Patent Application
20220243394
The present invention relates to a method for recovering fiber from screening reject, which makes it possible to recover additional fiber from screening reject that has been gained in a coarse sorting process when fiber is recovered from waste paper, and a fine sorting pre-processing device for use in the method for recovering fiber.
In order to recover fiber from waste paper, a disaggregation process for disaggregating waste paper with a pulper or the like, a coarse sorting process for removing foreign material from fiber slurry gained in the disaggregation process with a screen and a fine sorting process for removing smaller foreign material again with a screen are adopted as the main processes, and an appropriate screen is used respectively for the coarse sorting process and the fine sorting process.
Waste paper contains an adhesive that was used in the respective stages of printing on paper, processing, and packaging, as well as a binder that was mixed in the paper. When the screens fail to remove these sticky foreign materials, which are thus collected together with fiber and fed into a papermaking process, there is a risk that the materials could not only adhere to the papermaking machine or the dryer as stain, but also cause peeling or tearing of the paper, which lowers the quality of paper.
Therefore, the size of the slits of the screen is set to a smaller one from the stage of the coarse sorting process in order to remove the sticky foreign material as screening reject. Thus, the screening reject is discarded.
In the screening reject, however, fiber adheres to the sticky foreign material, and as a result, the fiber is also discarded together with the screening reject, which makes the yield of recovered fiber poor.
Patent Literature 1: Japanese Unexamined Patent Publication H10 (1998)-212680
In order to address the problem, it has been proposed to feed the sticky foreign material into the fine sorting process after being finely shredded by using a disaggregating machine as described in Patent Literature 1.
According to this proposal, the fine re-shredded sticky foreign material can prevent the papermaking machine from being stained as described above, and thus can prevent the lowering of the paper quality while increasing the yield of the recovered fiber. Contrary to this expectation, the quality of fiber is lowered due to the cutting effects of such a disaggregating machine, which damages or cuts the fiber. In addition, the sticky foreign material that has been finely shredded once aggregates again due to the heat of the dryer and becomes tangible.
It is also proposed to recover the screening reject that is gained in the coarse sorting process and return the collected screening reject to the pulper in the disaggregation process. Even when such treatment with the pulper is repeated, however, the yield of the recovered fiber does not change much.
The present invention is made by focusing on the above-described problem with the prior art, and an object thereof is to provide a novel and useful method for recovering fiber from screening reject which makes it possible to separate fiber well from the sticky foreign material without damaging the fiber by focusing on the screening reject gained in the coarse sorting process, and a fine sorting pre-processing device for use in the method for recovering fiber.
The present invention is provided in order to solve the above-described problem, and the invention according to the first aspect is a method for recovering fiber from screening reject in recycling of waste paper, characterized by: feeding screening reject that has been gained in a coarse sorting process using the fine sorting pre-processing device into a fine sorting pre-processing process, wherein such an environment that heat of 90° C. or higher is generated through friction between fibers and sticky foreign material is softened and becomes expandable and contractable is utilized in order to progress the detachment of sticky foreign material from fibers and the granulation and balling up of the detached sticky foreign material by kneading the sticky foreign material; and after that, discharging the resulting material from the fine sorting pre-processing device, and in the discharged state, feeding the resulting material into a fine sorting process, wherein the balled-up sticky foreign material is separated as screening reject, and then, fiber is recovered.
The invention according to the second aspect is the method for recovering fiber from screening reject according to the first aspect, characterized in that the relative amount of sticky foreign material is increased through condensation before the sticky foreign material is fed into the fine sorting pre-processing process in the case where the concentration of the screening reject that has been gained in the coarse sorting process is less than 25%.
The invention according to the third aspect is the method for recovering fiber from screening reject according to the first or the second aspect, characterized in that the same process as that in the fine sorting process for the screening fines that have been gained in the coarse sorting process is used for the screening reject that has been gained in the coarse sorting process after the screening reject has been fed into the fine sorting pre-processing process.
The invention according to the fourth aspect is the method for recovering fiber from screening reject according to any of the first through third aspects, using the fine sorting pre-processing device provided with: a cylinder body of which the direction of the axis is horizontal; a rotating shaft that is provided within the cylinder body in the direction of the axis so as to be rotatable around the axis; a group of rotating blades attached to the rotating shaft; and a group of stationary blades provided so as to protrude from the inner surface of the cylinder body towards the axis, and characterized in that the rotating blades in the group of rotating blades are diagonal relative to the rotating shaft as viewed in the direction of the axis, and the group includes feeding blades and retrieving blades of which the phases shift from each other in such a manner that the planes of the blades cross each other, the stationary blades in the group of stationary blades are located in one space between adjacent rotating blades after another as viewed in the direction that is perpendicular to the direction of the axis as the rotating blades rotate, and a successive change in the positional relationship between the rotating blades and between the rotating blades and the stationary blades due to the rotation of the group of rotating blades progresses the detachment of the sticky foreign material from the fibers that are included in the screening reject hit by the blades and the granulation and the balling up of the detached sticky foreign material by kneading the detached sticky foreign material.
The invention according to the fifth aspect is the method for recovering fiber from screening reject according to the fourth aspect, characterized in that, in the fine sorting pre-processing device, both the rotating blades and the stationary blades are formed of quadrilateral plate-like bodies.
The invention according to the sixth aspect is the method for recovering fiber from screening reject according to the fourth or the fifth aspect, characterized in that, in the fine sorting pre-processing device, the rotating blades of the group of rotating blades are attached so as to be exchangeable, and the arrangement of the feeding blades and the retrieving blades can be changed.
The invention according to the seventh aspect is the method for recovering fiber from screening reject according to fifth or sixth aspects, characterized in that, in the fine sorting pre-processing device, the rotating blades of the group of rotating blades are diagonal relative to the rotating shaft as viewed in the direction of the axis, and the group includes feeding blades and retrieving blades of which the phases shift by 180° so that the planes of the blades cross each other.
According to the present invention, fiber can be collected from screening reject gained in a coarse sorting process without damaging the fiber and with a high yield.
An embodiment of the present invention is described in reference to the drawings.
In order to recover fiber from waste paper, a disaggregation process for disaggregating waste paper with a pulper or the like, a coarse sorting process for removing foreign material from fiber slurry gained in the disaggregation process with a screen, and a fine sorting process for removing smaller foreign material again with a screen are adopted as the main processes. In the present invention, the screening reject gained in this coarse sorting process is targeted to be processed.
The screening reject contains as sticky foreign material an adhesive that is used in the stages of printing on paper, processing, and packaging, and a binder that is mixed in the paper, and single fibers, a bundle of fibers, or tangled fibers stick to or are mixed in the sticky foreign material. The screening reject is fed into the processes shown in
It is preferable for the concentration of the screening reject to have been increased to approximately 25%. When the concentration is high, the sticky foreign material is aggregated to an appropriate size, and thus, it becomes easy to expand or contract.
In some cases, the concentration of the screening reject is high depending on the screen, and in other cases, the screening reject is enriched in a concentration process.
In this concentration process, it is preferable to use a spin dryer with a drying drum. When the screening reject is concentrated through the drying effects, the fiber is not damaged or torn.
After that, the screening reject is fed into a fine sorting pre-processing process. The fine sorting pre-processing device 1 to be used in this fine sorting pre-processing process is described below in detail.
After that, the screening reject is fed into a fine sorting process. The screen that is appropriate for use in the fine sorting process has 10 to 6 cuts and a slit width in a range from 0.25 mm to 0.15 mm, and thus, it is recommended to adjust the screen in that range.
This screen is as fine as a fine sorting screen that is used for the final fine sorting process to which the screening reject that is gained as screening fines after passing through the screen in the coarse sorting process.
As shown in
As shown in
The inside of the cylinder body 2 has different configurations between the opening for input 3 side and the opening for discharge 4 side, and as shown in
In the detachment/granulation zone Z2, a group of rotating blades 7 is attached to the rotating shaft 5.
As shown in
The block 9 is attached to the rotating shaft 5 so as to be removable. As viewed in the direction that is perpendicular to the axis of the rotating shaft 5, the block 9 engages with the rotating shaft 5 in such a manner as to cover the rotating shaft 5 from the outside, in which state four rotating blades 8, 8, . . . can be seen as to spread towards the outside in the direction of the diameter in a radial manner.
In addition, the rotating blades 8, 8, . . . are attached so as to be aligned in series in the direction of the axis, and four lines of the rotating blades 8, 8, . . . are provided on the outer peripheral surface of the rotating shaft 5 along the direction of the axis.
The plate surface of a rotating blade 8 is diagonal relative to the rotating shaft 5 at an appropriate angle as viewed from the direction of the axis. Here, the rotating blades 8 are categorized into two types, where rotating blades 8a and rotating blades 8b are in such a relationship that the phases are shifted by 180° from each other. Accordingly, the respective plate surfaces of the rotating blades 8a and the rotating blades 8b, which are both attached to the rotating shaft 5, are in such a relationship as to cross through the planes that are extended from the respective plane surfaces. The rotating blades 8a and the rotating blades 8b shown in
The plate surfaces of the rotating blades 8a are inclined so that the screening reject that has been pushed from the conveyance zone Z1 is fed towards the opening for discharge 4 side, and thus, the rotating blades 8a work as feeder blades. Meanwhile, the plate surfaces of the rotating blades 8b are inclined so that the screening reject that has been pushed from the conveyance zone Z1 is returned toward the conveyance zone Z1 side, and thus, the rotating blades 8b work as retrieval blades.
As described above, the rotating blades 8 are attached to the rotating shaft 5 via the block 9, where the combination and arrangement of the rotating blades 8a and the rotating blades 8b are free.
In this embodiment, the rotating blades 8a and the rotating blades 8b are aligned along the direction of the axis so as to alternate.
Stationary blades 11 in a group of stationary blades 10 are also formed of plate-like rectangular bodies. One short side of each body is fixed to the inner surface of the cylinder body 2 in such a manner that the stationary blades 11 are provided so as to protrude toward the inside in the direction of the radius. In addition, the plate surfaces of the stationary blades 11 face in the direction of the axis.
The stationary blades 11 are fixed to two locations that are 90° away from each other as viewed along the direction that is perpendicular to the direction of the axis of the cylinder body 2. In addition, the stationary blades 11, 11, . . . are attached so as to be aligned in series in the direction of the axis, and two lines of the stationary blades 11, 11, . . . are provided on the inner surface of the cylinder body 2 along the direction of the axis.
As shown in
As shown in
As the rotating blades 8, 8, . . . rotate, the spaces S in which a stationary blade 11 is located shift. The stationary blades 11 and 11 are attached with a gap of 90°, and therefore, one space S changes from a wide space S2 to a wide space S2 to a narrow space S1 to a narrow space S1 to a wide space S2 . . . .
The detachment/granulation zone Z2 is formed as described above, and screening reject is pushed into the detachment/granulation zone Z2, which is thus filled in. As viewed in the direction of the axis, the screening reject is greatly moved in the direction of the axis while rotating. That is to say, the screening reject is fed in the feeding direction while rotating by means of the rotating blades 8a, and retrieved in the retrieving direction while rotating by means of the rotating blades 8b.
In addition, the screening reject receives force in the direction of being compressed in a narrow space S1 as viewed in the direction that is perpendicular to the axis, whereas the force is relieved in a wide space S2.
In this manner, the screening reject is moved three-dimensionally in a complex and dynamic manner.
The screening reject is characterized by the state where needlelike hard fibers are entangled in the sticky foreign material that is softened by heat, and therefore, when the material is moved as described above, the fibers cross each other, which emits heat through friction. As a result of this emission of heat, the temperature becomes close to 90° C. or higher than that in some cases, and thus, the sticky foreign material receives heat so as to be softened and is kneaded in this state so as to be expanded and contracted. At this time, hard fibers are naturally detached from the soft, sticky foreign material. The rotating blades 8 and the stationary blades 11 do not have an edge portion that acts to cut the fibers, and in addition, the spaces S between the blades are set to a size that is sufficiently large as compared to the length of the fibers, which prevents the fibers from being damaged or cut. Then, the sticky foreign material from which the fibers have been detached is granulated and balled up.
When the opening for discharge 4 is opened after the pre-processing and screening reject is discharged therefrom, the sticky foreign material that has been balled up is cooled so as to maintain its shape, and at the same time makes it difficult for the fibers to pierce through.
Accordingly, the sticky foreign material that has been granulated and balled up stays on the screen as screening reject when being fed into the fine sorting process in the state after being discharged from the fine sorting pre-processing device 1, and the needlelike fibers pass through the screen as screening fines.
As described above, fibers can be collected not only from the screening fines that have been gained in the coarse sorting process, but also from the screening reject, and thus, the yield of the fiber collection can be significantly increased. In addition, the fine sorting pre-processing device 1 works rather better in the separation between the fibers and the sticky foreign material in the case where a greater amount of sticky foreign material is included, and therefore, the size of the slits of the screen can be set smaller in order to prevent the sticky foreign material from being mixed into the screening fines in the coarse sorting process.
Accordingly, the process of treating screening reject by using the fine sorting pre-processing device 1 can be carried out simultaneously together with the existing process of recovering waste paper so that fibers in good condition, where the sticky foreign material has been removed, can be collected from waste paper with high yield.
This device has a simple structure, which causes few glitches, and thus can be operated continuously for a long period of time. In addition, the operation is possible with power that is smaller as compared to the amount of processing, and as a result, the running costs are low.
The embodiments of the present invention are described above in detail; however, the concrete configuration is not limited to these embodiments, and modifications of the design in the scope where the gist of the present invention is not deviated from are also included in the present invention.
For example, the combination and the arrangement of the rotating blades 8a and the rotating blades 8b are free, and this arrangement can be appropriately set, taking into consideration the amount and the degree of the viscosity of the sticky foreign material that is included in screening reject.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-131348 | Jul 2019 | JP | national |
The present application is a National Stage application of PCT Application No. PCT/JP/2020/017003 filed on Apr. 20, 2020, which claims priority to Japanese Application No. 2019-131348 filed on Jul. 16, 2019, the disclosures of which are hereby incorporated by reference in their entireties.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2020/017003 | 4/20/2020 | WO | 00 |