Patent Application
20170001358
The invention relates to a method for manufacturing an insulating bar for composite profiles, wherein the insulating bar is made from a thermoplastic plastics material and has a strip-like base body and, integrally formed on the opposite longitudinal edges thereof, connection strips.
Insulating bars of this kind are used during the manufacture of composite profiles for a shear-resistant mechanical connection and thermal insulation of metal profiles that are to be arranged on the outside and the inside, as are used in particular for manufacturing window frames, doorframes, facade elements and similar.
Insulating bars of this kind are known in many forms, for example among others from DE 32 36 357 A1, and depending on the spacing required between the metal profiles of the composite profile are made to appropriate widths.
Conventionally, the insulating bars have a substantially planar base body and are manufactured together with the connection strips in the course of extrusion, by means of a tool that is adapted to the cross sectional geometry.
More recently, it has been proposed to use insulating bars having a structured base body in order to improve the heat insulation without reducing the static strength of the composite profile (cf. for example EP 2 497 888 A2).
For improving the heat insulating properties of the composite profiles that are formed in this way, it has been proposed, among others in EP 2 497 888 A2, that the base body should be provided with a corrugated structure extending transversely as seen in the longitudinal direction of the insulating bar. The improvement in heat insulation that is achievable thereby results on the one hand from the fact that the corrugated structure increases the length of the path that the insulating bar provides for heat conduction from one metal profile to the other. On the other hand, the corrugated structure improves the rigidity of the insulating bar such that, with the same mechanical properties, smaller wall thicknesses are possible in the base body of the insulating bar, such that the cross section available in the insulating bar for heat conduction can additionally be reduced.
Moreover, losses due to both heat radiation and heat convection are expected to be lower as a result of using insulating bars of this kind.
In principle, this kind of insulating bar can be formed by machining out of an insulating bar that is manufactured with a substantially planar base body, or indeed can in principle be manufactured with the final structure by the method of injection moulding.
However, machining is not only time-consuming but also demands a high consumption of materials. The method of injection moulding, on the other hand, finds its limits very quickly, since the insulating bars are conventionally manufactured by the metre, for example to a length of 6 m. The injection moulds needed for this are not only extremely expensive but are also problematic, at the required insulating bar lengths, as regards sufficiently uniform filling of the moulds.
Further, a combined method based on injection moulding and extrusion is known (WO 2007/128787 A1) by means of which profiled elongate component parts can be made. With the method described there, it proves disadvantageous that the moulds that are needed for application to products described in this application require a very great longitudinal extent and are thus complex and disproportionately expensive. Admittedly, the structures described could be produced by this method in theory, but only with additional work steps that demand forming subsequent to the procedure of filling the mould during cooling of the product, or machining.
In insulating bars, it is important to keep within a small tolerance in the dimensions of the connection strips, since during processing to give composite profiles the connection strips have to be pushed into receptacles of complementary shape in the metal profiles. In order to ensure that the insulating bars are connected to the metal profiles as well as possible and in particular in shear-resistant manner, the dimensions of the cross section of the receptacles preferably differ only slightly from those of the connection strips. For this reason, a manufacturing method for the structured insulating bars must in particular also provide the assurance that it is possible to keep within the tolerance stipulations for the connection strips.
In order to take account of the different widths of the insulating bars, conventionally separate extrusion tools having extrusion nozzles of a specific construction are required, for each width and furthermore for each required alignment of the connection strips in relation to the base body, and for this reason a corresponding tool has first to be provided when there is a switch-over in production. This is not only associated with costs but also demands corresponding lead times for any required manufacture of the tools.
Frequently, insulating bars having connection strips that are arranged offset to the base body are needed, in particular in order to increase the path for heat conduction while maintaining the same overall size. For these variants too, separate extrusion tools are conventionally required.
It is the object of the invention to propose a method by means of which the known insulating bars may be manufactured economically with the respectively required dimensions and cross sectional shapes, in particular also having a corrugated structure of the base body.
This object is achieved according to the invention by a method as defined in claim 1.
In the first step, the strip-like extrudate is continuously produced, by means of extrusion or pultrusion of the plastics material, with a substantially rectangular cross section. Specific contours that are required for the insulating bar to be produced, including the connection strips, are produced in subsequent steps by forming of the strip-like extrudate.
By comparison with methods of the prior art, the invention does not follow the route of extrusion or pultrusion using an individual extrusion/pultrusion tool in order to produce an insulating bar in its finished cross sectional geometry, or indeed the even more complex route of the injection moulding method, but produces the required geometry of the cross section of the insulating bar in a step downstream of the extrusion/pultrusion.
In this way, first the not inconsiderable costs of specifically constructed extrusion/pultrusion tools or injection moulding tools are saved, since nozzles of simple shape having a rectangular cross section are sufficient for production of the strip-like extrudates. The cross sectional geometry that differs from a rectangular shape and which is required in individual cases is then produced by forming, subsequent to the extrusion/pultrusion procedure.
According to the invention, the insulating bar may be produced from the initially substantially planar strip-like extrudate by forming using tools that are not only usable for a single cross section but are suitable for producing various cross sectional geometries.
As it comes out of the nozzle, the plastics material is in the form of a molten extrudate which, on cooling, results in the extrudate that is handlable as a strip.
For the forming, the strip-like extrudate is supplied to a forming tool directly or indeed at a predetermined temporal/spatial interval after coming out of the nozzle, wherein the heat content of the extrudate is preferably deliberately utilised.
Preferably, during further processing of the strip-like extrudate a kind of calibration of the extrudate in respect of its thickness is first carried out. For this, a so-called calender is particularly suitable.
During calibration of the extrudate, the surfaces of the calibration tool, for example the surfaces of the rolls of the calender, are cooled to remove from the plastics material of the strip-like extrudate, in a controlled manner, sufficient heat to simplify handling of the planar sheet element that is then obtained, after it leaves the calibration tool.
For example, the surfaces of the calibration tool may be cooled to approximately 100° C. up to approximately 180° C., preferably approximately 120° C. up to approximately 150° C.
As the cooling agent, water having a temperature of approximately 15° C. may be used.
The strip-like extrudate may either pass through the calender in one plane, in which case a calender having two rolls is frequently sufficient for the calibration sought, or as an alternative it may be deflected about an angle, for example 90°, for which calenders having three rolls are preferably used.
After exit from the calender, a dimensionally stable but still plastically deformable planar sheet element is obtained, whereof the temperature is preferably above the heat deflection temperature under load (measured according to DIN EN ISO 75 under a load of 1.8 kPa).
Depending on the throughput rate of the strip-like extrudate or the planar sheet element that is produced therefrom and the heat content that is still present on entry into the (first) forming tool, cooling during the forming may also be advisable.
If a plurality of method steps are required for the forming, it may be advantageous to supply energy to bring the temperature of the plastics material back into a range that is preferred for the forming.
Forming downstream of the calender is carried out at a temperature that, in the case of (partially) crystalline plastics materials, is geared to the crystallite melting point. The term “crystallite melting point” is understood, in the context of the present invention, to mean the temperature at which the curve in a DSC measurement according to DIN EN ISO 11357-3 reaches the (first) endothermic peak.
During forming, the plastics material is preferably at a temperature in the region of approximately 30° C. below the crystallite melting point or a higher temperature.
Preferably, during forming the temperature is limited to a value of up to approximately 30° C. above the crystallite melting point.
Further preferably, during forming the plastics material is at a temperature in the range approximately ±25° C. either side of the crystallite melting point.
When amorphous plastics materials are used, a preferred temperature during forming is approximately 30° C. above the softening point (DIN EN ISO 306 VST A120) or higher.
Preferably, in this case the temperature during forming is limited to a value of up to approximately 60° C. above the softening point.
If the temperature of the plastics material before a forming step is more than approximately 30° C. above the crystallite melting point or higher than 60° C. above the softening point in the case of amorphous plastics materials, the forming tools are preferably cooled as described above.
If the temperature of the plastics material is in the preferred range of approximately 30° C. below to approximately 30° C. above the crystallite melting point or approximately 30° C. to approximately 60° C. above the softening point, the forming tool is preferably heated to a temperature of approximately 50° C. to approximately 80° C.
According to the invention, it is also possible for two or more insulating bars to be produced at the same time in a parallel arrangement, wherein the insulating bars are first still connected to one another by way of plastics material. Separation of the at first still joined insulating bars is performed in a subsequent step. Separation of the insulating bars may also in particular be performed after complete forming and stamping of all the features, including the corrugated structure.
Severing of the insulating bar arrangement into individual insulating bars, which may be required, is preferably performed at a temperature of the plastics material below the heat deflection temperature under load and further preferably below the maximum long-term service temperature of the plastics material or lower. The maximum long-term service temperature is determined according to DIN 53476.
According to the invention, it is possible to produce insulating bars having different bar geometries in parallel, wherein the different bar geometries may include not only different bar widths and the stamping of different corrugated structures, but also different cross sections of the connection strips.
According to a variant of the method according to the invention, in a first step the base body and the connection strips may be produced from the planar sheet element. Here, the connection strips may be produced in the plane of the base body.
In the event that the connection strips are to be arranged offset to the base body, this geometry may already be obtained during forming of the connection strips or in a subsequent step within the scope of a further forming.
Where appropriate, the calender may also be operated with contoured rolls such that simple cross sectional geometries that differ from a planar shape may already be produced by the calender. For example, in this way, in the simplest case the complete cross sectional geometry of the base body and the connection strips may be achieved. This also applies to insulating bars having connection strips that are arranged offset.
If, in addition to the connection strips, further features of the cross sectional geometry are required, then during forming the base body that is constructed between the connection strips may also be provided with raised portions and recesses such that insulating bars having the corrugated structure described in the introduction are also manufacturable according to the invention.
In that case, if desired, the raised portions and recesses are produced thereafter in a separate forming step. During this separate forming step, the connection strips, which have already been given their finished shape, are preferably protected to prevent their being deformed.
According to a further variant, the planar sheet element may be formed at the same time as the raised portions and recesses and the connection strips are produced. Optionally, if an offset arrangement of the connection strips is required, the connection strips may be given an offset geometry, or the connection strips may be offset in a subsequent forming step.
According to another variant, first the raised portions and recesses of the base body are produced during forming of the planar sheet element, and the connection strips are produced thereafter, in a separate forming step. In this variant too, the connection strips may be produced such that they are offset in in one step or the offsetting may be performed in a separate, where appropriate subsequent step.
As already mentioned, the method according to the invention in particular provides the possibility of producing a plurality of insulating bars at the same time. For this purpose, a strip-like extrudate that corresponds in its width to a plurality of parallel insulating bar geometries is produced. The plurality of insulating bar geometries are produced at the same time.
In particular, the present invention allows the insulating bar to be manufactured with its base body and the connection strips adjoining the latter having a dimensional accuracy that makes processing of the insulating bars with metal profiles to give a composite profile considerably simpler.
Surprisingly, the method according to the invention succeeds on the one hand in providing a sufficiently pronounced structure in the base body of the insulating bars, in particular also having raised portions and recesses, with a complexity that is economically acceptable, but at the same time in ensuring the dimensional accuracy of the geometry of the connection strips, with the result that processing of the insulating bars to give composite profiles is successful without further measures, in particular also without an after-treatment of the connection strips.
According to the invention, a plurality of insulating bars that are produced in parallel may also be separated from one another in the same step in which the bar geometry is produced. In that case, the forming tool at the same time includes the severing device for separating the individual bars.
Furthermore, insulating bars that have been manufactured according to the invention can be produced with receiving grooves in the connection strips, into which so-called sealing wires made from plastics material may be introduced. By means of these sealing wires, the shear-resistant nature of the finished composite profiles can additionally be ensured.
According to a preferred embodiment of the method according to the invention, during the forming process alternating raised portions and recesses are produced at regular intervals, as seen in the longitudinal direction of the base body.
Further preferably, the raised portions and recesses are produced during the forming process such that they extend substantially over the entire width of the base body. In this way, optimum heat insulation can be achieved using the insulating bars that are manufactured according to the invention.
Further preferably, the raised portions and recesses are oriented substantially perpendicular to the longitudinal direction of the insulating bar, also called the corrugated structure for short. In this way, a maximum effect of stiffening the insulating bars is achieved in relation to forces acting perpendicular to the plane of the base body. Moreover, stabilisation against so-called shunting is achieved, with the result that, if forces of different magnitude act on the two connection strips in the longitudinal direction of the insulating bar, deformation of the insulating bar is countered.
Further preferably, the raised portions and recesses extend at an angle of in particular approximately 30° to approximately 90° in relation to the longitudinal direction of the insulating bar, and stiffen the insulating bars in a manner similar to a framework.
Preferably, production of the raised portions and recesses provides a structure in which surface regions that are attributable to the raised portions and recesses deviate from the centre plane of the base body of the insulating bar by approximately 0.5 times to approximately twice the thickness of the base body. Within these limits, on the one hand a marked effect is achieved as regards the improvement in heat insulation, the improvement in the mechanical strength and hence the possibility of saving on materials, and on the other hand the plastics material is not put under excessive load during the forming process, so the long-term load-bearing capacity of the insulating bars remains ensured. Further preferably, the deviation of the raised portions and recesses from the centre plane is approximately 0.7 times to approximately 1.3 times the thickness of the base body.
As the thermoplastic plastics material for the insulating bars, there is preferably used a material that is selected from polyamides (PA), in particular PA 12 and PA 6,6, polypropylene (PP), acrylonitrile butadiene styrene copolymers (ABS), polyphenylene ether (PPE), syndiotactic polystyrene (sPS), polyvinyl chloride (PVC), polyesters, in particular polyethylene terephthalate (PET) and polybutylene terephthalate (PBT), polyketones, thermoplastic polyurethanes (TPU) and blends of the above-mentioned polymer materials.
For these preferred plastics materials, the crystallite melting points or softening points and the maximum long-term service temperatures are approximately as follows:
The plastics material may be present in the insulating bar as a compact, substantially pore-free material. In this case, the porosity or pore volume is below approximately 3 vol %.
In many cases, it is possible to achieve an improvement in the heat insulation properties of the insulating bars without the mechanical resistance of the insulating bars being insufficient if the plastics material is present as a porous material in at least a partial region of the insulating bar, in particular in the base body. Preferably, in this case the pore volume is approximately 5 to approximately 30 vol %, further preferably approximately 5 to approximately 25 vol %, and most preferably approximately 5 to approximately 20 vol %.
Preferably, the porous plastics material of the insulating bar has an average pore size of approximately 5 μm to approximately 150 μm, further preferably approximately 20 μm to approximately 140 μm.
The porosity of the plastics material of the insulating bar may be achieved by the use of a porous starting material, or indeed be produced only on heating the insulating bar blank to the forming temperature.
Further preferably, the thermoplastic plastics material may contain one or more additives, in particular selected from glass fibres, mineral fibres, plastics fibres, in particular aramid fibres, carbon fibres, hollow glass spheres, and fire retardants, in particular magnesium hydroxide, aluminium hydroxide, melamine derivatives, red phosphorus, inorganic and organic phosphates, and blowing and expansion agents.
Fibrous fillers have a particular significance as additives. These may be embedded in different forms in the plastics materials and the insulating bars that are produced therefrom. Particularly preferred are short, long and continuous fibres, which can be arranged on the one hand in an even distribution in the insulating bars, or at least in the base body, or on the other hand as a two-dimensional flat fibre structure, in particular in the form of felts, fibre mats, nonwovens and woven fabrics. Moreover, the fibrous fillers may also be integrated in the insulating profiles in the form of rovings and fibre strands.
Particularly preferably, the fibrous fillers are embedded in the plastics material with a preferential direction, for example parallel and/or perpendicular to the longitudinal direction of the insulating bar.
Fibrous fillers can be used not only in compact, non-porous plastics materials, but also in the above-described porous materials, in which case relatively large pore volumes can be realised even in the case of insulating bars that are intended to take up relatively high forces.
Further preferably, in the method according to the invention a thermoplastic plastics material that also includes a commercially available so-called impact modifier is used.
Preferably, the tool that is used for forming the base body undergoes a temperature control, wherein the temperature of the tool is in particular kept at a temperature that is approximately 120° C. or less, further preferably approximately 100° C. or less, most preferably approximately 90° C. or less.
Further preferably, the tool is kept constantly at a temperature in the range of approximately 50° C. to approximately 120° C., preferably in the range of approximately 50° C. to 80° C.
For example, when polyamide 6,6 having a glass fibre content of 25 weight % is processed, a tool temperature of approximately 50° C. to approximately 80° C. is suitable.
The forming itself may be carried out as a thermoforming method, as compressed air forming or as vacuum forming.
During the forming there is preferably used a stamping tool, in particular in the form of a stamping die, a stamping wheel, a stamping roller or a multiple-part, in particular chain-shaped, stamping tool.
The forming may be carried out with a sheet element that is conveyed in the longitudinal direction intermittently or indeed continuously, wherein if a stamping die is used a continuous method may likewise be implemented, in particular by moving the stamping die along with the insulating bar as the latter passes through the forming device.
These and further advantages of the present invention are described in further detail below with reference to the drawings and the exemplary embodiments.
Individually, in the drawings:
The cross sections of the connection strips 14, 16 are adapted to the cross sections of the corresponding receptacles in the metal profiles (not shown) such that, in a so-called “rolling” step, only a slight deformation of the receptacles in the metal parts is required in order for example to make a shear-resistant connection between the insulating bar and the respective metal profile.
Accordingly, it is of considerable significance that the connection strips 14, 16 have a defined geometry with only small tolerances. This is true in particular of processing insulating bars to give relatively large window, door or facade elements in which sections of the insulating bars and the corresponding metal profiles have to be installed with lengths of 1 to 2 m or indeed more.
The strip-like base body 12 has a structure obtained by the method according to the invention, which will be described in further detail below, having alternating raised portions 26 and recesses 28. Because of the structure of the strip-like base body 12 with raised portions 26 and recesses 28, the wall thickness of the strip-like base body 12 may be made smaller than in conventional insulating bars, since the production of the raised portions 26 and recesses 28 allows an additional improvement in the mechanical properties of the insulating bar 10 as a whole to be achieved. This results not only in a saving on materials when the insulating bars 10 are manufactured but additionally in an increase in the thermal resistance and hence in an improvement in the heat insulation of the composite profiles that are obtained using the insulating bar 10 manufactured according to the invention.
In
In illustrations X1 to X4, different examples of the arrangement of reinforcing fibres in the plastics material of the base body 12 are illustrated. In illustration X5, a porous structure is schematically shown.
Illustration X1 shows a fibre-reinforced plastics material in which the fibres have been oriented parallel and perpendicular to the longitudinal direction of the insulating bar. The reinforcing fibres may be embedded in the plastics material for example as a woven fabric.
Illustration X2 shows a fibre-reinforced plastics material in which the fibres are oriented in two mutually perpendicular directions, each at an angle of approximately 45° to the longitudinal direction of the insulating bar 10. Here too, the reinforcing fibres may be incorporated into the plastics material as a woven fabric.
Illustration X3 shows reinforcing fibres in the plastics material that run parallel to the longitudinal direction of the insulating bar 10, where in this case individual fibres, in particular long fibres or indeed fibre strands, may be used.
Illustration X4 shows reinforcing fibres that are embedded in the plastics material of the base body in the form of a tangled nonwoven.
Illustration X5 shows a porous structure in the interior of the base body.
In the case of illustrations X1 to X4, the presence of the reinforcing fibres is not necessarily visible at the surface of the base body. In many cases, the provision of the reinforcing fibres can be limited to the internal or core region of the insulating bars 10.
The same also applies to the pore structure that is shown in illustration X5, which can be limited to a core region of the base body 12 or insulating bar 10. As an alternative, the pore structure may also extend up to the surface of the insulating bar 10.
A first production plant 100 for the insulating profile bars 10 according to the invention is shown in
The plastics material of the strip-like extrudate is preferably cooled as it passes through the calender such that, as it leaves the calender 106, the planar sheet element 108 is preferably at a temperature that, in the case of (partially) crystalline plastics materials, is approximately 30° C. below the crystallite melting point of the plastics material or higher, and in the case of amorphous plastics materials is approximately 30° C. above the softening point or higher.
The planar sheet element 108, which has a predetermined heat content, is then fed into a first forming device 110, in which two rolls driven in opposite directions stamp the sheet element 108 with the connection strip geometry of a plurality of insulating bars that are arranged parallel next to one another (in the present example, nine insulating bars 10 are manufactured parallel to one another at the same time by forming). For this step, the forming temperature is likewise preferably, in the case of (partially) crystalline plastics materials, approximately 30° C. below the crystallite melting point of the plastics material or higher, and in the case of amorphous plastics materials is approximately 30° C. above the softening point or higher. If, at the time of entering the forming device 110, the temperature of the planar sheet element 108 is higher than approximately 30° C. above the crystallite melting point or approximately 60° C. above the softening point, the forming device 110 is preferably cooled. Otherwise, the forming device 110 or the tool thereof is preferably cooled to a temperature in the range of approximately 50° C. to approximately 80° C.
If necessary, there is provided downstream of the forming tool 110 a heating station 112 by means of which the temperature of the sheet element 108 may if needed be raised to a predetermined forming temperature before the sheet element 108′ is supplied to a further forming device 114 in which (if desired) a corrugated structure having raised portions 26 and recesses 28 can be produced in the insulating bars 10 (sheet element 108″).
Optionally, the forming tool 110 or the forming device 114 may be constructed as a severing device such that the individual insulating bars may be separated at the same time as forming.
Finally, the sheet element 108″, with the geometry of the insulating bars 10 already in its final shape, with connection strips and corrugated structure, is supplied to a separating tool 116 in which the connection between the insulating bars 10, as it is still present in the sheet element 108″, is removed such that mutually separated insulating bars 10 (of which only three are shown in
The second forming device 114 having rollers 128, 130 is shown in greater detail in a perspective view in
The sheet element 108′ or 108″ contains a plurality of parallel insulating bar geometries which are connected to one another by way of webs 132 of plastics material, as illustrated in
If no corrugated structure is needed in the insulating bars to be manufactured, the forming procedure is already complete after they have passed through the forming device 110, and all that is still required is to separate the sheet element 108′ into individual insulating bars 10. Otherwise, the sheet element 108′ additionally undergoes a second forming step in the second forming device 114, as described above, and is only then supplied to the separating tool 116 as sheet element 108″.
According to the invention, insulating bars of different geometry may be manufactured at the same time, in which case the rollers 124, 126 and/or 128, 130 are constructed in modular form as roller segments that are adapted to the different geometries, for example as discs that are pushable onto a drive shaft.
Different thicknesses of insulating bar can be taken into account by means of a calender 140 of modular construction having roller segments of different diameter.
The calender 140 contains three calender rolls 142, 143, 144 which are contoured on their surface in the peripheral direction, and by means of this contouring the strip-like extrudate 104 can be formed by making the thickness of the extrudate 104 uniform, directly to give a sheet element 108′ that already contains the connection strip geometry of the insulating bars 10 which are to be manufactured and are connected parallel to one another.
According to a further variant, the rollers 142, 143, 144 may additionally be constructed to have raised portions similar to the raised portions 131, 133 of the rollers 128, 130, as visible in
As an alternative, the insulating bar geometries may be connected by way of webs 132 that leave only a small spacing between adjacent insulating bar geometries. The webs 132 are then likewise removed in the separating device 116, wherein this may for example also be performed by machining, as described below with reference to
As an alternative, as shown in
The variant of a separating device 116d that is shown in
With reference to
In the corrugating machine 256, the strip-like extrudate 252 is formed such that at the same time the connection strips 14, 16 and the base body 12 having the raised portions and recesses (if desired) are produced to give an insulating bar arrangement.
The corrugating machine 256 includes two forming tools 260, 262 in the manner of belts or chains, which are driven in opposite directions and are composed of a multiplicity of mould block elements 264 and 265 that are movably connected one after the other, as seen in the longitudinal direction.
The forming tools 260, 262 are each mounted by means of a pair of deflection rollers 266, 268 and 270, 272 respectively such that they are drivable in synchronism with the speed of conveying the extrudate 252.
A plurality of the mould block elements 264 and 265 of the two forming tools 260, 262 are pressed against one another, in a position facing the extrudate 252, by way of a pressing device having press blocks 276, 278, in order to form the extrudate 252, which is guided between the mould block elements 264 of the forming tool 260 and the mould block elements 265 of the forming tool 262, by an appropriate pressure to give the desired geometry, in particular also the cross sectional and longitudinal sectional geometry. The extrudate 252 leaves the corrugating machine 256 on the downstream side as a sheet element 253 that has been formed into the insulating bar arrangement—and if the extrudate 252 has only the width of an individual insulating bar, as a finished insulating bar 10. If the width of the extrudate 252 corresponds to the width of a plurality of insulating bars 10, the plurality of insulating bars then leave the corrugating machine 256 connected to one another as a sheet element 253 and are then separated in a separating device to give individual insulating bars 10, as already described as a separating device 116 in conjunction with
On their side remote from the extrudate 252, the forming tools 260, 262 are preferably supported at their mould block elements by a guide 280, 282 such that as uniform as possible a movement sequence is obtained for the forming tools 260, 262.
In
The cross section of the individual mould block elements 264 and 265 varies over the length of the mould block elements in the longitudinal direction of the forming tools 260 and 262, as shown in
In the illustration of
The mould block elements 265 are constructed with their geometry facing the mould block element 264 in a correspondingly complementary manner in order to produce the configuration of the insulating bar 10 that was shown in
Finally,
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2014 103 729.4 | Mar 2014 | DE | national |
This patent application is a Continuation of International Patent Application No. PCT/EP2015/055698, filed Mar. 18, 2015, which claims the benefit of German Patent Application No. 10 2014 103 729.4, filed Mar. 19, 2014, which are each incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/EP2015/055698 | Mar 2015 | US |
| Child | 15267184 | US |