The present invention relates to a method for producing a catalyst used to synthesize a cyclic carbonate, a catalyst obtained by this method, and a method for synthesizing a cyclic carbonate with use of this catalyst.
A cyclic carbonate is one of important compounds used for many applications as organic solvents, synthetic fiber-processing agents, materials for medicines, cosmetic additives, electrolyte solvents for lithium cells, and further as intermediates for synthesizing alkylene glycols and dialkyl carbonates.
Heretofore, such a cyclic carbonate is synthesized by reacting an epoxide and carbon dioxide in the presence of a homogeneous catalyst under a suitable pressure. As the homogeneous catalyst, halides of alkali metals (Patent Literature 1) and onium salts such as quaternary ammonium salts (Patent Literature 2) are well known for a long time and are used industrially.
However, when such a homogeneous catalyst is used, it generally requires a separation procedure, such as distillation of the catalyst from the reaction mixture. Thus, not only the production process is complicated but also some problems such as degradation of catalyst and formation of byproducts may occur during separation step.
Then, for the purpose of simplifying the separation process of catalysts, a heterogeneous catalyst which has immobilized a quaternary phosphonium group having a halide ion as the counterion to a carrier such as silica gel has been proposed (Patent Literature 3). This catalyst can be produced by reacting a trialkyl phosphine and a commercially available carrier in which a haloalkyl chain is immobilized to a silica gel via a covalent bond to form a quaternary phosphonium product.
However, the production method disclosed in Patent Literature 3 needs the quaternary phosphonium formation reaction at a high temperature for a long period, and a considerable amount of the haloalkyl chains remains unreacted with the phosphine even if the reaction is performed for a long period.
Without using a commercially available product, a silica gel in which a haloalkyl chain or a haloaryl chain is immobilized by a covalent bond can be obtained by reacting a silane compound such as 3-bromopropyltriethoxysilane with a silica gel in toluene under reflux conditions. However, the reaction speed in this reaction is decreased generally when the concentration of the silane compound is decreased. Therefore, a large excess amount of the silane compound (several times to several ten times the amount of the silica gel) is used in order to introduce a sufficient amount of the haloalkyl chain, or the repeated operations of distilling the reaction solution so as to raise the concentration of the silane compound are employed.
However, when a large amount of the silane compound is used, not only a condensate between the silane compounds becomes easy to be formed, resulting in decrease of the catalytic activity, but also wastes in the manufacturing process of the catalyst increase, resulting in the reduction of production efficiency for the catalyst. In addition, a method for promoting the reaction while distilling off the solvent requires not only a complicated reaction system but also an increased number of steps.
As a method for easily producing a catalyst in which a quaternary phosphonium having a halide ion as the counterion is immobilized as described in Patent Literature 3, there has been proposed a method of preliminarily reacting 3-bromopropyltriethoxysilane and diphenyl monoalkyl phosphine to form a quaternary phosphonium and then modifying the surface of a carrier with use of this quaternary phosphonium compound as a catalyst crosslinking agent (Patent Literature 4).
However, when a silane compound obtained by the reaction with a diphenylmonoalkylphosphine to form a quaternary phosphonium is used as a catalyst crosslinking agent, the amount of the silane compound that binds to the silica gel surface is limited due to the steric hindrance. Thus, the supported amount of halogen and phosphorus is far from sufficient. Moreover, since a byproduct is formed as a result of the reaction between the quaternary phosphonium salt and the silane compound in the presence of silica gel, it is difficult to produce a catalyst exhibiting an activity that is corresponding to the amount of the phosphonium salt and the silane compound used.
Accordingly, the present invention relates to a method for easily producing a heterogeneous catalyst having excellent catalytic activity at a low cost, said heterogeneous catalyst being used for the purpose of synthesizing a cyclic carbonate by subjecting to a reaction an epoxide with carbon dioxide; a catalyst which is obtained by this production method; and a method for synthesizing a cyclic carbonate with use of this catalyst.
Then, as a result of extensive studies, the present inventors have found that a catalyst for synthesizing a cyclic carbonate can be easily and inexpensively manufactured by reacting a silane compound having a haloalkyl group or a haloaryl group with a silica gel in the presence of xylene to obtain a catalyst precursor and then reacting the catalyst precursor and a tertiary phosphine, said catalyst exhibiting excellent catalytic activity even if the amount used of the silane compound is small or the reaction time is short. The present invention has been completed based on these findings.
That is, the present invention provides a method for producing a catalyst that is used for the purpose of synthesizing a cyclic carbonate by reacting an epoxide and carbon dioxide. The method includes the following steps (a) and (b):
(a) a step of obtaining a catalyst precursor having a haloalkyl group or a haloaryl group by reacting a silane compound with a silica gel in the presence of xylene, the silane compound having a haloalkyl group or a haloaryl group and
(b) a step of obtaining a catalyst for synthesizing a cyclic carbonate by reacting the catalyst precursor obtained in step (a) with a tertiary phosphine.
Further, the present invention provides the catalyst obtained by the production method, the catalyst being used for the purpose of synthesizing a cyclic carbonate by reacting an epoxide with carbon dioxide.
In addition, the present invention provides a method for synthesizing a cyclic carbonate, comprising reacting an epoxide with carbon dioxide in the presence of the catalyst.
According to the manufacturing method of the present invention, a heterogeneous catalyst capable of synthesizing a cyclic carbonate in a high conversion rate and a high yield and having excellent catalytic activity can be easily and inexpensively manufactured even in the case where the amount used of the silane compound is small or the reaction time is short.
Thus, the catalyst of the present invention is useful as a catalyst for use in synthesizing a cyclic carbonate by reacting an epoxide with carbon dioxide. Further, according to the synthesis method of a cyclic carbonate of the present invention, the cyclic carbonate can be synthesized in a high conversion rate and a high yield.
The production method of a catalyst for use in synthesizing a cyclic carbonate by reacting an epoxide with carbon dioxide according to the present invention comprises the above steps (a) and (b).
[Step (a)]
Step (a) is a step of obtaining a catalyst precursor having a haloalkyl group or a haloaryl group by reacting a silane compound with a silica gel in the presence of xylene (silanization reaction), the silane compound having a haloalkyl group or a haloaryl group.
By using xylene as the solvent in step (a), it is possible to obtain a catalyst precursor having sufficient halogen content. When the concentration of the silane compound is low in the silanization reaction of silica gel, the reaction proceeds slowly and thus the reaction is carried out in the presence of a large excess amount of the silane compound, which is several times to several ten times the desired carried amount, or the reaction mixture is suitably distilled to partially remove the solvent and the reaction is allowed to proceed using a method to repeat the raising of the concentration of the silane compound. However, according to the method of the present invention, even if the silane compound is used in a small amount or the reaction time is short, it is possible to obtain a catalyst precursor having sufficient halogen content without adopting the approach described above.
The xylene includes any of o-xylene, m-xylene, p-xylene, and a mixture thereof. Note that xylene may be used in combination with other solvents, such as ethylbenzene.
The amount used of xylene is not particularly limited, and is usually from 100 to 1000 parts by mass, preferably from 100 to 750 parts by mass, more preferably from 100 to 500 parts by mass, furthermore preferably from 200 to 300 parts by mass, per 100 parts by mass of silica gel.
Further, the average pore diameter of the silica gel used in the above step (a) is preferably from 3.5 to 50 nm, more preferably from 3.5 to 25 nm, further more preferably from 5 to 20 nm, and especially preferably from 6 to 15 nm, in view of the catalytic activity and the prevention of the occurrence of byproducts in cyclic carbonate synthesis. By using a silica gel having an average pore diameter of such a range, it becomes easy to control the silica gel content and the phosphorus content in the catalyst. By adjusting the average pore diameter to 3.5 nm or more, it is easy to introduce a tertiary phosphine into the pores, enabling to suppress, for example, agglomeration on the surface and clogging of the pores.
In addition, the specific surface area of the silica gel is preferably from 80 to 2,000 m2/g, more preferably from 100 to 1,000 m2/g, further more preferably from 150 to 750 m2/g.
Further, the silica gel is preferably in the shape of particles from the viewpoint of handling properties during separation and recovery processes, etc. The shape of such particles is not particularly limited, and includes, for example, crushed shape, particle shape, bead shape, tablet shape, pellet shape, cylindrical shape, and powder shape, and may be an irregular one. If the silica gel is in the shape of beads, the particle diameter is preferably from 0.1 to 10 mm, more preferably from 0.2 to 8 mm, further more preferably from 0.5 to 5.0 mm. Also, if the silica gel is in the shape of powder, the particle diameter is preferably from 30 to 5,000 mesh, more preferably from 100 to 1,000 mesh.
The average pore diameter, specific surface area, and particle diameter of the silica gel can be measured by, for example, a specific surface area/pore distribution measuring apparatus.
Moreover, silica gel that has been dried in advance is preferable, and silica gel having an amount of adsorbed water of 1% by mass or less (adjusted to 1% by mass or less of adsorbed water content relative to the silica gel) is more preferable. By adjusting the amount of adsorbed water to 1% by mass or less, surface silanol is suppressed to inhibit an excessive carried amount of halogen, thereby improving the catalytic activity.
Here, the amount of adsorbed water refers to an amount of water present in the silica gel pores and it may be measured by a thermogravimetry device.
The drying method of the silica gel is not particularly limited and includes, for example, a method of heating under reduced pressure or in a stream of dry air (or inert gas) and a method of refluxing treatment using a Dean-Stark trap. The solvent used in the refluxing treatment is not particularly limited as long as water can be removed azeotropically; however, from the viewpoint of suppressing the intake of water due to substitution of the solvent, it is preferable to adopt such a solvent as the solvent to be used in step (a) without any substitution.
Silica gel may be treated with an acid such as hydrochloric acid before drying.
In addition, as the silane compound having a haloalkyl group or a haloaryl group used in step (a), those represented by the following formula (1) are preferred. The silane compounds may be used alone or in combination of two or more thereof.
X—R1—Si(OR2)3 (1)
In the formula (1), R1 represents a linear or branched alkylene group having 2 to 8 of carbon atom, an arylene group, an alkarylene group, an arylenealkylene group or an alkylenearylene group; R2 represents an alkyl group having 1 to 4 of carbon atom; and X represents a halogen atom.
In the formula (1), the linear or branched alkylene group having 2 to 8 of carbon atom represented by R1 includes, for example, ethylene group, trimethylene group, propylene group, tetramethylene group, pentamethylene group, hexamethylene group, heptamethylene group, and octamethylene group.
Also, the arylene group represented by R1 is preferably an arylene group having 6 to 10 of carbon atom, such as phenylene group and tolylene group.
The alkarylene group represented by R1 is preferably an alkarylene group having 8 to 10 of carbon atom, such as xylylene group.
The arylenealkylene group represented by R1 is preferably an arylenealkylene group having 6 to 10 of carbon atom, such as phenylene methylene group and phenylene ethylene group.
The alkylenearylene group represented by R1 is preferably an alkylenearylene group having 6 to 10 of carbon atom, such as methylene phenylene group and ethylene phenylene group.
Of these, preferred is a linear or branched alkylene group having 2 to 8 of carbon atom, more preferred is a linear or branched alkylene group having 2 to 6 of carbon atom, and especially preferred is a trimethylene group.
In the formula (1), the alkyl group having 1 to 4 of carbon atom represented by R2 includes, for example, methyl group, ethyl group, propyl group, and butyl group, among which preferred are methyl group and ethyl group, and more preferred is methyl group.
The halogen atom represented by X in the formula (1) includes chlorine atom, bromine atom, and iodine atom, among which bromine atom is preferable.
Specific examples of the silane compounds represented by the formula (1) having a haloalkyl group include, for example, a halo-C2-8 alkyl-trimethoxysilane, a halo-C2-8 alkyl-triethoxysilane, a halo-C2-8 alkyl-tripropoxysilane, a haloalkylaryl trimethoxysilane, a haloalkylaryl triethoxysilane, a haloalkylaryl tripropoxysilane, a haloalkylaralkyl trimethoxysilane, a haloalkylaralkyl triethoxysilane, and a haloalkylaralkyl tripropoxysilane.
The halo-C2-8 alkyl-trimethoxysilane includes, for example, 2-chloroethyltrimethoxysilane, 2-bromoethyltrimethoxysilane, 2-iodoethyltrimethoxysilane, 3-chloropropytrimethoxysilane, 3-bromopropyltrimethoxysilane, 3-iodopropyltrimethoxysilane, 4-chlorobutyltrimethoxysilane, 4-bromobutyltrimethoxysilane, 4-iodobutyltrimethoxysilane, 5-chloropentyltrimethoxysilane, 5-bromopentyltrimethoxysilane, 5-iodopentyltrimethoxysilane, 6-chlorohexyltrimethoxysilane, 6-bromohexyltrimethoxysilane, 6-iodohexyltrimethoxysilane, 7-chloroheptyltrimethoxysilane, 7-bromoheptyltrimethoxysilane, 7-iodoheptyltrimethoxysilane, 8-chlorooctyltrimethoxysilane, 8-bromooctyltrimethoxysilane, and 8-iodooctyltrimethoxysilane.
Moreover, the halo-C2-8 alkyl-triethoxysilane includes, for example, 2-chloroethyltriethoxysilane, 2-bromoethyltriethoxysilane, 2-iodoethyltriethoxysilane, 3-chloropropyltriethoxysilane, 3-bromopropyltriethoxysilane, 3-iodopropyltriethoxysilane, 4-chlorobutyltriethoxysilane, 4-bromobutyltriethoxysilane, 4-iodobutyltriethoxysilane, 5-chloropentyltriethoxysilane, 5-bromopentyltriethoxysilane, 5-iodopentyltriethoxysilane, 6-chlorohexyltriethoxysilane, 6-bromohexyltriethoxysilane, 6-iodohexyltriethoxysilane, 7-chloroheptyltriethoxysilane, 7-bromoheptyltriethoxysilane, 7-iodoheptyltriethoxysilane, 8-chlorooctyltriethoxysilane, 8-bromooctyltriethoxysilane, and 8-iodooctyltriethoxysilane.
The halo-C2-8 alkyl-tripropoxysilane includes, for example, 2-chloroethyltripropoxysilane, 2-bromoethyltripropoxysilane, 2-iodoethyltripropoxysilane, 3-chloropropyltripropoxysilane, 3-bromopropyltripropoxysilane, 3-iodopropyltripropoxysilane, 4-chlorobutyltripropoxysilane, 4-bromobutyltripropoxysilane, 4-iodobutyltripropoxysilane, 5-chloropentyltripropoxysilane, 5-bromopentyltripropoxysilane, 5-iodopentyltripropoxysilane, 6-chlorohexyltripropoxysilane, 6-bromohexyltripropoxysilane, 6-iodohexyltripropoxysilane, 7-chloroheptyltripropoxysilane, 7-bromoheptyltripropoxysilane, 7-iodoheptyltripropoxysilane, 8-chlorooctyltripropoxysilane, 8-bromooctyltripropoxysilane, and 8-iodooctyltripropoxysilane.
The haloalkylaryltrimethoxysilane includes, for example, p-chloromethylphenyltrimethoxysilane, p-(2-chloroethyl)phenyltrimethoxysilane, p-bromomethylphenyltrimethoxysilane, p-(2-bromoethyl)phenyltrimethoxysilane, p-iodomethylphenyltrimethoxysilane, and p-(2-iodoethyl)phenyltrimethoxysilane.
The haloalkylaryltriethoxysilane includes, for example, p-chloromethylphenyltriethoxysilane, p-(2-chloroethyl)phenyltriethoxysilane, p-bromomethylphenyltriethoxysilane, p-(2-bromoethyl)phenyltriethoxysilane, p-iodomethylphenyltriethoxysilane, and p-(2-iodoethyl)phenyltriethoxysilane.
The haloalkylaryltripropoxysilane includes, for example, p-chloromethylphenyltripropoxysilane, p-(2-chloroethyl)phenyltripropoxysilane, p-bromomethylphenyltripropoxysilane, p-(2-bromoethyl)phenyltripropoxysilane, p-iodomethylphenyltripropoxysilane, and p-(2-iodoethyl)phenyltripropoxysilane.
The haloalkylaralkyltrimethoxysilane includes, for example, p-chloromethylbenzyltrimethoxysilane, p-bromomethylbenzyltrimethoxysilane, and p-iodomethylbenzyltrimethoxysilane.
The haloalkylaralkyltriethoxysilane includes, for example, p-chloromethylbenzyltriethoxysilane, p-bromomethylbenzyltriethoxysilane, and p-iodomethylbenzyltriethoxysilane.
The haloalkylaralkyltripropoxysilane includes, for example, p-chloromethylbenzyltripropoxysilane, p-bromomethylbenzyltripropoxysilane, and p-iodomethylbenzyltripropoxysilane.
Specific examples of the silane compounds represented by the formula (1) having a haloaryl group include, for example, a haloaryltrialkoxysilane and a haloaralkyltrialkoxysilane.
The haloaryltrialkoxysilane includes p-chlorophenyltrimethoxysilane, p-bromophenyltrimethoxysilane, p-chlorophenyltriethoxysilane, p-bromophenyltriethoxysilane, p-chlorophenyltripropoxysilane, and p-bromophenyltripropoxysilane.
The haloaralkyltrialkoxysilane includes, for example, p-chlorobenzyltrimethoxysilane, p-bromobenzyltrimethoxysilane, p-iodobenzyltrimethoxysilane, p-chlorobenzyltriethoxysilane, p-bromobenzyltriethoxysilane, p-iodobenzyltriethoxysilane, p-chlorobenzyltripropoxysilane, p-bromobenzyltripropoxysilane, and p-iodobenzyltripropoxysilane.
The amount used of the silane compound is preferably from 0.001 to 0.5 mole, more preferably from 0.01 to 0.1 mole, further more preferably from 0.02 to 0.08 mole, especially preferably from 0.025 to 0.06 mole, relative to 1 mole of silica gel from the viewpoint of catalytic activity and low cost production of the catalyst.
Whereas the reaction temperature of step (a) is not particularly limited, it is preferably from 50 to 160° C., more preferably from 80 to 150° C., further more preferably from to 100-140° C., still more preferably from 110 to 140° C., even more preferably from 125 to 140° C. It is possible to suppress the degradation of the carried silane compound by keeping the reaction temperature at 160° C. or less, while it is possible to increase the reaction rate by keeping the reaction temperature at 50° C. or more.
The reaction time in step (a) is not particularly limited; but, it is preferably from 1 to 30 hours, more preferably from 3 to 28 hours, particularly preferably from 5 to 26 hours. Note that according to the present step (a), it is possible to obtain a catalyst precursor having a sufficient halogen content even if the reaction time is from 5 to 10 hours.
The halogen content in the catalyst precursor having a haloalkyl group or a haloaryl group, obtained in step (a), is preferably 1.0 mmol or less, more preferably from 0.1 to 1.0 mmol, furthermore preferably from 0.2 to 0.95 mmol, still more preferably from 0.3 to 0.9 mmol, even more preferably from 0.3 to 0.75 mmol, especially preferably from 0.3 to 0.5 mmol, per 1 g of the catalyst precursor from the viewpoint of catalytic activity.
By adjusting the amount used of the silane compound having a haloalkyl group or a haloaryl group or performing step (a) in the presence of xylene, a catalyst precursor having a halogen content in the above range can be obtained. Moreover, use of silica gel adjusted to have an amount of adsorbed water of 1% by mass or less becomes easier to further control the halogen content.
The halogen content may be measured in the same manner as in Example described below.
[Step (b)]
Step (b) is a step of obtaining a catalyst for synthesizing a cyclic carbonate by reacting the catalyst precursor obtained in the step (a) with a tertiary phosphine. By reacting the catalyst precursor and a tertiary phosphine, a haloalkyl group or a haloaryl group of the catalyst precursor is converted to a quaternary phosphonium group having a halide anion as the counterion. Thus, the catalyst for cyclic carbonate synthesis contains a quaternary phosphonium group having a halide anion as the counterion.
As the tertiary phosphine used in step (b), those represented by the following formula (2) are preferable. The tertiary phosphines may be used alone or in combination of two or more thereof.
In the formula (2), R3 to R5 each independently represents an alkyl group having 1 to 8 of carbon atom, an aryl group, an aralkyl group, an alkokyalkyl group or an alkoky-substituted aryl group, or a group in which one or more of hydrogen atom contained in these groups are substituted with a hetero atom-containing group.
In the formula (2), the alkyl group having 1 to 8 of carbon atom represented by R3 to R5 may be linear, branched, or circular, and includes, for example, methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, pentyl group, hexyl group, heptyl group, octyl group, and cyclohexyl group.
The aryl group represented by R3 to R5 is preferably an aryl group having 6 to 10 of carbon atom, such as phenyl group, tolyl group, xylyl group, and naphthyl group.
The aralkyl group represented by R3 to R5 is preferably an aralkyl group having 7 to 12 of carbon atom, such as benzyl group.
The alkoxyalkyl group represented by R3 to R5 is preferably an alkoxyalkyl group having 2 to 8 of carbon atom, such as methoxyethyl group.
The aryl group having an alkoxy group as a substituent, represented by R3 to R5, is preferably an alkoxyaryl group having 7 to 14 of carbon atom, such as methoxyphenyl group and dimethoxyphenyl group. Further, whereas the number and position of the alkoxy group of the aryl group may be arbitrary, the number of the alkoxy groups is preferably from 1 to 4, more preferably 1 or 2.
Incidentally, one or more of hydrogen atom contained in the alkyl group having 1 to 8 of carbon atom, aryl group, aralkyl group, alkoxyalkyl group and alkoxy-substituted aryl group described above may be substituted by a group containing a hetero atom. The hetero atom includes, for example, a nitrogen atom, an oxygen atom, a phosphorus atom, a sulfur atom, and a halogen atom (such as a fluorine atom).
Examples of the group containing the hetero atom includes, for example, a nitrogen-containing group (such as amino group, hydrazino group, nitro group, cyano group, isocyano group, and amidino group); an oxygen-containing group (such as alkanoyl group, carboxy group, alkoxycarbonyl group, and hydroxy group); a phosphorus-containing group (such as phosphanyl group, phosphono group, and phosphinyl group); and a sulfur-containing groups (such as sulfo group, sulfanyl group, alkylsulfanyl group, alkylsulfonyl group, alkylsulfonylamino group, alkylaminosulfonyl group, alkylsulfinyl group, alkylaminosulfinyl group, alkylsulfinylamino group, and thiocarboxy group).
Among the groups represented by R3 to R5 as described above, an alkyl group having 1 to 8 of carbon atom is preferable, a linear or branched alkyl group having 1 to 8 of carbon atom is more preferable, a linear or branched alkyl group having 1 to 4 of carbon atom is further more preferable, and butyl group is especially preferable.
Specific examples of the compound represented by the formula (2) include tri-C1-8-alkylphosphine, triarylphosphine diaryl-C1-8-alkylphosphine, aryl-di-C1-8-alkylphosphine, triaralkylphosphine, diaralkyl-C1-8-alkylphosphine, diaralkylarylphosphine, aralkyl-di-C1-8-alkylphosphine, aralkyldiarylphosphine, tris(alkoxyaryl)phosphine, bis(alkoxyaryl) C1-8-alkylphosphine, bis(alkoxyaryl)arylphosphine, bis(alkoxyaryl)aralkylphosphine, (alkoxyaryl)di-C1-8-alkylphosphine, (dialkoxyaryl)di-C1-8-alkylphosphine, alkoxyaryldiarylphosphine, (dialkoxyaryl)diarylphosphine, alkoxyaryldiaralkylphosphine, and (dialkoxyaryl)diaralkylphosphine.
The tri-C1-8-alkylphosphine includes, for example, trimethylphosphine, triethylphosphine, tripropylphosphine, triisopropylphosphine, tri-n-butylphosphine, triisobutylphosphine, tripentylphosphine, trihexylphosphine, triheptylphosphine, trioctylphosphine, tricyclohexylphosphine, dimethylethylphosphine, dimethylpropylphosphine, dimethylisopropylphosphine, dimethyl-n-butylphosphine, dimethylisobutylphosphine, dimethylpentylphosphine, dimethylhexylphosphine, dimethylheptylphosphine, dimethyloctylphosphine, dimethylcyclohexylphosphine, diethylmethylphosphine, diethylpropylphosphine, diethylisopropylphosphine, diethyl-n-butylphosphine, diethylisobutylphosphine, diethylpentylphosphine, diethylhexylphosphine, diethylheptylphosphine, diethyloctylphosphine, diethylcyclohexylphosphine, dipropylmethylphosphine, dipropylethylphosphine, dipropylisopropylphosphine, dipropyl-n-butylphosphine, dipropylisobutylphosphine, dipropylpentylphosphine, dipropylhexylphosphine, dipropylheptylphosphine, dipropyloctylphosphine, dipropylcyclohexylphosphine, diisopropylmethylphosphine, diisopropylethylphosphine, diisopropylpropylphosphine, diisopropyl-n-butylphosphine, diisopropylisobutylphosphine, diisopropylpentylphosphine, diisopropylhexylphosphine, diisopropylheptylphosphine, diisopropyloctylphosphine, diisopropylcyclohexylphosphine, di-n-butylmethylphosphine, di-n-butylethylphosphine, di-n-butylpropylphosphine, di-n-butylisopropylphosphine, di-n-butylisobutylphosphine, di-n-butylpentylphosphine, di-n-butylhexylphosphine, di-n-butylheptylphosphine, di-n-butylethyloctylphosphine, di-n-butylcyclohexylphosphine,
diisobutylmethylphosphine, diisobutylethylphosphine, diisobutylpropylphosphine, diisobutylisopropylphosphine, diisobutyl-n-butylphosphine, diisobutylpentylphosphine, diisobutylhexylphosphine, diisobutylheptylphosphine, diisobutyloctylphosphine, diisobutylcyclohexylphosphine, dipentylmethylphosphine, dipentylethylphosphine, dipentylpropylphosphine, dipentylisopropylphosphine, dipentyl-n-butylphosphine, dipentylisobutylphosphine, dipentylhexylphosphine, dipentylheptylphosphine, dipentyloctylphosphine, dipentylcyclohexylphosphine, dihexylmethylphosphine, dihexylethylphosphine, dihexylpropylphosphine, dihexylisopropylphosphine, dihexyl-n-butylphosphine, dihexylisobutylphosphine, dihexylpentylphosphine, dihexylheptylphosphine, dihexyloctylphosphine, dihexylcyclohexylphosphine,
diheptylmethylphosphine, diheptylethylphosphine, diheptylpropylphosphine, diheptylisopropylphosphine, diheptyl-n-butylphosphine, diheptylisobutylphosphine, diheptylpentylphosphine, diheptylhexylphosphine, diheptyloctylphosphine, diheptylcyclohexylphosphine, dioctylmethylphosphine, dioctylethylphosphine, dioctylpropylphosphine, dioctylisopropylphosphine, dioctyl-n-butylphosphine, dioctylisobutylphosphine, dioctylpentylphosphine, dioctylhexylphosphine, dioctylheptylphosphine, dioctylcyclohexylphosphine, dicyclohexylmethylphosphine, dicyclohexylethylphosphine, dicyclohexylpropylphosphine, dicyclohexylisopropylphosphine, dicyclohexyl-n-butylphosphine, dicyclohexylisobutylphosphine, dicyclohexylpentylphosphine, dicyclohexylhexylphosphine, dicyclohexylheptylphosphine, and dicyclohexyloctylphosphine.
The triarylphosphine includes triphenylphosphine, tritolylphosphine, and trixylylphosphine.
The diaryl-C1-8-alkylphosphine includes, for example, diphenylmethylphosphine, diphenylethylphosphine, diphenylpropylphosphine, diphenylisopropylphosphine, diphenyl-n-butylphosphine, diphenylisobutylphosphine, diphenylpentylphosphine, diphenylhexylphosphine, diphenylheptylphosphine, diphenyloctylphosphine, diphenylcyclohexylphosphine, ditolylmethylphosphine, ditolylethylphosphine, ditolylpropylphosphine, ditolylisoproylphosphine, ditolyl-n-butylphosphine, ditolylisobutylphosphine, ditolylpentylphosphine, ditolylhexylphosphine, ditolylheptylphosphine, ditolyloctylphosphine, ditolylcyclohexylphosphine, dixylylmethylphosphine, dixylylethylphosphine, dixylylpropylphosphine, dixylylisopropylphosphine, dixylyl-n-butylphosphine, dixylylisobutylphosphine, dixylylpentylphosphine, dixylylhexylphosphine, dixylylheptylphosphine, dixylyloctylphosphine, and dixylylcyclohexylphosphine.
The aryl-di-C1-8-alkylphosphine includes phenyldimethylphosphine, phenyldiethylphosphine, phenyldipropylphosphine, phenyldiisopropylphosphine, phenyldi-n-butylphosphine, phenyldiisobutylphosphine, phenyldipentylphosphine, phenyldihexylphosphine, phenyldiheptylphosphine, phenyldioctylphosphine, phenyldicyclohexylphosphine, tolyldimethylphosphine, tolyldiethylphosphine, tolyldipropylphosphine, tolyldiisopropylphosphine, tolyldi-n-butylphosphine, tolyldiisobutylphosphine, tolyldipentylphosphine, tolyldihexylphosphine, tolyldiheptylphosphine, tolyldioctylphosphine, tolyldicyclohexylphosphine, xylyldimethylphosphine, xylyldiethylphosphine, xylyldipropylphosphine, xylyldiisopropylphosphine, xylyldi-n-butylphosphine, xylyldiisobutylphosphine, xylyldipentylphosphine, xylyldihexylphosphine, xylyldiheptylphosphine, xylyldioctylphosphine, and xylyldicyclohexylphosphine.
The triaralkylphosphine includes tribenzylphosphine.
Moreover, the diaralkyl-C1-8-alkylphosphine includes dibenzylmethylphosphine, dibenzylethylphosphine, dibenzylpropylphosphine, dibenzylisopropylphosphine, dibenzyl-n-butylphosphine, dibenzylisobutylphosphine, dibenzylpentylphosphine, dibenzylhexylphosphine, dibenzylheptylphosphine, dibenzyloctylphosphine, and dibenzylcyclohexylphosphine.
The diaralkylarylphosphine includes dibenzylphenylphosphine, dibenzyltolylphosphine, and dibenzylxylylphosphine.
The arakyldi-C1-8-alkylphosphine includes benzyldimethylphosphine, benzyldiethylphosphine, benzyldipropylphosphine, benzyldiisopropylphosphine, benzyldi-n-butylphosphine, benzyldiisobutylphosphine, benzyldipentylphosphine, benzyldihexylphosphine, benzyldiheptylphosphine, benzyldioctylphosphine, and benzylcyclohexylphosphine.
The arakyldiarylphosphine includes benzyldiphenylphosphine, benzylditolylphosphine, and benzyldixylylphosphine.
The tris(alkoxyaryl)phosphine includes tris(2,6-dimethoxyphenyl)phosphine, tri-o-methoxyphenylphosphine, and tri-p-methoxyphenylphosphine.
The bis(alkoxyaryl)C1-8-alkylphosphine includes bis(2,6-dimethoxyphenyl)methylphosphine, bis(2,6-dimethoxyphenyl)ethylphosphine, bis(2,6-dimethoxyphenyl)propylphosphine, bis(2,6-dimethoxyphenyl)isopropylphosphine, bis(2,6-dimethoxyphenyl)n-butylphosphine, bis(2,6-dimethoxyphenyl)isobutylphosphine, bis(2,6-dimethoxyphenyl)pentylphosphine, bis(2,6-dimethoxyphenyl)hexylphosphine, bis(2,6-dimethoxyphenyl)heptylphosphine, bis(2,6-dimethoxyphenyl)octylphosphine, bis(2,6-dimethoxyphenyl)cyclohexylphosphine, di-o-methoxyphenylmethylphosphine, di-o-methoxyphenylethylphosphine, di-o-methoxyphenylpropylphosphine, di-o-methoxyphenylisopropylphosphine, di-o-methoxyphenyl(n-butyl)phosphine, di-o-methoxyphenylisobutylphosphine, di-o-methoxyphenylpentylphosphine, di-o-methoxyphenylhexylphosphine, di-o-methoxyphenylheptylphosphine, di-o-methoxyphenyloctylphosphine, di-o-methoxyphenylcyclohexylphosphine, di-p-methoxyphenylmethylphosphine, di-p-methoxyphenylethylphosphine, di-p-methoxyphenylmethylphosphine, di-p-methoxyphenylethylphosphine, di-p-methoxyphenylpropylphosphine, di-p-methoxyphenylisopropylphosphine, di-p-methoxyphenyl(n-butyl)phosphine, di-p-methoxyphenylisobutylphosphine, di-p-methoxyphenylpentylphosphine, di-p-methoxyphenylhexylphosphine, di-p-methoxyphenylheptylphosphine, di-p-methoxyphenyloctylphosphine, and di-p-methoxyphenylcyclohexylphosphine.
The bis(alkoxyaryl)arylphosphine includes: bis(2,6-dimethoxyphenyl)phenylphosphine, bis(2,6-dimethoxyphenyl)tolylphosphine, bis(2,6-dimethoxyphenyl)xylylphosphine, di-o-methoxyphenylphenylphosphine, di-o-methoxyphenyltolylphosphine, di-o-methoxyphenylxylylphosphine, di-p-methoxyphenylphenylphosphine, di-p-methoxyphenyltolylphosphine, and di-p-methoxyphenylxylylphosphine.
The bis(alkoxyaryl)aralkylphosphine includes: bis(2,6-dimethoxyphenyl)benzylphosphine, di-o-methoxyphenylbenzylphosphine, and di-p-methoxyphenylbenzylphosphine.
The (alkoxyaryl)di-C1-8-alkylphosphine includes: o-methoxyphenyldimethylphosphine, o-methoxyphenyldiethylphosphine, o-methoxyphenyldipropylphosphine, o-methoxyphenyldiisopropylphosphine, o-methoxyphenyldi(n-butyl)phosphine, o-methoxyphenyldiisobutylphosphine, o-methoxyphenyldipentylphosphine, o-methoxyphenyldihexylphosphine, o-methoxyphenyldiheptylphosphine, o-methoxyphenyldioctylphosphine, o-methoxyphenyldicyclohexylphosphine, p-methoxyphenyldimethylphosphine, p-methoxyphenyldiethylphosphine, p-methoxyphenyldipropylphosphine, p-methoxyphenyldiisopropylphosphine, p-methoxyphenyldi-n-butylphosphine, p-methoxyphenyldiisobutylphosphine, p-methoxyphenyldipentylphosphine, p-methoxyphenyldihexylphosphine, p-methoxyphenyldiheptylphosphine, p-methoxyphenyldioctylphosphine, and p-methoxyphenyldicyclohexylphosphine.
The (dialkoxyaryl)di-C1-8-alkylphosphine includes: 2,6-dimethoxyphenyldimethylphosphine, 2,6-dimethoxyphenyldiethylphosphine, 2,6-dimethoxyphenyldipropylphosphine, 2,6-dimethoxyphenyldiisopropylphosphine, 2,6-dimethoxyphenyl-di-n-butylphosphine, 2,6-dimethoxyphenyldiisobutylphosphine, 2,6-dimethoxyphenyldipentylphosphine, 2,6-dimethoxyphenyldihexylphosphine, 2,6-dimethoxyphenyldiheptylphosphine, 2,6-dimethoxyphenyldioctylphosphine, and 2,6-dimethoxyphenyldicyclohexylphosphine.
The alkoxyaryldiarylphosphine includes: o-methoxyphenyldiphenylphosphine, o-methoxyphenylditolylphosphine, o-methoxyphenyldixylylphosphine, p-methoxyphenyldiphenylphosphine, p-methoxyphenylditolylphosphine, and p-methoxyphenyldixylylphosphine.
The (dialkoxyaryl)diarylphosphine includes: 2,6-dimethoxyphenyldiphenylphosphine, 2,6-dimethoxyphenylditolylphosphine, and 2,6-dimethoxyphenyldixylylphosphine.
The alkoxyaryldiaralkylphosphine includes: o-methoxyphenyldibenzylphosphine and p-methoxyphenyldibenzylphosphine.
The (dialkoxyaryl)diarylphosphine includes 2,6-dimethoxyphenyldiphenylphosphine.
The amount used of the tertiary phosphine is preferably from 0.001 to 0.5 mole, more preferably from 0.01 to 0.1 mole, further more preferably from 0.02 to 0.08 mole, and especially preferably from 0.025 to 0.06 mole, per 1 mole of silica gel used in step (a).
Also, the molar ratio of the amount used of the silane compound having a haloalkyl group or a haloaryl group used in step (a) and the tertiaryphosphine [silane compound]/[tertiary phosphine] is preferably from 0.1 to 15, more preferably from 0.1 to 7.5, further more preferably from 0.1 to 1.2, still more preferably from 0.2 to 1.0, still further more preferably from 0.3 to 0.9, even more preferably from 0.4 to 0.9, especially preferably from 0.4 to 0.8, from the viewpoint of catalytic activity.
Moreover, step (b) is preferably carried out in the presence of a solvent, and a hydrocarbon solvent is preferred as the solvent.
As the hydrocarbon solvent, there are exemplified aliphatic hydrocarbon solvents, aromatic hydrocarbon solvents, and alicyclic hydrocarbon solvents. Incidentally, the aliphatic hydrocarbon solvent may be any of normal paraffin solvents (such as n-dodecane) and isoparaffin solvents (such as isododecane). These solvents may be used alone or in combination of two or more thereof.
Among these hydrocarbon solvents, aromatic hydrocarbon solvents are preferred from the viewpoints of suppression of side reactions and reaction rate in the synthesis of cyclic carbonates. The aromatic hydrocarbon solvent includes, for example, toluene, xylene, and ethylbenzene, among which xylene is more preferable. Xylene may be any of o-xylene, m-xylene, p-xylene, and a mixture thereof, and may also be one containing ethylbenzene.
Note that the solvent used in step (a) may be directly used as the solvent in step (b), thereby eliminating the need for the procedure of removing the solvent or drying it. Thus, a catalyst showing an excellent catalytic activity can be more easily obtained.
Whereas the amount used of the solvent is not particularly limited, it is usually from 100 to 2,000 parts by mass, preferably from 100 to 1,750 parts by mass, and more preferably from 500 to 1,500 parts by mass, per 100 parts by mass of the tertiary phosphine.
The reaction temperature in step (b) is not particularly limited; however, it is preferably from 60 to 160° C., more preferably from 100 to 150° C., further more preferably from 110 to 140° C., from the viewpoint of reaction efficiency and suppression of catalyst deterioration due to heat.
Whereas the reaction time in step (b) is not particularly limited, it is preferably from 10 to 100 hours, more preferably from 15 to 50 hours, from the viewpoint of maintaining a sufficient phosphorus content and suppressing an elimination amount of the halogen.
In each step described above, the isolation of the catalyst precursor and catalyst may be performed as needed by appropriately combining the conventional means such as filtration, washing, and drying.
Also, the molar ratio of the halogen content and the phosphorus content [halogen/phosphorus] in the catalyst for cyclic carbonate synthesis obtained in step (b) is preferably from 0.8 to 1.6, more preferably from 1.0 to 1.6, from the viewpoint of catalytic activity and suppression of the occurrence of byproducts in cyclic carbonate synthesis.
The molar ratio [halogen/phosphorus] can be easily adjusted with use of xylene in step (a). Also, it becomes easier to control such a molar ratio by adjusting the amounts used of the silane compound having a haloalkyl group or a haloaryl group and the tertiary phosphine, or by adjusting the average pore diameters of silica gel.
Further, the halogen content in the catalyst for cyclic carbonate synthesis is preferably from 0.25 to 0.8 mmol, more preferably from 0.3 to 0.8 mmol, per 1 g of the catalyst in view of catalytic activity and suppression of the occurrence of byproducts in the synthesis of cyclic carbonates.
The halogen content can be easily controlled by using xylene in step (a).
In addition, the halogen content can be more easily controlled by adjusting the amount used of the silane compound having a haloalkyl group or a haloaryl group, or by adjusting the average pore diameter of the silica gel, or by using a silica gel that has been prepared to have an adsorbed water content of 1% by mass or less.
Also, the phosphorus content in the catalyst for cyclic carbonate synthesis is preferably from 0.25 to 0.6 mmol and more preferably from 0.3 to 0.6 mmol, per 1 g of the catalyst in view of catalytic activity.
The phosphorus content is easily controlled by using xylene in step (a). In addition, the phosphorus content is more easily controlled in the above range by adjusting the amount used of the tertiary phosphine or maintaining the average pore diameter of silica gel from 3.5 to 25 nm.
The catalyst for cyclic carbonate synthesis is a heterogeneous catalyst (solid catalyst) having pores. The average pore diameter is preferably from 1 to 50 nm, more preferably from 3 to 20 nm, further more preferably from 3.5 to 15 nm, still more preferably from 5 to 15 nm, and even more preferably from 6 to 15 nm.
The specific surface area of the catalyst for cyclic carbonate synthesis is preferably from 80 to 2,000 m2/g, more preferably from 100 to 1,000 m2/g.
The content of the halogen and phosphorus, average pore diameter, and specific surface area may be measured in the same manner as in Example below.
Then, according to the manufacturing method of the present invention, a heterogeneous catalyst capable of synthesizing a cyclic carbonate in a high conversion rate, a high selectivity, and a high yield and showing an excellent catalytic activity can be easily manufactured at low cost, even in the case where the amount used of the silane compound is small or the reaction time is short. Further, when synthesizing a cyclic carbonate by using the catalyst obtained in such a production method, there is little formation of byproducts such as bromopropanol and bromoethanol.
The catalyst of the present invention is useful as a catalyst for use in synthesizing a cyclic carbonate by reacting an epoxide with carbon dioxide.
The synthesis method of cyclic carbonates according to the present invention comprises reacting an epoxide with carbon dioxide in the presence of a catalyst obtained by the above production method. The synthesis method may be conducted by a conventional method, but using the catalyst.
The amount used of the catalyst may be appropriately adjusted, and is usually from 0.01 to 106 parts by mass, preferably from 0.1 to 105 parts by mass, more preferably 1 to 104 parts by mass, per 100 parts by mass of the epoxide.
The epoxide is not particularly limited as long as it is a compound containing at least one epoxy ring (three-membered ring consisting of two carbon atoms and one oxygen atom) in the structural formula, and includes, for example, ethylene oxide, propylene oxide, butylene oxide, isobutylene oxide, vinyl ethylene oxide, trifluoromethylethylene oxide, cyclohexene oxide, styrene oxide, butadiene monoxide, butadiene dioxide, 2-methyl-3-phenylbutene oxide, pinene oxide, and tetracyanoethylene oxide.
Among such epoxides, those represented by the following formula (3) are preferred.
In the formula (3), R6 and R7 each independently represent a hydrogen atom, an alkyl group having 1 to 6 of carbon atom, a haloalkyl group having 1 to 6 of carbon atom, an alkenyl group having 2 to 6 of carbon atom, or a haloalkenyl group having 2 to 6 of carbon atom.
The number of carbon atom in the alkyl group and the haloalkyl group represented by R6 and R7 is preferably from 1 to 4. Examples of the alkyl group include groups similar to those as defined for R2. Halogen atom in the haloalkyl group includes a halogen similar to that as defined in X.
Among those represented by the formula (3), ethylene oxide and propylene oxide are preferred.
The synthesis method for cyclic carbonates according to the present invention may be carried out either in the presence or absence of a solvent. If the solvent is used, other than cyclic carbonates as the target compound, it includes, for example, aliphatic hydrocarbons (e.g. pentane, hexane, and heptane); aromatic hydrocarbons (e.g. benzene and toluene); alcohols (e.g. methanol and ethanol); ketone (e.g. acetone and methyl ethyl ketone); ethers (e.g. diethyl ether, methyl-tert-butyl ether, tetrahydrofuran, and dioxane); amides (e.g. dimethylformamide and dimethylacetamide); esters (e.g. ethyl acetate); tertiary amines (e.g. triethylamine, pyridine, methylpyridazine, N,N′-dimethylpyridazinone); sulfides (e.g. dibutyl sulfide); and phosphines (e.g. tributylphosphine). The solvent may be used alone or in combination of two or more thereof.
The reaction temperature of the synthesis method for a cyclic carbonate according to the present invention is preferably from 20 to 160° C., more preferably from 50 to 150° C., further more preferably from 80 to 140° C., from the viewpoint of reaction efficiency.
Whereas the reaction pressure is not particularly limited, it is preferably from 0.1 to 100 MPa, more preferably from 0.5 to 50 MPa, further more preferably from 1.0 to 25 MPa.
In addition, whereas the reaction time is not particularly limited, it is usually from 0.1 to 10 hours, preferably from 0.5 to 5 hours.
The synthesis method of the cyclic carbonate of the present invention can adopt a technique that is commonly used as a reaction mode, such as a stirring system or a fixed bed system. The reaction may be attained in any method of a batch type process, a semi-batch type process, and a continuous flow type process.
The batch type process is performed, for example, in the following manner. An epoxide and a catalyst are charged into an autoclave equipped with a stirring device. The autoclave is filled with carbon dioxide and then sealed. Subsequently, the autoclave is heated to a predetermined temperature while stirring the mixture in the autoclave, and further filled with carbon dioxide, thereby adjusting the internal pressure to a predetermined pressure. After the reaction for a predetermined period of time, the produced cyclic carbonate is separated by a desired means.
The continuous flow type process is performed as shown in
Whereas pretreatment of the catalyst is not particularly required, it is possible to improve the yield of the cyclic carbonate if evacuation is performed at from 20 to 140° C., preferably from 50 to 120° C., prior to the reaction or if treatment is performed in an inert gas stream such as helium, argon, nitrogen, or carbon dioxide.
According to the synthesis method of a cyclic carbonate of the present invention, it is possible to synthesize a cyclic carbonate in which the epoxy ring of the epoxide is converted into a carbonate ring (5-membered ring having an O—CO—O bond). Such a cyclic carbonate includes, for example, ethylene carbonate, propylene carbonate, butylene carbonate, isobutylene carbonate, trifluoromethylethylene carbonate, vinyl ethylene carbonate, cyclohexene carbonate, styrene carbonate, butadiene monocarbonate, butadiene dicarbonate, chloromethyl carbonate, pinene carbonate, and tetracyanoethylene carbonate.
Then, according to these synthesis methods of a cyclic carbonate of the present invention, it is possible to synthesize a cyclic carbonate in a high conversion rate and a high selectivity with a high yield. In the synthesis method, there is also little formation of byproducts such as bromopropanol and 2-bromoethanol.
Hereinafter, the present invention is described in more detail with reference to Examples, which, however, are not intended to restrict the scope of the invention. The average pore diameter, specific surface area, and particle diameter (or particle size) of silica gel are manufacturer's nominal values.
Analytical methods used in each Example and Comparative Example are as follows.
(1) In the production of the catalyst, the bromine-modified amount and the phosphorus-modified amount were measured using the fluorescent X-ray analysis (apparatus: product name “System 3270” (manufactured by Rigaku Industrial Co.), measurement conditions: Rh tube, tube voltage 50 kV, tube current 50 mV, vacuum atmosphere, detector: SC, F-PC).
(2) In the synthesis of cyclic carbonates, analysis of the composition of the reaction solution was performed by using a gas chromatography. The analysis conditions were as follows.
Apparatus: product name “GC-2010 Plus” (manufactured by Shimadzu Corporation)
Detector: FID
INJ temperature: 150° C.
DET temperature: 260° C.
Amount of sample: 0.3 μL
Split ratio: 5
Column: DB-624 (60 m, 0.32 mmID, 1.8 m, manufactured by Agilent Technologies)
Column temperature: 70° C., 3 minutes—5° C./minute—120° C.—10° C./minute—250° C., 5 minutes (31 minutes in total)
Ten grams of bead silica gel (CARiACT Q-10 (average pore diameter 10 nm, particle size 1.2-2.4 mm, specific surface area 300 m2/g), manufactured by Fuji Silysia Chemical Ltd.) and 25 mL of xylene were charged into a 50 mL-flask equipped with a Dean-Stark trap, and azeotropic dehydration of xylene-water was carried out under ref lux at 140° C. for 2 hours to remove the moisture in the silica gel. Then, the Dean-Stark trap was removed from the 50 mL-flask, and the atmosphere in the flask was replaced with nitrogen, after which 1.1 g (4.5 mmol; 0.45 mmol per 1 g of silica gel) of 3-bromopropyltrimethoxysilane was dropwise added to the flask. The mixture was directly heated under reflux at 135° C. for 7 hours so that silanization reaction was carried out.
Subsequently, the resulting reaction product was separated by filtration and washed thoroughly with acetone. Incidentally, it was confirmed that the amount of 3-bromopropyltrimethoxysilane in the solution after washing was found to be less than 50 ppm by gas chromatographic analysis. The obtained reaction product was placed in a 50 mL-flask and subjected to vacuum drying at 120° C. for 2 hours to yield a catalyst precursor X-1 (bromopropylated silica gel). The analysis results are shown in Table 1.
A catalyst precursor X-2 was manufactured in the same manner as in Manufacturing Example 1-1, except that the heating time was changed to 26 hours from 7 hours. The analysis results are shown in Table 1.
A catalyst precursor X-3 was manufactured in the same manner as in Manufacturing Example 1-1, except that the heating temperature was changed to 110° C. from 135° C. and the heating time was changed to 8 hours from 7 hours, respectively. The analysis results are shown in Table 1.
A catalyst precursor X-4 was manufactured in the same manner as in Manufacturing Example 1-3, except that the heating time was changed to 26 hours from 8 hours. The analysis results are shown in Table 1.
A catalyst precursor T-1 was manufactured in the same manner as in Manufacturing Example 1-1, except that the reaction solvent was changed to toluene from xylene, the reaction temperature was changed to 110° C. (under reflux) from 135° C., and the heating time was changed to 8 hours from 7 hours, respectively. The analysis results are shown in Table 1.
A catalyst precursor T-2 was manufactured in the same manner as in Manufacturing Example 2-1, except that the heating time was changed to 26 hours from 8 hours. The analysis results are shown in Table 1.
A catalyst precursor T-3 was manufactured in the same manner as in Manufacturing Example 2-1, except that the heating time was changed to 49 hours from 8 hours. The analysis results are shown in Table 1.
A catalyst precursor T-4 was manufactured in the same manner as in Manufacturing Example 2-1, except that the dropping amount of 3-bromopropyltrimethoxysilane was changed to 2.4 g (9.9 mmol; 0.99 mmol per 1 g of silica gel). The analysis results are shown in Table 1.
As shown in Table 1, a sufficient amount of halogen could be carried by using xylene as a solvent for the silanization reaction, even if the amount used of the silane compound having a haloalkyl group or a haloaryl group was small and the reaction time was short. When toluene was used as the solvent for the silanization reaction, a long time reaction was required in order to carry a sufficient amount of the halogen with a small amount of the silane compound (Manufacturing Example 2-3). In order to carry a sufficient amount of the halogen for a short time with use of a small amount of the silane compound, it is necessary to use a large excess amount of the silane compound having a haloalkyl group or a haloaryl group than the amount of halogen to be actually carried (Manufacturing Example 2-4).
The catalyst precursor X-1 (9 g) obtained in Manufacturing Example 1-1 and 30 mL of xylene were charged into a 50 mL-flask, and after the inside of the flask was replaced with nitrogen, 1.8 g of tri-n-butylphosphine was dropwise added thereto. The mixture was directly subjected to quaternary phosphonium formation under heating to reflux at 135° C. for 24 hours. After the reaction, the resulting reaction product was separated by filtration and washed thoroughly with acetone. Incidentally, it was confirmed that the amount of tri-n-butylphosphine in the solution after washing was found to be less than 50 ppm by gas chromatographic analysis. The obtained reaction product was placed in a 50 mL-flask and subjected to vacuum drying at 120° C. for 2 hours to yield a desired catalyst XX-1 (silica gel surface-modified with tributylphosphonium bromide). The analysis results are shown in Table 2.
A catalyst XX-2 was manufactured in the same manner as in Example 1, except that the catalyst precursor X-1 was changed to a catalyst precursor X-2. The analysis results are shown in Table 2.
Catalysts TX-1 and TX-3 were manufactured in the same manner as in Example 1, except that the catalyst precursor X-1 was changed to catalyst precursors T-1 and T-3, respectively. The analysis results are shown in Table 2.
Synthesis of propylene carbonate was carried out by the following batch process, and the activity of the catalyst was evaluated.
The catalyst XX-1 (800 mg) prepared in Example 1 was charged into a 50 ml-autoclave equipped with a stirring bar, and subjected to vacuum drying at 120° C. for 1 hour. After the pressure in the autoclave was brought back to the atmospheric pressure with nitrogen and the temperature was brought back to room temperature, 3.5 g (60 mmol) of propylene oxide was charged thereinto.
Subsequently, carbon dioxide was provisionally filled in the autoclave to 1.5 MPa, and then heating to 100° C. was carried out while stirring the mixture in the autoclave with a rotor at 1000 rpm. After the autoclave was further filled with carbon dioxide so as to adjust the internal pressure to 3 MPa, the reaction was performed for 1 hour. After cooling, the remaining carbon dioxide was released to depressurize the autoclave. The resulting reaction solution was analyzed by gas chromatography. The results are shown in Table 2.
Propylene glycol, 2-bromopropanol, and 1-bromo-2-propanol were detected as impurities. The detection amounts of these bromopropanols were also shown in Table 2.
Propylene carbonate was synthesized by the batch type reaction in the same manner as in Example 3, except that the catalyst XX-1 was changed to a catalyst XX-2, and the catalytic activity was evaluated. The results are shown in Table 2.
Propylene carbonate was synthesized by the batch type reaction in the same manner as in Example 3, except that the catalyst XX-1 was changed to catalysts TX-1 and TX-3, and the catalytic activity was evaluated. The results are shown in Table 2.
Bead silica gel (2,000 g)(CARiACT Q-10 (average pore diameter 10 nm, particle diameter 1.2-2.4 mm, specific surface area 300 m2/g), manufactured by Fuji Silysia Chemical Ltd.) and 5000 mL of xylene were charged into a 10 L three-necked flask equipped with a Dean-Stark trap and a stirring blade, and azeotropic dehydration of xylene-water was carried out under reflux at 140° C. for 2 hours to remove the moisture in the silica gel. The moisture content in the xylene solvent at this time was 14 ppm. Then, the Dean-Stark trap was removed, and the atmosphere in the flask was replaced with nitrogen, after which 219 g (0.846 mmol) of 3-bromopropyltrimethoxysilane was dropwise added to the flask. The mixture was directly heated under reflux at 135° C. for 7 hours so as to perform the silanization reaction.
Subsequently, the resulting reaction product was separated by filtration and washed twice with xylene to obtain 3810 g of a catalyst precursor X-5 (bromopropylated silica gel) containing xylene.
It was confirmed that the amount of 3-bromopropyltrimethoxysilane in the solution after two times washing was less than 50 ppm by the gas chromatographic analysis. The measurement result of the Br-modified amount in the obtained catalyst precursor was 0.38 mmol/g by the fluorescent X-ray analysis. Incidentally, the content of xylene was 57% by mass and the obtained precursor was estimated to be about 2170 g.
The obtained catalyst precursor X-5 and 5000 mL of xylene were charged into a 10 L three-necked flask equipped with a stirring blade, and after the inside of the flask was replaced with nitrogen, 453 g of tri-n-butylphosphine was dropwise added thereto. The mixture was directly subjected to quaternary phosphonium formation under heating at 120° C. for 25 hours. After the reaction, the reaction product was separated by filtration and washed six times with acetone. It was confirmed that the amount of tri-n-butylphosphine in the solution after washing six times was found to be less than 50 ppm by gas chromatographic analysis. The obtained reaction product was subjected to vacuum drying in a stream of nitrogen at 120° C. for 5 hours to yield 2,328 g of a desired catalyst XX-5 (silica gel surface-modified with tributylphosphonium bromide). The analysis results of the catalyst are shown in Table 3.
Synthesis of ethylene carbonate was carried out by the following batch type reaction, and the catalytic activity of the catalyst XX-5 was evaluated.
The catalyst XX-5 (800 mg) prepared in Example 5 was charged into a 50 ml-autoclave equipped with a stirring bar, and subjected to vacuum drying at 120° C. for 1 hour. Then, after the pressure in the autoclave was returned to the atmospheric pressure with nitrogen and the temperature was returned to room temperature, 2.8 g (60 mmol) of ethylene oxide was charged thereinbyto. Subsequently, carbon dioxide was provisionally filled to 1.5 MPa, and heating to 100° C. was carried out while stirring the mixture in the autoclave with a rotor at 1000 rpm. After the autoclave was further filled with carbon dioxide so that the internal pressure was adjusted to 5.0 MPa, the reaction was performed for 1 hour. After cooling, the remaining carbon dioxide was released to depressurize the autoclave. Since the resulting ethylene carbonate has a melting point of 36° C., 4 g of acetonitrile solvent was added to the autoclave so that the reaction mixture was dissolved. The resulting reaction solution was analyzed by gas chromatography to determine the conversion rate of ethylene oxide, selectivity of ethylene carbonate, yield, and the apparent first-order reaction rate constant k. The results are shown in Table 4. The results are shown in Table 4.
Note that the apparent first-order reaction rate constant k was determined by the following equation:
k=−ln(1−X/100)/t
wherein X is a conversion rate (%) and t is a reaction time (hr)
Ethylene glycol, diethylene glycol, and 2-bromoethanol were detected as reaction impurities in the gas chromatograph. The detection amount of 2-bromoethanol was also shown in Table 4.
Ethylene carbonate was synthesized by the batch type reaction in the same manner as in Example 6, except that the catalyst XX-5 was ground in a mortar and the resulting powder was sieved to collect ones having a particle size of 200-400 mesh, which were then used. And the catalytic activity was evaluated. The results are shown in Table 4.
As shown in the above Examples, by using the catalyst obtained according to the production method of the present invention, cyclic carbonates can be synthesized in a high conversion rate and a high yield, and it is also possible to suppress the generation of impurities such as bromopropanol and 2-bromoethanol.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-090239 | Apr 2013 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2014/061279 | 4/22/2014 | WO | 00 |