Patent Application
20200399127
The present invention relates to a method for preparing calcium phosphate, and a composition for removing harmful gas and odor containing the calcium phosphate obtained thereby.
Following the progress of industrialization, the atmospheric environment is gradually getting worse and pollutants are becoming more diverse, and in the present reality, the generation rate of various harmful gases including heavy metals, carbon monoxide (CO), nitrogen oxides (NOx) and volatile organic compounds (VOCs) which are critical to the human body is rapidly increasing. Accordingly, with growing interest in the atmospheric environment around the world, highly efficient air filters are being used to obtain a clean living environment and to maintain a highly-clean production process along with the development of electric, electronic, and semiconductor industries.
However, such a high efficiency air filter has a disadvantage in that the selling price is high due to an increase in production cost, and although improvement is possible by the removal of harmful gas, there is a problem in that the removal efficiency is still low.
There are a variety of pollutants in the air ranging from ones in a dust state and ones in a gas state. Among the exhaust gases are neutral gases such as butane, toluene, benzene, and acetaldehyde, and acidic gases such as sulfur dioxide, carbon monoxide, nitrogen oxide, and ozone. Tobacco smoke contains neutral gases such as toluene and acetaldehyde, acidic gases such as acetic acid, and basic gases such as ammonia and the like. The human body also generates carbon dioxide and ammonia, and livestock and such generate methyl sulfide which is a neutral gas, hydrogen sulfide which is an acidic gas and ammonia which is a basic gas.
These pollutants can be removed to some extent by a filter provided in a, an air conditioner, a total heat exchanger, and the like.
However, the filters provided in an air purifier, an air conditioner, a total heat exchanger and the like have high removal efficiency of particulate pollutants and biological pollutants but have a problem of low removal efficiency of gaseous substances.
Meanwhile, hydroxyapatite (HAP) is a calcium phosphate-based ceramic which is a main constituent of human bone and has excellent bone conduction, bioactivity, biocompatibility, protein adsorption, heavy metal adsorption, antibacterial and anti-viral properties and so in general, it is mainly used as a bone substitute in the fields of orthopedics and dentistry.
Therefore, the present invention is directed to provide a method for preparing calcium phosphate that can prepare calcium phosphate simpler than a conventional method for preparing calcium phosphate, wherein the prepared calcium phosphate has a large specific surface area so that even with a small amount it has excellent removal efficiency of harmful gases that are harmful to the human body, and is secured with durability.
The present invention is also directed to provide a method for preparing calcium phosphate which can significantly reduce the operation cost as compared with the conventional adsorbent or catalyst for removing harmful gas when calcium phosphate prepared according to the present invention is applied to an industrial or indoor air purifier or the like.
The present invention is also directed to provide a composition capable of removing harmful gas and odor by being applied to a filter, a pollution mask or the like.
In order to solve the above problems, a method for preparing calcium phosphate according to the present invention characterized in that the method includes, (a) preparing a calcium salt solution of 0.5 to 1.5 M, a phosphate solution of 0.3 to 0.8 M, and a carbonate solution of 0.1 to 0.5 M; (b) mixing the phosphate solution and the carbonate solution of above-mentioned step (a) to prepare a mixed solution; (c) adding a basic solution into the calcium salt solution of above-mentioned step (a); (d) adding a basic solution into the mixed solution of above-mentioned step (b); (e) mixing and reacting the calcium salt solution into which the basic solution has been added in above-mentioned step (c) with the mixed solution into which the basic solution has been added in above-mentioned step (d) to prepare a precipitate; and (f) filtering, washing and drying the precipitate of above-mentioned step (e) to obtain calcium phosphate, wherein a primary particle size of the calcium phosphate is 100 nm or less, and a specific surface area is 40 to 150 m2/g.
According to an embodiment, it is preferable that the calcium salt is one or more selected from the group consisting of Ca(NO3)2, Ca(OH)2, CaCO3, Ca(CH3COO)2, CaCl2) and CaSO4, the phosphate is one or more selected from the group consisting of (NH4)2HPO4, NH4H2PO4, H3PO4, H4P207, NaH2PO4 and KH2PO4, and the carbonate is at least one selected from the group consisting of (NH4)2CO3, NH4HCO3, K2CO3 and Na2CO3.
According to an embodiment, it is preferable that in above-mentioned step (c), the basic solution is added such that the calcium salt solution of above-mentioned step (a) has a pH of 8 to 12, and in above-mentioned step (d), the basic solution is added such that the mixed solution of above-mentioned step (b) has a pH of 8 to 12.
According to an embodiment, it is preferable that the basic solution is one or more selected from the group consisting of NH4OH, NaOH, KOH, LiOH and Mg(OH)2.
According to an embodiment, it is preferable that in above-mentioned step (f), the precipitate of above-mentioned step (e) is filtered with a filter, washed with distilled water or an organic solvent, and dried at a temperature of 50 to 100° C.
A composition for removing harmful gas and odor according to another embodiment of the present invention is characterized in that the composition includes, calcium phosphate as an active ingredient, and based on 100 wt % of the total composition, 0.1 to 10 wt % of calcium phosphate, 0.5 to 20 wt % of a binder, 69 to 99.35 wt % of a carrier solution and 0.05 to 1 wt % of a surfactant, wherein the calcium phosphate has a specific surface area of 40 m2/g or more, and removes least 10% or more of one or more harmful gases selected from the group consisting of nitrogen oxide (NOx), volatile organic compounds (VOCs), carbon monoxide (CO) and ammonia (NH3).
According to an embodiment, it is preferable that the calcium phosphate is hydroxyapatite.
According to an embodiment, it is preferable that the binder is one or more selected from the group consisting of polyvinyl alcohol, alginic acid, gelatin, cellulose, and derivatives thereof.
According to an embodiment, it is preferable that the carrier solution is one or more selected from the group consisting of water, ethanol, methanol, ethyl acetate, butanol, propylene glycol, butylene glycol and glycerin.
According to an embodiment, it is preferable that the surfactant is polyoxyalkylene-based.
According to an embodiment, it is preferable that a substance capable of generating the odor is methyl sulfide, hydrogen sulfide, methyl disulfide, methyl sulfide trimethyl amine, and sulfurous acid.
According to a method for preparing calcium phosphate of the present invention and a composition for removing harmful gas and odor containing calcium phosphate obtained therefrom, it can be used as an adsorbent or catalyst capable of removing harmful gases that are harmful to the human body in the air or that are generated in various factories and is superior in performance than a conventional adsorbent or catalyst for removing harmful gas, and is advantageous in that durability and stability can be ensured. In addition, by simply applying by way of spraying on a filter of an air purifier, on an air filter of a car, a pollution mask and such, it is possible to increase the efficiency of the filter and effectively remove odors as well, and the manufacturing process is simple, thereby lowering the manufacturing costs and having an economical effect.
First, Ca(NO3)2 was added to distilled water and stirred at room temperature (25° C.) for 30 minutes to prepare 100 ml of a 1 M Ca(NO3)2 solution (first solution).
Next, (NH4)2PO4 was added to distilled water and stirred at room temperature (25° C.) for 30 minutes to prepare 100 ml of a 0.6 M (NH4)2HPO4 solution (second solution) and (NH4)2CO3 was added to distilled water and stirred at room temperature (25° C.) for 30 minutes to prepare 100 ml of a 0.3 M (NH4)2CO3 solution (third solution).
The prepared 0.6 M (NH4)2HPO4 solution (second solution) and 0.3 M (NH4)2CO3 solution (third solution) were rapidly mixed and then NH4OH was added dropwise to adjust the pH to 10. NH4OH was added dropwise to 1 M Ca(NO3)2 solution (first solution) to adjust the pH to 10.
Thereafter, the mixed solution of the two solutions and 1 M Ca(NO3)2 solution were rapidly mixed and stirred at room temperature (25° C.) for 30 minutes to prepare a precipitate.
Finally, the precipitate was filtered with a filter, washed with distilled water and ethyl alcohol, and dried at 60° C. for 12 hours to complete the preparation of calcium phosphate.
Hereinafter, a preferable exemplary embodiment of the present invention will be described in detail with reference to the accompanying drawings.
The advantages and features of the present invention and the manner of accomplishing it will become apparent with reference to the embodiments described in detail below with reference to the accompanying drawings.
The present invention may, however, be embodied in many different forms and should not be construed as limited to the exemplary embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully disclose the present invention and to fully convey the scope of the invention to those skilled in the art. In addition, the invention is only defined by the scope of the claims.
Further, in the following description of the present invention, if it is determined that related arts or the like may obscure the gist of the present invention, detailed description thereof will be omitted.
Hereinafter, a method for preparing calcium phosphate according to an embodiment of the present invention will be described with reference to
The method for preparing calcium phosphate according to an embodiment of the present invention is characterized in that the method includes, (a) preparing a calcium salt solution, a phosphate solution, and a carbonate solution; (b) mixing the phosphate solution and the carbonate solution of the above-mentioned step (a) to prepare a mixed solution; (c) adding a basic solution into the calcium salt solution of the above-mentioned step (a); (d) adding a basic solution into the mixed solution of the above-mentioned step (b); (e) mixing and reacting the calcium salt solution into which the basic solution has been added in the above-mentioned step (c) with the mixed solution into which the basic solution has been added in the above-mentioned step (d) to prepare a precipitate; and (f) filtering, washing and drying the precipitate of the above-mentioned step (e) to obtain calcium phosphate.
In the method for preparing calcium phosphate according to an embodiment of the present invention, the above-mentioned step (a) in S100 is a step of preparing a calcium salt solution, a phosphate solution, and a carbonate solution.
The calcium salt solution may be prepared by mixing calcium salt and distilled water at a temperature of room temperature (22 to 30° C.) for 10 to 60 minutes using a stirrer, and more specifically, by mixing them for 30 minutes. The concentration of the calcium salt solution may be 0.5 to 1.5 M, and specifically may be 1 M. The concentration range of the calcium salt solution is for preparing calcium phosphate having a high specific surface area, and so in the case where the concentration is out of the above range, it affects the properties of the final product. Therefore, the above range is preferable.
Further, the phosphate solution and the carbonate solution are also prepared by the same method as the calcium salt solution, and the description of the preparation method is omitted.
The concentration of the phosphate solution may be 0.3 to 0.8 M, and specifically may be 0.6 M. The concentration range of the calcium salt solution is for preparing calcium phosphate having a high specific surface area, and so in the case where the concentration is out of the above range, it affects the properties of the final product. Therefore, the above range is preferable.
The concentration of the carbonate solution may be 0.1 to 0.5 M, and specifically may be 0.3 M. The concentration range of the carbonate solution is for preparing calcium phosphate having a high specific surface area, and so in the case where the concentration is out of the above range, it affects the properties of the final product. Therefore, the above range is preferable.
The calcium salt may be one or more selected from the group consisting of Ca(NO3)2, Ca(OH)2, CaCO3, Ca(CH3COO)2, CaCl2 and CaSO4, and specifically may be Ca(NO3)2.
The phosphate may be one or more selected from the group consisting of (NH4)2HPO4, NH4H2PO4, H3PO4, H4P2O7, NaH2PO4 and KH2PO4, and specifically may be (NH4)2HPO4.
The carbonate may be one or more selected from the group consisting of (NH4)2CO3, NH4HCO3, K2CO3 and Na2CO3, and specifically may be (NH4)2CO3.
In the method of preparing calcium phosphate according to an embodiment of the present invention, the above-mentioned step (b) in S200 is a step of mixing a phosphate solution and a carbonate solution of the above-mentioned step (a) in S100.
The step of preparing the mixed solution of the above-mentioned step (b) in S200 is not limited as long as it is a method capable of rapid mixing.
In the method for preparing calcium phosphate according to an embodiment of the present invention, the above-mentioned step (c) in S300 is a step of adding a basic solution into the Ca(NO3)2 solution of the above-mentioned step (a) in S100.
In the above-mentioned step (c) in S300, the basic solution may be added such that the calcium salt solution of the above-mentioned step (a) in S100 has a pH of 8 to 12, and specifically, may be added such that the calcium salt solution of the above-mentioned step (a) in S100 has a pH of 10.
If the pH of the calcium salt solution exceeds 12, Ca ions are re-precipitated in the form of Ca(OH)2, which affects the properties of the final product, and therefore the above range is preferable.
In the method of preparing calcium phosphate according to an embodiment of the present invention, the above-mentioned step (d) in S400 is a step of adding a basic solution into the mixed solution of the above-mentioned step (b) in S200.
In the above-mentioned step (d) in S400, the basic solution may be added such that the mixed solution of the above-mentioned step (b) in S200 has a pH of 8 to 12, and specifically, may be added such that the mixed solution of the above-mentioned step (b) in S200 has a pH of 10. In the case where the pH of the mixed solution in which the phosphate solution and the carbonate solution are mixed is out of the above range, it affects the properties of the final product. Therefore, the above range is preferable. The pH of the Ca(NO3)2 solution of the above-mentioned step (c) in S300 and the mixed solution of the above-mentioned step (d) in S400 can be measured using a pH meter, and a description thereof will be omitted.
In the method for preparing calcium phosphate according to an embodiment of the present invention, the above-mentioned step (e) in S500 is a step of mixing and reacting the calcium salt solution into which the basic solution has been added in the above-mentioned step (c) in S300 with the mixed solution into which the basic solution has been added in the above-mentioned step (d) in S400 to prepare a precipitate.
Here, the precipitate may be precipitated calcium phosphate.
The basic solution may be one or more selected from the group consisting of NH4OH, NaOH, KOH, LiOH, and Mg (OH)2, and may specifically be NH4OH.
The above-mentioned step (e) in S500 may be performed using a stirrer for 10 to 120 minutes and specifically, may be performed by using a stirrer for 30 minutes.
In the method for preparing calcium phosphate according to an embodiment of the present invention, the above-mentioned step (f) in S600 is a step of filtering, washing and drying the precipitate of the above-mentioned step (e) in S500 to obtain calcium phosphate.
In the above-mentioned step (f) in S600, the precipitate of the above-mentioned step (e) in S500 may be filtered with a filter, washed with distilled water or an organic solvent, and dried at a temperature of 50 to 100° C.
The filtering of the precipitate in the above-mentioned step (e) in S500 is for removing residue remaining in the solution after the reaction of step (e) in S500 and for recovering the generated calcium phosphate, but not limited as long as it is a method capable of obtaining calcium phosphate generated in the solution.
The precipitate of step (e) in S500 may be filtered and then washed with distilled water or organic solvent, wherein the precipitate may be washed repeatedly 2 to 3 times using the distilled water or the organic solvent, may be re-dispersed in the organic solvent, or may be washed alternately between distilled water and organic solvent, but the method is not limited.
The organic solvent is not limited as long as it can wash the precipitate, such as ethyl alcohol, methyl alcohol and the like.
After washing the precipitate, the washed precipitate may be dried at a temperature of 50 to 100° C. for 10 to 24 hours. Specifically the precipitate may be dried at a temperature of 60° C. for 12 hours. If the drying temperature is less than 50° C., the precipitate may not be dried well, and if the drying temperature exceeds 100° C., discoloration and property change of the precipitate may occur. Therefore, the above range is preferable.
The precipitate obtained in the above-mentioned step (f) in S600 may be calcium phosphate, and the specific surface area may range from 40 to 150 m2/g. In addition, the primary particle size of the calcium phosphate is 100 nm or less, and the primary particles may be in an aggregated form. Specifically, the size of the primary particle may be 1 to 100 nm.
The harmful gas to be removed by using the calcium phosphate prepared according to the method of the present invention may be one or more selected from the group consisting of nitrogen oxide (NOx), volatile organic compounds (VOCs), carbon monoxide (CO), ammonia (NH3), and the substance capable of generating odor may include methyl sulfide, hydrogen sulfide, methyl disulfide, methyl sulfide trimethyl amine, sulfurous acid, and the like.
Calcium phosphate according to an embodiment of the present invention may be provided.
The primary particle size of the calcium phosphate is 100 nm or less, and the primary particles may be in an aggregated form. Specifically, the size of the primary particle may be 1 to 100 nm.
The calcium phosphate may have a specific surface area ranging from 40 to 150 m2/g.
The calcium phosphate may have a harmful gas removal efficiency of 78 to 99.8%.
In the present invention, the primary particle means calcium phosphate.
The composition for removing harmful gas and odor according to another embodiment of the present invention may be provided.
The composition for removing harmful gas and odor according to another embodiment of the present invention is characterized in that the composition contains calcium phosphate as an active ingredient.
Specifically, the calcium phosphate may be hydroxyapatite.
The hydroxyapatite may be several nanometers to several tens of nanometers in size and may have a specific surface area of 40 m2/g or more.
The hydroxyapatite is a kind of calcium phosphate and is used as a substitute for a hard tissue of a living body such as artificial root for teeth or bone filler. A single crystal-like rod-type hydroxyapatite is used for increasing the fracture strength of an artificial bone. In addition, since the hydroxyapatite has both positive (+) and negative (−) charged surfaces of the crystal, it is possible to significantly increase the adsorbing ability, and thus has excellent deodorizing effects and is also used for soap and natural inorganic antibacterial agents. Further, other than the co-precipitation method, the hydroxyapatite may be synthesized by a hydrothermal synthesis method or a solid-phase reaction method, and a technique for controlling the aspect ratio of apatite and a technique for inducing defects on the crystal structure is applied to control the area and surface polarity intensity of the positive (+) and negative (−) charged surfaces, thereby it is possible to improve the adsorption ability of a target.
The hydroxyapatite is a solid component, and based on 100 wt % of a composition according to an embodiment of the present invention, the solid component may include 0.1 to 10 wt %, and when the solid content is out of the above range, the solid content cannot be uniformly dispersed in the composition, and the efficiency of the initial fractionation removal of the filter or pollution mask can be hindered.
The composition for removing harmful gas and odor according to another embodiment of the present invention may further include a binder, a carrier solution and a surfactant, and the content of the carrier solution may vary depending on the content of calcium phosphate in the composition.
Specifically, based on 100 wt % of the total composition, the calcium phosphate, the binder, the carrier solution, and the surfactant may be included in an amount of 0.1 to 10 wt % of calcium phosphate, 0.5 to 20 wt % of the binder, 69 to 99.35 wt % of the carrier solution and 0.05 to 1 wt % of the surfactant.
The calcium phosphate may specifically be hydroxyapatite and may be in powder form.
If the amount of the calcium phosphate is less than 0.1 wt %, the removal efficiency of harmful gas may deteriorate. If the amount of the calcium phosphate exceeds 10 wt %, there is a problem in that dust may be generated because after the composition is applied to the filter and dried, a complete adherence is not made, and therefore the above range is preferable.
If the carrier solution is less than 69 wt %, the hydroxyapatite is not sufficiently dispersed, and spraying cannot be performed uniformly. When the carrier solution exceeds 99.35 wt %, there is a problem in that the content of the binder is too low, so when applied to a filter or pollution mask, it fails to adhere sufficiently to the surfaces and the powder falls off. Therefore, the above range is preferable.
The carrier solution may be one or more selected from the group consisting of water, ethanol, methanol, ethyl acetate, butanol, propylene glycol, butylene glycol, and glycerin. Specifically, it may be water, and may be mixed according to the use environment and conditions.
If the amount of the binder is less than 0.5 wt %, there is a problem in that a solid component as an adsorbent in the composition may not adhere to the filter surface. If the binder exceeds 20 wt %, the viscosity of the binder may be too high to disperse calcium phosphate in the composition and fails to be sprayed uniformly. Therefore, the above range is preferable.
The binder may be one or more selected from the group consisting of polyvinyl alcohol, alginic acid, gelatin, cellulose and derivatives thereof, and may be specifically polyvinyl alcohol. The binder may be a solid component or may be used in a state dissolved in a solvent. In the case the binder is dissolved in a solvent, the solvent is included in the weight percentage of the organic solvent.
The surfactant may be a polyoxyalkylene-based surfactant and is not limited if it serves as a de-foaming agent and enhances the stability of dispersion.
If the amount of the surfactant is less than 0.05 wt %, the de-foaming function cannot be performed and so foaming may occur. If the amount of the surfactant exceeds 1 wt %, it may affect the adsorbing property of the raw material and is not economically preferable. Therefore, the above range is preferable.
The composition for removing harmful gas and odor according to another embodiment of the present invention may further include additives, a bactericide, and a perfume component that can improve the harmful gas removal efficiency in addition to the composition components described above. The % by weight of the further added components may be subtracted from the % by weight of the carrier solution, and the kind thereof is not limited.
The harmful gas to be removed in the present invention may be one or more selected from the group consisting of nitrogen oxide (NOx), volatile organic compounds (VOCs), carbon monoxide (CO), and ammonia (NH3), and the substance capable of generating odor may include methyl sulfide, hydrogen sulfide, methyl disulfide, methyl sulfide trimethyl amine, sulfurous acid, and the like.
According to another embodiment of the present invention, the composition for removing harmful gases and odors can remove 10% or more of one or more harmful gases selected from the group consisting of nitrogen oxide (NOx), volatile organic compounds VOCs, carbon monoxide (CO), and ammonia (NH3) and can remove 10 to 100% of harmful gas and odor according to environment, conditions and material.
The composition for removing harmful gas and odor according to the present invention may be prepared by using the above-mentioned calcium phosphate, water, polyvinyl alcohol and surfactant using a mechanical stirrer, and the stirring temperature and stirring time are not limited.
According to another embodiment of the present invention, a spray for removing harmful gas and odor may be provided, characterized in that the spray includes a case for spraying and a composition to be filled in the case, and the composition, includes a case for spraying and a composition to be filled in the case, and based on 100 wt % of the total composition, the composition includes 0.1 to 10 wt % of calcium phosphate, 0.5 to 20 wt % of a binder, 69 to 99.35 wt % of a carrier solution and 0.05 to 1 wt % of a surfactant.
The case for spraying is not limited to a generally used spraying device, and when spraying a large amount on a filter, the composition may be sprayed using a spray gun connected to a high-capacity compressor. Further, the viscosity and the weight ratio of the composition are described above, and a description thereof will be omitted.
The composition for removing harmful gas and odor according to an embodiment of the present invention may be applied by the above-described spray, or may be spray-applied using a spray gun connected to a compressor, but is not limited thereto, and the type is not limited as long as it can be applied in liquid form.
Hereinafter, the present invention will be described in more detail with reference to specific examples.
First, Ca(NO3)2 was added to distilled water and stirred at room temperature (25° C.) for 30 minutes to prepare 100 ml of a 1 M Ca(NO3)2 solution (first solution).
Next, (NH4)2PO4 was added to distilled water and stirred at room temperature (25° C.) for 30 minutes to prepare 100 ml of a 0.6 M (NH4)2HPO4 solution (second solution) and then (NH4)2CO3 was added to distilled water and stirred at room temperature (25° C.) for 30 minutes to prepare 100 ml of a 0.3 M (NH4)2CO3 solution (third solution).
The prepared 0.6 M (NH4)2HPO4 solution (second solution) and 0.3 M (NH4)2CO3 solution (third solution) were rapidly mixed and then NH4OH was added dropwise to adjust the pH to 10. NH4OH was also added dropwise to 1 M Ca(NO3)2 solution (first solution) to adjust the pH to 10.
Thereafter, the mixed solution of the two solutions and 1 M Ca(NO3)2 solution were rapidly mixed and stirred at room temperature (25° C.) for 30 minutes to prepare a precipitate.
Finally, the precipitate was filtered with a filter, washed with distilled water and ethyl alcohol, and dried at 60° C. for 12 hours to complete the preparation of calcium phosphate.
10 g of the calcium phosphate powder prepared according to Example 1 and 1 g of a surfactant were prepared.
600 ml of a solution of polyvinyl alcohol (5 wt %) and 389 ml of water were mixed and prepared.
Finally, the prepared raw materials were placed in a mechanical stirrer and stirred at 25° C. to complete the preparation of the composition.
A composition was prepared in the same manner as in Example 2 except that 20 g of calcium phosphate powder and 379 ml of water were added in place of 10 g of calcium phosphate powder and 389 ml of water.
A composition was prepared in the same manner as in Example 2 except that 30 g of calcium phosphate powder and 369 ml of water were added in place of 10 g of calcium phosphate powder and 389 ml of water.
A composition was prepared in the same manner as in Example 4 except that 319 ml of water, 40 ml of natural cypress water, and 10 ml of natural cypress oil were added in place of 369 ml of water.
A composition was prepared in the same manner as in Example 4, except that a commercially available A-type calcium phosphate powder of C company was used instead of the synthesized calcium phosphate powder.
The composition was prepared in the same manner as in Example 4, except that a commercially available B-type calcium phosphate powder of C company was used instead of the synthesized calcium phosphate powder.
A commercially available pollution mask was purchased and prepared.
Making of Test Equipment
To confirm the removal of harmful gas of the calcium phosphate prepared according to Example 1, a self-made test instrument was made as shown in
Briefly described, the test instrument 1 is configured to have an upper gasket adapter 10, a cover filter 20, a gasket 30, a circular hole 40 in the gasket, a lower filter and a pipe gasket adapter 50 which are coupled using a clamp, and calcium phosphate may be placed in the circular hole 40 inside the gasket to be used.
The operating principle of the test apparatus is that calcium phosphate is placed in the circular hole 40 in the gasket and then a Tedlar bag in which the harmful gas is collected is injected into the upper gasket adapter 10 and the gas discharged to the pipe gasket adapter 50 of a lower part is recollected and the concentration of the harmful gas can be measured. Harmful gas is sucked in by using a large-sized syringe of 500 ml or more with the pipe gasket adapter 50 of the lower part. The harmful gas collected in the syringe is transferred to a Tedlar gas sampling bag and the concentration can be measured with a harmful gas concentration meter.
A gas sampler (GV-100S) manufactured by Gastec was used for measurement of harmful gas concentration using a tube type gas detector.
(No. 91L was used as the detector tube for measuring formaldehyde (HCHO) gas, and No. 3L was used as the detector tube for measuring ammonia (NH3) gas.)
Formaldehyde was used as the harmful gas. The formaldehyde gas was prepared by vaporizing a formaldehyde solution and collecting it in a Tedlar gas sampling bag. The initial concentration of formaldehyde gas was set to 32 ppm.
In order to measure the concentration change of the harmful gas according to the above test equipment, the formaldehyde gas (concentration: 32 ppm) was injected and then the formaldehyde was collected to measure the concentration.
In addition, 0.1 g of calcium phosphate prepared according to Example 1 was placed in the circular hole in the gasket, and the formaldehyde gas was added to measure the ability of calcium phosphate to remove the formaldehyde gas.
The above procedure (measurement of the ability of calcium phosphate to remove formaldehyde by adding gas) was repeated 10 times and shown in the following Table 1 and
Referring to Tables 1, 2 and
In addition, the calcium phosphate prepared according to Example 1 is more effective because after the measurement of the 10th time (83.87%), as it can be confirmed from the results of the 1st time of remeasuring (89.92%) after being left for 30 minutes, the formaldehyde removal efficiency is improved, and it was also confirmed that after leaving for 3 days, the formaldehyde removal efficiency (97.98%) also improved.
The above results show that the calcium phosphate prepared according to Example 1 (repetition of using and not using) is excellent in formaldehyde removal efficiency and has excellent durability and stability.
Ammonia was used as the harmful gas. The ammonia gas was prepared by vaporizing the ammonia solution and collecting it in a Tedlar gas sampling bag. The concentration of the ammonia gas was set to 30 ppm.
In order to measure the concentration change of the ammonia gas according to the above test equipment, the ammonia gas (concentration: 30 ppm) was added and the ammonia gas was collected to measure the concentration.
Further, 0.1 g of calcium phosphate prepared according to Example 1 was placed in the circular hole in the gasket, and initial ammonia gas was added to measure the ability of calcium phosphate to remove ammonia gas.
The above procedure was repeated 10 times and then left for 30 minutes in the absence of ammonia gas and air flow. The measurement was repeated once and is shown in Table 3 and
Referring to Table 3 and
The reason the ammonia removal efficiency improves starting from the 3rd time more than the 1st time and the 2nd time is because the calcium phosphate located on the test equipment is not uniform at first but becomes more uniform as the experiment is repeated, so it can be seen that the efficiency is maintained.
The above results show that the calcium phosphate prepared according to Example 1 (repetition of using and not using) is excellent in ammonia removal efficiency and has excellent durability.
It was confirmed that the calcium phosphate prepared according to Example 1 had a form of aggregated particles of 100 nm or less and it can be confirmed that the calcium phosphate prepared according to Example 1 has an excellent removal efficiency of harmful gas, resulting from being configured of fine particles.
The calcium phosphate prepared according to Example 1 was measured for particle size and specific surface area by a BET measurement method.
The specific surface area (SSA) of calcium phosphate prepared according to Example 1 was found to be 134.3949 m2/g. It can be confirmed that the calcium phosphate prepared according to Example 1 had an excellent removal efficiency of harmful gas, resulting from a large specific surface area.
The compositions prepared according to Examples 2 to Comparative Example 2 of the present invention were applied to a pollution mask to evaluate the performance.
The compositions prepared according to Example 2 to Comparative Example 2 were sprayed on each of the same pollution masks 20 times about 3 ml, and then naturally dried at room temperature for 90 minutes.
Carbon monoxide and nitrogen oxides were prepared by collecting and diluting exhaust gas from a BMW company diesel vehicle that meets the euro6 standard.
The formaldehyde and ammonia gases were prepared by vaporizing the formaldehyde solution and the ammonia solution and collecting them in a Tedlar gas sampling bag.
A commercially available pollution mask was fixed on a self-made pollution mask test instrument, and the performance evaluation was performed.
Here, in the test apparatus, the gasket and the clamp were used to prevent a leak from occurring in the pollution mask.
The gas concentration was measured using a Gastec's gas sampler (GV-100S) equipped with tube type gas detector.
(No. 91L was used as the detector tube for measuring formaldehyde (HCHO) gas, No. 3L was used as the detector tube for measuring ammonia (NH3) gas, No. 1LC was used as the detector tube for measuring carbon monoxide (CO) and No. 11L was used as the detector tube for measuring nitrogen oxide (NO+NO2).
Tables 4 and 5 below show the compositions prepared according to Examples 2 to Comparative Example 2 applied to a pollution mask and the ability of the pollution mask to remove harmful gases.
Referring to Tables 4 and 5 and
Based on the above test results, it was confirmed that the composition according to the present invention has excellent characteristics of removing harmful gas and odor.
Although the method for preparing calcium phosphate according to an embodiment of the present invention and the composition for removing harmful gas and odor including calcium phosphate obtained by the method have been described above, it will be apparent that various modifications may be made without departing from the scope of the present invention.
Therefore, the scope of the present invention should not be limited by the described embodiments but should be determined by the appended claims as well as the equivalents of the appended claims.
That is, it is to be understood that the foregoing embodiments are illustrative and not restrictive in all respects and that the scope of the present invention is indicated by the appended claims rather than the foregoing description, and it is intended that all changes and modifications derived from the equivalent concept be included within the scope of the present invention.
The method for preparing calcium phosphate according to the present invention and the composition for removing harmful gas and odor containing calcium phosphate obtained therefrom can be used as an adsorbent or catalyst capable of removing harmful gases that are harmful to the human body in the air or that are generated in various factories, and is superior in performance compared to a conventional adsorbent or catalyst for removing harmful gas, and is advantageous in that durability and stability can be ensured. In addition, by simply applying by way of spraying on a filter of an air purifier used indoors, a filter of an air conditioner, an air filter of a vehicle, a pollution mask and such, it is possible to increase the efficiency of the filter and effectively remove odors as well, and the manufacturing process is simple, thereby lowering the manufacturing costs and having an economical effect.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2018-0026164 | Mar 2018 | KR | national |
| 10-2018-0030844 | Mar 2018 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2019/001712 | 2/12/2019 | WO | 00 |