Claims
- 1. A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of:
- (a) providing a self-supporting template preform structure having no to little reinforcing properties, made of a porous body or of a network of cross-linked building constituents containing particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by adding a binder substance;
- (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and
- (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
- 2. The method of claim 1, in which the reinforcing material has a packing density pattern which is uniform.
- 3. The method of claim 1, in which the metal or alloy is selected from light alloys, aluminum, magnesium, copper, zinc, lead, tin and alloys thereof.
- 4. The method of claim 1, in which the reinforcing material is selected from metal oxides, carbides, nitrides and borides.
- 5. The method of claim 1, in which the reinforcing material is selected from SiC, graphitic carbon, Si.sub.3 N.sub.4, WC, TiN, TiC, ZrN, ZrC, AlN and B.sub.4 C.
- 6. The method of claim 1, in which the reinforcing material has a packing density pattern which varies directionally.
- 7. The method of claim 6 in which said packing density pattern varies by steps.
- 8. The method of claim 6 in which said packing density pattern varies continuously.
- 9. The method of claim 1, in which the preform structure is temporary, the constituents therof being fused within the metal matrix during step (b).
- 10. The method of claim 9 in which said constituents are made of an alloy or metal which dissolves in the molten metal or alloy upon casting.
- 11. The method of claim 1, in which the preform structure is temporary, the constituents thereof being eliminated during step (b).
- 12. The method of claim 11 in which said constituents are made of an organic polymer which volatilizes at the temperature of the molten metal or alloy.
- 13. The method of claim 11 in which said constituents are made of an organic polymer which decomposes at the temperature of the molten metal or alloy.
- 14. The method of claim 1, in which the preform structure is permanent, the constituents thereof being made of a refractory mineral material.
- 15. The method of claim 1, in which said preform constituents are fibers selected from Al.sub.2 O.sub.3, SiO.sub.2, Al.sub.2 O.sub.3 -SiO.sub.2, magnesium silicate, rock-wool and asbestos.
- 16. The method of claim 1, in which said binder is selected from alkali metal silicates, colloidal silica, alkyl silicates, starch, sugars, hydroxylic polymers, glues, and gums.
- 17. The method of claim 1, in which pressure is applied over the molten metal in the mould, thereby squeeze casting the casting.
- 18. A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of:
- (a) providing a self-supporting template preform structure made of a porous body or of a network of cross-linked building constituents containing particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by adding a binder substance, said step (a) being achieved by,
- (i) forming a homogeneous slurry of preform building constituents and said binder in a liquid medium, and
- (ii) forming this slurry into a cake in a desired preform shape and removing liquid from the cake to obtain a dry preform structure;
- (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and
- (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
- 19. A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of:
- (a) providing a self-supporting template preform structure having no to little reinforcing properties, made of a porous body or of a network of cross-linking building constituents containing, particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by coating said constituents with said particles of reinforcing material;
- (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and
- (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
Priority Claims (1)
Number |
Date |
Country |
Kind |
87810114.6 |
Mar 1987 |
EPX |
|
Parent Case Info
This is a continuation of application No. 07/162,257, filed on Feb. 29, 1988, which was abandoned upon the filing hereof.
US Referenced Citations (8)
Foreign Referenced Citations (8)
Number |
Date |
Country |
627229 |
Jul 1963 |
BEX |
0143330 |
Jun 1985 |
EPX |
59-111970 |
Jun 1984 |
JPX |
WO8402927 |
Aug 1984 |
WPX |
WO8603997 |
Jul 1986 |
WPX |
1489346 |
Oct 1977 |
GBX |
1595280 |
Aug 1981 |
GBX |
2106433A |
Apr 1983 |
GBX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
162257 |
Feb 1988 |
|