This invention relates to color wheels for projection systems and to a method for producing color wheels.
The invention pertains to a color wheel of the type employed in generating sequential color images using projection equipment. Such a color wheel can be produced by appropriately coating and configuring a disk-shaped glass substrate. It is especially the configuration process, however, that is expensive. In practice, therefore, a color wheel is in most cases composed of circular sections. It is typically produced by separating ring sectors or circular sections from dichroic plates and attaching them on a rotary disk in such fashion that the outer regions of the circular sections protrude past the rim of the disk and the outer edges of the circular sections form an annular circle. The color wheel thus produced, when to be used, is positioned in the optical path of an illuminating beam which, depending on the optical characteristics of the circular section currently in the optical path, will be transmitted or reflected for instance as a function of the wavelength concerned. Rotating the wheel makes it possible to generate a sequence of different colors.
This invention also relates to a method for producing the circular sections for use in a color wheel. For a more comprehensible description of this invention the following will identify and define some of the geometric parameters of the circular sections with reference to
It is not generally possible to completely and fully cover a two-dimensional area with identical circular arc sections. As an inevitable result, the separation of such circular sections from plate material cannot make full use of all the material, i.e. parts thereof are wasted and the material yield is less than 100%. The plate material is usually preprocessed involving expensive procedures. For example, the plates used in making color wheels are first vacuum-coated. Maximum utilization of the material is therefore desirable. Another factor that further reduces material utilization in the separation process and that depends on the method by which the plate material is separated into circular sections, is the need for the individual circular sections to be more or less spaced apart so that clean, reproducible edges can be obtained. A widely used method for separating substrates from glass plates involves a scoring and breaking process (the S&B method). The surface of the plate material is first scored along the line of the intended edge and the glass is then broken along that line. There must be enough material on both sides of the scored line to permit the application of the force necessary for breaking it and making sure that the break actually follows the line of the intended edge. In that context, enough material means at least three times the thickness of the glass to be broken. If the glass is 1 mm thick, the circular arc sections must consequently be spaced at least 3 mm from the respectively neighboring circular arc section over its entire circumference, unless the circular sections share a common break line.
Accordingly, in order to increase the yield, an attempt is made to position the substrates that are to be cut out by appropriate separation on the plate material from which they are to be obtained, in such fashion that as many joint break lines as possible are produced. That, of course, depends in large measure on the intended geometric shape of the separated sections. For identical circular arc
sections the only possibility is to position a radial edge of a first circular arc section so as to coincide with a radial edge of another circular arc section. If the curvatures of circular arc sections are aligned in matching fashion, additional circular sections can be positioned along the free radial edges, provided they are not more or less completely closed circular arc sections and provided the size of the plate permits it. The circular sections thus form an undulating, serpentine strip. This method is therefore referred to below as the serpentine method.
Another possibility to produce joint cutting edges and thus to achieve a better yield is to use a modified circular section, assuming the application permits it. As an example in the case of the color wheel described, the inside center area of the circular sections is used for the mechanical mounting only, thus allowing the inner annular edge to be varied as necessary.
A desirably modified circular section features an inner annular edge whose curvature matches the outer annular edge. In that case the circular sections can be so positioned that the inner annular edge 7 of a circular section constitutes a common edge break line with the central section 11 of the outer annular edge 5 of another circular section. The circular sections will thus form columns in which they are positioned one above the other. This process is therefore referred to below as the columnar method.
Applying the columnar method by which the inner annular edge is adapted, only a small part of the perimeter shares a joint break line intended to minimize material loss. For the remainder of the perimeter, at least three times the distance to the break line must be allowed to permit proper breaking. Since in most cases the plate material used for the segmentation is preprocessed by a preceding, cost-intensive coating procedure, this loss of material is still a significant factor in terms of the manufacturing cost.
It is the objective of this invention to introduce a solution that overcomes the shortcomings of prior art.
Simply combining the serpentine method and the columnar method will not work: The technician who tries to apply the serpentine method by moving the undulations closer together will fail due to the fact that parts of the outer edges of the mutually adjoining circular sections have a differently oriented curvature, so that a common break line is not possible even in the case of a relatively unencumbered configuration of the inner annular edge.
The technician who, by applying the columnar method along the concept of the serpentine method, tries to align the radial break lines of one column with the radial break lines of another column will fail due to the fact that the circular sections would overlap.
According to this invention, the problem is solved by modifying both the serpentine method and the columnar method in a manner as to make a combination possible starting with a placement along the columnar method, the first step is to alternate the orientation of the curvature of the circular sections in neighboring columns. That already makes it possible, in due consideration of the spacing needed for the separation, to move the columns closer together than in the original columnar method. The columns are thus interlaced to a degree. In a next step the columns are staggered in a way as to permit still closer interlacing. This should progress to a point where the radial edges of neighboring columns form common edge break lines, with the columns meshing tightly. The components of the radial edges and of the outer annular edge that do not form a common break line with other circular arc sections, together in each case with 3 other circular sections, will enclose a resulting loss area that cannot be utilized. To maximize the material yield that area should be held to a minimum for as long as the requirements of the process are and can be met. For example, the S&B process must maintain a spacing of at least three times the thickness of the plate.
A particularly advantageous implementation of this invention is practicable whenever the application permits a modification of the outer annular edge of the circular section. In that case it is possible to tightly interlace the columns and all of the modified circular sections can be positioned on the plate material with common break lines, eliminating any loss of material that would have to be removed.
The following will explain this invention in more detail by means of a few different implementation examples and with reference to the attached drawings in which—
As can be seen, the serpentine method and the columnar method can only be combined by means of the inventive step involving only a partial butting of the radial break lines. Essentially, this can be done in one of two ways: i) Juxtapositioning the radial break lines only to a point where a loss area is intentionally created just large enough to permit the separation (for instance by the S&B method).
ii) A circular section approach is used that employs a modified outer annular edge.
Re i) Example of a Minimized Loss Area
In this example, circular sections are to be obtained from a plate material 1 mm thick. The plate material in this example is a glass plate coated with a color filter for a color wheel. The circular sections to be produced have an outer annular edge with a 40 mm radius of curvature. The central angle is 90°. The radial edges have a length of 22 mm each. The application of the color wheel is such as to permit the curvature of the inner annular edge to be adapted to the curvature of the outer annular edge.
In the example according to the invention, circular sections are positioned in close juxtaposition along the columnar method, in which case the curvature of the circular sections of two neighboring columns is oriented in mutually opposite directions. The radial edges of the circular sections of neighboring columns are positioned next to one another in such fashion that actually only 15.5 mm of their overall length of 22 mm make contact. The remaining 6.5 mm of the radial edges do not bound on another circular section. The result of that arrangement is schematically shown in
ii) Modified Circular Section
The fact that for the optical application of a color wheel the geometry of the outer rim is ultimately of no particular consequence can be used to advantage in the production process.
As is evident in
To avoid that, another form of implementation of the invention retains the radial edge but modifies the curvature of only the outer circular arc section.
The color wheel configured as shown in
The break lines described thus far are all of a more or less curved geometry. In the case of some separating methods, however, producing such curved edges is a fairly difficult matter. Especially when a separating process is to be automated, an edge break line that deviates from a circular arc can pose a substantial technical challenge. Modifying the circular sections in accordance with this invention, where permitted by the intended application, makes it possible to work with break lines containing strictly linear segments. One such design implementation is shown in
For some applications the outer contour of the wheel is of significance, albeit not optical in nature. For example, in practical use the color wheel rotates at more than 80 Hz, typically about 120 Hz. Deviations from the circular contour can be expected to engender air turbulences which in turn can generate noise. To counter such a phenomenon, it is possible to embed the wheel in a circular outer frame, which may even serve as an added stabilizer for the circular sections vis-a-vis any centrifugal force.