The present invention is directed to the production of cutlery. It is directed both to a method of producing cutlery and a blanking tool to be used in producing cutlery.
Today cutlery is normally made in a number of steps, which steps comprise blanking, trimming and grinding. The trimming and grinding steps are often performed a number of times, between other steps. Each piece of cutlery is often made by blanking of a sheet metal of stainless steel.
In the blanking step the first part of the cut of the cutlery blank will be relatively sharp while the next part will be relatively rough. This is a well-known phenomenon and is due to the fact that in the shearing process the first part will in practice be a cutting process while the second part will be a tearing process. The rough surface formed by the tearing process will have to be grinded rather extensively.
Normally there is a clearance of between 10 to 15% between the blanking tool and the final dimension of the piece of cutlery. Thus, trimming is necessary to arrive with the final cutlery. For cutlery stainless steel is normally used. During each trimming and grinding step the material is heated. Such heating may influence the material, in that chromium is released from the stainless steel. This will diminish the protection of the finished cutlery against rust.
In view of the above there is a need for a production method for cutlery, which reduces the risk of rust formation on the cutlery at normal use. Furthermore, it is a need for a production method for cutlery, which is more accurate than the one used today and which is suitable for industrial production of cutlery at a high speed, thereby being suitable for high volume production of cutlery.
In the method of the present invention the same presses as used today for blanking of cutlery may still be used. The blanking is done in what can be called a hybrid fineblanking tool. In the blanking tool block guiding is used to stabilize movement in the tool. Thereby, the clearance between the blanking tool and the final dimension of the piece of cutlery may be reduced to between 0.1-2.0%, preferably to 0.2-1.5% and more preferably to about 0.5%. The method of the present invention may be used without any anvil. In the method of the present invention there is less material usage than in known fineblanking methods, since in known fineblanking methods the holding means will need more material to hold on to. By holding the sheet metal of which the cutlery is formed during the actual blanking, the shearing will be completely a cutting process with no or little tearing. Thus, the problem with part of the shearing being a tearing process is avoided. It is essential to hold the sheet metal fixed on the die during the blanking. A person skilled in the art realises that different means can be used to hold the sheet metal. In the embodiment shown in the enclosed drawings the sheet metal is held at the die by means of a spring loaded holder.
In a first step of the present invention a piece of cutlery, or cutlery blank, may be blanked from a pre-polished material. The circumference of the cutlery blank is blanked by one blanking stroke in some embodiments. In other embodiments the circumference of the cutlery blank is blanked by two or more blanking strokes. In each such blanking stroke a part of the circumference of the cutlery blank is blanked. In an optional second step a radius is formed on the edges to prevent sharp edges and burrs. Thereby, grinding and/or polishing steps are minimized. In the second step the piece of cutlery is pressed into a tool having rounded surfaces to form the radii of the edges of the piece of cutlery. In an optional third step the piece of cutlery is given its three dimensional shape. The steps following the third step may include final polishing, cleaning, quality control and packing.
With the method of the present invention the piece of cutlery is produced using fewer steps than in the traditional method of making cutlery. Fewer steps means less time to produce each piece of cutlery and less time will reduce the costs. Fewer steps also means better quality since no grinding and less polishing may be used thereby less chromium is released from the stainless steel. Compared to traditional production of cutlery the number of steps in the method of the present application is about half the number of steps of traditional production of cutlery. The method according the present invention may be a grinding free method of producing cutlery.
In one embodiment, through openings and/or notches are punched in the cutlery prior to punching the circumference of the cutlery. The advantage with this embodiment is that through openings and/or notches may be arranged in a cutlery as an integrated part of the punching process. Through openings may for instance be used to enable storing the cutlery by hanging. Through openings may also be used for other purposes such as a punching step for improving the final cutlery. The notches may for example be for producing the tines of a fork.
Further objects and advantages of the present will become apparent to a person skilled in the art when reading the detailed description below of embodiments of the invention.
The invention will be described further below by way of example and with reference to the enclosed drawings. In the drawings:
In specific of the enclosed Figs. blanking or producing of one type of cutlery is shown. A person skilled in the art realises that the principles of blanking and producing the cutlery are the same irrespectively of the type of cutlery to be produced.
As used in this description the expression “cutlery” refers to table cutlery or tableware and comprises knives, spoons and forks.
As used in this description the expressions “upper”, “lower” and similar expressions are in view of the normal orientation of the cutlery blanking and forming tools.
The shown embodiment of one example of a cutlery blanking tool comprises three basic parts. Said parts are an upper part in the form of a punch 1, an intermediate part in the form of a holder 2, and a lower part in the form of a die 3.
The cutlery blanking tool is to be used in an ordinary press for blanking of cutlery. As the present invention is not directed to the press as such and as the function of such a press is well known to a person skilled in the art, the press will not be described further here.
The punch 1 comprises four guiding pins 4 placed adjacent the corners of the punch 1. The punch 1 further comprises two guiding blocks 5. Said guiding pins 4 and guiding blocks 5 are used to distinctly guide the punch 1 in respect of the other parts of the cutlery blanking tool. Furthermore, the punch 1 comprises a first blanking part 6, which in the shown embodiment is adapted for forming a knife. When producing forks or spoons the blanking part will have a shape corresponding with that particular fork or spoon. The first blanking part 6 projects from the punch 1 on the side facing the holder 2 and the die 3. The punch 1 comprises a further, or second, blanking part 7, which second blanking part 7 is used when blanking a recess. The number of blanking parts 6, 7 of the punch 1 may vary depending on the design of the piece of cutlery to be produced. Thus, the punch 1 may have one or more blanking parts 6, 7. In other embodiments only one blanking part is provided, which blanking part has a basic part in the general shape of the actual piece of cutlery to be produced and also one or more further blanking parts protruding from said basic part. Said further blanking parts are to form openings and/or recesses of the piece of cutlery.
The holder 2 has openings 8, for the guiding pins 4 of the punch 1, and guide openings 9, for the guiding blocks 5 of the punch 1. It also has openings 10, 11 for the blanking parts 6, 7 of the punch 1. All openings 8, 9, 10, 11 of the holder 2 are through openings.
The die 3 comprises openings 12, for the guiding pins 4 of the punch 1, and guide openings 13, for the guiding blocks 5 of the punch 1. Furthermore, the die 3 comprises openings 14, 15 for the blanking parts 6, 7 of the punch 1. The die 3 also comprises guides 16 for the material from which the cutlery is to be blanked.
A person skilled in the art will realize that the cutlery blanking tool will differ somewhat depending on the type of cutlery to be produced.
In use a sheet metal 17 is placed on the die 3, as shown in
During the first part of the blanking movement the distance between the punch 1 and the holder 2 is held fixed by means of springs (not showed) or the like, placed between the punch 1 and the holder 2. The springs are compressed in the last part of the blanking movement, in which last part of the blanking movement the holder 2 will abut the sheet metal 17. Thus, the force of the punch 1 will exceed the force of the means holding the distance between the punch 1 and the holder 2. As stated in the summary above, the sheet metal 17 can be held at the die 3 by other means than the holder described above. The important thing is that the sheet metal 17 is held fixed at the die 3 during the actual blanking.
The distance for the movement of the punch 1 during the last part of the blanking movement exceeds the thickness of the sheet metal 17. As indicated above there is no movement between the holder 2 and the die 3 during said last part of the blanking movement. The movement of the punch 1 is stopped in that the punch 1 hits the holder 2. The height by which respective blanking part 6, 7 protrudes from the punch 1, exceeds the sum of the thickness of the sheet metal 17 and the height of the openings 10, 11 of the holder 2 to receive said blanking parts 6, 7. In one embodiment the stroke length for the punch 1 in the blanking step is about 10 mm.
The steps of using the shown embodiment of a cutlery blanking tool will now be described with reference to
In
In
In the next step, as indicated in
In the following step, as indicated in
The holder 2 and the punch 1 is then again lifted from the sheet metal 17, after which the sheet metal 17 is pushed further into the cutlery blanking tool. The above indicated steps of producing cutlery are then repeated. As indicated above, the general production steps described in connection with
In
In one embodiment the thickness of the sheet metal 17 used is between 2 and 6.0 mm. Often the sheet metal 17 used for knives is thicker than the sheet metal 17 used for forks and spoons. In that the sheet metal 17 is held fixed during the actual blanking and that the movement of the punch 1 is meticulously guided, the clearance x, as shown in
After the blanking the cut blanks of the cutlery is deburred, in that the knife blank 20 is placed in a deburring die. The deburring die comprises an upper part 21 and a lower part 22. The upper part 21 has a die space 23 and the lower part 22 has a corresponding die space 24. There is a radius 25 between a bottom or top and respective side of each die space 23, 24. In use a knife blank 20 is placed in one of the die spaces 23, 24, as indicated in
The next step is the final three dimensional forming of the pieces of cutlery. Three dimensional forming of pieces of cutlery is a well known technique. It is normally made using a forming tool comprising a punch and a die. It is also known to use a hot forging process to give the three dimensional form.
After the final forming the cutlery is polished, cleaned, quality controlled and packed.
Number | Date | Country | Kind |
---|---|---|---|
1450850-1 | Jul 2014 | SE | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/SE2015/050790 | 7/3/2015 | WO | 00 |