FIELD OF THE INVENTION
This invention relates to corrosion protective coatings for metal surfaces, particularly, for iron which coatings contain, in addition to the other customary components, zinc and/or lead salts of nitrogen-containing heterocyclic organic compounds as corrosion inhibitors.
BACKGROUND OF THE INVENTION
In order to inhibit the metal corrosion process or to prevent it as completely as possible, metal surfaces are conventionally coated with primers or lacquers which contain corrosion inhibitors as the active components. It has been known for a long time to use such compounds as zinc potassium chromate, zinc tetrahydroxichromate, strontium chromate, barium chromate, or red lead oxide as corrosion inhibitors in corrosion protective coatings. Recently, however, the attention of the manufacturers of such coatings has been directed to the environmental behavior of such corrosion inhibitors. As a result, such time-tried inhibitors as zinc potassium chromate have been increasingly replaced by more environmentally acceptable corrosion inhibitors such as zinc phosphate.
The corrosion inhibiting property of zinc phosphate is based on the formation of protective layers in anionic pH ranges. The protective electrochemical reactions of zinc potassium chromate, do not take place with zinc phosphate, so that, until now, a combination of zinc phosphate with at least one electrochemically active corrosion protective pigment has always been recommended (Deutsche Farben Zeitschrift (Defazet) 29 (1975) 13-17).
Such electrochemically active corrosion inhibiting compounds are, for example, zinc and/or lead salts of 3-nitrophthalic acid, 4-nitrophthalic acid, 5-nitroisophthalic acid, or mononitroterephthalic acid, as are described in the German published patent applications DE-AS 22 04 985 and DE-AS 25 02 781. While such substances show an improved corrosion inhibiting effect (corrosion protection value) as compared with the conventional inhibitors, it appears that, when applied in the usual binder formulations, the coating materials such as paints and lacquers containing such corrosion inhibitors exhibit poor stability with respect to their sedimentation and the formation of solid agglomerated sediments which considerably complicate the practical application of such coating materials.
OBJECTS OF THE INVENTION
It is an object of the present invention to provide corrosion inhibitors for corrosion protective coatings which effect as large a corrosion inhibition as possible and do not have a deleterious effect on the sedimentation stability of the compounds and possess good dispersibility.
Another object of the present invention is the development of compositions for coating metal surfaces with corrosion protective coatings which contain a corrosion-protecting amount of at least one zinc and/or lead salt of a five- or six-membered nitrogen-heterocyclic compound substituted by at least one hydroxyl or mercapto group which contains at least one ring-nitrogen and at least two conjugated double bonds, of which at least one has the formation. ##STR2## in a film-forming vehicle suitable for application to metals.
These and other objects of the invention will become more apparent as the description thereof proceeds.
DESCRIPTION OF THE INVENTION
The compositions of this invention are therefore improved corrosion protective coatings for metal surfaces based on conventional coating components as well as zinc and/or lead salts of organic compounds where the improvement specifically includes the zinc and/or lead salts of five- or six-membered ring heterocyclic compounds substituted with at least one hydroxyl or mercapto group, which contain in their ring at least one nitrogen atom and at least two conjugated double bonds, of which at least one has the formation. ##STR3##
We have found, to our surprise, that the zinc and/or lead salts of such heterocyclic compounds demonstrate, in conventional binder formulations for corrosion protective coatings, excellent corrosion inhibiting effects. Further, coating compositions including such salts have excellent stability with respect to their sedimentation behavior.
In addition, such corrosion inhibitor compounds have further advantages, compared to the electrochemically-active inhibitors known to the state of the art. The extremely low water-solubility of the salts according to the invention (the solubility of the zinc salts in water (20.degree. C.) is 0.1% or lower, the solubility of the lead salts is 0.01% or lower), provides an improved stability and extended protection of the corrosion protective coatings or lacquer films prepared with them, since these salts cannot easily be washed out of the lacquer film when formed. This minimal solubility of the inhibitors, according to the invention, is a positive advantage with respect to their environmental behavior under leaching conditions. The drained waters have much lower concentrations of toxic materials.
Among the five-membered heterocyclic compounds that form the zinc and/or lead salts according to this invention, there may be mentioned the following as examples: ##STR4##
As examples for corresponding six-atom heterocyclic compounds, the following should be named: ##STR5##
As is apparent from the above, compounds suitable for heterocyclic compound inhibitors, according to this invention, may contain two nitrogen atoms in the ring or additional ring hetero-atoms. Heterocyclic compounds with one or more nuclei, as well as compounds that contain additional substituents in addition to the one or more hydroxyl and/or mercapto groups, are also suitable.
The effective corrosion inhibitors, in the sense of the invention, can therefore be considered, as an example, the zinc or lead salts of the following heterocycles: pyrroles, imidazoles, pyrazoles, pyridines, pyrazines, pyrimidines, pyridazines, isoindoles, indazoles, purines, quinolines, isoquinolines, quinazolines, phenazines, oxazoles, isooxazoles, thiazoles, benzothiazoles, benzimidazoles, benzoxazoles, and other heterocyclic moietes, provided that they contain at least one hydroxy or mercapto group in the structural configuration I and II, as defined above. It is, of course, understood that some of these moieties may exist in their keto-forms however, for salt formation with zinc or lead, only the corresponding enol form is suitable. The same is true for the mercapto group.
Of special importance and preferred in the sense of the invention, are the zinc or lead salts of the mercaptobenzothiazoles as well as the mercaptopyridines, since excellent corrosion protective values have been achieved with corrosion protective coatings based on these salts, and, particularly, since no sediment is formed in corrosion protective coating compositions containing these salts even over extended periods of storage.
Also preferred in the sense of this invention are the zinc and lead salts of s-triazine derivatives with single- or multiple-ring nuclei which contain at least one hydroxyl or mercapto group on the triazine ring.
Examples of single-ring s-triazine derivatives which form zinc and/or lead salts in the sense of the invention include:
cyanuric acid (2,4,6-trihydroxy-s-triazine),
monothiocyanuric acid (2,4-dihydroxy-6-mercapto-s-triazine),
dithiocyanuric acid (2-hydroxy-4,6-dimercapto-s-triazine),
trithiocyanuric acid (2,4,6-trimercapto-s-triazine),
Allantoxaidine (2,4-dihydroxy-s-triazine).
The triazine ring may contain in addition to hydroxy or mercapto groups, further substituents. Corresponding single-ring nucleus zinc and/or lead salt-forming compounds are, for example:
ammelide (2,4-dihydroxy-6-amino-s-triazine),
monothioammelide (2-hydroxy-4-mercapto-6-amino-s-triazine),
dithioammelide (2,4-dimercapto-6-amino-s-triazine),
ammeline (2-hydroxy-4,6-diamino-s-triazine),
thioammeline (2-mercapto-4,6-diamino-s-triazine),
acetothioguanide (2-mercapto-4-amino-6-methyl-s-triazine),
acetoguanamide (2-4-dihydroxy-6-methyl-s-triazine),
o-carboxybenzoguanide (2-hydroxy-4-amino-6-(o-carboxyphenyl)-s-triazine),
oxonic acid (2,4-hydroxy-6-carboxy-s-triazine),
2-hydroxy-4,6-dimethoxy-s-triazine,
2,4-hydroxy-6-(p-nitrophenyl)-s-triazine, and
2,4-dihydroxy-6-allyloxy-s-triazine.
In addition to the above exemplified single-ring nucleus s-triazine derivatives, multinucleic s-triazine derivatives, as long as they contain at least one hydroxyl or mercapto group per triazine ring, can also be considered for the formation of zinc and/or lead salts, according to the invention. Among these are, for example, the oligomeric condensation products of ammeline or thioammeline with formaldehyde, or, also, oligomers or polymers or thiocyanuric acid linked over disulfide bridges.
Also zinc and/or lead salts of polynuclear condensed s-triazine ring systems with hydroxyl and/or mercapto groups as, for instance, cyameluric acid (2,5,8-trihydroxy-tri-s-triazine), are also within the ambit of the corrosion inhibitors, according to this invention.
Of special importance, in the sense of the invention, are also the zinc and/or lead salts of cyanuric and thiocyanuric acid. These salts exhibit excellent corrosion protection values when compounded as anticorrosion coating compositions even over long periods of storage.
The coatings, according to this invention, are usually at least 5 .mu.m in thickness but, preferred, are coatings in the range 10 to 100.mu. and containing the zinc, lead or zinc-lead salts as defined.

The following Examples are illustrative of the practice of the invention without being limitative.
EXAMPLES
Preparation of the zinc and/or lead salts
The preparation of the zinc and/or lead salts of the above-mentioned s-triazine derivatives is easily accomplished by different methods. In the following, these methods are illustrated based on cyanuric acid.
Preparative method 1:
Lead and/or zinc carbonate is reacted with cyanuric acid in boiling water. The corresponding metal cyanurates are formed with evolution of carbon dioxide.
Preparative method 2:
Lead and/or zinc nitrate, chloride, or acetate in aqueous solution is reacted at room temperature with an aqueous solution of trisodium or tripotassium cyanurate. The appropriate zinc or lead cyanurate precipitates from the aqueous solution.
Preparative method 3:
Zinc and/or lead oxide is reacted with cyanuric acid in boiling water, preferably in the presence of a small amount of acetic acid as catalyst. The corresponding metal cyanurates are formed.
The preparation of other zinc or lead salts with other moieties is exemplified by their preparation utilizing mercaptobenzothiazole as a representative reactant.
Preparative method 4:
Lead or zinc carbonate is reacted with mercaptobenzothiazole in boiling water. The corresponding zinc or lead salts of mercaptobenzothiazole are formed with evolution of carbon dioxide.
Preparative method 5:
Lead or zinc nitrate, chloride, or acetate is treated, in aqueous solution at room temperature, with an aqueous solution of the sodium or potassium salt of mercaptobenzothiazole. The corresponding zinc or lead salts of mercaptobenzothiazole precipitate from the aqueous solution.
Preparative method 6:
Zinc or lead oxide is reacted with mercaptobenzothiazole in boiling water, preferably, in the presence of a small amount of acetic acid as catalyst. The corresponding zinc or lead salts of mercaptobenzothiazole are formed.
The salts according to the invention are easily incorporated by mixing with conventional binder formulations to prepare the corrosion protective coating compositions of this invention. Generally, small amounts of these salts suffice to obtain the described anti-corrosive effects; i.e., the salts are added to the binders in amounts of from 0.5% to 10% by weight, preferably 1% to 3% by weight, based on the total formulation. Suitable binders for such primer lacquer compositions are the resins conventionally used for such purposes, dissolved or emulsified and dispersed in suitable solvent systems and treated with the usual pigments and fillers used in such compositions.
The following examples demonstrate the effectiveness of the corrosion protective compositions and the resultant coatings according to the invention, with regard to the corrosion protective values (CV) obtained with them, as well as with regard to the improved dispersion of these novel agents in such lacquers. As a basis for comparison, the compositions, according to this invention, were compared with compositions that contained zinc and zinc/lead salts of nitroisophthalic acid, as well as also composition containing zinc potassium chromate or zinc phosphate, as the corrosion inhibitors.
The following testing methods were used to obtain the values reproduced in the Examples:
(A) Corrosion Resistance Testing
The corrosion protective coatings prepared according to each Example were applied on rustfree, degreased steel sheets (150.times.70.times.1 mm) by a lacquer-film centrifugal device (mfg. by Erichsen, Germany, type 334/II). The resulting film thickness was standardized to measure between 30 and 33 .mu.m. After drying, the lacquer films so formed for 2 hours at 60.degree. C., then 8 days at room temperature, two of the steel sheets, each coated with the corrosion protective coating, were subjected to the salt-spray test according to ASTM B 117-64 (continuous spray with a 5% sodium chloride solution at 35.degree. C.) for 200 hours for each corrosion inhibitor composition tested.
One of the test sheets was unmarked, the other was provided, prior to the salt-spray test, with a so-called Andreas cross (Andreas cross=cross cut with a blade of 0.1 mm) through the lacquer film to the substrate.
Two additional coated steel sheets, per each corrosion inhibitor composition under test, were subjected to the Kesternich test according to DIN 50 018 without Andreas cross for the duration of 12 cycles (1 cycle=8 hours at 40.degree. C. in a humid atmosphere containing 0.2 liter sulfur dioxide; followed by an additional 16 hours without load). The stressed test sheet evaluation was based on a rust degree scale according to DIN 53 210. The corrosion protection value (CV) was then calculated according to the method described by Ruf (Farbe and Lack 75 (1969) 943-949) from the results so obtained.
(B) Sedimentation Behavior
To test the sedimentation behavior of the pigments, that is, the corrosion inhibitors in the compositions of this invention, 250 ml wide-neck glass flasks were filled with samples of the corrosion protective coating compositions described in the Examples. By careful manual probing with a 3 mm wide steel spatula, the structure of the sediment, in question, was determined at regular intervals. The rating of the structure of the sediment was based on an evaluation scale of 0 to 4.
This evaluation scale was based on the following key:
______________________________________ Is the lacquer fit Is the pigment for practical appli-Number Sediment stirrable? tion?______________________________________0 none -- yes1 slight easily yes2 moderate moderately conditionally3 strong difficult barely4 very strong no, cemented no______________________________________
The following Examples describe the preparation of coating composition according to this invention and also describe and evaluate the results obtained with coating films prepared therewith. In addition, comparison is made with representative prior art materials.
EXAMPLE 1
Composition of the binder formulation:
______________________________________Parts by Weight______________________________________34.0 short oil, resin-modified alkyd resin with 44% linseed oil/wood oil, 60% solution in xylene9.0 xylene5.6 benzine, b.p. 145.degree. to 200.degree. C.2.3 ethylene glycol ethyl ether2.3 Decalin.RTM.0.2 calcium naphthenate, 4% Ca0.4 cobalt napththenate, 6% Co0.1 lead naphthenate, 24% Pb0.3 methyl ethyl ketoxime6.8 titanium dioxide, Rutile4.5 micro talc23.7 barium sulfate8.5 zinc phosphate97.7 parts Lacquer base(by weight)______________________________________
To each 97.7 parts of this lacquer base were added 2.3 parts by weight each of the corrosion inhibitors tested. The Examples 1.1 to 1.12 are the salts according to the invention. Examples 1.13 to 1.16 contain as corrosion inhibitors, compounds according to the state of the art. In Example 1.16, zinc phosphate was present from the basic composition without any additional inhibitor.
______________________________________Ex- CV Sediment after-ample Corrosion Inhibitor in % 3 days 21 days______________________________________1.1 lead salt of mercapto- 95 0 0 pyridine (44.0% Pb)1.2 zinc salt of mercapto- 89 0 0 pyridine (22.6% Zn)1.3 lead salt of 3-cyano-6- 88 0 0 hydroxy-4-methylpyridone-2 (56.4% Pb)1.4 zinc salt of 3-cyano-6- 80 0 0 hydroxy-4-methylpyridone-2 (30.2% Zn)1.5 lead salt of barbituric acid 88 0 0 (64.5% Pb)1.6 zinc salt of barbituric 78 0 0 acid (35.2% Zn)1.7 lead salt of 5-nitroorotic 90 0 0 acid (57.9% Pb)1.8 zinc salt of 5-nitroorotic 81 0 0 acid (28.8% Zn)1.9 lead salt of hydantoin 83 0 0 (56.9% Pb) 1.10 zinc salt of hydantoin 75 0 0 (40.0% Zn) 1.11 lead salt of mercapto- 96 0 0 benzothiazole (37.3% Pb) 1.12 zinc salt of mercapto- 88 0 0 benzothiazole (16.4% Zn) 1.13 zinc salt of 5-nitro- 73 2 4 isophthalic acid (44.1% Zn) 1.14 zinc/lead mixed salt of 83 1 2 5-nitro-isophthalic acid (31.0% Zn/; 19.1% Pb) 1.15 zinc potassium chromate, 70 0 0 lead containing acc'g to DIN 55902 1.16 barium sulfate (i.e., zinc 55 0 0 phosphate alone)______________________________________ (CV = corrosion protection value)
The PVC values (pigment volume concentration) of the corrosion protective coatings of Examples 1 to 16 is in the range of from 39.4 to 39.8%.
These examples of the formulation of Example 1 show the excellent corrosion-inhibiting effect of the salts of mercaptopyridine as well as those of mercaptobenzothiazole. Especially of note are the salts of mercaptobenzothiazole, as they show excellent activity at remarkably low contents of lead or zinc. Thus, the lacquer composition with 2.3% by weight mercaptobenzothiazole salt contains, in the case of the lead salt (37.3% Pb), only 0.86% lead and in the case of the zinc salt (16.4% Zn), only 0.38% zinc, when the small lead and/or zinc content of the other components of the binder formula are disregarded.
EXAMPLE 2
Composition of the binder base used:
______________________________________Parts by Weight______________________________________34.0 short oil, resin modified alkyd resin with 44% linseed oil/wood oil, 60% solution in xylene9.0 xylene5.6 benzine, b.p. 145.degree.-200.degree. C.2.3 ethylene glycol ethyl ether2.3 Decalin.RTM.0.2 calcium naphthenate, (4% Ca)0.4 cobalt naphthenate, (6% Co)0.1 lead naphthenate, (24% Pb)0.3 methyl ethyl ketoxime6.8 titanium dioxide, Rutile4.5 micro talc23.7 barium sulfate8.5 zinc phosphate97.7 parts Lacquer baseby weight______________________________________
To each 97.7 part portion of lacquer base were added 2.3 parts by weight each of the corrosion inhibitors tested. The Examples 2.1 to 2.7 are the salts according to the invention. Examples 2.8 to 2.11 show inhibitors according to the current state of the art. In Example 2.11, zinc phosphate is present without any additional inhibitor.
______________________________________Ex- CV Sediment after-ample Corrosion Inhibitor in % 3 days 21 days______________________________________2.1 zinc trithiocyanurate 83 0 0 (34.2% Zn)2.2 lead trithiocyanurate 90 0 0 (55.6% Pb)2.3 zinc-lead cyanurate 85 0 0 (61.2% Pb; 3.9% Zn)2.4 lead cyanurate (66.1% Pb) 90 0 02.5 zinc cyanurate 80 0 0 (31.7% Zn)2.6 thioammeline, lead salt 78 0 0 (41.2% Pb)2.7 thioammeline, zinc salt 73 0 0 (18.9% Zn)2.8 zinc salt of 5-nitro- 73 2 4 isophthalic acid (44.1% Zn)2.9 zinc/lead salt of 5-nitro 83 1 2 isophthalic acid (31.0% Zn; 19.1% Pb) 2.10 zinc potassium chromate 70 0 0 containing lead acc'g to DIN 55 902 2.11 barium sulfate (i.e., 55 0 0 zinc phosphate alone)______________________________________ (CV = corrosion protection value)
EXAMPLE 3
A binder base formulation analogous to Example 1 was used, omitting the zinc phosphate. Composition:
______________________________________Parts by Weight______________________________________34.1 short oil, resin modified alkyd resin with 44% linseed/wood oil, 60% solution in xylene9.1 xylene5.7 benzine, b.p. 145.degree. to 200.degree. C.2.3 ethylene glycol ethyl ether2.3 Decalin.RTM.0.2 calcium napththenate, 4% Ca0.4 cobalt naphthenate, 6% Co0.1 lead naphthenate, 24% Pb0.3 methyl ethyl ketoxime9.1 titanium dioxide, Rutile9.1 micro talc25.0 barium sulfate97.7 lacquer base______________________________________
To each 97.7 parts of this lacquer, 2.3 parts by weight of the tested corrosion inhibitors were added. The Examples 3.1 and 3.2 are salts according to this invention. Examples 3.3 and 3.4 are comparison compounds of the prior art.
______________________________________ CV Sediment after-Example Corrosion Inhibitor in % 3 days 21 days______________________________________3.1 lead cyanurate 83 0 0 (66.1% Pb)3.2 zinc cyanurate 73 0 0 (31.7% Zn)3.3 zinc/lead salt of 5-nitro 75 1 2 isophthalic acid (31.0% Zn: 19.1% Pb)3.4 zinc potassium chromate, 50 0 0 containing lead acc'g to DIN 55 902______________________________________
The PVC values (pigment volume concentration) of the corrosion protective coatings of Examples 2 and 3 lay in the range of from 39.4 to 39.8%. The effect of an improved sedimentation behavior obtained with the corrosion protection coatings according to the invention is shown in the following examples using two additional binder formulations, where the anti-sedimentation effect of the s-triazine salts according to the invention is apparent.
______________________________________Parts by Weight______________________________________400 epoxy resin-ricinen acid ester with a fatty acid content of 42%, 60% solution in xylene110 zinc phosphate120 micro talc 80 titanium dioxide, Rutile193.5 barium sulfate 15 ethylene glycol ethyl ether 15 n-butanol 30 tetralin110 higher aromatics110 unplasticized urea resin, 65% solution in n-butanol200 xylene1373.5 coating base______________________________________
To each 1373.5 parts base, 26.5 parts per weight each of the subsequently mentioned corrosion inhibitors were added. In Example 4.4, zinc phosphate without any additional inhibitor was present. The pigment volume concentration (PVC) was about 34%.
______________________________________ Sediment afterExample Corrosion Inhibitor 3 7 14 21 30 40 days______________________________________4.1 zinc cyanurate 0 0 0 0 0 0 (31.7% Zn)4.2 zinc salt of nitro-iso- 3-4 4 4 4 4 4 phthalic acid (44.1% Zn)4.3 zinc/lead salt of nitro- 3-4 4 4 4 4 4 isophthalic acid (31.0% Zn; 19.1% Pb)4.4 barium sulfate, i.e., 0-1 2 3-4 4 4 4 zinc phosphate by itself______________________________________
EXAMPLE 5
Composition of the air-drying base coat used:
______________________________________Parts by Weight______________________________________370 linseed oil/alkyd with an oil content of 38% and modified with 20% resin, 60% solution in xylene80 zinc phosphate110 micro talc168 barium sulfate60 titanium dioxide, Rutile20 Decalin.RTM.15 ethylene glycol ethyl ether 1 cobalt naphthenate, 6% Co 4 lead naphthenate, 24% lead 1 manganese naphthenate, 6% Mn56 higher aromatics 3 methyl ethyl ketoxime190 xylene1078 vehicle______________________________________
To each 1078 parts of this vehicle were added 22 parts by weight each of the tested corrosion inhibitors. In Example 5.3, zinc phosphate without any additional inhibitor was present. The pigment volume concentration (PVC) was about 38%.
______________________________________ Sediment afterExample Corrosion Inhibitor 3 7 14 21 30 40 days______________________________________5.1 zinc cyanurate 0 0 0 0 0 0-1 (31.7% Zn)5.2 zinc salt of 5-nitro 1 1-2 2 2 2-3 3-4 isophthalic acid (44.1% Zn)5.3 barium sulfate, i.e., 0 0 0 0 0 0-1 zinc phosphate by itself______________________________________
EXAMPLE 6
Regarding the proven improvement in the sedimentation behavior of the corrosion protection coatings by the salts according to the invention, the median particle diameter d of some of the corrosion inhibitors used, was determined by means of the so-called Coulter Counter apparatus. This device works according to a process where a dilute, electrically conductive suspension flows through an aperture (20 to 400 .mu.m). At the passage of a particle through this aperture, the electric conductivity changes proportionally to the volume of the particle. The impulses so obtained are counted and analyzed as to their magnitude (see H. Kittel, Textbook of Lacquers and Coatings, Vol. II, Colomb (Berlin 1974), page 512, as well as T. C. Patton, Pigment Handbook, Vol. III, Wiley (New York 1973), pages 101-106).
The following values were obtained:
______________________________________ Median particleCorrosion Inhibitor diameter -d in .mu.m______________________________________zinc cyanurate (31.7% Zn) 10.0zinc mercaptobenzothiazole 9.5(16.4% Zn)zinc salt of 5-nitroisophthalic 5.0acid (44.1% Zn)zinc/lead salt of 5-nitro 8.5isophthalic acid(31.0% Zn; 19.1% Pb)______________________________________
The surprisingly good anti-sedimentation effect of zinc cyanurate as well as of zinc mercaptobenzothiazole is therefore not conditional on the particle size, since all determined values for d lie at the same magnitude.
The preceding specific embodiments are illustrative of the practice of the invention. It is to be understood, however, that other expedients known to those skilled in the art or disclosed herein, may be employed without departing from the spirit of the invention or the scope of the appended claims.

Number	Date	Country	Kind
2807698	Feb 1978	DEX
2824508	Jun 1978	DEX

Number	Name	Date
2727879	Vincent	Dec 1955
3436364	Logemann et al.	Apr 1969
3535300	Gable	Oct 1970
3929794	McCrae	Dec 1975
3940482	Grand	Feb 1976

Method for providing corrosion resistance to metal objects

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (2)

US Referenced Citations (5)