The present invention relates to a method for producing a barrier rib substrate for a plasma display panel (hereinafter, referred to as PDP), a PDP and a method for producing the PDP.
The PDP includes a pair of substrates opposed to each other, and on one of the substrates, electrodes (for example, address electrodes) extending in a predetermined direction and barrier ribs for separating a discharge space are formed (hereinafter, a substrate with barrier ribs thereon is referred to as a “barrier rib substrate”).
Here, a method for producing a conventional barrier rib substrate will be described.
a) shows a barrier rib substrate for a large PDP and
As described above, patterns of the barrier ribs 53 in the barrier rib substrate for a large PDP differs from those of the yet-to-be-divided barrier rib substrate for plural small PDPs. A photomask to be used in a photolithography step is changed in order to change the pattern of the barrier ribs 53.
In the above conventional method, it is necessary to prepare a plurality of photomasks in producing a barrier rib substrate for a large PDP and a barrier rib substrate for small PDPs and to change the setup conditions of a production line in producing each barrier rib substrate. These all lead to an increase in the production cost of the barrier rib substrate.
The present invention has been achieved in view of the above-mentioned circumstances and provides a method by which a barrier rib substrate for a PDP can be produced easily.
A method for producing a barrier rib substrate for a PDP of the present invention comprises the steps of: producing a barrier rib substrate for a large PDP by forming electrodes extending in a predetermined direction on a substrate and barrier ribs on the substrate or in the substrate itself; and producing four or more barrier rib substrates for small PDPs with barrier ribs formed up to the substrate end by performing, in regard to the barrier rib substrate for the large PDP, division in a direction orthogonal to a direction in which the electrodes extend and at least one-time division in a direction parallel to the direction in which the electrodes extend.
In the method of the present invention, barrier rib substrates for small PDPs are produced by dividing a barrier rib substrate for a large PDP. Therefore, it is not necessary to prepare another photomask for producing the barrier rib substrate for small PDPs. Further, in a production line of the barrier rib substrate, it is possible to omit the effort to change the setup conditions of the production line since only one kind of barrier rib substrate needs to be produced. It should be noted that, in this specification, the term “small” does not indicate an absolute size and means that the size is smaller than that of “large”.
a) and 1(b) show a structure of a yet-to-be-divided barrier rib substrate for a large PDP according to a method for producing a barrier rib substrate for a PDP of a first embodiment of the present invention, and
a) to (b) show a state, in which phosphor layers are formed on the barrier rib substrate for a small PDP of
a) to 11(c) are plan views according to a conventional method for producing a barrier rib substrate for a PDP, and
1: substrate 1a: side orthogonal to an address electrode 1b: side parallel to an address electrode 3: address electrodes 5: dielectric film 7: barrier ribs 9: neighboring region of substrate end 11: region between barrier ribs 13: exhaust hole 15a to 15d: barrier rib substrate units for a small PDP 17: phosphor layers 51: substrate 53: barrier ribs
Hereinafter, an embodiment of the present invention will be described with reference to drawings. The drawings are used for convenience sake of description and accordingly, the present invention is not to be considered as being limited by the embodiments shown in drawings. In the following embodiments, the present invention will be described by exemplifying the case where barrier ribs are formed on the substrate on which address electrodes are formed, but the present invention can also be applied to the case where barrier ribs are formed on the substrate on which other electrodes such as display electrodes are formed.
A method for producing a barrier rib substrate for a PDP of a three-electrode surface-discharge PDP of the first embodiment of the present invention will be described.
First, as shown in
The barrier rib substrate for a large PDP of this embodiment can be used for producing one large PDP or can be used for producing four or more small PDPs by dividing the barrier rib substrate. Dotted lines A, B shown in
As the substrate 1, a substrate of glass, quartz, ceramic, or the like, or a substrate on which desired constituents such as an electrode, an insulating film, a dielectric layer, a protective film, and the like, are formed can be employed.
The address electrodes 3 are composed of Ag, Au, Al, Cu, Cr, laminates thereof (for example, Cr/Cu/Cr laminate structure), or the like. Desired number of the address electrodes 3 with desired thickness, width, and spacing may be formed by employing a printing method for Ag and Au and combining a film formation method such as a vapor deposition method, a sputtering method or the like with an etching method for the other materials. Typically, the substrate 1 is rectangular or square, and the address electrodes 3 extend in parallel to two sides of the substrate 1 and orthogonal to the other sides of the substrate 1. In this specification, the term “orthogonal” or “parallel” means substantially orthogonal or substantially parallel. The detailed shapes of the address electrodes 3 near the end of the substrate 1 are omitted for convenience of illustration and they are shaped so as to be electrically connected to a control circuit substrate at the end of the substrate 1.
The dielectric layer 5 is formed, for example, by applying a glass paste, formed by adding a binder and a solvent to low melting point glass frit, onto the substrate 1 by a screen printing method, and firing the paste. The dielectric layer 5 may also be formed by depositing silicon oxide by a CVD method or the like.
The barrier ribs 7 can be formed by the following method.
In this method, first, a barrier rib material layer is formed on the dielectric layer 5, and barrier ribs 7 are formed by partially removing the barrier rib material layer through etching the barrier rib material layer. A portion to be removed is a neighboring region 9 of two sides 1a, orthogonal to a direction in which the address electrodes 3 extend, of the substrate 1, and a region 11 which becomes a discharge space. In the neighboring region 9, the barrier rib material layer is removed thoroughly and the barrier ribs 7 are not formed. On the two sides 1b, parallel to a direction in which the address electrodes 3 extend, of the substrate 1, the barrier ribs 7 are formed up to the end of the substrate. In another embodiment, the barrier ribs 7 don't have to be formed up to the end of the substrate on one or both of the two sides 1b, parallel to the address electrode 3, of the substrate. The barrier rib material layer can be formed, for example, by applying a glass paste composed of low melting point glass frit, a binder, a solvent, and the like, onto the dielectric layer 5, and drying the glass paste.
Etching can be performed by physical etching or chemical etching. Physical etching is a method for removing an unnecessary portion physically such as by sand blasting. Chemical etching is a method for removing an unnecessary portion by use of chemical or gas which chemically reacts with a layer desired to be removed. Hydrofluoric acid may be used as the chemical for the barrier rib material layer made of glass paste. A portion not to be removed is covered with a resist pattern for protection before etching. The resist pattern can be formed by applying a photoresist or sticking a dry film resist onto the barrier rib material layer, exposing this resist through a photomask and developing this resist.
In another embodiment, as shown in
In this method, first, a barrier rib material layer is formed on the dielectric layer 5, and barrier ribs 7 are formed by partially removing the barrier rib material layer through irradiating laser light to the barrier rib material layer. An area to be removed and a configuration of the barrier rib material layer are similar to those of etching. Conditions under which laser light is irradiated may be appropriately determined so that the laser light does not create damage to the dielectric layer 5 during removing the barrier rib material layer.
In another embodiment, as shown in
When the barrier ribs 7 are formed by a method of using laser light, there is no merit of reducing number of photomasks, but there is the merit of omitting the effort to change the setup conditions of the production line of the barrier rib substrate.
In the first embodiment, the barrier ribs 7 are formed on the dielectric layer 5, but in another embodiment, as shown in
Next, by performing division A of the barrier rib substrate for a large PDP in a direction orthogonal to a direction in which the address electrodes 3 extend and at least one-time division B of the barrier rib substrate in a direction parallel to the direction in which the address electrodes 3 extend, four or more barrier rib substrates for small PDPs with barrier ribs formed up to the end formed by the divisions A and B are produced. The divisions A and B are performed, for example, along dotted lines A and B in
In the method of this embodiment, two adjoining barrier rib substrate units for small PDPs in a direction in which the address electrodes 3 extend in the barrier rib substrate for a large PDP (e.g., a pair of unit 15a and unit 15b, a pair of unit 15c and unit 15d) are located without leaving the space between the units. Further, two adjoining barrier rib substrate units for a small PDP in a direction orthogonal to a direction in which the address electrodes 3 extend in the barrier rib substrate for a large PDP (e.g., a pair of unit 15a and unit 15c, a pair of unit 15b and unit 15d) are located in such a way that a space between two barrier ribs 7 which are closest to a division line (dotted line B) is equal to the pitch of barrier ribs 7. In other words, a plurality of barrier ribs 7 are located in parallel at equal spaces in the barrier rib substrate for a large PDP, and division of the barrier rib substrate for a large PDP is performed at a location between specific two adjacent barrier ribs. Further, when the barrier ribs 7 of the barrier rib substrate for a large PDP have a terminal wall 7a as shown in
In another embodiment, as shown in
Next, a method for producing a barrier rib substrate for a PDP of the second embodiment of the present invention will be described. This embodiment is a method for producing the barrier rib substrate provided with barrier ribs up to the substrate end produced in the first embodiment easily from a different point of view. This method will be described with reference to
A production method of this embodiment comprises the steps of irradiating laser light to a barrier rib material layer on a substrate 1 or the substrate 1 itself to partially remove the material layer or the substrate in such a way that barrier ribs 7 are formed, and forming address electrodes 3 extending in a predetermined direction on the substrate, wherein the laser irradiation is performed in such a way that the above-mentioned material layer or a portion, having a depth corresponding to a barrier rib height, of the substrate is thoroughly removed in a neighboring region of one side of two sides 1a, orthogonal to a direction in which the address electrodes 3 extend, of the substrate, and the barrier ribs 7 are formed up to the end of the substrate at the other side of two sides 1a. The description of a method of laser irradiating is similar to that in the first embodiment. Conventionally, the material layer or a portion, having a depth corresponding to a barrier rib height, of the substrate is thoroughly removed in neighboring regions of four sides of the substrate 1, but in this embodiment, an amount of processing by laser is less since the barrier ribs 7 are formed up to the substrate end in place of thoroughly removing the material layer or the substrate in at least one side. Accordingly, a processing time can be shortened. At both or one of the two sides 1b, parallel to a direction in which the address electrodes 3 extend, of the substrate, the barrier ribs 7 may be formed up to the substrate end. In addition, in neighboring regions of both of the two sides 1b, the material layer or a portion, having a depth corresponding to a barrier rib height, of the substrate may be thoroughly removed.
It is also possible to reduce an amount of laser processing by not processing the substrate end in place of forming the barrier ribs 7 up to the substrate end. That is, as shown in
Next, a method for producing a three-electrode surface-discharge PDP will be described. A PDP can be produced by sticking the rear-side substrate and the front-side substrate to each other with a sealing material and introducing/encapsulating a discharge gas in a discharge space. Hereinafter, a method for producing a PDP will be described in detail.
(1) Rear-Side Substrate
A rear-side substrate can be formed by producing the barrier rib substrate by the above-mentioned method and forming phosphor layers between adjacent barrier ribs 7. As an example, a state in which phosphor layers 17 are formed on the barrier rib substrate shown in
The phosphor layers 17 can be formed by applying a phosphor paste containing phosphor powder and a binder to the inside of a groove between barrier ribs 7 by a screen printing method, a method of using a dispenser, or the like, repeating this application for every color (R, G, B), and firing the paste. The phosphor layers 17 can also be formed by a photolithography method using a phosphor layer material in a sheet form (the so-called green sheet) containing phosphor powder and a binder. In this case, by sticking the sheet of desired color to the whole display area on the substrate, exposing and developing the sheet, and repeating this operation for every color, the phosphor layers of the respective colors can be formed between the corresponding barrier ribs.
As the front-side substrate, a substrate on which display electrodes capable of generating surface-discharge are formed can be employed. For example, the front-side substrate described in JP-A No. 2003-5699 can be employed.
Sticking of the rear-side substrate and the front-side substrate can be performed by applying a sealing material to an area near a peripheral portion of the rear-side substrate, preliminarily firing the sealing material, and firing the front-side substrate and the rear-side substrate with the former overlaid on the latter. Thereby, a space, which communicates with the outside only through an exhaust hole 13, is formed between the rear-side substrate and the front-side substrate. A substance formed by sticking both substrates to each other is referred to as a “panel”. In another embodiment, sticking of the rear-side substrate and the front-side substrate may be performed by applying the sealing material to the front-side substrate, preliminarily firing the sealing material, and firing the front-side substrate and the rear-side substrate with the former overlaid on the latter. In this case, a phenomenon, in which the sealing material is sucked into a space between barrier ribs 7 by a capillary action, becomes less likely to occur. As the sealing material, a glass paste composed of low melting point glass frit, a binder, a solvent, and the like, can be used.
A glass tube is connected to the exhaust hole 13, and the inside of the panel is evacuated through this glass tube under a high-temperature environment and the discharge gas is filled through this glass tube. Thereafter, the glass tube is chipped off and the inside of the panel is sealed to complete the production of the PDP. This step can be performed according to a method described in JP-A No. HEI 7 (1995)-105848. If the barrier rib substrate for a large PDP shown in
The various characteristics described in the above embodiments may be combined. In the case where a plurality of characteristics are included in one embodiment, one or a plurality of these characteristics may be appropriately picked up and employed alone or in combination for the present invention.
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP2005/023387 | 12/20/2005 | WO | 00 | 4/16/2008 |