METHOD FOR PRODUCING COMPOSITE FILTER TUBE AND FILTER ELEMENT MADE OF MULTILAYER METAL MESH AND METAL POWDERS

Abstract

A method for producing a composite filter tube and filter element made of a multilayer metal mesh and metal powders, including: knitting to obtain metal meshes of different mesh numbers, obtaining a layered structure by means of a lamination method, then putting the layered structure in a vacuum furnace for sintering processing, sintering a metal composite layer to obtain a composite filter sheet and tube made of a multilayer metal mesh and metal powders with a multilayer metal mesh as a structure support layer and a metal powder sinter structure as a filter layer, then rolling the composite filter sheet and tube into a tubular filter element by using a shaping machine, and welding to obtain a composite filter tube and filter element product made of a multilayer metal mesh and metal powders.

Description

FIELD OF TECHNOLOGY

The following relates to the production technology field of oil refining and filtering equipment, and more specifically, to a method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders applied to the S-Zorb units 101, 102, 103, 104, 105, 110, 111, and 108, raw oil filter 104 units, and hydrotreating F100-B units of China Petroleum and Chemical Corporation.

BACKGROUND

Referring to FIG. 1, filter materials are required to provide as high of a filtering flow rate as possible while the filter itself has very low filtration resistance so as to make a larger filtration flux possible, thus reducing energy consumption. However, in practice, for example, various metal-mesh filters and common metal-powder tubes have the disadvantage that filter fineness and filtration flux cannot be achieved simultaneously, i.e. if the filtration flux is high, the filter fineness cannot meet the requirements; when filter fineness is adequate, and the filters cannot meet the requirements in the filtration flux.

In the application field of the petrochemical and steel industries, filters operating in high pressure and high temperature conditions often have low filter fineness that leads to leakage of catalysts and damaged valves and other equipment, causing the whole filtering system to fail and reducing the yield or stopping the production.

At present, the operating pressure differential of the current metal filter element used by China Petroleum and Chemical Corporation in the S-Zorb unit is generally 2.5 mpa-6 mpa. Such metal filter elements have low filtration flux, which leads to low capacity of the whole device.

SUMMARY

An aspect relates to a method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders featuring low filtration resistance, large filtration flux, and good pressure-withstand capability.

This aspect takes the following technical solution to solve the technical problems: a method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders, having the processing steps as below: First, weave wires to form metal wire mesh of different mesh numbers, and then stack up the metal wire meshes of different mesh numbers to obtain a layered structure on the principle that the mesh number increases from one side to the other, and the number of the layers is 1˜5; then put the layered structure in a vacuum furnace for 10˜30 hrs uninterruptedly sintering at 900˜1500° C. to obtain a multi-layer support layer; after cooling down, take the aforesaid supporting layer out, make a metal composite layer with a mesh number of 100˜600 on the side with high mesh number through electrostatic spraying or common spraying and casting method with the thickness of the composite layer controlled within 0.1˜0.5 mm, and then sinter the resultant structure at 900-1500° C., and after cooling down, a composite filter sheet and tube made of a multilayer metal mesh and metal powders with the multiple layers of metal meshes as the supporting layer and the sintered metal power structure as the filtering layer is obtained; then take the composite filter sheet or tube out and roll it into tubular filter elements with a forming machine; weld the middle seam of the tubular filter element with an argon arc welding machine or plasma welding machine to obtain a multilayer metal mesh and metal powder composite filter tube and filter element products.

The supporting structure is a composite one consisting of multilayer metal meshes.

The supporting layer of the structure has a thickness of 1˜19 mm and is formed by stacking up multiple layers of metal meshes with the filter fineness of 1 to 1000 and sintering.

The supporting layer made by weaving metal wires may be sintered with a filtering layer to form a dual-layer composite structure, or be formed with a metal powder sheet to be a composite structure.

The filtering layer with the mesh number of 100˜1000 is attached on the supporting layer and made by low temperature spraying (such as plasma spraying or common spraying) of metal powder and sintering together with the supporting layer.

Examples of metal powders used for the filtering layer are Fe, Co, Ni, W, Mo, Cr, Cu, Al, Ti, Zn, Sn, Ta, Nb, and Zr elementary substance metal powders, or alloy powders combining multiple selections of these metal elements.

Examples of metal meshes used for the supporting layer are formed by weaving Fe, Co, Ni, W, Mo, Cr, Cu, Al, Ti, Zn, Sn, Ta, Nb, and Zr elementary substance metal wires, or alloy wires combining multiple ones of these metal elements.

The composite filter sheet and tube made of a multilayer metal mesh and metal powders is processed to form an asymmetric powder-sintered filter tube with a composite structure by rolling and welding processes.

The beneficial effects of embodiments of the present invention are as below: the composite structure with the multi-layer metal meshes as the supporting layer and the metal powder as the sintered layer has low filtration resistance, great filtration flux, and good pressure withstand capability, and is intended for use with S-Zorb units 101, 102, 103, 104, 105, 110, 111, and 108, raw oil filter 104 units, and hydrotreating F100-B units of China Petroleum and Chemical Corporation; it can increase the filtration flux by 10%˜50% with the other components in the unit, causing the yield to go up substantially.

BRIEF DESCRIPTION

Some of the embodiments will be described in detail, with reference to the following FIGURE, wherein like designations denote like members, wherein:

FIG. 1 is a comparison between the test filtration flux of embodiments of the present invention and the products of the same kind made in China and made in other countries with the filter fineness of 1 μ˜10 μ.

DETAILED DESCRIPTION

A method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders , having the following processing steps:

Firstly weaving wires to form metal wire mesh of different mesh numbers, and then stacking up the metal wire meshes of different mesh numbers to obtain a layered structure on the principle that the mesh number increases from one side to the other, and the number of the layers is 1˜5″; then putting the layered structure in a vacuum furnace for 10˜30 hrs uninterruptedly sintering at 900˜1500° C. to obtain a multi-layer support layer; after cooling down, taking the aforesaid supporting layer out, making a metal composite layer with a mesh number of 100˜600 on the side with high mesh number through electrostatic spraying or common spraying and casting method with the thickness of the composite layer controlled within 0.1˜0.5 mm, and then sintering the resultant structure at 900˜1500° C., and after cooling down, a composite filter sheet and tube made of a multilayer metal mesh and metal powders with the multiple layers of metal meshes as the supporting layer and the sintered metal power structure as the filtering layer is obtained; then taking the composite filter sheet or tube out and rolling it into tubular filter elements with a forming machine; welding the middle seam of the tubular filter element with an argon arc welding machine or plasma welding machine to obtain a multilayer metal mesh and metal powder composite filter tube and filter element products.

The supporting layer of the structure is a composite structure with a thickness of 1˜10 mm and formed by stacking up multiple layers of metal meshes with the filter fineness of 20 to 1000 and sintering. The supporting layer made by weaving metal wires may be sintered with a filtering layer to form a dual-layer composite structure, or be formed with a metal powder sheet to be a composite structure. Examples of metal meshes used for the supporting layer are formed by weaving Fe, Co, Ni, W, Mo, Cr, Cu, Al, Ti, Zn, Sn, Ta, Nb, and Zr elementary substance metal wires, or alloy wires combining multiple ones of these metal elements.

The composite filter sheet and tube made of a multilayer metal mesh and metal powders has the multiple layers of metal meshes as the supporting layer and the sintered metal power structure as the filtering layer. The filtering layer with the mesh number of 100˜1000 is attached on the supporting layer and made by low temperature spraying (such as flame spraying or plasma spraying) of metal powder and sintering together with the supporting layer. Examples of metal powders used for the filtering layer are Fe, Co, Ni, W, Mo, Cr, Cu, Al, Ti, Zn, Sn, Ta, Nb, and Zr elementary substance metal powders, or alloy powders combining multiple selections of these metal elements.

The multi-layer metal mesh and metal powder composite filter sheet/tube is processed to form an asymmetric powder-sintered filter tube by rolling and welding processes.

Referring to FIG. 1, the powder-sintered composite filter sheet/tube with a double- or three-layer structure made according to embodiments of the present invention has the advantages of high filter fineness, low filtration resistance, and high strength and makes substantial progress compared with the prior art.

Embodiment 1: take one wire mesh with the mesh number of 100, two wire meshes with the mesh number of 40, and two wire meshes with the mesh number of 12, each 1000 mm long and 500 mm wide, then stack up these meshes neatly in such a way that the mesh number from top to bottom is 100, 40, 40, 12, and 12 respectively, butt-weld the edges, put the welded structure in a vacuum furnace for 10hrs. sintering at 900-1500° C. to obtain a supporting layer; after cooling down, take the supporting layer out, and take 1˜2 kg of stainless steel 316L, 304, and 310S powder with the mesh number of 100˜200 and mix it with 0.1%-20% of forming agent for 1˜3 hrs. in a mixer which can be V-shaped mixer or double cone mixer or ball mill; cast a layer of mixed stainless steel powder with thickness of 1˜5 mm on the 5-layer mesh supporting layer sintered; then put the composite structure in a vacuum furnace for second sintering at 1000˜1600° C.; after cooling down, a composite filter sheet and tube made of a multilayer metal mesh and metal powders is obtained; form the filter sheet/tube by a former and roll the filter sheet/tube into tubular filter elements; at last, weld the middle seam of the filter element with an argon arc welding machine or plasma welding machine; apply the filter element product obtained to the S-Zorb units 101, 102, 103, 104, 105, 110, 111, and 108, raw oil filter 104 units, and hydrotreating F100-B units of China Petroleum and Chemical Corporation for use. Embodiment 2: take one wire mesh with the mesh number of 500, two wire meshes with the mesh number of 40, and two wire meshes with the mesh number of 12*64, each 1000 mm long and 500 mm wide, stack up the five meshes neatly in such a way that the mesh from top to bottom is 500, 40, 40, 12*64, and 12*64 respectively, and butt-weld the edges; put the welded structure in a vacuum furnace for 15 hrs. sintering at 900-1500° C. to obtain a supporting layer; after cooling down, take the supporting layer out, and take 1-2 kg of stainless steel 316L, 304, and 310S powder with the mesh number of 50˜600 and mix it with 0.1%˜20% of forming agent for 1˜3 hrs. in a mixer which can be V-shaped mixer or double cone mixer or ball mill; cast a layer of mixed stainless steel powder with thickness of 1˜5 mm in thickness on the 5-layer mesh supporting layer sintered; then put the composite structure in a vacuum furnace for second sintering at 1000˜1,600° C.; after cooling down, a composite filter sheet and tube made of a multilayer metal mesh and metal powders is obtained; form the filter sheet/tube by a former and roll the filter sheet/tube into tubular filter elements; at last, weld the middle seam of the filter element with an argon arc welding machine or plasma welding machine; apply the filter element product obtained to the S-Zorb units 101, 102, 103, 104, 105, 110, 111, and 108, raw oil filter 104 units, and hydrotreating F100-B units of China Petroleum and Chemical Corporation for use. Embodiment 3: take one nickel mesh with the mesh number of 100, one mesh with the mesh number of 40 and two meshes with the mesh number of 10, each 1000 mm long and 500 mm wide, stack up the four meshes neatly in such a way that the mesh number from top to bottom is 100, 40, 10, and 10 respectively, butt-weld the edges, put the welded structure in a vacuum furnace for 20 h sintering at 900˜1500° C. to obtain a supporting layer; After cooling down, take the supporting layer out, and take 1˜2 kg of nickel powder with the mesh number of 50˜600 and mix it with 0.1%˜20% of forming agent for 1˜3 hrs. in a mixer which can be V-shaped mixing equipment or double cone mixer or ball mill; cast a layer of mixed nickel powder with thickness of 1˜5 mm in thickness on the 4-layer mesh supporting layer sintered; put the composite structure in a vacuum furnace for second sintering at 1000˜1600° C.; after cooling down, a composite filter sheet and tube made of a multilayer metal mesh and metal powders is obtained; form the filter sheet/tube by a former and roll the filter sheet/tube into tubular filter elements; at last, weld the middle seam of the filter element with an argon arc welding machine or plasma welding machine; apply the filter element product obtained to the S-Zorb units 101, 102, 103, 104, 105, 110, 111, and 108, raw oil filter 104 units, and hydrotreating F 100-B units of China Petroleum and Chemical Corporation for use.

Claims

1. A method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders, wherein the processing steps are stated as below: weaving wires to form metal wire mesh of different mesh numbers, and then stacking up the metal wire meshes of different mesh numbers to obtain a layered structure on the principle that the mesh number increases from one side to the other, and the number of the layers is 1˜5;putting the layered structure in a vacuum furnace for 10˜30 hrs uninterruptedly sintering at 900˜1500° C. to obtain a multi-layer support layer;after cooling down, taking the aforesaid supporting layer out, making a metal composite layer with a mesh number of 100˜600 on the side with high mesh number through electrostatic spraying or common spraying and casting method with the thickness of the composite layer controlled within 0.1˜0.5 mm;sintering the resultant structure at 900˜1500° C., and after cooling down, a composite filter sheet and tube made of a multilayer metal mesh and metal powders with the multiple layers of metal meshes as the supporting layer and the sintered metal power structure as the filtering layer is obtained;taking the composite filter sheet or tube out and rolling it into tubular filter elements with a forming machine; andwelding the middle seam of the tubular filter element with one of an argon arc welding machine or plasma welding machine to obtain a multilayer metal mesh and metal powder composite filter tube and filter element products.

2. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein the supporting structure is a composite one of multilayer metal meshes.

3. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein the supporting layer of the structure has a thickness of 1˜19 mm and is formed by stacking up multiple layers of metal meshes with the filter fineness of 1 to 1000 and sintering.

4. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein the supporting layer made by weaving metal wires may be sintered with a filtering layer to form a dual-layer composite structure, or be formed with a metal powder sheet to be a composite structure.

5. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein the filtering layer with the mesh number of 100˜1000 is attached on the supporting layer and made by low temperature spraying (such as plasma spraying or common spraying) of metal powder and sintering together with the supporting layer.

6. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein metal powders used for the filtering layer are selected from the group consisting of, Fe, Co, Ni, W, Mo, Cr, Cu, Al, Ti, Zn, Sn, Ta, Nb, Zr and alloy powders combining multiple selections of these metal elements.

7. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein metal meshes used for the supporting layer are formed by weaving metal selected from the group consisting of Fe, Co, Ni, W, Mo, Cr, Cu, Al, Ti, Zn, Sn, Ta, Nb, Zr and alloy wires combining multiple ones of these metal elements.

8. The method for producing composite filter tube and filter element made of multilayer metal mesh and metal powders of claim 1, wherein the composite filter sheet and tube made of a multilayer metal mesh and metal powders is processed to form an asymmetric powder-sintered filter tube with a composite structure by rolling and welding processes.