the layered composite is in a same container during the building of the layered composite and during the bonding of the particulate matter.
  • 17. The method of claim 16, wherein the predefined subarea of the layer is different from a predefined subarea of the subsequent layer.
  • 18. The method of claim 17, wherein during the bonding of the layered composite, an additional layered composite is built in the build location.
  • 19. The method of claim 18, wherein the binder is in the particulate material.
  • 20. The method of claim 19, wherein the binder is in the treatment agent.
CLAIM OF PRIORITY

This application is a continuation of U.S. patent application Ser. No. 14/292,961 filed on Jun. 2, 2014 which is a continuation of U.S. patent application Ser. No. 10/381,546 filed on Aug. 7, 2003. U.S. patent application Ser. No. 10/381,546 is a 371 of PCT Application Serial Number PCT/DE2000/003324 filed on Sep. 25, 2000. The contents of U.S. patent application Ser. No. 14/292,961, U.S. patent application Ser. No. 10/381,546, PCT Application PCT/DE2000/003324 are incorporated herein their entireties by reference.

US Referenced Citations (188)
Number Name Date Kind
2640629 Thomson et al. Jun 1953 A
2692142 Hunter Oct 1954 A
2857938 Wahl Oct 1958 A
3616969 Koizumi Nov 1971 A
3616972 Christy Nov 1971 A
3815527 Dobbins Jun 1974 A
3879339 Richard Apr 1975 A
3880687 Elmendorf et al. Apr 1975 A
3913503 Becker Oct 1975 A
4203674 Laleman May 1980 A
4239715 Pratt Dec 1980 A
4247508 Housholder Jan 1981 A
4279949 Esser Jul 1981 A
4369025 Von der Weid Jan 1983 A
4575330 Hull Mar 1986 A
4630755 Campbell Dec 1986 A
4665492 Masters May 1987 A
4669634 Leroux Jun 1987 A
4752352 Feygin Jun 1988 A
4863538 Deckard Aug 1989 A
4876294 Shriver et al. Oct 1989 A
4889433 Pratt Dec 1989 A
4938816 Beaman et al. Jul 1990 A
4944817 Bourell et al. Jul 1990 A
5017753 Deckard May 1991 A
5053090 Beaman et al. Oct 1991 A
5059266 Yamane et al. Oct 1991 A
5076869 Bourell et al. Dec 1991 A
5127037 Bynum Jun 1992 A
5132143 Deckard Jul 1992 A
5134569 Masters Jul 1992 A
5136515 Helinski Aug 1992 A
5140937 Yamane et al. Aug 1992 A
5147587 Marcus et al. Sep 1992 A
5149548 Yamane et al. Sep 1992 A
5155324 Deckard et al. Oct 1992 A
5156697 Bourell et al. Oct 1992 A
5182170 Marcus et al. Jan 1993 A
5204055 Sachs et al. Apr 1993 A
5216616 Masters Jun 1993 A
5221539 Pallerberg et al. Jun 1993 A
5248456 Evans et al. Sep 1993 A
5252264 Forderhase et al. Oct 1993 A
5284695 Barlow et al. Feb 1994 A
5296062 Bourell et al. Mar 1994 A
5316580 Deckard May 1994 A
5340656 Sachs et al. Aug 1994 A
5342919 Dickens, Jr. et al. Aug 1994 A
5352405 Beaman et al. Oct 1994 A
5354414 Feygin Oct 1994 A
5382308 Bourell et al. Jan 1995 A
5387380 Cima et al. Feb 1995 A
5431967 Manthiram et al. Jul 1995 A
5433520 Adams Jul 1995 A
5482659 Sauerhoefer Jan 1996 A
5490962 Cima et al. Jan 1996 A
5506607 Sanders, Jr. et al. Apr 1996 A
5518680 Cima et al. May 1996 A
5554330 Flannery et al. Sep 1996 A
5555176 Menhennett et al. Sep 1996 A
5573055 Melling et al. Nov 1996 A
5597589 Deckard Jan 1997 A
5601868 Gerhardt Feb 1997 A
5616294 Deckard Apr 1997 A
5639070 Deckard Jun 1997 A
5639402 Barlow et al. Jun 1997 A
5647931 Retallick et al. Jul 1997 A
5658412 Retallick et al. Aug 1997 A
5730925 Wilkening et al. Mar 1998 A
5753274 Wilkening et al. May 1998 A
5807437 Wilkening et al. Sep 1998 A
5851465 Bredt Dec 1998 A
5902441 Bredt et al. May 1999 A
5902537 Almquist et al. May 1999 A
5934343 Gaylo et al. Aug 1999 A
5943235 Earl et al. Aug 1999 A
5965170 Matsuoka et al. Oct 1999 A
6007318 Russell et al. Dec 1999 A
6036777 Sachs Mar 2000 A
6037389 Archibald et al. Mar 2000 A
6042774 Wilkening et al. Mar 2000 A
6048188 Hull et al. Apr 2000 A
6094994 Satake et al. Aug 2000 A
6116517 Heinzl et al. Sep 2000 A
6133353 Bui et al. Oct 2000 A
6146567 Sachs et al. Nov 2000 A
6147138 Hocksmann et al. Nov 2000 A
6155331 Langer et al. Dec 2000 A
6165406 Jang et al. Dec 2000 A
6193922 Ederer Feb 2001 B1
6217816 Tang Apr 2001 B1
6258170 Somekh et al. Jul 2001 B1
6259962 Gothait Jul 2001 B1
6286585 Twardowska et al. Sep 2001 B1
6305769 Thayer et al. Oct 2001 B1
6316060 Elvidge et al. Nov 2001 B1
6322728 Brodkin et al. Nov 2001 B1
6355196 Kotnis et al. Mar 2002 B1
6375874 Russell et al. Apr 2002 B1
6401001 Jang et al. Jun 2002 B1
6403002 Van der Geest Jun 2002 B1
6416850 Bredt et al. Jul 2002 B1
6423255 Hoechsmann et al. Jul 2002 B1
6436334 Hattori et al. Aug 2002 B1
6460979 Heinzl et al. Oct 2002 B1
6467525 Herreid et al. Oct 2002 B2
6476122 Leyden Nov 2002 B1
6500378 Smith Dec 2002 B1
6552130 Makino et al. Apr 2003 B1
6554600 Hofmann et al. Apr 2003 B1
6596224 Sachs et al. Jul 2003 B1
6610429 Bredt et al. Aug 2003 B2
6733528 Abe et al. May 2004 B2
6764636 Allanic et al. Jul 2004 B1
6830643 Hayes Dec 2004 B1
6838035 Ederer et al. Jan 2005 B1
7004222 Ederer et al. Feb 2006 B2
7137431 Ederer et al. Nov 2006 B2
7204684 Ederer et al. Apr 2007 B2
8741194 Ederer et al. Jun 2014 B1
20010050031 Bredt et al. Dec 2001 A1
20020026982 Bredt et al. Mar 2002 A1
20020111707 Li et al. Aug 2002 A1
20030083771 Schmidt May 2003 A1
20040012112 Davidson et al. Jan 2004 A1
20040025905 Ederer et al. Feb 2004 A1
20040026418 Ederer et al. Feb 2004 A1
20040035542 Ederer et al. Feb 2004 A1
20040038009 Leyden et al. Feb 2004 A1
20040056378 Bredt et al. Mar 2004 A1
20040094058 Kasperchik et al. May 2004 A1
20040145088 Patel et al. Jul 2004 A1
20040170765 Ederer et al. Sep 2004 A1
20050017394 Hochsmann et al. Jan 2005 A1
20050093194 Oriakhi et al. May 2005 A1
20050167872 Tsubaki et al. Aug 2005 A1
20060105102 Hochsmann et al. May 2006 A1
20060108090 Ederer et al. May 2006 A1
20060175346 Ederer et al. Aug 2006 A1
20060237159 Hochsmann Oct 2006 A1
20080001331 Ederer Jan 2008 A1
20080233302 Elsner Sep 2008 A1
20080237933 Hochsmann et al. Oct 2008 A1
20080260945 Ederer et al. Oct 2008 A1
20090261497 Ederer et al. Oct 2009 A1
20100212584 Ederer et al. Aug 2010 A1
20100243123 Ederer et al. Sep 2010 A1
20100244301 Ederer et al. Sep 2010 A1
20100272519 Ederer et al. Oct 2010 A1
20100291314 Kashani-Shirazi Nov 2010 A1
20110223437 Ederer et al. Sep 2011 A1
20110308755 Hochsmann Dec 2011 A1
20120094026 Ederer et al. Apr 2012 A1
20120097258 Hartmann Apr 2012 A1
20120113439 Ederer May 2012 A1
20120291701 Grasegger et al. Nov 2012 A1
20130000549 Hartmann et al. Jan 2013 A1
20130004610 Hartmann et al. Jan 2013 A1
20130026680 Ederer et al. Jan 2013 A1
20130029001 Gunther et al. Jan 2013 A1
20130092082 Ederer et al. Apr 2013 A1
20130199444 Hartmann Aug 2013 A1
20130234355 Hartmann et al. Sep 2013 A1
20130302575 Mogele et al. Nov 2013 A1
20130313757 Kashani-Shirazi Nov 2013 A1
20140202381 Ederer et al. Jul 2014 A1
20140212677 Gnuchtel et al. Jul 2014 A1
20140227123 Gunster Aug 2014 A1
20140306379 Hartmann et al. Oct 2014 A1
20150042018 Gunther et al. Feb 2015 A1
20150069659 Hartmann Mar 2015 A1
20150110910 Hartmann et al. Apr 2015 A1
20150165574 Ederer et al. Jun 2015 A1
20150210822 Ederer et al. Jul 2015 A1
20150224718 Ederer et al. Aug 2015 A1
20150266238 Ederer et al. Sep 2015 A1
20150273572 Ederer et al. Oct 2015 A1
20150290881 Ederer et al. Oct 2015 A1
20150321423 Gunther Nov 2015 A1
20150375418 Hartmann Dec 2015 A1
20150375419 Gunther et al. Dec 2015 A1
20160001507 Hartmann et al. Jan 2016 A1
20160052165 Hartmann Feb 2016 A1
20160052166 Hartmann Feb 2016 A1
20160257073 Mogele et al. Mar 2016 A1
20160107386 Hartmann et al. Apr 2016 A1
20160114533 Grasegger et al. Apr 2016 A1
20160263828 Ederer et al. Sep 2016 A1
Foreign Referenced Citations (54)
Number Date Country
720255 May 2000 AU
4300478 Aug 1994 DE
4325573 Feb 1995 DE
29506204.5 Apr 1995 DE
4400523 Jul 1995 DE
4440397 Sep 1995 DE
29701279 Jan 1997 DE
19545167 Jun 1997 DE
19511772 Sep 1997 DE
19723892 Sep 1998 DE
19846478 Apr 2000 DE
10047614 Apr 2002 DE
10216013 Apr 2002 DE
19853834 May 2002 DE
10117875 Jan 2003 DE
69634921 Dec 2005 DE
0711213 May 1995 EP
0361847 Nov 1995 EP
0431924 Jan 1996 EP
0739666 Oct 1996 EP
0688262 Jun 1999 EP
0734842 Aug 1999 EP
1163999 May 2001 EP
0968776 Oct 2002 EP
1415792 May 2004 EP
1442870 Aug 2004 EP
2790418 Sep 2000 FR
2382798 Jun 2003 GB
9518715 Jul 1995 WO
9605038 Feb 1996 WO
2000003324 Jan 2000 WO
2000021736 Apr 2000 WO
0051809 Sep 2000 WO
2001026885 Apr 2001 WO
2001072502 Apr 2001 WO
2001034371 May 2001 WO
2002026419 Apr 2002 WO
2002026420 Apr 2002 WO
2002026478 Apr 2002 WO
2002028568 Apr 2002 WO
2002064353 Aug 2002 WO
2002064364 Aug 2002 WO
2002083323 Oct 2002 WO
03016067 Feb 2003 WO
2003016030 Feb 2003 WO
2003086726 Oct 2003 WO
2003097518 Nov 2003 WO
2003103932 Dec 2003 WO
2004010907 Feb 2004 WO
2004110719 Dec 2004 WO
2004112988 Dec 2004 WO
2005080010 Sep 2005 WO
2005082603 Sep 2005 WO
20050113219 Dec 2005 WO
Non-Patent Literature Citations (37)
Entry
US 4,937,420, 06/1990, Deckard (withdrawn)
Cima et al., “Computer-derived Microstructures by 3D Printing: Bio- and Structural Materials,” SFF Symposium, Austin, TX, 1994.
Copending National Phase Application, WO 03/097518, Jun. 24, 2005(Published as 2006/0176346).
Copending National Phase Application, WO 05/113219, Dec. 1, 2005 (Published as 2008/0233302).
Copending U.S. Appl. No. 10/866,205, (Published as 2005/0017394), Jun. 11, 2004 (Published as 2008/02379331).
Copending U.S. Appl. No. 11/767,778, filed Jun. 25, 2007 (Published as 2008-0001331), Jun. 25, 2007.
Copending U.S. Appl. No. 11/320,050 (corresponds with PCT WO 02/26420), (U.S. Pat. No. 7,137,431),Dec. 28, 2005.
Machine Translation of PCT/DE07/01372, (Feb. 2008).
Co-pending Office Action of U.S. Appl. No. 12/377,137, filed Jun. 18, 2010.
International Search Report, PCT/DE00/03324, dated May 6, 2001.
International Search Report, PCT/DE01/03662, dated Jan. 3, 2002.
International Search Report, PCT/DE01/03661, dated Feb. 28, 2002.
International Search Report, PCT/DE01/01103, dated Sep. 30, 2002.
Copending National Phase Application, WO 02/28568, dated Apr. 11, 2002 with English Translation.
Copending National Phase Application, WO 02/26478, dated Apr. 4, 2002 with English Translation.
Copending National Phase Application, WO 02/26420, dated Apr. 4, 2002 with English Translation.
Copending National Phase Application, WO 02/083323, dated Oct. 24, 2001 with Enalish Translation.
Copending National Phase Application, WO 03/103932, dated Dec. 18, 2003.
Copending National Phase Application, WO 03/086726, dated Oct. 17, 2005.
Copending National Phase Application, WO 04/112988, dated Dec. 8, 2005.
Copending National Phase Application, WO 05/080010, dated Sep. 1, 2005.
EOS Operating Manual for Laser Sintering Machine with Brief Summary, (2005).
Sachs et al., “Three Dimensional Printing: Rapid Tooling and Prototypes Directly from a CAD Model”, Massachusetts Institute of Technology, pp. 143-151, Jan. 1990.
Sachs et al., “Three-Dimensional Printing: Rapid Tooling and Prototypes Directly from a CAD Model”, Massachusetts Institute of Technology, pp. 131-136, (1990).
Williams, “Feasibility Study of Investment Casting Pattern Design by Means of Three Dimensional Printing”, Department of Mechanical Engineering, pp. 2-15, Jun. 5, 1989.
EOS Operating Manual for Laser Sintering Machine, Part 1 with Brief Summary, Feb. 22, 2005.
EOS Operating Manual for Laser Sintering Machine, Part 2 with Brief Summary, Feb. 22, 2005.
Gephart, Rapid Prototyping, pp. 118-119, 1996.
International Search Report, WO 04/110719, dated Jan. 11, 2005.
Marcus et al., Solid Freeform Fabrication Proceedings, Nov. 1993.
Opposition of Patent No. DE10047614, Jun. 25, 2003.
Opposition to European Patent No. 1322458 B1, Jan. 19, 2005.
Jacobs et al., 2005 SME Technical Paper, title “Are QuickCast Patterns Suitable for Limited Production?”.
Feature Article—Rapid Tooling—Cast Resin and Sprayed Metal Tooling by Joel Segal, Apr. 2000.
Copending National Phase Application, WO 05/113219, Dec. 1, 2005.
Marcus, et al., Solid Freeform Fabrication Proceedings, Sep. 1995, p. 130-33.
US 4,937,420, 6/1990, Deckard (withdrawn).
Related Publications (1)
Number Date Country
20170136524 A1 May 2017 US
Continuations (2)
Number Date Country
Parent 14292961 Jun 2014 US
Child 15225381 US
Parent 10381546 US
Child 14292961 US