Claims
- 1. A method for producing a rare earth alloy magnetic powder which includes a ferromagnetic compound, comprising the steps of:
- (a) preparing a rare earth alloy material represented by R-T-B alloy, wherein R is at least one rare earth element inclusive of yttrium (Y); T is iron (Fe) which may be partially substituted with cobalt (Co); and B is boron (B);
- (b) subsequently subjecting the alloy material to a homogenization treatment while maintaining the alloy at a temperature in a range between 600.degree. C. and 1200.degree. C. to form a homogenized alloy ingot;
- (c) crushing the homogenized alloy ingot into homogenized alloy ingot fragments and placing the ingot fragments, in the absence of a regenerative material, in a vacuum tube furnace having heater disposed therearound;
- (d) subsequently introducing hydrogen into the vacuum tube furnace and subjecting the homogenized alloy in the vacuum tube furnace to hydrogenation, wherein said hydrogenation includes occluding hydrogen into the homogenized alloy while heating the furnace from room temperature to 500.degree. C. followed by elevating and maintaining the furnace temperature between 750.degree. C. and 950.degree. C. by controlling said heater using a first temperature detecting means attached to an outer surface of said vacuum tube furnace to form a hydrogenated alloy;
- (e) subsequently subjecting the hydrogenated alloy to dehydrogenation while maintaining the alloy, placed in the vacuum tube furnace, at a temperature in a range between 750.degree. C. and 950.degree. C. to form a dehydrogenated alloy, wherein said vacuum tube furnace substantially provides radiant heat and limits a temperature drop in the alloy due to an endothermic reaction occurring during the dehydrogenation to at most 50.degree. C., and wherein the maintaining of the temperature is carried out by controlling said heater using a second temperature detecting means held in contact with the ingot fragments; and
- (f) cooling and crushing the dehydrogenated alloy to obtain a R-T-B rare earth alloy magnet powder comprising particles, each particle having an aggregated structure of fine recrystallized grains of the ferromagnetic compound.
- 2. A method for producing a rare earth alloy magnet powder as recited in claim 1, wherein the alloy in the step (f) maintains the temperature drop of at most 20.degree. C. due to the endothermic reaction occurring during the step (f).
Priority Claims (1)
Number |
Date |
Country |
Kind |
3-349934 |
Dec 1991 |
JPX |
|
Parent Case Info
This is a continuation of application Ser. No. 07/980,483 filed on Nov. 23, 1992, now abandoned.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4981532 |
Takeshita et al. |
Jan 1991 |
|
Foreign Referenced Citations (2)
Number |
Date |
Country |
0304054 |
Aug 1988 |
EPX |
0411571 |
Jul 1990 |
EPX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
980483 |
Nov 1992 |
|