Patent Application
20100068501
The invention relates generally to a method of providing a carbonaceous material and, in particular, to a method of providing a substrate with a carbonaceous coating that includes nested carbon structures.
There has been a tremendous interest in carbon nanoparticles since the discovery of the carbon nanotube in a high-temperature arc. Concentric shell structures, 3-7 nm in diameter, have been observed in small, spherical particles of graphitized carbon deposited during the evaporation of carbon by arc discharge in vacuum.
It has been reported that when irradiating carbon soot, collected from an arc-discharge apparatus, in a 300 KV-transmission electron microscope (TEM), with an electron dose 10-20 times higher than under normal operating conditions, the originally tubular or polyhedral graphite particles start becoming spherical after 10 minutes of irradiation, and eventually completely transformed into a quasi-spherical morphology. It was further reported that the particles were composed of an assembly of concentric spherical graphitic cages with the distance between layers being that of bulk graphite (0.34 nm). The assembly of spherical shells obtained were on the order of 47 nm in size. Additionally, it has also been shown that electron irradiation at 700° C. could also anneal out defects resulting in spherical shells with a decreasing spacing towards the center of the onion.
More recently, a dc arc discharge employed in de-ionized water between two carbon electrodes produced nested onion-like carbon nanoparticles with diameters of 4-36 nm. In addition to spherical nano-onions, elongated structures have been reported. Other carbon structures have also been observed both in Nd:YAG laser ablation and CO2 laser ablation of graphite rods. These include nanohorns. Nearly spherical particles about 80 nm in diameter were observed and individual particles showed aggregates of horn-shaped sheaths of single-walled graphene sheets in high resolution. Carbon nanotubular structures have been observed using KrF laser irradiation of a graphite pellet at 248 nm at 1150° C. and high argon gas pressure (500 Torr).
It would be useful to be able to provide carbon nanostructures without having to employ a high temperature process. It would be useful to be able to use an excimer laser to provide carbon nanostructures without having to employ a high temperature process. It would be useful to be able to provide larger sized carbon nanostructures than those produced by presently known techniques.
Example embodiments of the present invention involve depositing graphitic nano-onion structures in an ambient of O2 at room temperature, by pulsed laser ablation of metal-doped graphite targets and targets of graphite filled organic compounds. For comparison, ablation of pure graphite targets is also discussed. In an example embodiment, nano-onion structures are produced in the presence of O2 gas at pressures greater than 0.1 Torr, but not in Ar atmospheres with comparable pressures. The resulting structures were observed to be 100-200 nm in diameter, significantly larger than nano-onions produced by arc discharge and electron irradiation. Time-resolved emission spectroscopy was employed to examine differences between evolving plume species under various conditions. The shell structure of these nano-onions makes them good candidates for trapping small molecules. Large 3D cages can serve as an excellent catalyst, again by trapping or adsorbing molecules on surfaces or within the cage. Potential applications for the structures described herein include, but are not limited to, energy storage, electrochemical applications, e.g., thin-film batteries and microbatteries, and nano-sensors, e.g., gas sensors, protein, and DNA sensors.
In an example embodiment, a method includes employing a laser process in an oxygen-containing atmosphere at room temperature to provide a substrate with a carbonaceous coating that includes nested carbon structures. In an example embodiment, the substrate is insulating. In an example embodiment, the substrate is conductive. By way of example, the substrate can include one or more of the following: a polymer, Silicon (Si), glass, quartz, Indium Tin Oxide (ITO), and metal (e.g., steel). In an example embodiment, the laser process includes laser ablation of a target facing the substrate. By way of example, the target can include one or more of the following: graphite, a graphite filled organic compound, graphite cement, metal-doped graphite (e.g., Ni-doped graphite, or Ni—Co-doped graphite). In an example embodiment, employing the laser process includes using an excimer laser. In an example embodiment, employing the laser process includes using a KrF laser. In an example embodiment, the oxygen-containing atmosphere is at a pressure of approximately 0.1 Torr or greater. In an example embodiment, the oxygen-containing atmosphere is at a pressure of approximately 2 Torr. In an example embodiment, the carbonaceous coating is low friction. In an example embodiment, the nested carbon structures are onion-shaped. In an example embodiment, the nested carbon structures have outer diameters of approximately 100-200 nm. In an example embodiment, the nested carbon structures have outer diameters of approximately 200 nm. In an example embodiment, the nested carbon structures include substantially concentric layers. In an example embodiment, the nested carbon structures include five or more layers. In an example embodiment, the nested carbon structures each include layers formed about a core. In an example embodiment, the cores include fullerene.
In an example embodiment, a method includes imparting energy to a target in an oxygen-containing atmosphere at room temperature to provide a substrate facing the target with a carbonaceous coating that includes nested carbon structures. By way of example, the target can include one or more of the following: graphite, a graphite filled organic compound, graphite cement, metal-doped graphite (e.g., Ni-doped graphite, or Ni—Co-doped graphite). In an example embodiment, the substrate is insulating. In an example embodiment, the substrate is conductive. By way of example, the substrate can include one or more of the following: a polymer, Silicon (Si), glass, quartz, Indium Tin oxide (ITO), and metal (e.g., steel). In an example embodiment, imparting energy includes using a laser to ablate the target. In an example embodiment, imparting energy includes using an excimer laser to ablate the target. In an example embodiment, imparting energy includes using a KrF laser to ablate the target. In an example embodiment, the oxygen-containing atmosphere is at a pressure of approximately 0.1 Torr or greater. In an example embodiment, the oxygen-containing atmosphere is at a pressure of approximately 2 Torr. In an example embodiment, the carbonaceous coating is low friction. In an example embodiment, the nested carbon structures are onion-shaped. In an example embodiment, the nested carbon structures have outer diameters of approximately 100-200 nm. In an example embodiment, the nested carbon structures have outer diameters of approximately 200 nm. In an example embodiment, the nested carbon structures include substantially concentric layers. In an example embodiment, the nested carbon structures include five or more layers. In an example embodiment, the nested carbon structures each include layers formed about a core. In an example embodiment, the cores include fullerene.
In an example embodiment, an electrode structure includes a substrate, and a carbonaceous coating over the substrate, the carbonaceous coating including nested carbon structures that have outer diameters of 100 nm or greater. In an example embodiment, the substrate is insulating. In an example embodiment, the substrate is conductive. By way of example, the substrate can include one or more of the following: a polymer, Silicon (Si), glass, quartz, Indium Tin oxide (ITO), and metal (e.g., steel). In an example embodiment, the carbonaceous coating is low friction. In an example embodiment, the nested carbon structures are onion-shaped. In an example embodiment, the nested carbon structures include substantially concentric layers. In an example embodiment, the nested carbon structures include five or more layers. In an example embodiment, the nested carbon structures each include layers formed about a core. In an example embodiment, the cores include fullerene.
Referring to
The laser 102 is configured to direct the laser beam 106 through a window 108 of chamber 110 (e.g., a high vacuum chamber) toward a target 112. The energy imparted by the laser beam 106 results in an ablation plume 114. A substrate 116 is positioned within the chamber 110 to face the target 112 so that the ablation plume 114 is incident upon the target 112. A gas inlet 118 via needle valve 119 from gas source 120 and one or more pumps 122 are also provided.
Referring to
In an example embodiment, the nested carbon structures are onion-shaped. In an example embodiment, the nested carbon structures have outer diameters of approximately 100-200 nm. In an example embodiment, the nested carbon structures have outer diameters of approximately 200 nm. In an example embodiment, the nested carbon structures include substantially concentric layers. In an example embodiment, the nested carbon structures include five or more layers. In an example embodiment, the nested carbon structures each include layers formed about a core. In an example embodiment, the cores include fullerene.
In an example embodiment, the laser 102 is a KrF laser (e.g., Lambda Physik 210 I, 248 nm). Other wavelengths such as 193 nm, 532 nm, 1.06 μm, 355 nm, can also be used. It is also contemplated that energy can be imparted to the target 112 with techniques other than laser ablation.
The target 112 can include one or more of the following: graphite, a graphite filled organic compound, graphite cement, metal-doped graphite (e.g., Ni-doped graphite, or Ni—Co-doped graphite). It is contemplated that other metals can be used, such as Fe, Co, Gd, B, Pt and Pd and/or mixtures of these. It is believed that a metal-free target such as from an organic aromatic compound can also be used.
In an example embodiment, the substrate 116 is insulating. In an example embodiment, the substrate 116 is conductive. The substrate 116 can include one or more of the following: a polymer, Silicon (Si), glass, quartz, Indium Tin Oxide (ITO), and metal (e.g., steel). In an example embodiment, the distance between the target 112 and the substrate 116 is between 0.5 inch and 6 inches.
In an example embodiment, the gas source 120 provides an oxygen-containing atmosphere within the chamber 110 at a pressure of approximately 0.1 Torr or greater controlled by the needle valve 119 and one or more pumps 122. In an example embodiment, the oxygen-containing atmosphere is at a pressure of approximately 2 Torr. It is believed that other ambients such as N2, H2, H2O, NO etc. are also potential candidates.
In example embodiments, the carbonaceous coating 202 is provided by deposition of graphitic nano-onion structures in an ambient of O2 at room temperature, by the pulsed laser ablation of a Ni-doped or Ni—Co-doped graphite target at 248 nm. For comparison, ablation of pure graphite targets is also discussed. The carbonaceous coating produced includes nano-onion structures with an overall diameter of 100-200 nm, which is significantly larger than prior spherical shell structures reported. Time-resolved emission spectroscopy was employed to examine differences between evolving plume species under various conditions.
In example embodiments, commercially available pure graphite targets (99.999%, 1.000 inch diameter) and composite Ni-doped and Ni—Co-doped graphite targets were used for laser ablation. The graphite-Ni targets (1.000 inch diameter, 1% Ni) were prepared by pressing a mixture of graphite powder (99.9999%, −200 mesh), a commercially available graphite cement (e.g., Dylan GC Graphite Cement), in a 1:1 ratio by weight, which serves as a binder and Ni powder (99.996%, −120 mesh) at 15 KPsi at 130° C. for 4 h, followed by annealing in flowing Ar at 450° C. for 8 h, or 800° C. for 8 h, followed by 1100° C. for 12 h. Graphite cement targets were prepared by the same procedure, using only a weighed amount of Dylon cement. The targets were irradiated with a KrF laser (Lambda Physik 210 I, 248 nm), with a pulse width of 25 ns. A laser intensity of 8×108 W/cm2 was used. The pressures of O2 and Ar gases were controlled with a needle valve. Gas pressures of 2 Torr were employed. The substrates were held 4″ in front of the target surface. Ablation products were deposited on Si substrates as well as holey carbon TEM grids. TEM was performed with a Hitachi H-9000 electron microscope at 300 KV. The best TEM samples were prepared by wiping a holey carbon grid across the Si substrate. Emission spectra of the plume were recorded with a gated, intensified, air-cooled ICCD detector (PI Max, 1024×256) mounted on the exit port of a 320I-f/4 spectrometer equipped with 3 gratings having 300 gr/mm blazed at 500 nm, 600 gr/mm blazed at 400 nm, and a holographic 2400 gr/mm for the UV. The ICCD was gatable to 4 ns and was triggered by the excimer laser.
TEM analyses show that the materials deposited from ablating a graphite-metal target at 2 Torr O2 and 2 Torr Ar are very different from each other. Nano-onion structures are observed from a graphite-Ni target with 2 Torr O2. The formation of such onion-like nanostructures using excimer laser ablation at room temperature has not been reported previously. The production of these nano-onion structures was readily observed in O2 atmospheres of 0.1 Torr and greater. The TEM images of these structures (
Structures that are observed in the TEM range from tightly wound and spherical to more extended and disorganized with open space. At first glance the TEM images appear to resemble filaments that are wound up.
Onion structures generated by the methods described herein have been observed under normal operating conditions in the TEM without any in-situ transformations during irradiation, hence ruling out the possibility of them being produced by electron beam irradiation.
In contrast, ablation in comparable pressures of Ar leads to the deposition of moss-like soot (
Although the present invention has been described in terms of the example embodiments above, numerous modifications and/or additions to the above-described embodiments would be readily apparent to one skilled in the art. It is intended that the scope of the present invention extend to all such modifications and/or additions.