Patent Grant
7617583
This application is a U.S. National Phase Application under 35 USC 371 of International Application PCT/JP03/11478 filed Sep. 9, 2003.
The present invention relates to a method and apparatus for producing a hot-dip plated metal strip.
Hot dipping is known as a method for plating a metal strip such as a steel strip continuously, in which the metal strip is immersed in molten metal such as zinc or aluminum and thus plated.
A metal strip 1 such as a steel strip after cold rolling is annealed in an annealing furnace 2 maintained at a non-oxidizing or reducing atmosphere; and subjected to surface cleaning and oxide film removal; and then continuously drawn into a molten metal bath 5 in a molten metal bath chamber 4 through a snout 3, and then turned around by a sink roll 6; and then drawn up from the molten metal bath 5 through support rolls 7; and then excessively adhered molten metal is wiped out by high pressure gas that is blown out from a gas wiping nozzle (wiper) 8 installed on the molten metal bath 5 in order to control plating weight in a predetermined amount, thereby a hot-dip plated metal strip is formed.
The support rolls 7, which are provided to correct a lateral warp of the metal strip 1 in the wiper 8 portion, and reduce scattering of an amount of the molten metal adhered in a lateral direction, are disposed in displaced positions along a forward direction of the metal strip 1 on both sides across the metal strip 1 like 7a, 7b shown in
However, since the support rolls 7a, 7b are driven by a motor (not shown) installed laterally to a molten metal bath chamber 4 at a higher position than a surface of the molten metal bath 5 through a spindle (not shown), the support rolls 7a, 7b do not rotate uniformly even if the motor rotates uniformly, and the rotation speed is not correspondence with conveyance speed of the metal strip 1, therefore unevenness of the coating weight in a chatter mark pattern occurs in the metal strip 1.
To solve the problem, idling (no driving) of the support rolls 7a, 7b may be considered. However, in this case, pushing amount of the support roll 7b needs to be increased to secure the rotation of the support rolls 7a, 7b, therefore the lateral warp of the metal strip 1 can not be corrected appropriately in the wiper 8 portion, and the lateral scattering of the coating weight of the molten metal becomes large.
When galvanized steel strip is produced using the apparatus shown in
To solve the above problem due to the support roll or problem of the dross defects, the inventors proposed a method in JP-A-2002-339051, in which the support roll in the molten metal bath is removed, and the lateral warp of the metal strip is corrected in a noncontact manner by magnetic force immediately before or after the wiper, or a method in which an enclosed member is provided in the molten metal bath such that it encloses the metal strip, thereby occurrence of the dross defects is prevented.
However, since the support roll was removed, in a metal strip having yield point elongation to which the baking hardening property is imparted, a problem newly occurred, that is, a surface defect known as buckling was apt to occur.
The buckling may occur even in the conventional operation using the support roll in some operation conditions or steel types. Therefore, to improve the yield and realize the stable operation, a technique for producing a hot-dip plated metal strip in which the buckling hardly occurs without regard to presence of the support roll is also desired.
It is an object of the present invention aims to provide a method and an apparatus for producing a hot-dip plated metal strip in which the buckling does not occur, the lateral scattering of the coating weight of the molten metal is small or the dross defects are few, when the support roll is not present in the molten metal bath. In addition, the invention aims to provide a method and an apparatus for producing a hot-dip plated metal strip in which the buckling hardly occurs without regard to presence of the support roll in the molten metal bath.
The objects are achieved according to the following methods.
1) A method for producing the hot-dip plated metal strip comprising the steps of: annealing the metal strip; imparting plastic strain to the metal strip; drawing the metal strip into a molten metal bath for plating; drawing sup the metal strip out of the molten metal bath without contacting the metal strip with a roll in the molten metal bath after turning around the metal strip upward with adhering the molten metal on the metal strip; and controlling the coating weight of the molten metal adhered on the metal strip using a wiper.
2) A method for producing the hot-dip plated metal strip comprising the steps of: annealing the metal strip; imparting surface plastic strain to the metal strip using at least one roll by bending after heating the metal strip to the maximum temperature in the annealing and before drawing the metal strip into the molten metal bath for plating; drawing the metal strip into the molten metal bath for plating and adhering the molten metal on the metal strip; and drawing up the metal strip out of the molten metal bath after turning around the metal strip using a sink roll, wherein the surface plastic strain of the metal strip is imparted such that the strain remained on a surface of the metal strip is 0.1% or more when the metal strip arrives at the sink roll (hereinafter, referred to as surface residual plastic strain).
3) A method for producing the hot-dip plated metal strip comprising the steps of: annealing the metal strip; imparting the surface plastic strain to the metal strip using at least one roll by bending after heating the metal strip to the maximum temperature in the annealing and before drawing the metal strip into the molten metal bath for plating; drawing the metal strip into the molten metal bath for plating and adhering the molten metal on the metal strip; and drawing up the metal strip out of the molten metal bath after turning around the metal strip using the sink roll, wherein a roll located at the most downstream side among the rolls for imparting the surface plastic strain to the metal strip by bending is disposed at a side of an opposite surface to a surface of the metal strip that contacts with the sink roll in the molten metal bath.
These methods are realized according to the following apparatus respectively.
1) An apparatus for producing the hot-dip plated metal strip comprising an annealing furnace for annealing the metal strip; strain imparting means for imparting the plastic strain to the metal strip after the annealing; a molten metal bath for adhering the molten metal for plating on the metal strip to which the plastic strain has been imparted; and a wiper for controlling the coating weight of the molten metal adhered on the metal strip, wherein only a turnaround device for turning around the metal strip is provided in the molten metal bath.
2) An apparatus for producing the hot-dip plated metal strip comprising the annealing furnace for annealing the metal strip; at least one roll for imparting the surface plastic strain to the metal strip by the bending, which is provided at apposition after the metal strip is heated to the maximum temperature in the annealing and before the metal strip is adhered with the molten metal for plating; and a molten metal bath for adhering the molten metal for plating on the metal strip, wherein the metal strip is turned around by the sink roll in the molten metal bath, and the surface plastic strain of the metal strip is imparted to the metal strip such that the surface residual plastic strain remained on the surface of the metal strip is 0.1% or more at a point when the metal strip arrives at the sink roll.
3) An apparatus for producing the hot-dip plated metal strip comprising the annealing furnace for annealing the metal strip; at least one roll for imparting the surface plastic strain to the metal strip by the bending, which is provided at the position after the metal strip is heated to the maximum temperature in the annealing and before the metal strip is adhered with the molten metal for plating; and the molten metal bath for adhering the molten metal for plating on the metal strip, wherein the metal strip is turned around by the sink roll in the molten metal bath, and a roll located at the most downstream side among the rolls for imparting the surface plastic strain to the metal strip by the bending is disposed at a side of an opposite surface to the surface of the metal strip that contacts with the sink roll in the molten metal bath.
As shown in
The support roll in the molten metal bath has a function of correcting such lateral warp of the metal strip. As shown in
However, when the support roll is present in the molten metal bath, in addition to the problems of the uneven coating weight in the chatter mark pattern or scratch as described above, there is a problem that shutdown of equipment is necessary for regular maintenance or exchange of the support roll, resulting in reduction of the operation efficiency.
Even when the support roll is used, if the warp of the metal strip can be reduced immediately after it has been turned around by the sink roll, pushing distance of the support roll can be set small, which is advantageous for preventing defects such as push flaw.
Thus, first, the inventors investigated what problem is occurred by removing the support roll from the molten metal bath.
First, since it is said that removal of the support roll increases the defects in the metal strip, because the support roll has a function of making adhesion of a foreign such as dross in the molten metal bath to be difficult, in addition to the function of correcting the warp of the metal strip; the following experiments were conducted for reality check. That is, rolls in imitation of the sink roll and the support roll and an endless belt in imitation of the metal strip were disposed in a container filled with water instead of the molten metal, and the roll diameter and roll rotational frequency were set such that Reynolds number or Floude number was equal to that around the roll in the actual molten metal bath, and behavior in the molten metal bath was hydrodynamically simulated, and aluminum powder was added as a tracer and flow of the powder was observed.
As a result, the roll in imitation of the support roll did not show the action of removing the aluminum powder adhered on the belt, and only showed an action of pressing the aluminum powder against the belt. Therefore, it is considered that the support roll in the molten metal bath has not the function of making the adhesion of the foreign to the metal strip to be difficult as described above, therefore removal of the support roll will not increase the defects. Actually, when the support roll was removed from the continuous-type hot-dip plated metal strip production apparatus shown in
To this end, it is desirable that the warp can be corrected in a noncontact manner, and the inventors confirmed that the warp of the galvanized steel strip was able to be corrected in the noncontact manner using magnetic force by an electromagnet.
However, by removing the support roll, if a galvanized steel strip having yield point elongation is produced, the steel strip being imparted with a baking hardening property, sometimes a strain pattern known as “buckling” is generated on a surface of the steel strip when the steel strip passes through the equipment mainly located at a downstream side of the molten zinc bath chamber. Although the defect can be made less noticeable by skin-pass, the defect sometimes appears again when the steel strip is pressed into final products, therefore it largely reduces product yield in some usage.
In some operation conditions or steel types, the buckling may occur even if the support roll is used.
The inventors had investigated causes of such buckling and a measure for preventing the buckling, consequently obtained the following findings.
1) When the steel strip passes through the continuous-type hot-dipping steel strip production apparatus, the band receives bending stress by rolls in various temperature ranges, and when the stress exceeds the yield stress of the steel strip, the bent portion of the steel strip locally yields, resulting in the buckling.
2) The buckling occurs in a temperature range lower than a certain temperature T1 (referred to as threshold temperature), and does not occur at the threshold temperature T1 or higher. It is considered that since the threshold temperature T1 corresponds to the temperature at which the yield point elongation disappears when tensile tests are conducted at various different temperatures, the yield point elongation is lost and thus local strain concentration is avoided, thereby occurrence of the buckling is suppressed.
3) Generally, at the room temperature, it is known that when the steel strip is previously imparted with strain, the buckling hardly occurs even if the band is subsequently machined. Also, similar effects are obtained when the steel strip is previously imparted with the strain at the above threshold temperature T1 or higher. That is, the buckling does not occur even if the band is subsequently machined at the threshold temperature T1 or lower. However, when the strain is imparted at a temperature of more than 650° C., the effects are reduced.
4) When the steel strip is previously imparted with the strain at the threshold temperature T1 or higher, the warp of the steel strip can be corrected, and sometimes, it may be an alternative of the function of correcting the warp of the steel strip using the magnetic force by the electromagnet.
5) Since the buckling occurs in a step at a downstream side of the molten zinc bath in the continuous-type hot-dipping steel strip production apparatus, temperature of the steel strip becomes the threshold temperature T1 at a position where the temperature of the molten zinc bath is 450 to 480° C. or higher, or a position between an annealing furnace and the molten zinc bath.
Therefore, when the temperature of the metal strip is 450 to 650° C. when the metal strip is a steel strip, if the metal strip is imparted with plastic strain before the metal strip is drawn into the molten metal bath after the annealing, the buckling can be prevented. That is, according to a method for producing the hot-dip plated metal strip, having a step of annealing the metal strip; a step of imparting the plastic strain to the metal strip; a step of drawing the metal strip into the molten metal bath for plating; a step of drawing up the metal strip out of the molten metal bath without contacting the metal strip with the roll in the molten metal bath after turning around the metal strip upward with adhering the molten metal on the metal strip; and a step of controlling the coating weight of the molten metal adhered on the metal strip using the wiper, a hot-dip plated metal strip can be produced, in which the buckling does not occur and the lateral warp of the metal strip in the wiper portion can be prevented.
Furthermore, if the support roll is designed to be installed in the molten metal bath and pushed against the metal strip, the buckling can be further reduced. In addition, while described later, in some strain impartation conditions, the previously imparted plastic strain may cancel the warp caused by the sink roll.
If the shape of the metal strip is corrected in the noncontact manner by the magnetic force immediately before or after the wiper, the coating weight can be made more uniform.
The stress causing the buckling is at maximum near the surface of the metal strip, when the stress is a bending stress given by the roll. Therefore, it is effective that the plastic strain imparted for preventing the buckling is imparted by bending, in which the strain is efficiently imparted to the vicinity of the surface of the metal strip. When the metal strip is the steel strip, the plastic strain is preferably imparted before the steel strip is drawn into the molten metal bath after annealing and when temperature of the steel strip is 450 to 650° C., as described above. Although the bending can be performed easily using the roll, the plastic strain amount to be imparted to the metal strip for preventing the buckling is preferably more than 0.1%, for example, in the surface plastic strain, and when the amount is more than 1.5%, the effect is saturated, in addition, material of the steel strip is sometimes deteriorated.
While described later in detail, surface residual plastic strain, which is remained on the surface of the metal strip at a point when the metal strip arrives at the sink roll in the molten metal bath, is more important for preventing the buckling and preventing the warp at the sink roll than the above surface plastic strain imparted to the metal strip, and preferably the surface residual plastic strain is made to be 0.1% or more. As the plastic strain is imparted at higher temperature, the strain is lost more easily before the metal strip arrives at the sink roll, and the surface residual plastic strain tends to be less than 0.1%, therefore the metal strip needs to be conveyed to the sink roll more speedily in a shorter time.
The plastic strain need not be imparted in one time, may be imparted in several times. When the strain is imparted in several times, the amount of the plastic strain is sum of the amount of strain imparted for each time. The imparted strain may be compressed strain or tensile strain, and the amount of the plastic strain when the two are present together is the total of them. It is assumed that this is because buckling prevention mechanism is due to transition that is independent of compression and tension.
To prevent the warp at the sink roll by giving the plastic strain by the bending using plural rolls, it is preferable that the roll located at the most downstream side, which can give the surface residual plastic strain in a certain level or more, is disposed such that the roll contacts with the opposite surface to the surface at which the sink roll contacts with the metal strip.
When the bending is performed using the roll, a roll having an outer diameter of 800 mm or less is preferably used. If the number of rolls is made to be 6 or more, and strain is imparted dividedly, the strain impartation effect is saturated, therefore number of rolls is preferably 5 or less.
Although JP-B-7-94704, JP-A-10-130801, and JP-2000-204460 describe that the steel strip is bent using the roll in the hot-dipping steel strip production apparatus, each of them assumes that the support roll is present in the molten zinc bath, and the problem and components are different from those of the invention. That is, the method of JP-B-7-94704 is a method in which the steel strip is bent using a roll having a diameter of 50 to 500 mm and then annealed to make the crystal grain size uniform; solid-liquid reaction in the molten zinc bath and the subsequent Fe—Zn alloying reaction are progressed uniformly; and a defect of an uneven surface produced in the alloying step is prevented, and bending is performed before the annealing. The method of JP-A-10-130801 is a method in which the bending and bending back are performed in a bending radius of 300 mm or less; diffusion reaction an interface between the steel sheet and plating is unified by imparting residual strain to a surface of the steel strip; and uneven alloying or uneven brightness due to uneven distribution of added elements such as Si, P, and Mn is prevented, in addition, it does not describe the buckling. Also, it does not describe that the above surface residual plastic strain involves the prevention of the buckling and the warp at the sink roll. The method according to JP-2000-204460 is a method in which the steel strip is pushed by the roll using two points on the path line as supporting points in a conveyance room at a non-oxidizing atmosphere; thereby the warp of the steel sheet is corrected, however, it is hard to impart sufficient tension stably to the steel strip because the sink roll is not present, and the plastic strain can not be imparted stably to the surface of the steel strip.
Next, an embodiment where the metal strip is the steel strip, and the molten metal is zinc is described in detail.
In this apparatus, the support roll 7 in the molten zinc bath 5 in the conventional production apparatus shown in
Although the strain may imparted in the molten zinc bath 5 or imparted after the steel strip being drawn up from the molten zinc bath 5 only for preventing the buckling, since problems such as the uneven coating weight of the molten zinc in the chatter mark pattern, push flaw, and plating separation occur, the strain impartation needs to be performed at an upstream side of the molten zinc bath 5.
The shape correcting means comprises a position sensors 10 that measure distances to the surface of the steel strip 1 moving upward in the figure; a controller 11 that receives a signal from the position sensors 10 and outputs a control signal; amplifiers 12 that amplify the control signal; and electromagnets 13 that exert sucking force on the steel strip 1 according to the amplified control signal and transforms the steel strip 1. The electromagnets 13 are installed plurally in a lateral direction of the steel strip 1, and disposed on both sides of the steel strip 1 in pairs. Since the electromagnets 13 exert the sucking force one-directionally on the steel strip 1, by disposing the electromagnets on the both sides of the steel strip 1 in pairs, a sucking direction of the steel strip 1 can be selected and the warp of the steel strip 1 can be corrected. Typically, in most cases, the lateral warp of the steel strip 1 has a C-section as shown in
If the sucking force of the electromagnets 13 disposed on the both sides of the steel strip 1 in pairs is controlled by the controller 11 according to the signal from the position sensors 10 that measure the distance to the surface of the steel strip 1, the warp of the steel strip 1 drawn up from the molten zinc bath 5 can be corrected.
While the shape correcting means 9, which is disposed immediately after the wiper 8, performs better control as it is closer to the wiper 8, when an alloying furnace, a touch roll, and a spangle adjustor are installed, it may be installed before the spangle adjustor. When the means 9 is installed immediately before the wiper 8, while it performs better control as it is closer to the wiper 8, it, may be installed between the molten zinc bath 5 and the wiper 8 in an actual line.
The strain imparting device 21 is installed at a downstream side of the point where the steel strip 1 arrives at the maximum temperature. Since the steel strip 1 is heated to the maximum temperature of 650 to 900° C. in a soaking pit 2b of the annealing furnace 2, if the strain imparting device 21 is installed at an upstream side of the point where the steel strip 1 arrives at the maximum temperature, the effect of imparting the strain is lost, and the buckling can not be prevented.
Although it is preferable in the strain imparting device 21 that the plastic strain is imparted such that the surface residual plastic strain is 0.1% or more as described above, to this end, the strain needs to be imparted more than 0.1%, more preferably not less than 0.3% and not more than 1.5% in the amount of the surface plastic strain.
As described above, from a viewpoint of imparting the plastic strain to the surface, bending using the roll is effective. When the bending is performed using the roll, it is preferable that an outer diameter of the roll is selected such that the radius of curvature of the steel strip 1 imparted by at least one roll is 400 mm or less, and the steel strip 1 is bent with the pushing amount of the roll being controlled. To bend the steel strip 1 at the radius of curvature of 400 mm or less, at least one roll having an outer diameter of 800 mm or less needs to be used. For example, the bending can be achieved in a method of controlling the pushing amount such that the steel strip 1 winds around the roll having an outer diameter of 800 mm sufficiently, or a method of controlling the pushing amount using a roll having an outer diameter of 400 mm. However, the pushing amount of the roll is different depending on material or thickness of the steel strip 1. To increase the amount of the imparted surface plastic strain, the pushing amount of the roll can be increased, or a roll having a small outer diameter can be used. The outer diameter of the roll is preferably 400 mm or less.
A roll having an outer diameter of more than 800 mm such as a hearth roll, which is generally installed in the vertical type annealing furnace 2, is not used as the roll for imparting the plastic strain.
When the same amount of surface plastic strain is imparted, the effect of imparting the strain is higher in the case that the number of the rolls is one. The strain may be imparted dividedly in a plurality of rolls, the effect is saturated even in 6 or more rolls, which is disadvantageous in a point of facility cost or facility maintenance, therefore the number of rolls is preferably 1 to 5. When the number of the rolls is one, the amount of impartable surface plastic strain can not be significantly increased, therefore more preferably, the actual number of rolls is made to be 2 to 3. When two or more rolls are used, each of rolls may have a different outer diameter.
The strain imparting device 21, which is provided at an intermediate position between hearth rolls 25 and 26 in the controlling cooled reactor 2d comprises three rolls 22, 23, and 24. The three rolls are disposed alternatively on both sides of the steel strip 1, and each of them is freely movable independently in a substantially perpendicular direction to the path line. At least one of the three rolls 22, 23, and 24 is pushed in a direction substantially perpendicular to the path line, thereby the steel strip 1 is imparted with the surface plastic strain. The amount of the imparted surface plastic strain is determined by the radius of curvature of the steel strip 1 that has been bent, and the curvature is determined by a space between adjacent rolls along the path line, the outer diameter, and the pushing amount of the roll. It is further simple that relation between material or thickness of the steel strip 1, operation parameters such as temperature, the space between the adjacent rolls, the outer diameter of roll, or pushing amount of the roll and the amount of surface plastic strain is previously obtained and a correlation table is prepared, and the pushing amount of the roll is set according to the operation parameter values based on the correlation table.
Although three rolls are disposed in the device shown in
The inventors found that when the steel strip 1 is imparted with the strain using the strain imparting device 21 shown in
In
In
In
In
On the other hand, in
It is more advantageous that the strain is imparted dividedly by the rolls 22 and 23 as shown in
Since the strain imparted by the roll 24 at the most downstream side is determined according to a relative positional relationship between the roll 24 and the rolls 22, 23 at an upstream side, when the pushing amount of the rolls 22, 23 is large, the roll 23 is sometimes displaced from the path line. For example, as shown in
Here, “roll is on the path line” is that the roll surface locates at a position where the roll surface contacts with the path line.
As described above, the surface residual plastic strain, which is remained on the surface of the steel strip 1 at the point when the steel strip arrives at the sink roll in the molten zinc bath, is more important for preventing, the buckling and the warp by the sink roll than the surface plastic strain, which is imparted to the steel strip by the strain imparting device such as the device in
Since the surface residual plastic strain A is in proportion to the amount of dislocation near to the surface of the steel strip, the strain A concerns with the first imparted surface plastic strain A0, average temperature T of the steel strip from the point of imparting the strain to the sink roll, and travel time t of the steel strip moving from the strain imparting device to the sink roll, and expressed in the following equation (1):
A=A0×exp{−t×b×exp(a×T)} (1),
where a and b are coefficients determined from a steel type, and the value of a is about 0.032 and b is about 1×10−10.
Specifically, the values of a and b are obtained by imparting a fixed amount of strain to a certain type of steel, and measuring the amount of strain after heat treatment for a fixed time at a certain temperature. Mean while, a concerns with the activation energy for diffusion of the strain, and b concerns with the diffusion coefficient.
Whether the strain is lost is similar to the problem of diffusion, therefore the lost strain is expressed in a function of exp (a×T), and the above equation (1) is obtained from boundary conditions that A is A0 at t=0 sec and A is 0 at t=∞.
Table 1 shows a calculation example of the surface residual plastic strain A when A0 is fixed to 0.1, and t and T are varied.
It was cleared from such calculation results that when surface plastic strain of 1.5% or less is imparted to a steel strip at 650° C. or more, the steel strip is preferably moved to the sink roll within 10 sec; when surface plastic strain of not less than 0.35% and not more than 1.5% is imparted to a steel strip at not less than 600° C. and less than 650° C., the steel strip is preferably moved to the sink roll within 40 sec; and when surface plastic strain of not less than 0.3% and not more than 1.5% is imparted to a steel strip at not less than 450° C. and less than 600° C., the steel strip is preferably moved to the sink roll within 120 sec. That is, according to such conditions, the surface residual plastic strain of the steel strip by the sink roll can be securely made to be 0.1% or more.
The inventors have obtained a finding that even if same amount of strain is imparted, there are cases with and without occurrence of the buckling depending on the elapsed time after the strain impartation to the roll where the buckling essentially tends to occur, such as the support roll located at the downstream side of the sink roll. From this, it is considered that as the dislocation increases, which is remained in the steel strip immediately before the temperature range in which the buckling occurs, the buckling is prevented more advantageously. It is also understood from that freely movable dislocation (movable dislocation) increases in proportion to the amount of the residual strain, and the movable dislocation is responsible for continuous plastic transformation (or the buckling is hard to occur).
Since the elongation percentage imparted to the steel strip in JP-A-10-130801 is not the amount of strain at the position where the buckling occur, in certain elapsed time from imparting strain or temperature of the steel strip, no strain remains at a point when the buckling occurs, therefore the buckling can not be prevented. In addition, since the elongation percentage is the average strain amount in a thickness direction, and is not surface plastic strain of the steel strip that is effective for preventing the buckling, the buckling can not be securely prevented by the elongation percentage.
The lateral warp of the steel strip 1 occurred at the wiper 8 portion in
While the above is a case that the support roll is not present, in the case that the support roll is present, since the support roll is present at the downstream side of the sink roll, the strain imparted by the support roll largely influences on the warp of the steel strip occurred at the wiper portion. However, it is not preferable to impart large strain by the support roll for preventing the warp of the steel strip, because defects may be increased.
To prevent the lateral warp of the steel strip 1 in the wiper 8 portion, as described above, it is necessary to impart the surface plastic strain to the steel strip 1. At that time, the required pushing amount of the roll is determined as follows. In addition to relations between conditions of the steel strip 1 such as material or thickness, and temperature, spaces along the path line among respective rolls, the outer diameter, and the pushing amount, and the amount of surface plastic strain, relations between the above conditions of the steel strip 1 and the amount of warp at the wiper 8 portion are previously obtained, and a correlation table between the above conditions of the steel strip 1 and the pushing amount of the roll, which is compatible with the prevention of the lateral warp by the amount of the surface plastic strain, is previously prepared, and the pushing amount of the roll by which the buckling can be prevented is determined based on the correlation table. Also when the outer diameter of the sink roll 6 is increased, such correlation table is prepared.
As described above, JP-A-2000-204460 describes the correction of the warp of the metal strip using a pushing roll. However, since the support roll is provided in the molten metal bath, a problem due to the support roll occurs. Moreover, the warp of the metal strip is corrected by combined use of the support roll with the pushing roll, therefore it is essentially different from the warp correction method of the invention. Furthermore, the sink roll is not present in the molten metal bath, it is difficult to impart tension force stably to the metal strip, and surface plastic strain can not be imparted stably as required.
When the support roll is not installed in the molten zinc bath, the outer diameter of the sink roll may be larger than that in the case that the support roll is installed.
If a generally used sink roll having an outer diameter of 750 mm is exchanged to a sink roll having a larger diameter of 950 mm, bending stress imparted to the steel strip can be reduced, therefore the lateral warp of the steel strip can be reduced. Therefore, it is possible to flatten the steel strip having a large thickness for which warp correction has been difficult heretofore. From this viewpoint, the outer diameter of the sink roll is preferably made to be 850 mm or more.
The sink roll is preferably arranged such that a distance between the top of the roll and a surface of the molten zinc bath is 50 to 400 mm. This is because when the distance is less than 50 mm, the bath surface is stirred by the rotation of the sink roll and a large amount of top dross is produced, and when it is more than 400 mm, a deep molten zinc bath chamber is required, causing increase in facility cost.
In the hot-dipping steel strip production apparatus of the invention shown in
The enclosing member 27 is opposed to a face of the steel strip 1 drawn into the molten metal bath 5; provided such that it encloses the face of the steel strip 1; divides the molten zinc bath 5 into an upper area 5A and a lower area 5B; and permits flow of the molten zinc between the upper area 5A and the lower area 5B. That is, the enclosing member 27 is a molten zinc chamber having an opened top provided in the molten zinc bath 5. Since the top is opened, the molten zinc in the chamber is flown out along with movement of the steel strip 1 and molten zinc is flown in from an outside of the chamber, and thus flow of the molten zinc is formed.
An upper end of the enclosing member 27 is located below a bath surface of the molten zinc bath 5, and an end 27b of the enclosing member 27 at a drawing-up side of the steel strip is located above a shaft core of the sink roll 6. The enclosing member 27 is disposed such that a distance to an underside of the steel strip 1 is at minimum directly under the sink roll 6.
The enclosing member 27 is made of stainless steel that may stand use of the high-temperature molten zinc. A leg-like supporting member (not shown) is installed on a lower portion of the enclosing member 27, and the enclosing member 27 is placed can be easily disposed on a bottom of the molten zinc bath chamber 4 through the supporting member. Accordingly, the enclosing member 27 can be easily disposed in the molten zinc bath chamber 4 and easily removed out of the molten zinc bath chamber 4.
Arrows around the enclosing member 27 in
The cleaned supernatant bath in the molten zinc bath 5 flows into the upper area 5A beyond the end 27a of the enclosing member 27 at the drawing-in side of the steel strip 1 with the accompanying flow of the steel strip 1. The steel strip 1 is drawn from the snout 3 into the molten zinc bath 5, turned around in the upper area 5A by the sink roll 6 with accompanying the cleaned molten zinc bath 5, and then drawn up from the molten zinc bath 5. While the steel strip 1 is drawn into the molten zinc bath 5 and drawn up from the molten zinc bath 5, the dross 16 influencing on the quality is not present in the movement area of the steel strip 1, therefore the steel strip 1 without the adhered dross can be produced.
The enclosing member 27 is preferably installed such that the proximal distance to the steel strip 1 is 50 to 400 mm. This is because when the distance is less than 50 mm, the member may contact with the steel strip 1 due to thermal deformation, or positioning is difficult in installing the enclosing member 27, and when the distance is more than 400 mm, an area is generated in the enclosing member 27, in which influence of the accompanying flow of the steel strip 1 does not appear, and the dross produced in the enclosing member 27 can not be discharged into the lower area 5B and deposits within the enclosing member 27.
The enclosing member 27 may be installed such that its upper end is above the surface of the molten zinc bath. In this case, in a portion of the end 27a of the enclosing member 27 on the bath surface at the drawing-in side of the steel strip 1, or in a portion in the bath close to the bath surface, an opening for flowing the molten zinc in the lower area 5B into the upper area 5A is installed. Alternatively, in a portion of the end 27b of the enclosing member 27 on the bath surface at the drawing-up side of the steel strip 1, or in a portion in the bath close to the bath surface, an opening for flowing out the molten zinc in the upper area 5A into the lower area 5B may be installed. However, when the enclosing member 27 is above the bath surface, operation of removing the top dross produced on the bath surface in the enclosing member 27 out of the molten zinc bath chamber 4 is complicated; and the top dross adheres on the enclosing member 27, the accompanying flow with the steel strip 1 may, flow out the molten zinc in the upper area 5A into the lower area 5B, and may flow the clean molten zinc from the lower area 5B into the upper area 5A; therefore the upper end of the enclosing member 27 is preferably installed below the bath surface. When the upper end of the enclosing member 27 is less than 100 mm below the bath surface, the accompanying flow with the steel strip 1 stirs the bath surface and thus increases the amount of produced top dross, therefore the upper end is preferably made to be not less than 100 mm below the bath surface.
To prevent that the accompanying flow with the steel strip 1 in the upper area 5A influences on an inside of the lower area 5B, and coils up the dross deposited on the bottom of the molten zinc bath chamber 4, the upper end of the enclosing member 27 must be above the shaft core of the sink roll 6, more preferably above the utmost portion of the sink roll 6.
Compared with the apparatus shown in
In the upper area 5A, the molten zinc in the molten zinc bath chamber 4 is flowed from the drawing-in side of the steel strip 1 to the drawing-up side of the steel strip 1 with the accompanying flow with the steel strip 1, and flowed out into the lower area 5B beyond the end 27b of the enclosing member 27 at the drawing-up side of the steel strip 1. In the lower area 5B, the molten zinc flows downward along the sidewall 4a of the molten zinc bath chamber 4 at the drawing-up side of the steel strip 1, and flows into the drawing-in side of the steel strip 1 through an underside portion and a side face of the enclosing member 27, or flows in a direction opposite to the direction in the upper area 5A. In this way, the molten zinc circulates between the upper area 5A and the lower area 5B, however, driving force of the molten zinc circulation is caused by the accompanying flow with the passing steel strip 1, and equipment for the circulation such as a pump is unnecessary, therefore there is an advantage that facility can be simple and inexpensive. The dross deposited on the bottom of the lower area 5B or the bottom of the molten zinc bath chamber 4 may be removed by removing the enclosing member 27 out of the molten zinc bath chamber 4, and then using conventionally known means.
This apparatus is an apparatus in which the shape correcting means 9 is removed from the apparatus in
This apparatus is an apparatus in which the enclosing member 27 shown in
In this apparatus, the support roll 7 (7a, 7b) is added in the molten metal bath chamber 4 in the apparatus in
Although the support roll 7 is added to the apparatus in
As the material for the galvanized steel strip, a hot-rolled steel strip that has been descaled after hot rolling and a cold-rolled steel strip obtained by, cold-rolling the hot-rolled steel strip can be used. The galvanized steel strip using the cold-rolled steel strip as a material is often used for an application required for good surface appearance such as an automobile outside plate, and the galvanized steel strip produced in the method of the invention is suitable for such application.
Using the galvanized steel strip production apparatus shown in
As the strain imparting device, a device having six rolls (rolls 1 to 6) shown in
A case of 2 rolls: Rolls 1, 2, 4, and 5 were not used, and a roll having an outer diameter of 1000 mm as the roll 3 and a roll having an outer diameter of 100 mm as the roll 6 are disposed, and the roll 6 was pushed in a direction substantially perpendicular to the path line, thereby the strain was imparted. The roll 6 was reinforced by a backup roll having an outer diameter of 400 mm from a point of roll stiffness.
A case of 3 rolls: Rolls 1 to 3 were not used, the roll 6 was disposed on the path line, and the roll 4 and the roll 5 were pushed into displaced positions from the path line as shown in
A case of 5 rolls: The roll 1 was not used, three rolls 2, 4, and 6 having the outer diameter of 250 mm were disposed on the path line, and in respective middle positions among these rolls, the rolls 3 and 5 were disposed oppositely across the steel strip, and the rolls 3 and 5 were pushed in a direction substantially perpendicular to the path line, thereby the strain was imparted.
A case of 6 rolls: The rolls 1 to 6 having the outer diameter of 250 mm were disposed as shown in
The diameter of the sink roll is 950 mm.
Above the wiper provided for wiping the surplus zinc, the shape correcting means shown in
The enclosing member installed in the molten zinc bath has a shape accommodated to the sink roll, and has a minimum space of 100 mm to the steel strip.
The enclosing member was removed from the apparatus in
For these steel strips 1 to 17, lateral deviation of the coating weight, presence of the dross, and level of the buckling were evaluated.
Regarding the level of the buckling, a press test simulated the press of an automobile door panel was conducted, and then the buckling was visually observed and evaluated in 6 stages of 0 to 5 according to the level of the buckling. Here, the buckling level is best at 0 (no occurrence), and becomes worse as the number increases. It is desirable that the buckling level is not more than 1 in the application of the automobile outside panel, and not more than 2 in the application of the automobile inside panel.
Table 3 shows results of the buckling level.
In the steel strips 2 and 4 to 15 that are the examples of the invention in which the strain was imparted and the warp was corrected by the shape correcting means, the lateral deviation of the coating weight was about ±5 g/m2, and in the steel strip 3 that was the example of the invention in which the strain was imparted, but the warp was not corrected, the lateral deviation of the coating weight was about ±10 g/m2. Moreover, presence of the dross on the surface of the steel strip was confirmed using a 300 mm square sample, as a result the dross was not confirmed in either condition.
While the buckling level was 5, or bad, in the steel strip 1 of the comparative example to which the strain was not imparted, the steel strips 2 to 15, in which the strain imparting conditions are within the scope of the invention, have a buckling level of not more than 2, which is slight in such a degree that the buckling defect is not a practical issue. Actually, the press test of an automobile door was performed, as a result no defect due to the buckling was found for the buckling level 0 and 1, and the defects were extremely slight for the buckling level 2.
In the steel strip 16 that is the example of the invention, which was produced without installing the enclosing member, the lateral deviation of the coating weight was about ±5 g/m2; and a surface of the steel sheet was observed using the 300 mm square sample, as a result the number of the dross was about 5. The buckling defect was not found.
In the steel strip 17 that is the conventional example, the lateral deviation of the coating weight was about ±10 g/m2 and a surface of the steel sheet was observed using the 300 mm square sample, as a result the number of the dross was about 5. The buckling defect in the buckling level of 4 was found over the entire surface of the steel strip, and further deteriorated buckling defect was confirmed after the press test.
In the steel strip 3, the strain impartation was set such that the strain was able to cancel the warp at the sink roll, however, the deviation of the coating weight was about ±10 g/m2 in each roll, which was almost equal to the conventional one. It is known from that that there is a similar warp correction effect in the example of the invention as in the conventional support roll.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-267890 | Sep 2002 | JP | national |
| 2002-267891 | Sep 2002 | JP | national |
| 2002-267892 | Sep 2002 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP03/11478 | 9/9/2003 | WO | 00 | 11/2/2004 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2004/024974 | 3/25/2004 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3499418 | Mayhew | Mar 1970 | A |
| 3808033 | Mayhew | Apr 1974 | A |
| 4078103 | Thornton et al. | Mar 1978 | A |
| 5023113 | Boston et al. | Jun 1991 | A |
| 6017643 | Kobayashi et al. | Jan 2000 | A |
| 6093452 | Ishii et al. | Jul 2000 | A |
| 6761936 | Reifferscheid et al. | Jul 2004 | B1 |
| 20030077397 | Kabeya et al. | Apr 2003 | A1 |
| 20040052958 | Dauchelle et al. | Mar 2004 | A1 |
| 20040052959 | Dauchelle et al. | Mar 2004 | A1 |
| 20040241336 | Brisberger | Dec 2004 | A1 |
| 20050048216 | Brisberger et al. | Mar 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 56-41365 | Apr 1981 | JP |
| 4-272162 | Sep 1992 | JP |
| 5-156417 | Jun 1993 | JP |
| 05171385 | Jul 1993 | JP |
| 7-94704 | Oct 1995 | JP |
| 7-268578 | Oct 1995 | JP |
| 11-100651 | Oct 1995 | JP |
| 10-130801 | May 1998 | JP |
| 2000-204460 | Jul 2000 | JP |
| 2000256884 | Sep 2000 | JP |
| 2002-339051 | Nov 2002 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20050115052 A1 | Jun 2005 | US |