The application relates to a method for producing at least one component for a hydraulic displacement unit.
Certain components for hydraulic displacement units, such as axial piston machines, are hardened after production of the final shape in order to be able to meet the high demands in regards to material strength and durability. Known are methods for the overall hardening of a component as well as for the partial hardening of merely specific surface portions of the component. Depending on the profile shape of the components, such as in the region of concave portions, abrupt changes of the obtained degree of hardness can occur in the material structure. Such abrupt transitions pose a weakness of the material in any case, and in view of the bending and torsion forces acting on the component.
One example for such a component is the drive shaft of a hydraulic displacement unit, such as the drive shaft of an axial piston machine. The said drive shaft is subject to high stress due to high absolute values and high time gradients of the torsional moment, to a longitudinal bending, as well as to tensile stress and pressure loads in the longitudinal direction. An increased risk for rupture exists, e.g. in notches present in the components, such as in those transitions of the component where the hardness of the material changes abruptly. It is therefore desirable to prevent such abrupt changes of the material hardness.
Surface hardening is also problematic in those components that have to be formed in the assembly of the displacement unit, e.g. in order to be joined or connected to complementary components, such as is the case in a ball joint connection. In this case, microcracks can occur in the surface structure in the hardened surface already in the joining process. One example for this may be presented by an axial piston machine, in which the pistons are provided with sliding blocks for hydrostatic relief of engines and actuators. The connection between the piston and its sliding block occurs through a ball joint connection.
Piston/sliding block units, in which the ball head is connected to the sliding block in an integral manner and in which the ball sits on the piston, require a higher production effort, but also allow higher oblique angles (also referred to as setting angles) of the sliding block surface. Operation of piston engines with higher oblique angles leads to better effects and to an increase of their power density. The piston/sliding-block units used in engines of piston machines are subjected to stress alternately due to high pressure and tensile forces acting in axial and vertical directions. Without limitation, the causes therefore are as follows:
In operation of the engine, the piston/sliding-block unit is applied with the oil pressure at the high-pressure side.
In operation of the pump, pressure is applied to the oil by the pistons at the high-pressure side, whereas at the low-pressure side, the pistons generate the negative pressure required for suctioning the oil and are therefore subject to a tensile force.
Irrespective of whether a piston machine is operated as a pump or as an engine, friction forces occur between the side wall of the piston and the engine bushing; likewise between the sliding block surface and the support surface thereof.
The resulting axial and radial forces exert stress on a piston/sliding-block unit and therefore also on the ball joint connection not only with absolute values, but also by fast changes in these forces, so-called transients. The latter are, amongst other things, created by pressure pulses in the hydraulic oil circuit, which are not completely prevented; likewise in the case of a pump operation by transient changes of the supplied mechanical power, and in the case of engine operation by transient changes of the mechanical load.
As is the case in rotary machines, also in piston engines increased performance can be achieved in a more cost-effective manner by means of specific measures which allow for operation with increased rotating speed, in contrast to the designing of the machine from the very beginning for an operating range that allows higher torques. However, an increase in rotating speed results in an increase of the centrifugal forces originating from the piston/sliding-block units, which on the one hand apply the piston and the cylinder directly-mechanically or indirectly mechanically-thermally due to the increase of the frictional force as well as effect a higher mechanical stress of the piston retraction direction and also of the ball joint connections of the piston/sliding-block units.
A measure for increasing the allowable speed range of axial piston machines effective in multiple regards lies with the weight reduction of the pistons used in the engine, which can compensate the centrifugal forces originating therefrom and therefore also the negative consequences mentioned-above. For a long time, the pistons used in engines are formed in lightweight design as hollow pistons, wherein the hollow space is sealed in an oil-tight manner. Despite the fact that the weight reduction of the pistons by the creation of larger voids causes a reduction in the forces applied to the pistons, there is a trade-off between the lightweight construction and the durability of the pistons.
The forming region of the protruding collar 1a of the recess for enclosing the ball head 2a constitutes a weakness region of a ball joint connection. Owing to forces acting between the ball head 2a and the cap 1b, there is a risk for material rupture damage in the forming region. Owing to pressure forces between the ball head 2a and the spherical cap 1b, the surface region can collapse, according to the principle of the so-called “eggshell effect.” Besides such obvious defects, microcracks can occur already in production when inserting the ball head 2a. A break-loose of the material or of parts of the material upon insertion and over the period of use leads to a slow but progressive damage, even in smaller amounts, which then causes a fast ageing of the joint connection. Instead of a rupture or abrasion of the material, a slowly-progressive widening of the forming region can occur. In view of the long period of use of piston engines used in commercial applications, e.g. in the construction form of an axial piston engine functioning as an hydraulic pump or as an hydraulic engine, in a mobile working machine, also slowly-occurring damages might be prevented in ball joint connections of their piston/sliding block units by means of a corresponding quality of the components, because these damages continue in a progressive manner and may lead to an early destruction of the concerned piston/sliding block unit, or to an early failure of the mobile working machine.
It is therefore the object of the present application to provide a production method for components of a hydraulic displacement unit, which reacts to the above-mentioned drawbacks. A focus of the application also lies with the provision of a corresponding ball joint connection or a suitable production method for a ball joint connection, by means of which the above described disadvantages of existing solutions of the conventional art can be overcome.
The subject-matter of the application is a method for producing a component for a hydraulic displacement unit, such as an axial piston machine. The objective of the method lies with achieving a specific hardness profile at the surface of the component, which can in any case be exactly optimized by the method individually dependent upon the type of component and use.
According to the application, it is provided to that end that a blank component for the at least one component is prefabricated intentionally with oversize on at least one defined surface region. For example, a blank of the component is to be produced from a blank body by means of a machining method such as drilling or turning. However, defined surface regions of the components are intentionally prefabricated with oversize, while the remaining sub-regions of the components may already produced in their final size. The component is subsequently surface-hardened.
The final forming of the component follows the hardening process. At least the excessive material is removed at the at least one defined surface region of the component that had been produced with oversize. The material removal can be effected by means of a machining method. By the subsequent material removal, the previously achieved surface hardness can be reduced in a targeted manner again. This achieves a component which is characterized by subregions of its surface with different degrees of hardness. One feature of the method according to the application lies with the fact that surface regions directly adjacent to one another can be produced to have different material hardness by means of this method.
Consequently, the finished component can be provided with different, clearly-defined and thus optimized material hardness depending on the area. A continuous transition from strongly-hardened to less strongly hardened or completely unhardened component surface regions can ideally be achieved by means of the controlled removal of the oversize along the component surface.
A use of the method is reasonable in those components of the displacement unit that need to be formed in certain subregions for the mounting of the displacement machine, for example in order to produce a connection to corresponding counterparts. In components that are joined with mating parts by cold-forming, the surface hardness in the forming region can be optimized by means of the method, in order to avoid the disadvantages described with regard to the conventional art.
Another aspect of the application proposes a method for producing a ball joint connection consisting of a first joint part with a ball head and a second joint part with a complementary ball head receptacle. Even though reference was initially made to such a connection between a piston and a sliding block of an axial piston machine, this aspect of the application is not at all limited to such an application, because the solution according to the application can be used for any ball joint connections concerned by the drawbacks mentioned at the beginning.
According to this configuration and application of the method, it is proposed to produce a first and/or second blank joint part of the ball joint connection in a prefabrication step. A blank of the first and/or second joint part is to be produced from a blank body by means of a machining method such as drilling or turning, for example. However, defined surface regions of the first and/or second blank joint part are intentionally prefabricated with oversize, while the remaining subregions of the respective blank joint part are might be produced with their final size already.
The first and/or second blank joint part is subsequently surface-hardened.
After the hardening process, the final forming of first and/or second joint part is effected. At least the excessive material is removed from the at least one defined surface region of the first and/or second blank joint part that has been produced with oversize. The material removal can occur by means of a machining method. The previously achieved surface hardening can be reduced again by the subsequent material removal, in a controlled manner. This achieves a first and/or second joint part, which is characterized by subregions of its surface with different hardness degree. A feature of the method according to the application lies with the fact that surface regions directly adjacent to one another can be produced to have a different material hardness by means of this procedure.
In the final step, the joint parts are joined and at least one joint part is correspondingly formed for establishing the ball-joint connection. By the use of the method according to the application, a region to be formed of the joint part is distinguished by a reduced surface hardness while producing a ball-joint connection. The resulting sufficient ductility of the material in this region is a prerequisite for a plastic formability, free of cracks, of the material, whereby also a cold-forming, e.g. by rolling-in, rolling or bending of the joint part becomes possible without material deterioration. The remaining subregions of the joint part, at least those subregions that are stressed by the axial and radial forces occurring in operation, have a sufficient surface hardness by the hardening process. Where required or appropriate, the hardened surfaces can be smoothened in an intense manner by suitable processes and measures in order to reduce friction and wear.
The ball head receptacle of the second blank joint part might have a calotte shape after prefabrication, adjoined by a protruding collar. This producing collar is to be formable in such a way, after the joining of the joint parts by forming, that it at least partially engages behind the received ball head. As a result, the forming of the protruding collar is to complete the calotte shape for receiving the ball head, so that a sufficient stability of the joint connection can be achieved. It can thus be reasonable when at least a subregion of the protruding collar is prefabricated with oversize, so that after the hardening process, the material hardening initially achieved on the existing surface can be reduced by means of a corresponding material removal, whereby even in the case of cold-forming, a plastic deformability of the collar which is free of cracks for the subsequent forming process by a sufficiently high ductility of the said collar.
In an configuration of the method, the prefabrication of the blank joint part with oversize occurs in such a way that the surface of the collar, which engages behind and contacts the ball head after the cold-forming process, includes a subsection with a surface hardness which is higher than that of the remaining section of the surface contacting the ball head after the cold-forming. On the one hand, the joining region of the workpiece (collar), where the cold-forming takes place directly, is to have a relatively low hardness. On the other hand, after inserting the ball head into the ball head receptacle and cold-forming of the collar, a contact surface of the said subregion exists toward the ball head. By providing a suitably selected allowance in the designing of the shape of the blank joint part, a part of the hardened zone can be removed after material removal which occurs after the hardening process and, as a result, a hardened layer of a desired thickness htf can be maintained. The sub-portion might not extend all the way to the end of the collar facing the first joint part, but it is not excluded.
A first and/or second joint part is/are made of a material having high ductility shows advantages. However, a sufficient surface hardness is to be achievable for this material by means of a suitable hardening process. The hardening process is usually effected by means of a heat treatment. Suitable methods are, for example, nitration, gas nitration, gas nitro carbonation, or plasma nitration.
According to a configuration of the application, the ball head receptacle of the second blank joint part, i.e. the surface or wall of the blank joint part forming the recess/receptacle, is prefabricated with a bulge-like oversize, such as with an annular bulge, which extends along the surface of the second joint part forming the calotte shape.
After the hardening process, the material forming the bulge at the collar can be removed along with the finishing, so that the material hardness is reduced at the collar along this longitudinal section. According to a configuration, the material removal can progress along the bulge so far that it is not only fully removed, but finally an annular groove develops in the surface that forms the ball receptacle. As a result, due to the relatively high material removal, a groove is produced, the surface of which has a strongly reduced material hardness. Such as, an annular internal groove is produced in the surface of the second joint part forming the ball calotte. The purpose of this design lies with the prevention that the forces to be applied by the tools are introduced into the wall region that is already form-fittingly adapted to the ball head or no forming at all is caused in this region. The latter would logically lead to a potential jamming of the ball head connection. The mere introduction of forces into this hardened and thus brittle region could trigger small amounts of material or material fractions to break-out.
According to a configuration of the application, the bulge-like oversize is configured with tangent-like transitions, i.e. the contour of the bulge does not have or has only few edges, and is thus distinguished by a substantially edgeless contour.
According to a further embodiment of the method, at least one joint part of the ball joint connection according to the application, such as the second joint part, is preformed to have a cylindrical or almost cylindrical shape. This can be the case in the fabrication of the piston-sliding block unit described at the beginning, wherein the second joint part corresponds to the piston of a piston machine here. Part of the external cylinder wall of the blank joint part forms a part of the protruding collar. The external cylinder wall is removed in sections in the region of the collar during the final forming, so that a surface with reduced hardness for the subsequent cold-forming is produced here. In contrast, the remaining external cylinder wall is distinguished by maximum surface hardness achievable in the hardening process.
In addition, it is also conceivable that the external cylinder wall is fabricated with a larger diameter in the region of the collar to further reduce the surface hardness by larger material removal.
Besides the method according to the application, the present application also relates to a ball joint connection consisting of two joint parts, with a first joint part, which comprises a ball head, and a second joint part, which provides a ball head receptacle. According to the application, the ball joint connection is characterized in that the surface forming the ball head receptacle has regions of different surface hardness. Such as, the ball joint connection is characterized by neighboring surface regions with deviating material hardness.
According to a configuration of the application, the ball joint connection is produced by means of a method according to the present application or a configuration of the method according to the application. As a result, the ball joint connection is characterized by the same advantages and properties as have been described above based upon the method according to the application. For this reason, a repeated description is omitted.
According to a configuration of the ball joint connection, at least one groove, such as an annular groove, is provided in the calotte-shaped wall of the ball head receptacle, wherein this annular groove is characterized by a reduced surface hardness compared to the calotte-shaped wall.
Furthermore, a protruding collar adjoining the calotte shape can be provided, the surface hardness of which is at least sectionally reduced compared to the calotte-shaped wall.
Moreover, at least one joint part of the ball joint connection according to the application is formed in cylindrical shape, wherein its circumferential cylindrical surface predominantly is present with high surface hardness. Furthermore, it can be possible that a part of the external cylinder wall of the joint part forms a part of the protruding collar. In this case, the region of the external cylinder wall representing the collar is characterized by a reduced surface hardness. The external wall of the joint part usually has a reduced diameter in the collar region.
According to an configuration, the surface of the collar of the second joint part that engages behind and contacts the ball head can include a subsection with a surface hardness higher with respect to the remaining section of the surface engaging behind the ball head. On the one hand, the joining region of the joint part, in which the cold-forming directly occurs, is to have a (comparatively) low hardness. On the other hand, after inserting the ball head, a contact surface toward the ball head exists in the subregion concerned here. In order to take account for this point, there actually is hardened material in this subregion in a completed piston according to the application, but with a significantly lower hardness or a hardened layer with a significantly lower thickness hrt than in the regions of the high material hardness, e.g. the shell of the piston contacting the bushing of the engine. The subsection with the low material hardness can extend all the way to the end of the collar facing the first joint part, or might not reach as far as to the said end.
According to an configuration, this subregion might have a hardening depth htf in the range from 0.02 to 0.7 mm, or in the range from 0.02 mm to 0.25 mm. A surface hardness for this subregion in the range between 300 HV and 1000 HV is advantageous, further benefits might arise between 300 HV and 600 HV or 300 HV and 500 HV. The length ratio between the distance of the central axis of an annular internal groove and the end of the collar facing the first joint part, and the distance of the subregion from the end of the collar facing the first joint part is in the range between 0 and 40%, 0 and 35%, or 0 and 30%.
The application also relates to a sliding-block-piston unit with a ball joint connection. In an embodiment, the first joint part corresponds to the sliding block and the second joint part corresponds to the piston. Ideally, the sliding-block-piston unit is fabricated according to the method according to the application.
However, the method according to the application can not only be used for the production of components with forming region, but can also be used for the production of those components in which an increased strength can be achieved by a location-dependent adjustment of the material hardness. A specific example for that is the production of a drive shaft for a hydraulic displacement unit, such as for an axial piston machine.
A drive shaft is subject to high stress by high absolute values and high time gradients of the torsional moment, a longitudinal bending as well as tensile and pressure forces in the longitudinal direction. Such a drive shaft usually comprises one or multiple concave portions along its axis direction, e.g. in the form of a tapering-diameter recess for receiving a securing ring. With respect to the bending and the torsional moments, such concave sections are weak points of the shaft. A higher risk of rupture exists, inter alia, in notches existing in the component, and on those transitions of the component where the material hardness changes abruptly.
To that end, the blank of the drive shaft is formed with oversize, namely on the point of the drive shaft where such a concave portion is provided afterwards after completed final forming. After the surface hardening, the excessive material can be removed during the final forming at the at least one defined surface region of the drive shaft that has been produced with oversize, in order to obtain the desired concave portion. By the subsequent material removal, however, the previously achieved surface hardness is reduced in a controlled manner at the same time, so that ideally a continuous transition from strongly hardened to less strongly hardened and completely unhardened component surface regions is finally achieved. This prevents the weak points of the component, i.e. the drive shaft, caused by the notch effect, which result from direct transitions from strong-hardened to unhardened component regions. Furthermore, the gradient of the course of hardness starting from the component surface into the component interior can be set.
It is also conceivable that the at least one defined surface region intentionally produced with oversize is located in a place of the drive shaft which, in the final-formed state, is directly adjacent a concave and tapering-diameter region. The exact position of the surface region and the dimensioning of the oversize clearly depends on the desired final form of the drive shaft, the desired hardness degree as well as on the type of the hardening process performed.
For example, a convex material bulge is provided as an oversize of the blank in the defined surface region, the maximum of which bulge is located in the position where this drive shaft has its maximum depression/taper in the final-formed state. The blank might be globally hardened afterwards, potentially through nitration, gas nitration, gas nitro carbonation, or plasma nitration.
It is also conceivable to provide at least one convex material bulge, as an oversize of the blank, in the transition to a concave/tapering-diameter section of the drive shaft. The concave/tapering-diameter section usually exists in the blank already, merely the transition area from the non-tapered region to the tapered region is post-processed in the way of final forming. A partial hardening of the surface region lends itself for such a procedure, namely of a longitudinal section of the drive shaft, which reaches from the non-concave or non-tapering-diameter section all the way to the convex material bulge. A partial hardening is potentially made by means of induction hardening and/or laser beam hardening and/or electron beam hardening.
As has been described multiple times, a drive shaft is subject to high stress in the region of specific sections. For example, a high local stress occurs by the abutting of the drive shaft drum in an axial piston machine, which introduces the transversal forces into the drive shaft, which in turn result from the supporting of the pistons on the swashed plate. Furthermore, the by far largest portion of the torsional moment is produced along a drive shaft between the shaft input (i.e. the toothing of the drive shaft outside the housing) and the shaft toothing with which the drum is connected to the drive shaft in a form-fit and co-rotational manner. Due to this high stress of this longitudinal section, measures for preventing any notch stress is desirable.
The problem can be addressed by creating a longitudinal section of the drive shaft for stress handling. By an variant of the method according to the application, instead of a completely hardened drive shaft, a drive shaft with a specific hardness profile in the axial direction can be realized. The surface profile is adjusted in such a way here that material stress occurring in the component during regular operation of the displacement unit, such as of the axial piston machine, can be handled. Potentially, a higher stress resistance and durability of the drive shaft can be achieved if the drive shaft has a hardness profile advantageous in the axial direction within two longitudinal sections, which are located directly next to the toothing for the form-fit and co-rotational connection of a drive shaft drum, with a hardness degree HV(x)≤Max [HV(x)]. The surface of the drive shaft has a material hardness of Max [HV(x)] outside these longitudinal sections.
To that end, a blank of the drive shaft is produced, for example, in which an oversize is provided in the regions of the drive shaft, which are directly adjacent or in direct proximity to the toothing of the drive shaft. By the final forming after surface hardening, the above mentioned hardness profile can be achieved there, in order to support the handling of stress.
The surface hardening of the engine shaft can be carried out by means of global surface hardening of the blank, e.g. by means of nitration, gas nitration, gas nitro carbonation or plasma nitration, or, instead, by a partial hardening of the one or multiple longitudinal sections including the toothing, e.g. by means of induction hardening and/or laser beam hardening and/or electron beam hardening.
Besides the method according to the application for fabricating the drive shaft, the application also discloses a drive shaft which exhibits a material hardness profile with varying hardness degree in the longitudinal direction, wherein the resulting hardness profile potentially does not have abrupt changes of the hardness degree, but instead a tangentially-constant course of the hardness degree in the axial direction.
Further advantages and properties of the application will hereinafter be explained in more detail by means of an exemplary embodiment illustrated in the drawings. The
The methods according to the application as well as the ball joint connection according to the application is to be explained in the following by way of example based upon a drive shaft 8 as well as a sliding block piston unit 2, 1 for a piston machine. For this reason, first the general construction of such a machine is to be briefly described. A sectional representation of such an axial piston machine is shown in
A retention device of the axial piston machine comprises a retraction plate 6 and a retraction ball 7. This ball is mounted on the drive shaft 8 coaxially as well as co-rotationally and in a linearly displaceable manner. The retraction plate 6 acting on the sliding blocks 2 is in operational connection with the retraction ball 7, i.e. the retraction plate 6 is actuated by a linear displacement of the retraction ball 7, whereby the sliding surfaces of the sliding blocks 2 are each being pressed against the swashed plate 4 over the entire surface thereof. Via the external toothing, the drive shaft 8 can be connected to the external device for the transmission of torque.
A focus of the application relates to the production of the engine pistons 1 as well as the of the sliding blocks 2, such as the existing ball joint connection between the two components 1, 2. The object of the application lies with the creation of a one-piece component, e.g. a one-piece piston or one-piece piston basic body, which has various different material properties in closely neighboring zones. On the one hand, a hardened and smooth surface is to be available, on the other hand a sufficiently high ductility is to be available, so that the requirement of a plastic formability without cracks is met and thus a cold-forming, e.g. by rolling, rolling-in, bending, etc. of the component is possible without material deterioration.
The blank piston prepared for a heat treatment consists of a relatively soft basic material and is produced with specified production oversize. The blank piston is subjected to an intensive heat treatment, until its surface has a material hardness which is sufficient for the range of strongest stress. After the removal of the fabrication oversize, a piston that has the required geometry is achieved. Due to the previous intentional oversize, the piston surface has a different material hardness, which is adapted to the different requirements.
For a better understanding, first the features of the piston according to the application are explained, and after that, the production method will be explained, underlining the sub-steps according to the application:
A) Piston According to the Application
The regions 14a, 14b, 14c, 14d indicated with the coarse hatches exhibit the layer hardened by heat treatment (e.g. nitration). The surfaces 14a, 14b, 14c, 14d facing inwards and outwards of these layers of the piston 10 have an extremely high material hardness, and clearly a smooth surface is to be present for the zones (i) and (ii) in the completed piston 10. These two properties are exhibited on the piston external wall 15 over the entire section that contacts the surface of the engine bore or the bushing installed there in the course of the axial piston movement. Furthermore, these properties are exhibited within the section of the surface 14c of the piston recess, which already has the form-fit ball calotte 11 for the reception of the joint head. In addition, the internal wall 14d of the piston 10, through which the oil channel 13 extends, has an extremely high material hardness, contributing to a higher strength of the piston 10. In the case of the hollow piston, the latter property allows an enlargement of the hollow space(s), which contributes to a further weight reduction.
The finer hatches in the enlarged view indicates the forming region 12 of the piston 10, which has a high ductility in the piston 10 according to the application, which enables a process-secure cold-forming. The requirement of a certain ductility and the advantages of a high ductility have already been discussed in the introductory part of this application. The first contact zone with the tool for cold-forming is indicated with reference character 18. Thus, high ductility is present along the surface sections indicated with reference character 12b, i.e. these sections have the same relatively low material hardness as is present in the inside of the core material. The same applies to the edge region 12c on the inside of the piston 10.
On the one hand, the joining region of the piston, where the cold-forming directly occurs, is to have a (relatively) low hardness. On the other hand, a contact surface to the ball head exists after the insertion of the sliding block into the edge region 14b marked here, which is why a hardened layer is provided in the region 14b.
The edge layer 12a in the forming region 12 of the piston that is located in direct proximity to the recess is illustrated in the enlarged view to be separated from the remaining larger forming region 12 bearing the fine hatches. The latter edge layer 12a has a medium ductility compared to the already mentioned extremely high and relatively low material hardness, which corresponds to that of the core material. However, this ductility is defined in a very precise manner and represents the best-possible compromise of the mentioned opposed component requirements. As already mentioned, a sufficient plastic formability is to be present, so that the forming region 12 will not be damaged on the piston 10 when inserting the joint head. On the other hand, a sufficient material hardness is provided, so that the creation of a smooth surface is possible and a high durability against the forces acting in operation is provided.
In the enlarged view, two sections of the piston wall are located outside the hatched regions. The section 16 along the external wall of the piston 10 between the forming region 12 and the strongly-hardened region 14a can suitably be referred to as a reserve zone 16. This zone has the hardness of the core material or a slightly higher material hardness, so that a sufficient strength of the piston 10 exists there in any case and, on the other hand, an unnecessary high brittleness is prevented, in order to prevent a pre-damaging of the piston 10 when inserting the ball head. It is possible for the forming region 12 to extend beyond the region marked with the finer hatches here.
The piston wall has an annular internal groove 17 and has a low material hardness in the near region of said annular groove 17. The purpose of this design lies with the prevention that the forces to be introduced by the tools when inserting the joint head are introduced into the wall region that is already adjusted in shape to the ball head and could even cause a forming in this region. The latter would logically lead to a potential jamming of the ball head connection. However, merely the introduction of forces into this hardened and thus brittle region could cause small amounts of material or material fractions to break-out.
In contrast to the pistons corresponding to the conventional art, where the material hardness present across the entire piston surface or at least present across parts of the surface areas are a compromise between high durability and sufficient ductility, a piston 10 according to the application comprises closely neighboring surface regions with strongly different material hardness in certain regions which might be advantageous. The compromise is restricted to a very small subregion of the piston surface, namely the protruding collar of the recess for receiving the ball head, wherein the production according to the application allows an exact specification of the material hardness there. Through the application of the fabrication steps according to the application explained in the following, the material hardness of the piston 10 can be adjusted to the requirements for its entire surface and, as can be taken from the following, for its entire material layer close to the surface, in an optimal manner.
As an alternative to the configuration as a solid piston according to
B) Fabrication, According to the Application, of Pistons 10
The left part of
As can be seen from the contours representing the surfaces, the surface of those wall regions that have a high material hardness in the completed piston 10, which concerns (i) section 14a of the external wall of the piston, which is in contact with the engine bore or the bushing present therein, and (ii) wall section 14c, which already has the ball calotte adapted in shape for the reception of the ball head, as well as (iii) the wall 14d of the central bore, are identical in both superimposed enlarged views.
By contrast, relatively large oversize of the blank piston 10′ is present in those wall regions where the material located at the surface is also ductile in the completed piston 10; this relates to the forming region 12, the reserve zone 16 and the annular groove 17. As can be discerned in
For the purpose of a simplification of the drawing, discrimination between hardened and non-hardened zones in made by a corresponding hatching in the Figures. As is known, these is not an abrupt transition from a soft to a hard material in a heat treatment. Instead, a locally and temporally continuous hardening process exists by the heat treatment. Based upon a hardened material surface, first a progressive decrease of the material hardness HV is present as the penetration depth x increases, and, from a certain penetration depth x on, practically a degressive decrease is present, so that the ductility of the non-hardened material is present as from a certain penetration depth (see diagram on the right in
From this conjunction, it becomes clear that a layer thickness of material determined for achieving the specified final shape of the piston by the intentional selection of the oversize at the internal side 14b of the protruding collar after the defined heat treatment is removed, and that thus the material hardness of this surface is predetermined. In accordance with the material hardness to be achieved there, and the surface hardness of the blank piston 10′ achieved after the heat treatment, this oversize is set.
In a further developed configuration of the production method according to the application, the intentional application of defined oversize in the shape of the piston 10′ is considered in conjunction with the degrees of freedom present in the heat treatment. The diagram of
The targeted use of oversize at the blank piston 10′ is not restricted only to regions where the hardened layer is to be removed completely or almost completely for finishing the piston 10, but also to the transition regions between the strongly-hardened and less strong surface regions. This aspect can be well be explained for the fabrication of the annular groove 17 (see
In order that the occurrence of notch effects, which causes a significant reduction of the component strength, is prevented, these so-called transition areas at the piston are rounded-off. A design of these transition areas results from a constant tangent-continuous (edge free) course of the contours of the blank piston 10′, as is illustrated in
The fabrication of the piston according to the application with the production steps according to the application and their advantages takes place in a chronological order:
Fabrication of the blank piston 10′ with the intentionally selected, exactly-defined oversize made of a material with a relatively high ductility, which is well suited for hardening and, after the hardening thereof, smooth surfaces can be achieved by corresponding postprocessing.
Intensive hardening of the blank piston 10′ potentially by a heat treatment. Here, the selection of the process of the heat treatment (e.g. nitration, gas nitration, gas nitro carbonation, plasma nitration, etc.) as well as the process design can be adapted to the temperature profile and the duration of the process application etc., so that the surface hardness is in a suitable range (strength versus efforts for the required material removal) and a comprise for the sensitive region of the piston is achieved. Likewise, an optimization under the trade-off between surface quality and production efforts is possible.
By contrast, compromise is not reached between the two opposed component requirements in the heat treatment.
Material removal for the final forming of the piston 10, as required for the insertion of the ball head. By this material removal, it is achieved at the same time that the surface of the piston has the desired local material hardness.
After the fabrication of the piston 10, the ball head is inserted. This process is potentially performed by a cold-forming (e.g. rolling, rolling-in, etc.), wherein the insertion can be supported by a moderate heating.
In the joining process of the piston 10 for the installation of the ball head, respectively the sliding block, the maximum deformation exists at the outer end of the protruding collar of the piston. This problem can be addressed by an modification of the piston 10. This variant is shown in
Regardless of the size of the ball head connection, respectively of the ball head diameter, an optimization of the known opposed component requirements can be achieved by an adaption of the size relation a=l2/l1, as can be taken from
With reference to the already used enlarged regions, the fabrication of a blank piston 100′ according to
By a corresponding shape of the blank piston 100′, as a further variant using the production method according to the application, pistons can be fabricated in which the material hardness has different material hardnesses on the internal surface of the protruding collar with respect to the depth direction of the recess. Potentially, the smallest material hardness would be present at the end of the collar, and an increase of the material hardness would occur with respect to the depth direction of the recess, till a longitudinal portion with a constant material hardness is present. Alternatively, this increase of the material hardness could continue to the vicinity of the annular internal groove.
Similarly, edge-free courses of the contours of the blank piston 100′ and of the completed piston 100, which correspond to the course of the diameter of the recess with respect to depth direction. The corresponding tangent-continuous transitions in the blank shape contour selected in accordance with
Each non-tangent-continuous change in contour along the oversize contour causes an abrupt change in hardness within the completed piston 100. An abrupt change in hardness within a component presents a local weakening of the material microstructure there. Weakness of the material microstructure in regions where the plastic deformation is to occur present an increased risk of component damaging during the cold-forming process.
Further advantages for the insertion of the ball head, and thus for the piston-sliding block unit can be achieved by the selection of the oversize of the blank piston 10′, 100′. Different forming methods can be used when establishing the ball joint connection. Through cold-forming, thermal stress will not act upon the hardened and polished surface, which could cause a damaging of the same; at least when a too strong heating is present over a long period of time. The insertion of the ball head into a piston 10, 100 according to the application does not necessarily have to take place by a cold-forming, but a piston 10, 100 according to the application is much more suitable for it. Besides the process temperature, further degrees of freedom are available for the forming, i.e. the selection of the method (e.g. rolling-in, rolling, bending) and the geometry of the deforming tool, respectively of the contact zone of the tool at the protruding collar of the piston 10, 100.
As explained above, the production according to the application of the piston 10, 100 achieves a better suitability of the protruding collar. This, in turn, creates a larger scope of using such a forming method and such a tool, by means of which possibly a ball joint connection that has a better quality or lower production efforts can be achieved. In this context, a ball joint connection with a higher quality means that it has a higher durability, or that a configuration of such a piston sliding block unit can be fabricated that provides other advantages for the conditions of use present in such an axial piston machine.
A very distinctive example lies with the enclosure width of the piston head. In this case, there is an opposite of two requirements in piston/sliding block units. On the one hand, a higher enclosure width is advantageous for stability and precise guiding of the ball head in the ball calotte. However, on the other hand, the maximum possible inclined angle of an axial piston machine is decreased by a higher enclosure width.
The current text describes pistons, which are connected to the ball head receptacle by material engagement, and the sliding is connected to the ball head correspondingly by material engagement. The above description on the piston/sliding block unit and on the manufacturing process according to the application can be translated into the shown piston/sliding block unit according to
As another exemplary embodiment, the method for producing a drive shaft according to the application is to be explained. The drive shaft 80 shown in
The recess 85 is a concave region of the drive shaft 80, which often has abrupt changes of the hardness degree in conventionally fabricated drive shafts, and thus tends to have the disadvantageous notch effect.
To prevent this problematics, the production method according to the application is used. Here, the drive shaft 80 is manufactured as a blank part 80a first. The blank part 80a already mainly has the final drive shaft shape of
The blank part 80a is then subjected to a global hardening, e.g. by nitration, gas nitration, gas nitro carbonation, and plasma nitration, where the entire component 85a is exposed to the hardening process, which finally leads to a constant material hardness of the drive shaft in the axial direction under ideal conditions.
The dotted line C indicates the end of the heat influence zone in the material interior of the drive shaft. In the hardening of the material, the workpiece is heated first, and then quenched. Line C thus indicates the depth effect of the hardening process, wherein the resulting material hardness decreases from the surface to the inside. As from line C in the direction of the central axis of the drive shaft, the material hardness does not differ from the original material hardness.
If now, after the effected hardening, the oversize 85a is removed in the region of the recess 85, e.g. by a metal cutting or machining process, logically the material hardness achieved after the hardening step is reduced in this region. For example, the material hardness from the left or right shaft end to the points X, Y corresponds to the maximum material hardness achieved by the hardening process. The material hardness continuously and steadily decreases from the points X, Y due to the material removal, until the original material hardness of the non-hardened blank 80a is present in points D. A tangent-continuous hardness profile course is achieved in the transition area X, Y by means of this method. As a matter of precaution, it is pointed out that
A modification of the method is to be explained in greater detail by means of
After the production of the blank 80′, this blank is subjected to a partial hardening. Partial hardening can, for example, be achieved by induction hardening, laser beam hardening, or electron beam hardening. An advantage of induction hardening lies with the independent control of hardening temperature on the material surface and the penetration depth, since two influencing parameters are available to that end. The amount of the local heat ingress, i.e. the local heating of the section of the component blank to be hardened is mainly determined by the resistivity of the component material and the intensity of the eddy currents caused. The latter results from the intensity of change of the magnetic field generated by the inductor. The intensity of change increases both as the amplitude of the magnetic field increases and as the frequency of the magnetic field increases. The frequency of the magnetic field is, at the same time, the frequency of the eddy current. Commonly known and referred to as skin effect, the penetration depth of the electric current or the eddy current in the conductor or of the component to be hardened is reduced as the frequency increases.
Although the hardening process can be restricted by partial hardening to those components where a hardening is to be effected, which in turn results in energy savings and reduces the hardening duration, but the pure partial hardening of highly-stressed components has a disadvantage compared to the here applied combination according to the application of partial hardening and oversize fabrication. The method according to the application allows achieving a continuous transition from the strongly hardened to the unhardened component surface regions. This prevents the weaknesses caused by the notch effect, which result in the case of direct transitions from strongly-hardened to unhardened component regions.
The indicated detailed illustration of the blank 80a′ in
Now, by a corresponding removal of the bulge-like oversize 85a′, a tangent-continuous transition of the hardened surface region into the non-hardened surface region of the recess 85′ can now be achieved.
The described advantageous effect of the application can be explained in an illustrative manner by means of the comparison between
Besides using the method according to the application for the processing of a concave section during the fabrication of a shaft, the method is likewise suitable to create one or multiple defined longitudinal sections of the drive shaft with optimized hardness profile. Such an optimized hardness profile of the shaft in the axial direction can be suitable to handle occurring stress, such as working stress such as internal stress, in a better manner. In the drive shaft, there is a local high stress in the region between toothing, e.g. the toothing 81, 82. Through the contacting of the drum 3 in the region of the toothing 82, transversal forces are introduced into the drive shaft 80, which result from the supporting of the piston 1 in the swashed plate 4. There is also a high stress of the material by the resulting torsional moment on to the drive shaft 80, which predominantly takes effect on the section between the shaft input, i.e. the toothing 81 of the drive shaft 80 outside the housing, and the shaft toothing 82.
An embodiment of this application is to provide this section of the drive shaft with a longitudinal section, which is characterized by an optimized material hardness profile, wherein such an optimized profile can be achieved by means of the method according to the application. Such as, any notch stress is to be completely avoided by means of the optimized hardness profile. Instead of a fully-hardened drive shaft, the material hardness of which has the value of HV0 across the entire surface, a higher durability and stress resistance of the drive shaft will be achieved if two longitudinal sections in the axial direction are provided immediately next to the toothing 82, which have an advantageous hardness profile with the material hardness of HV(x)≤max HV(x), with x indicating the position in the axial direction. Outside of these longitudinal sections, the surface of the drive shaft has a material hardness of maxHV(x).
This blank 80″ is now subjected to a global hardening.
Specifically, the oversize region 88a″ can be subdivided into a convex arcuate section a and a concave arcuate section b.
An alternative to the above-mentioned method is to be explained yet by
However, in this case, the shaft blank 80a′″ is produced in these longitudinal regions 88′ with a slightly deviating oversize 88a″, which exhibits an increasing diameter from each side of the toothing 82 in the axial direction of the respective shaft end. This prepared shaft blank 80′ is subsequently subjected to a partial shaft hardening. The axial extent of the partial hardening is indicated with the bracket E in
In the sectional view of the drive shaft in
In the sectional illustration according to
The above-mentioned methods for producing a drive shaft 80, 80′, 80″, 80′″ also allow for the advantages briefly summarized in the following.
a) If the strength of a drive shaft produced according to conventional art was too weak or tendentially too weak on the said points of weakness, a drive shaft with an increased safety margin is achieved by the method according to the application.
b) If a sufficient safety margin has already been provided by a drive shaft according to the conventional art, a corresponding drive shaft can be produced by means of the method according to the application possibly from a more cost-effective and/or a specifically more lightweight material.
c) If a sufficient safety margin has already been provided by a drive shaft according to the conventional art, the use of the method according to the application in a re-construction of the engine allows selecting a corresponding drive shaft having slightly smaller diameter, which accordingly provides for many subsequent advantages. In this way, reducing the drive shaft diameter also allows reducing the engine outer diameter. In addition, this results in an increased power density and material savings, and such as a reduction of the centrifugal forces. This, further on, leads to a reduction of friction losses, and to an increase of the efficiency, or a reduction of occurring wear.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1043/17 | Aug 2017 | CH | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20080166579 | Kotthoff | Jul 2008 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20190062893 A1 | Feb 2019 | US |