The present invention relates generally to a process for recovering copper from a copper-containing ore, concentrate, or other copper-bearing material, and more specifically, to a process for producing cathode copper without the use of solvent/solution extraction, ion exchange of copper, or related processes to refine and concentrate the copper-bearing solution.
Hydrometallurgical treatment of copper containing materials, such as copper ores, concentrates, and other copper-bearing materials, has been well established for many years. Currently, there exist many creative approaches to the hydrometallurgical treatment of these materials; however, common to almost all of the processes either now known or under development is the use of solvent extraction and electrowinning (SX-EW) for solution purification and copper recovery. Although SX-EW is not without its drawbacks, the proven success in the copper SX-EW field has made this approach standard for production of high quality copper products.
The traditional hydrometallurgical process for copper recovery involves first leaching copper-containing material with an acidic solution, either atmospherically or under conditions of elevated temperature and pressure. The resultant process stream—the so-called pregnant leach solution—is recovered, and in a solvent extraction (or solution extraction, as it is sometimes called) stage, is mixed with an organic solvent (i.e., an extractant), which selectively removes the copper from the pregnant leach solution. The copper-loaded extractant is then mixed with an aqueous acid solution, which strips the copper from the extractant, producing a solution stream suitable for electrowinning. This resultant solution stream is highly concentrated and relatively pure, and typically is processed into high quality copper cathode in an electrowinning circuit.
In general, electrowinning of copper consists of the electrolytic deposition (sometimes called “plating”) of copper onto a cathode and the evolution of oxygen at an anode. In a simple design of an exemplary electrowinning unit, a set of cathodes and anodes are set in a reaction chamber containing the copper-containing electrolyte. When the unit is energized, copper ions are reduced onto the cathode (i.e., plated). Plating of copper typically occurs on copper starter sheets or stainless steel blanks. Anodes are quasi-inert in the electrolyte and provide a surface for oxygen evolution. The copper plates produced by the electrowinning unit can be in excess of 99.99 percent pure.
Purification of copper from the pregnant leach solution by solvent extraction has proven to be a successful means of providing a concentrated copper solution suitable for electrowinning of highly pure copper metal. Direct electrowinning of copper—that is, plating of copper directly from the pregnant leach solution without the intervening step of purification by solvent extraction—is known. However, the copper recovered by such so-called direct electrowinning processes often is too impure for sale or use as is, and thus, generally must be further refined at an additional cost, or may be sold at a discount. More specifically, prior art techniques have shown the ability for direct electrowinning of copper to produce a relatively low-quality copper product.
An effective and efficient method to recover copper from copper-containing materials, especially copper from copper sulfides such as chalcopyrite and chalcocite, that enables high copper recovery to be achieved at a reduced cost over conventional processing techniques would be advantageous.
While the way in which the present invention addresses the deficiencies and disadvantages of the prior art is described in greater detail hereinbelow, in general, according to various aspects of the present invention, a process for recovering copper and other metal values from a copper-containing material includes obtaining a copper-containing solution from, for example, a pressure leaching system, and then appropriately conditioning the copper-containing solution for electrowinning. In a preferred aspect of the invention, the composition of the copper-containing solution is similar to the composition of the electrolyte produced by a solvent extraction circuit, for example, with respect to acid and copper concentrations. In accordance with the various embodiments of the present invention, however, the copper-containing solution is not subjected to solvent extraction.
In accordance with an exemplary embodiment of the present invention, a process for recovering copper from a copper-containing material generally includes the steps of: (i) providing a feed stream containing copper-containing material; (ii) subjecting the copper-containing feed stream to atmospheric leaching or pressure leaching to yield a copper-containing solution; (iii) conditioning the copper-containing solution through one or more chemical or physical conditioning steps; and (iv) electrowinning copper directly from the copper-containing solution, without subjecting the copper-containing solution to solvent extraction. As used herein, the term “pressure leaching” shall refer to a metal recovery process in which material is contacted with an acidic solution and oxygen under conditions of elevated temperature and pressure.
In accordance with an exemplary embodiment of the present invention, a process for recovering copper from a copper-containing material generally includes the steps of: (i) providing a feed stream containing copper-containing material; (ii) subjecting the copper-containing feed stream to atmospheric leaching or pressure leaching to yield a copper-containing solution; (iii) conditioning the copper-containing solution through one or more chemical or physical conditioning steps; and (iv) electrowinning copper directly from the copper-containing solution, without subjecting the copper-containing solution to solvent extraction. As used herein, the term “pressure leaching” shall refer to a metal recovery process in which material is contacted with an acidic solution and oxygen under conditions of elevated temperature and pressure.
In one aspect of a preferred embodiment of the invention, one or more processing steps are used in order to separate copper from the acid in a recycled portion of the lean electrolyte from the direct electrowinning process, thus enabling the rejection of a portion of the acid component from the process circuit without rejecting a significant portion the copper. As discussed in greater detail hereinbelow, a number of conventional or hereafter devised processes may be utilized to separate copper from acid in the feed stream. For example, in accordance with one aspect of an exemplary embodiment of the invention, a copper precipitation step may be utilized to precipitate solubilized copper from a lean electrolyte stream onto the surfaces of solid particles in a copper-containing material stream in advance of the pressure leaching step, thus separating the copper from the acid solution.
In an aspect of another embodiment of the invention, a recycle circuit is used intermediate to the leaching and electrowinning steps to facilitate control of the composition of copper-containing solution entering the electrowinning stage, and to thus enhance the quality of the copper recovered therefrom.
In accordance with various preferred aspects of the present invention, by providing for the electrowinning of copper directly from a copper-containing solution without first subjecting the copper-containing solution to solvent extraction, the present invention enables lower-cost recovery of copper and eliminates the expenses associated with solvent extraction, such as specialized reagents, process apparatus and equipment, and energy resources. Furthermore, in accordance with one preferred aspect of the invention, careful control of the composition of the copper-containing solution entering the electrowinning circuit enables production of high quality, uniformly-plated cathode copper.
These and other advantages of a process according to various aspects of the present invention will be apparent to those skilled in the art upon reading and understanding the following detailed description with reference to the accompanying figures.
The subject matter of the present invention is particularly pointed out and distinctly claimed in the concluding portion of the specification. A more complete understanding of the present invention, however, may best be obtained by referring to the detailed description and claims when considered in connection with the drawing figures, wherein like numerals denote like elements and wherein:
The present invention exhibits significant advancements over prior art processes, especially other so-called “direct electrowinning” processes, particularly with regard to product quality and process efficiency. Moreover, existing copper recovery processes that utilize a conventional atmospheric or pressure leaching/solvent extraction/electrowinning process sequence may, in many instances, be easily retrofitted to exploit the many commercial benefits the present invention provides.
In one aspect of a preferred embodiment of the invention, the relatively large amount of acid generated during the electrowinning stage as a copper-containing electrolyte stream is transported out of the copper recovery process after a separation step in which substantially all of the copper is removed from the acid stream. It is generally economically advantageous to utilize this generated acid stream in some way, rather than to neutralize or dispose of it. Thus, as discussed in greater detail hereinbelow, the present invention may find particular utility in combination with conventional atmospheric leaching operations, such as, for example, heap leaching, vat leaching, dump or stockpile leaching, pad leaching, agitated tank leaching, and bacterial leaching operations, which often require a substantially continuous acid supply.
In one aspect of an exemplary embodiment of the present invention, a feed stream containing copper-containing material is provided for processing. In accordance with the various embodiments of present invention, the copper-containing material may be an ore, a concentrate, or any other copper-bearing material from which copper and/or other metal values may be recovered. The copper in the copper-containing material may be in the form of copper oxides, copper sulfides or other copper minerals, and the copper-containing material may include any number of a variety of other metals, such as, for example, gold, platinum group metals, silver, zinc, nickel, cobalt, molybdenum, rare earth metals, rhenium, uranium and mixtures thereof. Various aspects and embodiments of the present invention prove especially advantageous in connection with the recovery of copper from copper sulfide ores, such as, for example, chalcopyrite (CuFeS2), chalcocite (Cu2S), bornite (Cu5FeS4), and covellite (CuS).
The feed stream of copper-containing material can be provided in any number of ways, such that the conditions of the feed stream are suitable for the chosen processing methods. For example, feed stream conditions such as particle size, composition, and component concentrations can affect the overall effectiveness and efficiency of downstream processing operations, such as, for example, atmospheric leaching or pressure leaching.
In accordance with a preferred aspect of the invention, the particle size of the copper-containing feed material is reduced to facilitate fluid transport and to optimize the processing steps of atmospheric or pressure leaching and subsequent metal recovery processes. A variety of acceptable techniques and devices for reducing the particle size of the copper-containing material are currently available, such as ball mills, tower mills, ultrafine grinding mills, attrition mills, stirred mills, horizontal mills and the like, and additional techniques may later be developed that may achieve the desired result of increasing the surface area of the material to be processed. With regard to one aspect of a preferred embodiment of the invention, such a result is desired because the reaction rate during leaching generally increases as the surface area of the copper-containing material increases, such that increasing the fineness of the copper-containing material before subjecting the material stream to pressure leaching generally will allow for more moderate temperature and pressure conditions to be employed within the pressure leaching vessel, and may reduce the residence time of the oxidation reaction during pressure leaching.
In another aspect of a preferred embodiment of the present invention, the comminuted copper-containing material is combined with a liquid to form a copper-containing material stream 101. Preferably, the liquid comprises water, but any suitable liquid may be employed, such as, for example, raffinate, pregnant leach solution, or lean electrolyte. For example, a portion of lean electrolyte stream 108 from the direct electrowinning process may be combined with comminuted copper-containing material to form copper-containing material stream 101 (not shown in
In another aspect of a preferred embodiment of the present invention, the comminuted copper-containing material is combined with a liquid to form a copper-containing material stream 101. Preferably, the liquid comprises water, but any suitable liquid may be employed, such as, for example, raffinate, pregnant leach solution, or lean electrolyte. For example, a portion of lean electrolyte stream 108 from the direct electrowinning process may be combined with comminuted copper-containing material to form copper-containing material stream 101 (not shown in
The combination of the liquid with the copper-containing material can be accomplished using any one or more of a variety of techniques and apparatus, such as, for example, in-line blending or using a mixing tank or other suitable vessel. In accordance with a preferred aspect of this embodiment, the material stream is concentrated with the copper-containing material being on the order less than about 50 percent by weight of the stream, and preferably about 40 percent by weight of the stream. Other concentrations that are suitable for transport and subsequent processing may, however, be used.
In accordance with one aspect of the present invention, it is desirable to separate the copper in a recycled stream of lean electrolyte from electrowinning from the acid, and also to reduce the amount of contaminants in the portion of the stream to be subjected to the metal recovery process. In such a separation process, the acid that is removed from the recycled lean electrolyte stream may be rejected from the process circuit, taking with it at least a portion of the metal contaminants and other soluble impurities from the copper-containing feed stream and the recycled lean electrolyte stream. Any number of conventional or hereafter devised separation processes and techniques may be useful to achieve the separation of copper from acid in the feed stream. For example, separation processes and/or techniques such as precipitation, low temperature pressure leaching, acid solvent extraction/ion exchange, membrane separation, cementation, pressure reduction, sulfiding, and/or the use of liberator cells may be useful for this purpose.
The separation aspect of a preferred embodiment of the invention contributes to providing a resultant acid stream that contains a relatively small fraction of copper, which can be used for leaching, pH control, or other applications. Moreover, utilization of a separation process in accordance with this aspect of the invention may be particularly advantageous in that it may enable contaminants from the unrefined copper-containing material stream to be removed from the copper-containing material stream and incorporated into the resultant acid stream. Because the resultant acid stream is preferably removed from the metal recovery process altogether and utilized in remote operations, disposed of, or neutralized, the contaminants contained therein are likewise removed from the metal recovery process and are thus prevented from accumulating in the process stream. This may be a significant advantage in that such contaminants, particularly metal contaminants, typically have a deleterious effect on the effectiveness and efficiency of the desired metal recovery process. For example, metal contaminants and other impurities in the process stream, if not carefully controlled and/or minimized, can contribute to diminished physical and/or chemical properties in the cathode copper produced by electrowinning, and can thus degrade the copper product and diminish its economic value.
Referring again to
In this preferred aspect of the invention, the precipitation step involves the copper-containing material stream being combined with a sulfur dioxide (SO2) stream 109 and a lean electrolyte stream 108 in a suitable processing vessel. For example, in the embodiment illustrated in
2Cu+2+CuFeS2+4SO2+4H2O→3CuS+3SO4−2+8H++Fe+2CuFeS2+Cu+2→Fe+2+2CuS (possible side reaction)
Other copper minerals and other sulfides react to varying degrees according to similar reactions, producing copper precipitates and a weak sulfuric acid by-product. In accordance with a preferred aspect of the invention, copper separation stage 1010 is carried out at a slightly elevated temperature, such as from about 70° C. to about 180° C., preferably from about 80° C. to about 100° C., and most preferably at a temperature of about 90° C. Heating, if necessary, can be effectuated through any conventional means, such as electric heating coils, a heat blanket, process fluid heat exchange, and other ways now known or later developed. In the exemplary process of
Other parameters to consider when conditioning the copper-containing material feed stream for processing are the fraction of solid particles in the feed stream and the total volume of the feed stream. Thus, these or other parameters, such as, for example, temperature, pressure, viscosity, density, composition, and the like, may be suitably addressed. Although these parameters may or may not be significant to the overall efficiency of processing operations downstream in all cases, these parameters can affect equipment size and material specifications, energy requirements, and other important aspects of process design. Thus, calculated adjustment of these stream parameters in advance of complex or resource-intensive processing stages can positively affect the economic efficiency of the chosen process. Solid-liquid separation systems, such as, for example, filtration systems, counter-current decantation (CCD) circuits, thickeners, and the like are useful in adjusting these parameters and are widely used in the industry.
In one aspect of the embodiment of the invention illustrated in
In accordance with a preferred aspect of the invention, the copper-containing material stream entering the pressure leaching stage contains from about 10 to about 50 percent solids by weight, preferably from about 20 to about 40 percent solids by weight. To adjust the solids concentration of product stream 102 in accordance with the desired parameters, in accordance with an exemplary embodiment of the invention, product stream 102 is sent to a solid-liquid separation circuit 1020. In one aspect of a preferred embodiment of the invention, solid-liquid separation circuit 1020 preferably includes a wash thickener circuit 1021 comprising multiple thickener stages arranged in a counter-current decantation (CCD) configuration that effectuate separation of a substantial amount of the acid in the product stream from the copper-containing solid particles therein. In the illustrated embodiment, the underflow of thickener circuit 1021 is pressure leaching feed stream 103 and the overflow is acid stream 110. Preferably, acid stream 110 contains only a negligible amount of copper.
Process effluent acid stream 110 may be utilized, processed, neutralized, impounded, and/or disposed of in a variety of ways, the appropriate choice of which is largely dependent upon economic and regulatory factors. In one aspect of the illustrated embodiment, the acid stream can be beneficially used in, for example, an atmospheric leaching operation, where acid is required to leach copper oxide or sulfide minerals. Such a leaching operation may be a heap leach, a vat leach, a tank leach, a pad leach, or any other similar operation. Acid is consumed in these operations through reaction with acid-consuming constituents in the ore.
In
In accordance with a further aspect of this embodiment of the present invention, as previously briefly mentioned, acid stream 110 advantageously may remove impurities from the process, for example the electrowinning process. Such impurities include, without limitation, iron, aluminum, magnesium, sodium, potassium and the like, often present as sulfates. In the absence of removal, such impurities may accumulate to deleterious levels, and, as such negatively impact production efficiencies and product (e.g. copper cathode) quality. The presence of such impurities in acid stream 110 generally does not negatively impact the aforementioned handling of acid stream 110.
In accordance with one aspect of a preferred embodiment of the invention illustrated in
In accordance with one alternative aspect of the invention, aqueous stream 204 may not be subjected to electrowinning immediately after leaving the solvent extraction unit, but may instead be blended with other copper-containing process streams, and the resultant stream then sent to an electrowinning circuit. For example, all or a portion of aqueous stream 204 (broken line) may be blended with copper-containing solution stream 106 and lean electrolyte stream 115 in electrolyte recycle tank 1060 (from
If effluent acid stream 110 is not used as a by-product reagent or otherwise utilized, the acid may be neutralized using, for example, acid-consuming gangue (i.e., mineral processing tailings) or a neutralizing agent, such as limestone or lime. Neutralizing with acid-consuming gangue can be relatively inexpensive, as the neutralizing reagent is essentially free. On the other hand, neutralizing with limestone or lime may be less desirable economically, as both these reagents will incur cost. Nevertheless, should neutralization be desired, any method for acid neutralization now known or hereafter devised may be employed.
Referring again to
In a further aspect of the present invention, the conditioned copper-containing feed stream preferably is subjected to a suitable process, such as pressure leaching, to produce a product slurry 104, which comprises a copper-containing solution and a residue 114. The process may be selected as desired, but, in general, enables production of a copper-containing solution that exhibits copper and acid concentrations similar to an electrolyte stream resulting from a solvent extraction circuit—that is, the copper-containing solution preferably is suitable for processing in an electrowinning circuit. Any suitable technique or combination of techniques that yields an appropriate copper-containing solution without employing solvent extraction techniques may be used. In a preferred embodiment of the invention, as illustrated in
In accordance with one aspect of this embodiment of the present invention, pressure leaching feed stream 103 is transported to a suitable vessel for pressure leaching, which can be any vessel suitably designed contain the process components at the desired temperature and pressure conditions for the requisite processing residence time. In a preferred embodiment, a pressure leaching vessel 1031 is employed for this purpose. Pressure leaching vessel 1031 is preferably a multi-compartment, agitated vessel.
Generally, the chemical conversions that occur during pressure leaching stage 1030 under certain conditions for the solubilization of the copper in copper-containing materials, such as chalcopyrite, chalcocite, or covellite are as follows:
4CuFeS2+17O2+4H2O→4CuSO4+4H2SO4+2Fe2O3
2Cu2S+5O2+2H2SO4→4CuSO4+2H2O
CuS+2O2→CuSO4
If desired, conditions during pressure leaching can be controlled such that a portion of the sulfide sulfur contained in the feed stream is converted to elemental sulfur instead of sulfate. The fraction of chalcopyrite and covellite that form sulfur instead of sulfate are believed to react according to the following equations:
4CuFeS2+4H2SO4+5O2→4CuSO4+2Fe2O3+8S0+4H2O
2CuS+2H2SO4+O2→2Cu+2+2SO4−2+2H2O+2S0
Pressure leaching, for example in pressure leaching vessel 1031, preferably occurs in a manner suitably selected to promote the solubilization of copper using these (or other) processes. In general, temperature and pressure in the pressure leaching vessel should be carefully controlled. For example, in accordance with one aspect of the invention, the temperature of pressure leaching vessel 1031 is maintained at from about 100° C. to about 250° C., preferably from about 140° C. to about 235° C. In accordance with one aspect of one embodiment of the invention, the temperature of pressure leaching vessel 1031 is advantageously maintained at from about 140° C. to about 180° C. or in the range of from about 150° C. to about 175° C. In accordance with another embodiment of the invention, the temperature of pressure leaching vessel 1031 is advantageously maintained between from about 200° C. to about 235° C. or in the range of from about 210° C. to about 225° C. Furthermore, the total operating pressure in pressure leaching vessel 1031 is necessarily superatmospheric, ranging from about 50 to about 750 psi. In accordance with one aspect of one embodiment of the invention, the pressure is advantageously in the range of between from about 200 to about 450 psi, and more preferably from about 250 to about 400 psi. In accordance with another embodiment of the invention, the pressure is advantageously maintained between from about 400 or about 500 to about 700 psi.
During pressure leaching, it is generally desirable to inject oxygen into the pressure leaching vessel. In one aspect of a preferred embodiment of the invention, during pressure leaching in pressure leaching vessel 1031, sufficient oxygen 112 is injected into the vessel to maintain an oxygen partial pressure in pressure leaching vessel 1031 of from about 50 to about 200 psi, preferably from about 75 to about 150 psi, and most preferably from about 100 to about 125 psi.
Because pressure leaching of many metal sulfides is a highly exothermic process and the heat generated is generally greater than that required to heat pressure leaching feed stream 103 to the desired operating temperature, cooling liquid 1111 is preferably contacted with pressure leaching feed stream 103 in pressure leaching vessel 1031 during pressure leaching. Cooling liquid 111 is preferably process water, but can be any suitable cooling fluid from within the refining process or from an outside source. In a preferred embodiment of the invention, a sufficient amount of cooling liquid 111 is added to pressure leaching vessel 1031 to yield a solids content in the product slurry 104 ranging from about 3 to about 15 percent solids by weight.
The residence time for pressure leaching generally depends on a number of factors, including the composition of the copper-containing feed stream and the operating pressure and temperature of the pressure leaching vessel. In one aspect of the invention, the residence time for pressure leaching ranges from about thirty minutes to about three hours.
In another aspect of the present invention, the copper-containing solution is conditioned for electrowinning through one or more chemical and/or physical processing steps. In much the same way that the copper-containing material feed stream is conditioned for processing in accordance with above-described aspects of the invention, the copper-containing solution intended to be utilized in the electrowinning circuit of the present invention is conditioned to adjust the composition, component concentrations, volume, temperature, and/or other physical and/or chemical parameters to desired values. Generally, a properly conditioned copper-containing solution will contain a relatively high concentration of copper in an acid solution and will contain few impurities. Preferably, the conditions of copper-containing solution entering the electrowinning circuit are kept at a constant level to enhance the quality and uniformity of the cathode copper product.
In a preferred aspect of the invention, conditioning of a copper-containing solution for electrowinning begins by adjusting certain physical parameters of the product slurry from the previous processing step. In a preferred embodiment of the invention wherein the previous processing step is pressure leaching, it is desirable to reduce the temperature and pressure of the product slurry. A preferred method of so adjusting the temperature and pressure characteristics of the preferred product slurry is atmospheric flashing.
Thus, in accordance with a preferred aspect of the embodiment illustrated in
Referring again to
Depending on its composition, residue stream 114 from liquid/solid separation stage 1050 may be impounded, disposed of, or subjected to further processing, such as, for example, precious metal recovery. For example, if residue stream 114 contains economically significant amounts of gold, silver, and/or other precious metals, it may be desirable to recover this gold fraction through a cyanidation process or other suitable recovery process. If gold or other precious metals are to be recovered from residue stream 114 by cyanidation techniques, the content of contaminants in the stream, such as elemental sulfur, amorphous iron precipitates, and unreacted copper minerals, is preferably minimized. Such materials may promote high reagent consumption in the cyanidation process and thus increase the expense of the precious metal recovery operation. As mentioned above, it is therefore preferable to use a large amount of wash water or other diluent during the solid-liquid separation process to maintain low copper and acid levels in the solids-containing residue stream in an attempt to optimize the conditions for subsequent precious metal recovery.
As previously noted, careful control of the conditions of a copper-containing solution entering an electrowinning circuit—especially maintenance of a substantially constant copper composition—can enhance the quality of the electrowon copper by, among other things, enabling even plating of copper on the cathode and avoidance of surface porosity in the cathode copper, which degrades the copper product and thus may diminish its economic value. In accordance with this aspect of the invention, such process control can be accomplished using any of a variety of techniques and equipment configurations, so long as the chosen system and/or method maintains a sufficiently constant feed stream to the electrowinning circuit.
Referring again to
Referring briefly to an alternative embodiment of the invention illustrated in
Referring again to
With reference to
As those skilled in the art are aware, a variety of methods and apparatus are available for the electrowinning of copper and other metal values, any of which may be suitable for use in accordance with the present invention, provided the requisite process parameters for the chosen method or apparatus are satisfied. For the sake of convenience and a broad understanding of the present invention, an electrowinning circuit useful in connection with various embodiments of the invention may comprise an electrowinning circuit, constructed and configured to operate in a conventional manner. The electrowinning circuit may include electrowinning cells constructed as elongated rectangular tanks containing suspended parallel flat cathodes of copper alternating with flat anodes of lead alloy, arranged perpendicular to the long axis of the tank. A copper-bearing leach solution may be provided to the tank, for example at one end, to flow perpendicular to the plane of the parallel anodes and cathodes, and copper can be deposited at the cathode and water electrolyzed to form oxygen and protons at the anode with the application of current. As with conventional electrowinning cells, the rate at which direct current can be passed through the cell is effectively limited by the rate at which copper ions can pass from the solution to the cathode surface. This rate, called the limiting current density, is a function of factors such as copper concentration, diffusion coefficient of copper, cell configuration, and level of agitation of the aqueous solution.
The general chemical process for electrowinning of copper from acid solution is believed to be as follows:
2CuSO4+2H2O→2Cu0+2H2SO4+O2
Cathode half-reaction: Cu2++2e−→Cu0
Anode half-reaction: 2H2O→4H++O2+4e−
Turning again to
In accordance with a preferred aspect of the invention, electrowinning circuit 1070 yields a cathode copper product 116, optionally, an off gas stream 117, and a relatively large volume of copper-containing acid, herein designated as lean electrolyte streams 108 and 115. As discussed above, in the illustrated embodiment of the invention, lean electrolyte streams 108 and 115 are directed to copper precipitation stage 1010 and electrolyte recycle tank 1060, respectively. Lean electrolyte streams 108 and 115 generally have a lower copper concentration than product stream 107, but typically have a copper concentration of less than about 40 grams/liter.
The present invention has been described above with reference to a number of exemplary embodiments. It should be appreciated that the particular embodiments shown and described herein are illustrative of the invention and its best mode and are not intended to limit in any way the scope of the invention as set forth in the claims. Those skilled in the art having read this disclosure will recognize that changes and modifications may be made to the exemplary embodiments without departing from the scope of the present invention. For example, although reference has been made throughout to copper, it is intended that the invention also be applicable to the recovery of other metals from metal-containing materials. Further, although certain preferred aspects of the invention, such as techniques and apparatus for conditioning process streams and for precipitation of copper, for example, are described herein in terms of exemplary embodiments, such aspects of the invention may be achieved through any number of suitable means now known or hereafter devised. Accordingly, these and other changes or modifications are intended to be included within the scope of the present invention, as expressed in the following claims.
This application is a continuation of U.S. patent application Ser. No. 10/737,420, which was filed on Dec. 15, 2003 and issued as U.S. Pat. No. 6,972,107 on Dec. 6, 2005, which application is a continuation of U.S. patent application Ser. No. 10/238,399, which was filed on Sep. 9, 2002 and issued as U.S. Pat. No. 6,663,689 on Dec. 16, 2003, which application is a continuation of U.S. patent application Ser. No. 09/912,921, which was filed on Jul. 25, 2001 and issued as U.S. Pat. No. 6,451,089 on Sep. 17, 2002, the disclosures of which are incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10737420 | Dec 2003 | US |
| Child | 11164767 | Dec 2005 | US |
| Parent | 10238399 | Sep 2002 | US |
| Child | 10737420 | Dec 2003 | US |
| Parent | 09912921 | Jul 2001 | US |
| Child | 10238399 | Sep 2002 | US |