Method for producing salts with a reduced water of crystallisation content

Information

  • Patent Grant
  • 10914519
  • Patent Number
    10,914,519
  • Date Filed
    Thursday, October 25, 2018
    5 years ago
  • Date Issued
    Tuesday, February 9, 2021
    3 years ago
Abstract
The invention relates to a method for drying salts with a water of crystallisation content in convective apparatuses that can additionally be indirectly heated. The invention is primarily characterised in that the drying process takes place with a moisture content of the drying gas above a determined level. The gas surrounding the salt particles during the drying process therefore has a specific humidity. In this way, the rate of drying is positively influenced.
Description
BACKGROUND

The invention relates to a method for drying salts containing water of crystallisation in convective devices.


Many salts form hydrate stages during crystallisation. The embedded water of crystallisation is often undesirable because it increases the transport costs, reduces the concentration and in some cases results in a product that is not stable when stored. The extent of the hydrate stage, i.e. the number of embedded water molecules, can be controlled favourably by means of the crystallisation conditions in some cases, but in many cases there is no way round thermal dewatering. The more water molecules embedded per salt molecule, the easier it is for the water molecules last embedded to detach themselves again, i.e. both the energy required to overcome the bonding energy and the temperature required for detachment increase as the number of water molecules already separated per salt molecule rises. Products with a high water content, such as Glauber salt (magnesium sulphate*10 water), already gives off water of crystallisation at a slightly higher room temperature and liquefies (become a solution). This behaviour is the reason for the different product qualities obtained after any thermal drying.


In technical practice, dusty and fine-grain products that are susceptible to abrasion or stable granulates with low dust content and intermediate or transitions stages of both products are obtained, depending on the drying process and the operating and design conditions selected. Drying is conducted typically in rotary dryers (drum dryers), flash tube dryers or fluidized bed dryers with or without built-in heat exchangers. Spray granulation in the fluidized bed is also used, but is less economical due to the increased water evaporation. In some cases, the drying methods are also combined with one another.


What all methods have in common is that the product quality differs and cannot be determined in advance. Many methods provide a dusty product that is susceptible to abrasion and which has a low bulk density of 800-1000 g/I, and others provide a firm granulate of 1200 g/I and more (e.g. spray granulation, fluidized bed dryers with built-in heat exchangers).


SUMMARY

The aim of the invention is thus to produce salts with a reduced water of crystallisation content that have certain defined properties regardless of the method used, where the properties depend to a large extent on the bulk density.


The invention is thus characterised in that drying takes place above a certain defined moisture content, for example an absolute moisture content of 10%, in the drying gas. The gas that surrounds the salt particles during drying thus has a certain moisture content. This has an effect on the drying speed. At high speeds, the water evaporates spontaneously first of all on the surface, and then more water of crystallisation is released inside the particle, evaporated and brought to the surface through pores and capillaries as a result of the rising temperature. The capillaries and pores are expanded as a result of the high mass flows, and a porous particle with low density and a weakened structure is created. At low drying speeds, the water of crystallisation that has separated remains in a liquid state for a longer period, and the saline solution partially formed can again close or reduce the size of some pores, cracks and capillaries. This results in a firm particle of high density.


An advantageous development of the invention is characterised in that the moisture content of the drying gas is set above the defined moisture value by the evaporated water alone, where the moisture content in the drying gas can be set by adapting the water evaporation rate with the aid of the drying gas temperature or, as an alternative, by means of additional heat exchanger surfaces.


An alternative embodiment of the invention is characterised in that the moisture content of the drying gas is set by recirculating some of the gas, where the moisture content of the drying gas can also be set above the defined moisture value by fully recirculating the gas, and the evaporated water here is discharged from the loop by means of condensation and the moisture content of the drying gas is set with the aid of the condenser temperature.


In particular, salts with a high water of crystallisation content, e.g. decahydrates or Glauber salt (sodium sulphate), already release water of crystallisation at low temperatures (well below 100°). As a result of the low temperatures, there is not enough evaporation and the salt liquefies or cakes.


A favourable development of the invention is thus characterised in that the dust and/or dried product is combined and, if necessary, mixed with the damp salt containing water of crystallisation before drying. The excess free water of crystallisation can be bound by means of recombination to obtain a non-critical mixture that can be dried further. This recirculation takes place typically in a mixer that precedes the dryer, but can also be performed in the dryer if it has the appropriate dryer geometry.


An advantageous development of the invention is characterised in that, instead of dust and/or dried product, oversized granules ground to dust are combined with the moist salt containing water of crystallisation (“coating with powder”).


A favourable development of the invention is characterised in that the moisture content can only be set in a partial geometrical area of the dryer, e.g. in the feed zone.


When drying iron sulphate heptahydrate (ferrous sulphate) to a monohydrate using the method according to the invention, it has proved an advantage to set the absolute moisture content in the drying gas to more than 15% when it leaves the dryer in order to obtain a product with a bulk density of more than 1100 g/I.


According to the theory of the method proposed, there are several possible ways of setting the advantageous conditions. In the drying units used, the gas carries off the evaporated water, and the energy can also be supplied via the gas and/or through contact surfaces.


In purely convective devices, the moisture content in the waste gas is generally too low, and the hot gas temperature and flow rate must, therefore, be selected with the aid of the energy balance such that the water thus evaporated raises the moisture content in the waste gas to the desired level. This does not necessarily succeed with all types of salts and dryers. There are limits when increasing the temperature (damage to product, material strength, energy sources available, . . . ), and any increase in the volume flow does feed more energy to the device, but it does not alter the status of the waste gas in the desired direction.


Convective devices with indirect heating can set the water evaporation rate independently of the volume flow, using the temperature of the heating surfaces on the one hand and the size of these surfaces on the other hand. For a fluidized bed dryer with built-in heat exchangers, for example, this means increasing the transfer surface area by increasing the packing density (m2 of heat exchanging surface area/m3 layer volume) or increasing the layer depth at unchanged packing density if the capacity to increase the temperature has already been exhausted. As a result, water evaporation and moisture content in the waste gas are raised as required at unchanged inflow.


Furthermore, it is possible to set the waste gas to any desired status by recirculating some or all of the waste gas. If it is partially recirculated, some of the moist gas is discharged and the rest is recirculated. The ratio of the gas flows determines the waste gas moisture content and all of the evaporated water is discharged with the partial flow.


In the event of full recirculation in a closed gas loop, the evaporated water is condensed in a condenser and discharged from the loop. The temperature of the condenser determines the moisture content in the waste gas.


EMBODIMENT EXAMPLE 1

Iron sulphate heptahydrate with surface moisture is dried to a monohydrate in a fluidised bed dryer with a built-in heat exchanger in the product layer. 420 kg/h of moist heptahydrate and 260 kg/h of dried recirculated material (monohydrate product and dust from the drying plant) were fed to the dryer via a mixer.


The drying air (1300 kg/h) had a temperature of 185° C., the heat exchanger 195° and the product layer 117° C., Together with the initial loading of 10 g/kg dry air, this resulted in an exhaust air load of 146 g/kg dry air, corresponding to an absolute moisture content of 12.7% and a dew point of approximately 63° C., due to the evaporated water. The result of this drying process at low moisture content was a light, dusty monohydrate granulate with a bulk density of 710 g/I, average grain diameter of 250 microns, and dust discharge of 66% in the exhaust air during drying.


EMBODIMENT EXAMPLE 2

In the same dryer, a mixture with the same amounts of heptahydrate and recirculated material comprising monohydrate and dust from the drying process was dried at virtually the same temperatures (air 178°, heat exchanger 195°, product layer 120°). The main difference compared to example 1 was that the air was fully recirculated and the evaporated water fully condensed in a washer. Due to the changing product, the amount of air conveyed through the loop had to be increased to 1730 kg/h. The washer had a temperature of 65°, which resulted in a total load of 205 g water/kg dry air, in the air recirculated to the dryer. Together with the evaporated water, the exhaust air then contained 329 g/kg after the dryer, equivalent to an absolute moisture content of 24.8% and a dew point of approximately 73°. As a result of this humid atmosphere during drying, the monohydrate produced was stable and heavy, with a bulk density of 1195 g/I, an average grain diameter of 450 microns and dust discharge with the exhaust air of only 15%.





BRIEF DESCRIPTION OF THE DRAWINGS

In the following figures, the variants of the method are described using a fluidized bed dryer as an example. These figures also apply by analogy to the other types of dryer mentioned above.



FIG. 1 shows a system according to the invention with a flow of recirculated material,



FIG. 2 shows a system according to the invention with partial gas recirculation, and



FIG. 3 shows a system according to the invention with full gas recirculation.





DETAILED DESCRIPTION

The supply air fan 10 (see FIG. 1) pushes ambient air through a heater battery 11 into the drying device (in this case a fluidized bed dryer) 12, in which the salt can be heated optionally by the heat exchanger 13, and releases the water of crystallisation. The moist drying gas leaves the dryer, the dust is removed from the gas in a filter or cyclone 14, then the drying gas passes through the exhaust air fan 18 into the fresh air 19 after undergoing optional, additional gas cleaning. The salt 20 with a moist surface and containing water of crystallisation is coated with the dust separated in the cyclone or filter 14 and optionally with recirculated product in the mixer 21 and fed to the dryer 12. After the drying process, the salt leaves the dryer 12 and the oversized grains are removed on an optional screen 22, ground 23 and fed to the mixer 21. The accept fraction enters an overflow silo 24, from which recirculated product for the mixer 21 is taken optionally by a dosing screw 25 and to which the final product 26 is fed for further processing.



FIG. 2 shows the variant of the drying process with partial gas recirculation in order to set a defined gas moisture content, i.e. a defined moisture content in the dryer. The product is treated in the same way as described in FIG. 1, but is not shown here for the sake of maintaining clarity. The fan 10 presses the gas in the circulating system through the heater battery 11, dryer 12 and dust remover 14. A partial flow of fresh air, which is cleaned with the optional filter 15, is added in metered doses with the aid of the throttling device 16. In this way, the moisture content of the gas is set in the dryer 12. The corresponding amount of moist waste gas is discharged through the pressure-controlled throttling device 17 on the discharge side of the fan. This flow of waste gas 19 also contains the evaporated water from the product. The smaller the partial flow of fresh air, the higher the moisture content in the gas.


If the circulating system is completely closed (see FIG. 3), the evaporated water must be removed selectively from the circulating gas. This can usefully be achieved by condensation in a surface or a wash condenser 30. The wash water is pumped 31 through the circulating system and the condensation heat is removed via the cooler 32. The volume of condensed water, which also corresponds to the volume of water that has evaporated from the product, is removed from the process with level control 33. With the aid of the cooler 32, the temperature of the wash water can be set such that the initial moisture content needed in the circulating gas results from the partial steam pressure of the water. The initial moisture content is calculated from the desired moisture content in the waste gas less the proportion generated by water evaporation from the product. The circulating gas is conveyed in a loop by the fan 10 through the heater battery 11, the dryer 12, the dust separator 14, and the washing condenser 30. The product route is the same as is shown in FIG. 1, but is not repeated here for the sake of maintaining clarity.


The systems shown are only intended as examples and are illustrated using a fluidized bed dryer (with or without built-in heat exchanger) as an example. However, rotary dryers (drum dryers), flash tube dryers or fluidized bed spray granulators could also be used.

Claims
  • 1. A method for drying moist salts containing water of crystallisation, comprising drying the moist salts with a hot drying gas having a moisture content and temperature in a convective dryer whereby water is evaporated from the moist salts as the moist salts are dried and said evaporated water increases the moisture content of the drying gas in the dryer;discharging the moist drying gas from the dryer into a loop that fully returns the discharged drying gas into the dryer;in said loop, removing moisture from the discharged moist drying gas by condensation at a controllable condenser temperature; andmaintaining an absolute moisture content of the drying gas in the dryer above a predefined moisture content value by controlling the moisture content of the drying gas that returns to the dryer through said loop, in dependence on controlling the temperature of a condenser.
  • 2. The method according to claim 1, wherein the moisture content in the drying gas in the dryer is maintained above said predefined moisture content value, in dependence on sensing a rate of evaporation of water from said moist salts and the temperature of the drying gas.
  • 3. The method according to claim 2, wherein said absolute moisture content is at least 10%.
  • 4. The method according to claim 2, wherein the moist salts containing water of crystallisation is iron sulphate heptahydrate;said moist salts are dried to a monohydrate product having a bulk density of more than 1100 g/I;the moisture of the drying gas increases as the drying gas passes through the dryer until it is discharged; andthe absolute moisture content of the drying gas is greater than 15% when it is discharged from the dryer.
  • 5. The method according to claim 1, wherein the moisture content in the drying gas in the dryer is maintained above said predefined moisture content value, in dependence on additional heat supplied to the dryer through heat exchanger surfaces.
  • 6. The method according to claim 5, wherein said absolute moisture content is at least 10%.
  • 7. The method according to claim 5, wherein the moist salts containing water of crystallisation is iron sulphate heptahydrate;said moist salts are dried to a monohydrate product having a bulk density of more than 1100 g/I;the moisture of the drying gas increases as the drying gas passes through the dryer until it is discharged; andthe absolute moisture content of the drying gas is greater than 15% when it is discharged from the dryer.
  • 8. The method according to claim 1, wherein said absolute moisture content is at least 10%.
  • 9. The method according to claim 8, wherein the moist salts containing water of crystallisation is iron sulphate heptahydrate;said moist salts are dried to a monohydrate product having a bulk density of more than 1100 g/I;the moisture of the drying gas increases as the drying gas passes through the dryer until it is discharged; andthe absolute moisture content of the drying gas is greater than 15% when it is discharged from the dryer.
  • 10. The method according to claim 1, wherein the moist salts containing water of crystallisation is iron sulphate heptahydrate;said moist salts are dried to a monohydrate product having a bulk density of more than 1100 g/I;the moisture of the drying gas increases as the drying gas passes through the dryer until it is discharged; andthe absolute moisture content of the drying gas is greater than 15% when it is discharged from the dryer.
Priority Claims (1)
Number Date Country Kind
A 379/2013 May 2013 AT national
CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional of U.S. patent application Ser. No. 14/888,608, filed Nov. 2, 2015, which application is a National Phase Entry of International Patent Application No. PCT/EP2014/001177, filed May 2, 2014, the entire disclosures of which applications are incorporated herein by reference in their entirety.

US Referenced Citations (33)
Number Name Date Kind
2033985 Haney Mar 1936 A
2118272 Smith May 1938 A
2204777 Smith Jun 1940 A
2272345 Kobe Feb 1942 A
2567959 Munday Sep 1951 A
2631084 Robinson Mar 1953 A
2715282 Niven, Jr. Aug 1955 A
3196930 Ebert Jul 1965 A
3212197 Crawford Oct 1965 A
3262213 Austin Jul 1966 A
3696520 Niedner Oct 1972 A
3815254 Mills Jun 1974 A
3884645 Kinne May 1975 A
4004352 Steffen Jan 1977 A
4005987 Jury Feb 1977 A
4043051 Lussenden Aug 1977 A
4151266 Robey Apr 1979 A
4244698 King Jan 1981 A
4324544 Blake Apr 1982 A
4704806 Gresens Nov 1987 A
5519948 Raehse May 1996 A
5603839 Cameron Feb 1997 A
5643548 Bammer Jul 1997 A
5915817 Zagorzycki Jun 1999 A
6085440 Getler Jul 2000 A
6931758 Sakamoto Aug 2005 B2
7182268 Kawahara Feb 2007 B2
20030012726 Oh Jan 2003 A1
20040047976 Narayan Mar 2004 A1
20070298993 Pawar Dec 2007 A1
20100059204 Stanke Mar 2010 A1
20110173836 Orr Jul 2011 A1
20110197467 Stanke Aug 2011 A1
Foreign Referenced Citations (4)
Number Date Country
1113666 Sep 1961 DE
388553 Mar 1933 GB
805159 Dec 1958 GB
2005036080 Apr 2005 WO
Non-Patent Literature Citations (2)
Entry
International Search Report dated Sep. 15, 2014 (PCT/EP2014/001177).
International Preliminary Report on Patentability dated Apr. 21, 2015 (PCT/EP2014/001177).
Related Publications (1)
Number Date Country
20190063836 A1 Feb 2019 US
Divisions (1)
Number Date Country
Parent 14888608 US
Child 16170263 US